By Bora Derin

The partial pressure ratios of sulfur and oxygen for several copper flash smelting plants were derived using the Reddy-Blander (RB) model and predicted dissolved sulfur contents available in the literature. The sulfide capacities (Cs) of six different flash smelting plants (FeO-CuOo.5- CaO-MgO-FeOu-AlO15-SiO2) slags were calculated. The log (PO2/PS2) versus matte grades of various industrial processes was determined. The PO2/PS2 ratio increased with an increase of copper grade. The calculated partial pressure ratios for the copper flash smelting are in good agreement with those of the experimental data.

Jan 1, 2003

By P. Kim, M. Tangstad, T. Larssen, R. Kawamoto

The reduction rates of MnO and SiO2 were investigated for various charge compositions. The empirical activation energies of MnO and SiO2 reduction from SiMn slags were calculated between 1500 and 1650 °C under CO atmospheric pressure. The amounts of metal produced at different temperatures were compared, and the Arrhenius plots were described for each slag A, slag B and synthetic slag, which shows that the raw material have significant influence on the reduction rate. The rate of Mn-produced in slag A was faster than slag B despite of the relatively lower driving force. The lower rate constant in slag B implies that other kinetic factors, such as viscosity, affects the reduction rate. The estimated activation energies of MnO were 920, 304 and 975 kJ/mol MnO for slag A, slag B and synthetic slag, respectively. The rates of Si-produced were similar and slow for all slag types. However, the different activation energies of SiO2 between industrial ores and synthetic materials implied that the trace elements can have catalytic effects toward SiO2 reduction in SiMn slags. The estimated activation energies of SiO2 reduction were around 800 kJ/mol for slag A and slag B.

Mar 1, 2017

By Sylvain Gouttebroze, Mohammed M'Hamdi

In a previous work, a small scale Bridgman furnace has been used to study silicon bi-grain crystallization at different cooling rate. This work expands the analysis by studying the mechanical interaction between the crucible and ingot during the solidification and cooling. The thermal model is based on a 2D-axisymetric heat-transfer model. The flux histories are then transferred to the ingot-crucible 3D-model. Anisotropic Elastic and Crystal Plasticity model are used to model the silicon deformation. Four different assumptions are applied to model the mechanical contact crucible-ingot and three grain misorientations are considered. The results show the strong impact of the alumina crucible contraction on the stresses and deformations in the silicon ingot.

Jan 1, 2015

By Guangshi Li, Xionggang Lu, Xueliang Xie, Xingli Zou, Yuyang Bian, Hongwei Cheng, Kai Zheng, Changyuan Lu

The corrosion resistance and corroded microstructure of MgO-C refractory in molten slag are investigated by immersion test in muffle furnace at 1600 °C . The microstructure and chemical compositions of the specimens after erosion experiment are characterized by scanning electron microscope (SEM) and energy dispersive X-ray (EDX). The results confirm that the oxidation of graphite is the most important degradation mode of MgO-C refractory. The structure of the refractory material is damaged due to the decrease of graphite, as a result, the periclase substrate reacts with the molten slag directly. The corrosion process is controlled by the dissolution of the refractory materials into slag, low melting point oxides are therefore generated which lead to the damage of MgO-C refractory finally.

Jan 1, 2015

By Joo Hyun Park, Soo Sang Park

The distribution behavior of Pb between molten copper and FetO-SiO2 (-CaO, Al2O3) slags was investigated at 1473 K (1200 oC) and p(O2)=10-10 atm in view of the reaction mechanism of Pb dissolution into the slag. The distribution ratio of Pb (LPb) decreases with increasing CaO content (~6 mass pct) irrespective of Fe/SiO2 ratio (1.4~1.7). However, the addition of alumina into a slag with Fe/SiO2=1.5 linearly decreases the LPb, whereas a minimum value is observed at about 4 mass pct Al2O3 at Fe/SiO2=1.3. The log LPb continuously decreases with increasing Fe/SiO2 ratio, and the addition of Al2O3 (5 to 15 mass pct) into the silica-saturated iron silicate slag (Fe/SiO2 < 1.0) yields the highest Pb distribution ratio. The log LPb linearly decreases by increasing the log (Fe3+/Fe2+) value. The Pb distribution ratio increases and the excess free energy of PbO decreases with increasing Cu2O content in the slag. However, from the viewpoint of copper loss into the slag, the silica-saturated system containing small amounts of alumina is strongly recommended to stabilize PbO in the slag phase at a low Cu2O content.

Jan 1, 2014

By Ehsan Vahidi, Fereshteh Rashchi, Amirhossein Shahnazi

"The pig iron from steel manufacturing plants contains a high concentration of vanadium-bearing materials smelted with iron ore. During the oxidation process of the molten pig iron with oxygen lances, vanadium transfers to the slag. In this research, recovery of vanadium from LD (Linz-Donawitz) converter slag of steelmaking plant was investigated. The leaching residue was characterized by XRD and XRF techniques. The maximum vanadium recovery was achieved at optimum leaching conditions of 70 °C, S/L: 1/15, sodium hydroxide concentration: 3 M and leaching time: 150 minutes. The dissolution rate increased with rising sodium hydroxide concentration and temperature and decreasing particle size. The experimental data are treated graphically to explain the kinetics of the vanadium recovery process using shrinking core model (SCM). As a result, the controlling regimes in the SCM were analyzed separately using liquid film diffusion control, solid product diffusion control, and reaction control mechanisms.IntroductionVanadium is commercially important as a constituent of several alloys and catalysts. Nowadays, vanadium is mostly recovered as a by-product from secondary sources or from industrial waste streams such as titaniferrous magnetite, fly ash, spent catalysts, and petroleum coke. Steelmaking operations are specifically concerned by this problem due to the production of a huge quantity of by-products [1]. These by-products, including LD converter slag, sludge, fly ash, spent catalyst, ash, and alloyed scrap, contain a notable amount of heavy metals which may cause environmental problems. Solvent extraction is one of the techniques being increasingly used for the recovery of vanadium [2]. Apart from vanadium ore, secondary resources such as titanmagnetite, ilmenite and slag from the ferrous industry are a major source of supply. The pig iron from steel manufacturing contains a majority of vanadium-bearing materials smelted with iron ore. In a heat resistant shaking ladle the molten pig iron is oxidized with oxygen lances, causing the vanadium to be transferred to the slag. Normally, the vanadium in LD converter steel slag (coming from Linz-Donawitz steelmaking process) is ca. 5% as vanadium pentoxide (V2O5). This slag is the world's principal raw material for vanadium production [3, 4]. Moskalyk and Alfantazi [4] reported that a roast-leach process is used in South Africa for the production of vanadium oxides from magnetite ores while some of the slag was converted to ferrovanadium. A portion of the slag was exported to Europe for the production of vanadium oxide. The researchers mentioned that alkaline roasting was the main process at that time employed to extract vanadium pentoxide from vanadium slags."

Jan 1, 2012

By Zhiqian Zhang, Chao Wu, Chao Li, Hongxu Li, Chuanqi Jiao

"Many used electronic and optical products contain cerium of rare earth oxides, but it is difficult to recover such rare earth compounds by traditional metallurgy methods. The proposed supercritical water metallurgy is a novel way, perhaps it will be very helpful for rare element recycling, but the thermodynamic properties at such special systems is not clear. In the paper the H20-CeO-CeO2 and H2O-CeO2-Ce2O3 ternary system phase diagram were produced under the pressure of30MPa with different temperature of350°C, 375°C and 400°C. The stability existing area of possible cerium compounds and different ions like Ce2+,Ce3+,Ce4+,W,HO2-,0ff ,CeOH2+,CeO+ and CeO2· were determined.IntroductionCerium is an extensively used metal element playing an important role in the rare earth elements. CeO2 is an apparently simple binary oxide with cubic fluorite structure [l]. Ce0O gives rise to a range of important technological applications because of its oxygen storage capacity at moderate temperatures as below: CeO2=CeO2.x+ X/2O2 [2]. The oxygen storage phenomenon gives ceria important technological uses in different fields as automobile exhaust purification catalyst [3-4], fluorescent powder, ultraviolet absorption material [5], polishing powder, fuel cell materials [ 6], and gas sensors, etc. The excellent properties of CeO2 nano powder make its synthesis and preparation become one of the hot spots of world scientists study."

Jan 1, 2013

By Asmo Vartiainen

Background of Direct-to-Blister Flash Smelting is discussed; especially slag chemistry relating to copper solubility, slag fluidity and impurity behavior. In December, 2000, Mini-pilot Flash Smelting test runs were carried out at Outokumpu Research Oy to produce blister copper from Chilean concentrate and white metal and from a mixture of them. Tested slag types were iron silicate slag, ferrous calcium silicate slag and calcium ferrite slag with different slag compositions and different concentrate/white metal ratios. The test runs were successful. The fluxing effect of copper oxide was clearly demonstrated and ferrous calcium silicate slags remained fluid on a very wide liquidus range. The distribution of arsenic between ferrous calcium silicate slag and blister copper is much higher than between iron silicate slag and blister copper. This successful test run with the new slag type offer new possibilities in Direct- to-Blister process design.

Jan 1, 2003

By William Petruk

A mineralogical and image analysis study was conducted on samples of U tailings from pilot-plant runs on Midwest ore in Northern Saskatchewan. The tailings had been subjected to simulated weathering for the equivalent of 10 years in a tailings facility (lysimeter). The pH varied from 7.0 at the beginning of the test to 5.9 at the end. The results show that during the simulated weathering sane of the gersdorffite, uraninite, galena and pyrite had oxidized, with gersdorffite being the most reactive and pyrite the least. Reaction was evident at the top of the lysilleter , but was most intense at the seepage discharge. sane of the released ions precipitated as Ni, Pb, and U arsenates, sulfarsenates, sulfates and oxides on particles of all minerals. Green crystals of Ni sulfate and white crystals of ca sulfate had precipitated at the surface of the lysilleter. Clay minerals and chlorite had washed from the top of the lysirneter towards the seepage discharge.

Jan 1, 1989

By G. Van Weert

Refractory gold ores and auriferous concentrates containing silver tend to form refractory silver jarosites during pressure oxidation. Earlier work with pure Ag2S has shown that the addition of iodine species to the autoclave feed yields cyanide soluble iodargyrite (Agl) instead. Near complete silver extractions from the autoclave product were obtained at a I-/Ag+ ratio of 5 or more. This paper reports on the pressure oxidation and cyanide leaching of two industrial refractory (arseno) pyritic silver-bearing concentrates: 1. from Peru (sulphosalts) and 2. from the USA (pyrite, with acanthite occlusions). While using a I-/Ag+ mol ratio of only 1 in the feed, it has been possible to obtain 98 and 97% Ag extraction from the two autoclave products by cyanide leaching, respectively. This compares to 11 and 54% Ag extraction from the as-received concentrates and 4 and 15% Ag extraction, respectively, after pressure oxidation without KI present. The results of the testwork are discussed in terms of concentrate mineralogy and pressure oxidation conditions.

Jan 1, 1994

By A. S. Usrnani

Due to both turbulence and the highly variable geometry of castings, a realistic numerical simulation of the metal flow is prohibitvely expensive with current technology. However, when the chief purpose is to achieve realistic thermal fields a precise How simulation is not necessarily required. In this paper we assume a laminar flow regime and obtain the flow field by solving the incompressible Navier-Stokes Equations using a velocity-pressure segregated semi-implicit finite element method. The free metal surface is predicted by advecting a pseudo-concentration function via the computed How field. This involves an explicit finite element solution of a pure advection equation. The thermal field is calculated by solving the convective-diffusive energy equation by an explicit finite element method using the computed flow field and the location of the free surface. All the advection terms are discretized using a Taylor-Galerkin method. The interface between the metal and mould is modelled using special interface elements. The model is demonstrated by solving practical example problems. The results show that a sharp thermal front is maintained during the course of filling without excessive diffusion. The heat diffusion in the mould can be controlled by varying the metal mould heat transfer coefficient.

Jan 1, 1994

By Frederico Muylaert Margem, Sergio Neves Monteiro, Marina Rangel Margem

Natural fibers presents interfacial characteristics with polymeric matrices that favor a high impact energy absorption by the composite structure. The objective of this work was then to assess the charpy impact resistance of polymeric composites reinforced with one or two layers of batt jute and malva fibers. The results showed a remarkable increase in the notch toughness with increasing layers of jute blankets and malva. This can be attributed to a preferential debonding of the fiber/matrix interface, which contributes to an elevated absorbed energy.

Mar 1, 2018

By Ygor Macabu de Moraes, Jean Igor Margem, Carolina Gomes Dias Ribeiro, Frederico Muylaert Margem, Sergio Neves Monteiro, João Batista Vasconcelos

A natural fiber presents interfacial characteristics with polymeric matrices that favor a high impact energy absorption by the composite structure. The objective of this work was then to assess the Izod impact resistance of polymeric composites reinforced with one or two layers of batt malva and jute fibers. The results showed are markable increase in the notch toughness with increasing layers of mauve blankets and jute.This can be attributed to a preferential debonding of the fiber/matrix interface, which contributes to an elevated absorbed energy.

Mar 1, 2017

By Takaaki Ishikawa

The distribution equilibria of lead, zinc and copper between CaO-Si02-Ah03 melts and liquid copper were measured at 1623K under a controlled H2-C02 atmosphere. The distribution ratios were plotted against the oxygen partial pressure, and reasonable oxide forms dissolved in the melts were estimated from the slopes of the plots. The activity coefficients of zinc oxide (ZnO), lead oxide (PbO) and cuprous oxide (CuO0.5) increased with increasing slag basicity, defined by XCao/Xsio2 The temperature dependence of the activity coefficients was also measured.

Jan 1, 2003

By Jilai Xue, Jun Zhu, GermainKouma Ndong, Luxing Feng

High-temperature corrosion behaviors of Fe-Ni-Cr alloy as inert anodes for aluminum electrolysis have been studied. The effect of anodic overpotential on layer growth of anodic surface is specially considered. The corrosion layers on the anodes tested were analyzed using XRD and SEM-EDS to provide a fundamental understanding of the layers growth at metallic anode surface. The dissolution of the scale layers on the metal anode occurred with low overpotential, while AlxM3-xO4 spinel phase within the scale layers was found with an increased overpotential. A mixture of multiple MyO layers existed on the anode substrate. The results may be useful for understanding and controlling the corrosion behaviors of Fe-Ni-Cr anode for potential application in aluminum electrolysis.

Jan 1, 2015

By M. -V. Wang

Hydrotreating and hydrorefining (HT and HDS) spent catalysts contain molybdenum, vanadium, nickel or cobalt at concentration levels that can make metals recovery economically viable. Quanzhou Jing-Tai of China has developed, through many years of operating experience in metal recovery from spent catalysts, a simple process for recovery of these metals and the production of environmentally benign residues. The process first subjects the catalysts to a low-temperature calcination step, followed by grinding of the calcine. The ground material is then leached with 10-20% v/v hydrogen peroxide to recover metals such as Mo, V and Ni or Co. This step has a selectivity that is greater than 95% for the metals. The undissovled residue, which contains mainly Ah03 and Si02, can be dewaterd and used in the production of masonry bricks. The pH of the rich liquor is then adjusted to between 0.5 and 2.5 by adding dilute sulfuric acid to co-precipitate Mo and V, with a recovery rate of greater than 99%. The lean liquor contains mostly dissolved Ni or Co, which can be recovered through precipitation at a pH of between 8.5 and 9.5 by caustic additions. The final liquor is then sent to an ion exchange step for final recovery and cleanup of residual metals. The effluent is then discharged after a simple wastewater treatment process, which has been found to meet all environmental requirements. The entire process has been found to be simple, cost-effective with minimal environmental impacts while achieving the goal of complete resource recovery from spent catalysts commercially.

Jan 1, 2000

By G. White

Traditional atmospheres used for Aluminum annealing have been air, exothermic gas, and cryogenic purity Nitrogen. Air and exothermic gas have several problems associated with them such as surface discoloration, toxic emissions, and explosion hazards. High Oxygen levels can cause Magnesium streaking and oil staining, and therefore pure Nitrogen has been the atmosphere of choice for high quality Aluminum coils. A comparative study was made on key Aluminum alloys annealed in Nitrogen with different Oxygen concentrations to determine the effect on surface quality. The atmosphere composition inside the furnace was analyzed during the purge and heat cycle to determine its effects on purge times and exhaust emissions. The Aluminum coils after annealing were visually inspected for surface staining before and after rolling. The lab study revealed that Nitrogen with up to 1.0% Oxygen is acceptable, and did not adversely effects the surface quality or any of the other processing variables. However it isbelieved that higher Oxygen concentrations are acceptable depending on the rolling oils and alloy systems.

Jan 1, 1996

By Seiji Yokoyama

As a series of fundamental study on the gas evaporation method, a levitation-melted aluminum was evaporated in the gas mixture of argon and ammonia to synthesize ultrafine particles of aluminum nitride. When the ammonia partial pressure were more than 2kPa, the formation ratio of aluminum nitride was about 95%. The particles of aluminum nitride were mainly hexagonal. The mean size of the particles of aluminum nitride was about 57 nm, and it was constant without depending on the temperature of the levitated aluminum and the partial pressure pf ammonia. The aluminum nitride was formed by the reaction between ammonia and condensed liquid aluminum particle whose size was relatively small.

Jan 1, 2006

By O. Kitamura, H. Kubota

The Harima Works started its ISP operation in 1966 and been expanding its production capacity from 3,000 tonne Zn/month and 1,500 tonne Pb/month to 7,500 tonne Zn/month and 2,500 tonne Pb/month. It is not only treating zinc, lead and bulk concentrates but also secondary materials like Waelz kiln oxide from the Shisaka Works of Sumitomo Metal Mining, waste treatment sludges, industrial wastes and others. Its final products cover Prime Western Grade (PWG) zinc, Special High Grade (SHG) zinc, continuous galvanizing grade zinc, electrolytic lead, cadmium, indium, thallium and sulfuric acid. This paper briefly describes the smelter's historical and present operations. The key data for the current impurity control management and for the distribution of impurities such as copper, iron and arsenic are presented.

Jan 1, 2000

By Joseph Hamuyuni, Dmitry Sukhomlinov, Pekka Taskinen, Mari Lundström

The standard thermodynamic properties of the compound Ca2CuO3 were determined electrochemically by the Electromotive Force (EMF) method. The ternary phase Ca2CuO3 was synthesized from the pure oxides CaO and CuO at CaO saturation using a ceramic route. The EMF measurements were performed over a temperature range 973 T/K 1124. The standard Gibbs energy of formation of the ternary compound Ca2CuO3 was determined using the EMF technique as: DfðoxÞGCa2CuO3 ¼ 21:88422:92 103 T: ð1Þ

Mar 1, 2017