A new copper continuous converting process was investigated to evaluate the possibility of its application in the commercial operation. The tests were performed both in the laboratory and in pilot plant scale. Bath smelting process with the use of the top submerged lance technology was applied in these tests. Furnace shape was modified to a lengthwise eylindrical one with a settling area. The furnace monitor was put in the settling area to check the furnace from inside, FeOx-Si02, FeOx-CaO and FeOx-CaO-Si02 based slag systems were used to check their efficiency, The optimum slag chemistry to have good metallurgical results was discussed and FeOx-CaO system with some Si02 content turned out to be preferable although it has not been practically used, In this pilot plant test feeding rate of I tIH of solid grain matte was charged consecutively for two weeks and continuous converting could be done successively. This process is expected to overcome the problems of existing processes and be easily applied in existing plants.

Jan 1, 2003

By Shizhe Liu, Bing Li, Heng Wang, Zuxin Zhao

In this paper, cyclic voltammetry and chronoamperometry have been applied to investigate the effects of Nd2O3 concentration on the anode effects, critical potential for the anode effects and Nd2O3 reduction in LiF-NdF3-Nd2O3 melts at 950℃. The results show that the oxidation peaks in the potential of about 2.7V are attributed to the oxygen ions oxidation and the peak current density increases with Nd2O3 concentration increase from 0 to 0.5wt%. The critical potential caused the anode effects shifts to 0.3V more positive value as Nd2O3 content in the melts decreases from 0.01wt% to 0.5wt%. The cyclic votammograms on W electrodes in the LiF-NdF3-Nd2O3 melts present two pairs of reduction and oxidation peaks, indicating that the reduction of Nd ions in the LiF-NdF3-Nd2O3 melts in two steps rather than one step.

Jan 1, 2014

By Jeffrey R. Taylor

The distribution of low concentrations of Cr, Mn, Rh, Co, Ni, Ag and Fe between copper matte and bullion phases has been measured at 1200oC. These results. together with values for nine other elements, have been used to develop a simple model to describe the distributions in terms of known thermodynamic properties?. The Temkin model for ionic melts was assumed to apply to the sulphide species in the Cu-S matte? phase and it is shown that the choice of sulphide species is particularly important for successful representation of the experimental .results?. In general, the lowest sulphlde (minimum sulphur :. metal ratio)? formed by the. metal is most suitable, although Ni, Co, Rh and Pd appear to associate with more sulphur in the melt than suggested by the? composition of their lowest sulphide. A correlation between the composition of the metal sulphide species formed in the ternary system and the? position of the minimum in the free energy of mixing curve in the metal-sulphur binary -system is? proposed.

Jan 1, 1983

By Ledjane Barreto, Tulio Flávio Accioly de Lima e Moura, Wilson Acchar, Antonio Carlos Silva da Costal

"Clays are common ingredients in pharmaceutical products both as exclplents and active substances. Clay minerals are naturally cationic exchangers and they may undergo ion exchange with basic drugs in solution. Smectites, and montmorillonite have been studied due their high cation exchange capacity as compared to other silicates. Recently a patented study reports the use of attapulgite as the encapsulating agents both for the protecting the active substance and modulating release into the body. Some clays such as kaolinite, smectites, talc, etc are also used as dermatological protectors. Sepiolite and smectites have the ability to form complexes with organic compounds with absorb ultra-violet radiation, enabling them to be used in sun screens with protection factors. The objective of this work is to characterize the attapulgite in order to study the potential use of this clay material in the human health.IntroductionSince the begimling of time, nature has served humanity as a source of various raw materials. Among these, clays such as kaolinite and ilitte are common ingredients in the tile production. Recently, special clay materials have been investigated in order to identifY new potential uses of these class of materials. Clay materials are natural raw material and have excellent properties such as low toxicity, good biocompatibility, making them a good material to be used in biological applications. Attapulgite (paligorskite) and sepiolite is so called special clays. These special clay materials are very sin1ilar and have a great potential to be used in some technological areas due their special catalytic, sorptive and colloidal-rheological properties [1-8]. Recently some works have reported the use of these special clays materials for many applications such as drug delivery, wound dressing, oil absorbent, pesticides, fertilizers [9-12]. Brazil has a significant reserve of attapulgite located in Piaui state, making the study of the potential of this mineral in special areas, very attractive. Attapulgite is classified a fibrous alluminous silicate material and shows the presence of micro pores and channels, fine particle size and high surface area making this material a good candidate alternative material to be used in many industrial applications [6,8,9,11,12]. The objective of this work is to characterize the physical and microstructure of attapulgite."

Jan 1, 2012

By Anette Mueller, Thomas Schnellert, Sérgio C. Angulo

"The use of automatically sorting technique, to separate gypsum components from recycled material of processed construction and demolition waste (C&DW), is motivated by environmental and economical aspects. Only if the gypsum can be separated the aggregates can fulfill the environmental requirements and also the structural characteristics according to the standards. Furthermore, the separation of red brick can also improve the quality of the aggregates.This paper aims at analyzing the separation of gypsum components and red brick by using the color sorting technique. The impacts on the composition and the envelope density of recycled aggregates are described. Depending on the gypsum content the application of two processing stages (rougher-cleaner) can be necessary to produce aggregates with sufficiently low gypsum content. Additionally, the separation of red brick and concrete is successful. So, the color sorting may be a promising technique to upgrade the quality of mixed C&DW aggregates.IntroductionConstruction and demolition waste (C&DW) is a mixture of different materials. Such mixtures can be used only in low grade applications. If the material is used as certified material for road construction or as aggregate in concrete the concrete particles must be separated from the other building materials. This paper aims at analyzing the separation of gypsum components and red brick by optical sorting. The needed stages of sorting for getting a product quality according to the German Standards are deduced.Gypsum is a building material that is increasingly used for interior works in Germany like it is shown in figure 1 [1]. At present the content of gypsum in C&DW is estimated at about 1 %. Assessments on the basis of material streams of gypsum and concrete and their life spans show that higher gypsum contents of about 3 % must be expected in future [2]. Also in other countries the use of gypsum has grown considerably in the last decades. From the characterization of C&DW available in some cities in Brazil, 4 to 15 % of total amount of C&DW that may arrive at the recycling plant to be processed is excessively contaminated by gypsum. In one of these cities, the average content of gypsum in the C&DW before processing was as high as 2.1 % [3]."

Jan 1, 2008

By David M. Davidson

Seven intrusive phases have been mapped to date in the 1 b.y. Red Bluff Granite Complex (RBGC) near El Paso, Texas. This batholith is 20 km2 in area and intrudes older supracrustal units as well as a trachyte ignimbrite cap. Two early microgranite sills are spatially separated 6 km from a porphyritic, three-phase "ring complex" by a tin-bearing, biotite granite which cores the RBGC. These units are intruded, in turn, by a riebeckite granite which locally exhibits lineated and pegmatitic textures as well as exceptionally high light REE and Zr values (800 ppm La; 3,000 ppm Zr). The riebeckite granite is exposed in three separate occurrences within the Franklin Mountains. REE values in the RBGC are depleted in HREE and show distinct negative Eu anomalies. Typical La/Yb ratios are 5:1-2:1 with Eu values ranging from 10-80 ppm. The mineral source of the high REE values in the riebeckite granite has not yet been specifically identified, but is believed to be zircon.

Jan 1, 1988

By Mahmood Alemrajabi

When LKAB processes their iron ores in northern Sweden, they generate apatite as a by-product. The apatite has been recovered by flotation and the concentrate contains about 0.4 wt% rare earth elements (REE). Both phosphate rock and REE are listed as critical raw materials for the European union. In the present study, the recovery of REE within the nitrophosphate process of fertilizer production has been studied. In the first stage, the REE are precipitated and isolated as a phosphate concentrate. For further purification and individual separation of REE by solvent extraction, removal of phosphorous from the concentrate to enhance the dissolution of REE in mild acidic solutions is essential. In this study, thermal treatment of the concentrate with sodium hydroxide at elevated temperatures followed by water leaching has been studied in order to separate the phosphorous and thereby facilitate dissolution of the REE. The results show that 95% of total phosphorous initially present in the REE phosphate concentrate is removed after thermal treatment with NaOH 1:1 mass ratio, at 400 °C.

By Godwin M. Beene

Large scale mining operations started in Zambia in 1913 and rapidly expanded during the post 1930 period with the opening of several mining and processing plants on the present Zambian Copperbelt. As a consequence of poor tailings dumps design methods at the start of the mines, and in view of stringent Government Legislation pertaining to environment in the recent years, Nkana Mine has developed a unique method of dump construction at its current tailings depository, Tailings Dam 15A. This method has enabled the revegetation of the dump retaining walls while construction is still in progress, a situation which was not possible on the older dumps. Cowdung has proved to be a superior fertilizer for providing plant nutrients on the tailings. The new method of dump walls construction and walls rainwater runoff drainage system has almost eliminated tendency of gully formation which is common on older dumps, as rainfall on the Zambian Copperbelt comes in intense thunderstorms. The decanted water from the dump is discharged to the natural environment in a controlled fashion after ensuring that it meets the Zambian Government Statutory requirements.

Jan 1, 1999

By P. E. Donaldson

Since 1992, Falconbridge has made available to the international copper industry, Kidd Creek's licensed refinery process technology under the name of the Kidd Process. This has resulted in the supply and installation of permanent cathodes and associated product handling equipment to refineries in Canada, the United States, South Korea, Chile and Mexico. These installations accommodate both electrorefining and electrowinning processes. The growth and industrial acceptance of the Kidd Process has generated technical advancements in the areas of product random sampling, corrugation, marking, labeling, product tracking and data acquisition. In a different area, the expanded development of custom materials processing at Kidd created a need to advance technologically. The process-related problem of high nickel concentrations in refinery electrolyte compromised an increase in current density to >300 A/m2. The need for nickel removal resulted in Kidd Creek's newly developed Nickel Recovery System. The effective and economical extraction of nickel, along with reduced antimony and bismuth levels, reduces bleed stream volumes and/or neutralization costs and simultaneously produces a marketable nickel carbonate product.

Jan 1, 1999

By Luiz R. P. De Andrade Lima

This paper presents a mathematical model for the oxide copper ore heap leaching process. The data used in the model include physical-chemical, .geometrical and operational data, as: leachable metals ore contents, .flow rate and acid concentration, parameters of passivity, ore size distribution, the average residence time of the solution in the heap, height, irrigated area and weight of ore in the heap. In this model the heap is divided into horizontal and plane layers of constant area. The flow of the liquid in the heap is considered unidirectional and the solid-fluid reaction model is considered under diffusive control. The average residence time of the solution into the heap and the apparent effective diffusivity of the acid through the ore particles have .a significant influence on the rate of the copper extraction and its concentration in the pregnant solution; therefore these parameters are used in the model calibration. When this algorithm was applied to a laboratory test, the results showed that the model is adequate to predict the process performance.

Jan 1, 1999

By Nathaniel Arbiter

The first ammonia leaching plants, applied to copper carbonate and native copper tailings in 19 15, were followed more recently by research and development of flowsheets for ammonia leaching of sulfide concentrates. These were applied to two commercial plants. Anaconda's Arbiter Plant started up in 1974 with a design capacity of 36,000 tons/year of cathodes, to be produced by ammonia leaching with oxygen, followed by solvent extraction and electrowinning. The plant shutdown in late 1977 as a result of high maintenance and operating costs, partly due to harsh winters; to complications associated with sulfate disposal; and to changes in mineralogy. BHP's Coloso plant in Chile was designed to produce 80,000 tons/year of cathodes by leaching part of Escondida's concentrate production. Using a similar flowsheet but with air and low temperatures to avoid sulfate production, it started up in late 1994 and shutdown in mid-1998, after failing to reach cathode design capacity, and experiencing problems with its technology. The paper reviews the technologies and also alternative methods for overcoming the problems.

Jan 1, 1999

By M. K. Patel, K. A. Pericleous, M. Molaei

"The future trading of carbon credits and increased financial cost necessitates substantial cuts in incidental C02 emissions in the production of metals (iron, steel, aluminum, zinc, lead). Although greener methods of production are being developed, in the short term the use of point-source C02 extraction using existing technology remains attractive. Accelerated natural carbonation, in a fluidized bed is a feasible technological route investigated in this research. CFD modelling has been used to study the efficiency of C02 capture in a fluidized bed reactor containing a CaO solid sorbent. A Lagrangian/Eulerian scheme describes describe CaO particle trajectories and exchange of mass, momentum and energy with the carrier gas, with a typical off-gas composition. Different reactor geometries are considered (with uniform, stepped and gradually expanding cross-section), to maximize conversion for a given particle loading and size distribution (100-200 microns). Removal efficiencies of up to 80% are demonstrated, making this a viable process.IntroductionBased on Intergovernmental Panel on Climate Change (IPCC) reports, the major cause of climate change and global warming is due to a high level of C02 concentration in the atmosphere resulting from fossil fuel combustion, particularly in coal-fired power plants [1]. Carbon capture and storage is therefore the most important action proposed to reduce C02 from combustion flue gases. In this process, carbon dioxide is captured and may then be regenerated as pure C02 and conducted to a permanent storage, or simply stored as a solid carbonate [2]. Capture and storage of C02 has an economic penalty and the main cost of this penalty is associated with the capture plant. Capturing C02 with a lime-based solid sorbent (CaO) is a very promising technique, due to the low cost and the wide availability of the reactant. In this process, the CaO reacts with C02 based on the following reaction in a reactor called a Carbonator:"

Jan 1, 2012

By Atinuke Oladoye, David Esezobor

"Particulate Copper Silicon carbide (Cu-SiCp) composites find application as wear and heat resistant materials in electrical sliding contacts such as in homopolar machines, railway overhead current collector systems where high electrical/thermal conductivity combined with good wear properties is required. However, challenges occur during machining due to the presence of hard reinforcement in the matrix. This may lead to high turnover of tool wear and poor surface finish. The adoption of near-net shape technology to produce such hard-to-machine metal matrix composites and subsequent finish machining with its attendant cost has reported limited success. This paper critically appraises the challenges and opportunities in the improvement of tribological characteristics of particulate Cu-SiC composites and identifies low cost reinforcement material that could be used to improve its tribological characteristics.IntroductionTribology consideration is increasingly becoming a decisive factor in the design and selection of materials for applications involving interacting surfaces in relative motion. The consideration is mainly on the combined effects of friction and lubrication on material's wear integrity and performance amongst other. Annual losses due to tribology in the US industries are estimated at between 1-2% of the Gross National Income [1], in Russia it is about 1-4% of the GDP [2]. Thus, the attributes of tribology has become imperative in modem machinery especially those applications involving sliding and rolling surfaces, and electrical contacts [3- 8].These are readily found in homopolar machines, internal combustion engines, aircraft engines, gears, cams, seals and railway overhead current collector systems [9-12]. In these systems, the dissipation of frictional heat arising from the interacting surfaces as quickly as possible imposes constraints on the choice of materials for such application to prevent softening, plastic and shear flow and the transfer of metal as wear debris onto the interacting surfaces. If these possibilities occur, system performance is compromised and premature failure may result. Materials for these systems are expected to possess high electrical and thermal conductivities, low coefficient of thermal expansion, good corrosion resistance and high melting point [3-8, 13]."

Jan 1, 2011

By Wilky Desrosin, Alicia E. Ares, Carlos E. Schvezov

"In the present research the horizontal directional solidification Zn-Sn alloys (Zn-4wt. %Sn, Zn- 6wt. %Sn, Zn-10wt.%Sn and Zn-30wt.%Sn) was carried out by extracting heat in two opposite directions. For this purpose, ceramic molds, a muffie, a horizontal furnace with two heat extraction systems at the ends, a measurement, acquisition and recording temperature system, eight K-type thermocouples and an electronic recorder were used. The main parameters involved in the columnar-to-equiaxed transition, CET, were: the moment of start and end of solidification at each position under consideration, cooling rates, the average temperature gradients and critical temperature gradients at the CET, the average speed of liquid and solid interphases left and right, advancing in opposite directions. Also, solidification kinetics was found to be different between horizontal solidification two-way heat extractions, with preliminary results of the vertical unidirectional solidification. In the solidification experiments, the velocity and accelerations of the liquidus and solidus interphases usually occurs at the end solidification zone of the samples.IntroductionSolidification of metal alloys, which starts in the external equiaxed region (chill), results in two basic types of structures in a single solidified alloy sample: columnar and equiaxed. The presence of both structures indicates the occurrence of the colunmar-to-equiaxed transition phenomenon[!].Studying the colunmar-to-equiaxed transition, CET, is of great technological interest for the evaluation and design of the mechanical properties of the solidification products. To this end it is necessary to understand the mechanisms by which it occurs. As found in previous studies [2-5], the CET occurs by competition between columnar and equiaxed growth. Mainly is controlled by the parameters of casting, such as the alloy composition, the density of the present nuclei in the liquid, the cooling capacity of the metal I mold, and the degree of convection in the liquid [7-10]."

Jan 1, 2014

By C. Y. Tang, Z. H. Chen, T. C. Lee

"In sheet metal forming process, the forming limit and strain distribution are governed by plastic instability and fracture following strain localization. It has been proved that the temperature gradient caused by plastic deformation as well as friction is one of the crucial factors to induce the strain localization in high-speed metal forming processes. In this paper, a numerical simulation of the sheet metal extrusion process has been conducted by using thermal-mechanical coupling finite element method. An improved mixed finite element method has been used to solve the large deformation elasto-plastic problem. In thermal phase, the transient heat transfer finite element method together with the Crank-Nicholson algorithm has been employed to determine the temperature field. Both the numerical results and the experimental observations reveal that the temperature gradient plays an important role in inducing the strain localization, which eventually leads to fracture failure in the sheet metal extrusion process.IntroductionSheet metal extrusion is such a process where the extrusion punch penetrates into one surface of the sheet metal material to let it extrude and flow towards the outlet of the die. This process can be used to produce protruding parts on a strip material. In engineering applications, the quality of the product is affected by many factors such as stress state, loading speed, material properties and lubrication condition. The research on failure mechanisms and improvement of formability in sheet metal forming processes by exploitation of differential thermal conditions has been of great interest recently [1-3]. It has been proved that the temperature gradient caused by plastic deformation, heat transfer, and friction between sheet and tools is one of crucial factors to affect 'the formability in high speed sheet metal forming processes [4]. In our previous study of sheet metal extrusion, it has been observed that plastic deformation is highly localized and some specimens are subjected to fracture failure in the form of crack propagation [5]. To understand this failure phenomenon, the effects of temperature gradients must not be ignored."

Jan 1, 2001

By Jian Li, J. Miles, P. Liu, W. Cook, W. Zheng, Alvin Qian

"High temperature corrosion resistance is one of the key challenges in water-cooled nuclear reactor material development. Iron based materials with low Cr content exhibits superior high temperature mechanical properties. However, due to the relatively low Cr content, their corrosion resistances under supercritical water (SCW) conditions are generally poor. High-Cr alloys, despite their much improved corrosion resistance, often suffer from embitterment due to the precipitation of sigma phase in the microstructure. In this study, corrosion resistance of an in-house produced high Cr steel (25%Cr) showed much better corrosion resistance compared to that of low Cr alloy (14%Cr). This high-Cr steel can potentially be used as a corrosion-resistant coating for structural materials in sew applications.INTRODUCTIONThe supercritical water-cooled reactor (SCWR) concept is one of the promising designs for the next generation nuclear reactor, in which the water coolant is designed to be at about 625°C and 25 MPa at the outlet of the reactor core. Under these relatively high-temperature and high-pressure conditions, the cooling water is at supercritical state. High-temperature mechanical properties, corrosion resistance and radiation damage are some of the key challenges. At present, no single commercial material can meet all the requirements of the severe SCWR in-core conditions. Canada supports research in several key areas of SCWR development, including materials selection. A major focus is on materials development, selection and evaluation for both in-core and out-of-core components.Allen et. al. [1] carried out a comprehensive study on the SCW corrosion resistance up to 600 °C on commercially available high temperature materials including Ni-based super alloys, various types of stainless steels and ferritic/matensitic steels. They concluded that ferritic steels develop a relatively thick but mechanically stable oxide layer, while austenitic alloys develop a thinner oxide layer that has been found to spall in some cases. Of the three types of alloys examined, the Ni-based alloys exhibited the lowest oxide thickness, however pitting was observed in the vicinity of intermetallic precipitates."

Jan 1, 2011

By T. T. Chen

Secondary copper anodes are generally rich in Sn, Pb, Ni and Sb, but are notably deficient in Se, Te and Ag. In the secondary copper anodes, most of the Ni, virtually all of the Ag, slightly more than one-fifth of the Pb, about one-third of the As and Sb, and approximately one-tenth of the Sn are in solid solution in the copper. The remaining impurity contents occur as 1-5 µm grain-boundary inclusions in the anodes, and these are mainly Cu2O, SnO2, Cu-Pb-As-Sb-Bi oxide, Pb-Sb oxide, Sn-Ni-Zn oxide, Cu-Sn-Ni oxide, Cu-Sb-Ni oxide (Kupferglimmer) and trace Cu2(Se,Te). Barium sulphate, which originates from the mold wash used in casting, is also present in the anodes. During electrorefining, the BaSO4, SnO2, Pb-Sb oxide, Sn-Ni-Zn oxide, Cu-Sn-Ni oxide and Cu- Sb-Ni oxide inclusions are liberated and accumulate in the slimes layer. Solid solution Ni dissolves and the Ni accumulates in the electrolyte. Solid solution Sn and Pb dissolve, but partly reprecipitate as Sn arsenate and PbSO4, respectively. Solid solution Ag dissolves but rapidly reacts to form Ag2(Se,Te), Ag powder, Ag-bearing Cu2O, (Cu,Ag)SO4 or a complex oxidate phase. Partial dissolution of the Cu-Pb-As-Sb-Bi oxide particles takes place; the Pb component is converted to PbSO4, whereas Cu, As, Sb and Bi dissolve. The reacted particles retain the morphology of the original Cu-Pb-As- Sb-Bi oxide phase. Some of the solubilized As, Sb and Bi remains in solution, but much reprecipitates as SbAsO4, As-Sb-Bi oxide, and as a poorly defined oxidate phase which consists mostly of Cu-Ag-Pb arsenate-sulphate. The high Sn contents of secondary copper anodes do not seem to affect the behaviour of the anodes during electrorefining.

Jan 1, 1999

By Lucas Barbosa de Souza Martins, Frederico Muylaert Margem, Nathalia Carneiro Garcia Rosa, Sergio Neves Monteiro

"A natural banana fiber extracted from the plant pseudostem has shown values of density and mechanical strength with potential for uses in engineering applications such as automobile interior parts and floating components. Moreover, natural fibers can also be used as insulating materials in packaging and building panels. In this case some thermal properties are required. Therefore, the objective of this work was to evaluate the thermal behavior of the banana fiber by means of TGA, DTG and DSC analysis. The TGA curves revealed weight loss related to release of humidity and molecular structure decomposition. Peaks in the DTG curves indicated two intervals in temperature associated with different decomposition processes. The only endothermic DSC peak found was attributed to the lignocellulosic water of hydration being lost around 121°C.IntroductionIn recent times, environmental aspects related not only to pollution caused by non-degradable synthetic leftovers, specially polymeric wastes, but also to climate changes as a consequence of industrial activities, are motivating the use of natural materials. A particular case is fibrous composites, like the fiber grass composites. These synthetic materials, made from non-renewable polymers, are practically non-degradable and contribute to global warming by the CO2 emission associated with the energy required for the fabrication process. In spite of these environmental shortcomings, fiber materials are essential for the production of many items such as insulating chests, automobile cushion, construction panels, etc. An environmentally correct alternative to replace synthetic fibers composites is the naturally existing ones extracted from plants such as ramie and sisal. These have some environmental advantages of being renewable and degradable, these banana plant provide a negative contribution to C02 emission by absorbing greenhouse gas during the plant life cycle. Banana fibers have been used since long time in simple items such as ropes and rugs. Today they are used in engineering applications related insulation in building panels [2] and finish parts in automobile interior components [3]."

Jan 1, 2012

By Honorio Oliveros Gómez, Oscar Jaime B. Restrepo

"Colombia produces nine tons of electronic waste per year and there are approximately 60 tons accumulation generated in the last nine years. This work aims to establish a general methodology in the laboratory to recover gold, silver and platinum group present in electronic waste, also explore other forms of recovery of metals contained in electronic waste. We selected seven types of electronic cards present in the computers, which have their parent desoldering electronic components. Initially, we characterized the components of the cards through X-ray diffraction and SEM, to identify the metal species and composition. Tests were conducted laboratory hydrometallurgical recovery of metals. This paper proposes a methodology for laboratory-scale work.INTRODUCTIONColombia produces nine tonnes of electronic waste per year and build there in about 60 tons generated in the last 9 years [1], Computers, TVs, audio equipment, monitors, cell phones, remote controls, printers and operated toys battery, among others are part of this inventory, which mostly comes to landfills, because the lack of legislation to control the final destination of waste electrical and electronic equipment, and lack of efficient technologies to recover materials [2]. Under these circumstances which have environmental implications, technological and economic recovery is essential metals present in the electronic cards of computers, by hydrometallurgical with subsequent base metal electrodeposition [3]. Pyrometallurgical route is discarded by major implications for economic and environmental [4]. Recovery From this perspective, the determination of the metal fraction and the relationship between the different metals, using the SEM characterization techniques - BSE and XRD is indispensable [5] It follows with electrolytic dissociation processes in the leaching and electrodeposition [6], and unit operations in the laboratory to carry out successfully these processes on a larger scale. Were randomly selected computer twenty-four postcards for nine types of cards have different functions in the computer, which, through the absorption desoldering technique, they broke the resistance (thermal, surface, photoresist, power), capacitors (ceramic, electrolytic), diodes (silicon, germanium, high frequency), transistor (NPN, PNP), processors, integrated (high, medium and low frequency), the RAM card and pin parallel port serial"

Jan 1, 2011

By Felipe P. D. Lopes, Jr. dos Santos, Sergio N. Monteiro, Frederico M. Margem

"Natural fibers are gaining attention as a class of low cost, biodegradable and renewable materials that also exhibit some interesting properties for specific applications. In particular, the incorporation of some natural fibers in polymeric matrix composites is nowadays providing opportunity of manufacturing a variety of industrial items, for instance automobile interior components. Among these fibers, ramie (Boehmeria nivea) is one of the least investigated and only recently was studied as polymeric composite reinforcement. Therefore, the objective of this work was to evaluate the possibility of ramie waste reinforced polyester composites to replace conventional building materials, such as plywood, plastic boards and gypsum panels in terms of a cost-benefit analysis.IntroductionThere is a growing concern over the environmental questions that are presently affecting our society in a global sale such as climate changes and generalized pollution. Among the solutions for these questions, the replacement of energy intensive materials, especially those long term degradable such as the synthetic fibers, is already being considered [1]. As a consequence, the past decades have witnessed an increase in research devoted to new biodegradable materials obtained from natural resources mainly the biomass. Important examples are the renewable natural fibers as well as composites incorporated with them [2,3]. In addition to their friendly status with respect to the environment, well know natural fibers like jute, sisal, wood, coir, hemp and flax are relatively low cost and recyclable. In recent works [4,5], the use of these cultivated and abundant lignocellulosic fibers was investigated as the reinforcement phase in polymeric composites.Other less know lignocellulosic fibers have also been recently investigated [6,7]. These are fibers that likewise show a potential of incorporation into the polymeric matrix of composite materials. Most of these less know fibers are typical of tropical regions and, in principle, their application in industrialized composites would represent job opportunities for developing countries in Africa, South Asia and Latin America."

Jan 1, 2008