By R. N. O'Brien, E. Peters

"It has been discovered that copper concentrates can be leached in strong (40-60%) sulfuric acid with nitric acid, or with oxygen if nitric acid is present as a catalyst. Chalcopyrite is rapidly decomposed at temperatures well below the boiling temperature of the lixiviant (-150 C.) and the resulting copper and ferric salts are precipitated as CuS04.H20 and FeH(S04)z.4H20. Other metal sulfides such as zinc, lead, nickel, etc. are also converted to sulfates that are nearly insoluble. Sulfur is partially converted to elemental and partially to sulfuric acid. Reduction products of nitric acid can be recovered from the distillate with good recovery. Conversion of as-received copper concentrates is largely complete in about 1 hour. Introduction9 molar sulfuric acid is an unusual hydrometallurgical lixiviant: it has a boiling point of about 150 C. and a low solubility for base metal sulfates. Below about 6 molar acid, the boiling point falls below 120 C. and yields much higher sulfate salt solubility, while above 12 or 13 molar acid and at higher temperature sulfuric acid becomes an oxidizing agent, yielding gaseous S02' Thus, sulfuric acid within this range of concentration is capable of acting well above the temperature of boiling water without requiring autoclave conditions, and if typical oxidative leaching conditions are applied to suspended mineral sulfide concentrates, it is possible to obtain a conversion of these sulfides into 'crystalline sulfates. Thereafter, the sulfates can be separated by filtration or by solid - bowl centrifuge and the solution can be recirculated to the reactor vessel. Meanwhile, the solid sulfates can be treated in a typical hydrometallurgical circuit, i.e., dissolved in a return stream that is essentially water, separated from each other by, for example, solvent extraction, and recovered as metals by electrowinning."

Jan 1, 1997

By Dachun Liu, Baoqiang Xu, Bin Yang, Yong Deng, Heng Xiong, Xiumin Chen

"In this paper, vacuum distillation technology has been employed to study the possibility and regularity of separating copper and enriching lead, silver and other valuable metals from copper- based multi component alloys. The result of experiment indicated the practicability of vacuum distillation dealing with copper base complex multi-component alloy to separating lead and silver, when the vacuum distillation temperature was 1637K, distillation time was 60min; residual gas pressure was 20-30Pa, the removal rate of silver was 95.86%, of lead was 99.63%; the evaporation rate of copper was 0.745%. The removal rate of arsenic, antimony and tin respectively were 83.09%, 48.12% and 24.54%. Vacuum distillation method is applicable for dealing with the copper-based multi component alloys, silver and lead can realize effective recovery.IntroductionCopper generally go with lead mineral, therefore, to remove copper from lead becomes an inevitable link in lead smelting. Dross from removed copper usually contains lead, arsenic, antimony, tin and noble metal silver. In abroad, soda ash-iron dust is adopted to process copper dross of this kind. The outcomes of this process are lead matte, wet lead, scoria smoke dust etc[1~5] The dominant components of all the outcomes are copper and lead. Moreover, in the process of tin smelting, copper contained by-products are produced, such as, crude tin alloy, tin lead electrolytic anode slime and so on. Copper content of all the products are ranging from few percentages to several tens percentage. Those products, no matter merge into main producing process, or separate treatment cost losses of valuable metal. For one hand, the containing of copper of outcomes from pyrogenic attack is less than 50%, for the other hand, a lot of valuable metal need to be processed, which increase the cost of retrieve."

Jan 1, 2013

By H. Matsuda, T. Iwashita, H. Awata, H. Liwei, D. Hirabayashi, Y. Saito, S. Ozawa, Y. Goto

"The present study is concerned with investigating the effect of chemical treatment on enhancing the HCl absorption capacities of coal burnt ash and slag. It was found that the HCl absorption capacity of coal burnt ash discharged from fluidized bed combustor was improved by hydration with water and 5% polyethylene glycol solution. This phenomenon was based on an increase of the specific surface area of treated coal burnt ash. The HCl absorption capacity of hydrated ash with polyethylene glycol solution was almost equivalent to that of standard CaO and Ca(OH)2. In particular, the specific surface area of hydrated ash with polyethylene glycol solution was found to be 19 m2/g, which was more than over eight times larger than that of raw sample. Hydrated slag treated with lON sodium hydroxide solution also showed high HCl absorption capacity, with highly improved surface area. It was found that the absorption capacity of slag for HCl depended on the treatment time, showing the maximum absorption capacity for 12 hours of hydration treatment.IntroductionA large amount of coal burnt ash, slag and dust are discharged from such industrial processes as coal combustion and metal refinery etc., and it becomes an serious problem to recover and diminish these solid wastes because of the shortage of dump sites and subsequent metal elution to the environment. Figure 1 shows the present situation of reutilization of coal burnt ash and slag in Japan [1,2]. It is shown in this figure that these solid wastes are recycled as materials in the fields of earthwork, agriculture and forestry etc. A part of these solid wastes, however, is still dumped to landfill. To decrease this dumped amount, the development of environmentally friendly reutilization technique for these solid wastes is of great importance."

Jan 1, 2000

By K. Ohmori, K. Takeya, S. Yoshizawa, A. Kawamoto, T. Ishikawa

"High performance Sm2Fe17N3 magnet powder is developed nitriding Sm2Fe17 alloy that 'is made using a reduction and diffusion method. Typical remanence, coercivity and maximum energy product of the fine powder are 1.40 T, 1.13 T and 323 kJ/m3, respectively. Decreasing samarium content, oxygen content and the amount of a-Fe are found to be the important factors to realize high-energy product.High performance injection molded Sm2Fe17N3 anisotropic magnet is also developed using the powder and an original binder system developed in order to mold at low temperature. Typical remanence, coercivity and maximum energy product obtained are 0.77 T, 0.78 T and 103 kJ/m3, respectively in the density of 4.77 Mg/m3The temperature coefficient of remanence is -0.07 %/K and that of coercivity is -0.54.%/K. The initial irreversible flux loss of the magnet that has a permeance of two is -5 % at 100 °C and the irreversible .flux loss of it is -4.4 % exposing it at 80 °C for 1000h.IntroductionSm2Fe17N3 alloy powder is expected to be very useful for a bonded magnet. The reasons are as follows. The magnetization is as large as the Nd2Fe14B alloy. Curie temperature is even higher than the alloy. The uni-axial anisotropy is comparatively higher than the alloy. Consequently it is possible to obtain high coercivity after just milling the powder and therefore possible to obtain high-energy product in a bonded magnet as it is realized in the SmCo5 bonded magnet. On the other hand, sintering is difficult because it will be decomposed into samarium nitride and a-Fe when heating it up to 500°C:"

Jan 1, 2000

By Hiroshi Tabuchi, Akihiko Takahashi

"High strength aluminum matrix composites were prepared and studied using as reinforcement newly developed nearly mono-dispersed a-alumina single crystal particles each of which has a regular polyhedral shape. The composites were formed by centrifugal casting using aluminum casting alloys (Al-Si and Al-Cu-Mg) as the matrices, followed by heat treatment. The volume fraction of the alumina particles was as high as 60%. The same matrix composites reinforced by conventional crushed fused alumina particles were similarly prepared as the reference. The bending strength and tensile strength of the Al-Cu-Mg matrix composites reinforced by the novel alumina particles of 10 µm in average diameter are as high as 1020 MPa and 560 MPa, respectively, which are higher than those of the conventional alumina composites. Furthermore, the bending strength of the novel alumina composites degraded less than that of the conventional alumina composites after thermal fatigue tests. The number of cracks in the matrix seemed to influence the thermal fatigue property because many cracks were observed in the conventional alumina composites, whereas only a few cracks were observed in the novel alumina composites. This was confirmed by SEM observation of the sample composites before and after the thermal fatigue tests.IntroductionAluminum matrix composites strengthened by dispersed reinforcements are of interest for various applications due to their improved properties, such as high specific strength and stiffness, wear resistance, etc .. A large number of investigations have been made concerning fabrication processes and properties of these composites. With regard to the fabrication processes, powder metallurgy has been well-known as a solid phase process, and recently many liquid phase processes such as a compocasting, a squeeze casting, the Lanxide process, and the Osprey process have been studied and developed.(1)"

Jan 1, 1998

By Manoj Kumar, Vinay Kumar, Nikhil Dhawan, Manish Wadhwa

"Electronic waste (e-waste) is a collective name given to discarded electronic devices such as Television, Cellular Phones and Personal Computers. Among the heterogeneous metals present in the e-waste are the base metals: copper, aluminium, nickel, tin, zinc, iron and precious metals: gold, silver, palladium, platinum apart from several hazardous and halogens metals. Hence there is a need to recover these metals from electronic scrap by recycling and then re-use, which can meet large amount of metals demand. Hydrometallurgical processing was employed for the recovery of metals from television printed circuit board (TV PCB). Different lixiviants such as hydrochloric acid, Sulphuric acid, and nitric acid were used to understand the dissolution behavior of copper, iron and lead present in the TV PCB. Effect of increasing concentration of nitric acid was also studied. Selective recovery of tin over 95% in the form of tin oxide was precipitated. The precipitated tin oxide was identified by X-ray diffraction technique. Tin oxide of purity more than 99.9% was obtained.IntroductionThe electrical and electronic industries comprising computers, television, mobiles, etc, which are manufactured utilizing printed circuit, boards, capacitors, resistance, soldering material etc. During production, at the end-of service life and degradation due to the advanced version with latest features generate valuable metallic and non-metallic constituents. European Union Council on waste electrical and electronic equipment (WEEE) has classified these into different categories as listed in Table 1 [Streicher-Porte et al., 2005]. Among these the information technology, telecommunications and consumer equipment constitute electronic waste (e-waste) [EC, 2002]. Almost all e-waste consists of an integrated part of printed circuit boards which is a valuable source of several metals such as copper, tin, lead, aluminium, iron, silver, gold, platinum etc. [Relay et al., 1990]."

Jan 1, 2008

By Hiroaki Nakano, Kenji Hara, Shunsuke Kawano, Takeshi Ohgai, Michiaki Ikeda, Hisaaki Fukushima, Shinji Yamashita, Tetsuya Akiyama, Hisayuki Kaku

"Ni-Fe alloys have an inverse magnetostrictive effect (Villari effect) in which its permeability varies according to the ·applied strain. This alloy film has a potential for application as force sensors such as torque sensors, tension sensors and so on. Electrodeposition is promising as a technique for preparing Ni-Fe alloy film because of its convenience and economy. In this paper, the effects of electrolysis conditions on the magnetic properties of electrodeposited Ni-Fe alloy films were investigated. Hysteresis loops of Ni-Fe alloy films on copper substrates from sulfate bath were measured by a vibrating sample magnetometer (VSM). The films of low coercivity, which were preferred when used as a force sensor were obtained by introducing certain additives to the sulfate type bath.INTRODUCTIONNi-Fe alloys show an inverse magnetostrictive effect (Villari effect) that their permeability varies depending on the applied strain. The films of this alloy have a potential for application as force sensors such as torque sensors, tension sensors and so on. The authors et al. tried to prepare Ni-Fe alloy films using the sputtering technique, and produced a prototype of Ni-Fe alloy torque sensor [I]. The sensitivity was higher in the torque sensor thus produced than the strain gauge type one, and this torque sensor enables non-contacted detection. It showed excellent durability and reliability. However, the formation of Ni-Fe alloys by sputtering requires higher costs and brought an another problem that the shape of the substrate on which the film was formed was considerably limited. This causes a hindrance to the wide-range application of the force sensors. Electrodeposition is promising as the technique for preparing Ni-Fe alloy films because of its convenience and economy. In this paper, the effects of the conditions of electrodeposition on the magnetic properties of Ni-Fe alloy films were studied."

Jan 1, 2000

By JiaPeng Xu, Brian Lo, Uday B. Pal, Yihong Jiang, Soumendra N. Basu

"The Solid-Oxide Oxygen-Ion-Conducting Membrane (SOM) electrolysis process has been successfully tested on a laboratory scale, producing silicon directly from silica in a cost-effective and environmentally friendly way. A yttria-stabilized zirconia (YSZ) tube, closed at one end was employed to separate the molten salt containing dissolved silica from a liquid metal anode placed inside the YSZ tube. When the applied electric potential between the liquid tin cathode in the molten salt and the anode exceeds the dissociation potential of silica, oxygen ions are pumped out of the molten salt through the YSZ membrane and oxidized at the anode while the silicon cations in the flux are reduced to silicon at the liquid tin cathode. The presence of high-purity silicon crystals on the surface of liquid tin cathode was confirmed by scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDS). Silicon crystals were extracted from tin cathode by chemical etching.IntroductionPhotovoltaics (PV) generate electrical power by using solar cells, and dramatically reduce the emissions of greenhouse gases (GHG). Through 2006 to 2011, it grew the fastest of all renewable technologies with operating capacity increasing an average of 58% annually [l]. However, the cost of manufacturing solar-grade silicon (SoG-Si) for high-efficiency solar energy production represents a major barrier to achieving the industrial goal for solar power of $1/Wp (watt at peak exposure) which would enable widespread grid parity. The current contract price of silicon to PV manufacturers is $50-$60/kg, with the spot market in 2007-2008 showing prices as high as $300/kg [2]. This makes the development of low cost and environmentally friendly manufacturing of high purity silicon very important."

Jan 1, 2013

By Srinath Viswanathan, Zhijing Zhang, Ramana G. Reddy

"The viscosity measurements were carried out on melts of 380 aluminum alloy containing 20 volume % SiC particulates under various shear rates at different temperatures using a Brookfield viscometer. Results showed that viscosities of the melts increased with decreasing temperature and decreased with increasing shear rate. These results were compared with those of 356 alloy and it was found that the temperature had a more significant effect on viscosity of 356 alloy than that of 380 alloy containing SiC particulates. Based on the present experimental data an empirical viscosity model, which considers the effects of both solid fractions in the melt and shear rate, is proposed.IntroductionDiscontinuously reinforced metal matrix composites materials (MMCs) such as aluminum alloy containing SiC particulates have considerable potential for applications in the automotive industry because of their superior stiffness, higher specific mechanical properties, better dimensional stability and strength retention at elevated temperatures when compared to their monolithic counterparts. They have a great advantage in the specificity of their properties, meaning that specific materials can be engineered for specific applications. With such freedom of design, materials engineers have to accumulate a very large database of mechanical properties. Among these properties, the viscosity of alloy slurries is very important for producing, casting and forming process of metal matrix composites materials because viscosity has a decisive influence on fluid flow. The understanding of the rheological behavior of alloy slurries is necessary for these materials to become economic reality. Therefore, a study was carried out to measure the viscosities of 380 aluminum alloy containing 20 volume % SiC particulates under various shear rates and temperatures. In addition, a viscosity model representing the primary features of the alloy slurries was developed."

Jan 1, 1999

By K. Kashiwaya, N. Hiroyoshi, H. Furuya, N. Sumiya, M. Tsunekawa, M. Ito

"The number of hybrid vehicles is increasing and this is causeing an increase in waste nickelmetal hydride batteries. The cathode activating agent of batteries is made of nickel hydroxide and the anode activating agent is an alloy of nickel and rare earth elements. Conventional rotary kiln methods cannot recover the rare earth elements, and hydrometallurgical treatment of crushed product consumes large volumes of agent. The physical separation of the anode alloy from the cathode hydroxide would make it possible to reuse the alloy. The authors have reported separation of anode and cathode components in the large size fractions using a newly developed dry magnetic separation method. Wet magnetic separation has been applied to the powder fraction and about 90% anode purity was achieved. This paper reviews experimental results from previous publications and proposes an integrated treatment process for crushed nickel-metal hydride batteries.IntroductionEnvironmentally-conscious clean energy vehicles have attracted much attention in developed countries and particularly hybrid vehicles are increasingly mass-produced as low emission vehicles. Hybrid vehicles have both a gasoline engine and an electric motor to save on gasoline usage and a nickel-metal hydride battery is used to store electric energy. The battery contains Nihydroxide and Co as the cathode activating agent and an alloy of Ni and mischmetal (mM), a rare-earth element mixture consisting of La, Ce, and Nd, as the anode hydrogen adsorption component. In conventional recycling, the Ni and Fe are recovered with a rotary kiln-electric melting process and the Co and mM go to the slag component [1] and hydrometallurgical treatment of crushed product consumes large volumes of agent. Japan Oil, Gas and Metals National Corporation have proposed a low energy and low cost recycling treatment process combining the physical and chemical treatments and the authors are investigating the physical treatment process."

Jan 1, 2008

By Biserka Lucheva, Tzonio Tzonev

"A unique DC electric arc rotary furnace with capacity 150 kg has been designed and constructed for the recycling of low-quality scrap and aluminum dross. The main constructive feature of this furnace is that the axially positioned graphite electrodes (cathode and anode) are placed 100 mm away from the rotation axis of the furnace. A specific characteristic of the construction is the possibility one of the electrodes (the anode) apart from moving axially (parallel to the furnace axis) to move at 90° outside the working space. High recovery rate of metal aluminum from aluminum dross (92%) was realized in this furnace. This is the reason for construction of industrial DC electric arc furnace.IntroductionThe consumption of aluminum waste has been rising continuously on a world scale, which is a great stimulus for the development of the technology for aluminum recycling.To recover the aluminum in dross, the conventional recycling process uses salt rotary furnaces heated with a fuel or a gas burner. This treatment process produces a secondary dross containing alumina, salts, impurities and a small amount of aluminum. Molten aluminum is tapped from the furnace and the residue is then dumped from the furnace. It has been the practice to dispose the residue in a landfill. Improvement of this technology, known as the oxy-fuel process, uses a gas burner enriched with oxygen to increase the thermal efficiency [1]. Recent studies show that the most efficient aggregate for recycling of aluminum scrap has turned out to be the rotary tilting furnaces, heated by plasma or electric arc, for which the use of flux is not necessary [2,3].Accordingly, there is a substantial need in the industry for an improved process for recovering free aluminium. It is particularly desirable that such process be cost effective and ecologically safe."

Jan 1, 2008

By Vojteh Leskov?ek

The tribological load is the load on forging tools resulting from the relative motions between the plastically deformed workpiece and the die. In comparison to many other forming processes hot die forging has an especially disadvantageous tribological system. The advantages of the application of hard coatings, which are well known for cutting tools, are to a much lesser extent explored for casting, extrusion, molding and forging tools. Increasing the lifetime of these tools is an important task in surface engineering because of the complex loading conditions and often complicated tool geometry. The plasma-assisted chemical-vapor-deposition (PACVD) technique is well suited to depositing hard coatings onto large dies and molds. The aim of this study is to present and discus results obtained on a duplex PACVD hard coating in an industrial application like the hot forging of automotive parts. A new generation of vacuum-melted and remelted (VMR) hot-work tool steels has been developed; these can reach a hardness of 58 HRc, and have a fracture toughness at this hardness equivalent to that of standard hot-work tool steels at 45 HRc. This offers one of two advantages: the steels can be used at the higher hardness to provide resistance to wear or deformation, or, when used at a hardness of 47?49 HRc for hot forging, to provide temper resistance, nitriding behavior and adhesive wear resistance. The results presented here are from a preliminary investigation. The experimental results indicate that the introduction of a proper duplex PACVD hard coating will lead to an improved wear resistance and a longer lifetime for the hot-forging dies. Furthermore, by using a hard, low-friction coating excellent anti-sticking properties can be obtained. At this stage of the investigation it is also necessary to carry out pilot trials to determine the wear resistance and the tool life in practice.

Jan 1, 2006

By Wilson Acchar, Fernando Barcelos, Luis Carlos Pereira

"Porous ceramics have been extensively investigated as structural materials for flow of fluids in many applications, such as filters for molten metals, water purification and hot gases, thermal protection systems and heat exchangers. This class of material must have two special features: high permeability and mechanical strength. However, these parameters are influenced in different ways by the processing method and the consequent cellular structure. In this work two different types of commercial ceramic filter materials are investigated. Characterization included the evaluation of the strength values as well as the permeability behavior and microstructural analyzes of the surface fracture. The results indicate that the strength values are strong dependent on the filament defects.IntroductionCeramic materials with a cellular structure have been extensively investigated as structural materials for flow of fluids applications [1-3]. Microstructural aspects such as morphology, size of the cell and the degree of interconnectedness are mainly parameters that influence the properties of these porous materials [4-6]. The most used industrial process to produce cellular ceramics for filter application is the polymeric sponge replication method. This technique consists in dipping the polymer foam into slurry containing an appropriate binder and the necessary ceramic materials, followed by a heating treatment [2,5].Mechanical properties of cellular ceramics depend basically on cell size, degree of interconnectedness and density [1,2,5,8,9]. Materials used as filters required a good strength and also permeability values. These properties are inversely proportional to each other. Higher porosity increases permeability values but decreases the strength values [1,2,5]. The objective of this work is to study the strength resistance of a commercial porous ceramic material (10, 20 and 30 ppi) based on silicon carbide."

Jan 1, 2012

By Jing Zhan, Chuanfu Zhang, Yonglin Yao

"The Ni/Co arbitrary ratios of fibrous precursor were investigated during coordinated coprecipitation by changing the precipitating medium. The results show that the original molar ratio ofNi2+ to Co2+ in reaction solution can be maintained in the coprecipitate at pH'.'05.0 and the coprecipitate is single phase solid solution using water and water-X precipitating medium. But the original Ni/Co ratios are no longer kept and composition of the coprecipitate is not uniform at pH>5.0 in water precipitation medium. In order to obtain the precursors with the required morphology and accuracy Ni/Co ratios, the optimum conditions of fibrous precursors were chosen as follows: ammonia used as complex agent and pH adjustor, water-X solvent as precipiting medium, oxalate as coprecipitated agent, 8.0-8.4 for pH value, 50-70°C of reaction temperature, 0.5-0.8 mol/L of initial nickel and cobalt salt concentrations and excesses of oxalic acid of 10% - 20%.IntroductionNi-Co alloy as an important transition metal alloy with high mechanical strength, good anti-deformation, corrosion resistance, thermal conductivity, thermal stability, electrical conductivity, electrical contact, and special magnetic properties indicates that it can be used as high-temperature catalyst, special magnetic material, high-temperature electrochemical devices, and so on [1-6]. An ideal composite powder should have an appropriate stoichiometric ratio, good uniformity of chemical composition, appropriate phase, low impurity content and small particle size [7]. Similarly, the composition of nickel-cobalt alloy powder has an important impact on its crystal structure, properties and applications. Guo[8] found that magnetisms of CoxNi1-x such as magnetic anisotropy, curie temperature, and the shifts of the spin steering are very sensitive to the composition of alloy powder."

Jan 1, 2013

By Xinghua He, Shujing Zhu

"In this paper, the chemical composition, the content and the leachability of heavy metals in dredged sludge are tested and analyzed. It is shown that the leachability of Pb and Cr exceeds the leaching toxicity standard, and so the dredged sludge is considered as hazardous waste and must be solidified. The effect of solidifying the dredged sludge by the hydraulic ash-slag cementitious composites is studied, and it indicates that the heavy metals can be well immobilized if the mass fraction of the dredged sludge is appropriate. The heavy metals are immobilized within the hydraulic ash-slag cementitious composites hydration products through either physical fixation, substitution, deposition or adsorption mechanisms.IntroductionDredged sludge is classified as a hazardous waste because it usually contains concentrated heavy metals and chlorinated organic compounds, as well as soluble salts, and is also composed of very fine particles. Moreover, inorganic pollutants are typically associated with soluble compounds, which are, therefore, highly leachable from dredged sludge when dredged sludge is contacted by a liquid medium[l1. Thus, dredged sludge must be stabilized in order to reduce its environmental impact on the final disposal site. The frequent means of dredged sludge disposal used include(!) Chemical stabilization (2) acidic extractionChemical stabilization is translating mobile heavy metals into low dissolution and low toxicity form through chemical reaction. The commonly chemical medicaments are sodium hydroxide, soldium sulfide, thiourea, EDTA. But Zhao et al [ZJ found sodium hydroxide is not fit for Pb stabilization, the other three are effective, but the chemical properties of sodium sulfide are not stable, thiourea and EDTA are very expensive, and so it is very difficult to apply them. Moreover, because of the complexity of heavy metal conformation and dredged sludge composition, it is very difficult to find a cheap and prevalent stabilization medicament in point[31 ."

Jan 1, 2013

By D. Kennis

"Union Miniere Precious Metal's (UMPM's) Hoboken Business Unit has a long tradition in complex Pb-Cu metallurgy, focussing on the recovery of precious metals from various types of secondary and recyclable materials. Although the old flow sheet, based on a traditional sinter plant, blast furnace, and lead refinery process was a very complete flow-sheet with the capability of dealing with almost every impurity, the weaknesses became clear:1. old and costly technology,2. too many unit operations,3. too much internal recycling, and4. dependency on concentrates for the sintering process.To maintain the competitiveness of the Hoboken Business Unit, the project ""Smelter 2000"" was born. This project represents a breakthrough in metallurgical processes and technology. A modem smelting technology was chosen together with the development of a new process. A lead-copper process combining lead slag and blister copper production, carried out in an ISASMEL T vessel, was the key to simplifying the Hoboken flowsheet. ISASMEL T smelting technology was chosen for its flexibility towards feed characteristics and process parameters.The new smelter was commissioned at the end of 1997. Although there were a lot of problems due to the high degree of technical innovations in the process, the new smelter came to design capacity within 1 year after start-up. During this period, however, UMPM had, a very difficult time because of the extreme clear-cut nature of going from the old to the new flowsheet.After two and a half years of operation, the new flowsheet has proven to fit with the strategy of UMPM, focussing on treating secondary Pb-Cu materials and a broad range of recyclable feeds such as electronic scrap (E-scrap) and catalysts. Together with the new Precious Metals Plant, efficient logistics, recognised world class sampling practices and a customer-focussed commercial organisation, UMPM Hoboken can definitely be considered reborn."

Jan 1, 2000

By Katsunori Okaya, Gjergj Dodbiba, Hiroyuki Ono, Toyohisa Fujita, Seiji Matsuo

"In an attempt to raise the copper grade of Printed Circuit board (PCB) by removing other components, carbonization treatment was investigated. The crushed PCB without surface-mounted parts was carbonized under nitrogen atmosphere. After screening, the char was classified by size into oversized pieces, undersized pieces and powder. The copper foil and glass fiber pieces were liberated and collected in undersized fraction. The liberation of copper foil from the oversized pieces was also investigated. The copper foil was liberated easily from glass fiber by stamping treatment. Liberation rate of copper foil was high at high carbonized temperature. The experimental results indicated that 90% of oversized char was liberated and the copper foil recovery from PCB carbonized at 1073K was 110kg/t. The copper recovery from char powder by flotation was also investigated. 15% of the copper grade and 80 % of the copper recovery were obtained, whereas the removal rate of silicon was 55%.IntroductionWaste Electrical and Electronic Equipments (WEEEs) should be recycled because they have many kinds of valuable materials and most WEEEs include Printed Circuit Boards (PCBs). In Japan, about 30 km2 per year of Printed Circuit board (PCB) has been produced [1], PCBs are normally separated from WEEEs and picked up by hand and sold to non-ferrous metal market because PCBs include high grade of copper and other precious metal such as gold, silver and palladium [2]. However, PCB also has impurities such as silicon, aluminum and calcium which are slag materials in non-ferrous smelting process, and other harmful elements such as lead, bromine and antimony. Low grade PCBs are sold after removal of invaluable parts or sometimes land filled without any treatment"

Jan 1, 2011

By Marko Suput

Titanium is a high-strength, low-density metal nearly immune to corrosion, but limited in use by its high price. The high price is due to the cost of smelting and processing the ore. The research on titanium production using the Solid Oxide Membrane (SOM) process aims to consolidate most of the processing steps required for conventional titanium production into a single step making it an energy-efficient and cost-effective method for producing CP billet and ingot and possibly also powders used to make titanium alloys. In the SOM process experiment, a steel crucible contains MgF2-CaF2-TiO2 flux; an inert metal/carbon rod serves as the cathode; an oxygen-ion-conducting yttrium-stabilized-zirconia (YSZ) membrane in the form of a one-end-closed tube contains either a liquid metal that acts as the anode or liquid MgF2-CaF2 ionic flux that connects the YSZ membrane to an anode. During electrolysis, when the voltage between anode and cathode is higher than the reduction potential of titanium oxide, titanium ions are reduced at the cathode and the oxygen ions pass through the YSZ membrane and are oxidized at the anode. The oxygen ions are oxidized at the anode by a reducing agent, hydrogen gas or carbon, forming steam or CO(g), respectively. To date, a suitable MgF2-CaF2-TiO2 flux has been selected and the operating temperature for the SOM process has been determined. Several electrolysis experiments have been performed. As expected, lower valence deposits of titanium oxides have been witnessed at the cathode prior to depositing pure titanium. Continuing work will aim to extend the electrolysis time in order to pass enough charge to produce a significant amount (100 g) of titanium at the cathode.

Jan 1, 2006

By Amanda C. Lima, Luiz Augusto H. Terrones, Sergio N. Monteiro

"Fabric from weaved yarns made of jute fibers have been considered as reinforcement for polymeric composites. In particular, these fabrics obtained from discarded sackcloth are presently being investigated as environmentally friendly composites with recycled polyethylene matrix. The objective of the present work was to compare the practical properties and economical aspects of these composites with those of conventional materials such as wooden board and gypsum panels for building application. The comparison showed that, depending on the amount of post-used jute fabric, a cost/benefit analysis favors these composites over the conventional materials.IntroductionThe increasing amount of wastes generated by human activities is becoming a worldwide problem of pollution with growing consequences to the environment. The question on how to dispose these wastes is, therefore, a major global issue. Among the possibilities of it gating the problem, the use of materials with characteristics of being renewable, biodegradable and recyclable is considered an environmentally correct solution. Examples of this type of materials are left over lignocellulosic fiber from coconut husks and sugarcane bagasse [1] that, after the primary extraction of edible pulp and juices, can be recover for industrial application. Nowadays, the main use of these fibers is to reinforce polymeric composites applied as components for building construction and automobile parts [2,3]. In addition to these applications, composites reinforced with residual lignocellulosic fibers may replace conventional furniture and panels made of wood and thus help to reduce deforestation [4].Environmental protection is not the only motivation for recycling natural fiber wastes. In developing regions activities associate with collecting and processing residual fibers provide job opportunities for low-income people. Moreover, if the lignocellulosic fiber is collected as a recyclable waste, it hes the economic advantage of a comparatively cost, which constitutes in a relevant difference as a choice for commercial utilization."

Jan 1, 2008

By Markus A. Reuter, Antoinette van Schaik

"Product design engineers select from a wide range of materials and combine them into multimaterial product designs. These include various materials (metals and non-metals) which are complexly integrated (e.g. welded, glued, alloyed, layered). The recycling/recovery rate of consumer products are determined by the different materials and alloys used, but also by the particle size and multi-material particle composition after shredding (combination of materials due to design). Eco-design (for recycling) and Design for Recycling (DfR) can only be conducted if the interconnectivity of material/metal in various unliberated materials is accounted for and its effect on material and energy recovery can be linked back to design. This paper will discuss the basic principles of these DfR models and it is shown how these tools (i) are linked Computer Aided Design (CAD) and Life Cycle Assessment (LCA) software, (ii) affect conceptual design specifications of products, (iii) integrate the complex detail of the recycling system and recyclate quality and hence (iv) make recycling an integrated part of the product system. Furthermore, it is shown how these assessment tools and models can be applied for benchmarking of the recyclability and environmental damage created by the recycling of end-oflife consumer goods in order to e.g. (i) provide the (original) equipment manufacturer with knowledge and solutions to support product stewardship and Extended Producer Responsibility; (ii) create awareness of the consequences/benefits of design, products and recycling systems to manufacturer, designer, legislator, recycler etc.; and (iii) assist the consumer in their choice of consumer goods from an end-of-life point of view.IntroductionA first-principles basis is required in order to be able to simulate and predict the recycling/recovery behaviour of products facilitating Design for Recycling (DfR) and Eco- Design. This links recycling technology and the environmental consequences of recycling directly to product design."

Jan 1, 2008