By Luis M. Chia

The direct dissolution of zinc in an organic solution of di-(2-ethylhexyl) phosphoric acid (D2EHPA) and kerosene was studied. The objective was to gain a better understanding of the fundamentals involved in the anodic step of the galvanic stripping process. Results showed that metallic zinc does dissolve spontaneously at ambient temperature by an electrochemical mechanism and the presence of additional oxygen activated the process. When oxygen was removed by prior nitrogen sparging, dissolution did not occur indicating a depolarizing cathodic reaction is necessary. The concentration of water in the organic also affected the rate of dissolution. A factorially designed experiment was made using four variables at two levels selected by evaluating results from previous screening tests. D2EHPA concentration, surface area and agitation were all found to be significant for the values chosen. Temperature was less significant and it was found that zinc dissolution is probably a diffusion or mixed controlled process, as indicated by the calculated activation energy of 6 kcal/mole.

Jan 1, 1995

By D. N. Wilson

The potential risks of working with lead have been recognised for centuries, but it is only with the development of sensitive measuring techniques in relatively recent years that it has been possible to establish effective approaches for the monitoring and control of lead exposure. This paper examines the principal control measures employed today - lead in air and lead in blood - and reviews the evolution of numerical standards, with particular reference to the latest understanding of health effects. In addition to lead, a large number of other metals are commonly encountered when producing lead and zinc - both primary and secondary - and the health effects of many of these are discussed. Modern hygiene practices and technologies, which have proved successful in reducing worker exposures, are reviewed. The paper concludes with a look at how exposure standards are likely to change in the near to medium future

Jan 1, 2000

By Ki Joo Sim, Sung Beom An, Joonho Lee, Minsoo Shin

Valorization of the electrical arc furnace oxidizing slag by coke was carried out by the reduction of iron oxide in the slag. Since the reduction of iron oxide by solid carbon is an endothermic reaction, supply of heat energy is required. In addition, slag has a low thermal conductivity; traditional fuel injection is not suitable for this reaction. Microwave can be used to supply heat energy to the system. Commercial oxidizing slag was reduced by coke under the microwave irradiation (1.7 kW, 2.45 GHz). The maximum recovery ratio of iron was 87%. In addition, slag composition modification was attempted to use the remaining slag for a mixture in cement clinker. Free-CaO in the slag was successfully suppressed, and the use of the remaining slag as a potential mixture was confirmed.

Jan 1, 2014

By Yuan Lu, Yiming Rong, Richard D. Sisson Jr

With the development of quench technology, there is a trend of using gas quench to replace liquid quench for less distortion and residual stress. The fundamental difference between the liquid and gas quench is the heat transfer coefficient, not only the values but also the shape of the curve as a function of temperature. The equivalent heat transfer coefficient for the liquid and gas quench is analyzed by simulations and experiments. Even it may result in the same hardness in the liquid and gas quench, the steel microstructure may be different because of the different cooling processes, and therefore other steel properties, such as toughness, may be different. The cooling process, microstructures and properties such as hardness and toughness should be examined when designing the liquid or gas quench processes.

Jan 1, 2015

By T. Shimizu

In Japan, the emission standard of selenium in effluent was set at a maximum of20 mgll in Feb. '94 for the first time, and it is scheduled to be further decreased to a maximum of 0.1 mg/I from Feb. '97 due to tightening of the Water Pollution Prevention Act. Selenium (IV) and (VI) are generally found in effluent from precious metals refineries. Although selenium (IV) can be easily eliminated by some reducing agents, selenium (VI) is more difficult to be reduced. Therefore, many smelters are having difficulty in complying with the new emission standard. At Mitsubishi Materials' Naoshima smelter, the behavior and the elimination of selenium in effluent have been extensively investigated. As a result, it was found that two strategies were particularly effective. One of them is improving the overall operation of precious metals refinery, that is, feeding uniformly the effluent to the waste-water treatment plant, reducing the effluent volume by recycling and recovering more selenium (IV) in the effluent. The other is eliminating selenium (VI) in the effluent from the precious metals refinery. It was found that selenium (VI) can be effectively reduced by using hydrazine under high? sulphuric acid concentration and high temperature conditions. By using these measures, it is considered that Naoshima Smelter will be able to comply with the new emission standard.

Jan 1, 1996

By Merete Tangstad, Fei Li

This paper studies the quartz and carbon black pellets at elevated temperature with varying temperature and gas atmosphere. High-purity quartz and commercial ultra-pure carbon black was mixed (carbon content wt.15%), and then pelletized into particles of 1-3mm in diameter. The stoichiometric analysis of the pellet during heating is studied in thermogravimetric analysis (TGA) furnace at different temperature in CO and Ar atmosphere. The microstructure, phase changes and element content of sample before/after heating is characterized by X-ray diffraction, scanning electron microscope, X-ray fluorescence and LECO analyzer. The reaction process can be divided into two stages. Higher temperature and argon atmosphere are the positive parameters for SiC formation.

Jan 1, 2016

By Wei-ling Wang, Ryosuke O. Suzuki, Xiang-ning Meng, Miao-yong Zhu

"A finite-element thermal-stress model of continuous casting mold is conducted to predict deformation of copper plates and its change with different cooling structure. The results show that deformation behavior of copper plates is mainly governed by cooling structure and thermal- mechanical conditions, deformation amount is related to structure geometry, and a small deformation mutation occurs in cooper-nickel boundary due to different properties. The maximum deformation of hot surface centricities of wide face locate at 100 mm below meniscus and that of narrow face locate at meniscus and terminal of water slots and significant curvature fluctuations on both sides of copper-nickel boundary. The maximum deformation of centricities is increased up to 0.05 mm with thickness increment 5 mm of copper plates, and maximum deformations are only depressed 0.01 mm and 0.02 mm with increments of 1 mm nickel layer thickness and 2 mm water slot depth respectively.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipate in primary cooling zone and make continuous casting mold under enormous heating load giving rise to thermal stress, deformation, high-temperature fatigue and creep not only depress mold life-span, but reduce casting stability [1] Many studies focused more on heat transfer, solidification and shrinkage of solidifying shell to provide inverse proposals for optimizing cooling system and even designing new taper of mold [2,3], but it is generally useless to those of having been manufactured or being put into production. Therefore, mold-related forward problems show necessity to be discussed deeply, and stress and deformation distributions based on special thermal conditions in mold should be analyzed in order to explore suitable cooling structure of mold directly. Samarasekera et al. [4] examined heat flow and distortion of two-dimensional longitudinal sections and investigated effect of cooling water velocity, copper plates thickness and carbon content on formation of rhomboidity and longitudinal comer cracks. O'Connor et al. [5] developed a three-dimensional mathematical model to compute thermo-mechanical state in thin-slab mold and calculated temperature and deformation of mold wall to assess roles of various process parameters on impacting mold life. Thomas et al. [6] predicted temperature, distortion and residual stress in mold and indicated increased distortion requires increased remachining, which reduces mold life and increased residual stress increases the probability of a catastrophic crack failure. Park et al. [7l determined heat-flux profiles in funnel-shaped and parallel thin-slab molds based on an inverse heat conduction model and thermocouple temperature measured in-plant and put them into three- dimensional finite-element thermal-stress model to predict temperature, distortion and residual stress of mold wall. Korie et al. [SJ focused on prediction of temperature, distortion and residual stress in mold and in particular to clarify that mold life is significantly affected by temperature and its rigidity, but little effect by mechanical including clamping force, bolt prestress, friction and ferrostatic pressure. Meng et al. [9l predicted temperature and thermal stress in a slab mold and analyzed effect by cooling system geometry and casting speed quantitatively. In present study, a three-dimensional finite-element thermo-mechanical model with type-switched element is transformed from previous heat-transfer finite-element model [9l, and mold deformation is simulated in order to shed light on thermo-mechanical behavior with special thermal conditions and different mold geometry at high casting speed."

Jan 1, 2013

By Douglas J. Harvey, Chi-Mou Ni

"This paper presents an analysis technique for the solidification of metal castings. This method, based on a modified finite difference scheme with an irregular mesh, is capable of dealing with the complex geometries of castings. The nonlinearities in material properties of specific heat and thermal conductivity, arising from the phase change during solidification, are accounted for in the step-by-step calculations. Two solidification problems are solved with this analysis technique and the calculated results compare satisfactorily with experimental data. IntroductionCasting process design engineers are often faced with the difficult problem of designing castings to be produced porosity-free. Since the solidification of metal is affected by many interacting variables such as the thermal conductivity, density, and specific heat of both the molten metal and the mold, it is easily seen why this is a difficult task.Typically, casting tooling design is an intuitive process which builds on past successful methods. After processing equipment is constructed, trial castings are made and examined for dimensions and integrity. Changes in the tooling are generally required to improve casting soundness or to reduce cycle time. In the permanent mold process, tooling is complex and difficult to alter after initial construction. The water-cooled steel molds are part of the complete automated system. Associated holding furnaces, pouring ladles, casting conveyers, and utility connections all make other than minor adjustments a costly and time consuming task. An analytical method for using the principles of heat transfer for predicting solidification patterns would be of great value in the permanent mold process by minimizing costly changes."

Jan 1, 1986

By David G. Dixon

A general, unsteady-state model for leaching of one or more solid reactant species from a non- reactive, porous, spherical pellet is derived in dimensionless form for the interpretation of leaching data, and for use in the design of coarse-ore leaching processes. The effects of diffusion rate, chemical reaction rate, variable reaction order, and competition between multiple solid reactants are examined using the concept of the effectiveness factor. It is shown that the model is capable of simulating both "reaction-zone" and "heterogeneous" kinetics, depending on the choice of three dimensionless parameters. Results of batch leaching tests of artificial ore pellets are presented, and their relationship to the model is discussed.

Jan 1, 1993

By Bruno Lebon, Koulis Pericleous, Georgi Djambazov, Mayur Patel

"High speed compressible jets are used in a number of steel-making applications. In the case of the BOF, a compressible oxygen jet reacts with a carbon-rich iron bath to reduce carbon levels and produce steel. The intensity of the process is governed by the speed of the jet and by the size and shape of the depression created in the metal and slag by the force of the jet, i.e. by the corresponding free surface. This is a difficult CFD problem, since there are compressible and incompressible regions in the flow domain, which need to be handled differently in a finite-volume (FV) pressure-correction scheme. Also, standard turbulence models do not account for compressibility, or the large difference in density between the cold oxygen jet and the hot reacting surroundings. Corrections are introduced to the k-E model to remedy this deficiency and the results are validated against experimental data. The compressible/incompressible boundary is handled through a transition region, based on Mach number.IntroductionThe deformation of a free surface by a compressible high speed jet is of paramount engineering interest, particularly for understanding the physical processes within a Basic Oxygen Furnace (BOF). In a BOF, a supersonic oxygen jet impinges on a molten iron surface, thereby creating a cavity. Oxygen penetrates the bath and removes carbon, resulting in low carbon steel [1].The challenges in modelling such a process lie in coupling a solution domain with distinct compressible and incompressible regions and in dealing with large density differences between the modelled gas and liquid. The modelling of compressibility within the jet is crucial, since the correct velocity profile in the jet is required to determine the cavity depth with accuracy."

Jan 1, 2012

By Luis W. Pommier

Large quantities of sea sludge containing halogenated organic compounds, such as PCB, oils and metals like arsenic and lead have accumulated throughout the years at the bottom of sea channels and harbors and are obstructing navigation and creating environmental problems which need to be resolved. A sludge from a California port would be dredged by suction pumps, it would be processed in a plant which would be built either on firm soil or on floating platforms. The sludge shows contents of up to 1 ppm of PCB, 15 % oil and 10 ppm of arsenic, which generates a very fetid odor. Bench scale work indicates that most of the contamination concentrates on the solid phase, in fact, only minor amounts of oil report to the sea water and can be readily removed by physical means. After separation of the sea water from the solids of the sludge by decantation, it is possible to solubilize the PCB, the oil and the metals into an organic solvent leaving a non-hazardous soil for disposal near the harbor. The PCB is dehalogenated during the solubilization process leaving a liquor solution containing the oil and metals. The oil is extracted leaving an aqueous solution containing the arsenic. Further process extracts the arsenic from this solution rendering the liquid non-hazardous. Transportation and disposal of the sludge is impractical. There are hundreds of thousands of tons of hazardous soils accumulated in each harbor, which would fill the hazardous waste disposal sites available and it would be, prohibitively expensive to do so. It is not possible to compare the costs of decontamination with a competitive method. If it were, the proposed process would be less expensive than transportation and disposal and it has the advantage of removing the liabilities from the Responsible party. After a full scale continuous pilot project is run to decontaminate a small, 500 cubic yards accumulation of this type of sludge in a California harbor, a full scale environmental project would be initiated. The decontamination of one million tons of sludge would be completed in five years.

Jan 1, 1995

By V. M. Paretsky

The basic work conducted by Prof. A.Yazawa has demonstrated that in order to ensure single- stage white metal production by autogenous smelting of copper sulfide raw materials, it is most favorable to use highly basic slags, in particular oxide systems CaO-FeO-Fe2O3-SiO2. The special studies have been conducted in the Gintsvetrnet Institute to investigate the composition and structure of slags produced on a semi-commercial scale when testing the KFP and FBP processes for white metal smelting. as well as the slag obtained in a full-scale KFP furnace at the Almalyk copper smelter. The investigations conducted have demonstrated why production of high-grade matte or white metal is associated with lower loss of copper in slag in a series: silicate slag I silicate-calcium slag I ferrite-calcium slag.

Jan 1, 2003

By Asmo Vartiainen

Background of Direct-to-Blister Flash Smelting is discussed; especially slag chemistry relating to copper solubility, slag fluidity and impurity behavior. In December, 2000, Mini-pilot Flash Smelting test runs were carried out at Outokumpu Research Oy to produce blister copper from Chilean concentrate and white metal and from a mixture of them. Tested slag types were iron silicate slag, ferrous calcium silicate slag and calcium ferrite slag with different slag compositions and different concentrate/white metal ratios. The test runs were successful. The fluxing effect of copper oxide was clearly demonstrated and ferrous calcium silicate slags remained fluid on a very wide liquidus range. The distribution of arsenic between ferrous calcium silicate slag and blister copper is much higher than between iron silicate slag and blister copper. This successful test run with the new slag type offer new possibilities in Direct-to-Blister process design.

Jan 1, 2003

A series of electron beam, cold hearth, single melt Ti-6Al-4V plates (nominally 2.5 cm thick) impacted by 2cm diameter, 4340 steel projectiles (with 54g nominal mass) at velocities ranging from 0.633 to 1.027 km/s were sectioned along the impact axis and examined by optical metallography to characterize the formation, growth, and microstructure of adiabatic shear bands. Near ballistic limit velocities, the shear bands propagate towards the rear of the target where they coalesce and grow to provide a cylindrical solid state flow regime for the plug volume.

Jan 1, 2006

By M. Fafard, R. Ahmed, O. Dion-Martin

"The optimization of aluminum sheet and tube forming needs the use of large strain finite elements software. The precision of the predicted results from those simulations depends mainly on the quality of constitutive law of the material used. In order to improve quality of these simulations, Barlat has suggested a new yield function named YLD2000-2d. This criterion describes the anisotropic behavior of the rolled aluminum plates. This work consists of characterizing the AA5754 alloy and estimating the material parameters needed for the YLD2000-2d criterion in LS-DYNA. In order to get these parameters, various mechanical testing were performed such as bulge and tensile tests. Moreover, the bulge test was also used to obtain an estimation of work hardening curve in large strain condition, up to 50%. The objective of this paper is to share the experimental results of the characterization of AA5754 aluminum alloy.IntroductionResearchers from National Research Council Canada's Aluminium Technology Center (NRCATC) and Aluminium Research Centre - REGAL, are working on aluminium tube hydroforming processes of AA-5754-0 alloy, used in automotive industries. Hydroforming process presents several difficulties such as wall thinning and section changes. In order to control them, some parameters can be set during the process like pressure rate and end feed level [1]. Given the complexity of the parts and the variability of the control parameters, the use of finite element method (FEA), like LS-DYNA, based on large strain theory is thus necessary. The accuracy of predicted results depends mainly on the quality of the constitutive law used to model the behavior of material. FEA results seem to be valid with the von Mises yield criterion used in some cases. But, given the anisotropic properties of the AA-5754 alloy, a more appropriate criterion could be used. The *MAT_ BARLAT YLD2000 shell material criterion, developed by Barlat [2], who's taking into account the anisotropic behaviour, was chosen due to its large flexibility and its good adaptation to particular elastoplastic behavior of aluminum. However, the use of this criterion needs to determine some material parameters by experimental way."

Jan 1, 2013

By Bora Derin

This study is a collection of both newly published and/or presented works on impurity capacity predictions in molten melts which were carried out by Derinetal. Some sulfide capacity prediction results of iron oxide containing ternary silicate melts and industrial lead and copper slags using the Reddy-Blander model and some impurity capacity predictions of multicomponent oxide and salt melts obtained using a Artificial Neural Network Approach are discussed.

Mar 1, 2017

By A. Siegmund, R. D. Prengaman

Lead anodes used in zinc electrowinning generally contain 0.5 - 1.0 % silver to reduce the rate of corrosion over the service life. For good quality zinc, the cathodes must contain less than 10 ppm lead. In order to reduce the lead contamination of the cathode, the lead anode must become coated with a protective layer of Pb02/Mn02. The formation of this layer may take as long as 30 - 60 days, during which time zinc production is substantially reduced and the cathodes are contaminated with lead. To improve the mechanical properties of Pb-Ag-anodes alloying elements such as calcium, strontium, barium and others are added. The production of cast lead-silver or lead-silver-calcium anodes often results in the formation of numerous holes, voids or laps in the anode surface that can initiate localized internal corrosion. Based on the experience as the major supplier of rolled anodes for copper electrowinning, RSR Technologies has developed an improved anode for zinc electrowinning. The anode consists of a rolled Pb- Ag-Ca-alloy with a controlled surface grain structure. It forms an adherent protective oxide coating within 2 - 3 days when placed in an electrowinning cell. The preferred calcium and silver contents of the alloy are 0.03 - 0.08 % and 0.3 - 0.4%, respectively. Rolling sheets significantly reduces the presence of internal porosity or laps. The lack of defects results in long anode life. The rolling also produces a uniform grain structure to which the corrosion product readily adheres, thus significantly reducing the conditioning period.

Jan 1, 2000

By P. K. Jha, M. M. Mahapatra, H. K. Mohanty, Pradeep Kumar

"During friction stir welding, the tool geometries affect the weld together with the process parameters like welding speed, vertical pressure and tool rotational speed. The present investigation deals with the three dimensional computational fluid dynamics modeling of friction stir welding process considering material flow around the tool, welding speed with respect to tool geometries. Friction stir welding tools with different tool geometries were used for the experiments to achieve acceptable aluminum welds. The temperatures near the welds for each tool were experimentally observed. A 3-D computational fluid dynamics (CFD) model was developed. Temperature-dependent material properties of the aluminum alloy were used in the CFD model. Thermal analysis was carried out considering rotational speed, vertical pressure and traverse speed for the tool geometries. The numerically predicted stirring patterns and temperature profiles closely matched with the experimental ones. IntroductionThe friction stir welding (FSW) is a solid state welding process where generally the metallic materials are joined by the combined action of frictional heating and weld zone stirring by a rotating tool [1]. The heat generated in the process is much below the requirement of melting the plates; hence the FSW process is devoid of harmful effects those are observed during arc welding. The FSW process utilizes a tool which has a shoulder and a protruding pin known as the probe. The shoulder is responsible for frictional heating while the pin probe facilitates stirring of the joint material. A schematic of FSW process is shown in Fig. 1."

Jan 1, 2012

By Yongxiang Yang

High temperature processing of raw materials in metals production and recycling often involves complex multi-phase fluid flow and heterogeneous chemical reactions at various scales. Good understanding of the process physics and chemistry is crucial for process operation and process development. The traditional scale-up process through laboratory scale ? pilot scale ? commercial scale route has been more and more complemented and partially replaced by full-scale process simulation. Computational fluid dynamics (CFD) has become a very useful simulation tool in process research and development. At the same time industrial applications challenge the CFD development with its complex transport phenomena, often in large-scale reactors with small-scale physics and chemistry. The current paper discusses the applications of CFD to a number of high temperature metallurgical and materials processing applications. The research was carried out by using commercial CFD codes as the framework, and the emphasis was given to the special efforts for the development and implementations of sub-models with process-dependent physical and chemical characteristics. To illustrate the application of CFD simulation to high temperature metallurgical processes and coupling of sub-models to the general-purpose CFD codes, five examples are given: (1) melting of aluminium scrap in a rotary furnace for recycling, (2) molten hot metal flow in a heterogeneous coke-bed of a blast furnace hearth, (3) gas flow heat and mass transfer in a submerge electric arc furnace for phosphorus production, (4) high temperature incineration of hazardous waste in a rotary kiln, and (5) transient heating of metals in heat treatment furnaces.

Jan 1, 2006

By Garth James

Bacterial consortia capable of degrading cyanide and metal-cyanide complexes were obtained from gold mine process waters using enrichment cultures. The cultures contained either cyanide, tetracyanonickelate, or ferrocyanide as a sole nitrogen source. Several bacteria were isolated from the consortia, but none of these organisms were capable of degrading cyanide or cyanide-metal complexes at rates equivalent to those of the intact consortia. The consortium from the cyanide enrichment was capable of completely degrading cyanide from an initial concentration of over 100 ppm in less than one day, when cultured using a fed-batch method. Tetracyanonickelate and ferrocyanide were degraded more slowly. Overall, these results demonstrate that bacteria capable of degrading cyanide and cyanide-metal complexes can be isolated from mine process solutions and are capable of significantly reducing cyanide concentrations under appropriate conditions.

Jan 1, 1998