By Jean-Christophe Gebelin, Mark Jolly, Samantha Jones

"The de-waxing process in investment casting is truly a black art which is carried out in a black hole - the autoclave. The process involves exposing wax, coated by a porous ceramic shell, to steam at a pressure of 10 bar and a temperature of about 180°C. The processes which then occur are truly multi-media and multi-physics. Steam condenses in the porous ceramic, wax melts and flows, the shells expand and sometimes crack. Why the shells crack is one of the most difficult questions asked in the industry.Modelling and validating the de-waxing process is not simple. The IRC at the University of Birmingham is attempting to model this process using Physica+ a code developed in the UK. This paper will present the latest results in this attempt to model one of the casting industries most intractable problems.IntroductionThe de-waxing process using an autoclave involves the following physical phenomena:· Flow of the steam in the autoclave;· Heat transfer from the steam to the wax, possibly through the shell;· Melting and flow of the wax.At the same time, other phenomena may occur, such as the flow of the steam through the shell, the condensation of the steam on the shell surface and on the wax pattern surface, the flow of wax the through the shell, etc ...This shows how complex the de-waxing process is from a physical point of view. The main defect that appears during this process is the cracking of the shell. Previous modelling work carried out by Snow [1] has shown that it is possible to predict the stress in the shell, making numerous assumptions. In this paper, the modelling to predict the state of stress in the shell that is currently in development at the University of Birmingham is presented together with the presentation ofthe physical phenomena to model and the assumptions used. The parameters that are needed in such models will also be discussed, and some experimental work undertaken at the moment presented."

Jan 1, 2001

By M. A. H. Shuva, M. A. Rhamdhani, G. A. Brooks, S. H. Masood, M. A. Reuter

Ferrous-calcium-silicate (FCS) based slag has been used in the copper industry over the last two decades. The FCS slag has also been used in a secondary copper processing such as in black copper smelting which has different operation conditions compared to that of typical primary copper processing. In the process, a variety of copper bearing scraps from sources such as industrial waste, consumer waste and electronic waste (e-waste) are used. The valuable metals in these sec- ondary resources are distributed in different phases during the process. Understanding the behaviour of the valuable elements at the relevant conditions is vital for optimizing the process and to maximize the recovery of the elements. In this study, we investigated the structure of Ge-containing FCS-based slag at different conditions (oxygen partial pressure and temperature) using Fourier-Transform Infrared (FTIR) spectroscopy to explore the effect of the polymerization on the behaviour of the valuable element Ge in the slag. It was found that experimental parameters significantly in fluence the slag structure, and therefore, the partitioning of Ge in the slag. A correlation between the distribution ratio of Ge and the slag structure has developed in the current study.

Mar 1, 2018

By D. Nozadze

A new method of isothermal electro-contact diffusion welding of layered composites under pressure is offered. The scheme is developed and laboratory installation is created on which preproduction models of the layered composite of steel and aluminum is produced. A new method of electro-contact hot deformation is proposed for realization of diffusion welding by pressure of stratified blanks providing high-temperature isothermal process. In this case a rolling process or composite pressing is meshed with simultaneous electric current transmission in deformation center. Considering that a resistance of transient layer far exceeds the resistances of composite components, the heat release takes place intensively just in this layer. As the surfaces are approached over a distance of inter-atomic forces, the energy of boundary atoms easily reaches the energy threshold of capture with a formation of qualitatively new metallic bond. Proposed method, providing isothermal process in deformation center, excludes a necessity of previous preparation and prevention of surfaces. In this case strength of layer connection may approximate or exceed strength limit of cladding layer.

Jan 1, 2006

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By G. E. S. Lima, I. K. R. Andrade, N. G. Viana, R. O. G. Martins, L. M. Sathler, L. G. Pedroti, C. M. M. E. Torres, W. E. H. Fernandes, C. M. Silva, M. A. Caetano

In Brazil, kraft pulp mills are rapidly expanding and industrial waste generation is increasing. Technical feasibility of using solid wastes from kraft pulp mills as raw material in other industries may be an interesting approach to manage environmental and economic aspects of the industry. This paper proposes the incorporation, in different proportions (0, 2.5, 5 and 7.5%), of alkaline solid wastes from pulp mills, namely dregs and grits, to clinker in the Portland cement industry. The research was carried out in two steps: (i) characterization of dregs, grits and clinker; (ii) laboratory testing (determination of soundness by the Le Chatelier method, determination of setting times, determination of water content of the paste with normal consistency, determination of compressive strength and static modulus of elasticity). The results showed that the addition of dregs and grits to the clinker up to 2.5% were feasible according to the Portland cement Brazilian standards.

Mar 1, 2017

By Jr. Loper, M. H. Kim, H. H. Jo, C. S. Kang, T. S. Song

"An investigation has been conducted to describe the effect of grain refiner (e.g.,Ti) or modifier (e.g., Sr) on the microstructure of an Al-11.3wt%Si alloy produced by the Ohno horizontal continuous casting process using a heated mold so as to obtain directional solidification at high cooling rate of 300 to 2000°C/s. Experimental results demonstrated that the directionality of the primary a grain was promoted by the addition of0.2 to 0.4%Ti or by the addition of0.02%Sr, whereas the addition of0.6%Ti suppressed this directionality. Feathery a grains were promoted by the addition of 0.2%Ti, while these feathery a grains were suppressed when over 0.4%Ti (grain refinement) or when 0.02%Sr was added. The addition of Ti also resulted in increased coarsening of the eutectic Si in these Al-1 l.3wt%Si alloys.IntroductionThe mechanical properties of conventionally cast Al-Si alloys can be enhanced through judicious control of the casting parameters, by the addition of grain refiners (e.g., Ti) and by the addition of eutectic modifiers (e.g., Sr).[1-3] The Ohno continuous casting process[4-5] uses a heated mold (maintained at a temperature above the alloy liquidus temperature) to produce a casting with a mirror surface free of shrinkage defects. The process is especially suitable for the production of high quality and non-deformable rods of small diameter. This study was conducted at investigate the effects of Ti and Sr on the microstructure of Al-1 l .3wt%Si rods cast by the 01).no process."

Jan 1, 1998

By Shoukun Wei, Cong Wang, Lin Cheng, Zhiyu Qiao, Jingkui Liang, Weidong Zhuang

"The subsolidus phase relations in the Sm2O3-CeO2-CuO ternary system sintered at 1000°C in air have been investigated by X-ray powder diffraction. The system can be divided into two ternary phase regions and three binary phase regions. Solid solution Sm2-xCexCuO4-y is the only ternary phase in the system. The maximum solid solubility was confirmed to be x = 0.2. The crystal structure, oxygen content and superconductivity of the solid solution Sm2-xCexCuO4-y have been investigated.I. INTRODUCTIONAfter the first discovery of the superconducting ceramic system La-Ba -Cu-O[l] with Tc = 30 to 40K, other families of cuprate-based ceramics have been synthesized with higher critical temperature. These oxides include the R-Ba-Cu-O (R: rare earth) systems (Tc=90K or so)[2,3], the Pb-Sr-(R,Ca)-Cu-O systems (T c = 50 to 100K), the Bi-Sr-Ca-Cu-O systems (Tc=80 to 105K)[4], the T1-Ba-Ca-Cu-O systems (Tc=85 to 125K)[5], the Hg-Ba-Ca-Cu-O systems (Tc=90 to 150K)[6,7], and some others. The improvement of Tc is very rapid. The measurement of the Hall and Seebeck coefficients shows that they all are p-type superconductors. In 1989, Tokura et al.[8] discovered the superconductors R2_XCexCU04_y(R = Nd, Pr, Sm) with Tc=20 to 24K (onset) and found that the charge carrier is electron in contrast to their hole doped counterparts. This discovery increases the fundamental understanding of the cuprate-based superconductors by comparing their characteristics and mechanisms to those of the p-type superconductors.One of the outstanding features of these n-type superconductors is the difficulty in obtaining samples in good charactors, such as the difficulty in obtaining zero resistivity state in single crystal or bulk samples; the semi-conductivity of bulk samples in ordinary state (opposite to the superconducting state) and a reducing reaction involved before the superconductivity has been found[9]. Therefore, it is necessary to optimize the sample preparation of the n-type superconductors. All the n-type superconductors have been found· considerable solid solubility. The compositional variations play a governing role in the carrier doping of the superconducting phases. Also, it is vital to the ceramic processing of superconductors to identify the compatible phases in the phase diagram. Finally, there is always the possibility of finding additional compounds, both superconducting and non-superconducting, in an unexplored system."

Jan 1, 1996

By Gennady I. Gulyayev

A mathematical model of plastic deformation occurring in cold plug drawing of mother tubes with initial cross-sectional wall thickness variations (CSWTV) has been developed. The main provision of the model is that eccentricity em is of such value that projection of all forces acting upon the plug in the deformation zone along the axis perpendicular to the drawing axis equals to zero. Calculations have proven that with other conditions being equal increase in the die cone angle and the deformation cycle number reduces CSWTV. Theoretical findings were confirmed by practical results. Keywords: cold, drawing, plug, die cone, plastic deformation.

Jan 1, 2003

By M. Ashraf, P. J. Hazell, A. A. H. Ameri, J. P. Escobedo-Diaz, N. N. Elewa

A novel methodology to estimate the dislocation density in cubic metals by using microhardness measurements has been established. The proposed methodology is based on the Indention Size Effect (ISE) phenomena and strengthening mechanisms of materials at the micro-level. The methodology was validated by using experimental data of lean duplex stainless steel 2101 alloy. The results are confirmed via X-ray diffraction measurements and they substantiate that the proposed approach can be used as a general method to estimate dislocation density in metals.

Mar 1, 2017

By Pragna N. H. Bhakta

The minerals industry is under political and economic pressure to reduce its processing wastes and minimize their impact on the environment: Recycling is one of the means by which the minerals Industry can reduce the quantities of effluents and residues that are discharged to the environment. The wise use of available resources is not only an environmental necessity but also an economic benefit as natural mineral resources are depleted and/or become more complex. The purpose of this paper is to review the technical and regulatory issues that will help shape the future of minerals recycling over the next ten years. Research and development to address technical issues will be discussed with emphasis on the Bureau of Mines recycling research program.

Jan 1, 1992

By Veneta Groudeva

A pyritic ore containing zinc, lead and copper as? the relevant primary sulfide minerals, .as well as gold and silver finely disseminated in the sulfide matrix, was? leached in percolation columns. Each column contained 30 kg of ore crushed to minus 10 mm. Firstly, zinc and copper were efficiently leached by means of chemolithothrophic bacteria? in acidic sulfate bearing medium. Zinc was leached more rapidly than copper but the final extractions of these metals were similar (about 75% in 300 days). A part of the galena was oxidized to the. insoluble lead sulfate during the leaching. The pyr:ite was, however, relatively slightly attacked. The ore was then leached by means of FeC11 - HCl solutions both in the presence and in the absence of bacteria to solubilize the lead. The chemolithotrophic bacteria grew in media containing both chloride and sulfat~ ions and maintained a high ferric to ferrous ion ratio in the percoiating solutions. The chemical leaching was, however, more efficient since ft was possible to carry it out at higher chloride ion concentrations. About 10% of the lead was leached in this way in 90 days. Finally, the ore was leached by thiourea in the presence of a gold-oxidant (oxone) to extract the gold and silver. Over 60% of the gold and over 55% of the silver were extracted from the ore in 150 days, while. the extractions of these precious metals from an untreated ore sample were lower than 25%.

Jan 1, 1991

By Mingmei Zhu, Xin Qiu, Xiaofei Dou, Yu Wang, Tiancheng Lin, Bing Xie

In this study, the slag forming route of the single-slag steel melting when smelting medium phosphorus hot metal was investigated. The CaO-SiO2-FeO-MgO-MnO-P2O5 as hexahydric slag system was adopted in the converter. The effect of slag composition on liquidus was calculated by FactSage, the isogram of phosphorus distribution ratio was calculated by using the regular ion solution model, combining these two tasks, the theoretical slag forming route was obtained. Through experiments, the actual melting point ofthe corresponding components on theoretical slag forming route was obtained, in this way, the theoretical slag forming route was confirmed. Then, the theoretical slag forming route was applied to industrial test in a 210t BOF. After using the new slag formating route, the dephosphorization ratio was increased 3.6% while the auxiliary materials consumption was reduced, and the cost of steelmaking was reduced.

Jan 1, 2015

By Oluwatosin A. Aladejebi, Apsara S. Jayasekara, Raymond J. Longbottom, Mark Reid, Marc in het Panhuis, Brian J. Monaghan

The coke analogue is a new research tool that has been developed to quantify and characterize the effect minerals in coke have on coke reactivity. The analogue material is made from a number of different carbon or carbon containing materials and minerals to in part replicate real industrial coke’s reactivity behavior. Elucidation of the effects of minerals on coke reactivity has proved difficult due to the complex and heterogeneous nature of industrial coke and the potential non-additive effects of minerals on coke reactivity. The coke analogue addresses this complexity and heterogeneity through control of its mineralogy, mineral size and mineral dispersion through the analogue, porosity and carbon structures. Initial studies using the analogue were focused on coke dissolution kinetics in liquid iron but recent work has focused in characterization of its porosity, carbon structure and rate of reaction.

Jan 1, 2014

By Olexandr Gydin

The evolution of grain and dislocation structures during cold deformation of the new steel LH800 of Salzgitter AG is investigated in the frame of this work. The main feature of this material is its ability to air-harden by carbon content of about 0.1%. The initial ferrite structure of the metal provides high plasticity at cold deformation and subsequent heat treatment increases tensile strength approximately two times. Described are results of in-situ tensile tests in the SEM. SEM and TEM analysis of grain and dislocation structures evolution in samples, which have been uniaxially deformed to certain strains, are carried out. After statistical evaluation of results the grain elongation against strain is determined. A microstructure of a deep drawn cup is analyzed by means of SEM. A quantitative evaluation of grain elongation on the different cup zones and comparison of these data with prediction results based on tensile tests are carried out.

Jan 1, 2009

By Marcos Aurélio S. Costa, Nilton F. Nagem, Andreia B. Henriques, Herman S. Mansur, Alexandra A. P. Mansur, Antonio E. C. Peres, Valeria G. Silva

The superfine material generated in the Bayer process was used in one innovatively way as a precursor to geopolymerization techniques because of the presence of Gibbsite. Gibbsite can play a role in system adjustment because of the SiO2/Al2O3 ratio. Furthermore in the geopolymeric system it was studied the influenceof the additives such as kaolin, metakaolin and sodium trisilicate in an alkaline media. Others conditions to form the geopolymer were also evaluated such as solid/liquid ratio, SiO2/Al2O3 ratio and total alkaline. The raw materials and geopolymeric products were characterized by several techniques e.g. XRD, DSC, FTIR and SEM. Through the FTIR technique it was observed an increase in intensity and bandwidth in the region centered at 1010 cm-1, which is related to the asymmetric vibration Si(Al)-O, this is an indicating of the possible geopolymer formation This broadening of the band promotes a relative disappearance (overlapping) peaks at 965 and 935 cm-1 associated with raw material (ESPDust).

Jan 1, 2015

By Yasuo Kudo, Wu, Hayato Sato, Hiroshi Nakazawa, Shouming

"In order to recover copper from a waste nickel condenser powder, bioleaching experiments were carried out using Thiobacillus ferrooxidans in a shaking flask. The content of nickel and copper in the waste nickel condenser powder in this study were 8.0% and 3.5%. X ray analysis showed the peak of barium titanate. In the preliminary study using metal nickel and copper powders , the dissolutions of nickel and especially copper were accelerated with the addition of ferric iron in the bioleaching of nickel and copper powders while not in the absence of ferric iron. Ferric iron oxidizes both metals, and Thiobacillusferrooxidans oxidizes ferrous iron resulting from the oxidation of metals, whereby the dissolutions of metals proceeds. The dissolution rates of nickel and copper increased with increase in the concentration of ferric iron in the bioleaching of the waste nickel condenser powder.1. IntroductionNickel condensers rejected from manufacturing plants are crushed and landfilled. Waste nickel condensers contain nickel and copper and could be considered as nickel and copper ores. Since the capacity of landfills is diminishing, it is required to recycle metals of waste nickel condensers in order to reduce the amount of wastes landfilled. Conventionally, metals in the waste were recovered by dry metallurgy after the incineration.Nickel has been refined by solvent extraction - electrowinning method (SX-EW method). Recently the amount of copper refined by SX-EW method has increased (Takahashi, et al. 1994). This method is cleaner and consumes less energy than conventional methods. Nickel dissolved well in acid solutions, but copper is not. If copper is leached efficiently from a waste nickel condenser powder, SX-EW method will be applied to recover copper from them"

Jan 1, 2000

By Liangying Wen, Jian Xu, Dongdong Wang, Kaihui Ma, Yang Xu

Slags play an important role in blast furnace operation, and their com- positions are based on the CaO –SiO2–MgO–Al2O3 quaternary system. However, there is not a clear understanding of the effects of gangue on of the formation of FeO-bearing primary-slags process in blast furnace. In this work, the softening and dripping experiments under the blast furnace conditions are designed to explore the influences of CaO-/SiO 2-/MgO-/Al2O3 on the softening and melting properties of FeO respectively. The results indicate that additions of CaO or Al2O3 decrease the starting softening temperature and no dripping behaviors are found in comparison with the base case results when only FeO is used. On the contrary, the addition of SiO2 or MgO rises the starting and ending softening temperature, as well as the dripping temperature. The lowest maximum pressure drop is obtained in the case with addition of SiO2. According to XRD analysis results, the initial phase with CaO addition in the primary-slags should be CaOFe3O4 and that with SiO2, MgO, Al2O3 additions are fayalite (2FeOSiO2), magnesioferrite (MgOFeO), hercynite (FeO2Al2O3), respectively.

Mar 1, 2017

By R. C. Hubli

A chemical model has been developed to investigate the dissolution of sulphide minerals in brine solutions containing copper and iron chlorides. The model has been employed to study the dissolution .of synthetic NiS using different initial concentrations of Cu(II), Cu(I), Fe(III) and temperature. The speciation of copper with particular reference to the formation of hydroxy-chlorides as a function of total chloride and H+ has been computed. The model predictions are in agreement with experimental results. It has been found that addition of Fe(III) results in the maintenance of a high Cu(II)/Cu(I) ratio leading to enhanced rates of dissolution and suppresses the loss of Cu(II) due to the formation of hydroxyl-complexes.

Jan 1, 1997

By D. F. Suarez

Spontaneous nodulation leading to growth of well developed glossy spheroids (generally hemispheres) of up to 0.06 cm width in 120 min has been observed during copper electrodeposition with certain levels of glue, thiourea and C1-. Thiourea alone can produce spontaneous nodulation but addition of glue and/or Cl- is required for rapid and sustained growth. In most cases once the glossy nodules develop they consume the majority of the copper deposited; thus, the specific current densities (and hence copper electrodeposition rates) on the glossy nodules are about an order of magnitude or, more greater than on the adjacent planar surfaces. The texture of the adjaoent planar surfaces is not glossy in appearance but is well faceted showing the usual deposition grain structure for such additives. Cathode potentials when spontaneous nodulation occurs are about TOO my more negative than with usual copper electroplating. This fact associated with evidence of extremely high levels of cathode surface passivation based on cyclic voltammograms indicates that the conditions which lead to spontaneous nodulation result from a very tightly adsorbed additive surface film. This film breaks down in specific points initiating the glossy nodules which then grow at extremely rapid rates. Current density is also important in spontaneous nodulation. At equal deposition times a current density of 21.5 mA/cm produced much larger glossy nodules than at 48 mA/cm2. The surface concentration of the glossy nodules was much greater in the latter case, however. The role of current density is still not well understood. The role of it as well as the relative roles of the three additives, thiourea, glue and Cl- in spontaneous nodulation is presented. Preliminary results and some possible correlations of these to help explain spontaneous nodulation are presented. It is believed that tankhouse upsets where cathode nodulation occurs may be related to this phenomenon.

Jan 1, 1987

By Yuanbo Zhang, Zijian Su, Bingbing Liu, Guanghui Li, Manman Lu, Tao Jiang

Acid wastewater containing toxic metal ions has become increasingly important global environmental concern and lead (Pb) is one of the prime toxic heavy metal ions. Humic acid (HA), a kind of natural organic matter, has been proventohaveagreatadsorptioncapacityformetalcations(Pb2+,Cu2+,etc.).Our previous study has verified that HA has excellent adsorbing ability on vanadium titanium-bearing magnetite(VTM) particles. In this study, VTM-HA complex magneticparticles werepreparedfor removing Pb(II)fromacidwastewater,which could be easily recycled by magnetic separation. The effects of pH value, ionic strength and VTM-HA concentration on the removal ratio of Pb(II) were deter- mined by isothermal adsorption tests. The results indicated that Pb(II) adsorption was subject topHand ionic strength. When initial Pb(II) concentration is 100 mg/ L, the residual concentration and removal ratio of Pb(II) reach 0.17 mg/L and 99.83%, respectively, which are much lower than the discharge standard. (cid:1) (cid:1)

Mar 1, 2018