By Jewel A. G. Gomes

Green rust (GR) are layered Fe(II)-Fe(III) double hydroxides, having a pyroaurite-type structure consisting of positively charged hydroxide layers and hydrated ions in interlayers. This special feature of GR is very efficient for wastewater treatment as the pollutants are easily taken in or exchanged with the anions in the interlayers. It can be simply and cost-effectively produced by electrocoagulation (EC). Chicken processing plant (CPP) produces large amount of wastewater containing variety of readily biodegradable organic compounds, fats, and proteins. The possible re-use of properly treated CPP wastewater would be economic and environment friendly. In this study, we present our work on treatment of CPP wastewater using EC, specifically for the removal of COD. Analysis of the EC-treated water for reuse in the same plant is discussed considering the U.S.EPA regulations. Two types of EC-reactors were used for this purpose. To better understand the treatment mechanism, EC-floc was also characterized using XRD and SEM-EDS.

Jan 1, 2010

A sinter plant baghouse dust has been treated as a hazardous solid waste, and disposed at a very high price. A series of leaching tests were conducted to examine the possibility to produce high grade potassium chloride from the solid waste. It is found that around 40% of the solid wastes can dissolve into water, and a deposit with more than 90% KCl can be produced after simply drying the solution.

Jan 1, 2009

By Zhao-cheng Liu

Iron oxide red pigment powders of high quality were synthesized from pyrite cinders. Iron ox-ide red pigment powders were synthesized by hydrothermal method from the precursor of Fe(OH)3 and Fe(OH)2 colloid, which were obtained after ammonia solution reacted with acidic leaching solution produced by the reaction of pyrite cinders with sulfuric acid. Effects of reaction concentration, reaction temperature, reaction time, pH value and n(Fe2+)/n(Fe3+) on main properties of oxide iron red were studied by experiments. The prepared particles were characterized by means of X-ray diffraction (XRD) and scanning electron microscope(SEM). The results revealed that the synthesized iron oxide red particles were _-Fe2O3 and pseudocubic with particle size of 0.50~0.75µm. Furthermore, the quality of iron oxide red pigment powders reached the first grade of national standard (GB1863-89 ).

Jan 1, 2009

By Felipe Perissé Duarte Lopes

The tensile properties of DGEBA/TETA epoxy matrix composites reinforced with different amounts of curaua fibers were evaluated. Tensile specimens with up to 35% in volume of long, continuous and aligned curaua fibers were room temperature tested in an Instron machine. The fracture was analyzed by SEM. The results showed significant changes in the mechanical properties with the amount of curaua fibers. This was compared to other bend-tested composites with distinct matrices. The fracture analysis revealed a weak fiber/matrix interface, which could be responsible for the comparatively low performance of some properties.

Jan 1, 2010

By Rameshwar Sreenivasan

This paper presents a sustainability analysis of Selective Laser Sintering (SLS) from an energy standpoint. Data of electrical power consumed by the system over an entire build were acquired using a LabVIEW 8.6 circuit. The power drawn by individual subsystems was also measured, and an energy balance was performed. These data were then used to arrive at a Total Energy Indicator of the process with the help of a specific type of Environmental and Resource Management Data (ERMD) known as Eco- Indicators, which indicates the level of sustainability of the process.

Jan 1, 2010

By J. W. Bridge

Triaxial compression tests at various confining pressures and temperatures, as well as tangent modulus tests using ultrasonic waves, were conducted for wax-coated granular composite materials. The material used is a surface for Thoroughbred horse racing. The purpose of these tests is to examine how track shear strength and tangent modulus at a range of loads respond to changing temperatures. Previous work has shown that a wide range of operational temperatures are experienced which have been reproduced in the lab. Using differential scanning calorimetry, it is confirmed that these operational temperatures correspond to distinct thermal transition regions for the wax that is used to coat the sand in these surfaces. Preliminary results show that both shear strength and tangent modulus are sensitive to temperature changes with maximum strength and modulus correlating with major DSC wax transition regions.

Jan 1, 2010

By F. A. Guo

Ultrafine-grained surface layers were obtained by surface mechanical attrition treatment (SMAT) in copper and titanium samples. The thermal properties of the deformed layers were characterized using a scanning thermal microscopy (SThM) that allows thermal conductivity to be mapped down to the submicrometer scale. A theoretical approach, based on this investigation, was used to calculate the heat flow from the probe tip to the sample and then estimate the thermal conductivities at different scanning positions. Experimental results and theoretical calculation demonstrate that SThM can be used as a powerful tool for the thermal property and microstructural analysis of ultrafine-grained microstructures.

Jan 1, 2006

By K. Morsi

The interest in spark plasma sintering has been growing considerable over the past few years. This has been brought about by the unique advantages of the process, which include reduced sintering temperatures and times and the production of materials with unique microstructures and properties. Despite its current reputation as an outstanding process that has solved major problems such as nano-powder consolidation, it has so far been largely limited to the manufacture of simple shapes, due to its inherent geometric configuration. In this paper we present preliminary results on spark plasma "extrusion" that can allow the production of extended geometries via electric-current processing. Preliminary results on the processing and microstructure of spark plasma extruded aluminum are discussed.

Jan 1, 2009

By Hector Carreon

Due to elevated temperatures, excessive stresses and severed corrosion conditions, turbine engine components are subject to creep processes that limit the components life such as a turbine bucket. The failure mechanism of a turbine bucket is related primarily to creep and corrosion and secondarily to thermal fatigue. As a result, it is desirable to assess the current condition of such turbine component. By using eddy current images, it was shown that the eddy current technique could be used to monitor creep damage in a nickel base super-alloy. The eddy current results also show a significative variation in the electrical conductivity on the creep damage zone with respect to the background zone in nickel-base super-alloy samples. In addition, the absolute thermoelectric power coefficient show also a strong dependence associated with creep damage in nickel base super-alloy samples using a copper hot tip reference. The eddy current and thermoelectric power techniques seems to show promise as nondestructive evaluation tools for monitoring the level of creep damage in metallic alloys.

Jan 1, 2010

By Liyuan Chai

In this study, spent grain was used as an adsorbent for the removal of Hg(II) from aqueous solutions, the process parameters such as contact time, solution pH, adsorbent dose, and initial Hg(II) concentration were studied in batch experiments. The initial adsorption process was fast, 91.08% of adsorption occurred within 5 min and equilibrium was reached at around 30min. Adsorption process was found to follow pseudo-second-order kinetics. The equilibrium data were better fitted to Langmuir isotherm than Freundlich isotherm with the maximum adsorption capacity 41.36 mg/g. The structure and component of spent grain before and after adsorption of Hg(II) were investigated using scanning electron microscope(SEM) and energy dispersive X-ray analysis(EDAX), these analysis also confirmed the adsorption of Hg(II) onto spent grain. The results indicated that spent grain had potential as a new inexpensive adsorbent for Hg(II) removal from aqueous solutions.

Jan 1, 2009

By Sergio Neves Monteiro

The efficiency by which an applied load is transmitted through the composite structure depends on the strength of the interface between the matrix and the second phase. In fiber reinforced composites, the interfacial shear stress plays a major role in the composite capacity to support the applied load. This interfacial stress can be obtained by means of pullout tests using the fiber embedded to a certain length in a socket of the matrix material. In the present work, pullout tests were performed to evaluate the interfacial shear stress of ramie, a relatively strong natural fiber, reinforcing polyester matrix composites. The general result permitted to calculate a critical length for the ramie fiber embedded in polyester resin. From this critical length, the value of the interfacial shear stress was calculated. An interpretation of this result together with SEM observation displayed a relatively weak bond between the ramie fiber and the polyester matrix.

Jan 1, 2010

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By J. C. Pandey

The paper highlights the experimental investigations to characterize texture and plastic strain ratio r-Bar in auto grade steel sheets by ultrasonic measurements, whereas attempts were made to characterize interlamellar spacings in pearlite, tensile stresses and torsional properties in prestressed concrete wires by eddy current measurements. Good correlations were obtained between the testing parameters (such as ultrasonic attenuation and velocity in case of steel sheets as well as eddy current out put voltage and phase angle in case of steel wires) and the materials properties (such as texture, plastic strain ratio r-Bar, interlamellar spacings in pearlite, tensile stresses and torsional properties). 15 MHz normal direct contact and 20 MHz delay line normal shear wave probes were used for ultrasonic measurements. Eddy current measurements were done using an absolute coil probe with variable frequency selection. The experimental results show the possibility of nondestructive on line measurement of the above microstructures and properties.

Jan 1, 2010

By Liang Sha

In this study, adsorption of copper by chemically modified orange peel was investigated. A conspicuous change occurs in the surface morphology of the biomass due to modification, which is depicted by SEM images. Equilibrium isotherms and kinetics were obtained and the effects of various factors, including solution pH, contact time, initial metal ions concentration and temperature, were studied by batch experiments. Kinetics was found to be best-fit pseudosecond- order equations. Equilibrium was better described by Langermuir isotherms rather than Freudlich isotherms. At 25?, pH5.30, the maximum adsorption capacity was 70.67mg?g-1 . With increase of temperature, adsorption efficiency decreased. The biosorbent was suitable for repeated use for more than five cycles.

Jan 1, 2009

By Helvio Pessanha Guimarães Santafé Jr.

The coir fiber extracted from the husk of the coconut has been extensively used as polymer composite reinforcement in a variety of industrial applications ranging from civil construction to automobile seat cushions. The hydrophilic coir fiber does not act as an effective reinforcement owing to its low interfacial strength with hydrophobic polymers. As a consequence, coir fiber composites display relatively low mechanical strength. The objective of this work was to investigate the effect of an acetylation treatment of the coir fiber surface on the mechanical behavior of epoxy composites with amounts of fibers up to 30% in volume. Coir fibers were immersed in an acid solution of acetic anhydride for one hour, washed and dried, before mixing with DGEBA/TETA epoxy to fabricate the composites. Flexural mechanical properties were obtained by bend tests. The results showed significant differences to similar composites with alkali treated coir fibers that have been previously investigated.

Jan 1, 2010

By Olga Frank-Kamenetskaya

The experimental results of study of atmospheric corrosion processes on Saint-Petersburg bronze monuments surface, received in situ and by means of simulating experiments, have been discussed. Influence of the time factor on corrosion film (patina) mineral composition has been analyzed. Direct dependence between patina mineral composition and environmental conditions has been proved. The sequence of patina phases crystallization has been established. Effect of the chemical composition and heterogeneity of artistic bronze and also monument surface structure on the rate of corrosion process has been regarded. The time variations of mass of the crystallized in the hydrochloric acid vapor phases have been investigated. The kinetic laws of their development at the initial stage of formation, indicating simple (non chain) reactions, have been revealed.

Jan 1, 2006

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By Zhuokun Cao

Manufacture of aluminum foams still suffer from nonuniformity and poor reproductively for there is lack of basic knowledge of foaming process. In this paper, carbon fibers are used as novel stabilizing additive for aluminum foams, and the structure evolution of aluminum foams with different fiber content was studied. A laser rangefinder was used to detect the expansion rate of different al foams. Al foam samples are solidified at different foaming time to determine its relative density and cell size distribution. Results indicate that the cell size of foams linearly increases with the decrease of density, and the slope of the line is influenced by fiber content. The relationship between expansion ratio, density and cell size of the foams is discussed. It is concluded that the density of resulting foam is influenced by the rate of gravity driven drainage, and its cell size is determined by expansion ratio and foaming time.

Jan 1, 2010

By Akihide Hosokawa

The void growth and coalescence in model materials involving a pre-existing three dimensional void array (i.e. multiple layers of a void array) was studied by X-ray computed tomography (XCT) coupled with in situ tensile deformation. To reduce the recording time, a new technique called fast tomography was employed. The model materials used in this paper were fabricated by the combination of an ultra-short pulsed laser machining system and a diffusion bonding technique, and two different types of arrays were prepared namely, FCC 1 and FCC 2 type array. This methodology allowed the authors to capture the entire process of growth and coalescence events of a void array embedded in the metal matrix. The failures in the both materials involved internal necking and shear localization. One of the highlights of this paper is that the plastic strain at the onset of void coalescence was measured for each model material. These values are in fact the adequate values to be compared with the coalescence strain predicted by existing void coalescence models such as the Brown and Embury model, the Thomason model and the Pardoen and Hutchinson model. The comparison suggested that the Brown and Embury model underestimated the coalescence in neither of the current model materials, while the Thomason model and the Pardoen and Hutchinson model showed a quite good agreement with the result for FCC 1 material. On the other hand the result from FCC 2 material agreed with none of the models probably due to the geometry of the void array that is not compatible with the existing models.

Jan 1, 2010

By S. Y. Tan

As continual complementary metal?oxide?semiconductor (CMOS) scaling requirements, metal gate/high-k dielectric/Si gate stacks are expected to replace poly-Si/SiO2/Si gate stacks in the future CMOS sub-45 nm technology node. Hafnium based oxide is a promising candidate to replace SiO2 as a gate dielectric, due to its much higher dielectric constant (high-k) and stability. The key challenges of successfully adopting the high-k dielectric/Si gate stack into advanced CMOS technology mostly come from the interfacial properties. The origins of the electrical and physical characteristics of the dielectric oxide/bulk interface were studied in detail. The leakage current density-voltage (J-V) and capacitance-voltage (C-V) measurement techniques were employed to study the dielectric oxide/Si interface. The effects of the post-deposition annealing (PDA) treatment on the interface charges of dielectric oxides were studied. We found that the PDA can effectively reduce the trapping density and leakage current, and eliminate hysteresis in the C?V curves. Besides, the changes in chemical bonding features at HfO2/Si, HfSiO/Si and HfSiON/Si interfaces due to PDA treatment were evaluated by XPS measurements. The XPS analysis provides a better interpretation of the electrical outcomes. As a result, both HfSiO and HfSiON films have exhibited superior performance in terms of thermal stability and electrical characteristics.

Jan 1, 2010