By Y. Zhoa

The surface morphology of materials is of fundamental importance to many surface related applications, such as wetting, friction, reflection, drag, and adhesion. Various approaches for micro/nano patterning atop polymer surfaces have been proposed in recent years. However, a cost effective technique is still highly in demand. In this paper, we demonstrate a novel but rather simple and generic approach for surface micro/nano patterning using shape memory polymers (SMPs). Different types of novel patterns are realized and their 3-D surface features are quantitatively analyzed by a PLµ Confocal imaging profiler.

Jan 1, 2010

By Xiaodong Wang

A liquid metal flow generated by a magnetic field whose traveling direction is periodically reversed, the Reversed Traveling Magnetic Field (R-TMF) is studied. The modulation frequency ranges from 0 to 6 Hz. Ultrasonic Doppler velocimetry probes the generated fluid flow. Depending on the modulation frequency, a number of characteristic flow features are exhibited. A transition frequency (approximately 4 Hz) exists, above which the flow is no longer sensitive to the force modulation. Below this transition point, the amplitude of the velocity oscillation increases, and then below fm = 0.05 Hz, it saturates around a value close to that observed without any modulation. A theoretical model to obtain an analytical solution of electromagnetic force and to predict flow motion is developed, which is fairly in agreement with the experiments.

Jan 1, 2009

By Xingjian Gao

The mechanical properties of a low carbon low alloy steel in the austenite and _-ferrite regions have been examined by thermal-tensile tests using a Gleeble-1500D system at temperatures in the range 600oC to 1300oC and at a strain rate of 10-3/s; these being the conditions that apply to the unbending operation during the continuous casting of steel. The yield strength and tensile strength of steel decreased with increasing test temperature and the embrittlement zone occurred in the temperature range 800oC to 970oC. In the embrittlement zone, the fracture surfaces and microstructures of the tensile specimens were examined by scanning electron microscope. The results showed that the cause of the embrittlement at 950oC in which the minimum %R of A was around 36% is the second phase particles precipitated along the _ grain boundary during deformation leading to inter-granular brittle fracture.

Jan 1, 2010

By Selda Ozkan

In this study, a combination of cathodic arc physical vapor deposition (PVD) and molten salt electrolysis methods were used to obtain ZrB2 layers on AISI 304 grade stainless steel surface. Prior to boriding, steel surface was coated with metallic zirconium via cathodic arc PVD method and then the zirconium coated steel was borided by molten salt electrolysis. Well adherent, dense, ZrB2 layers are formed on the substrates. The thickness of the ZrB2 layer showed dependence on the thickness of the metallic Zr coating layer and the time of boriding. During the boriding process the alloying elements of the substrate also took part in the coating structure depending on their diffusion characteristics.

Jan 1, 2010

By Yue-yuan Li

China has abundant magnesite resource, but the low-grade and powder ores have always been rejected, which influences the comprehensive utilization of resource and often causes circumstance problems. The present work investigated the preparation of magnesia whisker using magnesite tailings as starting materials by preparation magnesium carbonate whisker as precursor firstly in the route of calcination, hydration, carbonation and pyrolysis, follows by second calcination of the precursor. The influence of pyrolysis conditions and additives on morphology of magnesium carbonate crystal as well as the influence of calcination conditions on morphology of magnesia whisker was investigated. The results showed that thermal decomposition products was MgCO3?3H2O. Magnesium carbonate whisker with length of 10~60 µm and the length-to-diameter ratio of 10~20 was prepared when soluble magnesium salt was added. While temperature was elevated at 1°C?min-1, magnesia whisker with length of 10~60µm was obtained.

Jan 1, 2010

By Lifeng Zhang

The transport of fluid, heat ,and particles (bubbles and solid inclusions) in flowing molten steel is investigated in steel refining ladles, the continuous casting tundish, continuous casting mold and strand, and steel ingot casting processes. The two-equation k-?? model is used to simulate the turbulence. Multiphase fluid flow is numerically simulated with a Lagrangian-Eulerian approach, an Eularian-Eulerian approach and the Volume Of Fluid (VOF) method. The simulation can predict inclusion trajectories, inclusion removal fraction, free surface waves and other phenomena, which can be used to optimize these important metallurgical operations.

Jan 1, 2006

By M. T. Baquera

A comparison of microstructures associated with W single-crystal ([001], [011], [111]) rods prior to deformation (as grown), and after quasi-static compression (at a strain rate of ~1/s) by transmission electron microscopy (TEM) shows several orders of magnitude difference in dislocation density. Dislocation substructures were not significantly different amongst the deformed sample orientations. In contrast, [001] W rods penetrated into steel targets, at impact velocities of ~1.3 km/s, exhibited heavy dislocation densities and dynamic recrystallization as very distinct microstructural regimes accommodating the penetration process. Twinning on {112} also occurred as a precursor to, or remnant of, these microstructures near the projectile head. These results suggest that deformation accommodating the extreme strains and strain rates associated with the penetration of a single-crystal rod into a metal target is not adequately represented by conventional deformation

Jan 1, 2006

By Youliang He

Twin-roll casting is an integrated casting and rolling process that involves the continuous solidification of a melt and the plastic deformation of the solidified metal between two rotating rolls. Computer modeling is a valuable tool to help engineers understand the metallurgical process during twin-roll casting. However, commercially available software can only model either the fluid flow/heat transfer of the melt or the plastic deformation of the solid, but not both. In this study, an object-oriented finite element program was developed to simulate the steady-state fluid flow, solidification and plastic deformation of an A7,31 magnesium alloy in a horizontal twin-roll caster. The melt, the mush zone and the solid were treated as a generalized Newtonian flow in an Eulerian reference frame and different constitutive equations were employed to describe the material behaviours. The effect of operational parameters on the solidification process was discussed based on the simulation results.

Jan 1, 2010

By Alicia Esther Ares

The family of Zn-Al (ZA), Zn-Ag and Zn-Al-Ag (ZINAG) alloys offers high mechanical properties, ease of finishing, the advantage of low energy and pollution-free melting. Also, present alternatives to the well developed alloy systems, such as brasses, bronzes, cast irons and aluminum alloys. The main objective of this paper is to measure thermal parameters in ZA, Zn-Ag and ZINAG hypoeutectic and hypereutectic alloys directionally solidified which present columnar, equiaxed and columnar to equiaxed transition structures (CET). Also, estimate the mechanical properties, such as microhardness and tensile parameters and correlate these with the thermal (cooling rate) and structural parameters (grain size and dendritic spacing). The different types of structures were analyzed with optical and scanning electron microscopy. The results showed the influence of concentration, microstructural arrangement and thermal conditions during solidification on the mechanical properties. The results of the present investigation are compared with previous experiments.

Jan 1, 2010

By Marilia S. de Magalhaes

Keywords: sinter, characterization, agglomeration, iron ore Iron ore sinters are the main burden of blast furnaces for pig iron production. The evaluation of these agglomerates is very important due to their properties affect indirectly the productivity and costs of production of the steel industry. In the sintering plants, the standard procedure of sinter assessment has been carried out by particle size control, bulk chemical analyses, tumbler and/or shatter tests and determination of reduction degradation and reducibility indexes. Microscopy techniques have just been applied to characterize sinters produced in pilot conditions, however, these techniques, the classical ones and the less traditional, allow enhancing the industrial sintering process assessment. For investigation of the phases, microstructures and fabric, reflected-light and scanning electron microscopy(backscattered electrons images) were used; for micro analytical chemical examination, energy-dispersive X-ray spectrometry; for Kikuchi patterns registers, electron backscattering diffraction. In addition to the microscopy techniques, the magnetic behavior was depicted by means of magnetic susceptibility measurements. Iron ore sinters are made up by hematite, magnetite, silicoferrite of calcium and aluminium and silicates. These phases develop either during sintering or, in some proportion, represent remnants of ores and fluxes; this is the case of some hematite and Mg-bearing silicate, respectively. From the magnetic susceptibility results, three different behaviors were determined, which are directly related to the magnetiteproportion in the samples. The phase association and proportion, the sintering conditions andthe quality assessment are some features appraised by such procedures, which reveal themagnitude of this proposal in sintering plants.

Jan 1, 2005

By Shirleny Fontes Santos

Muscovite mica crystals lower than 15 mm diameter are discarded as waste in the mining area of Borborema-Seridó (BRAZIL). The objective of this work was the ore dressing and purification of this waste to be used in the preparation of pearlescent pigment. Muscovite was dry ground using knife mills and an ultrasound treatment. It was possible to achieve 67% of mica with particle size lower than 100 µm. This product was used in the preparation of brilliant pigments based on muscovite flakes covered with rare earth oxides (CeO2, PrO2, Ce0,95Pr0,05O2). The pigments were characterized by X-ray diffraction, thermal analysis and scanning electronic microscopy. The color of the resulting pigments was analyzed using the CIELAB method and it showed the following colors: muscovite-CeO2 ? yellow, muscovite-PrO2? black and muscovite-Ce0,95Pr0,05O2 ? orange. Those results have shown that ?trash mica? is suitable for use in pigment preparation.

Jan 1, 2010

By Hamed Mirzadeh

The hot working behavior of 17-4 PH stainless steel was studied using the hot compression test at temperatures of 950-1150 °C with strain rates of 0.001-10 s-1. A step by step procedure for data analysis in hot compression test was given. The work hardening rate versus stress curves were used to reveal whether or not dynamic recrystallization (DRX) occurred. At low Zener- Hollomon (Z) parameter, this material showed a new DRX flow behavior, which was called Multiple Transient Steady State (MTSS). At high Z, as a result of adiabatic deformation heating, a drop in flow stress was observed. The general constitutive equations were used to determine the hot working constants of this material. Moreover, after a critical discussion, the deformation activation energy of 17-4 PH stainless steel was determined as 337 kJ/mol.

Jan 1, 2010

By Rashmi Ramesh

Zinc oxide nanoparticles and nanostructures form an active area of research in the recent years. It can be doped to modify electronic, optical and other properties. Synthesis and characterization of zinc oxide is of extreme importance in order to understand the structure property relationship in this material which is now being considered of importance next to carbon nanotubes. Microstructure of zinc oxide nanomaterial is extremely sensitive to the preparation conditions. Nanocrystalline pure and Mn and Mg doped zinc oxide samples were prepared by wet-chemical method under different growth conditions. The samples were investigated for crystalline phase, microstructure, morphology and luminescence characteristics. The effect of Mn and Mg doping on the characteristics of ZnO have been discussed.

Jan 1, 2010

By M. Faraji

Inclusions formed in a high-carbon, manganese-silicon killed plain steel (Fe-0.77C wt%) were studied. Various techniques were used to characterise the inclusions, and the latter were classified according to their chemical composition, size and morphology. The main constituent elements entering the inclusions were Mn, S, Al, and oxygen. Alongside MnS and some Al2O3 inclusions many non-metallic inclusions appeared in complex forms, consisting of silicates, sulphides and oxides. Duplex oxy-sulphides, mainly MnS combined with Al2O3, or SiO2 were the most common complex multiphase inclusions in this steel. The nanoindentation technique was used to assess and rate different types of inclusions and data of the hardness and elastic modulus of individual inclusions at room temperature are presented.

Jan 1, 2010

By Kwong. Kyei-Sing

Gasification is a process that converts a carbon feedstock into synthesis gas (CO+H2). Slagging gasifiers operate at high temperature and pressure and in a corrosive-wear environment from the slag. Cr2O3-based refractory linings are used to protect the steel vessel that comprises the gasifier from the aggressive gasification environment. Increasing service life of the gasifier is one of the keys for wide spread development of this technology. In support of the goals, research on the gasifier atmosphere, the slag chemistry, the interaction of Cr2O3 refractory with different feedstock mixtures (e.g., coal and petcoke) were characterized by post mortem analysis of bricks from service in gasifiers and thermodynamics simulation of the environment. Examples demonstrating how thermodynamic calculations can explain the post mortem results and make predictions of material interactions will be given. Attention is placed on the possibility of Cr+6 in different feedstock mixtures and operating conditions.

Jan 1, 2010

By S. N. Lekakh

Phosphorous segregated at grain boundaries during solidification and heat treatment dramatically decreases low temperature toughness of precipitation hardened Fe-Mn-Al-C austenitic steel. A thermodynamic analysis was performed to evaluate the possibility of decreasing P and subsequent segregation by Ca- and Ce-additives in the melt. It was shown that the predicted probability of forming a P containing compounds depends on melt composition and treatment sequence. Experimental heats were performed and several micro- and macro-structural effects of Ca- and Ce-additives were recognized by using an automated inclusion analysis technique.

Jan 1, 2010

The effect of rare earth element Y (0-2.0at.%) on the microstructure of TiAl alloys at the as cast and rapidly solidified conditions has been investigated. The results show that the addition of Y greatly refined the microstructure of TiAl alloys at both conditions. The refinement is more significantly with higher Y content. The refinement of Y in the cast alloys is attributed to that the strip-shaped Y-rich phase locating on the grain boundaries impedes the grain growth during solidification. In the rapidly solidified alloys, Y-rich phase dispersing uniformly as spherical particles in the matrix acts as heterogeneous nucleation sites which increases the nucleation rate of ??phase during the ????phase transformation, and produces a refined initial microstructure during solidification. Higher cooling rate restricts the grain growth during subsequent cooling.

Jan 1, 2010

By Napisporn Memongkol

Syntheses of Al-TiC-Al2O3 and Al-SiC-Al2O3 composites were obtained in situ by carbothermal reduction of mixtures of Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders. The reductions were carried out in a horizontal tube furnace under flow of inert gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of aluminum reinforce with titanium carbide and alumina and aluminum reinforce with silicon carbide and alumina. The effect of the reaction temperature (1000 o C ? 1200 o C) and condition of precursors on the Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders were investigated using XRD and SEM method. The synthesized products showed those composites with aluminum matrix and titanium carbide and alumina as reinforced phases and aluminum matrix and silicon carbide and alumina as a reinforced phase was formed.

Jan 1, 2006

By P. N. Anyalebechi

The effects of solidification rate (0.4-26.1 K/s) and alloying elements on the cast microstructures of aluminum alloy 5182 have been investigated with directionally cooled laboratory-size ingots. The alloying elements examined included Mg (3.6-4.7 wt.%), Mn (0.35-0.75 wt.%), Fe (0.11- 0.42 wt.%), Cu (0.03-0.25 wt.%), and Si (0.11-0.28 wt.%). These reflect the chemical compositions of AA 5182 end stocks with high recycled used beverage container (UBC) content. For a given chemical composition, the average dendrite cell and constituent phase particle size decreased with increase in average solidification rate. In general, within the level investigated, Mg did not have a significant effect on the types, volume fractions, and average sizes of the constituent phase particles. However, increase in Mn, Si, Fe, and Cu increased average sizes and volume fractions of the constituent phase particles.

Jan 1, 2010

By Meghan McGrath

Third generation advance high strength steels with microstructures of acicular ferrite and retained austenite were investigated and meet mechanical property goals. A good combination of strength and ductility were achieved with duplex ferrite and austenite microstructures where cementite formation was suppressed. Transformation induced plasticity (TRIP) behavior produced rapid work hardening. The mechanical properties of two hot-rolled steels with duplex microstructures were compared and had the following compositions: (1) Fe-0.14C-13.87Mn-1.42Si-3.51Al; and (2) Fe-0.06C-14.2Mn-1.85Si-2.38Al. These steels were cast, homogenized, and hot rolled at 900ºC to obtain a refined microstructure with ultimate tensile strengths and elongations to failure of 865 MPa and 39% and 1,217 MPa and 28%, respectively. The amount of metastable austenite in both compositions decreased after tensile testing from 58% and 28% to 6% and 0%, respectively. Microstructures were characterized using optical microscopy, scanning electron microscopy (SEM), and x-ray diffraction.

Jan 1, 2010