A study was performed to determine whether mineral textures affect are breakage during grinding, and to establish a correlation between are breakage and mineral liberation. A base metal are from the Brunswick No. 12 deposit in New Brunswick, Canada was ground for different periods of time in a laboratory ball mill, and both the unbroken are and the ground products were studied by image analysis. Similar size distributions were obtained for material from the 15-minute grind in a laboratory ball mill (K. 0 67 pm), for the grinding circuit discharge from a commercial mill (K. 0 = 59-72 pm), and for pyrite grains in unbroken are (K,. = 74 pm). This similarity indicates that the 1S-minute grind separated weakly adhering pyrite grains along grain boundaries, and represents the limit of easy breakage for the are. At this grind (15 minutes) large discrete are mineral grains and weakly adhering interstitial fillings aIrong pyrite were liberated. On the other hand, the 15-minute grind neither separated rooderately bonded pyrite grains nor released rooderate1y bonded interstitial minerals from pyritei a 45-minute grind (K.. 31 pm) in a laboratory ball mill was required. For Brunswick No. 12 are, a 45-minute grind in a laboratory ball mill (Keo = 31 pm) is equivalent to regrinding in a commercial mill (K ?? Fl:$ 30 pm). Grinding beyond 45 minutes in the laboratory ball mill broke the are by fracturing pyrite across grain boundaries and by Chipping grain edges. Such intense grinding (longer than 45 minutes) did not markedly increase sphalerite liberation. In contrast, the intense grinding increased galena liberation because a significant proportion of the galena occurs as minute inclusions in pyrite. These findings show that ore breakage and coincident liberation depend upon size distributions, intergrowths, and mode of occurrence of the minerals in an ore.

Jan 1, 1988

By Jonkion M. Font

An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander model for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2, MgO-SiO2, FeO-CaO-SiO2, FeO-FeO1.5-CuOo.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-MgO and FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte (L s/m as), and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5-CaO-MgO slag and liquid copper (L s/Cu as) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte-metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for prediction in multi-component slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes.

Jan 1, 2003

By Jonkion M. Font

An expression for the distribution ratio of arsenic between slag and copper matte or liquid copper was developed by both, an extension of the Reddy-Blander moderl for deriving a priori the arsenic capacity, and by a relationship between the arsenic capacity and the arsenic distribution ratio. In this study, the a priori arsenic capacities in the FeO-SiO2, CaO-SiO2,MgO-SiO2, FeO-CaO-SiO2, FeO1.5-CuO0.5-MgO-SiO2, FeO-FeO1.5-CuO0.5-CaO-Mgo and FeO-FeO1.5-CuO0.5-CaO-Mgo-SiO2, slags were calculated at 1573 K. The a priori arsenic distribution ratio between the FeO-FeO1.5-CuO0.5-CaO-MgO-SiO2 slag and copper matte mn (Lx, )' and between the FeO-FeO1.5-SiO2 or FeO-FeO1.5-CuO0.5*-CaO-Mgo slag and liquid copper (Ls/cua) were calculated. The model calculated data are found to be in good agreement with the reported experimental data. The availability of reliable thermodynamic data for slag components and impurities in the slag-matte- metal system is essential for the accurate prediction of impurity capacities and distribution ratio data. The arsenic distribution ratio model developed here, can be extended for predication in multi-componet slags and mattes or liquid metal, and thereby may lead to the development of new slag systems for the efficient removal of arsenic in the copper smelting, converting and refining processes,

Jan 1, 2003

By Günter Petzow, Hans Leo Lukas, Hans Jürgen Seifert

"The CALPHAD method (CALculation of PHAse Diagrams) has been extensively developed in the last 25 years and became a useful tool in materials science. Thermodynamic descriptions for the functions of state of unary, binary and ternary phases are derived by the optimization of phase diagrams. These functions are stored in computerized thermochemical databases and can be combined to extrapolate to multi component systems. Depending on special demand, the actually most advantagous presentations of the calculated results can be chosen: tables or in a clear graphical form as phase diagrams, phase amount diagrams or volatility diagrams. The method will be desribed by the system Ti-Si-C-N-O including the ceramic subsystem Si3N4-SiC-TiCi,N1_1,-C-N-O which is very important for the development of ceramic composites. The calculations give the thermodynamic stabilities of the condensed phases as function of temperature, concentration and partial pressure of different gas species. Adjusting the sintering conditions to these results the formation of unfavourable compounds or liquid phases can be suppressed.IntroductionThe CALculation of PHAse Diagrams (CALPHAD-method) of multicomponent systems provides the possibility to plan experiments very efficiently and avoid the experimental trial and error approach for the development of materials. The main problem for best use of calculated results is their interpretation with regard to the specific applications under consideration. Tables give the exact quantitative data for the treated phenomena. However, most important to make best use of these thermodynamic data is their graphical representation especially designed for the solution of specific problems, scientific as well as application oriented. Only well chosen graphical representations support a comprehensive understanding of the thermodynamic interrelationships and the transfer to the problem."

Jan 1, 1996

By Adriana de Aquino Soeiro da Silva, Joao Alves Sampaioa, Luiz Carlos Bertolino, Francisco Manoel Garrido, Marta Eloisa Medeiros

"Brazil has a large agricultural potential and its production success is related to the chemicaland physical soil characteristics. Therefore, the demand in the use of a great quantity offertilizers to compensate the low amount of nutrients in the soil includes about 40% of foodproduction costs. In order to develop economical alternatives to traditional fertilizers, rockswith potential use in agriculture will be studied. In this work the potassium rock, a greensandslate, will be chemically and structurally characterized for the development of a potassiumthermophosphate. This alternative fertilizer will be obtained based on a fusion of a ponderedmixture of potassium, magnesium and phosphate rocks to be applied in the Brazilianagriculture. Preliminary characterization results indicate that the greensand slate presents ahigh percentage of glauconite, quartz and micas.Keywords: Potassium thermophosphate, alternative fertilizers, greensand slate.IntroductionBrazil has a great agricultural potential and its production success is closely related to thesoil's chemical and physical characteristics. However, the country's soils present lownutrients content and high acidity due to weather conditions. Thus, the use of a high amountof fertilizers makes up for the soils' lack of nutrients and accounts for 40% of food productioncosts. Therefore, research on obtaining new alternative fertilizers is a constant worry due tothe increase on food demand [ 1].The lack of raw material for the preparation of NPK fertilizers in Brazil is a concern and theissue of potassium fertilizers a priority. Such a fact is because in 2008 only 608.000 tons ofKCl were produced, corresponding to just 10% of the Brazilian necessity. Thus, the use ofrocks as agricultural nutrients can contribute to reduce the need for industrial fertilizers.This way, the development of a new agricultural raw material originated from a rock thatalready exists in the country's soil is of great importance for the mineral and agriculturalsectors."

Jan 1, 2011

By Wellington Pereira Inácio, Frederico Muylaert Margem, Artur Camposo Pereira, Sergio Neves

"Natural fibers are currently gaining attention as reinforcement of polymer composites for uses in engineering parts for automobile and building construction. In spite of environmental, economical and societal advantages, the natural lignocellulosic fibers are not as uniform in their dimension and properties as compared to synthetic. In recent works it was found that the variation in strength could be correlate to the equivalent diameters for several lignocellulosic fibers including the sisal fibers. In the present work an investigation on a possible correlation of the equivalent diameter with changes in density and elastic modulus was carried out. Precise measurements of the equivalent diameter, conducted in a profile projector, were correlated with the density and the elastic modulus by means of the Weibull statistic analysis. The results showed that an inverse correlation with the diameter also applies for both the density and the elastic modulus with a high degree of precision. SEM observation of the sisal fiber in structure and fracture aspects strongly indicate that defects and microfibril participation could be responsible for the inverse correlation.IntroductionAccording to Kalia [1], cellulose-based fibers are currently being pushed owing to their ""green"" image. Contrary to synthetic glass fiber, extensively used in our modem technology, these lignocellulosic fibers are renewable and can be incinerated at the end of the material's lifetime without adding pollution in the atmosphere moreover, the amount of CO2 released during incineration process is negligible as compared to the corresponding amount taken up by the plant throughout its lifetime. Even if an industrial processing equivalent of C02 release is added, the lignocellulosic fiber is considered neutral with respect to the emission of gases responsible for the global warming [2]."

Jan 1, 2012

By Douglas M. Matson, Rongbiao Gu, Christopher San Marchi, Anil Saigal

"Hydrogen embrittles most structural metals, although the form and magnitude of embrittlement depends on the source of the hydrogen as well as the stress in the metal. Hydrogen fuel cell systems typically store gaseous hydrogen fuel at high-pressure, which provides both a source of hydrogen and high stresses in the containment materials. Understanding and measuring the effects of hydrogen on the mechanical properties of common structural metals, especially fatigue properties, is important for safe, long-term operation of such systems. This work explores the use of thermography to efficiently and quantitatively evaluate hydrogen-assisted fatigue of type 304 austenitic stainless steel. In particular, thermographic analysis was used with rotating-beam fatigue testing and shown to provide repeatable results which are in general independent of test cycle frequency while reducing test times by several orders of magnitude. The effects of hydrogen were studied by thermally precharging fatigue test specimens in gaseous hydrogen prior to thermography-assisted fatigue testing and then compared to testing of non-charged specimens. Hydrogen-precharging increased the strength of this type 304 austenitic stainless steel and increased the fatigue life by a factor of about 50-100.IntroductionThe world is facing a severe energy and environmental challenge: how to provide competitive and clean energy for its citizens in light of an escalating global energy demand and concerns over energy supply security, climate change and local air pollution. As a carbon-free energy carrier, hydrogen provides a promising vector for storing and distributing renewable energy. Hydrogen is an important industrial gas that is used extensively in many industries. However, with growing demand for clean energy, hydrogen fuel cell systems are being developed for use in consumer products, such as fuel cell vehicles, which changes the landscape for safe design of high-pressure gaseous hydrogen systems."

Jan 1, 2012

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2 versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Florian Kongoli

While calcium ferrite slags have been successfully used in continuous copper converting for the last 30 years, ferrous calcium silicate slag was proposed about 8 years ago as an additional alternative for copper smelting. Although both slags are normal extensions of each other their phase relations have not been completely clarified. In this paper the liquidus relations of both slags have been quantified at various areas that cover both of them. The existing experimental data have been first reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict various diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeOx-SiO2-CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO2 and Fe/SiO2 versus CaO as well as Fe/CaO versus Temperature and Fe/SiO2 versus temperature are proven to be much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams the effect of SiO2 and CaO on the melting temperature is quantified. The effect of Cu2O is also quantified through the model. Some Fe/CaO versus Cu2O and Fe/SiO2versus CaO at various copper contents are predicted and the results show good agreement with the experimental data. It is also shown that in the presence of liquid copper, Cu2O is dissolved in the slag depending on the oxidation degree of the system and might lower the liquidus temperature. Some discussions are also presented taking into account plant observations and important conclusions are drawn for copper smelting and converting

Jan 1, 2006

By Merete Tangstad, Eli Ringdalen

"In Norway ferrosilicon/silicon and ferromanganese production are strong with world markets of 4 % / 9 % and 4 %, respectively. Research and development in the academia mirrors the national interest; hence, there has been extensive academic research in these areas. There are some vital drivers and premises for a successful cooperation between the academia and industry with the main driver being a win-win situation for both. For industry,the potential advantages include cost-, competence- or environmental- benefits; for academia, the important drivers are building of competence and equipment, educating more students at higher levels, and increased possibilities to publish. In Norway, the benefits of cooperation between industry and academia are basic knowledge regarding thermodynamic and kinetic data, as well as reaction mechanisms within core processes. In recent years, such research interests have focused on the depletion of raw materials as well as environmental issues.IntroductionIn 1989, the Norwegian Ferroalloy Producers Research Association (FFF) was funded on the belief that a common research association would benefit the industry by making it easier to perform basic research as well as paving the ground for better recruitment to the industry. The funding partners in Norway were the FeSi/Si and FeMn producers. Today, the producers are Elkem, Finnfjord, Fesil, Wacker, Eramet and Vale. The main research partners working with FFF are SINTEF (Materials and Chemistry) and the Department of Material Science and Engineering at the Norwegian University of Science and Technology (NTNU). With more than 1700 employees, SINTEF is the largest independent research organization in Norway and NTNU is the largest technical university. Together, the two organizations provide an exceptionally strong materials technology research environment, and especially so for pyrometallurgical research."

Jan 1, 2012

By Reza Kamali, Mohsen Bashiri, Hadi Fanisalek

"Nomenclature: A: area (m2), C: heat capacity (WIK), cp: specific heat (J/Kg K), d: internal tube diameter (in), F: correction factor for multi-pass and crossflow heat exchanger, h: convective heat transfer coefficient (W/m2K), k: thermal conductivity (W/mK), L: length (m), m: mass flow rate (Kg/s), W: flow rate, N: number, Q: heat rate (W), R: thermal resistance, T: temperature (°C), U: overall heat transfer coefficient (W/m2K), ;1,,P: pressure drop (Pa), ;1,,T: temperature difference (°C), p: density (lb/ft3), N: number of tube passes, U,: velocity in tubes, iJh: head loss in feet of flowing fluid, Up: velocity in the pipe leading to and from the heat exchanger (ft/sec), µ: viscosity ( cp ), Llpf frictional pressure loss (psi/l 00 equivalent ft of pipe) Subscripts: b: baffle, c: cold, cf counter flow, ex: exchanger, f: fouling, h: hot, i: inlet-inner, ib: inlet baffle, lm: logarithmic mean, m: mean, o: outlet-outer, s: shell, t: tube, w: wall AbstractThe main bottleneck for primary aluminum production industry is dealing with a huge amount of input energy. The fact is that part of provided energy to aluminum production smelters will be lost as waste heat and it never used for aluminum production. One part of waste heat is escaping from the potroom exhaust gases, which was studied for possible recovery in a desalination plant to produce distilled water and the paper was presented in 2011 TMS Annual Meeting. However, it was shown that waste heat recovery plant to produce distilled water is highly profitable but the main fact is that the exhaust gases from potroom are highly corrosive, abrasive and dusty. The main challenge for desalination plant construction, which is using aluminum smelter exhaust gases as the main heat source, is the highly corrosive environment that makes the situation difficult and complicated for equipments design and plant construction. In this paper, we are trying to study a detailed investigation regarding the heat exchangers fouling, corrosion in heat exchangers including heat exchangers' material, how often we need to shut down the plant for maintenance or cleaning, and plant thermal efficiency with considering fouling."

Jan 1, 2012

By Lawrence D. May, Harry Mudgett

"In the course of developing a new industrial process, information produced at the Research and Development (R&D) stage is critical to determining the technical and economic feasibility of the project. Understanding the fundamental operating parameters for each unit operation in a flowsheet typically comes from historical knowledge of similar systems or by technical development through a robust research program. This approach holds true for processes incorporating fluidized-bed technology. In this paper, the authors will present a practical approach for performing a research study that will allow a process owner to determine if the concept of using a fluidized-bed system can become a reality. Included are discussions of key steps required at each level of the R&D program, and the critical information required for advancing the project to the next stage.IntroductionThe conduct of a research and development program typically starts with a process owner identifying a new industrial need or modification to an existing operation. The owner can pursue this need through multiple routes, including initial in-house development, coordination through an engineering firm, contacting suppliers of key equipment envisioned for the process, or through direct contact with research and development organizations. Where and when the project is conducted is as variable as the number and types of owners who pursue them. Factors that can influence the decision of where to conduct a research program can include the type of process desired, the scale and scope of the project, the location of the project site relative to the R&D options, the experience, capability, and availability of the potential research sources, and the costs to conduct the program. Often, the owner may choose a combination of the available resources to achieve their objectives. In the end, the owner's choice should be based on a thorough understanding of their goals and objectives for the program, and a good understanding of how to measure success while achieving those objectives. Herein, the authors will describe the methods we have typically used to develop the information an owner needs to make an educated decision for investing in a new or modified process."

Jan 1, 2014

By J. R. Bhamidipati, Nagy EI-Kaddah

"Over the years, mathematical modeling has been established as a viable tool for design and analysis of melting and solidification processes. Modeling of electromagnetic casting and melting systems involves three coupled problems -- determination of the containment field, the shape of the meniscus, and the temperature field -- which have to be solved simultaneously. One of the difficulties in numerical simulation of these systems is in defining and gridding the solution domain as the meniscus shape of the liquid region is not known a priori. This paper describes a methodology for solving these coupled problems in a two-dimensional electromagnetic containment field. This method is based on the solution of the electromagnetic, free surface dynamic, and heat transfer equations in a fixed domain in computational space by mapping the physical space into an invariant computational space during the search for the equilibrium shape using a variable non-orthogonal coordinate transformation. This approach, also, eliminates the need for regridding the liquid and solid regions during phase change. This methodology is demonstrated for two electromagnetic confinement systems -- the Magnetic Suspension Melting process and the electromagnetic casting of aluminum. The model predictions are in good agreement with available data for these systems. It is suggested that the methodology presented here is likely to provide a useful tool in the design, analysis, and optimization of electromagnetic confinement systems. IntroductionDuring the past decade, mathematical modeling has emerged as a viable tool for the design, analysis, and optimization of casting and melting processes /1-2/. It is generally recognized that the usefulness of modeling to study the interplay between the various process parameters without resorting to extensive experimentation relies heavily on accurate representation of the physical phenomena in these systems. In modeling electromagnetic confinement casting and melting systems, it is important that the model address all aspects of electromagnetic field interaction with the metal, if accurate predictions are to be obtained /3/. The electromagnetic field affects the heat transfer phenomena primarily through joule heating. In addition, the electromagnetic forces play a key role in heat redistribution in the molten pool via melt stirring, and, in confinement systems, support the molten metal pool."

Jan 1, 1994