By Hiroyuki T. Takeshita

Ca-Ni based alloys were investigated on structures, hydrogenation properties and the effect of additive elements on hydrogenation properties. CaNi, samples were decomposed to form a new hydride with a CsCl-type structure on the constituent metal atoms at high temperatures such as 673K in a hydrogen atmosphere. The candidate of the third element which was added to stabilize the original compound was investigated by using the Miedema's semi- empirical model and, as a result, Pd was chosen. The hydrogenation of CaPd was conducted with a Sieverts' type apparatus and the synthesis of Ca-Ni-Pd ternary alloys was performed by high frequency heating.

Jan 1, 2002

By L. Cifuentes

Electrodialysis (ED), i.e. a technique based on the effects of electrically charged membranes on ions in solution in an electric field, has been applied to Cu-Fe-As-Sb- H2SO4 electrolytes similar to those used in copper electrorefining and electrowinning operations. The effects of current density, time and species concentration have been studied in a batch ED cell. The technique has shown to be effective in concentrating and separating a range of ions and points to possible new methods of treating copper electrometallurgy effluents.

Jan 1, 1999

By Ann M. Hagni

"Ceramic matrix composites are inorganic materials that are particularly resistant to heat and abrasion. A magnesia (MgO) and aluminum nitride (AlN) based composite is formed by exposing a magnesia preform to a metallic alloy block in a nitrogen atmosphere at 950°C. The metallic alloy, which is composed primarily of aluminum, is wicked into the preform. Aluminum nitride matrix is grown between MgO particles as the wicked metallic aluminum reacts with nitrogen. Unused metallic alloy, remnant metallic alloy (carcass), and composite produced after 8 hours, 50 hours, and 225 hours of processing are characterized mineralogically. Reflected light microscopy, transmitted light microscopy, scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction techniques reveal that in addition to anhedral to euhedral AhNi, AbSbSr, and Al crystallizing in the metallic alloy carcass, AIN and (Al,Si)N have formed as well. Nitride rings and nodules in the carcass may hinder AIN growth in the composite. Fine-grained residual AhNi and AhShSr are dispersed throughout the composite matrix. The nitride matrix is composed of AIN and (Al,Si)N. Rim replacement of MgO by spine! occurs in the composite. Aluminum nitrides in the metallic carcass cathodoluminesce deep violet-blue, unlike non-luminescent AIN in the composite matrix. This distinction in cathodoluminescence suggests a different mode of formation for composite AIN than for carcass AIN. Phase interpretations and textural characterizations deduced from the implementation of sophisticated mineralogical techniques have contributed to the understanding, and will aid in the improvement, of MgO/ AlN-based ceramic matrix compositeprocessing."

Jan 1, 1999

By Jorge Alberto Soares Tenório, Victor Bridi Telles, Denise Crocce Romano Espinosa, Felipe Fardin Grillo, Vicente de Paulo Ferreira Marques Sobrinho, José Roberto de Oliveira

"This research aims to study the process of incorporation of the metal iron in electric arc furnace dust (EAFD), from a steel mill producing long steel by liquid iron in addition to the changing temperature of 1400 degree Celsius altering experimental conditions such as how to add the EAFD (as received and in the form of briquettes), the percentage of EAFD to be added (10, 20 and 30% of initial weight of sample pig iron) and the time of withdrawal of the sample of pig iron and slag (30 minutes after the addition of EAFD). Previously, the EAFD will be characterized using the following techniques: chemical analysis, particle size analysis, X-ray diffraction, scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) microanalysis. After characterization, the eletric arc furnace dust to be added to the bath of liquid iron, will be divided into 2 types: the first order of addition will be in the form ""as received"" from the plant and the second is through the agglomeration of EAFD in the form of briquettes. The achievement of fusion experiments in laboratory scale, will take place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of the metal iron will use graphite crucibles. A flow of inert gas (argon) will be maintained inside the furnace during the experiments. It is expected that the results obtained at the end of the research allow the evaluation of the iron metal incorporation of eletric arc furnace dust in hot metal bath.IntroductionThe steel industry generates a variety of solid wastes, liquid effluents and gaseous emissions at various stages of processing. The electric furnace dust (EAFD), generated in electric arc furnaces, represents a major problem for their content of chemical elements such as zinc, iron, chromium, cadmium, among others, issued to the atmosphere during the manufacture of steel[1]."

Jan 1, 2012

By Fuqiang Guo

Scorodite (FeAsO4, 2H2O) is suitable mineral carrier for immobilization of arsenic-rich wastes. Its stability is, however, highly pH dependent (typically at 4 ≤ pH ≤ 7) and satisfactory only under oxic disposal conditions. In thiswork an encapsulation process using mineralized gels of aluminum hydroxy-oxides is developed to enhance the stability of scorodite under wider pH and redox potential range conditions. The encapsulation involves blending and ageing of synthetic scorodite produced by McGill’s atmospheric scorodite process with aluminum hydroxyl gels derived from controlled hydrolysis of aluminum salts. The amorphous hydrolyzed Al-gel encapsulates the scorodite particles,which upon short-term aging transforms into crystalline Al (OH)3/AlOOH mineral phases providing a robust protection microscopic barrier. Long-termstability testing demonstrates the encapsulation systemto be highly effective in suppressing arsenic release under either oxic or anoxic (100 mV < Eh < 600 mV) potential and neutral-alkaline pH (7 ≤ pH ≤ 9) ranges.

By Joo Hyun Park, Soo Sang Park

The distribution behavior of Pb between molten copper and FetO-SiO2 (-CaO, Al2O3) slags was investigated at 1473 K (1200 oC) and p(O2)=10-10 atm in view of the reaction mechanism of Pb dissolution into the slag. The distribution ratio of Pb (LPb) decreases with increasing CaO content (~6 mass pct) irrespective of Fe/SiO2 ratio (1.4~1.7). However, the addition of alumina into a slag with Fe/SiO2=1.5 linearly decreases the LPb, whereas a minimum value is observed at about 4 mass pct Al2O3 at Fe/SiO2=1.3. The log LPb continuously decreases with increasing Fe/SiO2 ratio, and the addition of Al2O3 (5 to 15 mass pct) into the silica-saturated iron silicate slag (Fe/SiO2 < 1.0) yields the highest Pb distribution ratio. The log LPb linearly decreases by increasing the log (Fe3+/Fe2+) value. The Pb distribution ratio increases and the excess free energy of PbO decreases with increasing Cu2O content in the slag. However, from the viewpoint of copper loss into the slag, the silica-saturated system containing small amounts of alumina is strongly recommended to stabilize PbO in the slag phase at a low Cu2O content.

Jan 1, 2014

By Xinghui Meng

The leaching behavior of platinum powder in .iodide solutions under oxygen pressure in an autoclave was investigated. Ammonium salts were added to the leaching solution at neutral pH as a key lixiviant for platinum. The effect of temperature, partial pressure of oxygen, concentration of iodide and of arttmonium salts on the dissolution rate of platinum was examined. Under experimental conditions, the leaching behavior of platinum powder exhibited a complex reaction mechanism. A precipitate was found during the leaching process and was identified to be platinum ammine iodide, Pt(NH3hI4. The dissolution rate was controlled by a series of chemical reactions, the equilibrium concentration of the platinum ammine iodide being responsible for the ultimate limit to the recovery.

Jan 1, 1996

By David R. Jessey

An ore microscopic and geochemical study of the nickel-cobalt occurrence in the Southeast Missouri Mining District has revealed several significant relationships. Siegenite [(Ni,Co)3S4] is the dominant nickel-cobalt sulfide in the ores, however, several other members of the thiospi¬nel group (AB2S4) occur: carrollite (CuCo2S4), nickelean carrollite [(Co,Ni,Cu)3S4], fletcherite [Cu(Ni,Co)2S4] and polydymite (Ni 3S4). In addition, bravoite [(Ni,Fe)S2], vaesite (NiS2), millerite (NiS) and gersdorffite (NiAsS) are present. Thiospinel composition varies dramatically within the district. Paragenetic studies have shown that the stratigraphically lowest thiospinels are the most cobalt-copper-rich. A detailed ore microscopic study of the AMAX Lead Company Buick mine has also shown significant changes in mineralogical association, texture and grain size of the siegenite along the north-south strike of the major ore bodies. Siegenite commonly replaces and veins chalcopyrite and is subsequently replaced by sphalerite. Less commonly, siegenite and chalcopyrite are observed to form linear replacements along sphalerite grain boundaries. The grain size of the siegenite varies markedly, but in a predictable north-south pattern that is consistent with a genetic model formulated from geo-chemical data. The compositional as well as textural trends displayed by the thiospinel mineralization could be exploited to optimize recovery of any or all thiospinels of economic interest.

Jan 1, 1981

By J. Priede, G. Gerbeth

"Two different instability mechanisms of electromagnetically levitated bodies are analyzed. The first is due to the virtual coupling between the electric current passing through the magnetic system and the variation of position of the body. This mechanism can result in unstable mass center oscillations of a levitated solid body. Another type of instabilities may occur because of the coupling between the motion and the electric currents induced in the body. This effect can cause a spontaneous rotation of the body setting in as the frequency of the alternating magnetic field exceeds certain critical threshold depending on the configuration of the field. This instability can be suppressed by an axial steady magnetic field of strength comparable to that of the levitating field. 1 IntroductionAn alternating magnetic field interacting with eddy currents induced in a conducting body causes repulsion between the body and the coil generating the field. Besides, the eddy currents provide a contactless heating of the body. In such a way metallic samples can be levitated and melted without a contacting crucible. This technique allows to avoid contamination of the melt with container material and so to achieve a considerable super-cooling of the melt before it solidifies. Nowadays electromagnetic levitation is widely used in material research for measuring of the thermophysical properties of molten metals (2) .It has been observed since early fifties when the first experiments on the electromagnetic levitation were done that under certain circumstances solid levitated samples start to rotate or oscillate [l]. Surface oscillations can appear in addition when the sample is melted. Such phenomena are undesirable because they often result in failure of the levitation. Recently we showed that rotational as well as oscillatory instabilities can have electrodynamic origin related to additional eddy currents induced by motion of the body in an alternating magnetic field [3] , [4].In the first part of the present paper we analyze another possible cause of oscillatory instability due to the coupling between the electric current passing trough the magnetic system with variation of the position of the levitated body. The second part of the paper deals with the origin and suppression of rotational instability in a uniform alternating magnetic field."

Jan 1, 1999

By Toshia Ishii, Jun Kubota, Noriko Kubo

"For steel continuous castings, it is essential to control molten steel velocity at the meniscus, since the velocity is closely related to surface defects on the resultant products. Argon gas is supplied with molten steel into the mold through the submerged entry nozzle to prevent nozzle clogging. In this study, to investigate the influence of argon gas on molten steel flow, a numerical simulation was carried out by a two-phase model. Simulation results indicate that as argon gas bubbles ascend near the nozzle by their buoyancy, they induce the molten steel flow with them and resulted a meniscus molten steel flow from the nozzle to the narrow face of the mold. This flow direction is opposite to the case without argon gas. The calculated data are compared with the experimental data. The comparison shows generally good agreement between the measured and the calculated data. IntroductionIn a steelmaking process, molten steel carried by a ladle is first fed into a buffer vessel called tundish. From the tundish, it is then fed into a continuous casting mold. Molten steel solidifies gradually in the mold (the primary cooling zone) forming a solidified shell. As the solidified shell is just thick enough to support the molten steel at the mold exit, it is withdrawn through the mold by pinch rolls. It is progressively thicken as it is further cooled with water sprays in the secondary cooling zone. At the end of guide roll zone, completely solidified steel is cut into desirable lengths. Schematic view of a typical continuous casting is shown in Figure 1."

Jan 1, 1999

By Michael K. Rhodes

A 120 tonne per day BacTech bacterial oxidation plant treating refractory gold concentrates for Gold Mines of Australia&apos;s Youanmi project in Western Australia commenced operation September 1994. This was the first commercial application of the BacTech process. A pilot plant trial on concentrates produced from Youanmi ore was carried out at BacTech&apos;s laboratory in Perth. Results and measurements from this trial were used by Signet Engineering Pty Ltd to design the commercial plant. This paper cover the results obtained from the piloting, their implementation in the plant design and the initial commissioning of the full scale plant.

Jan 1, 1995

By John J. Moore

This paper discusses the application of a video technique to construct stability diagrams for the combustion synthesis of ceramic-metal composites. Several model exothermic combustion synthesis reactions have been used to investigate the effect of the reaction parameters, eg. stoichiometry, green density, etc, on the stability of the propagating combustion reaction front and subsequent product morphology. The effect of varying the reactants and their stoichiometry to provide a range of reactant and product species ie. solids, liquids and gases, in the synthesis of both dense and expanded (foamed) ceramic and ceramic-metal composites was also investigated with respect to their corresponding combustion front stabilities.

Jan 1, 1993

By Xiaoming Huaa

The effect of the anodic polarization on the composition and morphology of the surface layer formed on chalcopyrite during ammonia–ammonium chloride leaching was investigated. The anodic polarization on the chalcopyrite electrode was used for oxidation and dissolution of chalcopyrite, and the resulting oxidized layers were characterized by XPS, SEM and optical microscopy. The results show that oxide layers exist on the chalcopyrite surface with or without any anodic polarization in the leaching solution at ambient atmosphere. However, the composition and morphology of the layers are strongly depended on the extent of polarization. The distribution of FeOOH and Fe2O3 within the oxidized layer was inhomogeneous for the sample at the open circuit potential (OCP). The composition and morphology of the oxidized layers which were formed at anodic potentials lower than 0.3 V versus SCE were similar to those of the chalcopyrite at the OCP. At anodic potentials above 0.4 V, the oxidized layers contained many cracks, and they were fragile and exfoliated. Furthermore, the sulfide had been oxidized to sulfur species with higher oxidation states. The oxidation of the chalcopyrite seemed to undergo a cyclically oxidative process that suggested growth and spallation of oxidation layers on chalcopyrite in a layer-by-layer sequence.

By Goren Lindkvist

Elkem has a small industrial scale. Muti-Purpose furnace at the MEFOS Metallurgical Research Facility in Lulea, Sweden. The furnace is 2 meters in diameter with installed power of 4.8 MVA, equipped with oil coiled freeze lining, gas tight electrode seals and feed chutes and a slag flow control for continuous tapping. During tests in June, 1991, the furnace was continuously operated on a high silica slag at loads from 1.5 to 4,0 MW. The slag was then charges to a low silica, high iron and lime composition. Steel plant dust was added, smelted and reduced. The slag was made more ceramic by adding alumobrick and alumina. Data from the start-up and initial operating phase of the, Elkem EAF dust plant at Laclede Steel will also reviewed.

Jan 1, 1992

By Georgina De Micco

The National Commission of Atomic Energy is investigating a suitable physicochemical process for the conditioning of spent nuclear fuel and treatment of the scrap of research reactors of the Al-UxSiy type. A possible way of processing is through dry chlorination of the cladding with the purpose of selective separation of the aluminium from the remaining elements such as Fe, Ni, Zn, Cu, etc. transforming them into volatile chlorides. Some important advantages of this method are the thermal stability of the chlorides that allow the easy separation of the halides by physical methods and the low volume of radioactive waste generated. The interactions in the following systems were studied in the range of temperature between 150º-500°C: Al-Fe, Al-Ni, Al-Cu, Al-Zn, Cu-Zn and the pure metals. We found that the reactivity was different depending on if the elements were alloyed or separated. The separation factors of the systems under study were determined. Nickel is perfectly separated from aluminium for all temperatures, whereas good conditions for copper separation were achieved below 400ºC. In the case of iron, complete isolation was never attained. However, by decreasing temperature to 150ºC it is possible to obtain aluminium chloride with less iron content. The separation of zinc from the product was also difficult. It was detected that zinc chloride volatilization decreases when other chlorides were present, for example cooper chlorides. In the Cu-Zn alloy, zinc chlorides remained in the condensed product due to interactions with copper. The samples were characterized by scanning- electron microscopy (SEM), X ray diffraction (XRD) and atomic absorption.

Jan 1, 2006

By Qiang Yu

This paper reports on a research project supported by NSF, which aims at developing a multi-scale methodology for systematic microstructure prediction in thermo-mechanical processing of metals. This methodology is based on combining mesoscopic microstructure models with macroscopic process formulations and involves the following three main steps: (I) based on the given global processing conditions, the gross deformation patternof the entire workpiece is modeled using a continuum-based algorithm, (2) the resulting parameters are then extracted from the continuum-based simulation, post-processed and passed on to the mesoscopic numerical module, and (3) the microstructural changes are finally modeled at the mesoscopic scale. This approach is expected to overcome the disadvantages of current microstructure prediction practice employing empirical relationships between microstructural features and processing parameters. Keywords: Thermo-mechanical processing, Microstructure, Grain growth; Recrystallization; Mesoscopic models; Finite Element Method

Jan 1, 2003

By L. B. Tsymbulov

Sulphide melts formed in the course of smelting of nickel and copper-nickel feed (matte) actually are sulphide-metallic melts since sulphur contained in the melts is in deficiency with respect to metals. The level of metallization is rather relevant feature of sulphide melts and is widely used in calculating material and heat balances for pyrometallurgical processes. Despite of the above parameter? importance, the investigators have no single opinion on what should be understood under metallization level and the method of its determination. In the present study we present the results of our own experimental and theoretical researches that have allowed determination of some mechanisms of sulphide melts? crystallization. Based on the mechanisms revealed new scientifically justified approach has been offered for determining level of metallization of the components present in sulphide melts. It has been demonstrated that sulphur distribution between the melts is substantially different from generally accepted concept.

Jan 1, 2006

By Thomas Prietl

The use of gas stirring systems through the furnace bottom is common for anode and holding furnaces in the copper industry The first implementation of a gas stirring COP KIN® system in a Peirce-Smith converter was performed at the New Boliden smelter, Rönnskar, Sweden. In addition to other benefits, a decrease in process time and a decrease of the oxygen content in the blister copper were observed. To determine the effects of the gas stirring system and the process endpoint, an optical production control ?Semtech OPC system? was used. The light emission of the converter flame as an optical process parameter provides qualitative on-line process information, and is also used for endpoint determination of the slag making process, on-line control of iron content in white metal, quality control of slag etc. The results, benefits and risks of using the COP KIN® and OPC system for a Peirce-Smith converter are reported.

Jan 1, 2005

By T. C. Tseng

Austenitization is a critical stage in heat treatment of steels. The available kinetic data in reference to various initial microstructures are very limited, particularly at high heating rates. In this study, integrated experimental and computational approaches have been conducted to quantify the progress of austenitization and the attained microstructure. In particular, the study is concentrated on cementite and carbide dissolution in two steel grades. Various computational methods are developed to facilitate the study: (l) an algorithm for direct determination of kinetics data as well as progress of transformation from high-rate dilatometer tests; and (2) a suite of mesoscale computational models for particle dissolution, elements diffusion, mechanics, thermodynamic and the resulting kinetics of transfonnation. Critical exprimentation is carried out using advanced techniques in microstructure characterization, chemical analysis, and Gleeble thermal-mechanical simulator on specimens of well-controlled initial microstructures. Keynotes: Cementite, Carbite, Dissolution, Steels, Austenitization

Jan 1, 2003

By Hai-Xing Fang, Chao Liu, Tao Zhang, Bing Xie, Hong-Yi Li, Cui Li

"Hongge Ore, a kind of vanadium-titanium magnetite ore containing high content of chromium, is valuable resource for extracting Fe, V and Cr in China. During present processing of the ore, vanadium and chromium were both concentrated in slag, leading to higher content of chromium in the vanadium slag than that of common one in Pan-Steel. Mineral phases and characteristics of spine! crystals, which influenced greatly subsequent roasting process, in the vanadium slag under different cooling conditions were investigated by using XRD and SEM/EDS. Results showed that vanadium slags containing various contents of chromium were composed of spine!, in which V and Cr were both concentrated, olivine and pyroxene. Growth rate of spine ls decreased sharply below 1350°C. The non-isothermal crystallization process could be described by modified Avrami equation and Ozawa equation. Avrami exponent and Ozawa index were calculated and growth mechanism of spine! crystals was discussed.IntroductionVanadium (V) as well as chromium (Cr) is important non-ferrous metal widely used in materials and chemical industries [1, 2]. Especially, both of them are important alloying elements for the production of high alloyed steels to achieve desired physical-chemical and mechanical properties. Vanadium-titanium magnetite ore in Panzhihua-Xichang area (China) is an important raw material for extracting vanadium. During the extracting process, vanadium is firstly reduced into hot metal and then concentrated in slag phase by blowing oxygen into the hot metal in converter [3]. This kind of slag containing 5~20 wt% V20 3 are usually roasted with sodium or calcium salts and then leached to obtain vanadium containing solution and final products. Current vanadium slag obtained from normal vanadium-titanium magnetite ore contains low content of Cr20 3 and chromium extraction is thus ignored. However, chromium content in the vanadium slag would be increased intensively when the Hongge Ore used, which is also important vanadium titanium magnetite in Panzhihua-Xichang area containing 0.2~0.8 wt% Cr203. Therefore, this kind of vanadium slag with high content of chromium would also be important sources for vanadium and chromium extraction. According to previous work [4], both vanadium and chromium could be extracted from vanadium slag with high content of chromium by salt roasting and leaching, which is illustrated in Fig.1."

Jan 1, 2013