By Feng Wang, Guojing Shi, Yangyang Xie, Zizong Zhu, Qiang Wu

The coal chars from northwestern part of China are characterized with high reactivity and low strength after reaction. Four type of coke-making coals selected from northwestern part of China were studied by proximate analysis, ultimate analysis, vitrinite reflectance analysis, and FTIR with curve-fitting analysis to obtain information on their chemical composition and chemical structure. The results show that the studied coals have relatively high values of final contraction of coke residue index (x) and relatively low values of maximum thickness of plastic layer (y) and average vitrinite reflectance. Based on the curve-fitting analysis of FTIR spectra, the aliphatic carbon (Cal), the aromatic carbon (Car), and the molecular structural parameters such as CH2/CH3, fa, Hal/Har, and (R/C)u are determined. The results of curve-fitting analysis indicate that the studied coals are characterized by a large amount of oxygen-containing functional groups and aliphatic side chains.

Mar 1, 2018

By Zhouhua Jinag

The attempt has been made to manufacture high nitrogen austenitic stainless steels by pressurized electro-slag remelting furnace with maximum nitrogen pressure of 7MPa. To obtain high nitrogen content in steels, the compound electrodes with different nitrogen sources (FeCrN, Si3N4) were prepared. Using the Si3N4 as the nitrogen alloying source, the silicon contents in ingots were prone to be out of the specification range, and the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved using FeCrN as nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen above 1.0wt% could be obtained. A series of high nitrogen austenitic stainless steels have been successfully developed by this method. The mechanical and pitting corrosion resistance properties of high nitrogen austenitic stainless steels were investigated. The results show that the steels exhibit excellent mechanical and pitting corrosion resistance properties.

Jan 1, 2009

By Jesús Contreras

Within its programme for continuous improvement and cultural change, Atlantic Copper has installed the Six Sigma methodology as a basic tool for the improvement of management techniques in all its production centres. Following an implementation period, the methodology is widely used for analysis and improvement, not only in the fields of production and maintenance, but also in other areas of the business such as supplies or energy management. The present paper describes, phase-by-phase, the project that was developed to improve the quality of converter slag through the application of Six Sigma techniques, from the initial set up to the final results obtained.

Jan 1, 2005

By Ken-ichi Machida

"Surface modification of R-Fe-N intermetallic compounds was made to improve their magnetic property and nitrogenabsorbing ability, arid high-performance resin-bonded magnets and nitrogen storage materials were developed: Surface coating for Sm2Fe11Nx by the zinc metal produced via photodecomposition of Zn(C2Hs)2 was effective to avoid the further oxidation in the molding process of the fine powders for bonded magnets and the resulting (BH)max values were improved to -186 kJm-3. Meanwhile, R2Fe17 as the mother compounds for RzFe11Nx was highly active for decomposition of NH3 molecule and subsequent nitrogen absorption as metal nitrides. Furthermore, even inert Nz molecule was dissociated on them by impregnating Ru metal and the resulting nitrogen atoms were absorbed in the crystal lattice of R2Fe17. These results demonstrated that the nitrogen storage system was established by cycling the nitrogenation and hydrogenation of RzFe11/R2Fe11Nx materials.IntroductionProcessing for rare earth metals and intermetallic compounds requires well-controlled conditions in order to avoid the oxygen contamination involved in it due to their high reactivity, as causes the serious damage for materials such as magnets, metal hydride for hydrogen storage, and so on. Rare earth-iron intermetallic compounds, R2Fe17, provide the corresponding metal nitrides (R2Fe11Nx) by heating in N2 or a mixed gas stream ofNH3-H2 [l] and, among them, Sm2Fe11N3 has been particularly noted as one of the promising materials for high-performance permanent magnets such as bonded ones [2- 6]. Usually, the nitrogenation for Sm2Fe17 is made in Nz, but it needs the much more hard conditions of reaction pressure (-10 MPa), temperature (-550°C) and time (-72 h) than the nitrogenation in the NH3-H2 mixture [l]. In the latter case, a significant amount of nitrogen can be interstitial introduced in· the R2Fe17 crystal lattice (x=-7) under the more moderate conditions than in N2 (at 0.1 MPa and -450°C for -3 h) [3-6] and then, in a similar manner as metal hydride systems [7], the excess nitrogen in RzFe1 7Nx (x>3) is reversibly desorbed by heating at a temperature around 500°C in Ar to form the RzFe11N3 compounds. This behavior of nitrogen absorption and desorption has a close relation to the sites for nitrogen in the crystal lattices."

Jan 1, 2000

By Timothy W. Ellis, John A. Howes

The production of lead-acid batteries is defined by a closed-loop product life-cycle. Active material and grid alloys converge on an adaptable specification that improves both performance and recyclability. This mapping of product requirements for lead-acid batteries has taken over 80 years to develop. But, as the use of batteries made with other chemistries continues to grow, the need for a comparable life-cycle management process becomes increasingly apparent given societal needs to manage raw materials, e.g. the European Union Battery Directive recycling targets. What has taken more than 80 years for lead-acid to evolve in a closed-loop paradigm must now be accomplished in less time for batteries using other chemistries and technologies. End-of-life costs are embedded in the product cost of lead-acid batteries. However, end-of-life costs are not reflected in the product cost of batteries made with other chemistries. Those costs are borne by other constituencies with often inefficient and environmentally damaging results. Lead-acid is a materials technology management model for other products.

Mar 1, 2017

A comprehensive numerical capability for the analysis of Thermal Spray (TS) systems consisting of a three-dimensional compressible, turbulent flow Navier-Stokes model and a multi-phase particle flow model in Lagrangian formulation, was developed. This capability is validated for a set of flow conditions typical for TS. The developed methodology is used for analysis of the JP-5000 TS gun gas and coating powder flow conditions. Modeling and analysis of particle/turbulent eddies interaction is performed. Details of gas flow field, particle temperature, and particle velocity histories, and particle temperature, velocity profiles in the system are presented. For the validation of numerical analysis, the computed results are compared with available experimental measurements. The flow phenomena for different flow parameters are analyzed and explained as the results of gas dynamics and heat and momentum transfer between the gas and particle phases. This methodology can be used for process control and reliability improvement, and has the potential to significantly improve TS gun performance through control of its parameters.

Jan 1, 1996

By Norbert L. Piret

From the copper smelter operation a various outputs are to exert negative impacts on the environment. Particularly, emissions like SO2 and dusts, solid wastes like contaminated gypsum and arsenic sludge, effluents and heated cooling water are generated. Most countries have sitipulated an environmental legislation to provide the framework for an efficient environmental management. As part of the planning activities for x major greenfield copper smelter, the Following elaborations are required and were drawn up. -The Environmental Impact Assessment which is the first step of environmental management and mandatory for every new project. - The Environmental Monitoring Plan, which describes the monitoring procedures for the main impacts identified and assessed. -The Environmental Management Plan, which deals with the minimization of environmental impacts, and the methods of its implementation.

Jan 1, 1996

By H. -P. Behrendt

Muldenhiütten Recycling und Umwelttechnik GmbH is a lead smelter with a very long tradition. The first reference to the existence of smelters on this site is given by a document of inheritance dated 1318. Originally run as a primary lead smelter, which was supplied with ores from the Freiberg mining district and from overseas, it was required to change it over to secondary raw materials due the abandonment of mining in the Freiberg area in 1968. Today, Muldenhüitten Recycling und Umwelttechnik GmbH has two production lines; lead production from secondary lead and waste incineration, which are closely connected and gain advantage from each other. Installations, improved technologies, and the highly skilled personnel have contributed to satisfy all demands for a production concerning quality and environment.

Jan 1, 2000

By Signe Kjelstrup, Leiv Kolbeinsen, Marit Takla, Odne Burheim

"This paper presents a Seebeck-type solid state thermoelectric power generator unit, designed to investigate the possible recovery of radiant waste heat at a silicon plant in Norway where roughly 703 of the total input energy leaves the process as waste heat. The unit is 0.5 m x 0.5 m and is built of 36 commercially available thermoelectric devices based on bismuth telluride p - and n - type semiconductors. Thermoelectric devices directly convert fractions of a heat flux into an electric current (and vice versa) and may therefore be convenient for recovery of waste heat when the heat source is discontinuously available. The purpose of the thermoelectric unit is to give a proof of principle of direct thermoelectric energy conversion on a large scale. We present the initial test results for the generator. At an average temperature difference between the heat reservoir and the heat sink of 98°C, we measured an open ciruit potential of 23.44 ± 0.06 V and the matched load power output was 39.4 W. At a temperature difference of 220°C, we predict the generator open circuit potential to be 40.8 V, which corresponds to an efficient Seebeck coefficient of 242 µV /K, and matched load power output to be 120 W.IntroductionThe world's power demand increases, driven by population growth and increase in living standards and simultaneously global warming is recognized as one of our most serious environmental problems. According to the International Energy Agency[l], the industrial sector accounted for approximately one third of the total global power consumption in 2005. Increasing the energy efficiency of industrial processes thus represents a benign and substantial route for addressing environmental concerns and energy security.In accordance with the second law of thermodynamics, all real processes are associated with lost work which is energy being dissipated as heat to the surroundings[2]. Improving the energy efficiency of industrial processes is about finding the process path associated with a minimum of lost work. The more evenly the losses are distributed, the smaller are the losses [3, 4]. In addition, exploiting the unavoidable waste heat will contribute to improve the energy efficiency. The waste heat may be utilized for heating purposes and/or it can be upgraded to work for instance via some sort of heat engine."

Jan 1, 2012

By C. R. Palmer

The Bureau of Mines investigated the use of ion-exchange technology for the recovery of precious metals from cyanide leach and spent electrolytic solutions. This research included adsorption of gold and silver on both weak-and strong-base anion-exchange resins. The effects of nickel, mercury. and iron on precious metal loading of strong-base resins were also determined. Due to the nonselectlvity of strong-base resins, selective elution also was investigated. Both commercially available and experimental weak-base anion-exchange resins were tested. None of the commercial weak-base resins tested were suitable for a caustic-cyanide system owing to their low recovery of precious metals at pH 10 or above; however, three experimental resins have possible application. Continuous tests conducted with mill cyanide solution in a multicompartmented ion-exchange column using strong-base anion-exchange resins adsorbed nearly 100 pct of the precious metals as well as the iron and nickel. During the elution of this loaded resin the iron was first removed with NaCI plus NaOH; then nickel with dilute H2S04 or HCl; finally gold and silver with thiourea in dilute HCl.

Jan 1, 1988

By Thomas J. Keefe, O&apos

Results of metal electrodeposition experiments conducted at the University of Brussels and University of Missouri-Rolla over the past few years are reviewed in terms of the relationship and impact on industrial processes. Examples are cited from common electrowinning, electrorefining, or electroplating operations for copper, zinc, nickel, cobalt and silver. The following topics are considered : metallographic structure, crystallographic texture, surface morphology, nucleation and growth, additive monitoring and effects, high current density, substrate related properties including adhesion. The studies were conducted on a variety of scales from laboratory beaker tests to full sized pilot and industrial operating plants.

Jan 1, 1993

By Deventer Johanna van

Ore bodies around the world are declining in grade, whilst increasing in complexity. The level of impurities relative to the valuable metal is steadily increasing, posing new challenges to existing operations. Ion exchange is widely used in the hydrometallurgical industry for both primary recovery of metals and the removal of impurities. The superior selectivity of ion exchange resins makes them exceptionally suitable for the removal of target impurities to very low levels, thereby saving operating costs, increasing the value of the final product and significantly improving revenue. The ion exchange process in these applications is very simple, using standard ion exchange equipment and acid regeneration. The process can be fully automated, requiring minimal operator interference and supervision Examples of impurities that are successfully removed via ion exchange include iron, antimony and bismuth from copper electrolyte. In the copper electrolysis process, antimony, bismuth and arsenic tend to form slimes which are dispersed in the electrolyte. These slimes contaminate the cathode and/or decrease the quality of the copper deposition. A special chelating resin was developed to remove antimony and bismuth, while at the same time ensuring minimal chloride leakage to the sulphate matrix. The work is described in more detail in this paper. Ion exchange is also used to remove copper, zinc and nickel from cobalt electrolyte. This paper addresses a few of these examples in more detail.

By Rina Kim

The addition of lead to a gold leaching reactor can effectively accelerate or retard the gold cyanidation reaction. This study explored the effect of lead on the gold dissolution kinetics using cyclic voltammetry (CV) experiments. It was illustrated that the gold leaching kinetics in the cyanide solution enhanced with the addition of lead salt in the low overpotential region (–0.35 V vs. Ag/AgCl). The similar behavior was observed in the presence of ore containing 0.25% galena. In contrast, the gold oxidation kinetics retarded at –0.35 V (vs. Ag/AgCl) in the presence of silicate and lead-bearing mineral under certain conditions. Likewise, the lead addition was not functional for the high sulfur ore. This was attributed to the oxidation of the sulfides to the elemental sulfur, which subsequently formed a passivating layer on the gold surface. The results were evidently affirmed by the electrochemical tests and X-ray photoelectron spectroscopy (XPS) analysis.

By M Philip Schwarz

"This paper reviews the status of computational modelling of a variety of common metals reduction processes, namely the blast furnace, rotary kiln and fluidised bed, and one new process not yet commercialised, namely smelting-reduction as in the HIsmelt Process. In each case, the last decade has seen the emergence of the capability to simulate the processes using multi-phase reacting computational fluid dynamics techniques. In some cases this capability is still in the process of being developed, and the next few years will see the maturing of the modelling techniques. As they become established, it will be possible to apply them to further refine the older technologies such as blast furnaces and rotary kilns, and assist in the optimisation, commercialisation and acceptance of the newer technologies such as fluidised bed and molten bath reduction. The development of a computational fluid dynamic model of bath smelting-reduction is described in some detail to illustrate how a large number of complex and interacting phenomena can be successfully simulated within a CFD framework. IntroductionPyrometallurgical reduction processes, such as the iron blast furnace, have become increasing more sophisticated through the centuries, so that today they are often highly efficient. There are continuing pressures, however, to refine existing processes and develop new ones. The imperatives are often economic, given that the long-term trend in the price of metals is always downward. In recent times, there has been the additional need to improve the environmental impact of metal production. Given that they almost inevitably require the use of carbon, metal reduction processes are large sources of greenhouse gases, and even a relatively small improvement in efficiency can be valuable in reducing CO2 production. Local environmental issues, such as the need to control of particulate emissions, are also driving incremental improvements in equipment.In addition to the economic and environmental drivers mentioned above, new process development is also being driven by the need to process new ores, and the need to produce unrefined metal in a form more compatible with alternative routes for downstream processing. An example of the latter is the production of DR! (Direct Reduced Iron) as a feed for EAF Electric Arc Furnace) in mini-mills.Further improvement of processes that have already been honed by continual plant experimentation over many years is not an easy task. To deliver further gains in efficiency, throughput, or product quality requires a highly sophisticated tool: one such tool· is computational modelling."

Jan 1, 2001

By Kazutoshi Haga, Atsushi Shibayama, Altansukh Batnasan

This study presents a viable approach for recovery of precious metals such as gold (Au), silver (Ag), palladium (Pd), and base metals, including copper (Cu), nickel (Ni), cobalt (Co), lead (Pb) and zinc (Zn) from waste printed circuit boards (WPCBs) via iodine-iodide leaching and precipitation. The behaviours of dissolution and precipitation of precious and base metals during iodine-iodide leaching and precipitation processes were discussed. Sodium hydroxide (NaOH) was used to remove base metal impurities exist in the pregnant leach solution under alkaline conditions. Precious metals remained in the resulting solution from NaOH precipitation were recovered by reduction using ascorbic acid (L-AA) solution. Results show that under optimum leaching conditions, almost all (> 99%) of Au was dissolved in an iodine-iodide solution when the dissolution efficiencies of other precious metals (Ag, Pd) and base metals, besides calcium (leaching of 25%) were less than 1 and 6%, respectively. The study revealed that more than 95% of Cu, Ni, Pb, Zn, Fe and Mn were initially removed from the pregnant leach solution at pH of 9.3 with addition of 0.1 M NaOH. Then 99.8% Au, 81.7% Ag and 74% Pd were precipitated from the obtained solution after NaOH precipitation while L-AA dose was 0.6 ml/ml at the condition. It can be concluded that the precious and base metals could be recovered selectively and economically from WPCBs via iodine-iodide leaching followed by precipitation using NaOH and L-AA.

Mar 1, 2018

By Takashi Miyamoto, Hideo Nakae, Hideki Yamaura, Takeshi Yanagihara

"For the production of partially composed metal matrix composites, namely discontinuous MMCs, using a casting· process, the interpenetrated phase composites with SiC particles were fabricated by pressureless iDfiltration using molten Al-Si alloys. This process is based on a wetting phenomenon, therefore, we discussed the technique based on the reactive wetting. The SiC particles coated by diluted water glass were sintered in a mullite Tammann tube and simultaneously infiltrated with molten Al-Si alloys in air at 1173~1573K. As for the improvement of the wettability between the SiC and the liquid aluminum alloy, Fe3O 4 powder was mixed with the water glass due to the thermit reaction between Fe3O4 and molten aluminum alloy. In some experiments, pure aluminum powder was placed on the sintered SiC to increase the interfacial area and the chemical reaction between the sintered Sic. and the melt. By combining these conditions, we succeeded in the complete infiltration without pressure at 1173K.IntroductionAs is well known, the mechanical properties of metal matrix composites (abbreviated MMCs) are superior than that of ordinary metals. However, their use has not been widely accepted because the production cost is very high due to their poor machinability. Therefore, the production of partially composed, namely discontinuous MMCs, by as the Lanxide process [l,2] has been investigated for many years. The Lanxide process, it takes a long time, sometimes up to 10h, in a nitrogen atmosphere for the infiltration. Therefore, the cost will be higher for common use. On the other hand, a high 'pressure process has been adopted for the production of discontinuous MMCs by the Toyota Motor Corp.[3]."

Jan 1, 2000

By Pingchao Ke

A crystalline polyferric sulfate (PFS) adsorbent was synthesized by oxidizing and precipitating ferrous ions under atmospheric conditions. The morphology, structure, composition and specific surface area (SSA) and adsorptive efficacy to As (III) of the adsorbent were characterized by SEM/EDS and TEM images, XRD patterns, FT-IR spectra, BET SSA analyses and adsorption experiments. The adsorbent presents as morphology of near-spherical aggregate and good crystallinity. A small amount of goethite co-precipitated with PFS in the case of the initial ferrous concentration of 1 mol/L and increased the SSA of the aggregates. The absorbent with co-precipitation of goethite showed good adsorption to As(III) and good filtering performance in the high As(III)-content solution of 10–100 mg/L under acidic, neutral and alkaline conditions (pH 2.09–9.01), and its maximal adsorption capacity and adsorption efficiency were 7911 μg/g and 96% separately. After Adsorption, the stability of the absorbents adsorbing As(III) were evaluated by TCLP tests, and the results indicated that the absorbents adsorbing As(III) were extremely stable, and the concentration of arsenic in all leaching solutions were less than 0.01 mg/L.

By George Owusu

A study has been carried out on the use of solvent extraction, instead of the traditional zinc dust cementation process, to remove copper from concentrated zinc sulphate leach solutions. In a series of experiments using plant solution containing 1.9 g/L Cu, 2 g/L Fe, 173 g/L Zn, 7.9 g/L H,SO,, 0.25 g/L Cd, 15 mg/L Co etc. and LIX 622 in SX-1, up to about 97-98 % of copper present in the zinc sulphate leach solution was extracted with negligible co-extractions of zinc, iron, cadmium, cobalt, etc. pH modification was not required for this reagent. The copper loaded organic was almost completely stripped using 150 g/L sulphuric acid. Investigations into the effect of any possible organiclextractant contamination on zinc electrowinning showed (if any) little effect on current efficiency if the organic contamination is less than 45 ppm; current efficiencies of 95-97 % were obtained. At organic contaminations higher than 45 ppm, the current efficiency dropped to about 92- 94 %. Visually, the organic-contaminated cathode sheets had rough surface morphology, becoming more intense with increasing organic concentration, compared to the non-contaminated cathode sheets.

Jan 1, 1998

By Joseph C. Rota

The Carlin Trend is one of the most significant gold mining districts in North America. Located in northeastern Nevada, a total of over 17 million ounces of gold have been produced since 1965 at Newmont Gold Company's open-pit and underground operations. Oxidized portions of the sediment-hosted, disseminated gold deposits at Carlin generally consist of finely disseminated concentrations of sub-micron sized native gold particles hosted in Paleozoic siliciclastic or carbonate rock. Oxide ore is commonly amenable to dump leach or heap leach processing, yielding an average 50 to 70% recovery of total contained gold. Refractory unoxidized ore requires some form of pretreatment oxidation to ensure economic gold recovery. Geologic ore control is typically combined with standard assay and engineering techniques to maintain both grade and metallurgical control ofleach grade ores. Mine geologists provide a vital function through field observation and recording ofmineralogic data during daily, visual blasthole logging. Intricately mixed refractory materials must be separated from oxide ore to ensure highest possible gold recoveries. Geologic information is combined with assay data to create mine polygons in an engineering computer database. Mining selectivity is further enhanced by in-pit ore control geologists who are available to make production decisions based on direct mineralogic observations at active mine faces.

Jan 1, 1997

By Xiang-dong XING, Zhen-yang wang, Jian-Liang Zhang

Distribution behavior of titanium between CaO-SiO2-MgO-Al2O3-TiO2 and hot metal was studied between 1350 °C to 1600 °C. Experimental results indicate that the reaction temperature influenced the activity coefficients of titanium and resulted in the variation of equilibrium constant. Finally, the Gibbs free energy formula of titanium carbothermic reduction was fit out using the thermodynamic model of Wagner and congregated electron phase models.

Jan 1, 2015