By W. G. Davenport

A flash furnace can be run many different ways. It can, for example, be operated with: (a) highly 02"enriched, ambient temperature blast and no fossil fuel (b) considerable fossil fuel and hot, slightly Or enriched blast. It can also produce different grades of matte. With all these possibilities, the flash furnace operator can benefit from any technique that will indicate the 'best' way to operate his furnace. One such technique is Excel's 'Solver'optimizationroutine#. This chapter shows how our matrices and Excers optimization.abllity can be used to optimize a flash furnace operation. The chapter sets three optimization goals: (a) minimum industrial oxygen + oil cost, $ per tonne of concentrate (b) maximum smelting rate, tonnes of concentrate per hour (c) maximum profit, $ per hour.

Jan 1, 2001

By K. C. Mills, P. N. Quested, A. P. Day, R. F. Brooks

"Methods have been developed to measure the physical properties of molten materials relevant to the fluid flow in high temperature processes. Data for the densities, viscosities and surface tensions of Al-, Ni- and Fe-based alloys are compared with (i) values for the pure metals and (ii) estimated values obtained from models making use of chemical composition of the alloy. Experimental values for metallurgical slags are also given and compared with estimated values.1 IntroductionPhysical property data has proved very useful in improving process control and product quality. For instance, in the continuous casting of steel the viscosity (TJ) of the mould flux is important since it determines (i) the optimum casting conditions, nVc = 2.5±1 dPas (m min-1) where V c is the casting speed and (ii) the level of slag entrapment (which leads to inclusions) in the metal. Thus data for properties like viscosity are exceedingly useful in understanding the process and the problems encountered and the causes of defects and problems.Another interesting development which has helped to increase our knowledge of processes and improve process control and product quality is the development of mathematical models of the fluid and heat flow in the process. These models have been developed to the stage where one of the prime requirements is for good physical property data for the industrial materials involved. Recently, Oxley [1] has shown that the use of reliable, experimental, property values for the commercial alloy in a commercial software package produced a significant improvement in the prediction of casting defects. Thus reliable property data are required for liquid metals but also for (i) liquid slags since many processes involve the use of a slag to refine and protect the metal or to lubricate the mould and (ii) refractories, sand and investment moulds."

Jan 1, 1999

By Hongfa Hu, Stavros A. Argyropoulos, Stephan Ferenczy

"Physical as well as mathematical modeling was carried out to investigate the exothermic mass transfer in liquid metal systems. In these systems, the exothermicity induces unique heat, mass and momentum transfer phenomena. Moreover, these phenomena are deeply coupled and they are further complicated by the presence of a moving boundary.In the physical model used, ice cylinders were immersed into sulfuric acid solutions, because the intermixing of ice with sulfuric acid is very exothermic. In this low temperature system, velocity and temperature measurements in the sulfuric acid were made as well as measurements of the ice melting in the sulfuric acid.The mathematical model developed solved simultaneously the heat, mass and momentum equations numerically, utilizing the control-volume finite difference approach. The enthalpy method was adopted to track the moving boundary. Predictions made by the mathematical model were in close agreement with the results obtained by the physical model.The results from the mathematical model were further validated with experiments involving high temperature liquid metals. Specifically, data were obtained in an experimental setup involving (a) dipping silicon cylinders into high carbon liquid iron and (b) dipping nickel cylinders into liquid aluminum. Results from these experimental studies supported the predictions of the mathematical model."

Jan 1, 1999

By Xinhua Wang, Qiangqiang Wang, Yubin Li, Shusen Li, Lifeng Zhang

"Numerical simulation on the fluid flow in a Flow-Control Mold (FC-Mold) were performed. The motion of inclusions were calculated. With FC-Mold, the flow pattern and surface velocity become more symmetrical, and at higher casting speed the velocity of liquid steel in the top region of the mold was largely reduced with the highest velocity of the meniscus reducing from 0.65 mis to 0.4 mis, and the meniscus shape became flatter. With FC-Mold, more inclusions approached to the surface of the slab and the amount of inclusion in the center of mold became fewer. Larger inclusions were easier to remove, however, the EM filed of the FC-Mold could hardly improve the removal of inclusions from the molten steel.IntroductionElectromagnetic brake technology is an effective method to control the flow pattern within continuous casting mold, together with other casting parameters, nozzle design and mold geometry [1-5]. Due to the interaction between the applied magnetic flux and the conductive molten steel inside the mold cavity, a force is generated in the direction opposite to the jet flow, which can decelerate the high speed steel jet from the SEN ports. The potential benefits include fewer surface and internal defects, fewer inclusion especially at higher casting speed. However if used imperfectly, electromagnetic forces can have opposite effect [6]. Numerical models are the best tool to optimize electromagnetic flow control. In the current study, numerical simulation was performed to investigate the flow field in a continuous casting FC-Mold, and the effect of different operation parameters on the flow, surface level and velocity in FC-Mold were discussed."

Jan 1, 2013

By Riyad N. Ahmad-Bitar, Shadia J. Ikhmayies

"CdS/CdTe solar cells were built by depositing a 200 nm layer of Sn02:F on glass substrates by the spray pyrolysis (SP) technique, a 500 nm CdS:In layer by the same technique and a 1-1.5 µm CdTe layer by vacuum evaporation. The cells were CdCh heat-treated in nitrogen atmosphere for 30 minutes at 350 -.C. The photoluminescence (PL) spectra were measured at the CdS/CdTe interface for two cells with different values of the CdTe layer's thickness at temperature T = 60 K. A deconvolution peak fit was performed from which it is found that the peaks are characteristic of the solid solution CdSxTei-x· The parabolic relation that relates the bandgap energy with the composition was used to estimate x, where xis [S]/([Te]+[S]) and [Te], [S] are the concentrations of Te and S atoms respectively. The results show that the interface is smooth and the change of the bandgap occurs gradually.IntroductionCdS/CdTe heterojunctions represent a combination of materials promising various applications, and for solar energy conversion in the first place [1]. In photovoltaic cells the CdS material acts as a wide bandgap window. Direct bandgap CdTe with high optical absorption coefficient is used as an absorber [1]. Solar cells with efficiencies of 10 to 16% have been obtained with CdTe grown by close space sublimation, electrodeposition, vacuum evaporation and rf sputtering methods [2]. In this work the CdTe layer was prepared by vacuum evaporation because it results with films of minimum impurities, while the Sn02:F and CdS:In layers were deposited by the spray pyrolysis technique because it is a low cost method which enables intentional doping and large area thin films."

Jan 1, 2011

By Batric Pesic

The interactions of mineral-pyrite with T. ferrooxidans were studied by using a cyclic voltametry technique. The interactions with bacteria were examined during the entire growth stage of bacteria (fermentation), The pyrite ?surface invariably drastically changed ' its. properties at the second day of fermentation. Beyond two .. days of fermentation, the cyclic voltamograms were insensitive to convective diffusion produced by stirring. The product layer was examined by SEM,. X-ray diffraction and chemical analysis. The SEM study revealed that bacteria populated the pyrite surface at an extremely high density levels. The high density of bacteria, and the solid reaction products formed on the pyrite surface created conditions for pore diffusion which explained why the CVs became .insensitive to convective diffusion in solution (stirring). The x-r:ay diffraction study confirmed jarosite as a product layer. A mechanism of T. ferrooxidans cells serving as nucleation sites for jiarosite formation is proposed.

Jan 1, 1991

By R. D. Irwin, W. M. Mullins, E. A. Medina

"Various stability criteria are introduced and thermo-kinetic models for metallurgical processes are used as concrete examples for evaluation. Kinetic criteria for the process of dynamic recrystallization are proposed. These criteria are compared to the non-equilibrium thermodynamic approaches discussed in the literature. The application of macroscopic stability criteria to materials processing is then discussed.IntroductionThe mechanical behavior of metals at elevated temperature is very well predicted by any of several empirical constitutive relations. Typical is the power-law (or Swift's) form,Equationwhere r-is the stress, y is the strain and m, n , t0, y0 and Q are material constants. This form has been used with some success in the metals processing area [1]. In general, though, all of the empirical constitutive equations are static, failing to account for any dynamical properties of the system they seek to describe.The physics of warm deformation is qualitatively well understood. An example is power-law creep, where the dominant mechanism is assumed to be lattice diffusion limited climb of dislocations, which allows the strain-rate to be determined by the applied stress through"

Jan 1, 1997

By P. D. Ferro

The direct oxide reduction (DOR) of plutonium oxide generates significant amounts of contaminated waste. This waste primarily consists of calcium oxide-saturated calcium chloride salt. This investigation explores the possibility of recycling the salt, by the electroreduction of the calcium oxide. Fused salt electrolysis of a simulated salt mix (CaC12 + ~10 wt. pct. CaO) is being carried out to electrowin calcium, and the process is being optimized in terms of the calcium solubility, cell temperature, current density and cell design to maximize the current efficiency. This work identifies the major concerns in the development of a process to electrowin calcium from this simulated salt mix.

Jan 1, 1992

By B. I. Hop

The f10wfield set up by the standard Hydro gas purging unit has been predicted by a numerical model. In addition turbulent trajectories of gas bubbles released from the rotor are predicted. Here the deposition rate of inclusions on the bubble surface is allowed to depend on local conditions. Bubbles passing regions with strong pressure gradients, such as close to the rotor, will experience large slip velocities and large deposition rates. This model can deal with any distribution of bubble sizes and inclusions. The results found from the multidimensional flow predictions are discussed in relation to what can be obtained from a much simpler metallurgical engineering approach. The differences between these two approaches to predict the same process will be discussed. The model predictions are compared to experimental results for removal of SiC-particles from aluminium.

Jan 1, 1996

By P. F. Stratton, M Huggahalli, N Saxena

"Several studies have been carried out to determine how the optimum atmosphere conditions in the heat treatment of metals can be established for a given product by using different gas injectors and varying atmosphere flow rate and composition. The most common approach taken to gain insight into furnace atmospheres has been to use commercial computational fluid dynamics codes and examples of their use are shown. However, the complexity of these codes, the difficulty in establishing boundary conditions, their cost and computational demands limit their usability in solving day-to-day production problems.A simplified, web-based model of a furnace atmosphere is described where the conservation equations are solved to determine the composition profiles of the atmosphere in the furnace. Although the model is restricted in scope to certain types of furnace, it is shown to give better results than CFD when boundary conditions are uncertain. The application of the model to the understanding of existing furnace conditions and to determining ways of optimising the use of gases are discussed. IntroductionThe important role of protective atmospheres during heat treatment of metals, furnace brazing of assemblies and soldering of printed circuit boards is well established. The atmosphere in the furnace prevents air ingress and oxidation of the parts, helps flush away any flux or binder from braze and solder pastes and provides an important mode of heat transfer [1]. In a batch furnace having typically one or two gas injectors, the gas utilisation and process can be optimised by minimising air leaks and mantaining atmosphere homogeneity with fans or other atmosphere circulation techniques. In a continuous furnace, however, atmosphere optimisation is more difficult as furnace inlets and exits can also let in air. The atmosphere requirements of different stages of heat treatment, brazing or soldering vary [2]. Achieving these atmospheres in different sections of the open-ended furnace is a relatively complex task. Methods such as atmosphere zoning and the use of physical curtains and gas injectors have evolved with time, though it is hard to predict how effective these techniques will be for a given furnace and process. Experts in the field tend to rely on experience and rules-of-thumb rather than scientific method to achieve the required results."

Jan 1, 2001

By M. Okido, R. Ichino, K. Kuroda

"Compound semiconductor, ZnTe, was electrodeposited in an acidic solution with K2TeO3, ZnSO4 and Na2SO4 solution. Since the reduction potential Te(IV)/Te(O) is remarkably noble from the solution comparing to Zn(II)/Zn(O), code position of Te and Zn was thought to be difficult from this solution. Resulting from EQCM analysis, furthermore, Te(IV) reduced to Te(O) and Te(-II) in this order so that Te catholically dissolved from the electrode surface at more negative potential. But ZnTe alloy were formed by the UPD of Zn at -0.7V at 298K on Te surface in lmM K2TeO3, 100mM ZnSO4 and 100mM Na2SO4 solution adjusted at pH 4. Content of Te in the deposits is, however, more than 80%.Electrolytic temperature is well known to affect on the deposits characteristics. The higher bath temperature was, the better ZnTe crystal was detected in this study. Thermal electrode method is a. process of heating only substrate by flowing ac current in substrate. This process makes the surface temperature of substrate higher than boiling point of the solution, 373K. From EDX analysis, deposits without thermal current were Te-rich, Te content in the deposits with thermal current decreased with increasing of thermal current. Te content was 62% for 5A ac current, 51 % for I OA and 45% for 20A, respectively. The deposits that produced with ac current of IOA were closed to the stoichiometric ratio, i.e. ZnTe.Consequently, thermal electrode method is more effective to obtain a good crystallized ZnTe without heat treatment after deposition.IntroductionThe current subject of solar cell materials is silicon. Compound semiconductors including GaAs and II-VI group are generally used in the developing field of digital information such as the rapid cellular phone and car telephone. Compound semiconductors consist of more than 2 kinds of element. There are many materials for these compound semiconductors such a SiC, InSb, CdS for binary system and CuinSe2 for ternary system. It becomes generally difficult, to produce high quality crystal with increasing of kinds of element due to a complicated structure and a compound ratio of element. Semiconductor materials as a device are usually simple binary compounds and/or these mixed crystals. Properties of compound semiconductors have variety of the forbidden band and lattice constant and that can be change easily by addition of another element for the usage of the solar cell. Since most compound semiconductors are direct interband transition type, which has steep optics absorption edge and large light absorption coefficient."

Jan 1, 2000

By Zemin Ma

A novel chromate [Cr(VI)] reducing bacterium was isolated from chromite ore processing residue disposal site of China and identified as a Leucobacter sp. by 16S rRNA gene sequence homology. The minimum inhibitory concentration of strain CRB1 was 820 mg l-1 of Cr(VI). The reduction of Cr(VI) occurred only under aerobic conditions. With an initial concentration of 2.5×108 cells ml-1, 1800 mg l-1 of Cr(VI) was reduced entirely within 38 h under the optimum conditions, at 30 °C and pH 9.0. Increasing Cr(VI) concentrations prolonged reduction process and higher cell densities meant quicker reduction. A blue precipitate was produced during chromate reduction of strain CRB1, which was binding to the surface of bacterial cells and determined as trivalent chromium with electron paramagnetic resonance (EPR) spectrometry. The conspicuous chromate reduction ability of Leucobacter sp. CRB1 suggested a potential for bioremediation of Cr(VI) containing wastes.

Jan 1, 2008

By H. Itou, J. M. Toguri, T. Takasu

"Marangoni convection has a large effect on materials processing since it remarkably enhances heat and mass transport near a free interface. To have a better understanding of the behavior of Marangoni convection in molten salts, observation and calculation of the thermal convection in a column held between a pair of Pt disks (2mm in diameter) fixed to hot thermocouples, were carried out.Calculated flow patterns and absolute values of fluid velocity agreed well with the observed results. When the temperatures of both disks were set equal and the height of liquid column was 2.4mm, four vortexes were generated on the longitudinal plane with a typical velocity of 15mm/s . From the calculated isothermal lines, the behavior of the enhanced heat transport was obvious; fluid heated at the disks was conveyed to the free surface and the cooled fluid at the surface was conveyed to the inner region. Increase in the height of column and/or increase in the absolute value of applied temperature difference lead to increase in fluid velocity lineally in this calculation range.IntroductionIn the processing of many materials, fluid flow of melts has a large effect on refining capabilities and on the characteristics of the produced material. Marangoni convection is generated when a spatial gradient of interfacial tension exists on the free interface due to differences in temperature and/or concentration. This promotes heat and mass transfer locally near the interface.For example, Marangoni convection which are created following the dissolution of interfacially active materials, increases the local corrosion rate of refractories (1-3). In absorption and discharge of oxygen and/or nitrogen in a molten metal, the effective reaction rate of the gas components through the gas-liquid interface increases (4-7). Also in crystal growth, the distribution of defects and impurities in the crystal is affected and this can alter its quality (8-11 ). The temperature distribution is also affected and can greatly change the productivity. For these reasons, the effectiveness of Marangoni convection in refining should be quantitatively clarified and its control should be better understood."

Jan 1, 1997

By Kazue Moriya

At the 1980 TMS-AIME world symposium, Dr. Davey mentioned that the traditional lead blast furnace is now being challenged by direct smelting processes. In the copper smelting field both the blast furnace and reverberatory furnace are also disappearing in favour of direct smelting processes such as Outokumpu flash smelting, Mitsubishi continuous smelting, Noranda furnace, Inco furnace and so on. Those new processes all have the following in common: (1) High degree of mechanization (2) Metallurgical reactions carried out in closed vessels (3) Application of oxygen and/or oxygen enriched air (4) Minimization of handling materials and gaseous volume (5) Minimum energy requirements (6) Removal of workers from near the furnace (7) Reduction of emissions of harmful gas to meet environmental regulations. (8) Improvement to the work place environment to avoid occupational hygiene hazards. Direct and continuous smelting of powdered concentrate in one vessel was a romance of the metallurgist since early times. However as mentioned above, in the copper field this objective is being achieved in practice. The industry however can't deny that the serious and severe regulation of environmental pollution in every country was the prime motive for the modernization of smelters. In early days, to meet regulations, it was anticipated that many economic difficulties such as higher capital and energy costs and extravagant use of resources and waste disposal would be the result. "Turn a misfortune into a blessing" is an old saying which reveals the current thinking and reacent developments in the nonferrous industries. In the last ten years in the lead smelting field, about two decades later than copper, commercial scale smelting using new furnance technology has started. The KIVCET process and QSL process, which is flash smelting and bath smelting respectively, are becoming major competitors. They will be sure to upgrade their processes to remain economically and environmentally viable in the comming decade.

Jan 1, 1990

By Richard L. Werner

The petrographic microscope as a tool in determining impurities and grain size of limestones, clays, sand and coal ash for possible use as raw materials is discussed. Its use in the determination of the mineral composition of various size fractions of the raw mix, after fine grinding in ball mills, and of the waste dust from the rotary kiln. A description is given of the typical clinker crystals; alite, belite, tricalcium aluminate and ferrite. The process problems indicated by various changes in the crystal characteristics are listed with possible solutions. Finally the microscope as used in relation to field problems with concrete such as air void volume, percent hydration of the cement, cement aggregate bonding and the determination of solid additives, is presented.

Jan 1, 1982

By Honglei Zhang, Wuguo Xiang, Xinhao Huang, Guotao Xu, Xilai Chen

"The service behavior of refractories used in hot air pipeline for hot air stoves in a 3200 M3 blast furnace of WISCO was analyzed. The damage factors can be concluded as the poor quality of and alusite based bricks, the severe thermal shock damage, the more porosity in structures, loose bonding capability, and the unreasonable choice of materials and design of bricks. By analysis, the service life of hot air stoves can be enhanced by the measurements such as the reasonable choice of materials and their match, the use of light-weight refractories, the improvement of brick type, etc. Thereafter, the normal production operation of hot air stoves is guaranteed.IntroductionThe No.7 blast furnace of WISCO has been used for about 5 years and it was mid-repaired in March, 2012. The top phenomena of worn hot air pipelines are brick drop, breakage, severely local wear and deformation, existing hidden danger, so the worn hot air pipelines were renewed. Investigations have been done on the stove damage and design [1,2]. In order to clarify the wear mechanism, the used refractories for hot air pipelines were sampled and analyzed, the properties and structures of worn materials and reused materials are relatively studied."

Jan 1, 2013

By C. M. Antony

The galvanizing process involves the use of accessory equipment in a series of aggressive environments including zinc ammonium chloride flux, molten zinc at 45S°C (850°F), and acid for stripping of adherent zinc. An Fe-Ni-Cr-Co alloy has been identified which combines excellent strength and resistance to molten zinc and acid attack making it suitable for accessory equipment. The alloy was field tested by a commercial galvanizer as basket material and was found to provide improved life compared to original low-alloy steel baskets while cross-section thickness was reduced 44%. Additionally, other associated processing cost savings were realized.

Jan 1, 1992

By E. T. White, Dean Ilievski

"Mathematical modelling of the precipitation process requires that the kinetics of crystal growth, nucleation and agglomeration be known. This paper reviews the current state of knowledge on these precipitation sub-processes (ie. growth, nucleation and agglomeration) and describes a number of experimental techniques for estimating their kinetics. The experimental methods used to generate the precipitation data and the data analysis techniques used to extract the kinetics information from the data are discussed separately. There is no universal ""best"" technique for determining the kinetics. However, studies on multi-crystal systems are more reliable for modelling purposes than are single crystal studies. The selection of a technique will depend on which sub-processes are present. A problem with all kinetics studies is that there is generally a large uncertainty in the estimated kinetic parameters. This stems from the scatter in the experimental data being further propagated by the mathematical techniques used to extract the kinetic parameters.IntroductionCrystallisation operations, including precipitation, are widely used in a number of hydrometallurgical processes to recover a desired component or to remove an undesired impurity. The goals of industrial precipitation processes are to maximise the recovery while maintaining product quality (generally product crystal size distribution, purity and morphology and product handling properties). Knowledge of the precipitation mechanisms and kinetics is invaluable for designing new precipitators or for improving existing units. The mechanistic and kinetic information is generally incorporated into mathematical precipitator models, which are then used for process design and optimisation."

Jan 1, 1996

By D. Van Dooren

The final goal of the research project is to develop a 3D FEM model that is able to predict the kinetics and micro-structural evolution during the bainitic transformation. The input parameters consist of thermodynamic and atomic mobility data obtained from the ThermoCalc and mCTRA databases combined with structural mechanics data extracted from the stress-strain curves of the fcc and bee phases. In this paper the general principles of the model are outlined and some interesting preliminary results are shown and commented. The full implementation of the model has presently not been achieved yet. In the model the bainitic transformation is considered as a sequence of martensitic (re)nucleation and growth of a ferritic subunit followed by the carbon rejection into the surrounding austenite. The (re)nucleation of the subunits will be described through a non-classical martensitic nucleation criterion. Once a nucleus has been activated at a specific location in the material, a full-sized subunit is instantaneously formed through a displacive mechanism. The stress state in the system that arises due to the transformation strain can be calculated by a 3D FEM programming code. Immediately after the formation of the subunit, another 3D FEM programming code calculates the carbon diffusion from the supersaturated ferrite into the surrounding austenite. The resulting stress state and carbon profiles will be used to determine where and when a new subunit will nucleate based on a renucleation criterion. Keywords: Bainitic Transformation, Modeling, Eshelby, Carbon Diffusion

Jan 1, 2003

By B. Mishra

The application of various bydrometallurgical, pyrometallurgical and electrochemical processes in the extraction, purification and production of radioactive metals as well as the use of various materials, eg. metals and alloys, ceramics, polymers, etc. in the process, construction and handling equipment in the nuclear industry has generated a large stockpile of radioactively contaminated waste material and scrap metal which can not be directly discarded, recycled or considered for long-term storage due to its volume and potential hazards, without the separation of radionuclides. This paper reviews the emerging methods that have been 'investigated and suggested for dealing with some of these wastes' and scrap material. The separation technologies studied for the recovery of radioactive components from the pyrometallurgical and electrochemical processing wastes have been discussed in details with results from some of the recent theoretical and physical modeling work as well as the data obtained? from the actual waste treatment. Specific processes shall be described in terms of its advantages and limitations. These emerging separation technologies are being considered by the US Department of Energy as alternatives for dealing with the issues of environmental management [EMI' and decontamination and decommissioning [D&D].

Jan 1, 1996