By Xin Li, Hai-Xing Fang, Bing Xie, Hong-Yi Li

Chromium-containing vanadium slag (V-Cr slag) was obtained by an industrial smelting process of Hongge Ore, which is valuable vanadium-titanium magnetite to extract V and Cr in China. Sodium roasting thermodynamics of V-Cr slag in presence of oxygen were calculated to evaluate the reactivity of chemical compounds. Results showed that the oxidation of FeV2O4 was intensified in presence of Na2CO3 while the oxidation tendency of FeCr2O4 was far lower than that of FeV2O4. It was probably that reactions of impurities including Al2O3, SiO2 and Fe2O3 with Na2CO3 happened and the products can promote the oxidation of vanadium or chromium compounds in lower valence. Based on thermodynamic analysis, a two-step selective extraction process of vanadium and chromium was proposed. Extraction rate of vanadium was 88.6% while 7.0% for chromium in the first extraction step; extraction rate of 90.7% and 95.4% for vanadium and chromium, respectively, were obtained in the second step.

Jan 1, 2014

By Cynthia Belt

"Energy management is critical to aluminum processing given the high energy requirements of melting and processing aluminum. Energy costs have always been a high percentage of the total production costs within this industry. Energy management at many plants relied on better technology that many times required high capital. As carbon management has grown in importance and project payback becomes more critical, a larger view of a plant's process is required. This paper looks at the energy requirement due to current typical practices in overall product recovery, metal loss, utilization, and technology to understand potential methods of reducing overall energy within a plant and within the aluminum processing industry.IntroductionFor many companies that process aluminum, energy is a major portion of their costs that can surpass the cost oflabor. Aluminum processing can include secondary processing of scrap and prime aluminum into sows and/or molten aluminum or casting aluminum by various methods such as direct chill, continuous casting, low or high pressure casting, mold casting, and extrusions. In the case of this paper, we are considering only plants that include the melting process as a portion of their process. The process of melting aluminum takes energy. In most cases, the aluminum must then be heat treated one or more times. Post processing of the aluminum includes rolling mills used for making sheet, extrusion lines, and machining such as saw cuts, drilling, or surface finishes that all take additional energy.While these high energy costs directly affect the profits of the company, energy management within the metals industry is still not widespread. A co=on misconception is that the solution to high energy costs is high cost capital equipment. While state-of-the-art equipment can certainly improve energy efficiency, it is not the only solution. To obtain a truly energy efficient plant, several directions needs to be addressed through an energy management thought process with a wider scope. Impact on potential savings is possible through: product recovery, metal loss, utilization, and new technologies. An understanding of the potential costs and savings from these means is important. Several of these methods provide low cost approaches to saving energy.The background data used in this paper is not a random sample within aluminum processing but yearly averages from various plants in different aluminum processing industries. As is normal in this industry, the plants have been under different corporate management over the years with different strategies for energy management. This data is not meant to be accurate for the entire industry but to suggest areas for energy efficiency work."

Jan 1, 2012

By Jillian Spindura

This work investigates the carbothermic reduction of the complex sulphide mineral, pentlandite, in the presence of lime. The effects of change in temperature and the use of different carbon sources are studied and the role of these variables on the reducibility of pentlandite mineral is discussed. The microstructures of the heat-treated pellets are examined using X-ray diffraction and scanning electron microscopic techniques. The latter analytical method also allows any variation in the morphology and composition of the metallic phases formed, with temperature, to be considered. The kinetics of the reduction process is studied and the magnitude of the overall activation energy is determined from the plots of percentage reduction versus time.

Jan 1, 1996

By Jesse White, Tyler Salisbury

Research projects contain many stages of development from the conception of an idea to a fullscale commercial operation. The transition from laboratory-scale research to bench-scale roasting can represent a significant increase in complexity and cost, depending on how many variables are being evaluated. Thermogravimetric analysis (TGA) can simulate roasting conditions and produce a small sample for chemical analysis or materials characterization. A simultaneous thermogravimetric and differential scanning calorimetry (TG–DSC) can identify endothermic and exothermic reaction temperatures. Using thermal analysis, some of the process variables can be tested and eliminated such as ore and reagent blends, retention times, operating temperatures, and some atmospheres.

Jan 1, 2015

By Richard A. Leiby

The recycling of lead-acid batteries in the United States has become a challenge as to how to balance ever increasing environmental regulation and cost with efficient operations. East Penn's captive secondary lead smelter has developed into a recycling facility producing lead, polypropylene, sulfuric acid, ammonium bisulfite, and non-hazardous discard slag. The emphasis has been to design a facility to comply with environmental regulations, to eliminate wastes, and to produce products, while at the same time, continuing to supply the company's battery manufacturing raw material needs.

Jan 1, 1993

By Gaballah I.

Elimination of arsenic, mercury and zinc from synthetic solutions containing H;\A.sD4. HgCI2 and ZnCI2 using modified barks was investigated. The pH range was varied from ?1 to 10. The initial concentrations of individual element were 10,100 and 1000 ppm. More than 99 % of mercury and 65 % of zinc cations were removed by the modified bark .. In this case, the modified bark reacts as a cation exchanger leading to the release of ' two protons for every HgII or ZnII fixed by this material. About 30 % of arsenic was eliminated from the solution. This 'low efficiency could be attributed to? the presence of arsenic ,as. anion. Decontamination of a treated industrial effluent containing 4 ppm of ion? metals was performed on a pilot plant scale by the modified bll(k. More than 70'% of these ion metals were eliminated.

Jan 1, 1995

By Tugba Basargan Çagatay Morall, Gülhayat Nasun-Saygili

"The aim of this study is to prepare the apatitic material using colemanite mineral (2CaO.3B2O3.5H2O) which was obtained from Eastern Anatolia, Turkey. For this purpose, colemanite mineral was reacted with different phosphate sources, namely, dipotassiumhydrogen phosphate, ammoniumhydrogen phosphate and ortophosphoric acid at various temperatures and time periods. Experiments were run in batch system. The apatitic material was prepared by a wet method and followed by heat treatment at various temperatures. Structure of the samples was analyzed by XRD, FTIR, XRF and SEM. The particle size analysis was also made for the result product. The experiments showed that reaction temperature, contact time and heating temperature are important parameters to transform the colemanite into apatitic structure. Reaction of colemanite with dipotassiumhydrogen phosphate and ammoniumhydrogen phosphate results in amorphous, non-stoichiometric hydroxyapatite type structure, while acid based phosphate source gives brushite and monetite type product before and after heat treatment, respectively.IntroductionBoron which has properties intermediate between metals and non-metals is a member of semiconductor group of elements. Its atom is very small and has three valence electrons. Boron exists in Earth's crust (from 5 mg/kg in basalts to 100 mg/kg in shale) and in the oceans (4.5 mg/l) [1]. Turkey has 60% of world's boron reserves which is mostly in the form of colemanite (2Ca0.3B203.5H20). Colemanite is the most important calcium containing commercial borate mineral with 5 mol of crystal water [2].Calcium phosphate cements are very useful for bone repair applications because of its chemical structure. They are injectable, easy to shape and can be maintained locally. Because of those reasons calcium phosphate cements are very effective to fill bone defects with an irregular shape [3]. Hydroxyapatite (Ca10(PO)6(OHh) is the major component of the bone (70 wt%). However, hydroxyapatite stoichiometry, composition and crystallinity differ in human skeleton system [4, 5].The main objective of the present work was to study the transformation of colemanite to apatitic material using different phosphate solutions at several time spans and temperatures. The experiments were run in a batch system, change in pH and also weight loss were measured after the experiments. Several analysis methods were used to investigate the chemical and structural changes."

Jan 1, 2012

By Robert D. Rogers

The demand for phosphate will continue into the future, because phosphate is currently irreplaceable as a plant nutrient and in many chemical applications. Phosphate is not recycled, so the supply must be replenished through a process of mining and purification. Numerous microbial isolates. obtained from the environment were screened find those which demonstrated the greatest promise of solubilizing PO4 from the ore of interest. Screening was accomplished in a step wise manner an agar plate bioassay, shake flask studies, and semi continuous growth conditions. It was found that with the proper conditions of nutrient supply and solution pH; the bacteria and. fungus used in the semicontinuous process were able to solubilize in excess of 80% of an Idaho rock phosphate ore (RP) within nine days. A significant amount of solubilization occurred within the first six days. There was a 'reasonable correlation between the occurrence of soluble Ca and PO.4 during the processing of the RP thus providing evidence that the RP was being disintegrated by the organisms. In all cases, HPLC analysis of the solutions in which PO4 had been. extracted from RP showed that organic acids, which have been implicated as the mechanism of solubilization, were present.

Jan 1, 1991

By Y. A. Chang, L. M. Pike, C. R. Kao

"Knowledge of the site preference of ternary solute additions is essential to developing an understanding of how these solutes affect the properties of B2 intermetallic compounds. A quasichemical model will be presented which is able to predict the site preferences of dilute solute additions to tliple defect B2 compounds. The only parameters required are enthalpies of formation at the stoichiometric composition. General equations are developed which can be used to determine site occupations and defect concentrations for dilute as well as non-dilute solute additions. These equations use atom pair bond enthalpies as the parameters. It is found that the site preferences of dilute additions are not always in agreement with predictions based on the solubility lobes in ternary Gibbs isothelms. Predictions for dilute additions to NiAl and FeAl are compared to expel1mental results found in the literature. Satisfactory correlation is found between the model and the experimental results. In addition, the predictions from the model on vacancy concentrations in Fe doped NiAl are compared to recent experimental results by the authors.1.0 IntroductionIntennetallic compounds with the B2 crystal structure such as NiAl and FeAl have been investigated recently for possible use as structural materials in high temperature, oxidizing, and/or corrosive environments. The major limiting property of these materials has been a lack of sufficient room temperature ductility. Attempts to improve the ductility have often been made through ternary or higher order alloying. For B2 compounds, substitutional alloying additions can occupy either of the two sublattices and this site occupancy can be crucial in determining how the alloying addition affects the properties of the alloy. In this manuscript we will discuss the use of thelmodynamic modeling to predict the site occupancies of ternary alloying additions in B2 compounds with the triple defect structure."

Jan 1, 1996

By P. G. Comba

Many gold producing states are requiring rinsing of spent heaps to render the leached ore compatible with the environment and are placing restrictions on effluent pa, cyanide, and metals concentrations. Parameters which may affect efficient rinsing of heaps have been investigated by the U.S. Bureau of Mines in laboratory column studies. Rinse profiles for cyanide, metals, and pH as a function of the volume of water passed through the spent ore are presented. Fresh water rinsing of spent ore in columns showed that rinsing of cyanide was not affected by the rinse solution application rate. Interrupted rinsing with a rest period between applications reduced the volume of water required to meet effluent cyanide concentrations. chemical oxidation of the effluent with recycle of the rinse solutions reduced effluent cyanide concentrations and the volume of waste solution generated. Water rinsing was not successful in reducing the alkalinity of the cement agglomerated ore. A dilute acid solution had to be applied after cyanide removal to reduce effluent pa levels to specified limits.

Jan 1, 1992

By J. M. Boxall

The electrolytic zinc plant at the Bartlesville division of Z.C.A. originally used lead anodes containing only 0.25% silver because only H.G. zinc and alloy was to be produced. In 1984, a small addition of strontium carbonate was made to control the surf ace morphology of the cathodes which reduced short circuits and increased current efficiency. Later a drastic reduction in colloid addition further reduced short circuits. Increased strontium additions allowed the production of some S.H.G. zinc. Increasing the silver content of the anodes reduced the lead in cathodes only slightly. More important, the anode scale that was not removed during anode cleaning, entered the electrolyte and contaminated the cathodes with lead. A piping system has been installed to purge the contaminated electrolyte directly back to the leaching section. This has allowed the plant to produce S.H.G. zinc consistently.

Jan 1, 1990

By Minh H. Pham

This paper presents a technique for imaging the extent of solidification of molten metal flowing in a cooled pipe based on the concept of eddy currents. A 3D mathematical model, which relates the geometry of solidification to the scattered field induced in a solenoid external to the pipe, is derived. The model is described by a set of integral equations which are solved numerically using the moments method. An iterative algorithm is developed to reconstruct the solidification distribution image. Experimental measurements have shown that the eddy current technique is sufficiently sensitive for practical purposes.

Jan 1, 2001

By D. L. Jones

The leaching of natural chalcopyrite was studied in both ferric sulfate and ferric chloride solutions. The chemistry of the two reactions is quite different, with substantial sulfur oxidation occurring only in sulfate solutions. Ferric chloride is a more effective reagent, for the leaching rate is greatly increased with finer particles and higher (Fe+++), and unaffected by high (Fe++); none of these advantages are found with ferric sulfate. In addition, the morphology of leaching appears to be different, with ferric sulfate leaching preferentially along fissures or grain boundaries. The kinetics were found to be linear over an extended period, rather than parabolic as reported elsewhere. An explanation of the observed phenanena is proposed using the electrochemical theory of leaching, and experimental measurement of the mixed potential of the mineral during leaching.

Jan 1, 1976

By Reed M. Izatt

SuperLig® materials are capable of individually separating Rh, Pd, and/or Pt in highly purified form (99.95 to 99.99%) from a variety of chloride-based feed streams in a single stage operation. The hydrophillicity and associated kinetics of the supported materials allow for operation at relatively high flow rates of both loading and elution in a packed bed format. Pilot and commercial systems have been operated with Rh, Pd, and/or Pt present in the feed from single digit ppm (mg/l) to tens of g/l. A dual SuperLig® system for one pass Au(CN)2- separation followed by Cu and CN- recovery for CN- recycle has also been tested up to a pilot level,

Jan 1, 1999

By Masami Taguchi

"It is found that lead monoxide, PbO, has an ionic conductivity, and the all solid-state electrochemical cell using this oxide as an electrolyte has attracted the attention of battery researchers. In this study, thin film PbO2/PbO/Pb solid cells were produced on glass substrates and their discharge properties were investigated. The acti.ve material for the positive electrode, PbO2, was obtained by reactive sputtering of a Pb target in oxygen plasma. The PbO electrolyte and the active material for the negative electrode, Pb, were vacuum evaporated from /3 -PbO powder and a Pb block, respectively. The open-circuit voltage of the cell agreed with the theoretical value based on the thermodynamic data, and the close-circuit voltage was improved by the addition of a univalent impurity such as sodium or potassium to the PbO electrolyte. The connection of the cells in series and in parallel produced a higher electromotive force and a larger capacity. Also, the charge-discharge cycling test revealed that the cell could be charged and function as a storage battery.IntroductionGenerally, the ionic conductivity of a solid-state electrolyte is lower than that of a liquid electrolyte near room temperature. This has been a serious obstacle to using such electrolytes in an electrochemical cell. However, some solid-state electrolytes, which can preferentially pass a specified ion and have high ionic conductivity, have been found. Lead monoxide, PbO, which is an oxygen ion conductor, is such an example (1)(2). If a solid-state electrolyte is adopted for use in an electrochemical cell the problem associated with a liquid electrolyte such as leakage can be alleviated. The cell structure also can be simplified, because the electrolyte plays the role of separator to prevent the active materials from mixing. Thus, physical vapor deposition technology may make it possible to develop a very thin film cell, which consists of only solid phases (3)(4). In this study, the thin film PbO2/PbO/Pb solid cell with a thickness· of only a few micrometers, in which all the constituents were systematically deposited on a glass substrate by reactive sputtering and vacuum evaporation, has been produced and the charge-discharge properties were investigated. An attempt was made to improve the discharge properties by doping impurities such as Na2CO3 and Sb2O3 into the PbO electrolyte. Moreover, the connection of the cells in series and in parallel to get a higher electromotive force and a larger capacity, and the charge-discharge cycling test to determine its use as a storage battery were carried out."

Jan 1, 2000

By Marcelo R. Esquivel

A MmNi5 alloy is synthesized by a combination of mechanical milling and low temperature heating processes. Synthesis time is 40 h for powders milled in a low energy ball mill at room temperature. A reduction in milling time is obtained if massive sample is mechanically milled at shorter times (2 h to 10 h) and heated at temperatures lower (600 ºC) than the usual temperatures used in equilibrium methods (>800 ºC). The alloy formation is detected even at a combination of temperatures as low as 200 ºC and milling times as short as 5 h. The temporal evolution of mechanical milling process was followed by both X-ray diffraction (XRD) and scanning electron microscopy (SEM) to detect the main stages of milling. Four stages were detected: Initial, Intermediate, Final and Completion. These stages were correlated to an enhancement of the synthesis method by combination of times of milling shorter than 10 h and temperatures of heating lower than 600 ºC.

Jan 1, 2006

By Cong Wang, Kexin Jiao, Yongan Zhao, Haibin Zuo, Jianliang Zhang

The carbon composite brick is a new refractory used in blast furnace hearth and bottom. It caused wide attention due to its high thermal conductivity and low erosion by molten iron. In this paper, chemical constituents, SEM-EDS and X-ray diffraction were carried out in order to understand reaction mechanisms. A series of experiments of oxidation resistance characteristics were made. The oxidation mechanisms of carbon composite bricks in the presence of air were analyzed. According to the analysis on many experimental results, the oxidation process of carbon composite bricks under different temperatures were controlled by different mechanisms. In the condition of high temperature, SiO2 as oxidation product hindered the diffusion of O2, and reduced the oxidation loss of graphite in the internal.

Jan 1, 2015

By F. Elgersma

Hydrometallurgical zinc winning processes ?are frequently based on iron containing concentrates which yield a goethite, jarosite or hematite residue. Jarosite or goethite are mostly stored in waste ponds which ,are lined with foil. Water percolating through the pond is withdrawn from the deposit ,and decontaminated before discharge. Despite these measures, more and more pressure is put upon zinc companies to treat their (historical) residues and to produce environmentally acceptable residues. The criterion which determines this acceptability is the potentiality of leaching out hazardous elements by natural processes. This paper provides the comparison of five different process designs for integrated jarosite treatment in a hydrometallurgical zinc winning plant leading to environmentally acceptable residues. The processes are esigned for producing 200 ktons/yr zinc and for treating 80 ktonslyr historical jarosite. Mass and energy balances are used to determme parameters such as: the energy use per ton waste treated and the amount and composition of final residues. The conclusion of the work is that. pyrometallurgical jarosite treatment integrated in hydrometallurgical zinc winning is preferable to hydrometallurgical jarosite treatment. Integrated pyrometallurgical processes lead to a ?smaller quantity of remaining hazardous residues and require less energy.

Jan 1, 1992

By Malti Goel

"Technology advancements in fossil fuel based energy generation and consumption are currently being aimed at minimization of CO2 emissions. To attain energy security, India must accelerate the pace of economic development, while achieving reduction in CO2 emissions per unit of energy consumed. It would need access to advanced coal utilization technologies to be demonstrated on indigenous coal characteristics. Of specific importance would be: improvement in coal quality, increasing energy efficiency and suitability of other CO2 sequestration technologies for reducing CO2 footprints. There is need to address related risks and financial burden through adoption of policies and regulations including the issue of open access in energy research. In this paper, seven important areas of strategic plan that need to be pursued for managing CO2 emissions in steel energy sector in India are discussed.IntroductionWorld is facing a crisis of climate change, which follows in the footsteps of global energy and environment crises. Accumulation of carbon dioxide from the generation and utilization of energy is leading to greenhouse warming and climate change. The global warming is causing the boundary between four seasons to be fuzzy and resulting in more spiky weather. Significance of its impact on environment is also determining the technology development needs in various sectors of economy for taking remedial measures.To respond to climate change concerns, the steel industry is undergoing a transition. It is at the threshold of a rapid change in technology as it targets innovation to achieve 50% reduction of CO2 emissions per ton of steel produced. Fossil fuel use is the main contributor of increasing concentration of carbon dioxide in the atmosphere. The control of air pollution and CO2 capture are thus relevant for a coal based industry, whether thermal power plant or a demand side energy intensive industry. World steel production has shown phenomenal increase in first eight years of 21st century increasing from 780 Mt in 2000 to 1343 Mt in 2008 [1]. It was merely 28 Mt in 1900. The global CO2 emissions from steel industry are also increasing and became 2550 Mt (3-4% of total GHG). Indian industry contribution was 161 Mt (15% of direct emissions from industry). It is likely to grow further to keep pace with the accelerated economic growth of 8-9% per annum."

Jan 1, 2010

By Rafael Colás

Computer visualization can be employed in industry as an aid to the understanding of the complex interactions between variables encountered in production. The examples of ingot casting of rimming steel and that of hot rolling of low carbon steel strip are presented. Both processes are mathematically modeled, and their results are presented in a graphical way. Such models have been proven to be an asset in quality improvements and increase of productivity as the personnel involved get a better understanding of their job.

Jan 1, 1993