By Marcelo R. Esquivel

A MmNi5 alloy is synthesized by a combination of mechanical milling and low temperature heating processes. Synthesis time is 40 h for powders milled in a low energy ball mill at room temperature. A reduction in milling time is obtained if massive sample is mechanically milled at shorter times (2 h to 10 h) and heated at temperatures lower (600 ºC) than the usual temperatures used in equilibrium methods (>800 ºC). The alloy formation is detected even at a combination of temperatures as low as 200 ºC and milling times as short as 5 h. The temporal evolution of mechanical milling process was followed by both X-ray diffraction (XRD) and scanning electron microscopy (SEM) to detect the main stages of milling. Four stages were detected: Initial, Intermediate, Final and Completion. These stages were correlated to an enhancement of the synthesis method by combination of times of milling shorter than 10 h and temperatures of heating lower than 600 ºC.

Jan 1, 2006

By Masami Taguchi

"It is found that lead monoxide, PbO, has an ionic conductivity, and the all solid-state electrochemical cell using this oxide as an electrolyte has attracted the attention of battery researchers. In this study, thin film PbO2/PbO/Pb solid cells were produced on glass substrates and their discharge properties were investigated. The acti.ve material for the positive electrode, PbO2, was obtained by reactive sputtering of a Pb target in oxygen plasma. The PbO electrolyte and the active material for the negative electrode, Pb, were vacuum evaporated from /3 -PbO powder and a Pb block, respectively. The open-circuit voltage of the cell agreed with the theoretical value based on the thermodynamic data, and the close-circuit voltage was improved by the addition of a univalent impurity such as sodium or potassium to the PbO electrolyte. The connection of the cells in series and in parallel produced a higher electromotive force and a larger capacity. Also, the charge-discharge cycling test revealed that the cell could be charged and function as a storage battery.IntroductionGenerally, the ionic conductivity of a solid-state electrolyte is lower than that of a liquid electrolyte near room temperature. This has been a serious obstacle to using such electrolytes in an electrochemical cell. However, some solid-state electrolytes, which can preferentially pass a specified ion and have high ionic conductivity, have been found. Lead monoxide, PbO, which is an oxygen ion conductor, is such an example (1)(2). If a solid-state electrolyte is adopted for use in an electrochemical cell the problem associated with a liquid electrolyte such as leakage can be alleviated. The cell structure also can be simplified, because the electrolyte plays the role of separator to prevent the active materials from mixing. Thus, physical vapor deposition technology may make it possible to develop a very thin film cell, which consists of only solid phases (3)(4). In this study, the thin film PbO2/PbO/Pb solid cell with a thickness· of only a few micrometers, in which all the constituents were systematically deposited on a glass substrate by reactive sputtering and vacuum evaporation, has been produced and the charge-discharge properties were investigated. An attempt was made to improve the discharge properties by doping impurities such as Na2CO3 and Sb2O3 into the PbO electrolyte. Moreover, the connection of the cells in series and in parallel to get a higher electromotive force and a larger capacity, and the charge-discharge cycling test to determine its use as a storage battery were carried out."

Jan 1, 2000

By Giacobbe Braccio, Alessandro Blasi, Assunta Romanelli, Massimo Morgana, Corradino Sposato

The solvent extraction technique is the only industrial way used to separate and purificate yttrium from other rare earths. In order to improve this process several extractants have been tested during last years. In this work, the behavior of sec-octylphenoxy acetic acid (CA-12) in Yttrium recovery from high concentrated heavy rare earth mixture was investigated. Sodium hydroxide solution was used in order to presaponify organic phase composed by CA-12 and Tributyl phosphate (TBP) diluted in kerosene. In the investigated condition, TBP confirmed its role of phase modifier not significantly altering the extraction behavior of CA-12. The CA-12-TBP system showed a high affinity in extraction for lighter rare earths such as Sm, Eu, and Gd, leaving yttrium in aqueous phase. Using a feed concentration (P [RE]) of 1 M, organic mixture is capable to extract around the 70% of metals in a single extraction test showing this extraction sequence Y < Lu < Yb < Tm < Er < Ho < Dy < Tb < Gd < Eu < Sm. Moreover for [CA-12] = 1.79 M and [RE] = 2 M the instability of extraction system occurs.

Mar 1, 2017

By Cong Wang, Kexin Jiao, Yongan Zhao, Haibin Zuo, Jianliang Zhang

The carbon composite brick is a new refractory used in blast furnace hearth and bottom. It caused wide attention due to its high thermal conductivity and low erosion by molten iron. In this paper, chemical constituents, SEM-EDS and X-ray diffraction were carried out in order to understand reaction mechanisms. A series of experiments of oxidation resistance characteristics were made. The oxidation mechanisms of carbon composite bricks in the presence of air were analyzed. According to the analysis on many experimental results, the oxidation process of carbon composite bricks under different temperatures were controlled by different mechanisms. In the condition of high temperature, SiO2 as oxidation product hindered the diffusion of O2, and reduced the oxidation loss of graphite in the internal.

Jan 1, 2015

By S. N. Monteiro, J. Alexandre, L. G. Pedroti, D. P. Santos, B. C. Mendes, A. R. G. Azevedo, G. C. Xavier

The glass cutting industry is responsible for generating large quantities of waste, during the stages of cutting and polishing. The disposal of this material generates a cost to the company, thus looking for ways to repackage it, so there is the possibility of incorporating it into the adhesive mortar. The objective of this work is the characterization of waste and assessment of the properties of these mortars, fresh, and check the possibility of their use. As for the characterization, were carried out particle size testing, density and pozzolanic activity, for the fresh state were performed tests of air content, water retention consistency and entrained particular index. Were incorporated 0,10, 15 and 20% of the amount of sand. The results showed that the material on display ha spotential for use in adhesive mortar, with values within the limits stipulated by Brazilian standards.

Mar 1, 2017

By F. Elgersma

Hydrometallurgical zinc winning processes ?are frequently based on iron containing concentrates which yield a goethite, jarosite or hematite residue. Jarosite or goethite are mostly stored in waste ponds which ,are lined with foil. Water percolating through the pond is withdrawn from the deposit ,and decontaminated before discharge. Despite these measures, more and more pressure is put upon zinc companies to treat their (historical) residues and to produce environmentally acceptable residues. The criterion which determines this acceptability is the potentiality of leaching out hazardous elements by natural processes. This paper provides the comparison of five different process designs for integrated jarosite treatment in a hydrometallurgical zinc winning plant leading to environmentally acceptable residues. The processes are esigned for producing 200 ktons/yr zinc and for treating 80 ktonslyr historical jarosite. Mass and energy balances are used to determme parameters such as: the energy use per ton waste treated and the amount and composition of final residues. The conclusion of the work is that. pyrometallurgical jarosite treatment integrated in hydrometallurgical zinc winning is preferable to hydrometallurgical jarosite treatment. Integrated pyrometallurgical processes lead to a ?smaller quantity of remaining hazardous residues and require less energy.

Jan 1, 1992

By Malti Goel

"Technology advancements in fossil fuel based energy generation and consumption are currently being aimed at minimization of CO2 emissions. To attain energy security, India must accelerate the pace of economic development, while achieving reduction in CO2 emissions per unit of energy consumed. It would need access to advanced coal utilization technologies to be demonstrated on indigenous coal characteristics. Of specific importance would be: improvement in coal quality, increasing energy efficiency and suitability of other CO2 sequestration technologies for reducing CO2 footprints. There is need to address related risks and financial burden through adoption of policies and regulations including the issue of open access in energy research. In this paper, seven important areas of strategic plan that need to be pursued for managing CO2 emissions in steel energy sector in India are discussed.IntroductionWorld is facing a crisis of climate change, which follows in the footsteps of global energy and environment crises. Accumulation of carbon dioxide from the generation and utilization of energy is leading to greenhouse warming and climate change. The global warming is causing the boundary between four seasons to be fuzzy and resulting in more spiky weather. Significance of its impact on environment is also determining the technology development needs in various sectors of economy for taking remedial measures.To respond to climate change concerns, the steel industry is undergoing a transition. It is at the threshold of a rapid change in technology as it targets innovation to achieve 50% reduction of CO2 emissions per ton of steel produced. Fossil fuel use is the main contributor of increasing concentration of carbon dioxide in the atmosphere. The control of air pollution and CO2 capture are thus relevant for a coal based industry, whether thermal power plant or a demand side energy intensive industry. World steel production has shown phenomenal increase in first eight years of 21st century increasing from 780 Mt in 2000 to 1343 Mt in 2008 [1]. It was merely 28 Mt in 1900. The global CO2 emissions from steel industry are also increasing and became 2550 Mt (3-4% of total GHG). Indian industry contribution was 161 Mt (15% of direct emissions from industry). It is likely to grow further to keep pace with the accelerated economic growth of 8-9% per annum."

Jan 1, 2010

By Rafael Colás

Computer visualization can be employed in industry as an aid to the understanding of the complex interactions between variables encountered in production. The examples of ingot casting of rimming steel and that of hot rolling of low carbon steel strip are presented. Both processes are mathematically modeled, and their results are presented in a graphical way. Such models have been proven to be an asset in quality improvements and increase of productivity as the personnel involved get a better understanding of their job.

Jan 1, 1993

By J. M. Demarthe

MINEMET RECHERCHE (IMETAL Group, formerly Le Nickel-Penarroya-Mokta) has studied on a laboratory scale and patented a new process to recover metal values -copper- from sulphide ores and concentrates. It combines a cupric leaching, solvent extraction and copper sulphate electrowinning according to the main following steps - A direct and selective leaching of copper sulphide ores or concentrates at atmospheric pressure with cupric chloride to form cuprous and ferrous chlorides and elemental sulphur. Pyrite remains in the sulphur residue. - The leach solution is separated into two parts -In the first one, air is injected to precipitate iron as goethite. The oxidation step can be easily realized at atmospheric pressure by maintaining an excess of cuprous and-ferrous chlorides in the liquor. Copper is extracted from the second part as cupric ion by an LIX reagent. Direct injection or air in the mixing chamber maintains good extraction conditions, so that only one mixer settler is required. - Iron, in the form of ferrous ion, is not coextracted. - Copper is stripped from the organic phase, transferred into a sulfuric phase and sent to sulphate electrowinning cells, which are now conventional in copper metallurgy. - Only electricity and air are required. After a feasibility study, the next step will be to develop it on a pilot and commercial scale.

Jan 1, 1976

By Wolfgang Van Hooff

Encouraged by a strongly growing and evolving market for granulated products, Paul Wurth continuously improves its granulation and dewatering technologies to provide customers with state of the art installations. Continuously developed know-how about the granulation process of iron blast furnace slag enabled application to non-ferrous materials such as Ni-Slag, Pb-Slag, Blister Copper, Cu-Matte and even TiO2-Slag, which rank among the most difficult materials to granulate. This paper identifies how critical objectives in granulation and dewatering technologies applied to different molten materials with respect to various product quality objectives can be addressed. The differences between hot and cold water granulation systems are explained, including the step from cold runner to granulation water tank. Development of a flow and pressure controlled blowing box is the latest step to optimize the granulation process in order to meet the latest standards in terms of quality, power consumption and environmental protection.

Jan 1, 2006

By Raj K. Rajamani, James R. Nagel, York R. Smith

In this work, we examine the efficacy of Electrodynamic Eddy Current Separation (EECS) to recover valuable materials from end-of-life solar panels. Traditional rotary-based eddy current separators are capable of excitation frequencies of 1 kHz or less and struggle to economically separate particles smaller than 1 cm. A new design of eddy current separators has been developed at the University of Utah which has no mechanically moving parts. The design is capable of excitation frequencies up to 50 kHz, allowing sorting of particles as small as 1.0 mm. Recently, we have been successful in separating mixtures of Si/Al and CdTe/Al particles (1–3 mm) with recovery and grades greater than 85%, an energy demand of 68 kWh/short ton of sorted material, and throughput of roughly 10 kg/h. Current and future challenges utilizing this method for valuable material recovery from end-of-life solar panels are discussed.

Mar 1, 2017

By Patrick R. Taylor

Iron phosphate glasses are promising host matrices for vitrifying actinide rich nuclear wastes materials because of their high solubility of actinide oxides, high chemical durability, and relatively low melting temperatures. An iron phosphate waste form was developed at the University of Missouri-Rolla. The structure and property of the waste form were well characterized by materials techniques. However, to scale the process and advance it to commercial viability, it is necessary to understand the processing parameters, such as the partitioning of waste elements and the viscosity as a function of temperature. Viscosity of 40 Fe203 - 60 P205 mole % iron phosphate melts (prepared with phosphorous pentoxide and ferric oxide) at 1000-1200 C was measured by the rotating-spindle method. It was discovered that this fluid has non-Newtonian behavior. Experiments were performed to study flow properties following the Standard Test methods for Rheological Properties of Non-Newtonian Materials by Rotational (Brookfield) Viscometer (ASTM D 2196-86). Samples prepared using ammonium phosphate and ferric oxide showed Newtonian behavior and the temperature dependence of the viscosity was studied over the range of 1000 to 1200 degrees C. The difference in flow behavior between the two fluids was analyzed in terms of preparation conditions and variation in the final composition and phases. The partitioning behavior of waste elements in the iron phosphate glass was studied by melting in a high temperature furnace and JCP analysis. The experimental results show that the solubility of Ce and Sr in phosphate glasses is significantly higher than the solubility associated with borosilicate glasses. This strengthens the conclusion that iron phosphate may be a viable alternative to borosilicate glass for immobilization of high heavy-metal-content wastes and actinide rich wastes.

Jan 1, 2002

By Takeshita. Takuo

"In this work, the progress of the HDDR process is discussed mainly on the Nd-Fe-B magnet system. There are three technologies being used for the Nd-Fe-B permanent magnet production; the sintering technique, the rapid quenching annealing and the HDDR process. The HDDR process utilizes· the HDDR phenomenon, in which hydrogen absorbing intermetallic compounds go through as they are heated in hydrogen atmosphere, Hydrogenation - Decomposition Desorption - Recombination. In the HDDR process, these four steps in the HDDR phenomenon are processed by choosing suitable reaction conditions regarding to hydrogen gas pressure, temperature, rate ·of desorption and etc., and we can produce permanent magnet powders of good magnetic properties with microstructures consisting with sub-micron size crystalline grains. In the anisotropic magnet powders, the sub-micron size crystals are being mostly aligned in the crystallographic c-axis direction. Possible applications of the HDDR process to other systems are also discussed.Microstructures of the Nd-Fe-B Permanent MagnetsIt is well known that magnet properties of magnetic materials are very sensitive to their microstructures [l]. This is seen in almost all magnet materials from soft magnetic materials and hard magnetic materials to magnetic memory materials. In this regard, the production technology is very important for the control of microstructures of permanent magnets The Nd-Fe-B magnet is the most powerful permanent magnet as a practical permanent magnet, and its coercivity force is much dependant on the microstructure as is the case for other permanent magnets."

Jan 1, 2000

By James C. Foley

In-situ characterizations of green state part density and sintering state have long been desired in the powder metal community. Recent advances in non-contact electromagnetic acoustic transducer (EMAT) technology have enabled in-situ monitoring of acoustic amplitude and velocity as sintering proceeds. Samples were made from elemental powders of Al (99.99%), Al (99.7%), Ag, (99.99%), Cu (99.99%) and Fe (99.9%). The powders were pressed in a uniaxial die and examined with acoustic waves for changes in velocity and amplitude during sintering. The changes in acoustic properties were correlated with mechanical properties. Evolution of a series of reverberating echoes during sintering is shown to provide information on the state of sintering, changes in sintering kinetics as well as having the potential for detection of interior flaws.

Jan 1, 2001

By G. A. Irons, D. Colbert

Several electric arc furnace (EAF) shops have increased the zinc and lead grades of EAF dust by reinjecting it into their furnaces; however, the kinetics of this operation are poorly understood. To understand the kinetics, EAF dust was injected into 70 kg heats of iron or steel in an induction furnace. Supplemental additions of carbon and oxygen to overcome the heat load on the system were also investigated. In all cases, the dust was chemically transformed, and the zinc content increased from 16% Zn to 60 - 80% Zn. About 50% of the zinc in the EAF dust dissolved in the iron or steel. The zinc oxide in the dust is thought to be reduced by carbon and the zinc vapour subsequently dissolved in the iron. A kinetic model for the dissolution process is proposed, and the implications for EAF dust recycling are discussed.

Jan 1, 2000

"Mechanical alloying (MA) synthesizing technology and thennohydrogen processing (THP) were utilized to produce nanocrystalline Ti-MMC's reinforced by TiB intermetallic compound by using TiH2-B powder mixtures. Powders MA'ed up to 8 hours were examined by X-ray diffraction and SEM study. All MA'ed powders afterwards were HIP'ed at 700, 800 and 950EC for 1 hour. Detailed XRD, SEM and TEM study of the samples were carried out to determine the structure and micrography of the Ti-TiB MMC material processed by MA+THP approach followed by HIP'ing at high temperatures.IntroductionThe fiber reinforced titanium base composites [1,2] which possess a great resistance to high temperature have been investigated. In these studies fibers of C and SiC were used as reinforcing materials. However, these fibers react with Ti-matrix at elevated temperature resulting in product formation at the interface between the matrix and the fiber. Because of the chemical reactions, strength of the product MMC material diminishes.In conventional techniques of whisker reinforced composite material production, the mixtures of matrix metal powders and dispersed fibers are consolidated by hot pressing, HIP and/or hot extrusion. These techniques, however, have some shortcomings. Hard and brittle fibers could be broken during mixing cycle of the processing. Consolidation techniques could also be the cause for fiber breakdown. Attaining of the uniform dispersion of fibers into the metal matrix is not an easy process. The chemical reactions at elevated temperature exposures in the interface between the matrix material and fiber reinforcement cause product formations leading to poor mechanical properties."

Jan 1, 1998

By den Bulck A. Van

In Europe, 50% of the copper originates from recycling. High-Cu containing scraps are regularly rich in impurities like Fe, Ni, Sn and Pb. Many high-Cu containing scraps are fed directly into anode-furnace casting installations or furnaces with limited refining capability. The impurities levels of the anodes produced in these processes should however remain acceptable for further electro-refining. The distribution of Sn between copper and slag has been investigated for conditions relevant to copper converting. Unlike previous studies, this work focuses on the behavior of Sn relevant to fire refining conditions, which are essential for anode refineries.In this study, liquid Cu–1Sn and CuOx–FeOy–SiO2 slag, with CaO additions, were equilibrated at 1300 °C in vacuum sealed SiO2 ampoules. After metal–slag equilibration, the samples were quenched in water. The composition of the slag and Cu metal was investigated with Electron Probe X-ray Microanalysis. The distribution coefficients of Sn between slag and Cu metal were determined as a function of slag composition.

By Nathaniel R. Quick

"Nd: YAG, KrF excimer, and Cu-vapor lasers are used in air to synthesize conductors and semiconductors as a second phase in silicon carbide and aluminum nitride. Conductor resistivities as low as 104 O-cm are formed in these substrates; the resistivities for the untreated substrates range from 10 11to 1014 O-cm. The silicon carbide conversion is relatively independent of wavelength while the aluminum nitride conversion shows a dependence on wavelength over the range 248 nm to 1064 nm. Silicon carbide conductors, evaluated over the range 15 K to greater than 300 K, exhibit metal like conductivity; resistivity increases with temperature. Silicon, carbon, and oxygen are identified as the principal chemical species associated with the conductor in SiC substrates while aluminum, nitrogen, and oxygen are identified as the principal chemical species associated with the conductor in aluminum nitride substrates. The silicon carbide system, which has the less complex phase diagram, is evaluated in more depth to explain the synthesis mechanism. Oxygen was principally on the surface and increasing SiC conductivity is associated with decreasing spacing between 5 µm, or less, diameter carbon globules. This technology is proposed as a replacement for metallization in electronic packages, sensors and devices. INTRODUCTIONCeramics are commonly used for multichip module, hybrid and multilayer electronic packaging; semiconductor device and sensor applications because of the insulating, conducting, semiconducting, or superconducting properties that these materials possess (1,2) The majority of ceramics, however, have not been known to exhibit conductive or semi conductive properties when exposed to rapid thermal heat processing. A ceramic and process which through selective conversion can combine two or more of these electrical properties to eliminate the need for metallization is of interest to both the commercial and military sectors."

Jan 1, 1994

By Manabu lshimaru

Solid-liquid interfaces as well as defect formation processes during crystallization of melted silicon (Si) have been examined by using molecular-dynamics (MD) simulations. The ordinary Langevin equation employing the Tersoff interatomic potential was used for the calculation of the atomic trajectories. A solid-melt interface has a tendency to form {]] I} microfacets during the crystal growth in the [001] direction, while it is essentially flat during the (Ill) crystallization. Because of the difference of the interfacial structures, the structures of grown-in defects and defect evolution depend strongly on the growth direction. We discuss defect structures and their formation processes within the context of our results as well as previous experimental observations.

Jan 1, 2001

By Muhamad Firdaus

There is a growing interest in Magnetoelectric (ME) materials in view of both fundamental understanding and novel desirable applications. The application potential for multiferroic materials with the possibility of reversing the magnetization by applying an electric field (or vice versa) is quite promising especially in data storage application. The rare earth ortho-ferrites (REFeO3), such as NdFeO3, have been studied extensively in recent study in the context of discovery of magneto-electric (ME)/multiferroic nature materials. In this paper a potential high temperature recovery of rare earth elements in the form of REFeO3 from waste permanent magnets using direct oxidation in air was investigated. It was found that REFeO3 (NdFeO3) phase can be separated from the other oxide phases by thermal treatment of NdFeB magnet waste at 1100 °C in air atmosphere. The REFeO3 also found to have different physical characteristic (density) from the other layers and can be separated physically. This paper will include a proposed flowsheet to recover Nd as NdFeO3 through powder separation. The technique can be beneficial and favourable for RE recycling and recovery from waste permanent magnets.