By Xiao-hui Fan, Li-shun Yuan, Xu-ling Chen, Wei Lv, Min Gan, Yi Wang

"As the amount of ferrous scrap increases every year, it becomes more and more urgent to deal with this iron-bearing resource properly. This paper puts forward a method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing), and these cold-bonded pellets can be used as coolant in a converter. The influence on the pellets qualities by using different kinds of chloride as rust agents is studied, and results show that the strength of cold-bonded pellets increases significantly by using a combination of the three kinds of chloride -NaCl,MgClz,FeCh, their best dosages are 1.2%, 0.2%, 0.1% respectively. Other iron-bearing materials also have an effect upon the pellets strength, by adding 5% iron powder and maintaining for 48h, the compressive strength of the clumps surpass 2500N/A, dropping strength surpass 4 times/ A, and 10% iron slag or 20% steel slag can replace 5% iron powder while obtaining the comparative quality. The influence of different ratios of three ferrous scrap (converter mud, iron scale and dust) is further studied, and results show that when the ratio is 30% : 30% : 40%, the pellet strength reaches the maximum. After maintaining for 24~48h, the clumps can meet the mechanical as well as the physical-chemical requirements as BOF steelmaking refrigerant.IntroductionGreat amounts of converter mud, dust and iron scale are produced in steel production process. These materials are of great values, and their accumulation not only leads to environmental pollution, but also wastes the precious resources, which restricts the sustainable development of the steel industry [1,2] The main approach at present to dealing with the ferrous scrap is to add them into sintering. But in this way, the utilization factor of sintering and the quality of sinter decline while the energy consumption increases [3].Therefore, more advanced and efficient technology is needed to make the best of these iron resources. Cold consolidation of ferrous scrap is a simple process that has many advantages such as less investment, quicker effect, lower energy and lower cost [4-5] But the conventional maintaining period is too long, usually up to four-six weeks, and the pellet strength is low. Therefore, the key points of the cold-bonded pelletizing are to develop a new adhesive [4,5] to shorten the natural maintenance cycle and to improve the strength of the pellets. A method on resource-oriented utilization of ferrous scrap (cold-bonded pelletizing) is brought forward, and these cold-bonded pellets can be used as coolant in converter. After maintaining for 48h, these cold-bonded pellets can satisfy the mechanical requirements to replace the converter coolant [6]."

Jan 1, 2013

By Farouk T. Awadalla

The presence of humic species in spent Bayer liquor causes many processing problems in the production of aluminum hydroxide. Ozonation of spent Bayer liquor was found to be an effective process to destroy the colored humic species. The kinetics of the decolorization in spent Bayer liquor was found to be slower than in the alkaline humic acid solution containing no alumina. However, the reaction kinetics ware enhanced by heating the solution during ozonation above room temperature. Copper ions which are used as catalyst to enhance the ozonation reaction were found to be ineffective due to the presence of large quantities of aluminum hydroxide in the liquor. Ozonation was a more favorable process than membrane separation as it achieved about 92% separation of color and produced lower amounts of organic material. The treated spent Bayer liquor can be recycled to the upstream process without causing any difficulties and the purity of aluminum hydroxide product would also be improved. A comparison of preliminary cost data indicated that ozonation compares very favorably with membrane separation in this application. Key words: ozonation, Bayer liquor, aluminum hydroxide, humic species, copper ions, membrane separation, purity and economic.

Jan 1, 1994

By James W. Reeves

DuPont was the titanium metal pioneer who put the greatest effort into both R&D and commercial sponge and powder metallurgy production. This was concentrated in the period 1945 through 1963. The commercial results were development of the chloride process for TiCl4 using ilmenite, development and improvement of the Kroll process, development of a modified Hunter process to make titanium powder and commercial development of a direct powder process. The powder metallurgical process failed because of the inability to meet powder chloride specifications. All this work remained a trade secret until published in NMAB -392 by Mahla in 1983. There were other processes explored by DuPont, both improved sponge and powder processes. Much of this work has been continued by others but none, as of yet, resulting in new improved titanium metal capacity.

Jan 1, 2001

By C. S. Griffith

Lithium Australia NL (ASX:LIT) and ANSTO Minerals have been working together since 2015 on the development of halide accelerated leaching for the extraction of lithium from lithium-bearing micas, spodumene and clays. This technology has been termed SiLeach® process. The driving force behind development of the SiLeach® process, initially, was to develop a hydrometallurgical process to extract lithium from micas and spodumene without the need for the energy intensive, high temperature processing conventionally applied to lithium extraction. This driving force remains today and continues to hold promise in realising the value of previously under-utilised lithium resources. A comprehensive understanding of the technology and its applicability to the processing of micas and spodumene currently exists, and the flowsheet has been rigorously piloted. Production of battery grade lithium carbonate has been demonstrate

By K. Morsi

Carbon nanotube (CNT) reinforced metallic composites have been recently generating significant scientific interest, due to their expected superior properties compared with other composites. Out of the metallic matrices investigated for reinforcement with CNTs, aluminum has received considerable attention. A major problem has been the dispersion of CNTs in metallic matrices. This paper discusses preliminary results on the mechanical dispersion of CNTs in aluminum powder, powder processing, stability and characterization of aluminum dispersed with CNTs at reinforcement levels equal to and below 5 wt.%.

Jan 1, 2009

By Yuanbo Zhang, Zhixiong You, FENG ZHOU, Guanghui Li, Zhengwei Yu, Zhiwei Peng

Reduction disintegration of sinter significantly affects the coke consumption and productivity of blast furnace smelting. As we know, the reduction disintegration index (RDI+3.15) of sinter obtained from titanomagnetite concentrate is relatively worse than those from ordinary iron ores. In this study, the effect of sintering parameters, mainly involving coke breeze dosage and basicity on sintering indexes was investigated using titanomagnetite concentrate as raw material in an experimental-scale pot. Subsequently, RDI+3.15 of the sinter was detected according to the Chinese standard of GB/T13242-91. The results show that RDI+3.15 rises with the increase of coke breeze dosage, while it decreases with increasing basicity from 0.5 to 2.0 and then increases in the basicity range of 2.0-3.0. Finally, the microstructure of sinter before and after reduction was studied. And the mechanism of reduction disintegration was preliminary revealed by analyzing the morphologies and distributions of minerals in the sinter.

Jan 1, 2015

By Zhang Hanbo, Niu Liping, Zhang Zhiqi, He Jicheng, Dou Zhihe

"Rutile, ilmenite and Al-Ca complex reducer were used to prepare high titanium ferrous alloy by enhanced reduction-SHS method. The effects of the complex reducer compositions and slag types on the enhanced reduction-SHS process were investigated. The high titanium ferrous alloys were characterized by XRD and SEM. The results indicate that the high titanium ferrous alloys consist mainly of TiFe2, AlTi3 and Al2O3. The oxide inclusions exist resulting in directly the high oxygen content and micro-structural defects in the alloys. The titanium and oxygen contents decrease, but the aluminum content in the alloy increases while the mass ratio of calcium in the Al-Ca complex reducers increases. When the mass ratio of Al/Ca in the Al-Ca complex reducer is 6:1, titanium, oxygen and aluminum contents are 63.75%, 3.01% and 10.72% respectively. When the mass ratio of Al/Ca is 5:1 titanium content is 55.00% nearly and aluminum content is higher than 14.00%, but oxygen content is lower than 2.0%.1. IntroductionThe high titanium ferroalloys with 65%~75% titanium have the advantages of low melting point and high titanium content. They are widely used in special steel refining, while they are also a kind of very important quality orientation alloys in the rage of aviation and aerospace. At present, the methods of preparing high titanium ferroalloy include vacuum remelting and thermit reduction. The alloys prepared by the vacuum remelting method have good qualities and low oxygen content, so it is widely used in Russia, Western Europe and other developed countries. In China, there are abundant rutile resources, but waste titanium is lack, therefore, the preparation method is the thermit reduction. But there are many quality defects in the high ferrotitanium alloy, including high oxygen content, unstable quality and so on. In order to improve the qualities of the high titanium ferroalloy, especially to reduce oxygen content, the domestic and overseas have done a lot of further researches. For example, Sichuan E-mei ferroalloy plant and Beijing Nonferrous Metal Research Institute have prepared high titanium ferrous with 73.77% titanium with natural rutile, but the oxygen content is high. Through controlling the quality of raw material, they obtained the better qualities, but the oxygen content is still very high. South Africa Mintek company have prepared high titanium ferrous alloy with low nitrate by plasma heating under the isolation air conditions, but they couldn’t also remove effectively oxygen in the alloy. The oxygen exists in the form of Al2O3 and titanium protoxide. So it can be speculated that except TiO2 not being fully reduced, the no-sufficient alloy-slag separation is the direct reason resulting in high oxygen and poor microstructure. In view of present technical difficulties during preparing high titanium ferroalloy by thermit reduction, this paper proposed a new method of preparing high titanium ferrous with low oxygen by enhanced reduction-SHS with Al-Ca complex reducer. Ca in Al-Ca complex reducer has stronger reductive ability, it can effectively strengthen the reductive degree of TiO2. The slagging agent CaO CaF2 and MgO can effectively reduce the viscosity of Al2O3 slag to improve its liquidities to strengthen alloy-slag separation effects so that to remove inclusions and oxygen. In this paper, effects of slagging agent type on the reduction and the qualities of high-titanium ferroalloy were studied."

Jan 1, 2012

By Supachai Surapunt

The distribution behavior of V A minor elements (As, Sb and Bi) in the smelting stage of the Mitsubishi process were evaluated thermodynamically based on thermodynamic data and operating data. The fractional distributions between the gas, slag and matte phases considered as the degree of vapor saturation of 1.0 are as follows: 53.8, 27.2 and 19% for As, 23.6, 56.6 and 19.8% for Sb, and 91.3, 1.1 and 7.6% for Bi, respectively. Arsenic is mostly distributed to the gas and slag phases. It is effectively eliminated by volatilizing and slagging. Antimony is mainly in the slag phase, which is suitably removed by slagging. Bismuth is easily vaporized to gas phase. The degree of vapor saturation has a large effeet on the distribution behaviors of the three elements between the three phases. The amount of a minor element in the charge has an effect on the distribution of As but no effect on the distributions of Sb and Bi. Increasing matte grade and temperature results in the change of distributions for As and Sb, significantly. The change in the distribution ratio between slag and matte phases also considerably affects the distributions of As and Sb. The distribution behavior of Bi is not significantly changed by the change in matte grade, temperature and distribution ratio.

Jan 1, 2003

By Supachai Surapunl

The distribution behavior of VA minor elements (As, Sb and Bi) in the smelting stage of the Mitsubishi process were evaluated thermodynamically based on thermodynamic data and operating data. The fractional distributions between the gas, slag and matte phases considered as the degree of vapor saturation of l.0 are as follows: 53.8, 27.2 and 19% for As, 23.6, 56.6 and 19.8% for Sb, and 91.3, l.1 and 7.6% for Bi, respectively. Arsenic is mostly distributed to the gas and slag phases. It is effectively eliminated by volatilizing and slagging. Antimony is mainly in the slag phase, which is suitably removed by slagging. Bismuth is easily vaporized to gas phase. The degree of vapor saturation has a large effect on the distribution behaviors of the three elements between the three phases. The amount of a minor element in the charge has an effect on the distribution of As but no effect on the distributions of Sb and Bi. Increasing matte grade and temperature results in the change of distributions for As and Sb, significantly. The change in the distribution ratio between slag and matte phases also considerably affects the distributions of As and Sb. The distribution behavior of Bi is not significantly changed by the change in matte grade, temperature and distribution ratio.

Jan 1, 2003

By Liu Chunpeng

Under an inert atmosphere, the temperature enhancement of nickel bearing pyrrhotite irradiated by microwave was measured with a special metal-sheathed thermocouple and the non-isothermal rate equations were obtained. Under the controlled oxygen potential of the reacting gas in the microwave field, over 90% sulfur contained in the pyrrhotite is converted into elemental sulfur directly, the iron and the nickel are transformed into FeO,, NiO, NiFe,O, and FeSiO,. According to the experimental data the rate of the elemental sulfur produced is in diffusional control and the non-isothermal equation derived is

Jan 1, 1993

By S. P. Mathew

The ISASMELT Lead Process is a continuous two stage process for the production of crude lead from concentrate. It is based on the use of a top entry submerged Sirosmelt lance to produce turbulent baths in which high intensity smelting or reduction reactions can occur. The process involves oxidizing the concentrates in the first stage to produce a high lead slag. This slag is tapped continuously and transferred down a launder to a second furnace where it is reduced with coal. Crude lead and discard slag are tapped continuously from this furnace through a single taphole and separated in a conventional forehearth. Process and engineering design work for a commercial scale Lead ISASKELT plant designed to produce 60000 tpa crude lead has been completed. This plant is planned to be operational in 1991.

Jan 1, 1990

By Oleg Ostrovski

Industrial pyrometallurgical processes in ferrous metallurgy are based on carbothermal reduction of metal oxides. Carbothermal reduction of stable oxides requires high temperatures. Lowtemperature reduction can be implemented by using methane-containing gas with high carbon activity, or by carbothermal reduction under reduced CO partial pressure. Under standard conditions, methane is thermodynamically unstable above 550 °C and decomposes to solid carbon and hydrogen. At appropriate CH4/H2 ratio and temperature, carbon activity in the methane-containing gas phase can be well above unity relative to graphite, which provides favorable thermodynamic conditions for reduction. To maintain these conditions, the rate of reduction/carburisation should be higher than the rate of solid carbon deposition. The paper discusses reduction of pure manganese and chromium oxides at relatively low temperatures, and constraints in reduction of manganese and chromium ores. Reduction of metal oxides by carbon in hydrogen as an alternative use of natural gas is also discussed.

Jan 1, 2014

By B. J. Jody

At Argonne National Laboratory, we have been developing a potentially economical process to recycle automobile shredder residue (ASR). We identified three potentially marketable materials that can be recovered from ASR and developed technologies to recover and upgrade these materials. We built and tested a field-demonstration plant for recycling polyurethane foam and produced about 2,000 lb (907 kg) of recycled foam. Several 300-lb (I36-kg) samples were sent for evaluation and were found to be of marketable quality. We are also preparing for a large-scale test in which about 200 tons (181 tonnes) of ASR-derived fines «0.25 in. [<0.62 cm]) will be used as a raw material in cement making. A major cement company has evaluated small samples of fines prepared in the laboratory and found that they meet its requirements as a substitute for iron ore or mill scale. We also produced about 50 lb (23 kg) of recycled acrylonitrile butadiene styrene (ABS) from obsolete automobiles and found that it has properties that could be readily upgraded to meet the specifications of the automotive industry. In this paper, we briefly discuss the process as a whole and summarize the results obtained from the field work on foam and fines recycling.

Jan 1, 1996

By J. Szekely, S. Rhee

"A mathematical formulation has been presented to describe heat and fluid flow phenomena in CVD operations. In the statement of the problem, which included consideration of plasma enhanced CVD systems, emphasis was placed on identifying the parameters which play a key role in determining the rate and the spatial uniformity of the deposition process. This was done both through the appropriate dimensionless groups and by presenting an extensive set of computed results. The main conclusions that may be drawn from this work are that the deposition rate will be inherently non-uniform for atmospheric CVD systems; this may be somewhat ameliorated by inclining the susceptor or changing the vessel contours. Operation at greatly redeced pressures and for PECVD systems will give a much more spatially uniform deposition rate.1. INTRODUCTIONIn recent years, there has been a growing interest in chemical vapor deposition techniques for the preparation of thin films for semiconductor, photovoltaic applications and for coatings in general, as evidenced by numerous journal articles and symposium proceedings devoted to this topic (1-6). An interesting variant of this technique is to perform the deposition in a plasma or glow discharge at low pressures because this technology obviates the need for the thermal decomposition of the precursor at the substrate surface and permits operation at greatly reduced temperatures (7-10).By far, the largest portion of the reported work dealing with both these aspects of the technology has been concerned with the characterization of the deposit, quite properly so. However, in more recent times it has been realized that the transport aspects of these processes are also deserving of attention because the understanding of heat flow, fluid flow and diffusional phenomena may provide the key to the solution of problems associated with obtaining uniform deposits and the proper scaling of laboratory measurements in order to design industrial CVD systems."

Jan 1, 1986

By B. J. Jody

Each year, about 11 million tons of metals (ferrous and nonferrous) are recovered in the U.S. from about 10 million discarded automobiles. The recovered metals account for about 75% of the total weight of the discarded vehicles. The balance of the material or shredder residue, which amounts to about 3 million tons annually, is currently landfilled. The residue contains a diversity of potentially recyclable materials, including polyurethane foams, iron oxides, and certain thermoplastics. This paper discusses a process under development at Argonne National Laboratory to separate and recover the recyclable materials from this waste stream. The process consists essentially of two- stages. First, a physical separation is used to recover the foams and the metal oxides, followed by a chemical process to extract certain thermoplastics. The status of the technology is discussed, and the process economics are reviewed.

Jan 1, 1994

By Yoshifumi Abe, Akinori Toraiwa

"Nippon Mining & Metals started a new copper anode slime treatment plant that processes slimes in a chloride media. The basic plan of the process was proposed by Mr. James E. Hoffmann and Nippon Mining & Metals modified and advanced to produce precious metals in acceptable qualities for the company. The process has a wet chlorination stage of decopperized slimes, a solvent extraction and a reduction stages of gold, a silver chloride reduction stage and separative reduction stage of its gold extraction raffinate. The new plant of this process started in 1997 and has been operated in good condition.IntroductionThe old anode slime treatment plant of Nippon Mining & Metals, located in it's Hitachi Refinery, processed anode slimes through a combination of pyrometarllurgical processing and electrorefining. There was a need to plan a future of the plant because the maintenance cost increased year by year and a new selenium registration was going to be applied to the plant. Some plans were discussed and the result was that the process proposed by Mr. Hoffmann was superior among them.Nippon Mining & Metals started 'to examine the process and the experimental result showed that the process had an ability to be its new process but further research should be necessary to produce precious metals in acceptable qualities. The final process flow has some modified and additional stages to be suitable for its requirement. Silver processing stage is quite changed. Gold extraction stage has a new step to polish gold loading DBC. Gold extraction raffinate treatment stage is advanced to be able to recover precious metals, selenium and tellurium, separately. Aeration under atmospheric pressure is employed in decopperizing stage.The basic design of the new plant started in 1995 and finished in 1997. The construction of the new plant began in April 1997 and finished in October. The plant has been operating well after the four months test operation."

Jan 1, 2000

By Richard D. Hagni

The techniques of reflected light microscopy and cathodoluminescence microscopy are uniquely suited to the study of the products from many important industrial problems. Ref1 ected 1 ight microscopy provides the means to rapidly identify the mineralogy of an industrial sample, determine the abundance of each phase, and examine the mineral intergrowths or textures. Cathodoluminescence microscopy is a relatively new instrument that provides the means to cause many minerals to cathodoluminescence under the microscopy. The cathodoluminescence of a mineral allows it to be readily distinguished from other phases that differ in cathodoluminescence but are similar in optical properties. Cathodoluminescence microscopy is especially useful to detect cathodoluminescence minerals that are present in only small quantities. Reflected 1ight microscopy and cathodoluminescence microscopy have been successfully applied in studies of beneficiation products, prediction of beneficiation and leaching problems, phosphatic iron ores and mill products, pyrometallurgical products, roasted refractory gold-bearing sulfides, ceramic build-ups, electric arc furnace and smelter dusts, and other industrial products.

Jan 1, 1993

By B. R. Davis, Neale R. Neelameggham, R. E. Brown

The element Calcium element has a unique place in the production of etals, intermetallics and other compounds. The unusualness arises from the fact that we have several possible reductants – metallic calcium, calcium carbide, calcium cyanamide and calcium hydride. A review of how metallic calcium is manufactured and utilized is presented. The difficulties involved in producing the metal in large quantities and price implications are noted. . Fundamental thermodynamics of how these act as reductants are shown, along with the historic application of these in metal production during the past century and a half. Alternate applications as to how to control the cost of the reductant is indicated, such as the numerous attempts in making low cost titanium utilizing direct or indirect calcium reductant.

Jan 1, 2014

By Armando Valenzuela

Arsenic has been a common impurity in copper sulfide concentrates treated pyrometallurgically in Chile, which inevitably during the smelting-converting process reports in the final copper product affecting its properties, but also affecting environment as a very toxic occupational hazard. The enforcement of air quality standards, which regulate pollutants such as sulfur dioxide, particulate matter, and arsenic, has resulted in the implementation of pollution abatement plans and emission reduction schedules mainly by state-owned copper concentrate smelters. Investments associated with these plans incorporated gas-handling systems in order to capture polluting emissions. Electrostatic precipitators recover dusts containing mainly Cu and As which are leached to recover copper, while arsenic is disposed currently in the form of ferric arsenate. Gases containing high sulfur dioxide content are treated in plants to produce sulfuric acid, which is used in various classical and new hydrometallurgical processes. Additionally, smelters have effluents treatment plants for arsenic disposal either as ferric arsenate or calcium arsenate/arsenite. This paper reviews the environmental situation of the Chilean metallurgical industry, and the present trends for arsenic management are particularly emphasized since Chile is the world?s largest copper producer.

Jan 1, 2006

By Jayagopal Uchil, M. Krishna, Shanta Sastcy

"Damping behaviour of aluminite particulate reinforced ZA-27 alloy metal matrix composites processed by compocasting method is studied. The weight percentage of particulate reinforcement is 0,1,2,3, and 4%. A dynamic mechanical· analyzer is used ·to measure the damping capacity and dynamic modulus at the natural frequency of the specimen over a temperature range of 30°C to 300 °C both in the heating and cooling cycle. The damping capacity of the material is found to increase with increase in temperature and weight percentage of aluminite reinforcement although this is accompanied by a decrease in dyliamic modulus.The damping capacity and dynamic young's modulus exhibit a sharp decrease in their values around 300 °C a8 ZA-27 alloy undergoes a first order phase transition in this region which is confirmed by Differential scanning calorimetric studies. Several damping mechanisms have been evaluated theoretically for the material under study. The damping capacity at low temperatures is attributed primarily to coefficient of thermal expansion mismatch induced dislocations and high intrinsic damping of the matrix. At higher temperatures the damping capacity is attributed to ZA-27/aluminite interface, phase transformations and thermoelastic damping.IntroductionMetal matrix composites. (MMCs) offer designers many added benefits, as they are particularly suited for applications requiring good strength at high temperature, good structural rigidity, dimensional stability, and lightweight [1-5]. At present, the usage of ceramic particles as reinforcement in MMCs has attracted considerable interest from scientists and engineers. The MMCs show substantially improved elastic modulus, strength, stiffiless, and tribological properties with low coefficient of thermal expansion compared with the unreinforced matrix material."

Jan 1, 2000