By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-SiO2 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [w(MgO)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, w(Fe)/w(Si02) is 1.1-1.4 and the temperatures are within 1473-1773K, the slag viscosities increased with the increase of W(MgO) and w(Fe)/w(SiO,). When w(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When w(MgO)>10%, the temperature should be kept above I 633K. When the content of MgO is higher, a lower viscosity slag can be produced by decreasing the ratio of w(Fe)/w(SiO,). The appropriate ratio of w(Fe)/w(SiO,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-Si02 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [m(Mgo)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, m(Fe)/m(SiO2) is 1.1-1.4 and the temperatures are within 1473?1773K, the slag viscosities increased with the increase of m(Mgo) and m(Fe)/m(sio,). When m(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When m(Mgo» 10%, the temperature should be kept above 1633K. When the content of MgO is higher, a lower viscosity slag ean be produced by decreasing the ratio of m(Fe)/m(sio,). The appropriate ratio of m(Fe)/m(sio,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Jinsheng Wang, Wei Lv, Xuewei Lv, Pingsheng Lai, Jie Dang

The isothermal reduction kinetics of vanadium titanium magnetite sintering ore was investigated by thermo-gravimetric analysis at a temperature range of 1123–1223 K under 30% CO + 70% N2 gas mixtures. The apparent activation energy of reduction was calculated by iso-conversional method and its value is 36.7 kJ/mol. The model function describing the reduction mechanism was discussed by Sharp analysis and the results revealed that the reduction process is controlled first by random nucleation and nucleus growth mechanism (RNNGM) as reduction degree is lower than 0.5, followed by the mixed influence of RNNGM and phase boundary reaction when reduction degree is higher than 0.5.

Mar 1, 2017

By A. J. Schindler, F-P Sawyer, T. Logan, M. L. Shutey-McCann, R. M. Perry

"Test work on biooxidation pretreatment of low-grade refractory gold ores has been ongoing at Newmont Gold Company since 1988, including laboratory testing and pilot biooxidation heaps (360 to 23,000 tonne). Metallurgical results of the biooxidation process utilizing Thiobacillus ferrooxidans (T. ferrooxiddans) have culminated in the design, construction, and operation of a biooxidation demonstration facility. The facility has processed 708,000 tonnes of refractory ore, using a batched process with separate pads for biooxidation and ammonium thiosulfate gold extraction. Siliceous sulfidic refractory (SSR) and carbonaceous sulfidic refractory (CSR) ores are treated separately during biooxidation pretreatment unit operation. Following biooxidation, the ores are neutralization with lime and placed on oxide leach pads or stacked on the ammonium thiosulfate leach pad. Gold is leached with either cyanide for SSR ores or ammonium thiosulfate for preg-robbing CSR ores.This paper will only address the biooxidation pretreatment process of the SSR and CSR ores.AcknowledgmentsThe authors appreciate the cooperation and approval of Newmont Gold Company Carlin Operations management for its support and permission to publish this paper. The paper draws on efforts and assistance of the following people and several others which are to many to list who participated over the past five years in bringing this project to its fruition: Dr. James A. Brierley, Chief Microbiologist, Newmont Metallurgical Services; Dr. Rong-Yu Wan, Metallurgical Manager, Newmont Metallurgical Services."

Jan 1, 1997

By Naiyang Ma

"High oil concentration is one of the major barriers for recycling of mill scale of steel hot rolling mills. It is of vital importance to find cost-effective technologies of reducing oil concentration in mill scale in order to recycle the mill scale without causing detrimental effects on production and environment. This paper discusses in-process separation of mill scale from oil at steel hot rolling mills. Formation of mill scale and status of oily wastewater at hot rolling mills are reviewed in the first place. A mathematical model is then formulated to relate oil concentration in mill scale to physical properties of mill scale, chemical and physical properties of wastewater and interacting parameters between mill scale particles and wastewater. From this model, three approaches of in-process separation of mill scale from oil are derived: (1) avoiding contacts between mill scale particles and oily wastewater, and (2) maintaining low oil concentration in wastewater, and (3) collecting mill scale in upper streams of wastewater flows. In-process separation of mill scale from oil might have advantages of lower capital cost, lower operating cost and less additional environmental concerns, compared to other strategies of separating mill scale from oil.IntroductionHot rolling is an inevitable step in producing finished steel products. Figure 1 schematically shows a steel hot rolling process. Semi-finished steel products, slabs here, are reheated first, and then the reheated slabs are discharged from the furnaces and transported on hot rolling trains to descaling units for removing scale with pressurized water. After being descaled, the slabs are rolled by roughing mills. After treated with cropping and the second descaling, the slabs are finally rolled into finished products, coils here, by finishing mills."

Jan 1, 2012

By Jerold L. Johnson

Remediation of small-arms firing ranges is being investigated by the Naval Civil Engineering Laboratory and the U.S. Bureau of Mines. Scheduled closures of military installations, as well as the management of active ranges, require the development of methodologies for heavy metals removal to prevent their entering the surrounding environment. The impact berms contain high concentrations of metals, and the soil and vegetation surrounding the berms were found to have slightly elevated levels. The heavy metals characterized are in the form of whole bullets, a wide size distribution of free fragments, smeared lead on the surface of the soil grains, and very finely attached particles. Gravity beneficiation can remove liberated metal contamination effectively. Weak acetic acid leaching shows promise in lowering the final metal contamination to allow the ,soil to pass the Environmental Protection Agency&apos;s (EPA) Toxicity Characteristic Leaching Procedure (TCLP) criteria.

Jan 1, 1993

By Zhou Wenbin

In this paper the mechanical properties of high carbon equivalent cast iron for automobile brake discs were analyzed through thermal analysis curves. Experiment results show that the mechanical properties have a strong correlation with thermal analysis curves and an effective way to predict the mechanical properties of high carbon equivalent cast iron was proposed based on the features of thermal analysis curves.

Jan 1, 2010

By Hong Yong Sohn, Miguel Olivas-Martinez, Zhixue Yuan

A novel flash ironmaking process that directly reduces iron oxide concentrate particles by gas is under development. The goal of this work was to study the possibility of reoxidation of iron particles in various gas mixtures. As the product iron cools down in the lower part of the flash reactor, conditions may become favorable for reoxidation because of equilibrium and high reactivity of iron particles. The effects of temperature (823 – 973 K) and H2O partial pressure (40 – 100 pct., Ptotal = 86.1 kPa) on the reoxidation rate were examined. The pressure dependence was first order with respect to water vapor, and the activation energy was 146 kJ/mol. A complete rate equation that adequately represents the experimental data was developed. For oxidation in O2-N2 mixtures, the effects of temperature (673 – 873 K) and O2 partial pressure (5 – 21 pct., Ptotal = 86.1 kPa) were determined. Reoxidation in pure CO2 was also investigated at 873 – 1073 K for comparison.

Jan 1, 2014

By Leonel Contreras

The gas treatment system, MALIGAS (in Spanish MAnejo y Llmpieza de GASes which means handling and cleaning of gas), is part of the Codelco-Chile Potrerillos Smelter decontamination plan; which includes the newly designed system for the cooling and cleaning of the gas generated from a Teniente Converter and four Peirce Smith Converters. The gas generated in the process is captured by water cooled hoods and mixed with air. Then the gas enters a cooling pre-chamber which utilizes a water cooled screen to capture and remove the coarse and semi-fused particles. At this stage; the gas loses a portion of its heat with temperature falling below 608°C which is a necessary condition to avoid damage to the pipes, ducts and other metallic structure of the gas handling system. The gas is further cooled at the Radiation Cooler to a temperature ranging between 315 and 380°C. The gas is conditioned to avoid damage to the electrostatic precipitators that are designed to clean the gas by removing significant amount of dusts from the: gas stream. This gas stream is currently discharged to the stack, however, it will be treated in a sulfuric acid plant that is currently under construction and is scheduled for commissioning during the second half of 1999. The gas handing and cleaning system has been operated without any significant interruptions. Minimal emissions of SO2 and dusts in the work place are noted. The system requires minimum maintenance. The key to the high availability of the system is due to the good, performance of he Radiation Cooler, which efficiently cools the gas before entering the electrostatic precipitators (ESPs). This enables the ESPs to remove the dusts efficiently.

Jan 1, 1999

By Batric Pesic

A hydrometallurgical process for recovery of Zn and Mn from Bunker Hill Water Treatment Plant sludge was developed. The process is unique because it treats an unusual combination of metals, Zn and Mn. Another non-standard feature of the process is that leaching takes place with ~S04 in the presence of a reductant (SO2). Zn and Mn are recovered simultaneously by electrowinning, Zn on a cathode and Mn on an anode, as MnO2 The major purpose of the process is to detoxify the sludge by removing toxic heavy metals. The recovered metal values could be marketed to offset the overall costs of water and sludge processing. This work is presented in two separate parts, 1. Leaching and Solution Purification, and II. Electrowinning. This paper covers only the first part of the hydrometallurgical process: Leaching and Solution Purification. Initially, the paper briefly discusses the history of the pollution problem at the Bunker Hill Superfund Site, the origin of heavy metals in the mine waters, and the development and use of the water treatment plant. The leaching of sludge was examined as a function of the following parameters: constant vs. initial pH, initial vs. delayed addition of SO2, temperature, and pulp density. It was found that leaching with H2SO4 at pH 2.0 for 15 minutes (at 60°C), followed by S02 addition for another 15 minutes, could completely dissolve Zn and Mn. Solution purifIcation was done in three stages. In the first stage iron was removed by adjustment of pH (to pH 5.0) and oxidation offerrous to ferric iron (with H2O2). In the second stage, Cu and Cd were removed by Zn dust cementation. Finally, Co and Ni were precipitated with the organic reagents 1-2 nitroso-naphthol and nitroso, respectively. Electrowinning of Zn and Mn is discussed separately in Part II of this paper.

Jan 1, 1996

By Shu Xinqian, Zhou Weining, Shan Zhiqiang, Feng Jifu

"Modified calcination conditions on the extraction of rubidium resources from muscovite (KAlz[AlSi301o](OH)2) ore are systematically studied. The impact of various factors on the rubidium leaching rate is also analyzed, including the agent types, roasting time, the mass ratio, roasting temperature, etc. The results indicate that the best agent is a combination of sodium chloride and calcium chloride, its mass ratio ofmuscovite/NaCl/CaClz is 1:0.25:0.25. Calcined at 8500 for 30 minutes, the rubidium leaching rate is up to 90%. The reaction of muscovite ore with the chlorinating agent CaC12 has been studied by TG/DSC, the calcined intermediates are identified by XRD, and the surface morphology before and after leaching is characterized by SEM. Rubidium chloride products can be obtained with a purity of 92% by using t-BAMBP extraction, hydrochloric acid reextraction and purification.IntroductionRubidium is one ofrare alkali metals, which is found in 1981 by German R.W. Bunsen and G.R. Kirchhof. Rubidium includes the following features: atomic number is 37, each atom weight 85, the body-centred cubic lattice, each unit cell has two metal atoms, and the density is 1.532g/cm3. The properties of low melting point (312.46 K) and malleability make rubidium have a strong chemical activity and photoemission. Rubidium provides a main material for manufacturing phototube with a wide range oflight waves, which possess high sensitivity and stability. Efforts are being made to carry out research on rubidium ion gngine, magnetic flux generators and thermoelectric transudcer, etc. Rubidium exists in muscovite ore(KA12[AlSh01o](OH)2 (monoclinic system and hexagonal layered structure) as isomorphism and replace the large radius of the potassium atoms, as well as part of rubidium locate between structure layers. The complex components bring great difficulty in comprehensive recycling."

Jan 1, 2013

By Chang Wei, Zhigan Deng, Minting Li, Cunxiong Li, Gang Fan, Xingbin Li

Molybdenum and nickel in black shale ore exists as amorphous sulfides which has highly active, and easily oxide to sulfuric acid and sulfate at low temperature in the presence of excess oxygen. Take advantage of the characteristic to leach molybdenum and nickel from black shale. Oxidation, conversion and dissolution behavior of amorphous colloidal molybdenum and nickel sulfide in pressure leaching process was studied. The effects of stirring speed, temperature, concentration of sulphuric acid, oxygen process and mineral granularity on molybdenum and nickel leaching were investigated. The results showed that dissolution rate increased with increasing temperature and stirring speed, but decreased with increasing concentration of sulphuric acid. And dissolution of molybdenum and nickel from ore only need oxygen without any other reagent.

Mar 1, 2017

By A. Arenas-Flores, Pandiyan Thangarasu, J. P. Hernández-Lara, F. R. Barrientos-Hernández, J. A. Romero-Serrano, A. Hernández-Ramírez, M. Pérez-Labra

BaTiO3 doped with Gd3+, was synthesized from BaCO3, TiO2, and Gd2O3 as powders using the solid state reaction method (Ba1-xGdxTi1-x/4O3). The milling of the precursors was performed in an agate mortar with acetone as control means and compositions x = 0.001, 0.005, 0.05, 0.15, 0.25, 0.35 Gd3+ (wt%). Firstly, the powder mixture was decarbonated at 900 °C for 8 h, after it was sintered at 1400 °C for 5 h. Tetragonality of synthesized BaTiO3 doped with Gd3+ was analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Raman spectroscopy (RS). Subsequently, the powders sintered were uniaxially compacted cold until to obtain pellets of about 10 mm in diameter; which again were sintered at 1400 °C for 4 h. XRD patterns and Raman spectra results revealed that the crystal phase of the obtained particles was predominately tetragonal BaTiO3.

Mar 1, 2017

By G. A. Brooks, R. W. Matusewicz, Nazmul Huda

"A computational fluid dynamic (CFD) model of a conventional tuyere blown slag fuming furnace has been developed in Eulerian multiphase flow approach. The model was developed by coupling CFD with kinetics equations developed by Richards et al. for zinc fuming furnaces. The model integrates submerged coal combustion and chemical reactions with the heat, mass and momentum interfacial interaction between the phases in the system. The model predicts the velocity, temperature field of the molten slag bath, generated turbulence, vortex and coal utilization behavior from the slag bath. The highest coal penetration distance was found to be at l/L = 0.2, where / is the distance from the tuyere tip and L is the total length (2.44m) of the modeled furnace. The model also predicts that 10% of the injected coal bypasses the tuyere gas stream un-combusted and carried to the free surface, which contributes to ZnO reduction near the free surface.IntroductionSignificant metal values are often discarded with slag in the form of metal oxide produced by the smelting industries. These metal values can be recovered from the slag by proper treatment. Zinc slag fuming is such a process, where a reductant source (usually coal) is injected in the molten slag bath to reduce dissolved ZnO from the bath into metallic zinc vapour. The process can be carried out in either conventional tuyere blown furnace or top submerged lance (TSL) smelting furnace. Conventional slag fuming processes are carried out on batch basis in a rectangular tuyere blown furnace. Approximately 50 tonnes of charge (either molten slag or solid slag) is fed to the furnace at the beginning of each fuming cycle. Two opposing sets of submerged tuyeres are employed to inject air and pulverized coal into the molten slag bath to carry out combustion and reducing reactions."

Jan 1, 2012

By Atul Kurnar

In the present research a two-cell polymer electrolyte membrane fuel cell stack (PEMFCS) with SS-316 bipolar plates has been tested. Different flow field designs were studied and a modified multi-parallel channel design is proposed. The stack is stable within ±3 mV even after 1000 hours of continuous operation, indicating efficient water management and effective removal of any metal ions from the stack. Also no iron is detected in membrane electrode assembly (MEA) by EDAX analysis after 1000 hours of cell operation. Results indicate that high operating pressures beyond 138 kPa didn&apos;t significantly increase the performance of cell, however added much to the pressurization cost of the system. Tests at different temperatures showed that at temperatures below 80°C, external humidification could be completely removed. The prototype stack is also tested under variable load conditions simulating highway-driving schedule. The experimental efficiency of PEMFCS is 48%, which is in good agreement with the model predicted efficiency of 53.8 %. Results show that 59% of the total losses are due to ohmic polarization in the cell. Further analysis on applications of the stack in automotive transportation system is in progress.

Jan 1, 2002

By Fabiano A. C. M. Passos, Vanessa P. R. Silva, Lillian M. B. Domingos, Fernanda A. N. G. Silva, Zuleica C. Castilhos, Roberto B. Faria

Wastes from gold mining need to be monitored from the beginning of mining activities until to the mine closure. Wastes from tailings dam were characterized by XRD, XRF, elemental analysis of carbon and sulfur and ICP-OES. In flotation waste (FW) were observed quartz, dolomite, pyrite, muscovite and chamosite were observed. Meanwhile, in cyanidation waste (CW), besides those described in FW, minerals such as sphalerite, galena, pyrrhotite, microcline and albite were detected, indicating a higher concentration of sulfide minerals in the cyanidation waste. In relation to C and S content, to FW and CW, they were 2.5 and 0.0% and 0.64 and 15.4%, respectively, confirming the majority of sulfides at CW sample and indicating the absence of the flotation organic reagents at the cyanidation waste. The analysis by ICP-OES indicated As, Zn, Pb, Cr and Cd content for FW and CW: 13.30 and 343 mg/kg; 399 and 7,900 mg/kg; 136 and 13,000 mg/kg; 130 and 260 mg/kg; 3.60 and 84.60 mg/kg, respectively. It was also verified significant levels of heavy metals, which indicates the necessity of performing wastes toxicity tests.

Mar 1, 2017

By Honggang Zhong, Tan Yi, Qijie Zhai, Zhao Dan, Xinping Mao, Huigai Li

"The influence of superheat degree on the distribution and volume content of inclusions were studied in 65Mn thin slab produced by compact strip production(CSP) in Zhujiang Steel in China, The results showed that the diameters of inclusions are mainly less than 5µm. Most of the inclusions gathered at the 1/4 thickness direction for the thin slab of 27? superheat degree, compared with the center position for that of 37?. There are more inclusions larger than 50µm in the low superheat samples, which is caused by the short floating time. In addition, the inclusions were observed and analyzed by metallurgical microscope, SEM and EDS in order to ensure their composition, type and further find their source. It was find that the types of these inclusions mainly are Al2O3, SiO2,CaO and their composites, a few of them are TiN and MnS.IntroductionIt is well known that inclusions have a great impact on the strength, plasticity, fracture toughness, cutting performance, fatigue property and corrosion resistance of steels. Especially, with the demand for thinner slab, the cleanness is increasingly becoming more significant as a quality criterion[1]. High manganese and carbon steels not only demonstrate high strength but also proper plasticity. There are many problems unsolved for 65Mn steel as a result of the low solidification rate, bad thermal strength, crack sensitivity and low casting temperature[2,3].The superheat of the molten steel has a great impact on the erosion of refractory lining, molten steel fluidity and non-metallic inclusion behavior[4]. The serious erosion situation of ladle lining, nozzle and casting tundish will give rise to more inclusions at a high superheat. Meantime higher superheat will make second dendrite arm spacing coursing and element segregation which lead to inclusion, bubble formation and shrinkage cavity. On the contrary, it is hard for non-metallic inclusions to float up with a low superheat value. Inclusions of 65Mn steel, which produced in different superheat condition by CSP, were studied for the sake of higher slab properties including statistics and EDS analysis."

Jan 1, 2012

By F. K. Letowski

Leaching in froth is a particular case of a three phase (liquid-solid-gaseous) process which combines flotation with leaching by using a reactive gaseous reagent as a flotation carrier and a leaching solution as the reactive liquid medium to fonn the foam (froth) in&apos; which the solid particles are suspended. Some physico-chemical and engineering aspects of leaching in froth are discussed and illustrated by its application for cleaning the mineral graphite. Leaching of the graphite concentrate containing 4L4% of the elemental carbon and 3.16% of the sulphidic &apos;sulphur was canied out in the froth fonned by: (a) a concentrated chloride solution, with a small addition of nitric acid, in the foam state; (b) a mixture of gaseous O2, NO., and H20 encapsulated in the foam; and (c) notable particles of graphite suspended in the foam. The laboratory experiments werecanied out in a "flotation column"-type reactor ala temperature from 80 to !08°C and under total pressure of 100 to 200kPa. In the 3-stage leaching-flotation process, the non-flotable fraction of particles was separated three times from the notable fraction. The concentration of carbon and elemental sulphur in the final flotable fraction was 96% C and 0.38% S respectively. The expected advantages and possible application in hydrometallurgy are suggested.

Jan 1, 1995

By C. Burton Clark

The important role of the petrographic microscope in the petrology of refractories is discussed, based on 45 years of industrial experience by the author. Highlights of his career are used to illustrate improvements in equipment and techniques during the period. Two specific investigations are described which emphasize the interrelated use of the petrographic microscope with other instruments such as the x-ray diffractometer and scanning electron microscope. Emphasis is placed on the use of phase equilibrium diagrams for guidance in predicting and interpreting reactions that occur under non-equilibrium conditions in the manufacture and use of refractories.

Jan 1, 1982

By Vladimir I. Skorohodov

The technology for copper utilization from circuit boards etching is proposed. The technology is based on combination of electrochemical and sorption methods. The conditions of copper electroextraction from ammonia-chloride solutions with obtaining of cathode copper are defined. The stage of electrolysis is destined for copper recuperation from etching process. Due to the electrochemical processes are unacceptable for cathode precipitation of the copper from diluted solutions such as rinse waters, the concentration on the strong-based cationites are used. After filtration throw the sorption columns solution is directed to the stage of circuit boards washing. It allows organizing close loop water recirculation. After saturation. resin is &apos;regenerated by chloride ammonium solutions. Obtained eluate directed to the etching stage, Generally. the technology provides copper recuperation and minimize wastes amount.

Jan 1, 2001