By Kimio Ilagaki

The distribution ratios of Ag, Pb, As, Sb and Bi for the Cu2S-FeS or Ni3S2-FeS matte I FeOx-SiOl, FeOx-Si02-CaO or FeOx-CaO slag equilibration in a MgO crucible were determined experimentally at 1523 ~1573K under controlled partial pressures of S2 and 02 at given PS02 of 10.1,50.7 and 101.3 kPa(O.I, 0.5 and I atm), and the observed dependency of distribution ratio on the matte grade, S02 pressure and slag basicity were analyzed on the basis of thermodynamics.

Jan 1, 2003

By Mingmei Zhu, Lang Hu, Yu Wang, Hongpo Wang, Congjing Zhang

Magnetic field has a great effect on the crystallization behavior of mold flux and properties of the flux film between mold and strand, on which the surface quality of strand was deeply depended in continuous casting process. Therefore, studying the change law of the crystallization properties of mold flux in magnetic field is of great significant. In the present work, based on intensity of the applied magnetic field with the range from 0mT to 60mT, the crystallization ratio, crystal size and mineralogical phases of the flux film were discussed. The results show that crystallization ratio increases with the increasing magnetic field intensity, and the crystal size becomes bigger at the same time. The magnetic field promotes the crystallization ratio and growth speed of the crystallized grains of mold flux. However, magnetic field doesn’t change types of the mineralogical phases.

Jan 1, 2015

By Phillip B. Messersmith, Emmanuel P. Giannelis

"A versatile in-situ polymerization approach is described for the synthesis of polymerceramic nanocomposites consisting of two-dimensional layers of mica-type silicate (MTS) within polymer matrices. Functionalized, organically modified mica-type silicates (OMTS) were used to promote delamination/dispersion of the host layers and initiate polymerization of organic rrionomer. Epoxy nanocomposites prepared in this manner exhibit substantial modulus reinforcement at low silicate loadings. The water vapor permeability of the poly(?-caprolactone) nanocomposite containing 4.8% silicate by volume was reduced by nearly an order of magnitude compared to pure poly (?-caprolactone).IntroductionPolymer matrix nanocomposites are a relatively new class of materials with dimensions typically in the range of 1-100 nm.1 In general, because of the ultrafine phase dimensions involved, nanocomposites exhibit new and improved properties when compared to their micro- or macrocomposite counterparts. We as well as others are currently investigating the design, synthesis and characterization of polymer-ceramic nanocomposites. Our effort, in particular, has focused on the use of mica-type silicates (MTS) with various thermoplastic and thermosetting matrices.2-5MTS's belong to the general family of 2: 1 layered silicates. Their crystal structure consists of layers of two silica tetrahedral sheets fused to an edge-shared octahedral sheet of either aluminum or magnesium hydroxide. Stacking of the layers leads to a regular van der Waals gap or interlayer.6 Isomorphic substitution within the layers generates negative charges that are counterbalanced by cations residing in the interlayers. Although the natural forms of MTS's usually contain hydrated Na+ or K+ ions, ion exchange reactions with organic cations (e.g. alkylammonium ions) can render the normally hydrophilic MTS's organophilic."

Jan 1, 1994

By D. M. Hausen

A refractory siliceous low-grade silver ore (265 g/t Ag) from a prospect in Sonora, Mexico was investigated mineralogically and metallurgically to evaluate extraction of the silver by conventional methods. Approximately half of the silver was recoverable, occurring as coarsely crystalline acanthite (70-300 Am) that was liberated in material crushed to minus 10 mesh. The remaining silver is refractory and occurs mostly as finely locked (-2 to 0.2 Am) acanthite in cherty quartz, and as minor amounts of finely disseminated stylotypite or freibergite in fluorite. The mineralogic data have thus served to explain the 50-60% recovery of silver by flotation and cyanidation.

Jan 1, 1991

By P. P. Knight

The Parkes Process is an important step in the pyrometallurgical refining of lead bullion and it is estimated that more than 50% of the Free world's primary silver production is processed by this route. The metallurgical efficiency of the process can have a significant impact on the overall refining costs, particularly with regard to zinc consumption and the costs of working up the silver-rich crusts?. Several authors have used mathematical or graphical methods in order to calculate the minimum required zinc additions and to study the merits. of alternative. operating procedures, but these methods are of necessity very cumbersome and are only able to deal with relatively simple systems. The paper explains how a computer model was developed which simulates the Parkes Process accurately and can predict the effects of changes made in operating methods. Examples are given of some of the findings and their relevance to the practical conduct of the process is? discussed.

Jan 1, 1990

By B. Sereda

As it is known the creation and development of new titanic alloys has been problematic up to now. They can be used in aircraft and vehicle construction, shipbuilding and as materials for keeping static loadings in high-temperature environments. In this work the synthesis of various titan aluminides is investigated. Mathematical model of structurization process was done. On the base of retrieved model the mechanisms of structurization in systems Ti + Al and Ti + 3Al was determined. Experimental researches were done at two different modes: burning and thermal spontaneous ignition. The method of retrieving compacted products combusted in SHS conditions (SHS-compacting) was used to gain these intermetallic compounds. The physical and thermal characteristics of technological process and their influence on structurization, homogeneity of structure and porosity of titan aluminides have been simulated and researched. It is established that the SHS-compactizing technology is fully capable of supervising the process of structurizations with the whole complex of advantages and can be applied for receiving qualitative titan aluminides with the set of chemical-physical properties.

Jan 1, 2010

By C. M. F. Vieira

This work has as its objective to characterize ceramic bodies for vitrified tiles elaborated with the mixture of nepheline-syenite flux and kaolinitic clay. Formulations were prepared with 0, 30 and 50 wt.% of nepheline-syenite incorporated in a kaolinitic clay. To determine the physical and mechanical properties such as dry bulk density, linear shrinkage, water absorption and flexural rupture strength, specimens were prepared by 30 MPa uniaxial pressure-molding and then fired in a laboratory furnace at 1150oC. The microstructure of the fired ceramics was evaluated by scanning electron microscopy. The results indicated that the nepheline-syenite improved the evaluated properties of the clay and attended the specifications of vitrified ceramic tiles.

Jan 1, 2010

By D. M. Hausen

It has been demonstrated that microscopic techniques can be applied in a practical manner to the study of spodumene liberation in the processing of pegmatitic ores at the Kings Mountain spodumene plant, Kings Mountain, North Carolina. Spodumene and associated non-opaque gangue minerals are identified and quantified by microscopic point-counting of polished thin sections of heads, concentrates, middlings and tails fractions. Specially prepared polished thin sections? provide uniform thickness of particles for measurement of diagnostic optical properties and the alternate use of incident and transmitted light in distinguishing the various gangue and ore minerals. Spodumene is commonly associated and interlocked with quartz, albite, microcline and muscovite. Concentrate grade depends on the degree of spodumene liberation, which in turn depends on the crystal size and textural association of interlocked minerals. The liberation of spodumene can be measured as a function of screen size by means of microscopic point-count data. Microscopic data also provide useful metallurgical information about the nature of diluent minerals in spodumene concentrates, and the form of lithia losses in the tails. Lithium assays correlate closely with microscopic spodumene analyses in various flotation products from Foote Mineral's Kings Mountain plant, and confirm the applicability of quantitative optical microscopy to the study of liberation and recovery of spodumene from pegmatitic ores. A better understanding of recovery-grade relationships was developed as a result of quantitative microscopy studies.

Jan 1, 1981

By Dietmar Eifler, Benjamin Jost, Marcus Klein

This paper focuses on the ductile cast iron EN-GJS-600 which is often used for components of combustion engines. Under service conditions, those components are mechanically loaded at different temperatures. Therefore, this investigation targets at the fatigue behavior of EN-GJS-600 at ambient and elevated temperatures. Light and scanning electron microscopic investigations were done to characterize the sphericity of the graphite as well as the ferrite, pearlite and graphite fraction. At elevated temperatures, the consideration of dynamic strain ageing effects is of major importance. In total strain increase, temperature increase and constant total strain amplitude tests, the plastic strain amplitude, the stress amplitude, the change in temperature and the change in electrical resistance were measured. The measured values depend on plastic deformation processes in the bulk of the specimens and at the interfaces between matrix and graphite. The fatigue behavior of EN-GJS-600 is dominated by cyclic hardening processes. The physically based fatigue life calculation “PHYBALSIT” (SIT = strain increase test) was developed for total strain controlled fatigue tests. Only one temperature increase test is necessary to determine the temperature interval of pronounced dynamic strain ageing effects

Jan 1, 2015

By C. M. F. Vieira

In the county of Campos dos Goytacazes, north of the State of Rio de Janeiro, Brazil, there is a large production of red ceramic, mainly perforated bricks. A percentage of these bricks are damaged during the firing processing and become a red ceramic waste. This work investigates a possible solution to this environmental problem through the mixture of fired brick wastes, up to 20 wt.%, with clay bodies to produce red ceramics. Cylindrical pressed bodies were fired at temperatures varying from 500 to 1100ºC. After firing, samples were then tested for linear shrinkage, water absorption and mechanical strength. The results showed that brick waste addition did not changed the workability of the clay and that up to 5 wt.% of waste no detrimental effect occurred on the fired properties at all temperatures.

Jan 1, 2010

By Shengli Wu, Jinming Zhu, Wei Huang, Xinliang Liu

The sinter of high basicity would interact with lump ores or acid pellets in the cohesive zone of blast furnace due to the difference of chemical composition and micro structures. The results of this work showed that the softening-melting properties of lump ores and acid pellet would be obviously improved by the high temperature interaction. However, the high temperature interaction index (INI) would be influenced by many factors, such as chemical composition, porosity, interaction interface and so on. The INI between sinter and porous limonite lump ore (L-2) was much higher than that of dense hematite lump ore (L-1) and acid pellet (P-1). In addition, though the softening and melting properties of L-2 were poorest in respective iron ores, the softening and melting properties of integrated burden B (consist of sinter and L-2) were not worse than other integrated burdens due to the strong high temperature interaction.

Jan 1, 2015

By A. P. Pavia

Investigation on profitable ways to recover significant quantities of silver remaining dissolved in highly concentrated chloride solutions frequently pass through the development of solvent extraction (SX) routes. In this work, the general pathways involving Ag(I) extraction by dibutylthiourea (DBT) or tetraethylthiuram disulfide (disulfiram, DSF), from concentrated acidic chloride solutions, are investigated. With this purpose, the dependence of Ag(I) distribution coefficient on ligand and chloride concentrations has been analysed. Furthermore, in order to check whether there is some protonation at any site of DBT or DSF after contact with adequate chloride phases, lH NMR has also been used. The collected spectroscopic data suggest that anionic Ag(I) extraction reactions are not likely to occur. Based on the overall results achieved, proposals for the most probable Ag(I) extraction reactions are made.

Jan 1, 2001

By Y. Zhoa

The surface morphology of materials is of fundamental importance to many surface related applications, such as wetting, friction, reflection, drag, and adhesion. Various approaches for micro/nano patterning atop polymer surfaces have been proposed in recent years. However, a cost effective technique is still highly in demand. In this paper, we demonstrate a novel but rather simple and generic approach for surface micro/nano patterning using shape memory polymers (SMPs). Different types of novel patterns are realized and their 3-D surface features are quantitatively analyzed by a PLµ Confocal imaging profiler.

Jan 1, 2010

By Bart Blanpain, Muxing Guo, Zhuangzhuang Liu

In order to stabilize free lime in the basic oxygen furnace (BOF) slag to achieve high value products, quartz sand and other additives are injected into slag. However, the current hot stage slag stabilization does not work in case of slag (before treatment) with a liquid fraction lower than 90%, where the slag containing solid particles is too viscous. Therefore, it is essential to understand how solid phases affect the viscosity of the slag system. In this study, the industrial BOF slags were investigated with respect to the correlation between volume fraction of solid phases and its viscosity. Slag viscosity was measured with a rotating type viscometer at temperatures below the liquidus. The volume fraction of solid phases was quantitatively calculated with FactSage. The Einstein-Roscoe equation was employed to predict the viscosity of BOF slag.

Jan 1, 2016

By Kimio Itagaki

The distribution ratios of Ag, Pb, As, Sb and Bi for the Cu2S-FeS or Ni3S2-FeS matte / FeOx SiO2, FeOx-SiO2-CaO or FeOx-CaO slag equilibration in a MgO crucible were determined experimentally at 1523~1573K under controlled partial pressures of S2 and O2 at given PSO2 of 10.1, 50.7 and 101.3 kPa (0.1, 0.5 and 1 atm) and be observed dependency of distribution ratio on the matte grade, SO2 pressure and slag basicity were analyzed on the basis of thermodynamics,

Jan 1, 2003

By A. Ohno

"A new near net shape casting process, OHNO Continuous Casting (OCC), has been recently developed. In this process, molten metal is fed into a heated mold maintained at a temperature above the solidification temperature of the metal being cast. Solidification begins from the central core of the casting rather than the wall of the mold. With the heated mold, the formation of crystals on the mold wall is prevented and solidification occurs out of contact with the mold surface. This produces near net shaped products with smooth, mirror-like surfaces and unidirectional grain structures free from cavities, porosity and segregation. Any crystals formed at the beginning of solidification decrease in number as solidification progresses and eventually a single crystal product is obtained. This process is applicable to any metal alloys, converting them into new materials with superior properties and quality.IntroductionAs a result of growing technical demands for more advanced and diversified materials, the OHNO Continuous Casting (OCC) technology has found many new applications in industry. Considerable interest in the process has been shown in Japan and other countries because of its distinct ability to:produce a single crystal, (1)produce a remarkably clean cast surface without a witness mark,provide extremely good ductility,and reduce casting defects and segregation.This paper provides an overview of the principle of the OCC process and describes the remarkable characteristics of the material produced by this method."

Jan 1, 1988

By Alaina Mallard, Jannette Chorney, David Hutchins, Grant C. Wallace, Jerome P. Downey

Current commercial processes for producing ceramic carbides require temperatures of 1400–2000 °C and often use extensive milling operations to produce a powder product. A process that could reduce the energy requirements of commercial carbide production could allow for these materials to be implemented in a greater number of applications. In this study, tungstate (WO4 2−) and silicate (SiO3 2−) anions were adsorbed onto activated carbon and converted into silicon carbide (SiC) whiskers and a mixture of tungsten and tungsten carbide (W/WC) crystals via carbothermal reduction using inert and reducing gas atmospheres at temperatures much lower than what is required by current commercial processes (950 °C for W/WC/W2C and 1200 °C for SiC). The adsorption process was statistically-optimized via a central composite response surface analysis using DesignExpert 9. Inductive coupled plasma optical emission spectroscopy (ICP-OES) was used to measure, and optimize, adsorption efficiency while the carburization products were characterized using X-ray diffraction and scanning electron microscopy.

Mar 1, 2017

By Luísa Maria Abrantes

Environmental control is becoming more and more stringent. As conventional processes for zinc production are pollutant routes, alternative methods have become an important subject of research. In this regard, the leaching processes have aroused a considerable interest, namely the electrochemically induced approach. The behaviour of zinc concentrate ore in the leaching processesses is influenced by several parameters. Chloride concentration and leaching solution pH, time and temperature of reaction were studied in order to evaluate their influence on the zinc recovery. The efficiency of the leaching process for zinc extraction is performed by factorial design. The experiments were carried out by 23 and 22 factorial designs of the factors. Results show that all factors, except for the time of reaction have a significant influence on the optimisation process, within each experimental region.

Jan 1, 2001

By George Owusu

A study has been carried out on the use of solvent extraction, instead of the traditional zinc dust cementation process, to remove copper from concentrated zinc sulphate leach solutions. In a series of experiments using plant solution containing 1.9 g/L Cu, 2 g/L Fe, 173 g/L Zn, 7.9 g/L H,SO,, 0.25 g/L Cd, 15 mg/L Co etc. and LIX 622 in SX-1, up to about 97-98 % of copper present in the zinc sulphate leach solution was extracted with negligible co-extractions of zinc, iron, cadmium, cobalt, etc. pH modification was not required for this reagent. The copper loaded organic was almost completely stripped using 150 g/L sulphuric acid. Investigations into the effect of any possible organiclextractant contamination on zinc electrowinning showed (if any) little effect on current efficiency if the organic contamination is less than 45 ppm; current efficiencies of 95-97 % were obtained. At organic contaminations higher than 45 ppm, the current efficiency dropped to about 92- 94 %. Visually, the organic-contaminated cathode sheets had rough surface morphology, becoming more intense with increasing organic concentration, compared to the non-contaminated cathode sheets.

Jan 1, 1998

By G. E. Lagos

This paper analyses the scope and instruments employed by the Basel Convention for regulating the transboundary movement of hazardous wastes, the present and projected hazardous waste regulations of Chile, reviews the Chilean import/export trade of wastes of the period 1985-1995, and discusses, the influence that the Basel Convention has had on mining trade, its perceived benefits and costs, and possible effects on Chile's trade of the application of the Convention's Decision III/l. There is no quantitative estimation as to the effect of the Convention on the general volume of imported or exported materials destined for recovery, recycling, reclamation, or reuse. All recycling imports, with the possible exception of residues of petroleum oil, which occurred during the decade 1985-1995, can be classified tentatively as non hazardous. The entry into force of the Convention has had several effects on Chile's trade. It has brought home the need to have a comprehensive hazardous waste legislation, it has been a base for applying import restrictions, which in all likelihood, would .have otherwise not been applied, The benefits and costs of this import restriction, as well as those of the multilateral export ban are analyzed.

Jan 1, 1999