By Guo-Sen Zhu

Research on the formation mechanism and control of corner transverse cracks was carried out. The optical microscope and SEM were applied to analyze the characteristics of cracks. It is found that the cracks occur at the relatively lower temperature due to unbending strain and have almost nothing to do with the mold cooling and powder. The keys to prevent corner transverse cracks are to optimize the corner temperature of slab and maintain the good state of casting machine. Increasing casting speed and decreasing the cooling water flux at the corner in the unbending segments, resulting in mild cooling, were applied during investigation to control corner temperature above the upper limit temperature of the No.3 brittle zone of Nb-contained steel tested by Gleeble-1500 system. As a result, corner transverse cracks were minimized, but centerline segregation got worse. And then increasing the cooling water flux at the corner (intensive cooling) was applied to make corner temperature below the lower limit temperature of the No.3 brittle zone. Great diminution of both corner transverse cracks and centerline segregation was achieved finally.

Jan 1, 2006

By K. D. Peaslee

The 150 metal producers in Missouri generate approximately 8,000 tons of spent refractories each year, most of which is landfilled. Spent refractory samples were characterized and recycling / reuse techniques developed for some of the largest waste streams. Products using recycled materials are compared with products made from virgin materials.

Jan 1, 2000

By Evan Jamieson

The conditions under which various iron(III) oxy-hydroxides phases precipitate from iron(III) chloride and sulfate solutions at ambient temperatures (<60°C) are reviewed. Many of these precipitates are slow settling and gelatinous but ultimately transform into other more stable or crystalline phases. The phase that forms depends upon the rate of precipitation and pH. A comparison has been made of the iron(III) oxides formed upon the neutralisation of various iron(III) solutions with caustic, slaked lime or slaked magnesia which provide different rates of neutralisation and slowly dissolving solids with localised high pH. Mössbauer spectra of ferrihydrites precipitated under these different conditions are compared and interpreted. Particular attention is paid to the settling rate and settled volume which is likely to relate to industrial thickener and filter performance. It is shown that in pure chloride solutions, poorly settling ferrihydrite is usually produced at 20oC regardless of the choice of base. However in sulfate solutions fast settling precipitates are produced using lime and magnesia but not with caustic. In mixed chloride/sulfate solutions, optimum settling rates occur when the molar ratio of [SO4]2to Fe3+ is about 1:1 and when the sulfate concentration is <0.20 M. It is proposed that ?dense amorphous basic iron sulfate? or well-ordered ferrihydrite is formed on slowly dissolving lime or magnesia surfaces. Implications for industrial liquors are considered.

Jan 1, 2003

By James A. Sommers

Combustion of niobium nitride powder in a stream of oxygen results in several niobium oxide phases, depending upon reaction parameters. Under rapid oxygen flow, the oxidation produces a molten mass which coalesces into droplets of ca. 2 mm dimension and effectively quenches to leave NbO2 and other lower oxides of niobium, despite the ambient atmosphere of oxygen. A preliminary survey of reaction parameters which govern the split between reduced and oxidized products is presented. This technique offers novel synthesis means for binary oxides when mixtures of NbN and other materials are combusted together, since the niobium moiety is generated in a molten state.

Jan 1, 1995

By G. F. Archer

Selenium and tellurium, trace metals found in copper smelting, report to blister copper during smelting. Winning these metals from anode slimes, the primary commercial source, is discussed. At Asarco&apos;s Amarillo Copper Refinery, slimes treatment segregates selenium and tellurium to a water-soluble soda slag. Aqueous precipitation of tellurium oxide and selenium by sulfur dioxide is valence dependent. Se+6 and Te+6, which constitute a portion of total selenium and tellurium, are not susceptible to this base case treatment. "Secondary Selenium" is formed from these hexavalent species. We describe a process whereby simultaneous oxidation of selenium and tellurium effects a separation. Process conditions for separating selenium dioxide, and efficiency of fume capture are examined.

Jan 1, 1995

By Xiyun Yang

Magnetite was prepared by hydrogen reduction method. For a conversion to cobalt-modified magnetite, magnetite particles were suspended into a solution containing Co2+ and Fe2+ to precipitate a cobalt ferrite layer on the surface. pH value influences the particle composition directly, the desirable CoFe2O4 is obtained when pH value is 12. The coercivity increases with the increase of cobalt content, cobalt efficiency reaches a maximum value at cobalt content of 2.71wt%. With cobalt modification, magnetite particles have similar lattice constant and squareness ratio to that without cobalt modification. TEM and XPS analyses indicate that acicular morphology is retained during the coating process, the epitaxial growth layer consists of CoFe2O4and 0.3Co2O3CoFe2O4 at cobalt content of 2.71wt% and 5.03wt%, respectively.

Jan 1, 2006

By R. M. Moon

Neutron scattering has played a crucial role in advancing our understanding of rare-earth materials. It has provided a detailed description of the rich array of exotic magnetic structures; it has confirmed the accuracy of theoretical wave functions for the 4f electrons; and it has provided fundamental data on the collective magnetic excitations in these materials. The fundamental property of the neutron which has been exploited in this work is the magnetic interaction which exists between the magnetic moment of the neutron and atomic magnetic moments on individual rare-earth atoms. This interaction produces scattering of neutrons in a manner closely analogous to the scattering of X rays by atomic charge distributions. In a material exhibiting long-range magnetic order, Bragg diffraction peaks will appear at scattering angles determined by the periodicity of the magnetic structure. The Bragg intensities are determined by the magnitude and relative directions of the atomic moments. The rare-earth metals and alloys are characterized by sinusoidal modulation of magnetic moment components which can be combined in various ways to produce a variety of magnetic structures. The periodicity of these modulations is frequently not related simply to the underlying periodicity of the chemical structure. The major features of these structures are explained by the combined, and sometimes competing, exchange and crystal-field interactions. At a more fundamental level, neutron diffraction also gives information on the spatial distribution of a magnetic moment in a rare-earth atom. This moment comes from the 4f electron shell, and accurate measurements of the neutron scattering amplitudes have been used to check the accuracy of atomic wave function calculations for the 4f electrons. It was found that relativistic Dirac-Fock calculations are in excellent agreement with the experimental results. Collective excitations of ordered magnetic systems are described in terms of spin waves, which are sinusoidal modulations in space and time of the direction of the ordered moments. Inelastic neutron scattering is used to measure the energy and wave length of these collective excitations. Analysis of these data gives direct information on the interatomic interactions responsible for the magnetib properties of these materials.

Jan 1, 1992

By Z. R. Llanos, W. G. Deering

Gulf Chemical and Metallurgical Corporation (GCMC) has been operating facility for treatment of spent catalysts in Freeport, Texas since 1974. Recently, GCMC expanded its operations with the addition of an electric furnace for the production of fused alumina and mixed alloys. GCMC and its affiliate Sadaci, started up a new pre-treatment facility in Ghent, Belgium in 1998. GCMC is also part owner of Bear Metallurgical Corporation, a major producer of ferroalloys in the United States. This paper reviews the processes at these facilities. Changes in the management of hydrotreating and hydrorefining spent catalysts are discussed in light of recently issued federal regulations that made the majority of spent catalysts a listed hazardous waste.

Jan 1, 2000

By Ximena Massone

Chile is the most important copper producer in the world and the mining sector plays a key value in its economy. However, at present the country does not have a satisfactory set of regulations about closure and restoration of mining operations. In our country many mining operations will, in the near future, shut down their activities, therefore, it is of utmost importance to elaborate and enforce a set of regulations to prevent risks and to protect the environment. The present study is focused on reviewing and analyzing the existing national regulations about the closure of mining operations and preparing a comparative analysis with other international regulations of countries with mining experience. The final results of the study will be a legal proposal to regulate the closure of mining operations in Chile, aiming at minimizing the potential environmental adverse impact, internalizing the social costs by the relevant operators and defining all aspects of liability for the environmental damage.

Jan 1, 1999

By Gregor Mori

Niobium electrolysis has been performed in a NaCl-KCl-NaF-NbCls electrolyte. By means of electrolytic .refining the average valency of the niobium ions was determined as well as the crystallization behaviour. In electrowinning runs the influence of the main parameters such as temperature, RF (mole ratio F/Nb), chemical prereduction, niobium content of the melt and current density has been determined with respect to low specific energy consumption and high purity of the deposit.

Jan 1, 1995

By Robert L. Opila

Negative electrodes for alkaline nickel-metal hydride batteries composed of MmNi3.5Al0.8Co0.7, where Mm is misch metal, have been characterized electrochermically and using x-ray photoelectron spectroscopy. The stability and rapid hydriding and dehydriding kinetics of the alloy in KOH are attibuted to a surface film. The protective surface film is shown to consist of an porous, outer hydrated layer and a dense, inner oxide layer. In addition, metallic nickel and cobalt are found throughout the film, and are presumed to form a conductive, percolative network that permits rapid electron transfer from the bulk to the solution, allowing rapid electrochemical formation of atomic hydrogen.

Jan 1, 1997

By Steven Wright

The extent and the rate of reduction of slags produced from the smelting of recycled lead batteries were investigated under laboratory conditions using graphite as reductant. Simultaneous reduction of PbO, Fe2O3, Sb2O3 and As2O3 occurred at temperatures of 1180 and 1200°C, with Sb and As reporting to the metal phase while the PbO content of the slag was above 2 wt%. Fuming of As from the metal occurred at lower concentrations of lead in the slag. Discard slags with low levels of As, Pb and Sb were produced. Arsenic levels were reduced to less than accurately measurable by ICP analysis, and Sb levels in the final slags were in the range of 0.1 to 0.2 wt%. The kinetic data obtained were analysed and compared with other measurements on lead oxide containing slags. The results showing a dependence of the reduction rate on the oxidation state and the basicity are consistent with other studies on well characterised industrial and. synthetic lead slags. These results indicate that when carbonaceous reductants are used, the rate of interfacial reactions play an important role in enabling the production of environmentally acceptable discard slags.

Jan 1, 1994

By Wen-Ming Chien

Low temperature X-ray diffraction and thermal property studies of the solid-solid state phase transition for the polyalcohols (pentaerythritol (PE), pentaglycerine (PG) and neopentylglycol (NPG)) thermal energy storage solid solutions have been investigated by using X-ray diffractometry and differential scanning calorimetry (DSC) methods. X-ray diffraction studies on polyalcohols solid solutions, PE-NPG and PG-NPG, are from ?10oC to 50oC. XRD results shows the + mixed phase at the related low temperature (?10oC) for both PE-NPG and PG-NPG solid solutions. At high temperature range, XRD results show phase for PG-NPG solid solution and + mixed phase for PE-NPG solid solution. There are only two Bragg peaks, (111) and (200), shown in phase XRD patterns. The polyalcohols solid solutions have been cycled 5 times between -20oC to 100oC at different DSC scan rates to study the phase transition properties. DSC results of both PE-NPG and PG-NPG solid solutions show that the solid-solid state phase transition is near room temperature. Details of low temperature phase transition XRD and DSC results of PE-NPG and PG-NPG solid solutions will be presented

Jan 1, 2006

By Guo Jun

In this study, BaTiO3 ultrafine particles surface-modified with stearic acid were synthesized by the hydrothermal method in a system of BaCl2-TiCl4-NaOH. The effects of NaOH/TiCl4 molar ratio, Ba/Ti ratio and time on structure and morphology of BaTiO3 ultrafine particles were investigated experimentally. The formation mechanism of different crystalline BaTiO3 particles was discussed, and it is considered that in a hydrothermal system, the main factors determining BaTiO3 crystalline are H+ replacement of Ba2+ causing H+ deficiency and anatase growth units involving in crystal growth, which clogs the axial channel for Ba2+ transference. By means of increasing the alkalinity of system and barium content, H+ deficiency and involvement of anatase growth units in crystal growth could be effectively controlled. The results show that when molar ratio of NaOH to TiCl4 is 9 and ratio of Ba to Ti 1.5, and time 8 hours, high purity tetragonal BaTiO3 ultrafine particles with a narrow grain-size distribution and nonpolar surface are obtained at 240oC. The particles have excellent flowability, which is ascribed that the surface polarity of barium titanium powder modified with stearic acid is changed and the interaction between the particles is weakened.

Jan 1, 2006

By M. Sadayappan

The grain refinement characteristics of four low-lead and lead-free copper base alloys for plumbing applications were investigated. These are leaded yellow brass (C85800). SeBiLOY III (C89550), silicon brasses (C87500 & C87800) and silicon bronzes (C87600 & C87610); Boron and zirconium were found to be the most effective .grain refiners for copper .alloys produced using the permanent mold cast processes. The study indicates that the type of grain refiner to be used is dependent on the alloy type, alloying constituents and their content. After grain refinement, hot tearing resistance of the alloys was improved but mechanical properties remained unaffected. Alloys refined with boron are prone to the formation of hard spots, which will have adverse effect on the surface quality of the castings during polishing and buffing.

Jan 1, 1999

By F. M. Doyle, K. Sreenivasarao

Copper and cadmium metal has been recovered from dilute (3 X 10-4 mol/dm3 ) chloride solutions by ion flotation with dodecysulfate, followed by electrolysis. This approach should facilitate treatment of effluents too dilute for effective direct electrolysis. . The adsorption density of metal dodecylsulfate complexes on bubble surfaces was estimated from surface, tension data, and compared well with experimentally-observed metal removal kinetics, and ultimate recoveries. Copper and cadmium were recovered by electrolyzing the foamate, using steel wool cathodes and a graphite anode. The stability constants of the copper and cadmium dodecysulfate complexes are estimated, and used to analyze the thermodynamics of electrolysis. Dodecysulfate was unaffected by the electrolysis process, and hence could be recycled to ion flotation. A conceptual flowsheet for an overall effluent-treatment process is presented.

Jan 1, 1997

By P. S. Seryogin

R & D works supported by industrial-scale tests, which were carried out by joint efforts of the OAO Gipronickel Institute and MMC ?Kola? engineers, have accomplished with the production of 90?95% metallized nickel powder in tube furnaces (NPTF), with its ?active fraction? (AF) to be further used for decopperization of nickel electrolyte by cementation. Consistently positive results obtained in the course of the lab and industrial experiments have allowed the Severonickel Combine management to effectively replace all activated nickel powder (ANP), which was then employed for cementation, with the AF, having activity over 80%, and eventually shut down the entire operation of gaseous reduction. Ever since the developed technology has been implemented, its annual economic effect exceeds 2 ml. dollars.

Jan 1, 2006

By Steven Wright

BHP Billiton?s Olympic Dam copper flash smelter employs the direct to blister process for smelting high grade copper concentrates. SO2 evolution during tapping gives rise to safety concerns. A thermodynamic model for the blister copper (Cu-Fe-S-O) was used to predict the volumes of SO2 evolved. The Multiple Phase Equilibria Model (MPE) was used to evaluate the slag chemistry inside the furnace. The blister copper model was used to explore the relationship between %S and %O in the copper and the amount of SO2 evolved on cooling. The volume of SO2 evolved was sensitive to the O content with reduction to levels below 0.2 ? 0.15% likely to suppress SO2evolution on cooling. Concentrations of S and O in copper samples from trials generally lay above the equilibrium line calculated for an average temperature of 1275C and a partial pressure of SO2 of 1 atm. Consequently there is a thermodynamic driving force for SO2evolution when cooling to this temperature during tapping. A number of potential process options to suppress SO2 evolution on tapping were investigated thermodynamically. Some of the options require treatment of the blister in a forehearth or separate furnace, while others impact on current practises in the flash furnace with slag present. The opportunities that these options present are discussed.

Jan 1, 2006

By Bora Derin

Optimization of slag composition has great importance on effective and clean metal production technologies. Reddy-Blander (RB) model, a priori, is very useful tool for prediction of impurity capacities of industrial slags. In this study, sulfide capacities (Cs) of 19 lead smelter slags indicated in the literature were calculated and effects of Cs values on sulfur content of lead bullions were discussed.

Jan 1, 2006

By Miguel Olivas-Martínez

A two-dimensional computational model for the hot filament chemical vapor deposition (HFCVD) process to produce diamond films is presented. The model incorporates the transport of momentum, energy, and mass inside the reaction chamber of a HFCVD reactor. The gas-phase homogeneous reactions were represented by a simplified reaction mechanism. The gas-phase transport equations were coupled to the kinetic expressions representing the catalytic dissociation of the molecular hydrogen at the filament surface and the deposition rate of the diamond film on the substrate. The computational model was solved numerically by means of a commercial software. The model predictions showed good agreement with the experimental data reported in the literature in terms of both temperature and methyl concentration profiles along the filament-substrate center distance. Examples of the potential applications of the present formulation for the design and further optimization of the HFCVD reactor are discussed.

Jan 1, 2006