By F. Mucciardi

With the increasing trend to continuous smelting and converting, granulation of copper matte is gaining prominence as a means of decoupling the smelting and converting operations. Moreover, granulation is also being seen as a possible avenue to using higher grade oxygen in converters. By feeding cold solid matte, the oxygen concentration can be increased to compensate for the lower enthalpy feed. This leads to a higher grade of SO2 in the off gas and a lower total flow rate. Current granulation technology relies on the cooling of a falling matte film by water jets. This technology while effective has several drawbacks including those related to safety. Noranda and McGill University have developed a new process (patent pending) for solidifying copper matte (or slag). It overcomes many of the negatives of current technology. The system is based on an air cooled twin roll caster. This: new system uses no water and instead incorporates heat pipe technology to transfer the heat from the solidifying matte to the cooling air to produce a thin strip of 1 to 2 mm in thickness. Testing of a prototype unit demonstrated its viability. This paper describes this newly developed, twin roll casting system that is completely waterless. The advantages of this process as well as the findings from several tests are also detailed.

Jan 1, 1999

By David Bequette, Ray D. Peterson, Cynthia K. Belt

"With a need to cut production costs in the metals industry, cost savings from energy efficiency improvements are critical. Opportunities can be found by reviewing furnace systems and practices so that the melting and holding processes operate at the highest energy efficiency. Many of the changes can be implemented with a minimum of expense or capital investment. This paper will review several low cost methods to optimize energy efficiency on reverberatory melting or holding furnaces. These five methods (furnace utilization, idle procedures, fire rate, controls, furnace pressure) will be explained and information given to implement these changes. Included are several rules-of-thumb and benchmarks for aluminum reverb furnaces.IntroductionEnergy can be a significant portion of the total manufacturing costs for metals and materials manufacturing involving thermal processing such as heat treating, melting, and high temperature processing. Natural gas prices have dramatically varied over the last few years. While no one can foresee the future, prices are expected to increase from the current low prices. More recently, emphasis is being put on the reduction of greenhouse gases with the potential of additional costs to industry.One of the first steps in an energy management program is to measure the energy usage of the process [1]. The results are typically understood in relation to the mass melted in kWh / mT [BTU / lb]. For the purposes of this paper, furnace energy efficiency is calculated over a month or even a year and thus includes hold times. This efficiency is typically different from the values quoted by furnace manufacturers. Those values are for limited short term tests at highutilization.Once you know the performance for your furnaces, these should be compared to industry benchmarks. For aluminum melt furnaces with cold air burner systems, a benchmark value or goal is 1800-2000 BTU/lb [1160-1290 kWh/mt], though some of the best have reached 1600 BTU/lb [1030 kWh/mt]. Furnaces with regenerative burners can attain 1100-1200 BTU/lb [710- 775 kWh/mt]. There are some designs of multi-chamber furnaces or oxygen furnaces that have improved on these numbers, perhaps as low as 950 BTU/lb [615 kWh/mt]. Typically, as the degree of sophistication and energy efficiency of the furnace increases, so does the cost."

Jan 1, 2010

By Katsuyoshi Tatenuma

"In order to mitigate the effect of global warming by preventing the accumulation of atmospheric CO2, a permanent fixation method of surplus CO2 as an insoluble mineral onto the sea bottom is proposed. As the proposed reduction method of atmospheric CO2, the concrete concept of this method is to form an insoluble carbonate mineral (CaCO3) by direct electrolysis of the seawater; Ca2++2HCO3 -+OH- ? ?CaCO3(insoluble)+CO3 2- (soluble)+H++H2O <not as coral reef reaction>, are directly disposed of itself onto the sea bottom. By this treatment, a concentration of carbonate is reduced in the section of superficial seawater, and therefore the absorption capacity of atmospheric CO2 increases depending upon the shift of chemical carbon equilibrium between the mass of superficial seawater and the atmosphere. As no additives are required, or no secondary waste are produced, the proposed method assuming as green-orientated, has possibility to resolve fundamentally the problem of global warming in a green orientate manner.IntroductionRecently, the amount of atmospheric CO2 has been exponentially increasing and it is a main greenhouse effect gas causing the global warming [1, 2]. The concentration of atmospheric CO2 has increased more than 30% (370ppm in 2001) during only last two centuries, therefore approximately 750 Gton-C of CO2 currently exist in the atmosphere, in which 180 Gton-C of CO2 are accounted for the increment during two centuries [1, 3, 4]. In order to avoid the progressive increase of CO2 global abundance, 3 Gton-C of the incrementing amount per year [4], have to be removed annually from the atmosphere."

Jan 1, 2008

By Suman Das, Justin J. Gambone, Rohan Bansal, Ranadip Acharya, Paul Cilino

"This paper focuses on generating a quantitative microstructure prediction model for Scanning Laser Epitaxy (SLE) process based on coupled flow-thermal modeling using Finite Volume method. SLE is a laser-based additive manufacturing process for the deposition of equiaxed, directionally solidified and single-crystal nickel superalloys through the melting of alloy powders onto superalloy substrates. In the current work, the detailed effects of natural and Marangoni convection on the flow field are studied and the results are analyzed in terms of the temperature gradient, vorticity parameter, melt pool dimensions and mushy region extent. The detailed property data of the processed superalloy and the laser scan path are incorporated in the model to predict the microstructure in realistic scenario. An optimization study is carried out to evaluate the critical parameter values at which the columnar-to-equiaxed and the oriented-tomisoriented transition take place. This work is sponsored by the Office of Naval Research through grant N00014-11-1-0670.IntroductionSLE is a laser-based additive manufacturing process for the creation of structures in equiaxed, directionally solidified and single-crystal nickel superalloys through the selective melting and resolidification of superalloy powders. In SLE, a tightly focused laser beam is guided by a highspeed galvanometer scanners allowing for tight control of the amount of energy being applied to the top of the powder bed, as well as the speed at which the melt pool moves across the substrate. Under the proper operating conditions and with sufficient substrate meltback, the solidification microstructure follows the morphology of the underlying substrate, allowing for directional and even SX growth.Several reports on the modeling aspects of laser cladding-based additive manufacturing approaches can be found in the literature. Approaches based on Finite Element Methods (FEM) and Finite Volume Methods (FVM) are employed for the thermal modeling of the system [1, 2]. Gaumann coupled the Columnar to Equiaxed Transition (CET) modeling with the Rosenthal solution in earlier work based on laser cladding [3]. Rappaz et. al. provided a detailed modeling of the microstructure/columnar orientation based on the solidification velocity and crystalline orientation [4]. This approach is based on the selection of the growth direction that closely follows the melt pool normal direction. Later on, substrate orientation is also taken into account [5, 6]."

Jan 1, 2013

By T. Shibasaki, S. Kamio, K. Kanamori

"Mitsubishi Process has been proven through fifteen years operation to be highly productive, cost efficient and easy to abate environmental requirements. However, in order the process to remain competitive from now on, it should also be adaptable to a variety of varying conditions. Various test works have been conducted from such a stand point of view and some of the new concepts have been implemented to the actual operation.The paper discusses the adaptability of the process to the change of concentrate grade with respect to copper and also impurities, acceptability of the secondary materials and the potential to increase unit capacity. IntroductionThe first commercial plant of Mitsubishi Process with 48,000 mt copper annual capacity started its operation at Naoshima Smelter of Mitsubishi Metal Corporation in 1974, and the second plant with 65,000 st annual capacity started in 1981, at Kidd Smelter, Timmins, Ontario, now Kidd Creek Division of Falconbridge Limited 2. These plants have increased their capacities to 90,000 mtpa respectively by adding oxygen and acid plant capacities while maintaining the original furnace design uncharged. Thereby both smelters have established more cost efficient operations. (3), (4)Mitsubishi Process applies so-called multi-furnace continuous system. Figure 1 shows conceptual flowsheet. Backgrounds that required and justified the development of such system are as follows:"

Jan 1, 1988

By J. R. Goode

There are at least a dozen methods of selectively removing cerium from a mixture of the rare earth elements (REE) including separation techniques based on the oxidation of cerium to the quadrivalent state. Several of the oxidation processes have been operated on a commercial scale, others have been tested and in some cases are part of proposed flowsheets. In this paper, we describe and compare the various methods. We also present preliminary estimates of the costs of early Ce removal and discuss recovery and purity aspects of the options.

By Qingzhu Li

The brewing industry byproduct, spent grain (SG), was evaluated for its ability to adsorb Ag(I) from aqueous solutions. Ag(I) adsorption was dependent on solution pH, contact time, adsorbent dose, initial Ag(I) concentration and temperature. The kinetic data were well described by pseudo-second-order kinetic model, indicating that chemical adsorption was the rate-controlling step. The equilibrium data followed Freundlich isotherm rather than Langmuir isotherm, suggesting heterogenity of the adsorption sites on spent grain. Ag(I) desorbed from Ag(I)-loaded spent grain was also evaluated in this study. HCl, NaOH, Na2S2O3 and ultrapure water were chosen as eluants and desorbed Ag(I)-loaded spent grain for 30min, Ag(I)-loaded spent grain desorbed in 0.1M Na2S2O3 exhibited higher elution efficiency as compared with other eluants. The results indicated that application of spent grain for adsorption and recovery of silver from aqueous solutions was feasible.

Jan 1, 2009

By Ying Mao, Zhancheng Guo, Long Ma, Huiqing Tang

"A new 2D computational fluid dynamic (CFD) model was developed for the gaseous reduction of iron ore fines in an innovative reactor-multilayer moving-fluidized bed. The solution of the proposed model was performed by integration of FLUENT and PHOENICS. Numerical results of cold state were compared with the experimental data and the agreement between them was good. A hot case-gaseous reduction of iron ore fines using syngas with this reactor was simulated using the present CFD mode. Results indicate that under the given simulation conditions, total pressure drop is 90 Pa less than that under cold state though the gas supply rate is increased about 4m3 under hot state. Gas temperature decreases from 1073 K at the bottom to 500 K at the top, Utilization efficiency of the gas reduction potential is about 27 %. For ore fines reduction, the final reduction fraction could reach 0. 70 and solid temperature 900 K.IntroductionWith the development of coal gasification technology, various coals could be converted to Syngas with air or steam. Therefore gaseous reduction of iron ore fmes becomes an acceptable alternative process for iron making besides blast furnace route[!] and moreover it still has some advantages in processing low grade iron ore fines[2]. Gaseous reduction using fluidized bed technologies is the most competitive in all direct reduction iron-making processes up to now. It has the advantage that ore fines can be directly charged to the process without prior treatment while its disadvantages are particle agglomeration and high gas/solid ratio[3]. To avoid these advantages, a new reactor, multilayer moving-fluidized bed reactor has been developed for carrying out the gaseous reduction. Hydrodynamic behaviors of gas and fines in the reactor were studied and the results were satisfying[4]. However, due to its unique structure of the multilayer moving-fluidized bed and unique gas-solid flow pattern, models of multiphase flow as IPSA, DPM and Eulerian Model could not give a satisfying solution. The current paper is developed a new CFD model and a new solution approach for simulation of the reactive gas-solid flow in the multilayer moving-fluidized bed for its optimization, design improvement and future scale-up."

Jan 1, 2013

By Bo Liang, Hongmin Zhu, Kai Huang, Shafiq Alam

A new approach of recovering platinum and palladium from electronic wastes by hydrochloric acid leaching followed by selective adsorption on low-cost and environmentally benign biomass sorbent prepared from easily available agriculture waste is suggested. The obtained adsorbents were prepared by a combination of chemical modification and hydrothermal carbonization process with (NH4)2C2O4. It was found that the maximum adsorption capacity of hydrothermal carbonized garlic peel for Pt( ) and Pd( ) was 1.64 and 0.42 mol/kg respectively. The Langmuir adsorption isotherm was applied to describe the adsorption process. Kinetics of the Pt( ) and Pd( ) ions adsorption was found to follow pseudo-second-order rate equation. The adsorbents were examined by scanning electron microscope (SEM), and Fourier transform infrared spectroscopy (FT-IR). Based on the characterization results, a possible mechanism of Pt( ) and Pd( ) ions adsorption with the hydrothermal carbonized garlic peel was proposed. This study provides a promising adsorbent with efficient adsorption property for platinum and palladium recovery from the leach solution of electronic wastes.

Jan 1, 2016

By Anja Pfennig, Thomas Böllinghaus, Marcus Wolf

During CCS components are exposed to a corrosive environment and mechanical stress which results in corrosion fatigue and is inevitably followed by the lifetime reduction of these components. The lifetime reduction of the cyclically loaded high alloyed stainless injectionpipe steel AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2- saturated hot thermal water is demonstrated in in-situ-laboratory experiments (T = 60 °C, brine: Stuttgart Aquifer, flow rate: 30 l/h, CO2) in an environment similar to the on-shore CCS-site in the Northern German Bassin. In-situ tension-compression experiments were established simultaneously along with electrochemical measurements using a newly designed corrosion chamber in a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h. S-N plots, micrographic analysis and surface analysis of the fracture surface are demonstrated. X46Cr13 (surface roughness Rz = 4) reached the maximum number of cycles (12.5 x 106) at stress amplitude of 173 MPa producing a low scatter range of 1:3.5. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists. Pit corrosion prior to crack initiation may be identified as failure cause.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Shu Bin, Lin Chen, Wanda Bin

"Vanyukov Process has been mainly applied for processing copper and nickel sulfide ore for more than 30 years. Based on the understanding of the Vanyukov Process, researchers from China introduced the technology into the areas of lead, antimony and bismuth extraction by changing the furnace structure and technical flow, which greatly extended the application area and raised the processing efficiency, thus developed the oxygen-rich side-blow bath smelting (OSBS) technology in 2000. This contribution reviews the history of OSBS technology from four respects: the quantity, the furnace structure, the process flow and the application area. Its potential research direction and industrial application are also summarized.IntroductionVanyukov bath smelting furnace and related bath smelting technology were developed by researchers from Soviet Union who devoted comprehensive research on fundamental theory as well as engineering technology [1,5]. Vanyukov process has been applied for large industrial production since the 1970s and it is still one of the major methods in modem pyrometallurgy process. The appearance ofVanyukov double district furnace and joint double furnace in the past ten years, which are applied for copper smelting, is the most valuable advances of the Vanyukov process [7,8,9]. However, the application ofVanyukov process was limited in copper and nickel sulfide ore smelting, and few countries adopted this process except Soviet Union."

Jan 1, 2013

By Khalid Hattar, Alexander McGinnis, Buchheitm Thomas, Paul Kotula, Luke Brewer

"Understanding the effects of extensive radiation damage in structural metals provides necessary insight for predicting the performance of those metals considered for application in the extreme radiation environment. Predicting mechanical performance after long term radiation exposure is of great importance to extending the life of current nuclear reactors and for developing future materials for the next generation of reactors. A combination of finite element modeling, nanoindentation, and TEM characterization were used to rapidly determine the microstructure and mechanical properties influences of ion irradiation on a standard 3 l 6L stainless steel sample. The results of this study found that ion irradiation and small scale mechanical property testing can be used to characterize extensive levels of radiation damage structure, only when significant consideration is given to ion irradiation depth, surface roughness and polishing condition, the irradiation temperature, and many other experimental parameters.IntroductionFor either the success of next generation nuclear reactors or the extension of current nuclear reactors significantly beyond their designed lifetimes, research is needed into the degradation of the microstructure and mechanical properties governing the performance of the reactor alloys exposed to extreme environments. Although the exact dose and temperature of these nuclear reactor plans may vary, the cladding and other structural components will be exposed to greater dose and at elevated temperatures. To acco=odate these severe exposures, established cladding materials are being testing to longer exposure and new alloy compositions are being considered. [1-3] For neutron test facilities to reach 100 dpa level, exposure times often span several years, significantly limiting the down-select process of potential new materials for extreme radiation environments. Ion irradiation has been used as a technique to provide a look at the effect of irradiation damage on materials in a significantly shorter time frame. Previous work using proton irradiation provides a deep, broad, and relatively uniform defect profile compared to heavy ion irradiation; however, using this type of radiation still requires weeks to months to reach the 100 dpa level. [4] In this research, we investigated the feasibility of using heavy ion (nickel) irradiation and small scale mechanical testing to provide in a few days a first order screening technique for potential alloys that are being considered for advanced testing."

Jan 1, 2012

By Halvor Dalaker, Pål Tetlie

The decomposition of methane has been studied experimentally in contact with various oxides at elevated temperatures. For each oxide, the temperature at which the cracking starts has been determined. No correlation was found to exist between the temperature for the onset of cracking for a given oxide and the affinity for carbon of the oxide's metallic component. In terms of potential for using methane as a reducing agent, calculations are presented that indicate that the suitability of an oxide for such reduction depends on the desired methane+oxide reaction being more energetically favourable than the methane+methane=ethylene/acetylene reactions.

Jan 1, 2014

By H. -P. Behrendt

Muldenhiütten Recycling und Umwelttechnik GmbH is a lead smelter with a very long tradition. The first reference to the existence of smelters on this site is given by a document of inheritance dated 1318. Originally run as a primary lead smelter, which was supplied with ores from the Freiberg mining district and from overseas, it was required to change it over to secondary raw materials due the abandonment of mining in the Freiberg area in 1968. Today, Muldenhüitten Recycling und Umwelttechnik GmbH has two production lines; lead production from secondary lead and waste incineration, which are closely connected and gain advantage from each other. Installations, improved technologies, and the highly skilled personnel have contributed to satisfy all demands for a production concerning quality and environment.

Jan 1, 2000

By G. C. Yao

Branch and needle-shaped intermetallic compounds of iron, silicon and aluminum normally exist in the molten aluminum. If a suitable amount of manganese metal is added into molten aluminum, the shape of the intermallic compound particles may become lumpish and spherical. According to the difference in electric and magnetic properties of these impurity particles and molten aluminum, these impurity intermetallic compound particles can be separated by applying an alternating magnetic field. In this experiment the alternating magnetic field was formed by a "c" type loop with AC (50Hz) current. The inner vacuum of the fireclay refractory separator is 25xl5xl30mm3 with a lateral baffle inside. The separator was put into the interspace of the "c" type loop. It was found that the longer the separation time, the larger the amount transferred of impurities. The amount of transferred impurities increases with the increase of separation time and intensity of magnetic field. The addition of manganese metal enhances significantly the efficiency of impurity separation

Jan 1, 2003

By J. W. Dini

Introduction The mission of the Materials Fabrication Division (MFD) is to provide fabrication services and technology in support of all programs at Lawrence Livermore National Laboratory (LLNL). MFD involvement is called for when fabrication activity requires levels of expertise, technology, equipment, process development, hazardous processes, security, or scheduling that is typically not commercially available. Customers are encouraged to utilize private industry for fabrication activity requiring routine processing or for production applications. MFD is .a large diversified service organization including approximately 400 full time employees. The group provides a wide variety of processes including all common machining and fabrications operations, laser and water jet cutting, electrical discharge machining, lapping, electron beam and laser welding, vacuum brazing, heat treating, forming, electroplating and metal finishing, optical polishing and grinding, vacuum coating, vacuum engineering and a variety of plastics operations. These operations occupy more than 1,250,000 square feet of floor space. For more detail on the many fabrication related services available from MFD, see Reference 1.

Jan 1, 1992

By D. A. Milligan

Ammonia leaching of copper sulfide concentrates, matte, scrap or other sources of copper yields copper amnine sulfate solutions which are converted to metal in a two-stage process involving precipitation of inter- mediate sulfites and their thermal decomposition to copper powder of high purity. Processing details and results are given. Considerable simplification in circuitry and cost savings are indicated. Energy requirements are reduced by substitution of copper powder precipitation and ammonium sulfate crystallization for solvent extraction, electrowinning and lime boil.

Jan 1, 1976

By Peng ZANG, Qihang Liu

Experimental work was conducted to determine the relationships of coal char conversion with temperature and heat absorption. The results show that at an earlier stage of the coke forming process, lump coal would absorb large amounts of heat but the increase of high temperature strength of lump coal was not significant. Contrarily, the lump coal’s high temperature strength was greatly improved at later stage of coke forming process. A number of residual coal was found in most tuyere coke samples illustrating that the lump coals added in the melter gasifier were not completely transformed into coke when they arrived at the tuyere region. The results indicate that the improvement of lump coal’s high temperature performance is limited in the melting gasifier by the low coke forming rate which could become the core factor of fines generation of lump coal in the melting gasifier.

Jan 1, 2016

By Rui-Qing Li, John G. Peacey, Peter J. Hancock

"Noranda has been investigating a pyrometallurgical process for the direct recovery of zinc from zinc concentrate and zinc and iron containing residues. The process consists of injecting dry zinc concentrate and secondary zinc materials into a molten iron oxysulphide bath, volatilizing metallic zinc into furnace off gas essentially free of sulphur or S02, fixing sulphur contained in the feed materials as iron oxysulphide matte which is disposed, and recovering metallic zinc in an ISP type lead splash condenser. Combustion of petroleum coke with air or oxygen enriched air inside the oxygen containing matte supplies part of the heat, and the products of combustion dilute the zinc-laden gas to a desired level.This paper describes the process concept, thermodynamic background, experimental tests, mass and heat balance calculation for a conceptual flowsheet, environmental stability of the residue and advantages and disadvantages of the process. Experimental tests have successfully proved the process concept and thermodynamic predictions. Direct smelting of zinc concentrate and residues inside an iron oxysulfide bath has a great potential to become a cost effective and flexible zinc smelting process.1. INTRODUCTIONZinc is mainly produced by a roast-leach-electrowinning process route, which accounts for about 80% of the world primary zinc production. This process produces high quality zinc with very high zinc recovery (>95%) but suffers from several major drawbacks such as using high cost electricity as reductant, producing environmentally problematic iron containing leach residue (jarosite or goethite) and the difficulty in treating secondary zinc feed materials containing high impurity levels, such as electric arc furnace dusts from the steel industry, and other complex sources. Also in some areas, markets for sulphuric acid are distant resulting in negative realizations on acid sales.The Imperial Smelting Furnace (ISF) process is the major pyrometallurgical process to treat zinc-lead concentrate. The advantage of this process over the electrolytic zinc process is its flexibility in treating high-lead, bulk concentrates with high recoveries of lead, copper and precious metals. However, this is a two-stage process involving sintering of Zn-Pb concentrates followed by blast furnace reduction. The process requires large amounts of high-quality coke which is a major operation cost, and the sintering process which results in serious environmental problems."

Jan 1, 1996

By A. G. Jackson, S. J. P. Laube

"Control of thin films during the growth process is dependent on several parameters that are difficult to monitor, including flux of film material, pressure, substrate temperature, composition, and thickness. One means for easing this difficulty is to take advantage of emission spectra associated with the process and the film. For pulsed laser deposition (PLD), the ion cloud generated by the laser has characteristic emission spectra that can be used to control the flux and, hence, the film. For chemical vapor deposition, the species present can be determined using mass spectroscopy and specific peaks can be used to control the deposition. Raman spectroscopy affords the possibility of real-time control by sensing characteristic peaks associated with film composition and thickness. These spectroscopic methods offer a real-time alternative to process control that is very attractive, because of the ability to accurately control films to achieve the engineered structures and properties sought. Examples are presented to illustrate the capabilities of these methods for thin film preparation.IntroductionThe drive to reduce costs and improve efficiencies of operation sets the tone for much of research, basic or applied. Basic research is limited by the ability of sensors and associated instrumentation to measure parameters accurately and reproducibly. Applied research has the same limitations and also the added constraints of time and costs. Hence, there are strong incentives to explore means for refining existing sensors with respect to performance and cost, as well as finding new sensors and techniques for more accurately and rapidly measuring quantities of interest in experiments and in various processes."

Jan 1, 1997