By Chang Wei, Zhigan Deng, Jiqiang Liao, Minting Li, Hongsheng Xu, Yan Song, Cunxiong Li, Xingbin Li

"Abstract: Direct ?otation of oxidized zinc-lead ore is characterized by recovery of zinc and lead only around 55% and 50%, respectively. Mineralogical analysis shows that the sample used in the present study is a carbonate hosted zinc-lead ore, with a zinc and lead carbonate content that accounts for 80.14% and 75.63% of the total minerals, respectively. The carbonate hosted zinc-lead ore was hydrothermally sulfidized with elemental sufur and the experimental data indicated that under the conditions employed up to 75% zinc and 82% lead sulfidation extent were achieved. As a result of pre-sulfidation followed by flotation, the recoveries of zinc and lead into flotation concentrate were over 90%. A flotation concentrate was obtained with 52% Zn and 37% Pb from the materials which was treated by sulfidation.IntroductionSulfide ores are the primary source of zinc and lead, and they are becoming depleted; thus, metallurgical investigators are interested in using abundant oxidized zinc-lead ore reserves. The high-grade zinc-lead oxidized ore, which normally has a zinc content higher than 15%, can be disposed of by acid leaching and electrolysis. However, the low-grade ore, which has a zinc content lower than 10%, is difficult to smelt with pyrometallurgy and hydrometallurgy, and the processes are very complicated and expensive in terms of production flow and energy consumption. Therefore, making the low-grade oxidized zinc-lead ore more beneficial has become more important in recent years. Flotation is the most common process, and the primary method of recovering zinc and lead from sulfide or oxide minerals. It is well known that there is a difference between sulfurized and oxidized minerals regarding their separation by flotation. Flotation of zinc and lead oxidized minerals is extremely complex because of the similarities in the physicochemical and surface chemistry of the constituent minerals. There are no known direct-acting collectors capable of producing single metal concentrates [1-3]."

Jan 1, 2012

By Priscilla Aki Mori de Hanashiro, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Hugo Hashimoto

"The LCDs are used in televisions, calculators, mobile phones, computers (laptops and tablets), video games and other electronic devices. The advancements in technology make obsolete these devices, causing excessive disposal of LCDs and therefore decreasing life span of landfills. In this context, the LCDs from LED LCD TVs arise as an additional source of waste electrical and electronic equipment (WEEE). Thus, it is essential to develop LCDs recycling methods, beginning with the LCD characterization followed by displays processing, aiming the materials separation and using some Ore Treatment Techniques, and finally, the recovery of indium using acid leaching. The analysis methods that will be used in this work are: Fourier Transform Infrared (FT-IR) and Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES).IntroductionLiquid Crystal Display (LCD) technology is applied in modem televisions, calculators, mobile phones, computers and a wide range of electronic devices. It has replaced Cathode Ray Tube (CRT) technology as the most advantageous display product, due to lower electrical power consumption, size and weight reduction, and no radiation emission [ 1]. The constant improving of LCD screen technology reflects on its growing contribution to the amount of waste electrical and electronic equipment (WEEE): an estimated 50 million tons of WEEE are produced every year [2]. Once the most common method of its disposal are landfills, the LCD technology therefore became an environment issue [3].LCD structure is composed by components made by different materials. In order to develop a LCD recycling methodology that gives the right destination to these materials, a previous characterization stage is required. This characterization includes a disassembly process and material identification analysis. One of the LCD components is the screen, which is composed by polymeric and glass layers. The liquid crystal glass was the starting material of this study. It contains indium in the form of indium tin oxide (ITO) film. This ITO film is deposited in the glass by a sputtering process and acts as the electrode material [4,5]. It has in its composition 90% ofln203 and 10% ofSn02 [6]."

Jan 1, 2014

By Qiang Guo, Zongliang Zuo, Mengqi Wei, Qingbo Yu, Qin Qin

Activated carbons, derived from waste ion-exchange resin by CO2 physical activation, were applied to separate CO2 from flue gas against global warming. The BET specific surface areas of activated carbons at different activation temperatures and times were investigated. The CO2 adsorption capacity was tested under non-isothermal and isothermal conditions. The experimental results show that when keeping the activation temperature constant, the specific surface area increases firstly and then decreases with increasing activation time. For the given activation time, the specific surface area rises firstly and then declines with increasing activation temperature. The adsorption capacity decreases with increasing temperature. The maximum adsorption capacity is 51.46 mg/g under the condition of 298 K and pure CO2. Fractional order kinetic model is the best one to describe the kinetics of CO2 adsorption. The activated carbons show the potential to be an effective adsorbent for the removal of CO2 from flue gas.

Mar 1, 2018

By Anna Wasilkowska

The study concentrates on the effects exerted by microstructure, deformation history and uniaxial stress conditions (temperature, stress state, strain rate) on the mechanical properties offerritic TRIP-aided steels for automotive applications. In low-alloyed TRIP-steels it is quite difficult to separate the effect of the austenite to martensite phase transformation from the influence of the ferritic matrix contributing to the yield stress and uniform elongation. Investigation of transformation kinetics of retained austenite as a function of the deformation temperature show that using the parameter k to characterize the retained austenite stability allows to identify regious of different temperature sensitivity separated by a transition temperature of 10±5°C. The observed low strain-rate sensitivity of the flow stress is an intrinsic property of the ferritix matrix and points to defomtation governed by slip. The ultimate tensile strength is much stronger affected by temperature than the yield stress. The influence of the temperature on the elongation is complex, because of the heating of the specimens by 60-l20°C at moderate and high strain rates. The increase of the total strain can be understood in terms of thermal softening of the ferrite. On the other hand, the steep increase of the stress during dynamic testing is an effect of accommodated elastic and plastic strains in the matrix. The strain- hardening exponent is dependent on the conditions imposed during testing. The martensite transfomtation rate is lower and the critical stress for martensite nucleation is much higher under compression compared to tensile loading. In secondary tensile tests, the yield stress increases steeply, and the ultimate tensile strength and the total elongation depend linearly on the amount of pre-straining. The results confirm that in the range of 8=10-4 s-l the TRIP-effect governs room temperature plasticity. Keywords: TRIP-steels, mechanical properties, strain rate sensitivity, temperature sensitivity, austenite stability

Jan 1, 2003

By Debbie Marshall

Nickel and cobalt in lateritic ores can be extracted by either a hydrometallurgical or a pyrometallurgical route. The high-iron limonitic fraction of a deposit is best processed' hydrometallurgically while the magnesium-rich transitional and saprolitic fractions are more suited for pyrometallurgical processing. During hydrometallurgical processing, it may be attractive, for economic reasons, to blend the limonitic component with transitional and saprolitic ores, which contain higher nickel levels. However, blending increases the concentration of magnesium in the feed, leading to increased acid demands. The decision on how much ore to process then becomes an economic one. Ore samples with different magnesium contents were prepared for the leach test program by blending limonitic and transitional ores. The ore samples were slurried in seawater and tested in the Falconbridge Hydrometallurgical Pilot Plant. As expected, acid consumption increased with increasing magnesium content of the ore. For target extractions of 95% nickel and 92% cobalt, the required residual free acid concentration increased from 30 g/L at 1.7% magnesium to 50 g/L at 2.7% magnesium. When the magnesium content was raised to 3.8% and 4.6% in subsequent pilot plant testing, the final free acid requirements did not increase beyond what was observed at 2.7% magnesium. Thus, the cut-off ore composition to maximize nickel units and minimize acid requirements is between 1.7- 2.7% magnesium. Keywords: high pressure acid leaching, laterites, magnesium

Jan 1, 2004

By Jie Ma, Shun-Li Zhao, Jian Zhao, Jie-Yu Zhang

"Microstructural morphology evolution of Ni-45wt.%Mo droplets during rapid solidification process was investigated using an advanced modified 3D cellular automaton-finite element(CAFE) model by CALCOSOFT software. The model was modified by User-defined functions (UDFs) and validated with experimental solidification microstructural morphology of Ni-45wt.%Mo droplets available in the literature. Then, the influences of convection heat transfer coefficient, superheat of the alloy droplets and droplets size were investigated during the rapid solidification process. The predictions show that microstructural morphology is obviously sensitive to convection heat transfer coefficient and droplet size. With the decrease of convection heat transfer coefficient, the grain density decreases. In addition, the decrease of the droplet size could obtain refined microstructure. However, decrease the superheat ofNi-45wt.%Mo droplets has little effect on microstructural morphology.IntroductionFor several decades, much attention has been paid to undercooled alloy droplets of rapid solidification process for which can obtain refined microstructure, decreased microsegregation and extended solubility of alloying elements [1-3]. Extensive prior work shows that solidification of droplets plays an essential role in advanced material properties [ 4]. Consequently, it is very important to investigate the microstructural morphology evolution, especially for dendrite growth during non-equilibrium solidification process, for dendrite growth reflected the kinetics of the crystal growth process."

Jan 1, 2013

By K. Sarveswara Rao

"Any innovative approach made in non-ferrous metallurgical industry centers upon developing new processes, saving materials, improving production quality, and bornagain materials. Aqueous processing is commonly used to treat lean grade or more complex ore bodies. Its sustenance largely depends on energy and environmental compliance including water and wastewater management. The present paper focuses the importance of using particle size distribution and surface area measurements during ammoniacal dissolution of a Cu-Pb-Zn sulphide bulk concentrate and with an overview of the effect of water salinity on the process chemistry and residue mineralogy. Accordingly, an effort is made here to discuss the emerging perspective and highlight the recent successes and trends in terms of energy savings in non-ferrous hydrometallurgy.IntroductionThe nature and structure of the global energy industry is likely to change significantly in the 21st Century. Rabago et al [1] have comprehensively discussed how the mining and minerals industries can adapt to the challenges and opportunities posed by trends and drivers in global energy use. According to the authors, the drivers of sustainability include water, efficient energy use, climate modification, transportation technologies and energy security. Sustainability and competitiveness for the minerals industry will depend on natural capitalism, resource efficiency, new processes, saving materials, improving production quality, born-again materials and the solutions economy. Based on this motivation, the theme of the present paper is centered upon applications as relevant to energy and sustainable development in non-ferrous hydrometallurgy."

Jan 1, 2009

By Vincent Canaguier

Methane is increasingly considered as a promising reductant for metal oxides, including chromite. To assess the possibilities of such reduction route, the gas-solid reactions between Ar–CH4–H2 gas mixtures and synthetic chromites are studied between 950 and 1050 °C. The influence of Mg and Al additions on the reduction-caburization of (Fe,Mg)(Cr,Al)2O4 solid solution is investigated thermodynamically, structurally and kinetically. The product phases are examined by x-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). The reaction rate is derived from real-time exhaust gas measurements and post-reaction product analyses such as oxygen analysis. Kinetic models are proposed based on the product phase morphologies and confronted with the empirical data.

By J. W. Bridge

Triaxial compression tests at various confining pressures and temperatures, as well as tangent modulus tests using ultrasonic waves, were conducted for wax-coated granular composite materials. The material used is a surface for Thoroughbred horse racing. The purpose of these tests is to examine how track shear strength and tangent modulus at a range of loads respond to changing temperatures. Previous work has shown that a wide range of operational temperatures are experienced which have been reproduced in the lab. Using differential scanning calorimetry, it is confirmed that these operational temperatures correspond to distinct thermal transition regions for the wax that is used to coat the sand in these surfaces. Preliminary results show that both shear strength and tangent modulus are sensitive to temperature changes with maximum strength and modulus correlating with major DSC wax transition regions.

Jan 1, 2010

By Wei-ling Wang, Ryosuke O. Suzuki, Xiang-ning Meng, Miao-yong Zhu

"A finite-element thermal-stress model of continuous casting mold is conducted to predict deformation of copper plates and its change with different cooling structure. The results show that deformation behavior of copper plates is mainly governed by cooling structure and thermal- mechanical conditions, deformation amount is related to structure geometry, and a small deformation mutation occurs in cooper-nickel boundary due to different properties. The maximum deformation of hot surface centricities of wide face locate at 100 mm below meniscus and that of narrow face locate at meniscus and terminal of water slots and significant curvature fluctuations on both sides of copper-nickel boundary. The maximum deformation of centricities is increased up to 0.05 mm with thickness increment 5 mm of copper plates, and maximum deformations are only depressed 0.01 mm and 0.02 mm with increments of 1 mm nickel layer thickness and 2 mm water slot depth respectively.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipate in primary cooling zone and make continuous casting mold under enormous heating load giving rise to thermal stress, deformation, high-temperature fatigue and creep not only depress mold life-span, but reduce casting stability [1] Many studies focused more on heat transfer, solidification and shrinkage of solidifying shell to provide inverse proposals for optimizing cooling system and even designing new taper of mold [2,3], but it is generally useless to those of having been manufactured or being put into production. Therefore, mold-related forward problems show necessity to be discussed deeply, and stress and deformation distributions based on special thermal conditions in mold should be analyzed in order to explore suitable cooling structure of mold directly. Samarasekera et al. [4] examined heat flow and distortion of two-dimensional longitudinal sections and investigated effect of cooling water velocity, copper plates thickness and carbon content on formation of rhomboidity and longitudinal comer cracks. O'Connor et al. [5] developed a three-dimensional mathematical model to compute thermo-mechanical state in thin-slab mold and calculated temperature and deformation of mold wall to assess roles of various process parameters on impacting mold life. Thomas et al. [6] predicted temperature, distortion and residual stress in mold and indicated increased distortion requires increased remachining, which reduces mold life and increased residual stress increases the probability of a catastrophic crack failure. Park et al. [7l determined heat-flux profiles in funnel-shaped and parallel thin-slab molds based on an inverse heat conduction model and thermocouple temperature measured in-plant and put them into three- dimensional finite-element thermal-stress model to predict temperature, distortion and residual stress of mold wall. Korie et al. [SJ focused on prediction of temperature, distortion and residual stress in mold and in particular to clarify that mold life is significantly affected by temperature and its rigidity, but little effect by mechanical including clamping force, bolt prestress, friction and ferrostatic pressure. Meng et al. [9l predicted temperature and thermal stress in a slab mold and analyzed effect by cooling system geometry and casting speed quantitatively. In present study, a three-dimensional finite-element thermo-mechanical model with type-switched element is transformed from previous heat-transfer finite-element model [9l, and mold deformation is simulated in order to shed light on thermo-mechanical behavior with special thermal conditions and different mold geometry at high casting speed."

Jan 1, 2013

By Chu Yong Cheng

The solvent extraction (SX) processes of the three pressure acid leach (PAL) nickel plants in Western Australia have been reviewed. The use of intermediate precipitation, solids/liquid separation and re-leach in the three W A nickel plants make these processes complicated and costly in capital and ?operation. The research work carried out by the SX group at the AJ Parker Cooperative Research Centre for Hydrometallurgy I CSIRO Minerals has led to the development of direct solvent extraction (DSX) processes to recover and purify nickel and cobalt from leach solutions. The simplicity of the process flowsheets and the expected savings in capital and operating costs are the major advantages of the new DSX processes over the reviewed processes. By using a new synergistic organic system in semi-continuous tests with a pilot plant leach solution (after iron precipitation) from BHP-BiIliton Stainless Steel Materials, the metal values (Ni and Co) together with zinc and copper were separated from the major impurities (Mn, Mg and Ca, together with Cl) in the first SX circuit. The co-extracted manganese, magnesium and' calcium were easily scrubbed out. After stripping, the metal values (Ni and Co) together with zinc and copper were concentrated, resulting in a much smaller second SX circuit and equipment in the down stream processes. The extraction and stripping kinetics of the metals with the new synergistic organic solution were very fast. The extraction and stripping almost reached steady state within 0.5 minutes. Semi-continuous test work with a synthetic leach solution, a cobalt pilot plant leach solution from Peko Rehabilitation Project Pty Ltd and a synthetic solution to simulate a concentrated laterite leach solution from BHP-Billiton Stainless Steel Materials showed that manganese, calcium, copper and zinc can be effectively and efficiently separated from nickel, cobalt and magnesium by extraction, scrubbing and stripping. This led to the development of another DSX process using D2EHPA to recover nickel and cobalt from leach solutions.

Jan 1, 2003

By Hoda Emami

In this study, a combined pyrometallurgical and hydrometallurgical technique has been designed and used to recover rare earth mixture elements (REE) and cobalt from a NdFeB magnetic waste. while addressing the cost of reagent and process facility. This process can be adjusted to different magnetic wastes regardless of their compositions. Prior to the leaching, the magnet scrap was pretreated by two rounds of roasting (750°C in air) and a mechanical grinding in between, to convert iron metal to ferric oxide. Subsequent leaching was performed using optimized conditions (pH, temperature and retention time) where the extraction ratio of REE to Fe III is the highest. After removing iron content from the leachate (pH ≈ 3), REE was precipitated selectively and purified further. The produced REE concentrate reaches 99% purity with 85% recovery in a single run. The cobalt oxide was isolated from the PLS as a by-product with 99.8% purity.

By Shanlu Yang

In this study, laser-GTAW hybrid welding was used to the lap joint of galvanized dual-phase (DP) 980 steel in a gap-free configuration. The effects of welding parameters such as the laser power, the distance between the laser beam and the electrode torch, the arc current on the quality of hybrid welds were fully studied. The reason for the formation of different weld defects arises from the development of the highly-pressurized zinc vapor at the interface of two metal sheets. Experimental results demonstrated that the elongated molten pool introduced by the GTAW can suppress the formation of spatters to some extent. However, the hybrid laser-arc welding process still suffers from a large amount of spatters that degrade the weld quality. Furthermore, it was found that the weld quality was enhanced with the increase in the laser beam-arc distance and welding current.

Jan 1, 2009

By H. Hahn, B. H. Kear, K. Kan, S. C. Danforth, G. Skandan, W. Chang

"A new chemical synthetic process for the production of non-agglomeratednano structured ceramic (n-ceramic) powders, starting from metalorganic precursors, is described. The process combines rapid thermal decomposition of a precursor/carrier gas stream in a hot tubular reactor with rapid condensation of the product particle species on a cold substrate. Critical to the success of this Chemical Vapor Condensation (CVC) process are (1) a low concentration of precursor compound in the carrier gas, (2) rapid expansion of the gas stream through an uniformly heated tubular reactor under a reduced inert gas pressure of 1-35 mbar, and (3) rapid quenching of the gas phase nucleated clusters or nanoparticles as they exit from the reactor tube. A wide variety of metal organic precursors is available commercially, all of which can be utilized in the CVC process to produce n-ceramic powders, including single phase, multiphase and multicomponent systems.The CVC process has been used to synthesize non-agglomerated n-SiCxNy and n-ZrOxCy powders, with controlled particle size in the range 2-20 nm. Heat treatment of the assynthesized n-powders in various high purity gas streams causes compositional and structural modifications, including particle purification and crystallization, as well as transformation to a whisker-like morphology. Thus, as-synthesized amorphous n-SiCxNy particles transform to (1) cubic n-SiC particles, when heated in flowing argon at temperatures> 1350 °C, (2) hexagonal n-Si3N4 whiskers, when heated in flowing NH3IH2 at 1400 °C, and (3) cubic nSiC whiskers, when heated in flowing H2 at 1400 °C.Non-agglomerated n-ceramic powders form uniformly dense powder compacts by cold pressing, which can be sintered to theoretical density at temperatures as low as 0.5 Tm' For example, full densification ofn-Zr02 powder compacts under free sintering conditions can be achieved at 1125 °C."

Jan 1, 1994

By Makoto Ohtsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SMB), The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force, The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films, The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a NisoMn2sGa25 or Nis2Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace, The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains, After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature, The martcnsitie transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated, After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found, The constraint-aged films also showed the two-way 5MB by thermal cycling,

Jan 1, 2003

By Makoto Ohlsuka

The ternary Ni2MnGa intermetallic compound is an intelligent material which has both a ferromagnetic property and a shape memory effect (SME). The use of the shape memory alloy films for an actuator of micro-machines is very attractive because of its large recovery force. The purpose of the present study is to investigate the effects of fabrication conditions and to clarify the relationships between these properties and fabrication conditions of the Ni-Mn-Ga films. The Ni-Mn-Ga films with a thickness of nearly 5 um were deposited with a radio-frequency magnetron sputtering apparatus using a Ni50Mn25Ga25 or Ni52Mn24Ga24 target. They were heat-treated at various temperatures between 873 and 1273 K for homogenization and ordering and then cooled in a furnace. The composition of the films depended on the sputtering power. The as-deposited films were crystalline and had columnar grains. After the heat treatment the grains widened and the grain boundary became indistinct with the increasing heat treatment temperature. The martensitic transformation temperature of the heat-treated films increased with increasing nickel content. Furthermore the effect of plastic deformation and constraint aging on SME is also investigated. After plastic deformation, the two-way SME was shown through the martensitie transformation and its reversion, The intensity of X-ray diffraction peaks from stress-induced martensitie phase was found. The constraint-aged films also showed the two-way 3ME by thermal cycling.

Jan 1, 2003

By Luciano E. Ramírez, Jesús L. Valenzuela, José R. Parga

"An innovative process for removing copper cyanide complexes including silver and zinc from cyanidation circuits has been developed. The technology was based on the inducing the nucleated precipitation of copper and silver in a tube serpentine reactor, using sodium sulfide as the precipitate and sulfuric acid as pH control. The results showed that pH had a great effect on copper cyanide removal efficiency and the optimum pH was about 3 to 3.5. At this pH value copper cyanide removal efficiency could be achieved above 97 and 99 % ,when influent copper concentration ions were 650 and 900 ppm respectively. In this process (sulphidizaton-acidification-recycle-thickening), the cyanide associated with the copper cyanide complexes is released as HCN gas under weakly acidic conditions, allowing it to be recycled back to the cyanidation process as free cyanide. This system was successfully commercial applied at Minera William in Mexico.IntroductionThe recovery of gold and silver from minerals and concentrates with cyanide is an important hydrometallurgical process, which has been studied for more than 124 years. Patented by MacArthur in 1888 [1], the process relies on the fact that gold dissolves in aerated cyanide solutions to produce the gold cyanide complex. The stoichiometry by wich this reaction occurs is known as the Elsner equation as shown here. Silver is accomplished in the same fashion."

Jan 1, 2012

By Yukihito Sasaki

Sumitomo Metal Mining Co. Ltd. planned an expansion program for the Toyo smelter and refinery in order to increase the production capacity of electrolytic copper to 450,000 tpy in 2007. Regarding the flash smelting furnace, a drastic increase in the average concentrate smelting capacity from 2,300 tpd to 3,950 tpd was required to achieve the plan. It was necessary to examine the performance of the Sumitomo concentrate burner when the feed rate was considerably increased. The authors developed a mathematical model to describe the combustion phenomena in the Toyo flash smelting furnace. This model was developed incorporating the fluid flow, heat and mass transfer, and chemical reactions of the copper concentrate and ancillary fuel. The copper concentrate was considered to mainly comprise chalcopyrite (CuFeS2). The reaction of CuFeS2 was assumed to consist of two steps, namely, the decomposition of CuFeS2 and the oxidation of the resulting pyrrhotite (FeS) and sulfur (S). The combustion phenomena in the furnace at the increased feed rate were predicted using this model. It was found that the Sumitomo burner was capable of enhancing the smelting capacity. This is attributed to the wide dispersion of the concentrate particles caused by an increase in the particle mass and a long residence time in the reaction shaft; this is due to the low temperature of the reaction air. However nonuniformity of the reaction in the reaction shaft was enhanced with the increased feed rate. In order to improve the nonuniformity of the reaction, an increase in oil-burner oxygen and an enlargement of the diameter of the dispersing cone were useful. By combining the expertise of the Toyo smelter staff and the calculation results, the concentrate smelting capacity of the Toyo smelter has been stably increased to 3,600 tpd thus far, and further improvements of the smelting performance are still being carried out.

Jan 1, 2006

By R. G. Robins

The effective removal of arsenic(V) from process streams and waste waters by precipitation with excess iron(II1) is sometimes attributed to the formation of basic ferric arsenates. The authors have investigated this system extensively using a variety of techniques and conclude that the solid phase produced is iron(II1) oxyhydroxide (ferrihydrite) with arsenic(V) adsorptively bound to the 2-3 nm particles.

Jan 1, 1992

By Nan Wang

Based on the commercial computational fluid dynamics software, Fluent, the fluid flow and temperature field in an iron-bath reactor were simulated numerically, and the effects of top-blown and side-blown operating parameters on the mixing time of iron bath, distribution range of oxygen in top space, and post-combustion ratio were investigated. The simulated results showed that the mixing time of iron bath increased initially and then decreased with the increase of inclined degree and immersion depth of side-blown lance. The distribution range of oxygen became wider as pulling the top lance away from the iron bath. Furthermore, post-combustion ratio was reduced given the top lance was too close the bath. The simulation results provide theoretical base for the process optimization of iron-bath reactor and further development of new type iron-bath smelting reduction process.

Jan 1, 2009