Search Documents

By Daniel Kim, Justin McAllister, Shijie Wang

"At the Kennecott Utah Copper Refinery, impurities in the electrolyte are being precipitated in the circulation system and form a hard scale in the piping. This scale must be removed periodically for proper electrolyte flow. Distinct layers of differing composition form as the operating conditions of the tank house change. Scale samples from the inlet and outlet pipes were analyzed to discover the nature of the precipitates. Each sample was sectioned and examined under optical microscopy and SEM. The composition of the scale was analyzed using ICP, XRD, and SEM/EDX mapping. The rate of deposition was determined by measuring the amount deposited on new pipes after elapsed time intervals. In order to determine how to minimize the formation of the scale, the mechanism was studied and the results are presented in this paper.IntroductionIn copper electrorefining, impure copper anodes are refined into pure copper cathodes. The impurities from the anodes are either insoluble and report to the slimes or soluble and dissolve concentrating in the electrolyte. These impurities are controlled by bleeding electrolyte from the system. Over time, the impurities combine to precipitate a hard scale on the surfaces contacted by the electrolyte. The scale causes problems with tank house circulation systems. In order for the refinery to operate properly, the scale must be removed periodically from the walls of the pipes. The first step to control the buildup of scale on the pipes is to understand the composition and the phases that are present in the scale."

Jan 1, 2012

By Marcel Sturzenegger

Though the extraction of copper is well established, generation of sulfur dioxide (S02) is still a troublesome issue. Conventional processes are further challenged by the increasing amount of impurities in the concentrates. Direct decomposition of the metal sulfides into the metal(s) and elemental sulfur under concentrated solar radiation offers a promising path to solve both problems. Thermogravimetric measurements under inert atmospheres have shown that synthetic chalcocite or chalcopyrite yield copper at temperatures as low as 1773 K. Even though optimum reaction temperatures might be somewhat higher, such temperatures are straightforwardly accessible in solar chemical reactors. The absence of oxygen will reduce the extent of slag forming reactions and thereby alter the evaporation characteristics of volatile impurities such as arsenic or antimony. Chemical equilibrium calculations for a chalcopyrite-enargite feed, e.g., have shown that under inert atmospheres arsenic compounds are completely evaporated at temperatures above 1000 K and an effective separation of arsenic from the matte is expected. An important step towards a solar production of copper is the design and testing of prototype solar chemical reactors for this reaction. Numerical modeling is a key tool supporting a rational design but it requires data of the high-temperature properties that prevail in these processes. Development of techniques for determining the essential quantities such as decomposition rates or radiative properties at temperatures up to 2000 K is therefore a main activity in our laboratory in order to control and optimize the process. Though developed in the frame of high-temperature solar technology, the experimental techniques are also suited to advance the understanding of conventional high-temperature processes. Keywords: Solar technology, Sulfur dioxide, Solar Radiation, Thermogravimetry, Chalcocite, Chalcopyrite, Numerical modeling.

Jan 1, 2003

By Paul-Dominique Oudenne

This paper reviews the experience gained by CMI NESA over the last thirty years for the treatment of arsenical and antimonical bearing concentrates and other complex metallurgical by-products. The importance of preliminary mineralogical characterization is emphasized as a preliminary step for the success of the roasting. Stage selective roasting appears as an attractive and efficient route for the treatment of complex concentrates. Numerous examples will be given for confirmation of such thermal treatment.

Jan 1, 2006

By Shadia Ikhmayies

Thermo-Calc software was used to investigate the phase diagram of the calcium silicon (Ca–Si) system for the range of Si mass percent 0–100, and temperature range T = 200–1800 K. The melting points of Ca and Si deduced from the phase diagram are very close to the values obtained experimentally. Three stable intermediate solid phases were found, which are Ca2Si, CaSi, and CaSi2, where the first one appeared in the Ca rich side of the phase diagram, and the third one in the Si rich side. In addition, three eutectic points were found at Si mass percents of 3.95, 33.00, 62, and temperatures T = 1048.7, 1519.14, 1308.5 K respectively. Atomic Si (Diamond structure) is found mixed with CaSi2 intermediate phase for temperatures less than 1305 K, and mixed with a liquid CaSi for higher temperatures. These results are important for thermodynamic and metallurgic studies of these intermediate phases.

Mar 1, 2018

By E. J. Peuraniemi

Recently commissioned Kennecott-Outokumpu flash converting was developed to replace the approved but environmentally outdated Peirce-Smith -converting to satisfy the globally tightening emission regulations. In the present study, dust formation and reaction mechanisms of two copper mattes with different experimental parameters were studied in lean suspension conditions. Both mattes had very high copper content of approximately 75 wt% and low iron content of 4.5 wt% and 1.2 wt% Fe. A laboratory scale, vertical laminar-flow furnace with a low feeding rate was used to simulate the phenomena taking place in the reaction shaft of a flash converter. Experimental conditions included temperature of 1300 °C with reaction gas oxygen contents of 20 vol%, 50 vol%, and 75 vol%. In the experiments, sieved particle fractions were fed to the furnace and sampled after short reaction time intervals by quenching them into a water film. Collected particles were analysed chemically for their main elements to define their removal rates. Also, optical and scanning electron microscopy with EDS-analyser were applied to determine phenomena occurring during reactions. Kinetics of oxidation as well as ignition of particles are discussed. Changes in particle morphology, size, and composition are reviewed to describe dust formation and reaction mechanisms.

Jan 1, 1999

By Antonio Martin, Jesus Hurtado, Francisco Jimenez

"Atlantic Copper is one of the largest copper producers in Europe. Its production facilities, including a primary copper smelter and an electrolytic refinery, are located in Huelva, on the southwest coast of Spain. These installations enable the smelting of over 1 million tpy concentrates to produce up to 260,000 tons per year of cathodes and 900 ktpy of sulphuric acid.Since 1970, several improvements have been made at the Converters Area such as modifications of primary hoods, operations with an OPC system, installation of scrap chargers, the recent installation of the secondary hoods and other environmental projects. All these modifications have been aimed at increasing the capacity of our smelter while keeping our continuous environmental commitment.This paper describes the modifications and improvements carried out at the converters area and our proposals for future developments."

Jan 1, 2012

By Xianwen Dai

One of the biggest challenges for the gold industry in the 21st century is the presence of copper in gold containing ore bodies. This is because copper consumes large quantities of cyanide. In addition, copper cyanide species are more stable than free cyanide, and hence are problematic in events of tailings spillage. The present paper compares cyanide and thiosulfate leaching for the recovery of gold from a copper containing ore. For cyanide leaching, the extraction of gold using copper cyanide complexes instead of free cyanide was tested in the presence and absence of added ammonia. For the thiosulfate leaching, the effect of the minerals present in the ore on the solution potential and thiosulfate consumption are illustrated.

Jan 1, 2003

By Anestis Vlyssides, Elli Maria Barampouti, Sofia Mai, ?postolos Vlyssides

"A new anaerobic reactor variation, the UASB/CO2-stripper reactor was conceived. It consisted of a conventional UASB reactor that recirculated the biogas produced. The sludge characteristics of this system were examined when treating high strength wastewater. From the data collected, it was obvious that the UASB/CO2-stripper system can satisfactorily operate at higher loading rates (25 g COD·L-1·d-1). A pronounced effect on the quality of the granular sludge was observed. The VSS/TSS ratio decreased sharply. A considerable decrease in the mean granule diameter was observed, while the specific gravity of the granules increased. The sludge bed porosity increased significantly leading to a considerable expansion of the sludge bed. These changes in the sludge properties led to a gradual shift of the system towards a fluidized bed process as far as its hydraulic characteristics were concerned.IntroductionIn recent years energy considerations and environmental concerns have increased the interest in direct anaerobic treatment of industrial wastes. The anaerobic method of waste treatment offers, under the present circumstances, a number of significant advantages with trivial or more serious drawbacks over other treatment methods. The major obstacle to the application of the process for this specific purpose is perhaps the difficulty of extending it to a stable and simple operational form. A number of reactor configurations has been developed leading to high biomass concentrations, e.g. the contact process, the filter reactor, the UASB reactor, and the fluidized bed systems, but the process stability problem still remains [1].A prime objective in the operation of anaerobic waste treatment process is the maintenance of a proper pH range. Thus, a possible solution to the process stability problem could be obtained by increasing alkalinity in the anaerobic systems. Therefore, the main objective of this paper is to present and evaluate the results of a system (UASB/ CO2-stripper) with increased alkalinity concentrations."

Jan 1, 2008

By K:-I. Rhee

The recovery of tellurium from Te-cement obtained during the processing of copper anode slimes was carried out by a series of hydrometallurgical processes, i.e. leaching Te-cement in NaOH solution, precipitation of impurites with the addition of Na2S followed by direct electrowinning of tellurium in NaOH solution. The optimum conditions for each process were determined and discussed in terms of various parameters associated with each step to maximize the recovery and purity of tellurium. The final purity of tellurium from electrowinning in alkaline solution was found to be more than 99.9 %.

Jan 1, 1997

By Jorge Alberto Soares Tenório, Amilton Barbosa Botelho Jr, Denise Crocce Romano Espinosa, Mónica M. Jiménez Correa

Wastewater from nickel lateritic process still has valuable metals that could be recovered. Using an ion exchange to recovery these metals, the iron becomes a problem due to the fact that it precipitate at pH 2. The aim of this research was to make iron soluble by reducing Fe+3 to Fe+2. A synthetic solution was prepared with sulfate ferric. The reducing agent sodium dithionite was used and the potential was varied (initial potential: 700, 600, 500, 450 e 400 mV) using as a reference the Pourbaix diagram for iron created by HydroMedusa software. The pH was ranged between 0.5 and 2.5, the reducing agent’s concentration was 0.5 M and the reaction time ranged between 30 and 120 min at room temperature. The ferric iron and total iron concentration were verified using a spectrophotometer with 5-sulfosalicylic acid (SSA) to determine Fe(III) and ammonia to determine Fe(II) and Fe(III) in 500 and 425 nm, respectively. The results indicated that total reduction was at 400 mV in any pH between 0.5 and 2, but less than 40% in pH 2.5 at this potential value.

Mar 1, 2017

By Ibrahim Yusufoglu, Cem Kahruman, Mert Zoraga

In this study, a strontium sulfate mineral (celestite) was converted to strontium oxalate in solutions containing ammonium oxalate as a reactant. The experiments were carried out under isothermal conditions. The effects of stirring speed, ammonium oxalate concentration, particle size and temperature on the conversion rate were investigated. During the conversion process, definite volumes of solutions were taken from the reactor after different reaction times for the determination of sulfate ions using ICPOES. Fractional conversions of strontium sulfate were determined at different times and fractional conversion vs time diagrams were generated. It was found that the conversion of strontium sulfate was increased by increasing the ammonium oxalate concentration and temperature in addition to decreasing the particle size. The effect of stirring speed was negligible on the reaction rate. It was observed that above 328 K, a protective layer of strontium oxalate was formed on the strontium sulfate particles. X-ray Powder Diffraction technique was used for characterization of solid substances.

Jan 1, 2014

By A. I. Okunev

The investigation results are submitted on separation into layers in the systems Cu (Ni) - Fe - Ca - 0 - S - (Si), as well as on physico-chemical properties of oxide - ferrite, oxide-sulfide melts (density, surface tention, viscosity, electric conductivity), on kinetics and oxidation macromechanism of iron and sulfur in the oxide-silicate, oxide-ferrite and oxide-sulfide melts, kinetics of reduction of oxide-silicate and oxide-ferrite systems. Conditions are discussed for copper, nickel and zinc recovery from oxide-silicate and oxide-ferrite slag in liquid and solid states. Some promising technique is the technique of future, as is considered.

Jan 1, 1988

By Q. Chen

The magnetic properties and phase evolution of Nd-lean and/or boron-rich melt- extracted ribbons of Nd98Fe90.2xBx, where x = 6 through 11, have been studied using XRD, DTA, TMA, and VSM. The off-stoichiometric Nd2Fe14B compositions cause additional phases to be present after crystallization and affect the magnetic properties obtained. The crystallization temperature of this alloy series rises with the increasing) boron content. In addition to Nd2Fe14B and a-Fe, Fe3B is detected. It is found that increasing the boron content reduces B, within this composition range. The magnetic properties are directly associated with the relative magnetic phase content in the samples.

Jan 1, 1997

By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By Hee Dong Jang, Hong Yong Sohn, Miguel Olivas-Martinez

"Tetramethylorthosilicate (TMOS), a precursor of silica nanoparticles, is prepared from the waste silicon sludge, followed by the synthesis of silica nanoparticles from the TMOS by flame spray pyrolysis. A two-dimensional multiphase computational fluid dynamics (CFD) model for the flame spray pyrolysis process (FSP) for the synthesis of silica nanoparticles has been developed. The model incorporates the governing turbulent equations of overall continuity, momentum, energy and species mass transport to represent the gas phase and the population balance model (PBM) to account for the silica nanoparticles. The model has been validated with experimental data in terms of gas temperature and average particle size. Introduction Silica (SiO2) nanoparticles are used in various industrial applications, such as catalyst, pigments, thin film substrates, electronic and thermal insulators, and humidity sensors [1]. They are also used as additives in plastics and rubbers to improve the mechanical properties of elastomers, and in liquid systems to improve their suspension behavior. These applications rely on the particle morphology, average particle size, particle size distribution, and phase composition [2]. Silica nanoparticles can be synthesized by wet chemical processes such as sol-gel methods and high-temperature processes such as flame spray pyrolysis (FSP). The FSP process provides a unique control of particle size and crystalline structure and it can also produce high-purity, thermally stable particles continuously with minimal further treatments. The sizes of the flame- made particles range from a few to several hundred nanometers, depending on the operating conditions [1]. The synthesis of silica nanoparticles from organic compounds that contain silicon by the FSP process is of interest because it generates no harmful by-products [1, 3]. Several compounds such as tetraethylorthosilicate (TEOS) and tetramethylorthosilicate (TMOS) can be used to synthesize silica nanoparticles, but most such compounds are expensive. Thus, it is desirable to prepare the precursor compounds from waste materials. In the present study, TEOS and TMOS synthesized from silicon sludge were used as precursors of silica nanoparticles [4]."

Jan 1, 2008

By Youn-Bae Kang

Evaporation mechanism of S from liquid Fe–C–S alloys at 1873 K was proposed by analyzing available experimental data. It has been known that increasing C content in liquid alloy increases activity coefficient of S ðfSÞ, and it could raise driving force for the evaporation reaction S = S(g). However, experimental data of the evaporation of S in the Fe–C–S alloys could not be accounted for only by considering the increases of fS. In the present study, formation of carbosulfides, CS(g) and CS2(g), was additionally taken into account in order to explain role of C for the accelerated S evaporation. Surface adsorption of S was also taken into account, which retards the evaporation rate of S. An evaporation model equation was formulated. It can be applied to calculate the evaporation rate of S over wider C content (from zero to its saturation to liquid alloy).

By Toshiyuki Nohira, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The electrochemical formation of Tb-Ni alloys was investigated in a molten LiCl–KCl–TbCl3 (0.50 mol% added) at 723 K. Open-circuit potentiometry was conducted using a Ni electrode after electrodepositing Tb metal at 0.20 V (vs. Li+/Li) for 300 s. There were four potential plateaus at (a) 0.66 V, (b) 0.80 V, (c) 0.95 V and (d) 1.56 V, respectively. Alloy samples were prepared by potentiostatic electrolysis at 0.60 and 0.70 V at 723 K. The alloy phase was identified as only TbNi2. Anodic dissolution of Tb from the formed TbNi2 was conducted at 0.90, 1.20 and 1.60 V, respectively. In the sample obtained at 0.90 V for 3 h, the existence of TbNi3 was identified by the XRD. Phase of the sample obtained at 1.20 V for 3 h was TbNi5. The sample obtained at 1.60 V for 3 h was Ni. Alloy samples were prepared by potentiostatic electrolysis at 0.50–0.80 V for 1 h using Ni plate cathodes in a molten LiCl–KCl containing TbCl3 (0.50 mol%) and NdCl3 (0.50 mol%). The highest mass ratio of Tb/Nd in the alloy sample was 56 at 0.70 V.

Mar 1, 2018

By Seong-Jong Kim

The formation behavior and corrosion characteristics of anodic oxide films on pure Mg and Mg-AI alloys were investigated focusing on the effects of anodizing potential, Al content, temperature and NaOH concentration. Pure Mg and Mg-AI alloys were anodized for 10 min at 3, 10, 40, and 80 V in NaOH solutions. Mg(OH)2 was generated by an active dissolution reaction at the surface of the specimen and the product was affected by temperature while MgO generation increased with NaOH concentration. Moreover, the current density after anodizing for 10 min at a constant potential decreased with increasing AI content in Mg-AI alloys,

Jan 1, 2003

By Osvaldo A. Bascur

Several new hydrometallurgical plants have been built in the past years. They have implemented new processes to treat new type of ores. New technologies have been used to improve metallurgical performance from the start. The cycle times between knowledge generation and innovation are often neglected in the traditional capital expenditures and building of these new process plants. The paper reviews several implementations in which they have started with new ways of using information management from the beginning. The implementation of a real time performance management infrastructure is reviewed to assist in the implementation of mine to product strategies, metallurgical mass balances, solvent extraction composition statistical process control, methods to minimize organic losses, reduce variable costs and to improve metal extraction. Several examples are provided to improve operations by simplifying the access and analysis of information from assets and metallurgical processes. Continuous improvement and innovations have been enabled to minimize start times and for faster troubleshooting and resolution of operational problems.

Jan 1, 2006

Microstructural investigation has shown that grain splitting or deformation banding ( DB ) develops progressively with increasing strains during cold rolling. Of particular significance to simulating texture development in cold rolled BCC polycrystals is the operation of higher order slip systems other than 110 and, the occurrence of DB in the rolling plane since the latter allows a new relaxation of the shears. Deformation banding ( DB ) model includes grain subdivision in the rolling plane and applies the Relaxed Constraints ( RC ) mechanism for the other shears. An energy criterion for deciding whether deformation banding occurs or not has been postulated, referred to as Deformation Banding Criterion ( DBC ). This paper reports the results of the investigations into the effects of different slip systems, i.e., those based on 110, 112 and 123 slip planes and their combinations using RC, DB and DBC models, in developing simulated BCC rolling textures.