By Xiaowen Liu

The DSC/TG, IR and XRD analysis were used to characterize the heating phase transformation of illite, which came from Ouhai deposit, China. It was discovered that the dehydration and de-hydroxylation of illite carried out stage by stage during heating. The adsorptive water and layer-inter water were dehydrated from room temperature to 500°C; and dehydroxylated in the range 500°C~800°C. In these stages of process, illite?s layer structure kept almost unchanged. After 800°Cillite began to change into disorder structure. At about 1100°C, the layer structure of illite had been destroyed, and amorphous SiO2 and mullite crystallite appeared. At about 1200°C the structure of illite completely destroyed and mullite crystal phase had become perfect..

Jan 1, 2006

By A. E. M. Warner

Inco Limited has long and extensive experience in converting nickel-copper primary smelting mattes over a broad range of nickel/copper weight ratios and combined nickel-copper-cobalt contents. At the Copper Cliff Smelter, the composition of the converter product matte has to meet the requirements of the matte separation process; at the Thompson Smelter, converter matte of a different composition is cast into anodes for nickel electrorefining; and in Soroako, Indonesia, a very low copper product matte is granulated for the Japanese market. Recently, Inco has conducted pilot plant testing of three possible nickel-copper matte continuous converting routes, namely flash converting, oxygen top blowing-nitrogen bottom stirring, and tuyere blowing. This test work has generated substantial new information on nickel-copper matte converting chemistry. This overview paper reviews the metallurgy of nickel-copper matte converting, in particular the behaviour of cobalt and the operating conditions required to meet the iron and sulfur specifications of the product matte. The relevant thermodynamic information is used to discuss the industrial data.

Jan 1, 2003

By T. H. Jeffers

The U.S. Bureau of Mines' Salt Lake City Research Center. has developed porous polymeric beads containing immobilized non-living biological materials for extracting metal contaminants? from wastewater&. Immobilized biological materials include peat moss, algae, biological polymers, and other materials that demonstrate high .affinities for heavy metals. The beads, designated as BIO-FIX beads, have distinct advantages over traditional methods of utilizing biological materials in that they have excellent handling characteristics . and can be used in conventional processing equipment or low-maintenance systems.. Toxic metals such as copper, cadmium, zinc, lead, and mercury are several of the many heavy metals effectively removed from mine wastewater& using B'IO"FIX beads. Continuous cyclic testing indicated that the beads continued to produce treated effluents which met National Drinking Water Standards (NDIJS) after 175 loading-elution cycles, Adsorbed metals were removed from the beads using dilute ?mineral .acids. In many cases" the extracted metals were further concentrated to enable processors to reclaim the metals, thus minimizing the generation of a hazardous sludge. Tests indicated that use of the beads in a low-maintenance system was particularly effective for treating remote acid mine drainage waters? and small toxic seeps from hardrock mining districts ..

Jan 1, 1991

By A. E. M. Warner

In co Limited has long and extensive experience in converting nickel-copper primary smelting mattes over a broad range of nickel/copper weight ratios and combined nickel-copper-cobalt contents. At the Copper Cliff Smelter, the composition of the converter product matte has to meet the requirements of the matte separation process; at the Thompson Smelter, converter matte of a different composition is cast into anodes for nickel electrorefining; and in Soroako, Indonesia, a very low copper product matte is granulated for the Japanese market. Recently, Inco has conducted pilot plant testing of three possible nickel-copper matte continuous converting routes, namely flash converting, oxygen top blowing-nitrogen bottom stirring, and tuyere blowing. This test work has generated substantial new information on nickel-copper matte converting chemistry. This overview paper reviews the metallurgy of nickel-copper matte converting, in particular the behaviour of cobalt and the operating conditions required to meet the iron and sulfur specifications of the product matte. The relevant thermodynamic information is used to discuss the industrial data.

Jan 1, 2003

By A. K. Kyllo, N. B. Gray, B. N. McCurry

"Dynamic control of the formation of a solidified layer between a pipe wall and a flowing melt enables the flow rate to be adjusted in real time. This solidified layer can be generated by using a coolant on the outside of the pipe wall to remove the required heat. The coolant, and hence the solidified layer, can be controlled remotely. The dynamic behaviour of the solidified layer was investigated by both physical experiments and mathematical modelling. The mathematical model has been developed using a finite difference technique to describe conduction through the pipe wall and solidified layer. Results from the model were consistent with previous steadystate experimental results using molten lead. Experiments are currently being carried out using molten tin in a recirculating circuit with a cooling system that is instrumented for accurate computer control to validate the model. The circuit is designed for flowrates of up to 24 kg/s (86 tph) of molten tin. Steady-state and dynamic predictions were made for the current rig.Industrial SignificanceThe current method of choice for tapping slags, metals and mattes from many metallurgical furnaces is using an oxygen lance to open the taphole and using a clay plug to close it. There are, however, some significant drawbacks in this method. The heat generated by the oxygen lance erodes the refractory lining of the taphole, as well as the clay plug, and the furnace products themselves corrode the taphole. Using an oxygen lance is also a significant safety hazard to the operators as they must work in close proximity to the furnace and be subjected to a shower of sparks while opening the taphole. Also, the flowrate of material through the taphole cannot be controlled online as the diameter of the opening cannot be varied easily. This feature means that the level of product in a furnace cannot be kept constant."

Jan 1, 1999

By Wenxian Zhu, Xuema Li, Patrick R. Taylor

"Experiments were performed in a non-transferred arc, thermal plasma flow reactor to investigate the synthesis of ultra fine boron nitride (BN) powder from the reaction system of boron oxide (Bz03), methane (CH4), ammonia (NH3) and hydrogen (H2). Argon (Ar) and nitrogen (N2) were used as plasma gases. The thermodynamics and kinetics of the synthesis reactions were examined and a chemical reaction mechanism was proposed. The powders produced under certain operating conditions had high purity and good conversions. All the products were extremely fine powders (< 30nm) and were uniform in size distribution. The powder products were analyzed by chemical and physical characterization. The effects of the reaction variables on the conversions from B203 to BN and the purity of the products were investigated.IntroductionIn the past few decades, boron nitride (BN) has attracted a great deal of interest because of its excellent thermal, chemical and electrical properties (1-4) It has a high thermal stability and thermal conductivity. Chemically, it is very stable and is not wetted by most molten metals and slag. It is also an excellent low loss insulator. Since hexagonal boron nitride (h-BN) is light in weight, strong and easily fabricated, it has applications in a variety of specialized high temperature areas, such as a high temperature lubricant, crucibles for molten metals, thermocouple protection tubes, break rings for horizontal continuous casting of steel, and friction reducing coatings. In cubic form, boron nitride is one of the hardest materials known, second only to diamond, and it is an excellent material for tools in which the use of carbon based materials is limited by oxidation or reaction with metals."

Jan 1, 1998

By Yuhsuke Mizukami

Crude high Cr containing steel such as tool steel, heat-resistant steel or stainless steel is produced by dissolution of high carbon ferro-chromium into molten crude steel. In the refining process, decarburization is performed at the first stage, and deoxidation is followed in the next stage. Therefore, the equilibrium relation between dissolved Cr and 0 in molten Fe-Cr alloy after decarburization is very important when yield of deoxidizer is considered for the ovemll control and optimization of the process. It is well known that the yield of deoxidizer does strongly depend on the kinds of refractories of furnace in the secondary refining process. In the present work, the equilibrium relation between dissolved Cr and O in molten Fe-Cr alloy has been measured in a Cr2O3, MgO or Al2O3 crucible at steelmaking temperature. O contents at given Fe-Cr components have been lower in order of Cr2O3, Al2O3 and MgO crucible. The present results have been discussed based on the activities of the constituents in pure solid Cr2O3, and FeO-Cr2O3, MgO Cr2O3 and (AI,Cr)2O3 solid solutions.

Jan 1, 2003

By D. R. Parker

"This paper canvasses emerging trends in public policy and law, which may influence the zinc industry's interest in recycling. There are forces at work beyond direct economic benefits that will drive recycling of zinc, including:• corporate determination to pursue sustainable practices and product stewardship.• public perceptions and pressure,• customer and investor demand,• workforce recruitment, and• protection and expansion of marketsIn this paper, these ""indirect"" forces are examined with particular focus on the zinc industry: It is concluded that, in today's world with an emerging precautionary approach to policy and law making, public perception concerning the environmental implications of metal products, and the need to conserve resources for future generation, a strong industry response is required."

Jan 1, 2000

By Liping Gu, Gordon A. Irons

"A 1/3 scale ""thin-slice"" model of an electric arc furnace was developed so that gas could be injected to simulate foaming gas evolution. The influence of arc jets, oxygen lancing and bottom bubbling was also simulated. Liquid velocities were measured by a white light particle image velocimetry system. Numerical simulations of some of these effects were made using commercial CFD packages. Comparisons with measured results show that considerable care is required to select the appropriate model and to interpret the computational results.INTRODUCTIONDuring recent years electric arc furnaces (EAF) have captured a significant share of steel production, partially due to increased productivity through the introduction of advanced technology such as oxygen injection, slag foaming and long-arc operation, process automation and post-combustion. However, systematic analysis of the process and these effects on heat transfer and fluid flow in the furnace is still in its infancy. Most investigationsl1 6l have been restricted to a specific application such as oxygen lancing or bottom stirring. In addition, it is very difficult to make comparisons between these computed results and experimental/industrial results. In this work a 1/3-scale ""thin-slice"" model of Dofasco's 190 ton EAF was built. The fluid flow in the bath due to the arc jets, bottom stirring, oxygen lancing and CO evolution was simulated. The velocity distributions in the bath were measured using Particle Image Velocimetry (PIV) System. In addition, numerical simulations of bottom stirring and CO evolution were carried out using two commercial CFD packages (Fluent and Phoenics). The objective of this work is to validate the mathematical models so that they can be applied to the full-scale furnaces."

Jan 1, 1999

By Tianzu Yang, Weifeng Liu, Shu Bin, Lin Chen, Wanda Bin

"Vanyukov Process has been mainly applied for processing copper and nickel sulfide ore for more than 30 years. Based on the understanding of the Vanyukov Process, researchers from China introduced the technology into the areas of lead, antimony and bismuth extraction by changing the furnace structure and technical flow, which greatly extended the application area and raised the processing efficiency, thus developed the oxygen-rich side-blow bath smelting (OSBS) technology in 2000. This contribution reviews the history of OSBS technology from four respects: the quantity, the furnace structure, the process flow and the application area. Its potential research direction and industrial application are also summarized.IntroductionVanyukov bath smelting furnace and related bath smelting technology were developed by researchers from Soviet Union who devoted comprehensive research on fundamental theory as well as engineering technology [1,5]. Vanyukov process has been applied for large industrial production since the 1970s and it is still one of the major methods in modem pyrometallurgy process. The appearance ofVanyukov double district furnace and joint double furnace in the past ten years, which are applied for copper smelting, is the most valuable advances of the Vanyukov process [7,8,9]. However, the application ofVanyukov process was limited in copper and nickel sulfide ore smelting, and few countries adopted this process except Soviet Union."

Jan 1, 2013

By Min Chen

A numerical simulation of the stress field of the solidified shell in the mold during continuous casting of peritectic steel slab was calculated with commercial software. The results showed that the maximal stress on wide face of the solidified shell was located at the corner and near middle of the slab, and it increased with increasing the width of slab. In addition, the stress was also influenced by operating parameters such as superheat degree, drawing speed and cooling intensity of the mold, and the maximal stress value and its position changed with these parameters. For the slab with section size of 3200mm×150mm, the proper drawing speed was around 1.2m/min, with cooling intensity of 5500L/min while the superheat degree was 15°C to 25°C in order to prevent longitudinal crack occurring during peritectic steel continuous casting.

Jan 1, 2009

By Hongxu Li, Pu Liu, Hao Bai, Daqiang Cang, Lihua Zhao

"Coal, as the main energy in ferrous metallurgy, is consumed on a large scale and great amount of CO2 is emitted likewise. In this paper, a model, based on carbon balance, was developed for CO2 emission analysis, with data obtained from a typical integrated steelworks in China. The result shows that, CO2 emissions increase almost constantly with the growth of steel production. However, coals of different classes and product variety in the steelworks exerted an influence on CO2 emissions. Furthermore, three scenarios, including natural gas instead of coal for power generation, EAF process partly replacing integrated steelmaking, and feasible techniques applied to achieve lowest process energy consumption (FLPEC), were assumed to seek possible ways of carbon emission reduction. The result proves that the second scenario is most effective. If 40% of the steel product could be from EAF process, CO2 emissions would be reduced by 45.07%.IntroductionGlobal warming has become a global environmental problem, which is generally caused by excessive emission of greenhouse gases, such as CO2, generated from human activities and industrial processes. It is estimated that about 7% of global CO2 emissions was from iron and steel industry. Further, if the ore and coal’s mining and transportation are included, the CO2 emissions would reach 10%[1]. In general, the relationship between energy saving and CO2 emission reduction is positive correlation. However, in iron and steel enterprises, due to different types of energy resources like coal, heavy oil, natural gas, the consumption of which will generate different amount of CO2, are used, different energy consumption structure in iron and steel enterprises will lead to difference of CO2 emissions.In order to assess the CO2 emission reduction potential of China’s steel industry, Ke Wang etc.[2] developed a model using LEAP software to generate 3 different CO2 emission scenarios for the industry from 2000 to 2030. LEAP is a scenario-based software tool for integrated energy-environment and greenhouse gas mitigation analysis. The amount of CO2 emissions was obtained by the following equation:"

Jan 1, 2011

By Gabriel Riveros, Ariel Balocchi, Andrzej Warczok, Daniel Smith

Blister copper from converting of copper matte is processed by fire refining prior to electrorefining. The fire refining consists of two steps: copper oxidation with impurities slagging and copper reduction. The classical batch process is carried out in vascular or reverberatory furnaces called anode furnaces. A new process for continuous copper fire refining has been proposed. The copper flows through two reactors in cascade, where is oxidized and reduced. The flow of a liquid copper through a ceramic packed bed increases the surface area and the rate of oxidation as well as the rate of reduction in the packed bed of charcoal. Mathematical modelling allowed for the design of a laboratory scale demonstration installation and industrial-pilot installation in Hernan Videla Lira Smelter (Paipote). The results have demonstrated the process feasibility and flexibility in operation.

Jan 1, 2009

Equilibrium calculational software programs can be effectively utilized to illustrate the importance of activity or concentration, solubility, temperature, solution pH, solution potential, and ligand complexation to students studying hydrometallurgy. The calculational program STABCAL will be demonstrated. illustrative examples for the creation of diagrams such as EH-pH, activity or concentration-pH and activity or concentration-EH will be presented to demonstrate the fundamentals of real hydrometallurgical systems. Speciation, titration and mixing will be used to simulate or predict operational processes. Applications will include treatment of Acid Mine Drainage (Berkeley Pitlake water and sediments), mass balance potential/pH diagrams, leaching and selective separation of metals from electroplating sludge, metal adsorption at femhydrite surfaces, and flowsheet development for treating mercury sulfide K106 sludge.

Jan 1, 2002

By Jose R. Parga

In mining operations, cyanidation is the ,predominant method by which gold and silver are recovered from their ores and it is recognized that cyanide consumption can be a major factor that contributes to the operating costs for such operations. Also after extraction and recovery of precious metals a certain amount of cyanide is delivered to the tailings pond and must be considered with respect is environmental problems due to the toxicity of cyanides. In this regard, the Air-Sparged Hydrocyclone (ASH) has been used as a reactor for the treatment of cyanide solutions in two ways; first for cyanide recovery by acidulation using the Mexican modification of the Mills-Crowe process and second for cyanide destruction by oxidation with the use of chlorine dioxide (ClO2). In both cases, excellent performance can be achieved using the high capacity ASH system.

Jan 1, 1998

By S. K. Varma, Miriam Regalado, Daniel Salas, Erica Corral, Erika Esquivel

"Age hardenable 2014 aluminum alloys and composites containing 0.10 and 0.15 volume fractions of alumina particles (VFAP) have been solutionized at 540 and 550°C for up to 20 hours. The solutionized samples, heat treated for 5 and 20 hours, have been subjected to room temperature rolling until cracking develops. The work hardening curves have been compared to determine the effect of solutionizing time on the rolling characteristics from both hardness and the microstructural evolution points of view. Solutionizing at two different temperatures results in differences in the extent to which the composites can be rolled until fracture. The microstructural characterization by TEM has been performed to understand the room temperature rolling behavior.IntroductionThe effect of solutionizing on the age hardening response of 6061 and 2014 aluminum alloys and composites reinforced with 0.10, 0.15 and 0.20 volume fractions of alumina particles (VFAP) have been reported in the literature [1-4]. A comparison of the monolith and composites indicates that particles promote the aging process through differences in the microstructures in solutionized condition. The first effect of solutionizing is to produce a grain growth process which follows a grain growth law (square of grain diameter as a function of solutionizing time). It appears that it is possible for vacancies to be emitted during grain growth period as they try to minimize the total grain boundary surface area by increasing their diameter. This may be common to both the monolith and the composites. However, the second effect must be exclusively considered for the composites. The particles generate dislocations during the solutionizing process due to the differences in the values of the coefficient of thermal expansion (CTE) between the particles and aluminum base metal. It has been determined [1] that the dislocation density increases with increase in solutionizing time in the composites of 6061 aluminum alloys reinforced with 0.10, 0.15 and 0.20 VFAP. The improved bonding between particles and matrix can give rise to additional generation of dislocations due to curvature effects [1] with the result that the dislocation density continues to increase with increase in solutionizing time even after the CTE effect is considered to have been stabilized."

Jan 1, 1998

By den Bulck A. Van

In Europe, 50% of the copper originates from recycling. High-Cu containing scraps are regularly rich in impurities like Fe, Ni, Sn and Pb. Many high-Cu containing scraps are fed directly into anode-furnace casting installations or furnaces with limited refining capability. The impurities levels of the anodes produced in these processes should however remain acceptable for further electro-refining. The distribution of Sn between copper and slag has been investigated for conditions relevant to copper converting. Unlike previous studies, this work focuses on the behavior of Sn relevant to fire refining conditions, which are essential for anode refineries.In this study, liquid Cu–1Sn and CuOx–FeOy–SiO2 slag, with CaO additions, were equilibrated at 1300 °C in vacuum sealed SiO2 ampoules. After metal–slag equilibration, the samples were quenched in water. The composition of the slag and Cu metal was investigated with Electron Probe X-ray Microanalysis. The distribution coefficients of Sn between slag and Cu metal were determined as a function of slag composition.

By Huang Kai

Uniform needle-like and spherical nickel oxalate particles were prepared by the chelating precipitation process, which was based on the reaction of oxalate acid and the solution of ammonia nickel chloride. The molar ratio of ammonia to nickel ion in the mixed solution is essential to determine whether the spherical or needle-like particles are formed, which means actually the concentration of ammonia is the key to determine the growth mechanism. When oxalate acid is added in the form of solid, it may act as the nucleation interface for the eariy-precipitated substance and so induce the formation of spherical particles. The PVP agent can improve the dispersing degree of the needle-like particles and higher reacting temperature leads to larger particles. The composition of the needle-like particle consists of ammonium and nickel oxalate instead of the pure nickel oxalate.

Jan 1, 2003

By Corby G. Anderson

Hydrometallurgical technology for the pretreatment of refractory gold concentrates has been developed at Sunshine Mining and Refining Company. It employs a patented nitrous-sulfuric acid pressure leaching process which&apos; was proven industrially at the Sunshine refinery. Additionally, pretreatment for removal of antimony and some other impurities is done with alkaline sulfide leaching. This paper will discuss the successful application of these two technologies for pretreatment of a refractory gold concentrate prior to CIL gold recovery. A complex gold concentrate composed of pyrite, arsenopyrite and stibnite was tested. Results of antimony leaching in alkaline sulfide media will be discussed including some details of a novel and selective recovery method for gold leached by polysulfide or thiosulfate" Also, the factors important in and the results of the application of nitrogen species catalyzed pressure leaching to refractory gold concentrates will be detailed.

Jan 1, 1996

By C. Lupi

"The energy consumption of copper production by electrowinning, generally represents more than 1/4 of the total energy requirement in hydrometallurgical traditional process (roasting, leaching, purification and electrowinning). The considerable saving can be achieved just in this step that requires about 2.2 kWhlkg of the produced copper. To save energy the cell voltage, or more appropriately its anodic component, can be reduced: that is because the anodic voltage represents the main component of cell voltage and so it is largely responsible for the excessive energy consumption in copper sulphate electrowinning.In this work some ways are studied to lower the anodic voltage. First the cobalt ions were added to the sulphate solution in order to study the catalytic effect on oxygen discharge. Then lead alloys anodes (Pb-Ag, Pb-Sb-Ag and Pb-Ca) were used to promote a better oxygen evolution as a result of a different anodic surface. Their behaviour was compared with the PbSb traditional ones. Finally, as already pointed out by several authors for zinc electrowinning, ethylene glycol was employed as anodic depolariser in order to verify its effectiveness in the case of copper electrowinning. By combining all the above-mentioned ways, energy saving ranging from 20% to 27% is achieved.All the tests were carried out on a laboratory pilot-plant for long time to simulate the industrial conditions. The obtained copper deposits were observed by SEM to highlight their morphology."

Jan 1, 1997