By Seiji Yokoyama

As a series of fundamental study on the gas evaporation method, a levitation-melted aluminum was evaporated in the gas mixture of argon and ammonia to synthesize ultrafine particles of aluminum nitride. When the ammonia partial pressure were more than 2kPa, the formation ratio of aluminum nitride was about 95%. The particles of aluminum nitride were mainly hexagonal. The mean size of the particles of aluminum nitride was about 57 nm, and it was constant without depending on the temperature of the levitated aluminum and the partial pressure pf ammonia. The aluminum nitride was formed by the reaction between ammonia and condensed liquid aluminum particle whose size was relatively small.

Jan 1, 2006

By J. Ipinza

The slime formation with several metallic impurities from acidic electrolytes of copper has been studied. On fresh Pb-Ca-Sn anode surface firstly the formation of PbSO4 takes place, then, it is transformed in the conducting PbO2, which covers the anode surface. It has been experimentally established the formation of a manganese dioxide double layer at the anode; this double layer was always composed of a thick external layer of non-adhering and easily removable scales, and of a thin internal layer, which adheres relatively well to the surface of the electrode. It was found that manganese dioxides present in the slime were of different nature: a non-adhering layer produced by electrolysis (-MnO2) on the PbO2 surface and a pure chemical precipitation in the solution (-MnO2). When iron is present in the electrolyte on this last layer of manganese, lead sulfate was found. In the case of arsenic and antimony in the electrolyte the slime generated was found to be lead sulfate and amorphous compounds of those ions. The lower slime generation in Chilean EW plants could be due to the lower contents of iron and manganese in the electrolytes. It was found that this slime formation rate not only is due to the electrolyte composition but also to the poor control of operational parameters at EW plants.

Jan 1, 2003

By J. D. Zhu, T. Ohmichi, H. Yasuda, S. Kashiwai, I. Ohnaka

"Since the casting process affects the properties of castings, its computer simulation has been greatly developed in the last decades. This paper presents our recent works, especially on mold filling simulation, because most casting defects such as porosities and inclusions that greatly affect the properties originate during mold filling. The first topic is the mold filling simulation with consideration of cavity pressure change during mold filling, including direct observation of flow phenomena with X-ray and pressure measurement. The second .one is the mold filling simulation in the lost foam process, in which gasification of polystyrene pattern and gas outflow through the coating and mold have been considered. The simulation can predict not only the mold filling sequences but also periodical vibration of the gas layer between the melt and pattern. The third one is the comparison of simulation of Al melt flow in a metallic runner and direct observation through a transparent mold, showing that the entrapped gas or inclusions is expelled ahead through the melt and its simulation needs very fine meshes. These examples show that the comparison of simulation and observation is very important to develop the numerical simulation further.IntroductionThe mechanical properties of castings are greatly affected by casting defects such as porosities and inclusions, and solidification structure. Although recently the structure simulation has greatly progressed [1-4 ], the application in plants is very limited, because the structure is mostly determined by chemical compositions and cooling rate, enabling us to estimate it from the structure of past similar castings without simulation.On the other hand, the casting defects often vary with each casting or time. Among the defects, porosities and inclusions are main causes to deteriorate the properties and mostly originate during mold filling. Therefore, a lot of efforts to simulate the mold filling and estimate those defects have been made in the last decades [l,5,6]. These efforts have been mostly to develop numerical techniques to solve the Navier-Stokes equation. However, the flow phenomena in molds have not been well understood, because the direct observation of the flow phenomena in mold is not easy. This means the accuracy of the simulation is still not clear."

Jan 1, 2000

By Yuanyuan Zhang, Patrick J. Masset

"The reduction of FexO in slag is one of the fundamental reactions in iron and steelmaking technology, including the blast furnace process (BF). Experiments on the reduction reaction of iron oxide using CaO-SiO2-Al2O3-FexO-C mixtures were carried out using thermogravimetric analysis (TGA) under reducing conditions at temperatures up to 1100°C. The composition of the primary slag was chosen so that the FexO concentration varied between 0 and 75 wt % and the CaO/SiO2 ratio being kept constant to 0.90. From the TGA curves recorded isothermally at different temperatures the kinetic parameters of the iron oxide reduction were determined.IntroductionIn blast furnace the iron ores and coke are charged in layers from the top. The reduction of iron oxide by coke is one of the fundamental reactions in the blast furnace process. Although a great amount of work has been done on the topic of reduction of composites [1, 2, 3], gasification of carbon [4, 5] and reduction of iron oxides by CO [4, 5, 6], the mechanism of reduction in iron oxide - carbon powder mixtures is not fully understood. Fruehan [1] and Rao [2] studied the reaction rate of the reduction of iron oxide by different types of carbon and concluded that the reaction mechanism is controlled by the oxidation of carbon at temperatures up to 1200°C. Rao [2] studied the reaction of hematite with graphite as carbon source up to 1080°C. An activation energy close to 300 kJ/mol was calculated within the temperature range of 950°C to 1087°C. In his study, Fruehan [1] determined the rate of reduction of Fe2O3 and FeO by coal, coke and coconut charcoal as carbon sources within the 900°C to 1200°C temperature range. He found that the reduction of Fe2O3 by carbon occurs in two stages and that the reduction of Fe2O3 to FeO is faster than that of FeO to Fe. This is due to the fact that the CO2/CO equilibrium ratio is higher, and hence, the rate of oxidation of carbon is faster. Fortini and Fruehan [3] have studied the reduction reaction of wustite by graphite and wood charcoal. They found that the wustite reduction can have a significant effect on the overall rate of reduction in composites at high temperatures or in the presence of a large excess of carbon. The calculated activation energy of the reduction reaction by wood charcoal was close to 368 kJ/mol, while the activation energy of the reduction reaction by graphite was 444 kJ/mol."

Jan 1, 2011

By Vladimir Lobanov, Vladimir Skorohodov, Andrew Evdokimov, Ural State Technical University 19, Boris Radionov

"The bulk of raw materials in metallurgy of secondary platinum metals are the wastes such as multilayered ceramic-metal systems, e.g. the spent catalysts of the chemical and petrochemical industry, automobile catalysts, etc. Due high chemical resistance of a ceramic basis the extraction of platinum metals by leaching even at very fine crushing is poor. The study of sorption leaching of platinum and a palladium from the spent automobile catalysts are carried out. The average content of PGM is 0.5%. A few methods of raw materials sampling were compared: 1) direct hydrometallurgical leaching of platinum metals from the fine-grained catalyst and atomic absorption analysis of the obtained solutions; 2) fusion to a metal or sulphidic collector of precious metals with the alloy analysis by direct spectrometry; 3) fusion with dissolution of a precious metals collector and atomic absorption analysis of PGM in solutions. Leaching allows detecting out no more than 90% of a palladium and 80% of platinum. Fusion to a collector gives the best results at the chemical ending. Researches on sorption leaching are executed. Under optimum conditions the extraction of platinum metals to concentrates is comparable with similar indicators of collector fusion.The large part of raw materials in metallurgy of secondary platinum metals are the multilayered or tridimensional ceramic-metal systems, in particular the spent catalysts of the chemical and petrochemical industry, automobile catalysts, ceramic-metal condensers, etc. The content of the sum of PGMs can be from hundreds grams per ton to several percent. For processing of such materials the hydrometallurgical methods of platinum metals leaching by various reagents are used commonly. High chemical resistance of the ceramic basis covering the metal particles causes low recovery even at very fine grinding. Other fundamentally different method of catalysts opening includes dissolution of the ceramic basis in the solutions of hydrofluoric acid and the subsequent recovery of platinum metals from insoluble residue. Application of this method is associated to use of corrosive medias and appropriate equipment. Fusion of the specified materials with collecting of PGM by copper, nickel or lead at the specialized enterprises provides higher extraction in semiproduct. At the same time, complexity and duration of the subsequent extraction of platinum metals concentrates causes high total cost per unit. Thereby this method is economically acceptable only for rather poor raw materials (no more than 0,1%). Undoubtedly, that the raw materials with the high content of PGM are reasonable to process by individual technology. In the present work the processing of some kinds of ceramic-metal raw materials, particularly automobile catalysts (neutralizers) with various collectors at the conditions of a target fusion are investigated."

Jan 1, 2008

By Volker Uhlenwinkel

The design of a free fall atomizer as well as the process parameters affect the particle mass flux distribution in the spray cone. The mass flux distribution is important in spray forming because of its influence on the deposit shape and enthalpy input into the deposit. In this article the effect of different process parameters on the mass flux distribution is shown. Furthermore, different melts were atomized with the same atomizer. An empirical correlation will be introduced to predict the mass flux in the spray cone. This correlation will be compared with experimental results.

Jan 1, 1999

By Sheng-hai Yang

The ultrafine, monodispersed, spherical cobalt powder has been fabricated by reducing cobalt hydroxide with glycol. It were investigated that the effect of NaOH concentration on the reaction rate and the effects of the concentration of cobalt hydroxide and surfactant on the morphology and particle size. The particles were characterized by the X-ray diffraction(XRD), scanning electron microscope(SEM), laser diffraction particle size analyzer and BET specific surface analyzer respectively. The XRD shows that the cobalt powders exist mostly in face centered cubic (fcc) structure, a little in simple hexagonal. The cobalt powders prepared at Co(OH)2150g/L, NaOH 40 g/L and surfactant 30g/L, its average particle size, specific surface area and cobalt content, were 0.88µm, 2.705m2/g. and more than 99.5% respectively.

Jan 1, 2006

By U. Lauwers

The influence of different waste materials in sinter blends on the quality and mineralogical composition of a sinter is described. As a result of partial preservation of the original textures of waste materials in the final product the degree of assimilation of the original material in the sinter product can be ascertained. Recycling of waste materials such as dolo char , arc-furnace slag, scrap fmes, mill scale and BOF-mud via the sintering process a saving on costs of raw materials such as flux and fuels, and a reduction on pollution can be achieved. A comparison of a typical sinter with a sinter produced through the utilization of waste materials showed a distinct correlation between certain types of waste material and some metallurgical properties. Dolochar in a sinter blend acts as part of the fuel and flux that are normally added to a sinter mix. Generally dolochar improves the quality of the sinter and decreases the consumption of coke. Other waste materials adversely influence the quality of the sinter. The glass and calcium ferrite content of a sinter when dolochar is used in the blend is similar to that of a sinter produced with only coke as a fuel in the sinter mix. The glass content is lower and the calcium ferrite content is higher, in a sinter produced from dolo char in the blend compared to a sinter produced with additions of other waste materials. Changes in the mineralogical composition are related directly to the metallurgical properties of the sinter product.

Jan 1, 1991

By Oleg B. Girin, Yuliya O. Proshenko

"Several approaches to electrolytic synthesis of new types of composite coatings with improved properties were devised using the authors' findings on development of texture, substructure and structural state in metal electrocrystallization. Addressed are texturally composite coatings having improved resistance to wear and corrosion; substructurally composite coatings having improved hardness and corrosion resistance; phase-change constitutionally composite coatings having improved corrosion resistance, reflectance, hardness and resistance to wear; structure-change constitutionally composite coatings having improved electric and magnetic properties; restricted-substructure composite coatings having improved resistance to abrasive-impact wear; and modified-substructure composite coatings having improved strength and plasticity.IntroductionIn recent years, some trends in the formation behavior of crystal texture, crystal substructure and structural state of electroplates were revealed and effects of texture, substructure and structural type on electroplate properties were discovered (1-3). Our interest was in using these findings and effects to develop some ways of synthesizing new types of composite electrolyte coatings having enhanced properties."

Jan 1, 1998

By Banqiu Wu, Ramana G. Reddy, Robin D. Rogers

Experimental studies on aluminum recycling via electrolysis in ionic liquids were carried out at the temperature of 105°C. Impure aluminum was dissolved at the anode and pure aluminum was deposited on a copper cathode. The products were characterized using an optical microscope, micro-image analyzer, X-ray diffraction, emission spectrometer, and atomic absorption analyzer. The electrorefining process with a current density of 310 - 730 AJm2, and current efficiency of about 99% was obtained. Impurities such as Si, Cu, Zn, Fe, Mg, Cr, Ni, Mn and Pb were removed as anode residue. Impure aluminum was purified from 79.8wt% to 99.9wt%. At a cell voltage of 1 volt, the energy consumption of about 3 kWh/kg-Al was obtained. The process has advantages of low energy consumption and low pollutant emissions, compared with the current industrial refining process.

Jan 1, 2000

By Keizo Uematsu, Satoshi Tanaka, Nozomu Uchida, Ronne Hendrajaya

"The influence of microstructural defects on strength in Si3N4 is reviewed. The presence of cracks, pores and inclusions greatly affects the strength of Si3N4. The micron order crack size and distribution were quantified by micrographic technique. The observed defect size was range from 4 µm to 28 µm.The density of defect increases as the defect size decreases. The correlation between defects size and density was better represented on the logarithmic graph. The correlation was linier. IntroductionFracture in ceramics materials occurs from. In order to understand the relationship between strength and defects, it is necessary to examine the fracture process quantitatively.1In this study, the micrographic technique is used to determine the defects size and distribution in Si3N4. The observed data will be used to predict the material strength by using fracture mechanics rnodel.2Experimental ProcedureThe sintered Si3N4 specimens ( SNl, Japan Fine Ceramics Center) were sliced into 1mm thick . The both sides of specimen surface were polished into by using diamond slurries with particle size down to 2µm. The final thickness was 0.045 mm. The optical microscope (NIKON OPTIPHOT02-POL) was used to observed the internal defects with transmission mode. The reflection mode was used to determine the surface defects, so that the internal defect could be distinguished from surface defect. The measurement and counting was taken on the micrograph and the longest part of the defect was measured as the defect size. The size density distribution of internal defect is taken."

Jan 1, 2000

By Veronica Escobar

This paper presents results from a two month pilot evaluation of EMEW® technology at CODELCO Radomiro Tomic, in Chile. A prime focus in the test programme was to assess the technology?s capabilities to recover high quality copper from the Radomiro Tomic electrowinning tank house bleed stream. The EMEW® cell developed by Electrometals Technologies Ltd. tolerates substantially higher levels of contaminants than those found in conventional tankhouse, operating at high current densities while maintaining high cathode copper quality all the way down to low copper concentrations. To maintain high copper purity in a copper electrowinning (or electro-refining) tank house, a continuous bleed of solution must be taken from the tank house inventory to prevent build-up of contaminants, and resulting degradation in cathode quality. In an SX-EW operation, this bleed stream is normally recycled back to the solvent extraction circuit, but is occasionally sent to the raffinate pond to re-enter the leach circuit. Return of the bleed stream to the solvent extraction circuit creates a continually recycling load of copper in solution, which may reduce overall plant capacity and expansion potential. Return to the leach circuit has a similar effect, and methods to reduce its impact are always under consideration. The use of the EMEW® technology allows for direct and efficient recovery of near 100% of the contained copper instead of recycling. Tests were run at ambient temperature on bleed electrolyte using current densities which varied between 250 and 1100 amps per square meter, with copper concentrations between 38 and 1 g/l. A profile of maximum allowable current density with respect to concentration was developed, showing that high grade copper can be obtained at all levels of concentrations tested, by choosing an appropriate current density and electrolyte flow rate. The results of this programme show that the recirculating bleed electrolyte from an SX-EW operation can be converted into an expansion in copper production at a comparatively low investment cost.

Jan 1, 2003

By Albert W. Spitz

Profitably recovering copper and precious metals from copper bearing scrap is a demanding and frustrating combination of art, science and economics. With fluctuating markets, varying raw materials and increasingly stringent environmental regulations requiring process revisions, practically everything is changing. The volatile copper market constantly shifts the percentage of copper in the scrap that can be economically processed. Scrap that has value one day may incur a disposal cost the following day. Also with less copper in the scrap, more residuals, slag, fume, etc. are generated which frequently present disposal problems and infrequently generate income. The ever increasing amounts of electronic scrap add value to the copper produced by virtue of the precious metals present. Printed circuit board materials create more slag and organic off gases which must be treated. Finally, the emphasis on reducing emissions of organics and other metals, especially lead, is a continuing challenge. Stack gases, fugitive emissions and ambient air quality all demand constant surveillance.

Jan 1, 1997

By M. Suzuki, M. Dobashi, M. Kahata, T. Yoshida

Almost 30% of steel in Japan is produced by electric arc furnace (EAF) treatment of iron scrap. EAF dust includes approximately 20 wt % of Zn and 3- 5 wt % of CI and is treated by the pyrometallurgical processes to recover Zn as Zn oxide. Direct hydrometallurgical processing is one of the most effective methods to recover high purity Zn. In this case, CI in the EAF dust is dissolved in the liquid phase by leaching, and the CI anion in electrolyte attacks anodes which are commonly made of a lead base alloy. Several processes have been proposed to remove CI anions from acidic sulfate solution. In this study, an electrolytic process was examined to eliminate CI anions from Zn sulfate electrolyte. From our study it can be said that the elimination rate of CI anion depends on the anode material ( i.e., the elimination rate is Pb-Ag alloy == Pb > DSE== Pt). In industrial Zn electrowinning process, the electrolyte contains Mn, which means the influence of Mn should be considered in the elimination of Cl. Mn dioxide deposition on an anode plate reduces the efficiency of CI removal. A periodical reverse current electrolytic system was examined to prevent this efficiency decrease, and deposited Mn dioxide could be removed very rapidly when the current is reversed. More than 95% of CI anion could be removed by this method in a shorter period than direct current method.

Jan 1, 1997

By A. K. Kyllo

A study has been carried out on the dusts from Hudson Bay Mining and Smelting's Flin Flon copper smelter. The aim of the work was to determine the mechanisms of dust formation and the deportment of the various constituents. The work concentrated on the copper converters, but the electrostatic precipitators and baghouse also clean the reverberatory furnace off gas, so some mixing will have occurred. The dust composition was found to vary with distance from the furnace, and to be made up of three major components: solidified droplets, unreacted flux, and condensed particles. The solidified droplets were formed from material ejected from the converter during blowing, while the flux was blown out of the converters immediately after charging. The condensed particles contained the majority of the lead and zinc, as well as the volatile impurities. There was also a significant soluble content of the dusts, increasing with distance from the furnace. The condensed material may be separated from the remainder by a simple washing and sizing technique.

Jan 1, 1996

By Fangqing Yin, Qingyu Deng, Zhengfeng Qu, Mengjun Hu, Meilong Hu

Titanium bearing blast furnace slag, which contains 20%-30% TiO2, is a valuable secondary titanium resource. Based on the thermodynamics calculation effect of the temperature on the reduction of the slag in vacuum were studied at certain vacuum degrees. The results show that magnesium vapor and silicon monoxide vapor can be obtained at the condition of high temperature and low pressure. The purity of TiC increases with temperature increasing. When the temperature arrives at 1623K TiC can be obtained besides the reductant carbon. XRD result of the powder collected from the furnace cover show that magnesium and silicon in the titanium bearing BF slag leave the slag system during carbothermal reduction in vacuum. From the above it can be concluded that TiC can be obtained from the titanium bearing BF slag and silicon and titanium in the slag can be separated by carbothermal reduction in vacuum and acid leaching.

Jan 1, 2016

By E. Burgos Cruz

The behaviour of S, N and P during refining of Fe-18 wt%Cr-10 wt%Ni with calcium carbide was investigated. The effects of the initial contents of C and N in the metal phase, as well as the supply method of calcium carbide to the melt on the removal degrees of S and P were evaluated. Heats were carried out at 1873K, in MgO crucibles, using a laboratory induction furnace. It was observed that simultaneously with S and P, N and O have also participated in the reactions. It seems that, in fact, O governs the behaviour of the other elements dissolved in the melt and that N is had to the removal of P with calcium carbide. It was also noticed that high C content in the metal phase have not altered the dephosphorization and desuffirization degrees, but that the supply of calcium carbide done by injection led to a lower dephosphorization degree than the one obtained by dumping it.

Jan 1, 1995

By W. G. Davenport

Smelting oxidizes Cu-Fe-S concentrate to matte. Converting oxidizes this matte to metallic copper. Smelting and converting are, therefore, part of the same oxidation process. It would seem natural, then, that smelting and converting should be combined to produce metallic copper in one step. This would: (a) maximize S02 capture by restricting S02 emission to a single, continuous source (b) minimize industrial oxygen and fuel requirements (c) minimize cost. This chapter discusses one step, direct-to-copper flash smelting as it is practiced in 2000. It then uses. the matrices of this book to determine: (a) the industrial oxygen and oil requirements of direct-to copper flash smelting (b) the distribution of Cu between metal and slag during direct-to-copper flash smelting. It concludes that direct-to-copper flash smelting: (a) captures?S02 efficiently from its single continuous stream of SO2 off gas (b) minimizes oxygen/oil consumption but: (c) sends -114 of its Cu-in-feed to slag.

Jan 1, 2001

By Yuanbo Zhang, Zhixiong You, Li Qin, Guanghui Li, Tao Jiang

Low-grade manganese oxide ore is generally characterized by high iron content. In this work, sulfidation roasting of an iron-rich manganese oxide ore with elemental sulfur was characterized. The experimental results indicated that manganese dioxide can be selectively reduced over iron oxide by using elemental sulfur. The manganese phases in roasted product included low-valence manganese oxide, manganese sulfide and manganese sulfate, while those of iron mainly depended on the sulfur addition. Iron oxide would only be reduced or sulfidized at larger sulfur additions. The effect of roasting temperature and S/Mn mole ratio on the phase transformations was also investigated; extractions of Mn/Fe by sulfuric acid were evaluated. An extraction of Mn greater than 95% was obtained while that of Fe was controlled less than 10% under the optimal conditions.

Jan 1, 2016

By Mitsuhiro Ohtaki, Tetsuzo Arakawa, Fujio Murata

Refining of Zn from aluminum scrap melt by some vacuum distillation processes was studied to promote aluminum scrap recycling. Effects of distillation conditions, such as melt temperature, vacuum pressure and holding time, on Zn distillation behavior were investigated theoretically and experimentally by 0.3kg/ch scale vacuum resistance furnace. Three methods to increase the surface-area/volume ratio of liquid metal, such as gas atomizing, mechanical atomizing and mechanical stirring, were tested to increase the Zn distillation rate in 5kg/ch scale vacuum resistance-furnace. It was easy to lower the remaining Zn content to less than 0.1 wt% within one minute by mechanical stirring method. A water-model simulation experiment indicated that a significant agitation of the melt by stirring would be effective to increase the distillation rate. Continuous agitation vacuum distillation process (CA VP) has been designed and the pilot plant is now in construction.

Jan 1, 2000