By I. Moscoso, R. Padilla, M. C. Ruiz

Antimony and arsenic are impurities in copper concentrates found normally as stibnite (Sb2S3), tetrahedrite (Cu12Sb4S13) and enargite (Cu3AsS4). When copper concentrates contain appreciable amounts of As and Sb, they must be removed before smelting to avoid environmental pollution. Oxidizing volatilization roasting at 500–700 °C has been used to eliminate these impurities. However, only a fraction of Sb volatilizes in those conditions; thus, a more effective process to eliminate antimony from concentrates is needed. In this study, the chloridizing roasting of Sb2S3 using CaCl2–O2 was investigated to remove the antimony from concentrates. XRD analysis of calcines indicated that the overall reaction could be written as: Sb2S3 þ3CaCl2 þ6O2 ¼ 2SbCl3 þ3CaSO4 Temperature and oxygen partial pressure have a significant effect on the rate of reaction. An estimated conversion of about 90% was obtained at 750 °C, 5.4% oxygen in 20 min. High oxygen concentrations arrest the advance of the reaction forming various antimony oxides including Sb6O13, Ca5Sb5O17 and Sb2O4.

Mar 1, 2017

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By Milan Lj. Stamatovic

The hydrometallurgical recovery of zinc from recycled blast furnace dust from a steel plant (Smederevo Metallurgical Company, Yugoslavia) was investigated. The dust contained 22% Fe, 17% Zn and 0.2% Pb. X-Ray diffractometry showed that the main components were hematite and magnetite, in combination with zinc oxide. Individual particles were generally spherical and ranged in size from 10 to 150 microns; 63% were less than 33 microns in diameter. An effective hydrometallurgical approach proved to be by caustic leaching and electrowinning. Recovery of zinc in the form of zinc powder was over 90%; this material can be used for the cementation of impurities in the conventional hydrometallurgical process for zinc production.

Jan 1, 1994

By T. Shibasaki

Purification of copper electrolyte at Naoshima is carried out by two stage liberation to completely depress copper and impurity ions followed by concentration of the solution to produce crude nikel sulfate as by-product. A new nickel recovering process has been developed and pilot tested recently. It consists of the following process steps.; neutralization of spent electrolyte from liberation section to remove free acid and most part of remaining impurity ions, refining and nickel concentration by solvent extraction, and crystallization of pure nickel sulfate from concentrated strip solution. This paper describes the results of laboratory and pilot plant tests, then briefly discusses feasibility of the proposed process.

Jan 1, 1987

By Kazuhiro Nisizono, Takashi Kuroki, Nobuyuki Mori, Keisaku Ogi

"The improvement of critical current density and mechanical property is essential to the practical application of the superconductive oxides. A solidification technique is developed in this study for the growth of columnar or single Y123 crystal with finely dispersed Y211 and Ag particles through a monotecto-peritectic reaction of Li.(Ba-Cu-Ag-0 rich liquid)+ Y211-+ Y123+Lz(Ag rich liquid). The large solidification rate and temperature gradient can refine the Ag and Y211 particles. But Ag-free region is widely formed along the crystal growth direction in the central part of the Y123 cell. Since this phenomenon occurs because of the cellular growth, it is necessary to narrow Y123 cell width or to grow Y123 crystal with flat freezing interface. By controlling crystal growth direction using a seed crystal, Y123 columnar or single crystal with uniformly dispersed fine Ag particles are obtained. The· behavior of Ag and Y211 particles during the solidification of Y123 crystal is simulated by the peritectic growth model of faceted Y123 crystals.IntroductionY-Ba-Cu-0 superconducting oxide (YBCO) with high critical temperature also has excellent superconducting characteristic under the high magnetic field. The critical current density (Jc) has been enhanced by ·using unidirectional-solidification technique, which can overcome the weak-link problem at grain boundaries and control the crystal orientation and the distribution of Y211 particles which give effective magnetic flux pinning centers in the Yl23 matrix [1-4].In addition to improving superconducting properties, it is necessary to improve mechanical property for the practical application. The silver addition to the melt-textured YBCO superconducting oxide has been reported as the effective method to improve mechanical properties without degrading superconducting properties. Since the material properties are considered to be largely affected by silver particle size, form, dispersion state etc. in the Y123 phase, it is important to control Ag distribution in YBCO/Ag composites. Besides, it is also reported that the silver addition improve the corrosion resistance to the water and CO2 [5,6]. Nishizono et al. [7-9] have reported that the silver distribution in the YBCO/Ag composites is largely affected by the solidification condition, but yet some unclear points are also remained. YBCO has been also fabricated by the zone melting method [10-12], and Furuya et al. [5] and Hirano et al. [13] have reported the fabrication of silver added YBCO composites, but the distribution and behavior of Ag are not investigated in detail"

Jan 1, 2000

By Michael F. Kitto

The production of sulphuric acid at base metals smelters is predominantly an involuntary activity and now comprises approximately 17% of all-forms sulphur supply in world terms. The majority of elemental sulphur is also produced involuntarily in response to environmental regulations regarding emissions from hydrocarbon processing plants. The paper examines the points of similarity and difference in the sulphur and smelter acid markets, and reviews their interactions. The reasons for the merchant acid market collapse of 1993 are analyzed, and the prospects of a recurrence are considered.

Jan 1, 1996

By C. A. Silva

The kinetics of chlorination of titanium-bearing raw materials has been investigated. For comparison purposes pellets of controlled macro-porosity, made of analytical grade TiO2 and anatase concentrate (Brazil) , have been exposed to different combinations of gas composition - CO, CO2, C12 -, gas flowrate and temperature. A thermogravimetric technique and an adapted grain model have been used in order to assess the influence of the several experimental parameters upon the chlorination behavior.

Jan 1, 1997

By Milton Manrique

The thermal decomposition of zircon concentrates in a non-transferred arc thermal plasma flow reactor was investigated. The plasma torch was operated using argon-helium and argon-nitrogen mixtures as plasma gases. The effect of power, feed rate and zircon particle size was studied. Products were characterized by XRD, SEM, TEM and chemical analytical techniques. The average size of the product was in the submicron range. Free energy minimization plots were used to predict the behavior of the system under different operating conditions. A kinetic model to describe the different stages of the thermal decomposition process is proposed. The results of this investigation showed a significant segregation process where the zirconia-rich product is collected in the reactor while the silica-rich product is collected in the filter. TEM analysis indicated that silica vapor is condensed on the surface of the zirconia particles.

Jan 1, 1996

By Yoichi Takeda

Copper solubility in SiO2-CaO-FeOx slag equilibrated with copper matte in 10% SO2 atmosphere at 1573K was estimated. Essential parameters are activity coefficients of copper oxide and sulfide, oxygen and sulfur potentials and activity of copper in the slag-matte system. A large number of experiments provide proper parameters to calculate copper solubility in slag, A classical thcrmodynamic model postulating CuO0.5 and CuS0.5 moleculcs assists in estimating copper solubility in slag. Additions of Si02 and CaO reduce copper solubility almost in any condition. Copper loss, that is function copper solubility and slag volume, in the silica saturated SiO2-FeO. binary slag is minimally equilibrated with less than 66% copper matte while copper loss in the 50% FeO.-SiO2-CaO ternary slag saturated with 2CaOSiO2 is minimally equilibrated with over 66% copper matte. This slag composition has potential for continuous copper converting, direct copper production or high-grade matte production.

Jan 1, 2003

By Takeshi Nagano

Copper pyrometallurgy in Japan has experienced quite fundamental changes in last fifteen years. The severe environmental restriction coupled with increase of energy costs accelerated the development work of the new continuous process in Mitsubishi Metal Corporation. After several years of pilot plant test work the commercial plant was put into operation at Naoshima Smelter in 1974, the design capacity of which was 4,000 tonnes of copper per month. Many modifications and improvements have been incorporated into the process and 7,200 tonnes per month of copper production was achieved in 1983, proving that continuous process was much more economical than conventional process. It is now possible to design and operate the continuous process in wide range of capacity. This paper will review the process and describe the progress of the process in these 10 years. 311

Jan 1, 1985

By Jinrong Zhang

Major components of soil were tested for their ability to attenuate cyanide. Feldspar, kaolinite, plagioclase and bauxite are found to degrade cyanide at an appreciable amount mainly through adsorption. A soil near a mining site in northern Nevada was studied in detail using a tall column. Many species of cyanide were anlyzed to determine the mechanisms of the reactions of cyanide with soil. Volatilization, adsorption, oxidation, precipitation and complexing were quantitatively identified, being 5 to 10, 11.7, 4.2, 7.3 and 4 per cent of the total cyanide added, respectively. It is found that the oxidation of cyanide to cyanate is due to the catalytic effect of nickel and copper leached from the soil. Precipitation of metal-cyanide complexes occurred at low pH values.

Jan 1, 1991

By Samantha Moodley, Rauf Hurman Eric, Cevat Kucukkaragoz, Aditya Kale

"Two titania slags, rutile and synthetic rutile were chlorinated with petroleum coke and CO in a small bubbling fluidized bed reactor. The study aims to identify differences in chlorination mechanism, compare conversion rates, blowover and the chlorination of impurities for the various titania feedstocks at different temperatures.Chlorination rates were highest at 1000ºC; rutile chlorination significantly increases as temperature increases from 800ºC to 1000ºC. At 1000ºC, synthetic rutile had the highest chlorination conversion rate; this was followed by Slag B which in turn was more reactive than Slag A and rutile. The mechanism for slag, synthetic rutile (SR) and rutile chlorination differs. Synthetic rutile feed is porous, providing a larger surface area for the chlorination reaction, hence the highest conversion rates was attained. Titania slag becomes porous with the initial chlorination of FeO and MnO whilst rutile remains solid. As the porosity of slag particles increases so does its tendency to be elutriated. Ti2O3 is oxidized within the early stages of chlorination during the chlorination of FeO and MnO. Ti2O3 not oxidized is then rapidly chlorinated.IntroductionTitanium dioxide (TiO2) is the most common compound of titanium, about 95 - 98% of extracted titanium minerals is processed into TiO2 white pigment [1]. Two processing routes exist for the production of TiO2 pigments, i.e., sulphate and chloride based processes. In the chloride process, titania feedstock is fed to a fluidized bed reactor together with reductant and chlorine gas. A temperature of 1000 - 1300ºC is maintained in the reaction zone and apart from silica, zirconia, uranium and thorium, virtually all the metal oxides in the feed are converted to their respective chlorides [2]. Chlorine is recovered and recycled back to the reactor."

Jan 1, 2012

By Philippe Charlier

Recycling of aluminium contained in used aseptic beverage cartons is a difficult task which has nevertheless to be tackled by our modern societies. Techniques have earlier been developed by the paper and pulp industry for the recycling of the board fibres from collected post-consumer beverage cartons. A joint technical feasibility study by Granges and a leading beverage carton producer has dealt with different techniques for handling residues from repulping facilities. The aluminium obtained can be used as raw material for the production of thin gauge foil, thus closing the recycling loop.

Jan 1, 1995

By Dae Jin Ha

Sticking phenomenon occurring during hot rolling of two STS 430JlL ferritic stainless steels was analyzed by hot-rolling simulation tests. The sticking started from the initial nucleation stage in which the rolled materials were stuck onto the roll specimen surface, proceeded to the growth stage in which stuck fragments grew further, and reached the saturation stage. The modified 430JlL steel had a smaller number of sticking nucleation sites and slower growth rate than the conventional 430JlL steel because of higher high temperature hardness, thereby leading to less serious sticking. When the simulation test was conducted at 1070 °c, Cr oxides were formed on the surface of the rolled materials, and thus the sticking was drastically reduced because of the increased surface hardness of the rolled materials. In order to prevent the sticking, high-temperature properties of the rolled materials should be enhanced when rolled at 900°C or 1000 °C, and rolling conditions and alloying compositions, under which the oxide formation was promoted, were more important than high-temperature properties when rolled at higher temperatures than 1000 oC.

Jan 1, 2008

By Shin-ya Kitamura

Kinetic modeling is very important to understand steelmaking reactions. The coupled reaction model proposed by Prof. D.G.C Robertson is the best suited program, and therefore, the author has applied it to the various steelmaking reactions, a few examples of which are discussed. Hot metal dephosphorization occurs under non-equilibrium conditions as it takes place between the slag, which has a high oxygen potential, and the hot metal, which has a low oxygen potential. A process simulation model based on the coupled reaction model was constructed. This model considers the solid and liquid slag, liquid metal phases, and the reaction between the solid and liquid slag, besides the reaction between the liquid slag and liquid metal. Using this model, the ruling factor to increase the reaction efficiency of dephosphorization has been verified. In the secondary refining process, the values of inclusion composition calculated by the thermodynamic model, under the assumption of equilibrium with the metal composition, were found to be different from those observed in practice. A kinetic model, incorporating the reactions between slag, metal, inclusion, and refractory has been postulated, and the composition change of inclusion during treatment has been analyzed.

Jan 1, 2014

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By M. Rockandel

"Universal Dynamics Ltd. of Vancouver, Canada has developed, patented and commercialized the ""REMERC"" process for the treatment of mercury contaminated sludges and soils. Mercury is extracted into an acidified and oxidizing, sodium chloride brine solution. REMERC was initially developed to treat mercury contaminated EPA listed wastes (K106) generated by the chlor-alkali industry. More recent work has expanded the capability;' of REMERC to include remediation of mercury contaminated sites, equipment and building materials.In the process mercury is currently recovered from solution by cementation on iron powder in an agitated reactor. The process recovers high purity elemental mercury (99.9% purity). Cementation typically recovers about 90-95% of the mercury in 30 minutes. Higher recovery is not necessary because of the recirculation of the leach solution. When treating highly contaminated chloralkali wastes (5-13% mercury content), REMERC will reduce the mercury laden solutions from 400-1,000 mg/L mercury to 50-100 mg/L. In the treatment of less concentrated wastes «1,000 mg/kg mercury) such as those encountered in site remediation, the treated solutions will generally contain 10-20 mg/L mercury. Cementation while being simple and able to achieve the required recovery has the. undesirable properties of; requiring a solid-liquid separation and adding iron to solution which must be precipitated, ultimately increasing the weight of residue to landfill. .The potential advantages of electrolysis were recognized early in the development of REMERC. Mercury electrolysis is well known in gold and chloralkali processing. Initial testwork utilized a liquid mercury cathode and a coated titanium anode both common to chloralkali producers. The mercury cathode appeared susceptible to polarization and solution impurities significantly affected performance. Agitation of the mercury pool improved performance but it was still not possible to achieve the reduction objectives. Current efficiencies were low, near 10%, and it was apparent that a relatively large cathode pool would be required to limit the current density. A number of electrode combinations with and without a membrane were then tested in a vertical electrode' configuration but the desired performance was not obtained."

Jan 1, 1997

By R. M. Reynolds

Engitec Impianti, S?.p.A. of Milan, Italy has successfully designed, constructed and has in operation state-of-the-art battery breaker systems at two European locations. A third facility i:s partially completed in Toronto, Ontario, Canada. The CX system crushes whole batteries, separates the various components and desulfurizes the battery paste. The system also produces sodium sulfate from the sulfuric acid and lead sulfate contained in the batteries. Actual plant operating data indicates that the desulfurized paste contains less than 0. 6 percent sulfur and less than 0. 5 percent antimony. The CX system utilizes mechanical screening and an up-flow hydrodynamic separator to accomplish the component separation. Sodiwn hydroxide or sodium carbonate is used for desulfurization. The sodium sulfate brine is evaporated and crystallized to produce clean anhydrous sodium sulfate suitable for use by detergent or glass manufacturers. Plant data also indicates that an increase in furnace productivity of about 25 to 30 percent is achieved using feed from the CX system. The desulfurized paste is very suitable for electrolytic processing as an alternative to pyrometallurqical processing.

Jan 1, 1990

By Roland Kammel

In combination with various physical and chemical methods also electrochemical techniques are most frequently used to improve the recovery of metals from aqueous dilute process streams or effluents e.g. in electroplating, metal finishing, mining and metallurgical plants. To insure cathodic metal recoveries with favorable current efficiency and high throughputs per unit of cell volume seve¬ral types of electrolysis cells have been developed comprising extended electrode surface areas and/or intensive electrolyte. agitation. The practical experiences with these units indicate especially for the electrolytic recovery of metals whose values are high, that the treatment cost permits profitable operations with relativly short payback periods for the units. Anodic reactions can be utilized for the removal of undesired anion contents or buildups of impurities. Appropriate combinations of these recovery methods are used to improve the versatility and the overall economy. Industrial applications reveal their potentional as addidtive techniques for existing processes to reduce the metal content of effluents to values that meet the guide lines of environmental legislation whereas integrated in-operation recovery methods are nowadays increasingly introduced to approach nearly close-loop operations.

Jan 1, 1992

By F. G. Prado

The technology for the extraction of zinc from zinc residues, such as zinc ashes, drosses and metallurgical flue dusts, by way of ammonium chloride solutions is well established, at least at the laboratory and bench scale levels. (3, 4) Zinc is soluble in ammonium chloride solutions in the form of zinc diammine chloride. Its solubility depends upon the concentrations and temperatures employed. The procedure and the equipment required are simple, and they can be applied either to small or large operations. As a by-product, zinc diammine chloride is produced with extremely low impurities in quantities which are stoichiometrically proportional to the zinc removed. The technology has been applied experimentally to galvanized steel residues. The dezincing results, including removal performance, energy and reagents required, and by-products are summarily presented in this paper.

Jan 1, 1992