By Shun Myung Shin, Kang Jeong, Kyoungkeun Yoo, Jin Koo, Dong Hyo Yang, Soo Sohn

"The optimum discharging condition to dismantle the batteries without explosion was investigated to recycle the lithium primary batteries, which could be exploded by heating too much or crushing. The 3 waste lithium primary battery cells were discharged with 500 cm3 of 0.5 kmol·m-3 sulfuric acid. Fe concentration and pH increased rapidly after 3 days at 35? and after 1 day at 50?. Chromium concentration increased by 4 days at 35? and 2 day at 50?and then decreased, and nickel concentration was very low. Because Li concentration increased gradually, Li became dissolved after the dissolution of cover material. When the discharged batteries were shredded, the batteries discharged at 50°C were not exploded and those discharged during 3 days at 35°C were exploded. This result shows that the waste batteries could be stabilized within 1 day at 50°C and 4 days at 35°C. Introduction Lithium has some advantages for battery e.g. it is the lightest metals and also has the highest electrochemical potential at 3.04V[1]. For over thirty years lithium primary batteries became famous for their performance in various applications such as IT, medical, and military[2,3]. They gained a reputation for their long shelf life, constant voltage, wide operating temperature range, and low self-discharge characteristics[3-5]. World primary lithium battery market was expected to grow from $820.6 million in 2003 to $1,1355.3 million in 2010 (http://www.frost.com, Frost & Sullivan)[2-4]. The lithium primary batteries have very various sizes and components. Lithium batteries are made with lithium metal as anode active material and non-aqueous solvent as electrolyte. As cathode active material, various kinds of materials were used such as manganese dioxide (nominal voltage, 3.5V), thionyl chloride (3.6V), and carbon monofluoride (3.0V). In Korea, 50 % of the spent lithium primary batteries must be recycled because spent lithium primary batteries have been listed in EPR (Extended Producer Responsibility) of the enforcement degree of the act on the promotion of saving and recycling of resources. However, the batteries have been landfilled since there is no economic method to recycle the batteries in Korea[2,3]. When the batteries were heated too much, charged, pierced, over discharged, or short-circuited, the batteries explode because lithium reacts violently with water or air and because contents such as lithium, electrolyte, and sulfur become flammable by high temperature[4]. Therefore, it is so difficult to recycle safely the spent lithium primary batteries."

Jan 1, 2008

By K. C. Liddell

"Cu/Ni multilayers exhibiting giant magnetoresistance were deposited from a single electrolyte under stepped potentiostatic control. To enable transport measurements to be made without remounting the multilayer film, we developed a novel method that involved plating on a thin metallic basal layer atop a rigid non-conducting Si substrate. Rotating ring-disk electrode techniques were used to monitor the composition and thickness of individual plated layers. Transmission electron microscopy confirmed that the interfaces between adjacent layers were sharp and that the structure of the layers was uniform throughout the film. Atomic force microscopy images indicated that the film's surface was smooth and free of defects.ELECTRODEPOSITION OF THIN MULTILAYER MAGNETIC MATERIALSI. IntroductionElectrodeposition of compositionally modulated films will in all likelihood continue to be used to produce the read heads for stored magnetic data. However, the next generation of head materials will require both improved sensitivity and reduced film thickness. Certain multi layers consisting of thin alternating ferromagnetic and nonmagnetic layers exhibit giant magneto resistance and consequently are promising candidates for read head applications. We have successfully made multilayer films with giant magnetoresistance that have total thicknesses as low as 25 nm, approximately 120 times thinner than the thinnest similar films reported in the literature. This paper describes early results from our work on electrodeposition and characterization of Cu/Ni multilayers, a model system with enhanced magnetic and mechanical properties, including the GMR effect. The structure and composition of the multilayers were determined using TEM, AFM, and electrochemical methods, and their magnetoresistance was measured by the standard four-probe technique. A novel method developed in this work enabled the transport properties of the ultrathin films to be measured reliably without the need to dissolve the cathode or handle the films. To provide a context for these results, short accounts of other work on giant magnetoresistance and multilayer electrodeposition are also included."

Jan 1, 1997

By H. Y. Sohn

The ignition and combustion of chalcopyrite particles under suspension-smelting conditions, in which the particle-particle interaction is neglected, has been analyzed by considering the intrinsic kinetics of oxidation and heat and mass transfer between the particle and its surroundings. Reasonable agreement has been obtained between the calculated results and experimental results from a laminar-flow furnace reported in the literature. This computation- al procedure has further been applied to flash-smelting conditions. Under suspension-smelting conditions (Sh = Nu = 2), chalcopyrite particles ignite at around 960 K. The effects of various parameters, such as oxygen concentration, particle size, and gas temperature, have also been evaluated. Comparison between calculated results in this work and experimental observations indicates that SO is the important gaseous product that forms at the surface of the particle.

Jan 1, 1993

By B. C. Blakey

The economic feasibility of the sulphuric acid pressure leaching route for the extraction of nickel and cobalt values from limonitic ores is highly dependent upon the behavior of aqueous aluminium. This is primarily due to its precipitation as hydronium alunite ((H30)A13(S04)2(OH)6), which is one of the major scale-forming compounds found in autoclaves used for pressure leaching. As a result of renewed interest in the pressure leaching process, an investigation of the aqueous-solid eqilibria in the aluminium-sulphate-water system under acidic (< pH l), high temperature (230 to 270°C) conditions has been conducted. Pure hydronium alunite was synthesized in an autoclave by leaching boehmite (A100H) at elevated temperatures in sulphuric acid solutions initially 0.25 to 0.75 m H2S04 in concentration. Spontaneous, in situ precipitation of hydronium alunite followed. A high temperature solution speciation model was used for the analysis of the resulting solubility data in order to calculate equilibrium constants for the precipitation reaction.

Jan 1, 1994

By T. W. Gonzales

The refractory performance of Peirce-Smith converters is considered to be mainly determined by effects of process control and refractory installation design. BHP Copper has shown that, over the last four years, considerable improvements in tuyere line life can be affected .by maintaining a uniform temperature in the operating converter and by ensuring sufficient and specific placement of expansion allowance in the construction of the refractory brickwork. A combination of optimized crane availability, rapid matte transfer, converter operating practices, new refractory installation techniques and applications has minimized out-of stack time. In addition, larger diameter tuyere pipes and hard piping have increased blowing rates and lowered cycle times, which has resulted in a tuyere line performance in excess of 62,500 tonnes of blister copper before maintenance is required. This paper discusses the refractory installation design changes that were made to increase tuyere line life.

Jan 1, 1999

By A. R. Kiani-Rashid

Controlled graphitization has become known as a practical method for improvement of wear resistance and machining properties in steels. In this paper, the effect of heat treatment on microstructure of CK45 steel has been investigated. Austenitising was carried out at 920°C for 5 hours. Besides, isothermal transformation was conducted at 750°C in the time range of 1-20 hours. The microstructure of the steel considerably changes by this heat treatment process which exhibits the effects of temperature, appropriate austenitising duration and isothermal transformation. Conducted experiments show a suitable distribution of semi-spherical graphite particles especially on the surface of the steel. Also, analyses demonstrate that the amount of formed graphite in the austenitising temperature 920°C is more than graphite in single heat treatment temperature of 750°C.

Jan 1, 2010

By O. Chemezov, Yu Zaikov, A. Apisarov, A. Isakov

"Silicon deposits containing 99,9 wt.% of main component were obtained by SiO2 electrolysis from chloride-fluoride melts. The operating temperature was varied from 973 up to 1073 K. The conditions for obtaining crystalline fibrous micro- or nanodeposits were determined. The deposits were investigated by ESM methodIntroductionThere are large reserves of natural quartz of high purity in Russia. Processing of this raw material by electrolysis in molten salts produces silicon containing 99.9 weight percent of basic substance.[1]This method is less energy-consuming in comparison to existing methods for producing high purity silicon from gas phase.Another advantage of the electrolytic method for producing silicon from its oxide in molten salts is the possibility of production of high-purity silicon under air atmosphere. It dramatically reduces costs of the electrolytic cell construction, and the operating costs at electrolysis.On our opinion, the main advantage of the electrolytic production from SiO2 in molten salts is a unique opportunity to obtain micro-and nanostructures of silicon deposits. In particular, it is possible to obtain fibrous structures of silicon. The electrolytic method allows smoothly adjusting the thickness and length of silicon micro- and nano-wires by varying the cathode current density and temperature of the process."

Jan 1, 2012

By S. A. Platias

Large amounts of dunile tailings can be recycled for olivine produdion from the existing beneficiation adivity of chromite ore in northern Greece. This olivine production aims at the preparation of a material suitable for the substitution of the environmental hazardous quartz sand in the foundries of Europe In smelting of chromite ore the losses that occur ore usually of the order of 6-8% Cr that report in the slag. Most of this is in the form of oxides that cannot be recovered, but usually 30-35% is in the form of FeCr alloy that can be recovered by gravity methods. About 90% of the produced slag is sold for road construdion after crushing to a desired grain size. Finally, recycling of chromites sludges from the ferrochrome produdion plant, through the preparation of pellets, improved the total chromite yield by 2%.

Jan 1, 1996

By Charles Zimmerman

The Genesis gold mine, owned and operated by Newmont Gold Co., is located in section 31, T36N, R50E within Eureka County, Nevada along the Carlin Trend of sediment-hosted disseminated gold deposits. Mining commenced in 1986 with present mineable and stockpiled reserves listed at 17,711,000 tons of ore averaging 0.073 opt Au, totalling 1.292 million ounces of gold. Ore is primarily hosted within Devonian calcareous siltstones that have been subjected to intensive argillization and silicification episodes. Additional mineralogic and geochemical features of the Genesis ores include enrichment in iron-oxides, kaolinite, arsenic and antimony; the ore zone is relatively depleted in carbonates and sulfides as a result of supergene and hypogene oxidation. Two major structural zones enhanced the permeability of the siltstones and served as the main hydrothermal conduits within the deposit. Prior to the main ore stage, the host rocks were subjected to metasomatic effects caused by emplacement of the Juro-Cretaceous Goldstrike granodiorite pluton and associated dikes and sills. Micron-size gold occurs in clays, micro-crystalline quartz, and in arsenical complexes. Non-oxidized carbonaceous and sulfidic ores and silica-locked ores result in variable preg-robbing and refractory responses during cyanide recovery. Selective mining and milling has resulted in the successful treatment of the Genesis orebody.

Jan 1, 1988

By K. Ono

A new process for extraction of titanium metal from its oxide is demonstrated. In this process, row material to be reduced is titanium oxide synthesized from ilmenite. The reducing agent is the Ca+CaCI2 two-phase mixture. TItanium is elaborated in the medium consisted of liquid Ca, Caq and solid TI02 at the temperature range 1200 to l300K by means of mixing mechanically the ingredients in the reactor into a smooth paste. Fluidity of the feed which enables continuous scheme depends on the CaCl2 content. The oxygen level of the reduced titanium is the range 500 to 1000 mass ppm varying with the operational conditions. The Ca+CaCI2 reducing agent is taken out from the electrolysis of CaC12 at 11401(, and this CaCl2 is produced by aqueous chemistry conversion using Cl2 gas recycled from the electrolysis.

Jan 1, 2001

By Thomas F. Nederpel

The production of zinc and zinc-aluminum coated strip can be reasonably accomplished on a single operating unit. However, if the hot dip coating line is equip d with only one mo 7 ten metal holding furnace, it is necessary to transfer liquid metal of different chemistries and reintroduce virgin material to obtain the 18" necessary balance of elements in the bath. Dofasco produces Galvanize and Galvalume on a coating line with a sin le liquid metal furnace and has developed not only an efficient liquid metal trans& system but also an effective means of reutilizing the zinc-aluminum mixtures without detrimental quality affects.

Jan 1, 1992

By Kathryn C. Sole

A novel solvent-extraction process for the refining of gold was recently commercialised, with the commissioning in May 1997 of a 24 t a-&apos; refinery at Harmony Gold Mine in Virginia, South Africa. The MinataurTM Process (Mintek Alternative Technology for Au Refining) uses solvent-extraction technology to produce gold of 99.99% purity from the cathode sludge arising from a conventional carbon-in-pulp / electrowinning circuit. Implementation of this process introduces significant cost benefits compared with the conventional dore smelting / toll-refining route previously followed. This paper outlines the process, presents selected operating results obtained during the first few months of operation, and provides some details of the associated techno-economic advantages.

Jan 1, 1998

By H. -P. Behrendt

Muldenhiütten Recycling und Umwelttechnik GmbH is a lead smelter with a very long tradition. The first reference to the existence of smelters on this site is given by a document of inheritance dated 1318. Originally run as a primary lead smelter, which was supplied with ores from the Freiberg mining district and from overseas, it was required to change it over to secondary raw materials due the abandonment of mining in the Freiberg area in 1968. Today, Muldenhüitten Recycling und Umwelttechnik GmbH has two production lines; lead production from secondary lead and waste incineration, which are closely connected and gain advantage from each other. Installations, improved technologies, and the highly skilled personnel have contributed to satisfy all demands for a production concerning quality and environment.

Jan 1, 2000

By Tom Lewis

This report discusses the evaluation of the ENVIRO-CLEAN PROCESS, a technology developed by Lewis Environmental Services, Inc. for the recovery of metals such as chromium, mercury, copper, cadmium, lead, and zinc from surface and groundwater streams. This new heavy metal removal process (patent-pending) utilizes granular activated carbon with a proprietary conditioning pretreatment to enhance heavy metal adsorption combined with electrolytic metal recovery to produce a saleable metallic product. The process generates no sludge or hazardous waste and the effluent meets EPA limits. A 50 gpm system was installed for recovering hexavalent chromium from a ground water stream at a site located in Fresno, California. The effluent from the activated carbon system was reinjected into the ground water table with the hexavalent chromium concentration < 10 ppb. The system simultaniously removed trichloroethylene (TCE) to concentrations levels < 0.5 ppb. The activated carbon is regenerated off-site and the chromium electrolytically recovered. The full scale system has treated over 5 million gallons of ground water since installation.

Jan 1, 1996

By Neng-Wen Yu, Miao Wang, Ji-He Wei

The mass transfer characteristic between powder particles and liquid steel in the RH-PTB (Powder Top Blowing) refining has been investigated in a water model of 1/5 scale for a 90t RH degasser. The sodium chloride powder with analytical purity has been used as the flux for blowing. The mass transfer coefficient of the liquid side has been determined under the conditions of RH-PTB process. The influences of the main technological and structural parameters on the mass transfer rate have been examined. The results indicated that under the conditions of the present work, the mass transfer coefficient on the liquid side increases with raising the lifting gas blowing rate, inner diameter of the up-snorkel, circulation rate of the liquid and particle size of powder flux. And it decreases with an increase in the inner diameter of the down-snorkel. It is in the range of (l.36-7.30) x 10·4 mis, the appropriate dimensionless relationships have been obtained as follows:

Jan 1, 2000

By Chuanfu Zhang, Liwei Liang, Yanxin Wu, Jinliang Wang

"According to the reaction shaft operation characteristics during the flash smelting process, 15 groups of slag samples containing high Fe3O4 were prepared by some chemical reagents, and then the slag viscosities were measured using a RTW-10 type synthetic test instrument for melt physical property by the rotating cylinder method. The effects of Fe/SiO2 ratio (mFe/mSiO2), Fe3O4 content (wFe3O4), Cu2o), MgO content (WMgO) and Cao content (wCaO) on the slag viscosity were also studied. Results show that slag viscosity is decreased with the increase of temperature, mFe/mSiO2, wCu2o, wMgO and wCao, and with the decrease of wFe3O4, under the range of slag contents: mFe/mSiO2 1.36~1.78, wFe3O4 17.83%~21.18%, wCu2o 3.51%~8.34%m wNgI 2.21%~6.57%m w/caI 6.22%~9.387% and temperature range if 1250 o/c~1450 oC. Only wFe3O4m and w/caO have great influence on the slag viscosity when temperatures as high as 1400 oC. Only wFe3O4 and wCaO have great influence on the slag viscosity when temperatures as high as 1400 oC or so. To form a freeze slag with higher viscosity inside the reaction shaft, wFe3O4 should be more than 20% and wCaO should be less then 6%.IntroductionSince its appearance in 1949, Outokumpu flash smelting technology has making continuous innovation and has become the most competitive intensified smelting technology [1], widely considered to be the standard clean smelting process [2]. At present, flash smelting technology is adopted to newly build or reconstruct most of the world's copper or nickel smelting enterprise [3]. Reaction shaft is the most important part of the flash smelting furnace. During the flash smelting process, reaction shaft must be able to withstand the following harsh conditions at the same time: 1) high temperature varying from 1400 °C to 1500 °C. 2) strong oxidative atmosphere containing 50% - 80% oxygen. 3) solid particles and melt with speed up to l00 m/s. 4) high acidic or basic slag with strong chemical corrosiveness. 5) smelting gas containing 50% - 80% SO2. 6) matte with strong dissolution."

Jan 1, 2012

By M. -L. Metsärinta, J. Nyberg, A. Roine

The Kokkola roasting plant uses more than 20 different zinc concentrates every year. During recent years there has been an increase in the variation in concentrate quality; in particular, the amount of fine-grained and low-grade concentrates has increased. Therefore, a great deal of development work has been carried out to improve the operational flexibility, online availability, production capacity and calcine quality of the roasting plant. This work consisted of a heat and material balance model of the roasting based on HSC Chemistry software, a new water admixture system for the concentrate feed, a new oxygen feed system for the process air line, improved cooling of the furnace and boiler and improved operational practices, dust removal and concentrate mixing. These new process control tools and other improvements, as well as some test results, will be described in this paper. The oxygen feed may be used to improve production capacity and to decrease the sulfide content of the calcine. The water feed may be used with fine concentrates to decrease both dust carry-over and the temperature in the top part of the furnace. Improved cooling of the furnace and boiler helps to increase production capacity.

Jan 1, 2000

By M. M. Kim

As-electrogalvanized coatings of pure Zn, Zn-11% Fe, and Zn-18% Fe coatings were characterized in terms of initial crystal structure and surface morphology. Samples were then subjected to heat treatments simulating the paint bake cycle of automobile manufacturers. Surface morphology changes were correlated with the process variables, and crystallo.graphic changes were interpreted by mapping heat treatment routes on the Fe-Zn phase diagram. The morphology of pure zinc electrogalvanized coatings with heat treatment from platelets to smeared platelets. The zn-11% Fe coating changes with heat treatment from tetrahedral nodules to a mixture of round and tetrahedral nodules, with the Zn-:18% Fe coating always having round nodules. Regarding crystal structure, a critical transformation time can be defined at any selected temperature, below which the crystal structure does not change. This temperature is related to iron content.

Jan 1, 1990

By Corby G. Anderson

For over a century, the Sunshine Mine in Idaho has been a major producer of silver. An estimated 335,000,000 troy ounces of silver has been mined. This has established the Sunshine Mine as the largest single source of silver in the world. Because the dominant silver containing mineral is tetrahedrite, a copper and antimony sulfide, normal metallurgical treatments to recover the precious metal are not practical. Thus, over the course of the company&apos;s history, novel, hydrometallurgical technologies have been developed on-site to handle complex, precious metal containing materials. Recently, the use of Sunshine technology has been extended to the recycle of secondary materials. As well, the use of Sunshine technology by other organizations for treatment of both primary and secondary feedstocks containing precious and base metals is an area of growing interest. This paper will provide an overview of Sunshine hydrometallurgical technologies including the applicability of Sunshine technology to the recycling of precious and base metals.

Jan 1, 1995

By Konstantina Chalastara

Mixed phase titanium dioxide (TiO2) nanoparticles synthesized through hydrolysis of TiCl4 solution at different conditions, namely concentration, pH, and residence time are characterized and evaluated as photocatalysts. The process is operated in a continuous stirred-tank reactor, CSTR giving blends of anatase, brookite, and rutile nanoparticles that were further evaluated to find the optimum mixture for a photocatalytic sorption material. The titania nanoparticles are first characterized in terms of photocatalytic activity under UV light illumination using an organic model compound (methyl orange) and after that are tested for removal of toxic selenate and selenite species from simulated effluent waters.