By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-SiO2 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [w(MgO)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, w(Fe)/w(Si02) is 1.1-1.4 and the temperatures are within 1473-1773K, the slag viscosities increased with the increase of W(MgO) and w(Fe)/w(SiO,). When w(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When w(MgO)>10%, the temperature should be kept above I 633K. When the content of MgO is higher, a lower viscosity slag can be produced by decreasing the ratio of w(Fe)/w(SiO,). The appropriate ratio of w(Fe)/w(SiO,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Z. Yang, R. W. Smith, Jr. Wharton

"Microorganisms have the ability to remarkably adsorb and/or absorb heavy metal ions. Hence they are being studied widely as a means of removing metal ions from aqueous solutions both in order to clean up toxic streams and to recover valuable metals from these and other streams. It is often difficult to harvest organisms such as bacteria and unicellular algae since they are usually too small to be readily screened out. Froth flotation may prove to be a feasible method to harvest such organisms subsequent to the ad/absortion of the metal Ions. The present paper discusses the surface/electrokinetic properties of microorganisms and the modifier-collect conditions under which they should float. The zeta potential of the green alga Chlorella vulgaris was measured in the presence of AI(III) and Pb(II) ions and in the presence of dodecylammonium chloride and sodium dodecylsulfate. Present and past data suggest that the organisms should behave similarly to other finely divided, charged (polar) solids with their behavior sometimes modified by the non-polar surface regions present.IntroductionThe overall field of bioengineering is growing at a remarkably accelerating rate. Hydrometallurgy and mineral processing are included among those disciplines where there has been actual or proposed commercial use of bioorganisms. Further, the actual or proposed use includes bacterial enhancement of leaching of a number of different types of ores (1-5), modification of the flotation or oil agglomeration separation of minerals by bacteria (6,7) and microorganism (algae, bacteria or fungi) concentration of metal ions present in effluent or other mineral processing or hydrometallurgy aqueous streams (8-23)."

Jan 1, 1988

By Tiruttani Munikamal, Suresh Sundarraj

"A numerical model of the induction hardening process of steel cranks has been developed and the predicted results of temperature and phase distribution during this solid state phase transformation process are verified with experimental data from the literature. This heat treatment process involves heating the crank to the austenitic temperature range followed by rapid quenching in water to harden the surface of the crank. The model has been developed using ABAQUS, commercial FEA software. The formation of martensite, pearlite, and retained austenite phases are modeled and implemented through a user defined function in ABAQUS. A sensitivity study on the various process parameters affecting the amount of phase distribution has been carried out.IntroductionThe type of surface and sub-surface microstructure as well as the residual stresses that are present in a component after manufacturing, significantly affects it fatigue performance. The wear resistance of the automotive components such as crankshaft, gears, camshaft and bearings depends on the surface hardness. In order to achieve the surface hardness, these steel components are subjected to a type of quench hardening heat treatment process. There are several heat treatment processes available for the industrial application to improve the mechanical properties of the final part. Case hardening using induction heating is one of the widely used industrial techniques for improving the surface microstructure of a steel component. It consists of two stages i.e. induction heating cycle, followed by quenching in a fluid medium (usually water or oil)"

Jan 1, 2012

By K. G. F. Janssens

In the process of annealing a deformed metal the microstructure changes due to concurrent recrystallization, grain growth and precipitation. It is common knowledge that all three of these microstructural transformations show a strong dependence on each other, and that an overall model must take the relevant interactions into account. Aiming at the development of an approach which is useful in the more general case, a computational model is being developed which allows the prediction of the three dimensional grain topology and orientation distribution function of any metal submitted to subsequent deformation and annealing, taking into account concurrent recrystallization, grain growth and precipitation and starting from a statistical representation of the deformed microstructure. In this contribution a case study is presented which illustrates the potential and limits of the state of the art in the field. Keywords: Microstructure Evolution Modeling, Irregular Cellular Automata, Deformation, Precipitation, Recrystallization, Grain Growth

Jan 1, 2003

By Xiao Long, Ting Wu, Lilong Zhu, Qian Wang, Shengping He

"During the continuous casting of peritectic steel slabs, mould fluxes with high crystallization capacity are usually chosen for improving slab surface quality. However, the lubrication condition of casting shell also could be deteriorated. Since precipitation of crystals within liquid slag film can change the composition and property of liquid slag over solid-liquid slag film interface region, its impacts on continuous casting process also are not clear. In order to clear this phenomenon, an experiment method was put forward, and mould fluxes for peritectic steel slabs continuous casting were selected and examined. The results reveal that after crystals have been separated, the crystallization capacity of leftover liquid slag increased with different levels, which could deteriorate the lubrication condition of casting shell and cause a series of problems. Thereby, mould fluxes with high crystallization capacity at beginning for heat transfer control and then weaker after crystallization should be considered in the future.IntroductionIn the continuous casting of peritectic steel slabs, contradiction between heat transfer control and slab shell lubrication by mould fluxes has been treated as a key problem for maintaining a smooth manufacturing process [ 1]. Strong and uneven horizontal heat flux over the meniscus region will cause uneven solidification of casting shell, especially for peritectic steel slab with enormous volume change caused by phase transition. All of those could cause surface defects like longitudinal crack [2-4]."

Jan 1, 2013

By Emmanuel N. Zevgolis

Energy required for roasting and smelting of a nickeliferous laterite ore by the rotary kiln - electric furnace process is investigated. From this work it comes that thermal energy is about 65% of the total energy needed and the rest is electrical. Also, 61.3% of thermal energy input in the roasting step (of all combustibles fed into the rotary kilns) is used for pre - heating, 11.6% for pre - reduction and the rest (27.1%) corresponds to the energy of the remaining carbon in the rotary kiln products (i.e., calcine, dust and coatings). Carbon entering the system is used as follows: 57.9% for combustion, 37.1% for reduction and the rest (5.0%) remains unburnt. Exploitation of energy from gases of both furnaces, as well as the higher possible reduction degree, the optimum temperature of the calcine and also elimination of the excess air in the rotary kilns, improve significantly energy balance and economics of the process.

Jan 1, 2006

By Zhigang Liang

A carbon free precast block was prepared by using high-alumina fused corundum as aggregate and fused magnesia, and ultra-fine Al2O3 and ultra-fine SiO2 powders as matrix materials. A small linear expansion for the precast block was achieved through spinel formation from the reaction of MgO with Al2O3. The precast block showed a lower apparent porosity, higher hot modulus of rupture and better slag corrosion resistance compared to the traditional Al2O3-MgO-C brick. Moreover, the practical application of the precast block to the ladle lining proved it to possess a better thermal insulation which could effectively prevent the temperature drop of molten steel during the refining process. It can be predicted that the carbon free precast block could possibly be accepted as a new type of ladle lining material for the production of low-carbon and ultra-low-carbon steel.

Jan 1, 2009

By T. T. Chen

Gold in the Twin Creeks ore is primarily associated with arsenian pyrite. During pressure oxidation, the sulphides are solubilized, but part of the dissolved iron reprecipitates as jarosite and as an iron sulphate-arsenate-phosphate phase. The pressure oxidation products are subjected to cyanide leaching. The cyanide leach residues consist of quartz, gypsum, bassanite, anhydrite, small amounts of jarosite, an iron-sulphate-arsenate-phosphate phase, as well as trace amounts of orthoclase, rutile, pyrite, hematite and monazite; all these particles are dispersed in a fine grained matrix of illite-muscovite. The autoclave leach residues contain a small amount of carbonaceous matter. Many gold grains are detected on the surfaces of the carbon particles, and these gold particles are not leached during cyanidation. The gold particles are typically 0.1-0.2/Lm in size and commonly are embedded in the carbon surface or are coated with a K-AI-Si-S-O phase on the surface of the carbon. The gold grains are consistently associated with elevated CI contents (50-300 ppm Cl). The poor gold cyanide leach recoveries, which initially occurred in the Twin Creek developmental circuit under certain operating conditions, are attributed to the presence of chloride in the feed. This results in the formation of soluble gold chlorocomplexes in the autolcave and the subsequent sequestering of the gold on the surfaces of the carbon particles.

Jan 1, 2000

By Petrus Christiaan Pistorius, Ming Tang

Magnetite concentrate is pelletized and then hardened by elevated-temperature oxidation to hematite, to produce pellets for ironmaking. Previous work showed that the rate of oxidation is under mixed control of gaseous mass transfer of molecular oxygen through the pellet pores, and solid-state diffusion into the oxidizing grains. Because of the partially limiting role of solid-state diffusion, concentrate size distribution strongly affects pellet oxidation. Previously, a simple mixed-control model was formulated to describe isothermal oxidation. In that model, the main effect of concentrate size distribution was on the plateau level of oxidation which is reached at a given temperature. However, the extent of plateau oxidation increases with increased temperature, requiring a more complex model for non-isothermal oxidation. In this paper, predictions of the non-isothermal model confirm the strong effects of concentrate size distribution and oxygen enrichment. In particular, a greater fraction of coarse magnetite particles would be beneficial, decreasing the size of the macroscopic unoxidized pellet core.

Jan 1, 2015

By Pietro Navarra

A great deal of effort has been expended on how to optimize conventional water cooling circuits in furnace cooling elements, and the results have been largely satisfactory. However, there is a general agreement that the proximity of high-pressure water passages to the flow of molten furnace products is a safety concern. Nonetheless there exists little alternative to the formula: increasing furnace integrity implies the incorporation of more extensive forced-convection water cooling systems. Recent developments in evaporative cooling technology have resulted in the development of a high-capacity heat pipe capable of operating under the thermally intense environments of a metallurgical furnace. The system functions using several kg of a working fluid (water) in total, has no moving parts, and allows for a significant reduction in cooling water requirements. Full-scale pilot tests of a copper tap hole and slag launder were done in 2003 and2005, with detailed results given in this paper.

Jan 1, 2006

By Vincent Canaguier

Methane is increasingly considered as a promising reductant for metal oxides, including chromite. To assess the possibilities of such reduction route, the gas-solid reactions between Ar–CH4–H2 gas mixtures and synthetic chromites are studied between 950 and 1050 °C. The influence of Mg and Al additions on the reduction-caburization of (Fe,Mg)(Cr,Al)2O4 solid solution is investigated thermodynamically, structurally and kinetically. The product phases are examined by x-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA). The reaction rate is derived from real-time exhaust gas measurements and post-reaction product analyses such as oxygen analysis. Kinetic models are proposed based on the product phase morphologies and confronted with the empirical data.

By Junfeng Shen

Geosynthetic clay liner (GCL) is a kind of waterproofing material used widely in engineering. The waterproof mechanism is understood in terms of bentonite particles becoming a water-obstructcolloid layer after they absorb water and swell. The swell stress, however, has not been determined directly till now. In our experiment, the swell stresses of the GCL under saturated and water absorbing conditions are measured directly using a custom-made instrument. The results show that (1) the instrument designed by the authors performed satisfactorily and the test results are reproducible; and, (2) The trend line of swell stress variation with time can be divided into three segments. The first segment is characterized by a quick increase of the swell force in the first 0?50 hours. The swell stress increases by 7.00×10-4?1.00×10-3 Mpa / hour. The second segment shows a slow increase of the swell stress during the 50?1730 hours. The swell force increases by 7.54×10-6?2.02×10-5Mpa / hour. The third segment is characterized by little variation in the swell stress after 1730 hours. In this segment, the average value of the swell stress measurements is 0.0719Mpa and the maximum value is 0.0729Mpa. It is suggested that the swell stress is mainly raised by water entering the pores among montmorillonite particles and the interstitial layers in individual montmorillonite crystals, leading to an increase in volume and manifested as a stress on the surrounding materials.

Jan 1, 2006

By D. J. Droppert

This paper describes the precipitation-production of crystalline scorodite (FeAs04.2H20) from arsenic-rich sulphate-based metallurgical solutions at ambient pressure (95°C). Arsenic is precipitated by means of a controlled precipitation technique in which the supersaturation of the solution is carefully controlled. By controlling the supersaturation in the presence of seed material. the formation of amorphous ferric arsenate is prevented. Scorodite is known to be the most stable As(V) compound and is therefore preferred as host mineral for arsenic immobilization. The effect of the following parameters on the preCipitation behaviour and kinetics of scorodite are discussed: Type of base seed concentration initial [As]. sulphate concentration. neutralization rate. seed recycling and method of Fe(ll!) addition to Fe-deficient arsenic solutions.

Jan 1, 1996

By Zdzislaw Miczkowski

At KGHM Polska Miedz S.A, a direct flash smelting process is used for smelting of chalcocite concentrate for the production of blister copper. The paper presents a model of complex oxidation process of single concentrate grains smelted at KGHM. The description covers main chemical reactions, phenomena of heat and mass exchange inside the grains and between a grain and the surrounding space. In the model, two zones describing the course of process inside the grain were distinguished: ? The first one, which moves faster towards the centre of a grain, both organic and carbonate carbon are freed, The process takes place without the presence of oxygen and results in an increase of the temperature in the core of the particle. ?The second zone moves slower into the grain and the rate of the movement is determined by the presence of oxygen, In that zone the sulphur is eliminated and the oxidation of the organic compounds vapours moving from deeper layers of a grain takes place. Based on the results of laboratory tests, the coefficients that describe the oxygen transportation into the grain and decide the progress in the chemical reaction were determined, The paper contains the results of model calculations for single grains reacting in environment of various content of oxygen as well as the results of model calculations for the laboratory reactor system.

Jan 1, 2003

By Xiangru Chen, Qijie Zhai, Wei Zhang, Haicheng Li, Chao Yang

In this paper, ductile iron material with different content of niobium was prepared by a scientific melting method. Image Analysis Software was used to studied the effect of niobium microalloying on both pearlite content and pearlite lamellar spacing in ductile iron quantitatively. The results showed that the addition of a small amount of niobium could increase the pearlite content and decrease pearlite lamellar spacing of ductile iron effectively.

Jan 1, 2015

By Micheal McCarter, Biswadeep Saha, Meenakshisundaram Ramanathan, Chai Ren, Sivaraman Guruswamy

"Three-point bend test was used to study the effect of electrochemically charged hydrogen and magnetic field on the embrittlement behavior of AISI 4340 steel in this work. Acoustic emission signals were collected during the test and analyzed to gain an understanding of the crack growth process. Cathodic hydrogen charging in AISI 4340 steel resulted in drastic reduction of ductility and strength. Hydrogen embrittlement was characterized by a change in fracture surface from dimpled ductile surface to quasi cleavage type fracture. No significant effect was observed in the presence of magnetic field. The acoustic emission signals collected during the test provided an indication of the extent of energy released during the crack growth process.*Support of this work by NSF through the award DMR-0854166 is gratefully acknowledgedIntroductionGrowing interest in hydrogen as a clean fuel and use of steel and other iron based alloys for storage and transport of hydrogen has led to extensive study of the influence of hydrogen on the mechanical properties of these alloys. Hydrogen interaction with materials may result in degradation of mechanical properties. Embrittlement, either ductile or brittle, can be described as a condition which decreases the toughness of the material or increases the ease of crack growth. Hydrogen present even in few parts per million is sufficient to embrittle steels at room temperature [1]. In most cases, hydrogen exposure is through an electrochemical process in aqueous corroding environments. In such cases, they are prone to be exposed simultaneously to electrically induced magnetic fields, which are also believed to affect the hydrogen embrittlement susceptibility of these alloys. So it is also important to study the effect of magnetic field on the hydrogen embrittlement susceptibility. Hydrogen solubility by electrochemical process in aqueous solution is proportional to square root of current density for iron. [2,3]"

Jan 1, 2012

By Zdzistaw MiGzkowski

At KGHM Polska Miedi S.A. a direct flash smelting process is used for smelting of chalcocite concentrate for the production of blister copper. The paper presents a model of complex oxidation process of single concentrate grains smelted at KGHM. The description covers main chemical reactions, phenomena of heat and mass ex-change inside the grains and between a grain and the surrounding space. In the model, two zones describing the course of process inside the grain were distinguished: ? The first one, which moves faster towards the centre of a grain, both organic and carbonate carbon are freed. The process takes place without the presence of oxygen and results in an increase of the temperature in the core of the particle. ? The second zone moves slower into the grain and the rate of the movement is deter-mined by the presence of oxygen. In that zone the sulphur is eliminated and the oxidation of the organic compounds vapours moving from deeper layers of a grain takes place. Based on the results of laboratory tests, the coefficients that describe the oxygen transportation into the grain and decide the progress in the chemical reaction were determined. The paper contains the results of model calculations for single grains reacting in environment of various content of oxygen as well as the results of model calculations for the laboratory reactor system.

Jan 1, 2003

By Xiaojie Gao, Shufeng Yang, Jingshe Li, Chengsong Liu

In the blast furnace process, the dust entrained in the blast furnace gas enters into the down-comer, flows through the gravity dust separator (to eliminate coarse particles) and then is collected in a bag-house. The powder collected by the baghouse is called bag dust, while both fractions are called blast furnace dust whose main components are C and Fe. The dust also contains small amounts of nonferrous metals such as Zn and Pb, which have some value. Also, due to the small particle size and low density the dust is easily suspended in air and so can endanger human health. Therefore it is necessary to develop a process to both treat the dust to recover the metal values and to dispose of the residue – preferably by recycling to the blast furnace itself via the sinter strand. These objectives will result in good economic, environmental and social benefits [1].

Jan 1, 2014

By Naiyang Ma

"High oil concentration is one of the major barriers for recycling of mill scale of steel hot rolling mills. It is of vital importance to find cost-effective technologies of reducing oil concentration in mill scale in order to recycle the mill scale without causing detrimental effects on production and environment. This paper discusses in-process separation of mill scale from oil at steel hot rolling mills. Formation of mill scale and status of oily wastewater at hot rolling mills are reviewed in the first place. A mathematical model is then formulated to relate oil concentration in mill scale to physical properties of mill scale, chemical and physical properties of wastewater and interacting parameters between mill scale particles and wastewater. From this model, three approaches of in-process separation of mill scale from oil are derived: (1) avoiding contacts between mill scale particles and oily wastewater, and (2) maintaining low oil concentration in wastewater, and (3) collecting mill scale in upper streams of wastewater flows. In-process separation of mill scale from oil might have advantages of lower capital cost, lower operating cost and less additional environmental concerns, compared to other strategies of separating mill scale from oil.IntroductionHot rolling is an inevitable step in producing finished steel products. Figure 1 schematically shows a steel hot rolling process. Semi-finished steel products, slabs here, are reheated first, and then the reheated slabs are discharged from the furnaces and transported on hot rolling trains to descaling units for removing scale with pressurized water. After being descaled, the slabs are rolled by roughing mills. After treated with cropping and the second descaling, the slabs are finally rolled into finished products, coils here, by finishing mills."

Jan 1, 2012

By Jianhua Xin, Min Chen, Cuihuan Huang, Shan Yu, Xiaoao Li, Nan Wang, Guanghao Chen

Copper enrichment behavior in continuously cast slab induced by scale formation after continuous cooling in H2O vapor atmosphere and consecutively in air has been experimentally investigated by combining with SEM-EDS analysis, for the purpose to examine the effects of initial slab surface temperature and contents of copper and nickel. For Slab 1 with copper content of 0.1 percent, no visible copper enrichment is found at scale-substrate interface irrespective of the various scale microstructures formed at different initial slab surface temperatures. For Slab 2 with higher contents of copper and nickel, copper-rich phase accumulates and stays at scalesubstrate interface under the condition of lower initial slab surface temperature; while Cu-rich phase in the porous scale formed at higher initial slab surface temperature is noted with simultaneous Ni-enrichment appearing in front of the steel-scale interface. Both a porous scale and high nickel content work together to provide pores for copper-rich phase migration away from interface and occlude within the scale layer.

Jan 1, 2016