By Chang Wei, Zhigan Deng, Jiqiang Liao, Minting Li, Hongsheng Xu, Yan Song, Cunxiong Li, Xingbin Li

"Abstract: Direct ?otation of oxidized zinc-lead ore is characterized by recovery of zinc and lead only around 55% and 50%, respectively. Mineralogical analysis shows that the sample used in the present study is a carbonate hosted zinc-lead ore, with a zinc and lead carbonate content that accounts for 80.14% and 75.63% of the total minerals, respectively. The carbonate hosted zinc-lead ore was hydrothermally sulfidized with elemental sufur and the experimental data indicated that under the conditions employed up to 75% zinc and 82% lead sulfidation extent were achieved. As a result of pre-sulfidation followed by flotation, the recoveries of zinc and lead into flotation concentrate were over 90%. A flotation concentrate was obtained with 52% Zn and 37% Pb from the materials which was treated by sulfidation.IntroductionSulfide ores are the primary source of zinc and lead, and they are becoming depleted; thus, metallurgical investigators are interested in using abundant oxidized zinc-lead ore reserves. The high-grade zinc-lead oxidized ore, which normally has a zinc content higher than 15%, can be disposed of by acid leaching and electrolysis. However, the low-grade ore, which has a zinc content lower than 10%, is difficult to smelt with pyrometallurgy and hydrometallurgy, and the processes are very complicated and expensive in terms of production flow and energy consumption. Therefore, making the low-grade oxidized zinc-lead ore more beneficial has become more important in recent years. Flotation is the most common process, and the primary method of recovering zinc and lead from sulfide or oxide minerals. It is well known that there is a difference between sulfurized and oxidized minerals regarding their separation by flotation. Flotation of zinc and lead oxidized minerals is extremely complex because of the similarities in the physicochemical and surface chemistry of the constituent minerals. There are no known direct-acting collectors capable of producing single metal concentrates [1-3]."

Jan 1, 2012

By Sheng-li Wu, Guo-liang Zhang, Bo Su

One of the major challenges for the Canadian Gen IV Super-Critical Water-cooled Reactor (SCWR) concept is the selection of fuel cladding materials. The Canadian SCWR concept will operate at a core outlet temperature of 625 oC and 25 MPa of pressure with peak cladding temperature reaching as high as 800 oC. Corrosion resistance is an important factor for material selection. Austenitic stainless steels that contain Cr contents greater than 18 wt.% are generally considered to provide adequate corrosion resistance. In this work, the pressure dependence of the corrosion of austenitic stainless steel 310 containing 24 wt% Cr is assessed at 625 C for exposures of 1000 hours to evaluate the suitability of superheated steam as a surrogate for supercritical water at 25 MPa. Transmission Electron Microscopy (TEM) revealed that 310 exposed to different pressure conditions at 625 oC. (i.e., 0.1, 8 and 29 MPa) had generally the same type of the oxide structure, i.e., a Cr-rich oxide with the spinel structure on outer surface adjacent to the water phase. The material exposed at 8 and 29 MPa had a double layer oxide structure, with the outer oxide layer having a much larger grain size, while the samples exposed at 0.1 MPa showed only a single spinel-phase oxide layer. Cr-depleted recrystallized austenite grains were found underneath the spinel phase oxide. The adjacent large-grained austenite substrate had M23C6 carbides in the grain interior. The implications of these results are discussed.

Jan 1, 2015

By Wolfgang Van Hooff

Encouraged by a strongly growing and evolving market for granulated products, Paul Wurth continuously improves its granulation and dewatering technologies to provide customers with state of the art installations. Continuously developed know-how about the granulation process of iron blast furnace slag enabled application to non-ferrous materials such as Ni-Slag, Pb-Slag, Blister Copper, Cu-Matte and even TiO2-Slag, which rank among the most difficult materials to granulate. This paper identifies how critical objectives in granulation and dewatering technologies applied to different molten materials with respect to various product quality objectives can be addressed. The differences between hot and cold water granulation systems are explained, including the step from cold runner to granulation water tank. Development of a flow and pressure controlled blowing box is the latest step to optimize the granulation process in order to meet the latest standards in terms of quality, power consumption and environmental protection.

Jan 1, 2006

By Zhou Shu-cai

"A method has been proposed for the pre-treatment of high phosphorus iron ore by carbothermic reduction assisted with microwave irradiation and magnetic separation on a laboratory scale. Chemical analysis of the reduced ore sample, the metal sample and the slag sample were conducted. Based on the above research, the influences of carbon addition, microwave power and microwave irradiation time on the recovery of Fe and dephosphorization were discussed. It indicated that the increase of microwave irradiation time and power had substantial effect on the recovery of Fe while the influence of carbon addition was not obvious and the highest iron recovery ratio reaches some 95.5% when the dephosphorization ratio was 37.68%. A high iron recovery ratio and a reasonable dephosphorization rate were incompatible under the conditions investigated in this study due to the reduced iron and because unreduced P-contained gangues were not efficiently separated. This method may provide a reference for the future utilisation of high-phosphorus iron ore.IntroductionWith the rapid growth of crude steel production in China, the source of iron ore tends to become increasingly strained and is facing the risks of raw material shortage for the iron and steel industry. In order to decrease the production cost, China has to focus on the utilization of its domestic low grade iron ores for the iron and steel plants [1-2]. China has a large deposit of high phosphorous iron ore with a reserve of 7.45 billion tons which is unused in any large scale [3]. Therefore, the development of a successful and economically viable technology for high phosphorus iron ore is of profound importance. To remove phosphorus from the high phosphorus iron ore, several mineral and metallurgical processes have been proposed, such as bio-leaching [4], roasting reduction plus melting separation [5], pre-reduction and screening methods combined with mechanical crushing or air jet milling[6] selective agglomeration plus reverse flotation [7]. However these processes are not cost effective or are time consuming. The traditional pyrometallurgical process( BF+ BOF) refuse this kind of ore mainly because that molten iron is saturated with carbon or high carbon content and thus all phosphor us in the burden goes to the molten iron[8]. Therefore, it is important to exploit the cheap and abundant high phosphorus iron ore as a resource in ironmaking. In recent years, the microwave was widely introduced as a heat resource for extractive metallurgy of iron ore or other minerals. For example, microwave assisted ore milling, microwave assisted carbothermic reduction of metal oxides and microwave assisted mineral leaching issues[9-10]"

Jan 1, 2014

Physical and chemical methods were investigated to tower thorium levels in Eneabba Ilmenite from the natural levels of 180-500 ppm to give Becher Process synthetic rutile with less than 100 ppm thorium. Chemlcal treatments, but not physical separations were successful. A pilot plant trial of a sodium hydroxide leach (25M NaOH at 75°C and 40 wt% solids for Ih) followed by a sulphuric acid leach (3M H2S04 at 90°C and 60 wt% solids for 211) confirmed that thorium could be removed to below 100 ppm. However, the activity of the ilmenite was not lowered to the same extent

Jan 1, 1996

By J. Riccardi

Copper refineries use massive copper castings as moulds into which impure molten copper from the reverberatory furnace is poured to form anodes for further electrolytic refining. To facilitate removal of the copper anodes from the mould and to prolong the life of the mould itself, it is traditional to spray the mould surface prior to each use with a slurry of baryte in water. This slurry application leads to poor housekeeping, operating costs are escalated by the cost of the slurry, and additional problems in the subsequent refining process are experienced due to carry-over of excess undesirable baryte powder. A one-time application of a diffused layer of aluminum to the surface of the copper mould prior to putting the mould into service has been found to provide extended mould life and facilitate anode removal, as well as reducing baryte consumption; thereby reducing operating costs at both the anode manufacturing and refining stages.

Jan 1, 1999

By R. P. King

The linear intercept distributions provide unambiguous and accurate characterizations of the texture of mineralogical materials. The relation between the measured linear intercept distributions and the spatial correlation function is shown to be given by: in the Laplace Transform domain. The linear intercept distributions of the two phases in a low- grade chromite-serpentinite ore were measured. and the spatial correlation functions for both phases were evaluated using the above relation. The correlation functions are the primary relations for integral geometric models of mineralogical texture and this work demonstrates the relation between the 10 stereological model and the 3D integral geometry model for mineral liberation.

Jan 1, 1991

By Behrouz Abedian, Livia M. Racz

"We address dynamic interactions between high-energy, reactive surfaces of polymer-matrix composites and solid surfaces. A common characteristic of these interfaces is that bonding occurs readily upon contact. In many industrial and biomedical applications, it is desirable to suppress this bonding phenomenon. This interfacial effect is discussed in light of the development of our new method of handling polymer-matrix composites in dental applications. This method involves vibration of the solid-polymer interface at different frequencies. For each material, there is a critical frequency at which the sum of the viscoelastic and inertial energies of the fluid at the surface exceeds the energy available for bonding. When the polymer is vibrated at or beyond this frequency, it does not adhere to solid surfaces. An important aspect of the developed process is that it can be used to characterize surface and interfacial properties of polymers under dynamic conditions, whereas existing techniques are restricted to the study of bulk dynamic properties.IntroductionThe purpose of this paper is to report on the development of a new method for manipulating polymer-matrix composite materials used in dental applications, and the potential of this process for use in materials characterization. The materials under discussion have polymer matrices of a combination of bisphenol A-glycidyl methacrylate (BIS-GMA) and triethylene glycol dimethacrylate (TEGDMA), and contain filler particles of silica and/or zirconia glasses. These materials are called direct aesthetic restorative materials, and are used for filling of cavities, repairing chipped teeth, and for other restorations in which appearance is of importance. They have the appearance of natural tooth material, and are therefore in great demand for use in the anterior portion of the mouth(l,2)."

Jan 1, 1998

By Ken-ichi Machida

"Surface modification of R-Fe-N intermetallic compounds was made to improve their magnetic property and nitrogenabsorbing ability, arid high-performance resin-bonded magnets and nitrogen storage materials were developed: Surface coating for Sm2Fe11Nx by the zinc metal produced via photodecomposition of Zn(C2Hs)2 was effective to avoid the further oxidation in the molding process of the fine powders for bonded magnets and the resulting (BH)max values were improved to -186 kJm-3. Meanwhile, R2Fe17 as the mother compounds for RzFe11Nx was highly active for decomposition of NH3 molecule and subsequent nitrogen absorption as metal nitrides. Furthermore, even inert Nz molecule was dissociated on them by impregnating Ru metal and the resulting nitrogen atoms were absorbed in the crystal lattice of R2Fe17. These results demonstrated that the nitrogen storage system was established by cycling the nitrogenation and hydrogenation of RzFe11/R2Fe11Nx materials.IntroductionProcessing for rare earth metals and intermetallic compounds requires well-controlled conditions in order to avoid the oxygen contamination involved in it due to their high reactivity, as causes the serious damage for materials such as magnets, metal hydride for hydrogen storage, and so on. Rare earth-iron intermetallic compounds, R2Fe17, provide the corresponding metal nitrides (R2Fe11Nx) by heating in N2 or a mixed gas stream ofNH3-H2 [l] and, among them, Sm2Fe11N3 has been particularly noted as one of the promising materials for high-performance permanent magnets such as bonded ones [2- 6]. Usually, the nitrogenation for Sm2Fe17 is made in Nz, but it needs the much more hard conditions of reaction pressure (-10 MPa), temperature (-550°C) and time (-72 h) than the nitrogenation in the NH3-H2 mixture [l]. In the latter case, a significant amount of nitrogen can be interstitial introduced in· the R2Fe17 crystal lattice (x=-7) under the more moderate conditions than in N2 (at 0.1 MPa and -450°C for -3 h) [3-6] and then, in a similar manner as metal hydride systems [7], the excess nitrogen in RzFe1 7Nx (x>3) is reversibly desorbed by heating at a temperature around 500°C in Ar to form the RzFe11N3 compounds. This behavior of nitrogen absorption and desorption has a close relation to the sites for nitrogen in the crystal lattices."

Jan 1, 2000

By Wei-ling Wang, Ryosuke O. Suzuki, Xiang-ning Meng, Miao-yong Zhu

"A finite-element thermal-stress model of continuous casting mold is conducted to predict deformation of copper plates and its change with different cooling structure. The results show that deformation behavior of copper plates is mainly governed by cooling structure and thermal- mechanical conditions, deformation amount is related to structure geometry, and a small deformation mutation occurs in cooper-nickel boundary due to different properties. The maximum deformation of hot surface centricities of wide face locate at 100 mm below meniscus and that of narrow face locate at meniscus and terminal of water slots and significant curvature fluctuations on both sides of copper-nickel boundary. The maximum deformation of centricities is increased up to 0.05 mm with thickness increment 5 mm of copper plates, and maximum deformations are only depressed 0.01 mm and 0.02 mm with increments of 1 mm nickel layer thickness and 2 mm water slot depth respectively.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipate in primary cooling zone and make continuous casting mold under enormous heating load giving rise to thermal stress, deformation, high-temperature fatigue and creep not only depress mold life-span, but reduce casting stability [1] Many studies focused more on heat transfer, solidification and shrinkage of solidifying shell to provide inverse proposals for optimizing cooling system and even designing new taper of mold [2,3], but it is generally useless to those of having been manufactured or being put into production. Therefore, mold-related forward problems show necessity to be discussed deeply, and stress and deformation distributions based on special thermal conditions in mold should be analyzed in order to explore suitable cooling structure of mold directly. Samarasekera et al. [4] examined heat flow and distortion of two-dimensional longitudinal sections and investigated effect of cooling water velocity, copper plates thickness and carbon content on formation of rhomboidity and longitudinal comer cracks. O'Connor et al. [5] developed a three-dimensional mathematical model to compute thermo-mechanical state in thin-slab mold and calculated temperature and deformation of mold wall to assess roles of various process parameters on impacting mold life. Thomas et al. [6] predicted temperature, distortion and residual stress in mold and indicated increased distortion requires increased remachining, which reduces mold life and increased residual stress increases the probability of a catastrophic crack failure. Park et al. [7l determined heat-flux profiles in funnel-shaped and parallel thin-slab molds based on an inverse heat conduction model and thermocouple temperature measured in-plant and put them into three- dimensional finite-element thermal-stress model to predict temperature, distortion and residual stress of mold wall. Korie et al. [SJ focused on prediction of temperature, distortion and residual stress in mold and in particular to clarify that mold life is significantly affected by temperature and its rigidity, but little effect by mechanical including clamping force, bolt prestress, friction and ferrostatic pressure. Meng et al. [9l predicted temperature and thermal stress in a slab mold and analyzed effect by cooling system geometry and casting speed quantitatively. In present study, a three-dimensional finite-element thermo-mechanical model with type-switched element is transformed from previous heat-transfer finite-element model [9l, and mold deformation is simulated in order to shed light on thermo-mechanical behavior with special thermal conditions and different mold geometry at high casting speed."

Jan 1, 2013

By Michael S. Moats, Scott C. Campin, J. Brent Hiskey

"Electrochemical techniques are a valuable means of analyzing the passivation of commercial copper anodes. Electrochemical impedance spectroscopy (EIS) provides information concerning transport and reaction phenomena occurring at an electrode surface. Commercial. copper anodes of varying compositions have been examined using EIS. Experiments were conducted in a flat cell with an electrolyte of 40 gil Cu2 + and 160 gil H2S04 maintained at 65 DC. Impedance spectra were obtained at the potentials characteristic of the open circuit voltage and passive region for each anode. The spectra of the passivating films exhibited a flattened resistive/capacitive loop at middle to high frequencies and an inductive loop at low frequencies. An equivalent· circuit utilizing an inductor-resistor series in parallel with the double layer capacitance and charge transfer resistance was adequate in modeling the impedance data. The influence of anodes impurities on the components of the equivalent circuit is discussed and correlated with a hi-layer passivation model.IntroductionPassivation of copper anodes during industrial electrorefining has received considerable attention in the past few decades. Great strides have been made in understanding the roles of anode impurities [1-25], electrolysis parameters [20,26], and electrolyte chemistries [20,26]. Even so, passivation still occurs even in the most modem of refineries. The exact cause of passivation is not fully understood. It is known that the anode surface becomes covered by a passivating film. This film has been proposed to be CuS04'&5H20, Cu20, or mixed oxides. The localized concentrations of Ft, Cu+, and Cu2+ ions determines which phase is more favorable. The presence of these ions is controlled by the reaction kinetics and diffusion of species through the slimes layer.Reaction kinetics between Cu, Cu +, and Cu2+ are based on the dissolution mechanism of copper. There exists four different models to describe the dissolution of pure copper. The classical model of Mattsson and Bockris [27] involves two single electron transfers with the cuprous-cupric reaction being the rate detennining step. More recently, Wong, Collier, and MacFarlane [28] used ac impedance to elucidate a more complex mechanism involving the affect of pH and anions. Their findings indicate that the formation of cuprous ions in solution, Cu(I)so~ is favored over Cu(1I) ions adsorbed to the electrode surface in the presence of sulfate and as pH increases from pH 1 to pH 5."

Jan 1, 1997

By Priscilla Aki Mori de Hanashiro, Viviane Tavares de Moraes, Denise Crocce Romano Espinosa, Hugo Hashimoto

"The LCDs are used in televisions, calculators, mobile phones, computers (laptops and tablets), video games and other electronic devices. The advancements in technology make obsolete these devices, causing excessive disposal of LCDs and therefore decreasing life span of landfills. In this context, the LCDs from LED LCD TVs arise as an additional source of waste electrical and electronic equipment (WEEE). Thus, it is essential to develop LCDs recycling methods, beginning with the LCD characterization followed by displays processing, aiming the materials separation and using some Ore Treatment Techniques, and finally, the recovery of indium using acid leaching. The analysis methods that will be used in this work are: Fourier Transform Infrared (FT-IR) and Inductively Coupled Plasma Optical Emission Spectrometry (ICP-OES).IntroductionLiquid Crystal Display (LCD) technology is applied in modem televisions, calculators, mobile phones, computers and a wide range of electronic devices. It has replaced Cathode Ray Tube (CRT) technology as the most advantageous display product, due to lower electrical power consumption, size and weight reduction, and no radiation emission [ 1]. The constant improving of LCD screen technology reflects on its growing contribution to the amount of waste electrical and electronic equipment (WEEE): an estimated 50 million tons of WEEE are produced every year [2]. Once the most common method of its disposal are landfills, the LCD technology therefore became an environment issue [3].LCD structure is composed by components made by different materials. In order to develop a LCD recycling methodology that gives the right destination to these materials, a previous characterization stage is required. This characterization includes a disassembly process and material identification analysis. One of the LCD components is the screen, which is composed by polymeric and glass layers. The liquid crystal glass was the starting material of this study. It contains indium in the form of indium tin oxide (ITO) film. This ITO film is deposited in the glass by a sputtering process and acts as the electrode material [4,5]. It has in its composition 90% ofln203 and 10% ofSn02 [6]."

Jan 1, 2014

By J. M. Shneerson

At Gipronickel Institute a technological flowsheet of pressure leaching of copper from rich copper concentrates (i.e. containing: Cu -59-75%; Ni -D.5-4.64%; Fe -D.2-J.3%; S -21.8-26.9%) was developed. As a result, the possibility of deep decomposition of copper-containing minerals with extraction of elemental sulphur (up to 90-95%) was established. The obtained sulphur concentrates contain 80-90% of elemental sulphur, which can be separated from sulphide residue through autoclave melting and settling. As a rule, sulphide concentrates remaining after extraction of sulphur contain up to 1-2% of noble metals. The sulphide concentrate can be purified to the level of rich concentrates or pure metals using the well-known methods as in the case of tankhouse slimes. The presented research specifies the parameters of main operations: pressure leaching and sulphur extraction. It was established that 98% of copper could be transferred into solution at temperatures of 108-1 10°C and oxygen partial pressure 0.4-0.6 MPa. Experiments were carried out in autoclaves of various volumes using the products of nickel matte processing.

Jan 1, 2003

By Hideyuki Itou

Municipal wastes are mainly incinerated in Japan. Both bottom ash and fly ash from the incineration treatment are smelted recently to decrease the volume. Direct smelting of municipal wastes is also becoming popular. The smelting treatment generates fly ash which contains concentrated heavy metals such as Zn, Pb and Cu, and the harmfulness is causing concern. The smelter fly ash is mainly landfilled after stabilization. An effective treatment process of the smelter fly ash is required to recover the metals. For the treatment process, an application of chloridizing volatilization technique is considered. Chloridizing volatilization experiments were carried out to determine the effects of various factors on the volatilization behaviors in this study. A pretreated ash was mixed with a main raw material which mainly consists of hematite. Calcium chloride water solution was added into the mixture. The mixture was pelletized, dried and used as samples for the volatilization experiments. The sample was placed in the reaction tube heated in an electric resistance furnace. 5%02-95%N2 gas with controlled humidity was introduced into the reaction tube. Effects of humidity in the carrier gas, addition of calcium chloride and mixed ratio of the ash to the main raw material were investigated on the volatilization of Zn, Cu and Pb. To determine the volatilization behavior, samples were taken from the furnace at specified temperatures on the heating stage. In addition, experiments at specified holding temperatures for 15 minutes with shortened heating time were conducted. The two series of experiments revealed the effect of heating temperature on the volatilization behavior of Zn, Cu, Pb and Cl.

Jan 1, 2006

By Hazoor Singh Sidhu

Materials degradation due to corrosion is the major problem in power generation equipment, gas turbine, fluidized bed combustion, industrial waste incinerators etc. Some super alloys have been developed, but they are unable to have different properties to meet the demand of today?s industry. Therefore, a composite system of a base material providing the necessary mechanical strength with a protective surface layer different in structure and/or chemical composition can be an optimum choice in combining material properties. Thermal spray coating of the components before they put into service by suitable surfacing alloy and with suitable coating method can increase the life of these components several fold. Choice of right coating method and alloy for a particular application is extremely important to get the desired service life. The corrosion of some materials and the role of HVOF thermal spray coatings to counteract the same have been reviewed, with an aim to understand the phenomena along with various applications.

Jan 1, 2006

By M. Ide, K. Takemura, S. Taenaka, K. Shinzawa

"The laser characteristic is strongry dependent upon the stoichometry of forsterite (Mg2Si04) and YSO (Y2Si05) single crystals, because of change in the valency and occupied sites of doped Cr in the lattice so that mole ratios of Mg0/Si02 and Y203/Si02 in the above single crystals must be precisely analyzed. In this study ICP-AES was applied for analyzing the mole ratios. Emission intensities corresponding to Si and Mg or Si and Y were measured at the same time with internal standard method. Preparation of sample solutions, measurement conditions of ICP-AES and interferences by coexisting components were discussed, resulting in excellently precise detennination of stoichometry of the above single crystals.IntroductionIn conventional stoichiometric analysis of single crystals, the stoichiometry is detennined by analyzing each component separately with titrimetry and gravimetry techniques. On the other hand, by stoichiometric analyses using ICP-AES, emission intensities corresponding to components are measured at the same time with internal standard method. Consequently erros caused by variation of analytical condition are canceled out.Cr-doped Mg2Si04 and Y2Si05 syngle crystals are known as laser materials. The change of valency and occupied sites of doped Cr affect the characteristic of single crystal as aleser materials. The change of state of doped Cr.Stoichometric composition of Mg2Si04 is constructed by 2mole of MgO and 1mole of Si02, and Y2Si05 is constructed by 1mole of Y203 and 1mole of Si02. In this study, required analytical precision in component mole ratio is within an error of 0.0010 for Mg2Si04 (CV=0.05wt%), and within an error of 0.0030 for Y2Si05 (CV=0.05wt%) (Table I )."

Jan 1, 1998

By Bruce W. Wessels

"Metal-organic chemical vapor deposition has been shown to be a highly versatile technique for the synthesis of complex oxides. High dielectric constant oxide thin films of SrTiO3, BaTiO3, Ba1-xSrxTiO3 and SrxBa1-xNb2O6 can be be be deposited at 800 ºC with this technique. The fluorine substituted B-diketonate precursors have been shown to be well-suited for the deposition of high quality, epitaxial thin films of these materials.IntroductionThere has been a resurgence of interest in thin film ferroelectric oxides as a result of the development of techniques to deposit high quality material. Both physical and chemical vapor deposition techniques have been realized. Of the chemical vapor deposition techniques, metal-organic chemical vapor deposition (MOCVD) has received the most interest for the deposition of ferroelectric oxide thin films. This results, in part, from the availability of a number of volatile metal-organic precursors.(l) Moreover, MOCVD offers the advantages of high growth rates, uniform coverage over large areas, conformability, abrupt interfaces and excellent epitaxial crystallinity. Of the metalorganic precursors, the B-diketonate complexes have played an important role especially in the deposition of ferroelectric oxides containing alkaline-earth metals such as BaTi03 and Ba1•XSrxTi03. For example, barium tetramethylheptanedionate Ba(thd)2 has been used in the preparation of BaTi03 by MOCVD.(2) These compounds, however, are not without their problems. Ba(dpm)2 has a relatively low volatility; and as a consequence, temperatures in excess of 180·C are required for volatilization. This leads to the necessity of a complex precursor delivery system to insure that the precursor does not condense before the reaction zone. Moreover, the Ba precursor tends to oligomerize leading to a decrease in vapor pressure as well as a problem with reproducibility. To counter these problems, novel liquid source and solid source precursor delivery systems have been developed. (3)(4)"

Jan 1, 1994

By C. B. Piazzarollo

Red Ceramic materials are widely used in Civil Construction in Tropical Countries. However, these materials have high porosity and low mechanical strength. Thus, in order to improve these properties, recycle mineral wastes was incorporated into clay from Campos - RJ, ornamental rock waste, from the gneisses cutting of Cachoeiro - ES, 150 km from Campos. After the addition of up 10% of waste in clay mass, ceramic pieces were produced and subjected to the tests of porosity (P) and flexural strength (FS). The test material contains 53.3% clay and 67% waste slit. The X-ray diffraction identified the presence of kaolinite, quartz and feldspar for the clay and, for the waste, quartz and orthoclase. The results of FS and P showed that the residue influenced, positively, the ceramic piece, with strength gains especially from 920º up to 960°C.

Jan 1, 2015

By Kamal Adham

Hydrochloric acid is used as lixiviant in such hydrometallurgy processes as synthetic rutile production and nickel extraction. The intermediary metal chloride is normally roasted to release gaseous HCl and a solid metal oxide. A large amount of fuel is required for this thermal regeneration, mainly to vaporize the water content of the feed solution. To conserve fuel, some energy recovery from the off-gas is currently achieved, but the fuel costs can further be reduced by process optimization and energy recovery from the gaseous, aqueous and solid products of the regenerator. Here, first the existing limitations to fuel efficiency in the industrial scale HCl regeneration roasters are described. Then, for the case of a dilute feed solution, options for pre-evaporation and fuel minimization are modeled and compared. Finally, energy recovery technologies including heat pumps, acid heat exchangers and solid waste heat boilers are described, and their potentials as the heat source for pre-evaporation of the feed are evaluated.

Jan 1, 2003

By Byung-Su Kim

The recovery of elemental sulfur from sulfur dioxide has important implications for coal- burning power plants and nonferrous metal smelters. The thermodynamic analyses showed calcium sulfide to be suitable for recovering elemental sulfur from sulfur dioxide. At the temperatures of 1023 to 1153 K under the sulfur dioxide partial pressures of 5.0 - 60.1 kPa, elemental sulfur from sulfur dioxide was recovered by its reaction with calcium sulfide. The kinetics of this reaction were measured at the same conditions using a thermogravimetric analysis technique. This reaction scheme would be attractive if the coproduct calcium sulfate can be reduced to regenerate calcium sulfide. This is the topic of another paper. At 1073 K under the sulfur dioxide partial pressure of 25.8 kPa, 48 % of the original calcium sulfide was converted to calcium sulfate in an hour. Under the same conditions, 55 % of the regenerated calcium sulfide were converted to calcium sulfate in an hour even after third regeneration.

Jan 1, 1999