By M. I. Novgorodova

Most of the gold in the earth's crust occurs as finely-dispersed gold and accounts for much of the gold lost in extraction processes and during exploration for gold. The Compositions, sizes, and morphology of fine gold particles (0.01 to 10 ~m in diameter) were studied with high resolution electron microscopy coupled with electron microprobe and microdiffraction devices, using colloidal carbon replicas. Correlations were made between fine gold, mineral associations and ore genesis. The results provide qualitative information on the proportions of finely dispersed, invisible and visible gold distribution in ores. Such knowledge is fundamental when planning an optimum technological recovery process.

Jan 1, 1991

By Germán Richter a

To comply with the chilean air quality regulation requirements, the Hernan Videla Lira Smelter which is a custom smelter having to cope with a wide variety of concentrates, has developed a two-step modernization plan. The main steps are: - A second acid plant of 80,000 Nm3/hr to be operating at the end of 1996. This will increase the sulphur capture from 43% to 701/o in association with the replacement of the Hoboken converter by a second PS-converter to reduce the operation problems resulting from the treating of high garde matte. - Oxygen enrichment, is going to be incorporated in 1998 in the Teniente Converter and PS-converters in association with tuyere injection of dry concentrates, increasing the sulphur capture to 90 - 93% of sulphur inputs. By this program, sulphur emissions will be decreased from 40,000 tpy today to less than 8,000 tpy and in this way to carry out the environmental regulations.

Jan 1, 1996

By Elli Nurminen

Fouling of heat recovery process equipment may significantly decrease their heat transfer efficiency. In Copper Flash Smelting process flue dust tends to form build-ups on the heat recovery boiler walls. Thermal transportation properties of copper flash smelting flue dust and its components have been studied. The effects of porosity and temperature on thermal transportation properties have also been determined. The results indicate that dust and its components are effective thermal insulators and build-up layers on the boiler walls are likely to decrease greatly the heat transfer efficiency of the boiler. Decreasing dust layer porosity has a strong increasing effect on thermal conductivity and increasing temperature has a slight decreasing effect on thermal conductivity. The results may be used in CFD-modelling and optimisation of the process.

Jan 1, 2006

Lead blast furnace water-jacket stability was investigated by examining samples from the Port Pirie Lead Smelter. The compositions of the phases formed in the samples were analysed using Scanning Electron Microscopy (SEM) and Electron Probe X-ray Microanalyser (EPMA). Phase equilibria analysis and thermodynamic modelling was undertaken using FactSage with latest thermodynamic database for the slag/matte/metal/speiss/solids multi-component Cu2O–PbO–ZnO– Al2O3–CaO–MgO–FeO–Fe2O3–SiO2–S major and As–Bi–Sb–Sn–Ag–Au minor elements system. Results indicated that the stability of the water-jacket steel wall without freeze-lining is influenced by formation of the complex Fe-rich speiss phase at critical As concentrations. The integrity of the furnace walls with freeze-lining is critically dependent of the stability of the oxide-based freeze-lining which is dependent on various factors including most critical one—the proportion of solids determined by the slag chemistry and fluxing. Thermodynamic modelling of the lead blast furnace operation indicated limiting thermochemical conditions for the water-jacket stability. Factors and controls critical to the water-jackets integrity are discussed.

By Yunyan Wang

Diagrams of pc-pH for the complex ions concentration and pH value and -g- for activity coefficient and ionic strength ln±MnSOI4had been drew based on the thermodynamic principle of coordination chemistry and combined with Pitzer theory at 298.15K. The diagram of -g- indicated that -gincreased sharply from 0.0000 up to 1.2147 when I changed from 0.00 ln±MnSOIln4±MnSO4to 0.09; The increase of -gbecame slowly when I was more than 1.00 and less than 1.69; kept still when I ln±MnSOln4-g±MnSO4was more than 2.25 and less than 4.00. Diagrams of pc-pH illustrated that the minimum solubility of Mn(OH)2(s) increased with the increase of I, the pc increased from 6.5 to 5.5 when I increased from 0.00 to 4.00; The pH of the minimum solubility of Mn(OH)2(s) increased with the increase of I, the pH increased from 11.80 to 12.76 when I increased from 0.00 to 2.89, the pH kept still when I (I was less than 4.0) increased. There is single function relationship between the minimum solubility of Mn(OH)2(s) and relevant pH in different I.

Jan 1, 2010

By Mark William Kennedy

"Electric furnaces containing high quantities of slag are applied in many areas of pyrometallurgy, often for smelting or slag cleaning. A variety of ratios or rules of thumb have been employed in the industry for the dimensioning of these vessels, in most cases with no clear technical basis.In this paper, several design guidelines are presented (electrode size, spacing, vessel dimensions, energy intensity, etc.) as an attempt to provide some technical basis for optimal dimensioning.Furnace heat generation is related to side wall copper cooler heat losses, in an attempt to establish a methodical design strategy particularly for minimum electrode to wall spacing for modern furnaces with cooled linings.Issues regarding the true nature of heat production in a slag furnace are discussed with regards to the possible impact on accurate modeling and design.IntroductionSlag furnaces have passed through a number of design 'generations' characterized by increasing energy intensities, improved electrode technologies and advancing development in their physical structure or 'furnace integrity' as shown in Table I f 1]. A 3rd generation furnace using ultra-high-power (UHP) graphite electrodes is shown in Figure 1, as a generic example of the types of physical structures present in modern slag furnace designs [1]."

Jan 1, 2012

By J. R. Rendón

Cylinders of commercial aluminium alloy 6063 were homogenized under different conditions. The experimental results indicated that the general mechanical behaviour as related to curves of 0.2% yield strength, ultimate tensile strength and Brunnell hardness versus homogeneizing process is the same in both cases. The mechanical properties as compared to those required by plant specifications, tend to be better with increasing values of % Mg2Si in the alloy, as expected. The electron microscopy investigations revealed that in both homogeneizing processes the resulting microstructure consist of significant spheroidizing of the alpha phase (AlFeSi) and fine-needle type structure of beta phase. The alpha phase was also present in a Chinese type scripture. Furthermore, the slow cooling within the furnace resulted in the nucleation and growth of Mg2Si precipitates generally along the grain boundaries.

Jan 1, 1997

By Alexander V. Derevyanko, Victor P. Popov, Alexander I. Raitchenko

"If an electric current flows along some electroconductive suspension in columnar form the solid particles are 'experienced thermal, mechanical, and electromagnetic influences.The objects were suspension Sn (liquid) - Ni-Cr-Mo-W alloy (solid particles). This is refractory alloy on the Ni base. The direct constant current (with density -106 A/m2 ) flowed through the named suspension during 180+300 sec. At the beginning of experiments samples were ones containing particles suspended uniformly in volume. Although density of solid particles was ~9x103 kg/m3 , i. e. higher than density of liquid Sn (-6.8x103 kg/m3 ), after end of this processing, the non-uniform distribution of particles in volume of samples was observed: concentration of Ni-alloy particles in lower part was smaller than their concentration in upper part of samples, and simultaneously their concentration is increased near outer surface. There was probably the natural convection of Benard-Rayleigh type which had carried, so lid particles upwards, and, in same time, there was the action of spatial Lorentz-forces directed to center forcing the radial movement.The knowledge of named phenomena can be useful for elaboration of technology of gradient dispersed materials and development of some materials science fields.IntroductionThe liquid metal with the electric current or under the alternating magnetic field is experienced compression. This action causes the pressure within metal and the change of the surface of the metal column (see, for example, [1-4]). One of results of such an electromagnetic compression is extraction of the foreign solid particles from a cylindrical liquid sample to surface in the radial directions. However, more complicated paths of the inclusions are observed under some conditions of electric treatment."

Jan 1, 1999

By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems are necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed by the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-1 to 102 Pa) at 1573K. The effect of Fe3+/Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By D. J. Cassidy

This document discusses commercial strategies and applications of specialty processing plants for the recycling of nickel, copper, zinc and cobalt bearing by-products. For this discussion, I will focus on materials originating from the metal plating, electronic circuit board· and chemical industries. The review of select processes and the required service, sourcing, material handling, processing and marketing strategies necessary for a successful recycling program are highlighted. Materials discussed in this summary include filtercakes, filters, dusts, spent catalysts, spent solutions and solids. Both pyrometallurgical and hyrometallurgical applications to these materials are addressed. A comparison of targeted finished markets, including smelter feeds and value added products are also reviewed.

Jan 1, 2000

By Tianjiao Luo

The electroless copper plating process for continuous carbon fiber using CuSO4?5H2O as the main salt and formaldehyde as reducing agent was experimentally studied, including the effects of pH values and concentration of chelating agents, stabilizing agents and reducing agent on the electroless plating process. The surface morphology and the composition of coating were investigated by means of Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS), and deposited the coating thickness was measured by way of dissolution. The results indicated that the pretreatment of carbon fiber before plating was so important. This pretreatment could prevent the formation of the black cores, furthermore, it could form many active absorption cores with Ag as the center on the carbon fiber surface. Used the optimized parameters in this process, which led to a stable solution for plating, a homogeneous copper coating was conducted with the carbon fiber plated with favorable mechanical performance and high adhesion strength.

Jan 1, 2006

By Lin Li, Xiang Li, Yifang Zheng, Jilai Xue, Jun Zhu

"Al drops and gas bubbles in the anode-cathode space of aluminum electrolysis cell are of great importance for cell operation improvement in metal loss, current efficiency and energy consumption. A direct observation on the Al drop, gas bubble and ultrasound was carried out through a see-through cell. The Al drop immersed into the cryolitic melt was found moving up and down irregularly in the anode-cathode space without electrolysis, which was then completely dissolved into the melt. During electrolysis, the Al drop came to the anode area and reacted with the gas bubbles generated on the anode. Under ultrasound, the gas bubbles were removed from the anode surface while the Al drop was kept on the side of anode. The observed phenomena were useful for technology improvement in reducing the anode-cathode distance or lowering the energy consumption in aluminum electrolysis.IntroductionDuring aluminum electrolysis, aluminum metal drop and anodic gas bubble are in close contact each other within the anode-cathode space, and the interaction between them can produce significant impact on metal loss, current efficiency and energy consumption. The motions of the Al drop and the gas bubble are also related to the dissolution of aluminum metal into cryolitic melt and the cell voltage drop due to the bubble layer covering the anode surface.A number of studies have been carried out using different types of see-through cells, where the dissolving process of metal Al into cryolitic melts (metal fog) in the anode-cathode space was directly observed and photographed [1, 2]. With the similar method, some direct observations on the anodic bubble behaviors with and without ultrasound were performed during aluminum electrolysis [3-6]. However, to our best knowledge, there is no published work on direct observation on the behavior of Al drops and anodic gas bubbles staying together within the same anode-cathode space, as well as the motion and interaction of them in cryolite-alumina melts."

Jan 1, 2011

By E. A. Thiers

The causes of structural changes in the markets for high technology alloying metals are discussed in terms of technological, economic, and financial trends. Recent market imbalances have affected producers in developed and developing countries differently. Possible response strategies for suppliers in the two types of countries are examined that may alleviate future market imbalances.

Jan 1, 1988

By Shu Yamaguchi

The behavior of halide impurities in pyrometallurgical processes such as Wealtz kiln and MF process has been discussed based on the thermochemical data and the reported data of PbO activity in PbCl2-PbO melts. The role of PbCl(g) has been estimated to be significant in the chloridization evaporation reaction. From reported data on the PbO activity in PbC12-PbO melts, activity of PbCl2 has been calculated by the numerical integration of Gibbs-Duhem equation, and the stability domains and the composition of the liquid phase as well as the vapor pressure of PbCl2 have been estimated as functions of log P2HCI/PH2O and temperature. From the discussion of the path during cooling process on the log P2 HCI . PH2O vs. temperature diagram, the authors proposed a possible dechioridization process that utilize water vapor as a dechloridizer for the direct precipitation of PbO from gas phase.

Jan 1, 2003

By P. A. Treasure

The EMEW® cell has been developed to overcome a number of inherent limitations in conventional electrowinning technology, particularly the high cost and restricted process windows characteristic of conventional hardware. The technology has been widely demonstrated to achieve high performance for various metals under chemical conditions well outside the limits required for efficient operation of conventional cells. This process flexibility offers significant opportunities for cost savings. in recovery of zinc from primary and secondary sources. The EMEW® technology is now available on a fully engineered basis, as a versatile commercial alternative to conventional electrowinning hardware. Application of the EMEW® cell for recovery of secondary zinc material offers significant advantages to the recycling industry. For example, a selective caustic leach can be used where there are high levels of iron or other contaminants in the target material. The reagent requirement is minimal as most of the caustic is regenerated in the bell and zinc dust that may be required for electrolyte purification is produced in the cell. A high purity zinc powder or cathode is produced in the cell. In the case of acidic zinc electrolytes, the cell is capable of operating over a much wider range of operating conditions than a conventional cell.

Jan 1, 2000

By Yuuki Yoshida

Electrolytic manganese dioxide, EMD, is the positive electrode material of primary batteries and the raw material of LMC used as the positive mass of lithium ion batteries and is currently produced by anodic deposition on and harvesting from a titanium anode in acidic manganese sulfate solutions prepared by dissolving high purity of manganese sulfate into sulfuric acid solutions. This paper presents an alternative method of EMD production using a novel anode, Mn2O3 coated titanium, at lower operating temperature than the current process to explore a possibility of manganese recovery from zinc electrowinning solutions. The Mn2O3/ Ti anode prepared by thermal decomposition of a precursor solution containing Mn (II) showed the anodic deposition of MnO2 by constant current electrolysis and the current efficiency was 95% in maximum, while the current efficiency and the crystallographic structure of deposited MnO2 depended on the current density, the electrolysis time, the bath temperature, and the concentration of Mn(II). The deposited MnO2 was successfully harvested from the anode and the recovery rate was 98%.

By Chuanyu Feng

In this paper, a load-based micro-indentation technique suitable for field applications was developed. This technique bears the same theoretical background as traditional load-depth sensing indentation, and does not need any direct measurement of indentation depth or contact area. The removal of this requirement will reduce much of the cost associated with traditional instrumented indentation. To demonstrate the feasibility, a portable indentation system suitable for online material characterization was developed. Design issues of the portable unit were discussed and preliminary results using the portable unit were also presented.

Jan 1, 2009

By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems arc necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed bi the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-3 to 10 2 Pal at 1573K. The effect of Fe3+ / Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By Svetlana Nikitina

While many question "sustainability" as an intellectual field on the grounds that it is too broad and "undisciplined," we are able to achieve a good balance between breadth of coverage and depth of inquiry in our team-taught seminar "The Grand Challenges: Sustainable Development for the 21st Century" offered to first year students at Worcester Polytechnic Institute. We strike this balance between breadth and depth by a) problematizing key sustainability issues in class discussions; b) by explicitly exploring the lenses of different disciplines (the historical context, the scientific facts, the engineering interventions and the philosophical foundations of unsustainable behaviors); and c) by offering our students opportunities to pursue a targeted project on specific sustainability issues (vertical gardening, metals recycling on college campus) through which they gain depth of understanding as well as practical exposure to all components of the problem, which puts them on the path of seeking effective solutions.

Jan 1, 2010

By Mikio Kobayashi

Extraction of valuable metals from sulfide ores continues to be a very important, process and so the strict control of discharge of harmful metals in effluents from refineries becomes more important in the future. The recovery methods for heavy metals have been developed. Some metals such as Se and As are still difficult to be removed to very low concentration, although the techniques for recovery and removal for many kinds of heavy metals have already been developed. Especially, in case of Se the recovery system from water with low concentration has not be developed yet, although the WHO decided Se to be harmful for human beings and then the discharge control is under obligation now. In general Se exists as selenite ion and/or selenate ion in aqueous phase and selenite ion is able to be recovered by coprecipitation with ferric hydroxide or by reduction to solid selenium by general reductants. Selenate ion, however, has a strong resistance to conventional treatments. Therefore the new technique for the recovery of Se from water including selenate ion has to be developed. In this presentation the new approach for removal of selenate ion using the reaction in which ferrous ion is oxidized to ferric ion is presented. Selenate ion is reduced to selenite ion during the reaction and then to solid selenium, while ferrous ion is oxidized to ferric ion. The coexistence of activated carbon is very useful to increase the reaction rate. The use of iron powder is also effective and very useful for reducing gel-like precipitates mainly consisted of ferric hydroxide. The concentration of the residual selenate ion is probably under 0.1 ppm after recovering Se by the mentioned-above approach. In addition to the mechanisms of these reactions, the effects of pH, coexistent positive and negative ions, and reaction temperature are also presented. Furthermore the investigation of the behavior of selenosulfate is presented.

Jan 1, 1998