Search Documents

By P. N. Anyalebechi

The effects of solidification rate (0.4-26.1 K/s) and alloying elements on the cast microstructures of aluminum alloy 5182 have been investigated with directionally cooled laboratory-size ingots. The alloying elements examined included Mg (3.6-4.7 wt.%), Mn (0.35-0.75 wt.%), Fe (0.11- 0.42 wt.%), Cu (0.03-0.25 wt.%), and Si (0.11-0.28 wt.%). These reflect the chemical compositions of AA 5182 end stocks with high recycled used beverage container (UBC) content. For a given chemical composition, the average dendrite cell and constituent phase particle size decreased with increase in average solidification rate. In general, within the level investigated, Mg did not have a significant effect on the types, volume fractions, and average sizes of the constituent phase particles. However, increase in Mn, Si, Fe, and Cu increased average sizes and volume fractions of the constituent phase particles.

Jan 1, 2010

By John C. Carpenter

Solvent extraction is used to selectively recover copper from iron containing sulphate solutions. As chloride ions, which form series of complexes with transition metals, are now being used for leaching. Little is known of the effects of these ions, on solvent extraction behavior. It has been shown that commercial extractants of the L1X and Kelex series extract copper from chloride media: (1) at a lower pH than from sulphate solutions, (2) to similar loadings, and (3) except for L1X 63, without transferring chloride to the organic phase. A process for selective extraction of copper from chloride solutions should thus be compatible with standard stripping and electrowinning practice. Of several diluents, differing in aromaticity, kerosene gave enhanced extraction only with L1X reagents. A change in operating temperature had little effect on equilibrium metal distribution. All the extractants examined gave adequate separation of copper from iron. L1X 63 was found to extract chloro-complexes of copper and of iron and thus transfer chloride to the organic solution. Consequently this extractant and its mixtures are not preferred for use with chloride leaching systems.

Jan 1, 1976

By M. Oliazadeh

The present study was performed to develop a process for solvent extraction of molybdenum and cobalt from an acidic solution generated by an electrodeposition process of nanocrystalline cobalt alloys. Solvent extraction is a common practice in hydrometallurgical and refining processes to produce metals; however its application for separation of molybdenum and cobalt from this specific solution is new, because molybdenum and cobalt are not commonly associated together in nature. Five commercial organic extractants were examined for extraction of cobalt and molybdenum from synthetic acidic solutions with pH ranging from 1 to 5. Preliminary results showed that at pH 2, any of the Cyanex 923, Alamine 336, Aliquat 336 and Hostarex A327 could be used to extract 99% of molybdenum from solutions, while from pH 3 to 5, Aliquat 336 was able to extract about 100% of molybdenum. Cobalt extraction, on the other hand, varied from 15% to 23% at pH 3 and 30% to 53% at pH 2 using different extractants. Based on results obtained, Aliquat 336 was applied on mixed solutions of cobalt and molybdenum at various pHs. The results showed that molybdenum could be extracted as much as 99% from a mixture of molybdenum and cobalt at acidic pHs, while less than 1% of cobalt was separated at pH 2 to 4 simultaneously.

Jan 1, 2003

By Kee Jeung Lee

In this study the characteristic factors and formation mechanisms for the hydrothermal preparation of a -quartz crystal powders were investigated to find the optimum synthetic conditions. The degree of Q -quartz crystal face development depended on the relative growth rate of a particular form that varies considerably with the degree of supersaturation, the reaction temperature, the concentration of mineralizers, and the presence of seed crystals in the feedstock. Alkali hydroxides and alkali halides were found to be effective in the reactions as mineralizers, which added in order to increase the solubility of the feedstock. The fine Q -quartz crystal powders were obtained in the temperature range of 250-450% and pressure range of 100-300atm. As the concentration of mineralizers increased, the particle size of crystalline powders became smaller at lower reaction temperatures. The fractional size distribution of synthetic crystal powders was depended on the hydrothermal conditions. As the reaction time and the amount of seed crystals increased, the width of particle size distribution became narrower. The weight mean particle size was in the range of 1 to 10m. The characterization of the products were carried out using XRD. SEM. PSA, FT-IR, Raman spectrometer.

Jan 1, 1997

By F. Shahbazian

attempt to systematize the knowledge on slag viscosities, the present work was carried out. The Among the physical properties of slags, viscosity is very important in understanding the mass out in the temperature range 1438-1762 Q The rotating cylinder method was used in the viscosity measurements. Crucibles and spindles made out of pure iron were employed. The transfer phenomena in metallurgical processes. The viscosities of fayalitic slags are of great interest in the non-ferrous metal industry, with special reference to copper production. In an slags were prefused before the measurements. In order to take into account the vaporization reactions involving CaF2, pre- and post measurement samples of the slags were chemically analysed and the compositions were ascertained. The results show that in the case of the CaO-SiO2 system, CaF2 additions tend to decrease the viscosity, in accordance with the expectations. In the case of the "FeO"-SiO2 system, at higher "FeO" / SiO2 ratios in the slags, a reverse trend was observed. The results are discussed on the basis of a viscosity model for silicate melts developed in the present laboratory as well as the structural considerations of silicates.

Jan 1, 2000

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Jorge Alberto Soares Tenório, Victor Bridi Telles, Denise Crocce Romano Espinosa, Felipe Fardin Grillo, Vicente de Paulo Ferreira Marques Sobrinho, José Roberto de Oliveira

"This research aims to study the process of incorporation of the metal iron in electric arc furnace dust (EAFD), from a steel mill producing long steel by liquid iron in addition to the changing temperature of 1400 degree Celsius altering experimental conditions such as how to add the EAFD (as received and in the form of briquettes), the percentage of EAFD to be added (10, 20 and 30% of initial weight of sample pig iron) and the time of withdrawal of the sample of pig iron and slag (30 minutes after the addition of EAFD). Previously, the EAFD will be characterized using the following techniques: chemical analysis, particle size analysis, X-ray diffraction, scanning electron microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) microanalysis. After characterization, the eletric arc furnace dust to be added to the bath of liquid iron, will be divided into 2 types: the first order of addition will be in the form ""as received"" from the plant and the second is through the agglomeration of EAFD in the form of briquettes. The achievement of fusion experiments in laboratory scale, will take place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of the metal iron will use graphite crucibles. A flow of inert gas (argon) will be maintained inside the furnace during the experiments. It is expected that the results obtained at the end of the research allow the evaluation of the iron metal incorporation of eletric arc furnace dust in hot metal bath.IntroductionThe steel industry generates a variety of solid wastes, liquid effluents and gaseous emissions at various stages of processing. The electric furnace dust (EAFD), generated in electric arc furnaces, represents a major problem for their content of chemical elements such as zinc, iron, chromium, cadmium, among others, issued to the atmosphere during the manufacture of steel[1]."

Jan 1, 2012

By Orlando C. Gaspar

The textures of the ores, the fine mineral intergrowths, the complex distribution of the deleterious minor elements, and the low base metal contents in some ore types, pose many technological problems to the beneficiation of the volcanogenic massive sulphides occurring in the Iberian Pyrite Belt. In particular fine intergrowths of the base metal sulphides with pyrite impose extremely fine liberation sizes (Kao=15 to 25um). The mineralogical, textural and metallogenic studies have provided an understanding of the distribution of vertical and lateral metal zoning in the ore bodies. Mapping of the ore types, carried out by mine geologists, and the metal zoning patterns computed from data base have shown that ore types are distributed as ore lenses, and that vertical and lateral base metal zoning exists in several orebodies. Since ore processing efficiency is affected by ore textures, and because the same mineral often shows different textural features, a relationship between the textures of the feed ores and those of the middlings must be established for all ore types defined at the deposit scale. For supplying, on time, the information needed for the optimization of the concentration processes, empirical methods of determining the mineralogical and textural characteristics of the several ore types have been developed.

Jan 1, 1995

The effect of change in slag composition upon metal losses to the slag and the relationship between slag composition and slag matte separation was investigated at 1400°C. The synthetic slags containing CaO, MgO, SiO2,, A1,0, and FeO were similar to those employed in the electric furnace smelting of sulphide Cu-Ni concentrates containing PGM (Precious Group Metals) from the Merensky Reef of South Africa. The matte with a grade of 9.3% Cu and 16.0% Ni was a typical electric furnace product. The results indicated that the Cu and Ni solubility in the slag increases with the increase of the basicity ratio and CaO and MgO contents of the slag. At constant CaO/MgO ratios the rise in basicity decreases the metal losses. When FeO and SiO2 contents of the slag are kept constant, the substitution of MgO with CaO decreases the metal losses. The relationship between slag composition and matte-slag separation was found to depend primarily on the basicity ratio and the FeO content of the slag. The net effect comes from a strong interaction of the two in such a way that increasing basicity and decreasing FeO contents deteriorate the clean separation of the two phases.

Jan 1, 1994

By Md. Maniruzzaman

The quenching performance of a liquid quenchant can be controlled by controlling the agitation in the quench tank. Without agitation, a vapor layer or bubbles form at the hot part surface and the natural convention of the quenchant limit the heat extraction rate at the quenched part surface. Resistance to the heat extraction rate can be reduced by breaking the vapor layer or by inducing a turbulent convection at the part surface through agitation (Le. forced circulation of the quenchant). To determine the effects of agitation on the quench performance of a mineral oil based quenchant, the CHTE quench probe system was used with AISI4140 steel probe tip. Quenching performance of the oil is evaluated by computing the effective heat transfer coefficients of the steel probe as a function of surface temperature using Lumped Parameter Analysis. In addition, computational fluid dynamics (CFO) simulation of the quench tank with an impeller type agitator has been done to understand and predict the fluid flow pattern in the tank. CFO simulation also provides insights for determination of optimal location of the impeller and the quench probe tip. Keywords: CHTE Quench Probe, agitation, CFD simulation, liquid quenchant, 4140 steel

Jan 1, 2003

By Matthias Merzkirch, Volker Schulze, Kay Andre Weidenmann

"Unidirectionally reinforced light weight compounds based on light metals such as the aluminium alloy EN A W-6082 are adequate materials for the future use in transportation means like automobiles and airplanes. Due to the occurring cyclic loads knowledge about the crack growth behaviour of such composites is needed. The investigations at a load ratio of R = 0.18 show that the crack growth rate of the aluminium matrix is reduced if reinforced by spring steel wire with a reinforcing ratio of only about 1 Vol.-%. Additionally, the acoustic emission analysis allows detecting crack growth within the matrix material, crack propagation along the interface wire/matrix and crack closure which could also be determined with the help of a self designed capacitive displacement measuring gauge. The damage behaviour could be verified by metallographic and SEM investigations.IntroductionIn the field of lightweight structures for transportation means the need for light, strong and stiff materials, in particular composite materials, is increasing in order to save resources and costs. Lightweight materials such as aluminium and magnesium alloys are highly efficient candidates to be used in the composite extrusion process [1] which allows for a simple production of unidirectionally reinforced profiles with a large diversity of geometries at low costs. Figure 1 depicts the principle of the composite extrusion process; within the first part of the tool the billet material is split into several strands whereas the middle part of the tool allows the supply of the reinforcing elements. The third part of the tool rejoins the matrix material and the reinforcing elements and defines the final shape of the profile."

Jan 1, 2011

By William Petruk

A mineralogical and image analysis study was conducted on samples of U tailings from pilot-plant runs on Midwest ore in Northern Saskatchewan. The tailings had been subjected to simulated weathering for the equivalent of 10 years in a tailings facility (lysimeter). The pH varied from 7.0 at the beginning of the test to 5.9 at the end. The results show that during the simulated weathering sane of the gersdorffite, uraninite, galena and pyrite had oxidized, with gersdorffite being the most reactive and pyrite the least. Reaction was evident at the top of the lysilleter , but was most intense at the seepage discharge. sane of the released ions precipitated as Ni, Pb, and U arsenates, sulfarsenates, sulfates and oxides on particles of all minerals. Green crystals of Ni sulfate and white crystals of ca sulfate had precipitated at the surface of the lysilleter. Clay minerals and chlorite had washed from the top of the lysirneter towards the seepage discharge.

Jan 1, 1989

By Adam J. Gesing

The eddy current separator (ECS) is designed to separate nonmagnetic (nonferrous) electrically conducting (metallic) particles from nonconductive residue. Nonferrous metallic particles are repelled out of the material stream passing over the eddy current rotor (ECR). The rotor is housed in a fiberglass composite outer shell that serves as a conveyor head pulley. This results in the desired metaVnonmeta1 separation. The behavior of ferromagnetic particles, mainly iron and iron oxide (i.e. rust), is quite different. These particles are strongly attracted to the magnets and the smaller particles tend to align their long axis in the direction of the magnetic flux. Since the direction of the flux changes with the passage of each magnet pole, the small particles spin at very high rates causing wear of the belt and of the composite outer shell housing the ECR. Large particles, when trapped under the ECS belt, cannot spin, but can be heated by the eddy current effects and subsequently can burn through the composite outer shell. We discuss the practical implication of this behavior of iron and rust on the design, performance and maintenance of eddy current separators.

Jan 1, 1999

By Lin Li, Xiang Li, Yifang Zheng, Jilai Xue, Jun Zhu

"Al drops and gas bubbles in the anode-cathode space of aluminum electrolysis cell are of great importance for cell operation improvement in metal loss, current efficiency and energy consumption. A direct observation on the Al drop, gas bubble and ultrasound was carried out through a see-through cell. The Al drop immersed into the cryolitic melt was found moving up and down irregularly in the anode-cathode space without electrolysis, which was then completely dissolved into the melt. During electrolysis, the Al drop came to the anode area and reacted with the gas bubbles generated on the anode. Under ultrasound, the gas bubbles were removed from the anode surface while the Al drop was kept on the side of anode. The observed phenomena were useful for technology improvement in reducing the anode-cathode distance or lowering the energy consumption in aluminum electrolysis.IntroductionDuring aluminum electrolysis, aluminum metal drop and anodic gas bubble are in close contact each other within the anode-cathode space, and the interaction between them can produce significant impact on metal loss, current efficiency and energy consumption. The motions of the Al drop and the gas bubble are also related to the dissolution of aluminum metal into cryolitic melt and the cell voltage drop due to the bubble layer covering the anode surface.A number of studies have been carried out using different types of see-through cells, where the dissolving process of metal Al into cryolitic melts (metal fog) in the anode-cathode space was directly observed and photographed [1, 2]. With the similar method, some direct observations on the anodic bubble behaviors with and without ultrasound were performed during aluminum electrolysis [3-6]. However, to our best knowledge, there is no published work on direct observation on the behavior of Al drops and anodic gas bubbles staying together within the same anode-cathode space, as well as the motion and interaction of them in cryolite-alumina melts."

Jan 1, 2011

By Yuanbo Zhang, Xiaoming Mao, Zhixiong You, Zhenyu Fan, Tao Jiang

"It is generally known that the formation of calcium ferrite is favorable during the iron ore sintering, which dominatingly contributes to the improvement of strength and reducibility of the finished sinters. In this study, effects of roasting temperature and 02 content of inlet gas on the sintering mineralization properties of typical iron ores, including hematite, limonite, specularite and magnetite, were investigated. The results showed the amount of calcium ferrite initially increased then decreased with the increase of the roasting temperature. The temperature of maximum calcium ferrite generation amount for different iron ores was determined as follows: hematite and limonite was 1275 °C, whereas specularite and magnetite was 1250 °C. Increasing 02 content of inlet gas was advantageous to the generation of calcium ferrite during the sintering. The sequence of 02 content affecting the mineralization properties of different iron ores was determined as follows: magnetite > hematite > specularite > limonite.IntroductionThe mineralization property of iron ore plays a significant role in the mineral composition and microstructure of finished sinters, which determine the quality and output of the sinters [1-2]. The mineralization process of sinters is composed of solid-phase reaction, formation of liquid-phase and crystallization. The formation and crystallization of liquid-phase is the foundation to the mineralization as the quality of the sinter is poor when concreted by solid-phase consolidation [3-4]. With respect to the iron ore sintering, liquid-phase regarded as bonding phase is generated between the iron ores and fluxes at high temperature [5]. Calcium ferrite is the most favorable liquid-phase among the bonding phases which dominatingly contributes to the improvement of strength and reducibility of the finished sinters [6-8]. Especially for high iron-low silicon sintering and high basicity sintering, making sure sufficient calcium ferrite quantity and reasonable distribution is crucial to the sinters [9-10]. Therefore, carrying out the researches on the high temperature reaction properties of iron ores is of great significance [11]."

Jan 1, 2013

By Djona M. Gaballah I.

Selective chlorination of unroasted and roasted spent hydrorefming catalysts was studied between 300 and 600°C using the following gas mixtures : C12+CO, C12+N2 and CI2+air. Such materials contain Co, Ni and Mo compounds supported by alumina and/ or silica. They also contain variable amounts of V compounds, C, S, etc., accumulated during the life time of the catalyst. Direct oxychlorination of the C+S rich sample allows higher extraction rates than those obtained by the carbochlorination of the same roasted one. It seems that the roasting step doesn't favor the economic metals' recovery. Results of the chlorination of C+S poor spent catalysts, in the presence of CO, in the chlorinating gas mixture, or of carbon added to the sample, were comparable. Cobalt and nickel chlorides were .extracted from the chlorination residues by their dissolution with acidified water, whereas molybdenum and vanadium chlorinated compounds were recovered by selective condensation from the vapor phase. The recovery rates of valuable metals as well as the selectivity were higher for the chlorination of spent catalysts than results obtained by the hydrometallurgical processing of the same sample. Results of the scale-up of the oxychlorination of the unroasted sample confirmed those of the laboratory scale. The global recovery rates were about 88 pct of cobalt, 93 pct of molybdenum and 76 pct of vanadium. The carbochlorination was applied to the recovery of W and Ti from Denox catalyst that is a carbon and sulfur free one. Recovery rates higher than 99 pct at temperatures lower than 500 °C could be obtained. This may indicate that the chlorination process can be applied to the treatment of various industrial wastes or by-product containing transition and/or refractory metal compounds A flow - sheet for the pretreatment of these materials is proposed.

Jan 1, 1995

By Stein Tore Johansen, Fionn Iversen, Jon Arne Bakken

"A new marker chain front tracking method is used for modelling the meniscus movement during DC casting of aluminium ingots. Modifications have been made to an earlier method developed by Popinet and Zaleski [12] to adapt the model for simulations of meniscus dynamics in the casting process.Initial casting simulations show that wetting conditions in the mould greatly influence the meniscus stability. Controlling the wetting conditions seems to be important for improving the cast ingot surface quality.IntroductionIn conventional direct chill (DC) hot top casting of aluminium extrusion ingot with gas-slip poor surface quality of the cast ingot can be a problem. In the worst cases pronounced surface wrinkling occurs coupled with periodic zones of reduced grain size, macrosegregation and exudation at the surface. The observed surface irregularities are believed to be linked to Periodic surface oscillations or folding of the meniscus resulting in varying solidification conditions.The focus of this work is to gain a better understanding of the dynamics of the meniscus and the influence it has on the finished cast ingot surface through numerical simulations of meniscus movement during the casting process.A two phase marker chain front tracking technique[12] using cubic spline surface reconstruction is applied for modelling the meniscus movement. The advantage of this type of model is its accuracy in the calculation of surface tension forces. Also the wetting can be implemented directly as a boundary condition on the surface spline function. The method is applied in the FLUENT solver, which is based on a finite volume method using the SIMPLE algorithm."

Jan 1, 2001

By Boris Arlyuk

The system of short term forecast of metal prices at LME is based on correlation between prices within the quarter forward and at the first place by economic parameters at the West, determining the consumption of metals. Such economic parameters are presented by data of indexes of Western World industrial production (WW IP), official data of IP and Dow Jones indexes at USA. For price forecast within the quarter forward (one day ahead, 3 day -65 days MA forward prices) are significant the changes of actual prices (official and close) at the past and the parameters of daily trade at LME at the past (futures turnover, open interest, LME stocks). It is developed subsystem of price forecast within the quarter forward based on analytical approach determining the relations between the participants of the market. It gives the opportunity to reduce the number of empirical coefficients at the model and receive good accuracy of forecast the MA prices and its direction at the future. Very important part of short term forecast is subsystem determining analytically the probability that the price forecasted for the next trading day will be the maximum or minimum daily price within the quarter forward. The thresholds probabilities are defined by identification the model at the past by maximal commercial efficiency. Such system was tested at the past at period since 2000 till 2005 and gives very high commercial results at operations on 1M forwards and hedging the sales of nonferrous metals traded at LME (primary aluminium, light alloys, nickel, copper, zinc, lead and tin).

Jan 1, 2006

By K. V. Sreenivas Rao

Solidification experiments have been conducted to study the effect of interface heat flux and air gap formation on cooling rate of the casting during solidification of Al-4.5wt%Cu alloy. The thermal history of the casting and mold during solidification is recorded using thermocouples connected to computer interfaced data logger. The measured temperatures in the mold are used as input to the IHCP (inverse heat conduction problem) algorithm for simulating multiple heat flux components at the boundary. It is observed that the filling effects induce spatial variation in the thermal field in the mold and casting regions and greatly influence the cooling rate of the casting. The study demonstrates the use of IHCP and in-situ measured thermal profile in analyzing the cooling rate and microstructure.

Jan 1, 2008

The high pressure acid leach process (HPAL) is being commercially used in four plants around the world to treat limonitic laterites. The two major operating costs of the HPAL process are the sulphuric acid and the energy required to heat the pulp to the desired temperature (>240°C). As an alternative to acid injection and steam heating, the in-situ generation of sulphuric acid and heat, produced during the high temperature pressure oxidation of sulphur-bearing materials blended with laterites, has been investigated at the laboratory scale. Various sources of sulphur have been examined, in particular, elemental sulphur, pyrrhotite and a Cu-Ni low-grade bulk concentrate. Under the proper blend ratios, all sulphur sources tested generated sufficient acid to result in equivalent nickel and cobalt dissolutions. A significant improvement to the process economics can result from the addition of sulphur sources containing valuable by-products, such as nickellcobalt andlor precious metals (gold and PGMs). This is especially true in the latter case, when the HPAL can be operated under Platsol conditions (i.e. with the addition of 5-10g/L of chloride), to dissolve the base metals and precious metals simultaneously in the autoclave. Various examples of the application of this concept are presented, together with a brief discussion of its implication on the autoclave design and the downstream processes to recover the values from the leach solutions. Keywords: limonite, co-treatment, acid consumption, sulphur, sulphur compounds, pressure acid leach (HPAL, PAL), Platsol process

Jan 1, 2004