By Yuanbo Zhang, Huanpeng Mi, Guanghui Li, Binjun Liang, Zhiwei Peng, Tao Jiang

Ludwigite ore has not yet been utilized on an industrial scale due to its complex mineralogy and fine mineral dissemination. In this study, sodium salts were employed to enhance the separation of iron and boron by reductive roasting-magnetic separation. It was found that the separation of iron and boron as well as the iron grade and recovery were significantly improved b y the addition of Na2SO4 or Na2CO3. Under the reduction temperature of 1050 °C, reduction time of 60 min and magnetic intensity of 0.1T. Compared with the inexistence of sodium salts, the iron grade and recovery of the magnetic concentrate increased from 83.3% and 88.6% to 93.2% and 95.1%, respectively, by adding 6% Na2CO3. The XRD and microstructure analyses indicated that the iron oxides were transformed into metallic iron and the average metallic iron grains were grown to over 40μm which was beneficial for separation of metallic iron from gangue.

Jan 1, 2016

By Toshiyuki Nohira, Eiichi Takeuchi, Tetsuo Oishi, Hideki Ono, Hirokazu Konishi

The Dy-Nd-Pr-Ni alloy sample was prepared by cathodic potentiostatic electrolysis at 0.65 V (vs. Li+/Li) for 1 h using a Ni plate in a molten LiCl-KCl-DyCl3-NdCl3-PrCl3 system at 723 K. The highest mass ratio (Dy/Nd+Pr) in the alloy sample was observed to be 50 at 0.65 V. Anodic potentiostatic electrolysis at 2.20 V for 12 h was conducted using the Nd-Fe-B magnet electrode in a molten LiCl-KCl system. All elements were almost dissolved from the magnet, and the original form of the magnet disintegrated. After anodic potentiostatic electrolysis at 2.20 V, cathodic potentiostatic electrolysis was conducted at 1.00 V for 5 h using a Mo plate in order to remove the dissolved Fe from the bath. Finally, cathodic potentiostatic electrolysis was conducted at 0.65 V for 12 h using a Ni plate. The mass ratio of Dy/Nd in the alloy sample was determined to be about 18.

Jan 1, 2015

By R. C. Hubli

Copper (II) chloride has proven to be an efficient lixiviant for copper sulphide ores and secondary sources of copper such as scrap. Nickel sulphides are generally associated with copper ores and copper-nickel matte is an intermediate product of processing mixed sulphides. While the copper species in aqueous chloride media are present as chlorocomplexes, the presence of nickel as Ni++ offers effective separation between the two by solvent extraction techniques. Oxidation of millerite by cupric chloride in sodium chloride solutions has been studied as a function of rate of agitation, leaching time, temperature, acid concentration and total initial cupric concentration. The reaction has a 1/2 order of dependence on initial cupric concentration in the range of 0.0 to 0.5M. The activation energy for the temperature range 333 -363 K has been found to be 59.2 kJ/mol with chemical reaction at the unreacted mineral surface as the rate controlling step. The rate expression, according to the shrinking-core model, for initial cupric concentrations between 0.0 to O.5M, is evaluated as

Jan 1, 1996

By Xiang Ma, Halvor Dalaker, Kai Tang, Stefan Andersson

Silicon carbide (SiC) is one of the most important non-oxide ceramic materials for many industrial applications and is mainly synthesized by carbothermic reduction of silicon oxide by coke above 2200°C. Replacing natural gas (mostly methane, CH4) for coke in SiC synthesis could considerably reduce energy consumption and CO2-emissions owing to higher carbon activity of CH4 at lower temperature. The generally accepted reaction mechanism is that SiC is synthesized through gaseous intermediate silicon monoxide, SiO. In the present study, the reaction mechanism for the SiO and CH4 gaseous mixture has been examined using atomic scale modelling. Molecular dynamics (MD) using a reactive force field (ReaxFF) has been utilized to examine the initial stages of reactions involving a gas mixture of SiO and CH4 and surfaces of SiC. The MD results revealed some interesting SiC formation mechanisms. The reaction energies of the critical intermediate species were also estimated by density functional theory (DFT) calculations and the implications for the force field parameters used in ReaxFF was discussed.

Jan 1, 2015

By M. Misra, J. Nanor

The precipitation and removal of arsenic from process waters can be accomplished with addition of lanthanum chloride alone or in conjunction with ferric sulfate. The long term stability of these corresponding precipitated compounds is critical from the disposal stand-point. In this paper the characterization of ferric, lanthanum and lanthanum-ferric arsenate compounds formed at room temperature in acidic and alkaline pH is presented. The characterization techniques used included zeta potential, XRD and SEM. Zeta potential measurements of ferric and lanthanum hydroxides in the presence of arsenate indicate that oxyanions of arsenate are chemically adsorbed onto the positively charged surfaces of these hydroxides. In alkaline pH there is desorption of arsenate species from the ferric hydroxide surface, hence the product is thought to be unstable. On the contrary, lanthanum arsenate is stable in alkaline pH. XRD patterns show that the ferric arsenate formed in acidic and alkaline pH is amorphous, whereas lanthanum arsenate and lanthanum-ferric arsenate formed in acidic and alkaline pH are crystalline.

Jan 1, 1999

By Qian Xu, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Shuhua Geng, Hongwei Cheng

Herein we report an electrochemical route from oxides (SiO2, TiO2)/sulfide (MoS2)/carbon mixture precursors to Mo-Si-Ti-C composites in molten salt. The electrochemical process was carried out in molten CaCl2 at 800 °C with a potential of 3.1 V, and a graphite-based anode was used in the electroreduction process. The reaction mechanism and the influences of the stoichiometry of the initial mixture precursor on the morphology and phase composition of the final products were investigated. It has been found that Mo5Si3/MoSi2/Mo3Si/Mo, Mo5Si3/MoSi2/Mo2C/SiC, and Mo5Si3/Mo2C/Ti3SiC2/TiC/Mo composites can be electrosynthesized directly from their oxides/sulfide/carbon mixture. The preliminary experimental results suggest that the electroreduction process can be used for the controllable electrolytic production of alloys/carbide-containing composites from oxides/sulfides/carbon precursors.

Jan 1, 2016

By Geoffrey Brooks, Mehedi Bin Mohammad, M. Akbar Rhamdhani

Molten alkali nitrates are used commercially as thermal storage fluids (HTF) for solar thermal electricity generation. Their range of operation is limited by the thermal stability and this limits the energy (steam-Rankine cycle) efficiency of these processes. In this study, the effect of atmosphere on the thermal stability of nitrates was investigated using simultaneous thermal analysis techniques (STA). The use of oxygen (O2) as a blanket gas was found to delay the decomposition point of the ternary NaNO3–KNO3–LiNO3 (13.23–57.14–29.63 weight ratio) mixture by 55 °C. By which operating range will increase 65 °C more compared to the binary solar salt. Higher heating rates increased the decomposition point but had less effect on premelting and melting properties. Nitrogen monoxide, and O2 evolution after melting indicates concurrent reversible reactions. Similar phenomena were observed for single and binary nitrates. The eutectic melting point of ternary nitrate obtained from the STA agreed well with FactSage eutectic composition prediction.

Mar 1, 2017

By S. R. Reddy

Thennodynamic properties of several quaternary systems are calculated using our recently modified Margules equations. The modified Margules equations are expressed up to infinite order in the vicinity of solvent. Quaternary system of one solvent and three,solute partials are derived. First order interaction coefficients of binary, ternary and cross -interaction parameters of quaternary system are used to'evaluate the partial functions. In the original fonn of Margules equations,derived partial functions are convergent and same 'as Unified ,Interaction Parameter Fonnalism. But considering up to infinite order of the Margules coefficients, the functions are divergent, in order to overcome this restriction, Margules equations are modified to get consistent equations. Derived partial functions are thennodynamica Hy consistent with Maxwell and Gibbs Duhem relations. The derived logarithmic activity coefficient of the solvent and solutes are consistent with the ternary systems. The calculated data, ie., activity coefficient values of nitrogen and interaction coefficients are in good agreement with the data of Fe-Cr-V -N. Fe-Ni-V -N, Fe-Cr-Ta-N and Fe-Ni-Ta-N systems.

Jan 1, 1999

By G. Haesebroek

In L969 Metallurgie Hoboken-Overpelt started an industrial plant for the separation of iron and zinc from a concentrated CoCL2 solution. Iron and zinc are extracted in column contactors by a solvent containing 12 vol % of tertiary amines in xylene. The extracted metals are stripped from the pregnant organic phase by precipitation with a NaOH solution at pH LL. In this paper an overview is given of the industrial process. In order to overcome some drawbacks of this process (low flash point of the diluent, reagent consumption, batchwise stripping) an alternative solvent extraction process has been examined. In this alternative process, iron and zinc are extracted with an or¬ganic phase containing 50 vol % of TBP in Escaid 110. The pregnant solvent is stripped with water in conventional mixer settlers. Despite the ability of this process to overcome most of the inconveniences due to the use of tertiary amines, it suffers from the poor stability of TBP in concentrated chloride solutions, resulting in unavoidable and inacceptable precipitation phenomena in the stripping section.

Jan 1, 1988

By Ludovic Charpentier

Production of metallic wires directly from liquid jets would avoid drawbacks of extrusion (space needed, damaging, cost?) and enable recycling. But liquid jets tend to break, due to capillary instabilities, unless a solid layer (coating or start of solidification) surrounds it. We recently developed a process to produce tin wires, cooled by water flow parallel to the jet. Superficial oxidization of tin produces a glass coating around the jet. Studies showed the length of wires increased when increasing speed of tin jets, and that water average speed should be the closest possible to the jet one to have smooth fibers. Producing 1 mm diameter wires is possible. The length of wires is limited by the experimental setup, which does not provide possibilities to coil the wire. Most of other metals do not generate glass-like oxides. The lack of coatings makes it necessary to reduce the capillary instabilities to obtain fibers.

Jan 1, 2006

By M. J. Adam

As part of its research program, the U.S. Bureau of Mines is investigating the partitioning of complex minerals to simpler phases using sulfidation reactions for selective extraction of mineral constituents of value from extraneous elements early in processing schemes. This report describes research in which thermal processing of the complex Ti -bearing mineral ilmenite (FeTiO, ) resulted in partitioning of the valuable Ti metal to the simpler compound rutile (Ti0 ). Samples of ilmenite were blended with elemental S for thermal treatment a2 various temperatures under controlled atmospheres in an effort to dissociate the Fe from the ilmenite complex. Product characterization revealed that the Fe was partitioned from the ilmenite, forming a rim of pyrrhotite/pyri te (FeS/FeS,) on a rutile core. The products were agate milled and then subjected to cursory magnetic and flotation techniques in an attempt to physically separate the partitioned phases. Partitioning results and phase concentration data are reported relative to thermal treatment variables and physical separation techniques.

Jan 1, 1993

By Tarek M. Abd El Hamid, Suzane Ali

"Treatment of industrial waste materials is created serious problem in Egypt. Aluminium sludge is generated as a by-product from aluminium household industry which contains significantly high alumina content exceeding 90%. This by-product randomly disposed and creates serious environment problems to locate community. To develop the treatment process of this material, the recovery of high purity alumina and identify the potential application is being the primary objective, This paper represents the recovery process of alumina process waste sludge High purity alumina material <99.8% aluminium oxide with originate particle size 0.125-0.420mm and apparent density 0.39g/cm3 was obtained with a specific surface area 139m2/g. Alumina produced was modified by cerium oxide doped alumina. The catalytic activity and selectivity was investigated in conversion of iso-propanol via dehydrogenation reaction yielding only acetone indicating an excellent selectivity the dehydrogenation. The presence of 10% CeO2 increase in the catalytic activity of 82% for the originated alumina. Introduction Approximately 20 thousand tons of aluminium waste produced in Egypt in 2006 with increasing amounts expected in succeeding years. A part of this waste contains organics impurities which coexisted with aluminium waste as a result of manufacture final aluminium products, waste usually content <1 to 2 wt% of organic carbon. It's generally admitted that the organic species are present in the form of lubricant oils used in rolling and pressing equipments for aluminium sheet. Both industry and government face possible high-cost disposal problems that more magnified by large volume of waste produced. The alumina recovery leachable study conduct in this paper had the following objectives: 1- Develop a process that can provide an environmentally acceptable residue and also recover the available alumina. 2- Evaluate the alumina produced in terms of grade and catalytic application."

Jan 1, 2008

By Fu-Shen Zhang, Mengjun Chen, Jianxin Zhu

"In the present study, different types of cathode ray tube (CRT) glasses were examined by sequential extraction combined with TCLP to provide possible explanations for how Pb and Ba leach out from the waste CRT glasses and to give possible reasons for why they leach out. Sequential extraction results showed that Pb and Ba in the CRT glasses dominanfly presented as the residual fraction. The exchangeable fractions of Pb and Ba were extremely low, less than 0.01 % of the total content, but they were higher than those required by the regulation limits, 5 and 100 mg/L for Pb and Ba, respectively. TCLP tests of the original CRT glasses and CRT glasses residues after each step of sequential extraction demonstrated that the extremely high leaching toxicity of CRT glasses mainly caused by its exchangeable and carbonate fractions of Pb and Ba.IntroductionIn recent years, the amount of cathode ray tube (CRT) contained monitors or TV sets in the market were sharply reduced, since they were substituted by novel and better electronic and electric equipments such as LCD and PDP, leaving huge amount of end-of-life CRTs. 50-85% of the total weight of this kind of computer monitor or a TV set is glass[1,2], which was classified to three categories according to their chemical compositions: black & white glass (BW), color panel glass (CP) and color funnel glass (CF)[3]. In order to provide shielding from X-rays generated during the picture projection process, lead, barium and strontium oxides were used in the glass. In general, a color CRT contains 1.6-3.2 kg of lead . Therefore, these glasses have attracted wide and tense attention due to the potential risk to the environment and human health."

Jan 1, 2011

By N. R. Green, N. J. Humphreys, D. McBride, T. N. Croft, M. Cross, D. M. Shevchenko

"Centrifugal casting offers a route to high quality products in difficult to cast high temperature low superheat alloys and thin section molds. Under centrifugal forces metal is forced into thin sections and can fill thicknesses of less than a millimeter. However, due to the high liquid metal velocities there is a high risk of surface turbulent flow and air entrainment within the liquid metal. The combination of interacting flow-thermal-solidification phenomena and associated defects is a challenging modeling task which the authors have previously described and validated. Capturing the metal-air interface, on what are inevitably complex three dimensional geometries, results in highly computationally expensive simulations and simulating a single cast can take weeks on a single processor. This contribution reports on modeling a complex centrifugal cast, gas entrainment, bubble transport and solidification, employing meshes of up to a million elements and investigates the scalability of the model on high performance clusters.Introduction The ultimate goal of any casting procedure is to produce a defect-free product. For difficult to cast alloys, such as Titanium, centrifugal casting has a number of advantage over conventional gravity methods [1]. In the casting of thin sections, such as turbine blades, the metal is forced into the thin sections under centrifugal forces. The centrifugal force can overcome the backpressure due to surface tension and the metal can fill mould sections with thicknesses substantially less than a millimeter. However, the materials used in these castings [2] tend to be highly reactive and requires low superheat. High liquid metal velocity gives rise to a high risk of free surface turbulent flow and of associated entrainment through free surface turbulence [3] and trapping of gas present in the flow [1]."

Jan 1, 2012

By F. Ríos

Fundamental research, at laboratory scale, on the biomass adsorption capacity of a liquid mining effluent has been done. The biomass used corresponds to a Chilean seaweed called Gracilaria chilensis. The waste water effluent corresponds to clear water coming from thickeners of a Chilean copper mining operation. The biomass was dried, washed, treated with an acid solution, and then reduced in size. A characterization of Zeta potential was made, finding negative values in a wide pH range with a ZPC equal to 2.5 1. Adsorption tests were made- in an agitated system containing an artificial solution of CuS04 at a controlled temperature of 25 degrees Celsius; also, the effect of pH over the copper adsorbed was studied. Maximal adsorption of copper was found at pH equal to 6, and the Langmuir model indicated values for saturation of 52.08 mg/g and for standard free energy of about -21 KJ/mol. Kinetic adsorption was very high and fitted very well with a second order model equation, finding that 90 per cent of the adsorption occurred during the initial 10 minutes. After stoichiometric when 1 mol of copper is adsorbed, 2 mol hydrogen are released, showing that the main mechanism to remove heavy metals is the ionic exchange, and the seaweed ensures total discharge of copper adsorbed when the pH value is about 1. Experiments done with real waste water from thickeners lead us to conclude that optimal results for copper and molybdenum adsorption are at pH around 3.25 and the remaining treated water may be partially discharged into the water currents, thus showing that Gracilaria chilensis can be used to remove heavy metals easily from liquid effluents in the copper mining industry.

Jan 1, 1999

By I. Mc Dougall

"The matte/slag tidal zone in a platinum smelting furnace is subject to severe process conditions which can often lead to premature failure of the lining. The MgO-FeO-Si02 slag is aggressive to refractory bricks, whilst the Ni-Cu-Fe-S matte is aggressive to water-cooled copper cooling elements, and can penetrate and sulphidize refractory bricks, particularly at the high matte temperatures often experienced in the PGM industry. A novel approach to the lining design was taken at Lonmin's new 10MW Furnace 2. An indirectly-cooled graphite ring was applied in the matte/slag tidal zone, with refractory bricks on the hot face. Thermal Finite Element modeling was conducted to determine the optimal lining design in this region of the furnace. The resistance of two graphite grades to damage by slag and matte was evaluated experimentally. The graphite lining is not wet by the matte, and is resistant to slag attack at operating temperatures. In comparison to water-cooled copper in various configurations, cooled graphite shows promise as an indirect refractory cooling system in the tidal zone area of furnaces.IntroductionIn South African Platinum Group Metals (PGM) smelting operations, the PGMs are associated with nickel-copper sulphides in magmatic rocks. After ore is mined, it is concentrated by means of a flotation process prior to smelting. Both rectangular 6-in-line and circular 3 electrode AC submerged arc furnaces are used for this purpose. A new 10 MW round furnace is currently under construction by Tenova Pyromet at Lonmin's Marikana Smelter Division. An overview of Lonmin's smelting operations and Lonmin's approach to smelting high chromite containing PGM concentrates is given by Eksteen et al. [1]"

Jan 1, 2012

By A. J. Davidson

A novel sensor is described for the measurement of the copper content of copper matte. Due to the high copper concentrations found in matte, potentiometric sensors are not sufficiently sensitive. A highly sensitive sensor has been developed based on a modification of the amperometric technique using a copper ion conductor, Cusicon. The results correlate closely with the theoretical predictions.

Jan 1, 1998

By V. Gel

An analysis of the operation of rotary tilting furnaces has indicated that they ensure better recoveries of metal when smelting lump scrap from aluminum slags, brass and bronze. On the other hand, processing of slags (concentrates obtained by mechanical upgrading) in pear-shaped furnaces results in much lower performance values as might be expected. At the Novgorod metallurgical plant a process for blister copper production in a rotary TROF converter (Outokumpu, Finland) has been introduced on a commercial basis. Smelting of brass and bronze scrap to produce blister copper is carried out using the technology developed in Russia and differing from the Outokumpu technology by the types of flux used and the blowing conditions in fuel burners and for melt oxidation, as well as by the design of gas removal system, the design of nozzles for melt blowing and the use of carbonaceous reductant (coal) for magnetite reduction in slags. Industrial-scale testing has demonstrated that by means of special techniques the 30-tonne converter productivity can be increased by 30% to 40% as compared with its rated productivity.

Jan 1, 2006

By Yiming Rong, Gang Wang

"Water quenching is one of common heat treatment processes but with complex physical phenomenon, in which vaporizing, bubbling and convection are involved. The general simulation of liquid quenching processes is conducted by using temperature dependent value of heat transfer coefficient (HTC) obtained from experimental measurement under a strong assumption. A preliminary multiphase flow model developed by using Ansys-CFX for water quenching has been presented in this paper, which shows a distributed HTC with a time dependent feature. The conjugate heat transfer is used to describe thermal conduction in the simplified workpiece, and generation, growth and flow of bubbles are modeled by using Eulerian-Eulerian method for the gas-liquid multiphase flow. The simulation result shows the intense variation of heat exchange through the interface between workpiece and liquid, and the unsteady distribution around the solid surface.IntroductionQuenching is a rapid cooling process which makes the desired solid phase transformations happen for the certain material properties. For aluminum alloy, rapid quenching will prevent all phase transformation and generate a supersaturated single phase."

Jan 1, 2012

By J. L. Delplancke

During copper electrowinning in sulphate electrolyte, intense oxygen evolution takes place at the anode. Lead alloy anodes are progressively replaced by dimensionally stable anodes in order to avoid the cathode contamination by dissolved lead. The electroactive coating of these anodes has to be as cheap as possible, adherent to the substrate, electrochemically stable and has to be efficient at high current density and high temperature. This requirement is even demanding in case of copper electrodeposition for the production of thin copper foils for the electronic industry. The production of thin (20 µm thick) copper foils for the printed circuit boards requires high purity copper electrodeposited at a current density as high as 7,000 A/m2. The choice of a long term coating composition is driven by economics. The purpose of this paper is mainly to review the anode compositions suitable for copper electrowinning and for copper electrodeposition at high current density. A short description of preliminary results obtained with a new anode coating on a titanium substrate is also presented.

Jan 1, 1999