By I. Gaballah

Spent hydrorefining catalysts may contain 4 to 6 % of COO and/or NiO, 8 to 16 % of Moo3 and up to 10 % V205 generally supported by alumina. Raw samples are roasted in order to eliminate carbon, sulfur and hydrocarbons contained in the spent catalysts. The roasting optimum temperature and time are 500 "C and 7 hours. Selective chlorination of roasted samples with Cl2 + air, Cl2 + N2 and Cl2 + CO is investigated in order to recover the valuable metals. Depending on the chlorination it is possible to recover more than 80 % of the Ni and Co about 95 % of the Mo and up to 80 % of vanadium compounds. Cobalt and nickel chlorides are obtained by leaching the chlorination residues' by acidified water. Molybdenum and vanadium chlorides and/or oxychlorides are obtained by selective condensation from the vapor phase. The chlorination of the catalyst support, Al2O3, can be limited to less than about 5 %. Besides the reaction temperature and time, the oxygen partial pressure of the chlorinating gas mixture appears to be the key factor for the reactions' selectivity.

Jan 1, 1993

By R. Craig McClung

Contrary to other sulfide minerals, where recovery is principally liberation controlled, the recovery of molybdenite is more complex. It is this complexity that initiated a geometallurgical investigation of molybdenites from Bingham Canyon. The aim of this investigation was to determine the effect mineralogy and/or mineralogical attributes have on recovery. All samples were analyzed using normal mineralogical techniques. The results reveal the presence of two distinctly different types of molybdenite. These have been identified as the two polytypes of molybdenite: i.e. hexagonal (2H); and rhombohedral (3R). The 2H-polytype occurs as textbook-shaped particles in quartz-molybdenite veins that are located in the current pit bottom. The 3R-polytype occurs as disseminated, “ball”-shaped particles with a dull or frosted appearance and are concentrated along the margins of the current pit. Concerning their metallurgical behavior, each type exhibits unique metallurgical properties that are consistent with those reported in the published literature. The 2H-polytype is easily ground and kinetically “faster” floating with surface attributes that are amenable to higher rates of recovery. This results in the production of a high quality concentrate under normal operating conditions. The 3R-polytype, by comparison, is difficult to grind and kinetically “slower” floating with surface attributes that are less amenable to recovery. Therefore, in deposits with higher concentrations of the 3R-polytype, modifications to the normal operating parameters may be necessary to improve recovery. This investigation highlights the necessity for understanding the mineralogical characteristics of any economic mineral(s), as these will have a direct impact on recovery.

By Haibin Wang, Baojun Zhao, Xueyi Guo, Zhixiang Cui, Zhi Wang

In conventional copper production, anode copper is produced from concentrate in three furnaces in a process that entails four oxidation steps and one reduction step. Three types of slags are produced that require further treatment to recover copper. Dongying Fangyuan Nonferrous Metals recently developed a simplified process which requires only two custom-designed furnaces instead of the conventional smelting, converting and re fining furnaces. The first furnace continuously produces high-grade matte (>75 wt% Cu) that contains little iron (<2 wt% Fe). The liquid matte is continuously fed to the second furnace, which produces anode copper. The new process signi ficantly reduces the capital and operating costs and increases productivity and environmental sustainability. This paper presents fundamental concepts that enable the simpli fied process to be developed. The detailed operations in Dongying Fangyuan Nonferrous Metals are also described.

Mar 1, 2018

By P. J. Uggowitzer, H. Kaufmann

"New Rheocasting is a novel route of semi-solid casting, in which the globular semi-solid precursor material is produced by controlled cooling of only slightly superheated melts in conventional steel crucibles. The resulting semi-solid slugs are placed into the sleeve of a vertical Squeeze Casting Machine and then filled into steel dies. Solidification occurs under hydraulic pressures up to 100 MPa Due to the reduced cost of precursor material, reduced investment cost and easier recycling, the New Rheocasting process offers cost reductions of up to 25% over conventional semi-solid casting · routes. The New Rheocast products are pore free, pressure tight, weldable and heat treatable castings.In the present work the New Rheocasting Process is introduced and the influence of heat treatment on mechanical properties of the New Rheocast alloy A356 is discussed.The alloy A356 is cast under ideal New Rheocasting conditions into a step die on an UBE HVSC 350 Squeeze Casting machine. As-east, TS and T6 heat treatment conditions with variations in solutionizing and aging time/temperature parameters are applied and the samples are tested by tensile testing. Alternatively, the same heat treatment conditions are applied to conventional Squeeze Casting parts and compared with New Rheocasting.Questions of potential cost savings due to modified heat treatment conditions are also addressed in this paper."

Jan 1, 2000

By J. D. Ecuyer, L&apos

he microstructure of galvanneal coatings formed on extra low carbon and interstitial free steel substrates has been characterized using electron microscopy (TEM and SEM) and x-ray diffraction. The coatings are found to consist of a mixture of gamma, delta and zeta phases, of which delta is the main constituent. The amounts of each phase influences the powdering resistance of the coating which was evaluated using reverse Olsen testing and 60" bending. For the three heat input conditions considered, IF coatings were always found to contain a significant amount of gamma and only those which retained zeta phase on the surface exhibited a satisfactory powdering resistance. In much the same way, ELC coatings with relatively thick gamma layers performed satisfactorily only when some zeta was retained. It was also found, however, that coatings with minimal zeta and gamma had an excellent powdering resistance. The latter coatings were produced under galvannealing conditions of lower relative heat input. These results indicate that in addition to the zinc bath composition, coating weight and galvanneal thermal cycle, the base steel chemistry also has an effect on the coating microstructure. Knowledge and control of all aspects of galvannealing is therefore essential to consistently produce acceptable coatings.

Jan 1, 1992

By Susanne Pignolet-Brandom

Reflected light microscopy scanning electron microscope energy dispersive spectroscopic analysis and backscatter electron image and electron microprobe chemical analysis have been used to study lead sinter and lead blast furnace slag. These studies provide invaluable information on the phases present their intergrowths, and their chemical composition. Such information increases the understanding of the nature of pyrometallurgical processes and the behavior of minor elements during these metallurgical processes.

Jan 1, 1987

By J. T. I. Poijärvi

The smelter off-gas cleaning and the weak acid treatment at Outokumpu Harjavalta Metals Oy are presented and described in this paper. The smelter consists of the copper and nickel smelters and the acid plant of three separate acid plants two of which are double contact and one single plant and of one liquid sulphur dioxide plant. The preliminary cooling and flue dust separation of the smelter off-gases from the copper and nickel flash smelting furnaces and converters in the waste heat boilers and in the hot electrostatic precipitators are described. The final cooling and cleaning of the gases in the scrubbers at the sulphuric acid plant and the treatment of the weak acid in the vacuum and in the submerged combustion evaporators for the removal of impurities are pre¬sented as well as the treatment of the condensates from the evaporators. The attention is paid to the generation of sulphur trioxide in the smelter off-gas and to the treatment of that in the weak acid bleed-off and to the utilization of the treated acid.

Jan 1, 1992

By Jiang Fan, Wang Haigang

"The three-dimensional complex multiphase turbulent flow in U-beam separators was simulated using the Reynolds stress equation models (RSM). To account for the effect of the stochastic characteristic of the instantaneous gas velocity on the particles, the improved Lagrangian stochastic model based on the Reynolds stress model for gas phase was adopted, which attributed to the successful prediction of the turbulence anisotropy and particle crossing trajectories effects. The interaction between the particles was also considered using the HardSphere model. To treat the particle-wall collision, the influence of the roughness of the wall on the motion of the solid particles was taken into consideration by imposing random collision angles. The result from this study not only shows the dynamic characteristics of the multiphase flow- in the separators, but also gives the relationship among the efficiency, structure and pressure losses of the separator.IntroductionCirculating fluidized bed (CFB) combustion is one of the most promising clean coal techniques. A main feature of CFB boilers is the un-delayed recycle of solid, coal and sorbant particulate, in an external loop. Separator, which is required to separate the solid particle from the flue-gas leaving the reactor of CFB, plays an importance role in the external solids recycle loop. It affects the combustion of CFB system greatly. Presently cyclone is the most commonly used as separators for CFB system and other chemical industrial processes. It provides high level of separation for CFB system for fine particles. However it suffers from some inherent disadvantages. It's volume and size is huge. Moreover, it is difficult to design and install when the CFB workload rises. The application of U-beam separators instead of hot cyclone separators in CFB boilers has many advantages. Publications indicate proposals or successful use of Ubeam separators in Swedenr11, USA 21, Russia r3land China [4]• But it is not possible to find results in the literature of detailed investigations of this new. type of separators or recommendations on the choice and calculation of an optimal design. For this reason, numerical simulation for the three-dimensional gas-particle two-phase flows with several rows of vertical U-beam elements, local in the chess order and blocking a way of outgoing from a CFB boilers dusted gases was carried out in this study."

Jan 1, 2004

By Jacques J. Eksteen

Any effort to improve the metallurgical control of industrial furnaces employed in the primary extraction of high carbon ferroalloys are bound to fail unless the variability of the melt is not fully accounted for. A number of sampling campaigns were performed on both 3phase AC submerged arc and single phase DC open arc furnaces at different smelter sites in South Africa where High Carbon Ferrochrome is produced. It was found that the heterogeneity between multiple samples during a single taps were much higher that for heterogeneity found within a sample. Moreover, this heterogeneity (as quantified by the relative standard deviation per tap) varied with the operating conditions of the furnace, the element monitored and the type of furnace. A relationship was found between the relative standard deviation of certain elements and the degree of subcooling of the melt.

Jan 1, 2006

By Cynthia K. Belt

Improved energy efficiency has grown in importance within industry as energy costs have escalated. The analysis of trends and changes to a process is critical in making the best business decision in energy management. Frequently, energy use per day (Kilowatt-Hour or British Thermal Units) is used to track energy efficiency. Sometimes, the somewhat more complex method of energy per processed weight (Kilowatt-Hour per Metric Ton or BTU per Pound) is used to make this evaluation. Yet both methods ignore the effects due to throughput and weather. In this paper, different thermal processes and systems will be evaluated using statistical methods to highlight alternative methods to evaluate energy efficiency. Examples and potential problems will be discussed for both a single process and a collection of processes within a plant or corporation.

Jan 1, 2008

By William Brinkman, Mark Jolly, Nasim Soleimanian, Karl Dearn, Oliver Brinkman

"Glass manufacturing is a heat intensive process. There is a direct correlation between the batch distribution techniques and the furnace energy consumption, productivity, and quality of the glass manufactured. All four major segments (float, container, fibre, and specialty glasses) would benefit from using an optimised batch distribution technique where possible. Oscillating batch chargers (OBC) have been in use since the early 70s, despite their superior batch shape, coverage, and in turn positive effects on the energy consumption and productivity of the furnace they are almost exclusively used in container glass manufacturing. The OBC’s main difference compared with other charging methods is its ability to directly influence the batch initial velocity. This paper reports on results achieved in CFD models (GFM) used to study effect of the machine on the overall energy consumption in the doghouse and the melt space.IntroductionGlass manufacturing can be divided to four major segments float glass, container glass, fiberglass, and specialty glasses. The financial cost of manufacture, its impact on the environment, lack of standardisation and mounting pressure imposed by the authorities for reduction in emissions means that the industry and its suppliers are utilising CFD modelling in order to tackle these challenges. The need for high temperature to create and maintain the viscous flow, homogenisation of the glass melt, and maintenance of the process to allow continuous output of glass of the right quality are the contributors to the energy intensive activities that are involved in continuous glass manufacturing. This in turn has resulted in design of large container glass furnaces which have high energy consumption, low specific performance, and high CO2 emissions where the most efficient furnaces in the container glass sector have a specific primary energy consumption of 3.8 GJ /tonne of glass at a level of 50% cullet in the batch making even very small improvements in efficiency by operation optimisation a value adding activity [1-14].The theoretical calculated energy required to melt glass is 2 to 3 times less than the energy actually used to melt glass as a result of glass melt passing a zone 5 to 8 times before leaving the tank.[8]. This causes contamination as the result of mixing between the completely molten glass free from bubbles returning to the batch area where there is freshly molten non-homogeneous glass, still containing very large numbers of bubbles and un-molten batch. At high temperature some components are dissolved rather than melted. Given that an un-molten batch is a good thermal insulator, it can be transported a long way into the furnace, increasing the need for homogenization which also increases the glass residence time of glass melt. This is why large unbroken strings of batch should be avoided, as should an overall blanket without gaps."

Jan 1, 2014

By Dan Wang, Qian Xu, Guangshi Li, Xionggang Lu, Xingli Zou, Zhongfu Zhou, Hongwei Cheng, Changyuan Lu

The preoxidation of the ore has a profound significance to the concentration, separation and purification of nickel and copper from the lean complex ore. In this paper, the natural Ni-Cu sulfide mineral samples under the elevated temperature condition in air were investigated, as well as under isothermal condition at 600 oC in air. The mineralogical characterization was studied using XRF, ICP and the Rietveld method. The oxidation behavior and the element migration of the Ni-Cu sulfide ore were studied by XRD, SEM-EDS and TG. The XRD Rietveld method was successfully developed in the phase identification and quantification of this complex ore powder sample. The oxidative intermediates (Cu/Ni-ferrite) were detected by XRD, and the process of the element migration was obviously revealed by the line scans using SEM-EDS. It is the preoxidation of this mineral that provides guidance for the extraction of valuable metals from low-grade Ni-Cu sulfide ores in the future.

Jan 1, 2015

By Thomas Niehoff

Many industrial processes require energy. Energy is required for melting or heating purposes. The heat can be generated by electrical heating or combustion/oxidation of hydrocarbons. Oxygen supports the combustion process. Oxygen is naturally contained in air with about 21 vol.-percent. The use of technical oxygen will allow an increase to the natural oxygen concentration of combustion air. Altering the combustion process by increasing the oxygen content has various effects. These effects are described and analyzed with regard to heat transfer, emissions and energy consumption. Industrial processes requiring oxyfuel are described and discussed regarding energy aspects.

Jan 1, 2008

By T. W. Gonzales

The refractory performance of Peirce-Smith converters is considered to be mainly determined by effects of process control and refractory installation design. BHP Copper has shown that, over the last four years, considerable improvements in tuyere line life can be affected .by maintaining a uniform temperature in the operating converter and by ensuring sufficient and specific placement of expansion allowance in the construction of the refractory brickwork. A combination of optimized crane availability, rapid matte transfer, converter operating practices, new refractory installation techniques and applications has minimized out-of stack time. In addition, larger diameter tuyere pipes and hard piping have increased blowing rates and lowered cycle times, which has resulted in a tuyere line performance in excess of 62,500 tonnes of blister copper before maintenance is required. This paper discusses the refractory installation design changes that were made to increase tuyere line life.

Jan 1, 1999

By Wilhelm Wendt

About five years ago we showed that it is possible to use the spectral in- formation in the light emitted by the off-gas flame of a PS converter for on-line production control. Very recently measurements have been performed using improved optical equipment and data evaluation software, resulting in both improved accuracy and the establishment of new optical process parameters. Using the optical signals the slag heats could be stopped at a predetermined Cu content of the white metal with an accuracy of +0.2% Cu m the range 74-78% Cu. A good correlation was found between the slag composition and optical data, providing a possibility for on-line monitoring of the SiO2 content of the slag. The measurements indicate the possibility of predicting the optimum end-point of the copper-making stage and having real time information on the impurity removal. Factors influencing the optical parameters, such as blowrate, Pb content, temperature etc. will be discussed.

Jan 1, 1993

By Harald Laux, Stein Tore Johansen

The plunging jet in tapping of steel from converters or electric arc furnaces entrains gas into the steel bath contained in a ladle. Gas entrainment rate and the effect of the gas on the flow pattern in the ladle are studied by means of Computational Fluid Dynamics CFD. The work focuses on the mathematical modeling. Two numerical methods, one for free-surface flows and one for dispersed multiphase flow are combined. A transport equation for the average bubble diameter that incorporates the effect of coalescence and breakup is presented. Results from computations for one ladle and tapping configuration are shown. Our findings indicate that the gas entrainment rate is affected by the material properties of the liquid in the sense that the material properties determine the shape of the jet. Moreover, bubble sizes in the range of two-orders of magnitude are predicted in the ladle. The dispersed diameter model seems to work well. It showed the expected response to material parameters and the turbulent field. However, the presented analysis is just a first step that was limited due to certain simplifications. In order to obtain better insight in the tapping process improvements of the analysis seem necessary.

Jan 1, 1999

By Dachun Liu, Baoqiang Xu, Bin Yang, Yong Deng, Heng Xiong, Xiumin Chen

"In this paper, vacuum distillation technology has been employed to study the possibility and regularity of separating copper and enriching lead, silver and other valuable metals from copper- based multi component alloys. The result of experiment indicated the practicability of vacuum distillation dealing with copper base complex multi-component alloy to separating lead and silver, when the vacuum distillation temperature was 1637K, distillation time was 60min; residual gas pressure was 20-30Pa, the removal rate of silver was 95.86%, of lead was 99.63%; the evaporation rate of copper was 0.745%. The removal rate of arsenic, antimony and tin respectively were 83.09%, 48.12% and 24.54%. Vacuum distillation method is applicable for dealing with the copper-based multi component alloys, silver and lead can realize effective recovery.IntroductionCopper generally go with lead mineral, therefore, to remove copper from lead becomes an inevitable link in lead smelting. Dross from removed copper usually contains lead, arsenic, antimony, tin and noble metal silver. In abroad, soda ash-iron dust is adopted to process copper dross of this kind. The outcomes of this process are lead matte, wet lead, scoria smoke dust etc[1~5] The dominant components of all the outcomes are copper and lead. Moreover, in the process of tin smelting, copper contained by-products are produced, such as, crude tin alloy, tin lead electrolytic anode slime and so on. Copper content of all the products are ranging from few percentages to several tens percentage. Those products, no matter merge into main producing process, or separate treatment cost losses of valuable metal. For one hand, the containing of copper of outcomes from pyrogenic attack is less than 50%, for the other hand, a lot of valuable metal need to be processed, which increase the cost of retrieve."

Jan 1, 2013

By Kazuyuki Kakegawa

"Sintered body of lead zirconate titanate (PZT) was prepared through the spark plasma sintering (SPS) technique. When the mixture of raw materials was calcined at 800°C and sintered at 900°C for 10 min. with SPS technique, the sintered body had almost theoretical density but was a mixture of lead titanate (PT) and PZT. When a calcining temperature of 1100°C was employed, sintered body had a single PZT phase but a lower density. High dielectric constant was obtained for a sample calcined at 800°C, sintered with SPS tecbriique and fired again in the air at 1100°C.IntroductionSpark plasma sintering (SPS) is a recently developed technique for sintering metals and ceramics1. The scheme of SPS is shown in Fig. 1. Sample is put in a graphite die in a vacuum chamber. It is pressed and pulse voltage is applied. The electric current heats the die. It is said that the pulse causes a spark-plasma between particles in the sample. Because of the spark- plasma, sample can be sintered at temperatures lower than that in the ordinary sintering by several hundred degrees of Celsius. The sintering period is also very short2Low sintering temperature and short sintering period in SPS technique cause low reaction rate. It is both disadvantage and advantage. In some cases, the reaction cannot be completed under the SPS conditions. If a mixture of several compositions having different properties can be sintered without a compositional change by the diffusion during the sintering, combination of properties, and therefore a design of property will be possible3. The low reaction rate of SPS may enable such combination."

Jan 1, 2000

By Yoshinao Kobayashi

he removal of oxygen from titanium and zirconium is important for use in application because it significantly affects the mechanical and physical properties such as ductility and toughness. However, thermodynamic properties of oxygen in molten titanium and zirconium have not been clarified and the effective deoxidation process of molten titanium and zirconium has not been established. In this study, the standard Gibbs energy of reaction of oxygen and yttrium in molten titanium and zirconium have been measured by a chemical equilibrium technique. Molten titanium, zirconium, and their alloys with aluminum were equilibrated with a Y2O3, A12O3, or Zr02 pellet in a cold crucible. The results are summarized as follows:

Jan 1, 2000

By Nicholas Zabaras, Deep Samanta

"Solidification of metal aluminum and aluminum alloys is modeled on uneven surfaces characterized by sinusoidal curves. Wavelengths and amplitudes of these sinusoidal surfaces are varied to study their effects on processes like solidification, macro-segregation and inverse segregation. Solidification and macro-segregation are modeled using a slightly modified form of a stabilized finite element method developed recently to model high Rayleigh number solidification and porous media flows. For pure metal solidification, the effect of varying amplitudes and wavelengths is observed in heat transfer, fluid-flow ~nd phase change processes. The relative importance of shrinkage driven flow and solutal convection on the redistribution of solute for an alloy solidifying in a rectangular cavity is compared. The analysis is then extended by modifying one of the surfaces to a sinusoid. In this case the effects of varying amplitudes and wavelengths are studied in heat transfer, fluid flow, phase change, macro-segregation and inverse segregation processes.1 IntroductionTransport phenomenon during solidification of alloys is a major cause ofcasting defects such as segregation, micro-voids, hot tears, porosity, internal and surface cracks. Heat flow across metal and mold surfaces directly affects the phase change process and plays an important role in determining freezing conditions within the metal. In alloys, natural convection and shrinkage play an important role in determining the final solute redistribution, macrosegregation and evolution of solid macromorphology. Surface unevenness plays an important role during the early stages of solidification. It influences the heat transfer rate and fluid flow in the melt, which in turn affect the morphology and shape of the solid-liquid interface. The effect of surface unevenness on solute redistribution is important during solidification of alloys, where solute driven flow in the mushy zone is prominent. Thevik and Mo in [7] and [8] used a one dimensional model for studying surface segregation and macrosegregation in alloys under the influence of exudation and solidification shrinkage. Air-gap formation in their model was expressed through a variable convective heat transfer coefficient at the boundary. Tsai et al. in [3] and [4] have modeled macrosegregation in an aluminum-copper alloy driven by shrinkage and solutal convection. They used a single domain model based on mixture theory and solved the transport equations using finite difference methods. Our aim is to model solidification of aluminum followed by macrosegregation and inverse segregation in aluminum-copper alloys on uneven surfaces by finite element methods. These surfaces are modeled as sinusoids characterized by amplitudes, ?s and wavelengths, As, By varying As and ?s, changes in heat transfer, fluid flow, phase-change and macrosegregation are studied."

Jan 1, 2004