By J. Wendt, P. R. Sahm, T. Uloth, M. Weck, F. Foertsch

"The FEM program systems CASTS (Computer Aided Solidification TechnologieS) (1) and FINELF (FINite ELement Frontal Solver) are used to optimize a thin walled die casting. After a short description of the programs it will be worked out how to use them not only for simulating solidification processes but also for optimizing the design of workpieces. The calculations will be done for an automobile's support bracket which is manufactured in a well known car factory in Stuttgart, FRG.IntroductionAt the Aachen Foundry Institute the software package CASTS was developped to simulate solidification of castings. In order to optimize the whole manufacturing process it does not appear sufficient any more to take into account only the specific aspects of casting. For instance one has to consider additionally the stress situation under service load. For this reason the Foundry Institute together with the Aachen WZL-Institute (Machine Tool Laboratory) and the car factory mentioned above started to probe into a first step in that direction. Figure 1 shows the support bracket which shall be optimized."

Jan 1, 1986

By K. Prashant Sarswat

Isotopes are critical to a variety of applications including physical science analyses, biology, medicine, pharmaceuticals, and national security. In most cases isotopes must be relatively pure or highly enriched before they become useful. Current isotope separation technologies are relatively inefficient, capital and labor intensive, and often produced by a limited number of suppliers. In the category of isotopes, lithium is among other important candidates. Lithium is found naturally in two isotopes, 6Li which accounts for 7.5% of all lithium, and 7Li which makes up the balance of 92.5%. Each of these isotopes is important to the nuclear industry. 7Li is often used in the form of lithium hydroxide which is used to control pH in pressurized water reactors. The current supply of 7Li is based mostly outside of the United States, and its long-term supply is uncertain. Apart from supply issues, the use of mercury for 7Li separation is also a concern in commercial processing using the most common and efficient approach [1–3]. Hence, a reliable, environmentally friendly, and efficient technique is needed to produce 7Li. In this line of investigations, the authors used a two-compartment system and significant separation was achieved. In this piece of research, some preliminary results are presented including cell design and actual isotope ratio after enrichment. Applying an electro-potential across two electrodes can be used to drive electromigration of Li isotopes. The electromigration is in addition to normal diffusion. Note that 6Li diffuses faster and hence there will be a lowering of the 6Li concentration near the positively charged electrode and an enhancement in 6Li near the negative electrode during the separation process. Similarly, 7Li will be more prevalent near the positive electrode and less prevalent near the negative electrode during the initial separation stage [1].

By Riqing Ye

Laser Engineered Net-shaping (LENS TM) is an emerging manufacturing technique that ensures significant reduction of process time between initial design and final components. The fabrication of fully dense parts with appropriate properties using LENS TM process requires an in-depth understanding of the entire thermal behavior of process. In this paper, the thermal behavior during LENSTM processing of 316 stainless steel was studied both numerically and experimentally. Temperature distribution and gradient in the fabricated 316 stainless steel part were obtained by Finite Element Method (FEM) simulation. The numerical results are in good agreement with the experimental observations. The numerical method may be used to optirnize process parameters and predict the thermal response of LENSTM fabricated components. Key words: Laser Engineered Net-shaping, Thermal Behavior, Finite Element Analysis

Jan 1, 2003

By Bowen Li

Copper vermiculite is a special nanomaterial with excellent antibacterial and antifungal performance. By means of ion exchange, copper vermiculite containing up to 5.8wt% copper was prepared. The chemical and mineralogical characterization of the material was investigated in this study based on the XRD, AAS, TEM and EDS analysis, as well as the calculation of crystalline parameters and crystal chemical formula. Cu2+ and Mg2+ have similar atom radius and same electrovalence. Correspondingly, the structure character of copper vermiculite is very close to that of standard Mg-vermiculite. Most of the CU21 may have occupied the interlayer cationic positions in the form of hydrate in vermiculite. However, some may have entered into octahedral coordinate positions. The values of au and bo of the copper vermiculite crystal cell have no obvious change compared to that of original vermiculite micropowder, but the Co value decreased slightly, which is desirable for the stabilization of the Cu2+ in copper vermiculite.

Jan 1, 2003

By G. Glinski, K. A. Pericleous

"Recent advances in new computational modelling techniques such as Lattice-Boltzmann and Dissipative Particle methods offer the prospect of simulating complex fluids such as colloidal and dense suspensions in industrial processes. They are referred to as mesoscopic methods since they lie between molecular dynamics at a microscopic atomistic scale «lO-9m) and traditional macroscopic CFD methods (> 1O-2m). The models behave like a 'coarse-grained' gas consisting of fictitious interacting particles, which are much larger than the real molecules of the actual fluid they represent. Inter-particle forces are set so that the collisions collectively mimic the phenomenological transport properties and flow of the underlying fluid at a macroscopic scale.Much of the developmental work to date has focused on laying theoretical foundations based on thermodynamic and kinetic theory. Successful applications include predictions of macroscopic transport properties of complex fluids and flows in porous media and filters. With the constant increase in computational power, these mesoscopic methods are now sufficiently developed to determine their suitability to simulate complex fluid flows in real industrial processes. This work describes the application of meso scopic methods to the stencil printing of solder pastes in the assembly of electronic components. The aim of this work is to assess the ability of these methods to study the transport mechanisms of individual solder particles suspended in the flux solvent as they enter and fill the micro-apertures of a stencil. This paper demonstrates the coupling of such mesoscopic methods to continuum CFD methods to predict the flow of dense suspensions (i.e. solder paste) in industrial processes."

Jan 1, 2001

By S. Shrivastava

A structure based model has been developed for the prediction of viscosities of K20-B20, melts. These melts exhibit an anomalous behavior of viscosity with continuous variation in B203 content. A maximum and a minimum are observed at low temperatures, which disappear on raising the temperature above the softening range. The addition of K20 to the borate melts causes two opposing phenomena: (1) depolymerization effects and the related breakdown of network structure resulting in the formation of singly bonded oxygens, which weakens the structure and hence causes a decreases in viscosity, and (2) the formation of four coordinated borons (BO4 tetrahedra) which strengthen the structure leading to an increase in the viscosity. The structural changes taking place in these melts on varying the temperature and the alkali content have been reviewed and are incorporated in developing this model. The predicted values are in excellent agreement with the experimental values over the whole temperature and composition range.

Jan 1, 1992

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of 873°K is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composition formed under roasting of concentrates with particle sizes less than 0.02 um (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CuFeSz2 each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forchamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By S. Mattlgod

Self-assembled monolayers on mesoporous supports (SAMMS) have been developed for the removal of heavy metals and some transition metals. The thiol functional groups were assembled on the internal and external surfaces of mesoporous silica with a uniform pore size of about 55 A. The mesoporous supports provide high surface area (>900 m2/g) needed for high metal loading in chemical separation. Self-assembled monolayers of organic molecules bond to the ceramic substrate with prescribed densities, and with terminal functional groups for excellent molecular selectivity. The unique characteristics include: (1) High metal absorption capacity, up to 3.2 mmol/g of SAMMS. (2) Fast Hg-binding kinetics (reducing mercury concentration from 0.5 ppm to 0.5 ppb in less than 5 minutes). (3) High selectivity in the presence of a range of cations, anions, and organic species. (4) Applicability in both aqueous and non-aqueous solvents. (5) Flexibility in surface chemistry. The materials can be designed to adsorb heavy metals, transitional metals, and radionuclides. (6) Chemical stability, and potential for regeneration or waste storage. This paper discusses the results on mercury adsorption.

Jan 1, 1999

By L. A. Bertram, F. J. Zanner

"The goal of this paper is to present a tool to simulate transient melting of the electrode tip. This capability is needed to develop and test furnace control algorithms since experimental determination is difficult and expensive. Simulation incorporates parameters (including arc voltage, arc current, electrode gap and furnace pressure) from previous quasi steady experiments with 460 mm diameter Inconel 718 electrodes.Cathode heating rates (determined by classical as well as experimental arc models) are linked to these independent variables. After radiative loss adjustments to the heating, transient one dimensional melting is computed. IntroductionThe vacuum arc remelting (VAR) process attempts to improve the physical and chemical homogeneity of a static-cast electrode by remelting and solidification in a quasisteady manner. To achieve steadiness of furnace operation requires automatic controls based on inputs measuring physically relevant state variables of the process. Previous industrial scale VAR studies (1,2,3) involving stainless steels, superalloys, and other alloys have provided a basis on which control strategies of some generality can be proposed (4). Of these measurements, the data for Inconel 718 is the most complete, so discussion in this paper is restricted to this alloy.Studies of the In 718 alloy subjected to the VAR process have established that melt rate M (kg/hr) depends not only on the melt current 1m (kA) supplied to the furnace, but also on ambient gas pressure of CO, PCO (micron), and electrode gap ge (mm) as well (1):"

Jan 1, 1986

By Chu Yong Cheng

Manganese is one of the main impurities in the recovery of base metals from their ores. This is especially true when laterite ores are processed using the pressure acid leach (PAL) process. The use of intermediate precipitation, solids/liquid separation and re-leach in the three Western Australian nickel laterite plants to separate nickel and cobalt from manganese and other impurities makes these processes complicated and costly in capital and operation. The research work carried out by the solvent extraction (SX) group at the A J Parker Cooperative Research Centre for Hydrometallurgy (CSIRO Minerals) has led to the development of direct solvent extraction processes to separate nickel and cobalt from manganese and other impurities. The simplicity of the process flowsheets and the expected savings in capital and operating costs are the major advantages of the new direct solvent extraction processes over the existing processes. By using a new synergistic organic system, Versatic 10 / dccyl-4-pyridinccarboxylatc ester, with a pilot plant leach solution from BHP¬Billiton (after iron precipitation), the metal values (Ni and Co) together with zinc and copper were separated from manganese and other major impurities (Mg, Ca and Cl) in the first SX circuit. The co-extracted manganese, magnesium and calcium were easily scrubbed out. The extraction and stripping kinetics of the metals with the new synergistic organic system were very fast and the synergistic system was found to be chemically stable. pH-extraction isotherms of metals with D2EHPA showed that the extraction order as a function of pH50 was Zn2+ > Ca2+ > Mn2+ > Cu2+ > Co2+> Ni2+> Mg2+. Semi-continuous test work with a cobalt pilot plant leach solution from Peko Rehabilitation Project Pty Ltd and a synthetic solution to simulate a concentrated laterite leach solution from BHP-Billiton showed that manganese, together with calcium, copper and zinc can be separated from nickel, cobalt and magnesium. This led to the development of another direct solvent extraction process to separate manganese and other impurities from nickel and cobalt and to recover nickel and cobalt from leach solutions. A project was initiated by HiTec Energy Ltd to recover manganese from waste laterite leach solutions using SX technology and to further purify it to produce high purity electrolytic manganese dioxide (EMD) for the high quality alkaline battery industry. Batch tests were conducted to select a suitable organic system for the extraction of manganese in terms of selectivity and extraction and stripping kinetics. A total of eight organic systems were tested using waste laterite processing solutions. A Versatie 10 / synergist system showed very promising results. By using the synergistic system, high manganese recovery would be obtained, fewer SX stages would be required and a higher A:O ratio could be used in extraction, resulting in a smaller organic inventory and lower capital costs. The risk of gypsum formation is also minimised with the synergistic system. Keywords: Solvent Extraction, Manganese, Laterite, Synergist

Jan 1, 2004

By Jun Chang, Jin-hui Peng, Jing Chen, Li-bo Zhang

The leaching of indium from refractory zinc oxide flue dust(ZOFD) is attempted to utilize microwave sulfating roasting process, followed by water leaching. The ZOFD and roasted product were characterized by XRD and SEM/EDS analysis. The effects of various roasting parameters, such as roasting temperature/duration, the proportion of sulfuric acid, as well as the leaching parameters such as the leaching duration and liquid/solid ratio, were assessed. The results indicate that nearly 97% of indium could be leached under the following conditions: mass ratio of concentrated sulfuric acid to ZOFD to be 0.5, roasting temperature of 150 ℃ and duration of 1.5 hours; while the optimal leaching conditions hold at temperature of 25 ℃ for 1 hour, with 4:1 of liquid/solid ratio. The indium leaching rate by the microwave roasting increased by 8% as compared with the conventional roasting process under identical conditions.

Jan 1, 2015

By M. M. Kim

Zn-27% Al was pressure infiltrated into a column of 20 micron diameter abrasive grade SiC particles to give billets with particle loading of 50 voli.une %. Some billets were heated to a temperature where they became semi-solid and diluted with liquid Zn-27% Al alloy to give billets with particle loadings of 12 and 16 volume %. Some of these billets were then extruded into wire with an area reduction of approximately 98%. Tensile properties of the as-cast billets were always inferior to those of the matrix alloys; however, the extruded composite samples showed at 37% improvement in ultimate tensile strength compared to their extruded conventional counterparts. The fracture surfaces of these samples are described.

Jan 1, 1990

By Junji Shibata

Heavier rare earth, which is contained in a small amount in ores such as bastnesite and monazite, has been accumulated as a heavier rare earth residue without doing separation and purification due to the lack of suitable methods. The heavier rare earth residue includes seven rare earth elements such as Tb, Dy, Ho, Y, Er, Tm and Yb. Separation and recovery process of Dy, Y, Tm and Yb from leached solution of the heavier rare earth residue was investigated by using a column method with solvent impregnated resin. The solvent impregnated resin was prepared by impregnation of organophosphorous extractant whose trade name is PC-88A into a macro porous resin, Amberlite XAD-7. It was almost impossible to separate them in simple adosorption and elution steps. However, we attained to individually separate Dy, Y, Tm and Yb from the leached solution first by changing eluent concentration gradually from pH2 to 0.02kmol/m3 HC1 in the elution step, and secondly by using a development column and changing eluerit concentration in the elution step. The separation process flow was proposed for a heavier rare earth residue by using the solvent impregnated resin method.

Jan 1, 1998

By Jiann-Yang Hwang

Microwave heating has been proved an effective method to rapidly heat iron oxide. This offers an opportunity to apply microwave heating in the steelmaking process. The reduction reaction of iron oxide is traditionally achieved at high temperature with reducing gases such as H2 and CO generated from various sources, including coke, coal, and natural gas. This study investigates the differences in iron oxide reduction using conventional and microwave heating under H2 and CO atmospheres. A special microwave thermal gravimetric device was designed and built to facilitate the investigation. With this device, iron oxides can be heated by electric resistance heating, microwave heating, or a combination of methods. The incoming CO and/or H2 also can be preheated to simulate a potential utilization of recovered heat. The iron oxide weight and temperature can be monitored during an entire reduction period. A series of reduction experiments have been conducted. The results are presented and discussed.

Jan 1, 2006

"Recycling of solid wastes plays an important role in environmental protection. However, solid wastes are often contaminated with some undesired components so that many of these solid wastes are hardly economically recycled. Therefore, effective and efficient separation of undesired components from solid wastes becomes a crucial step for sustainable recycling of the solid wastes. There exist three general strategies of separation of undesired components from solid wastes: before-process separation, post-process separation and in-process separation. In this paper, different separation strategies are discussed in terms of energy requirement and availability, implementation complexity and additional need for environmental protection. It is concluded that of all separation strategies, in-process separation has the least energy requirement, the least implementation complexity and the minimum need for additional environmental protection.IntroductionIn industries, solid wastes almost come with every production process. Multi-million tons, if not billion tons, of solid wastes are being generated globally each year. These solid wastes are lowvalue materials in general, and often have very limited markets. As a matter of fact, many of these solid wastes have been stored on site or have been disposed of at landfills for many years, not only occupying lands, but also polluting environment. Therefore, effective and efficient recycling of solid wastes has been a very challengeable task and has played a very important role in environmental protection.One of the major barriers which hinder recycling of solid wastes is contamination of the solid wastes with some undesired components. These undesired components are components which are not wanted by production processes or applications where the solid wastes are consumed or recycled, since the undesired components often degrade qualities of the solid wastes, imposing negative effects on operations, facilities and product qualities of the production processes or applications. Sometimes, the undesired components may also pose severe environmental concerns. When undesired components are present in solid wastes at over-limit levels, the solid wastes tum to become destructive, useless and non-recyclable. Consequently, effective and efficient separation of undesired components from solid wastes becomes a crucial step for sustainable recycling of the solid wastes."

Jan 1, 2014

By N. M. Komkov

The main operation of obtaining zinc from sulfide raw materials by hydrometallurgical technologies is the oxidation roasting of zinc concentrates in fluidized bed furnaces. The technical-economic parameters are determined by the parameters of the roasting process, which depend on the composition of the initial raw materials, the temperature of the bed and on other factors. The predetermined roasting temperature is maintained due to the change of specific efficiency as well as to the quantity of the heat removed from the bed. The efficiency of caissons depends at a high degree on the composition and the thickness of the accretion formed on the surface of the caissons. Forecasting the roasting results is impossible unless we know the mechanism of the accretion formation. The aim of the present paper is the thermodynamic analyses of the behavior of the charge compositions under roasting and the determination of the potential mechanism of the accretion formation. The thermodynamic analyses show that under conditions of the oxidation roasting the thermodynamic probability of the formation of zinc sulfate is higher than the probability of the oxide formation until a temperature of873 OK is reached. The thermodynamic probability of the formation of the lead sulfate is higher than the probability of oxide formation in the entire temperature range of roasting. The probability of formation of ferrites and silicates of zinc decreases only insignificantly the sulfate stability. The results of the investigation of the accretions composItion formed under roasting of concentrates with particle sizes less than 0.02 J..lm (60%), containing 65% of sphalerite (ZnS), 12% of pyrite and chalcopyrite (FeS2 and CufeSz) each, 3% of galenite (PbS), 7% of silica and other non-ore minerals, have shown that the composition of accretion varies depending on the depth of the accretion layer. The accretions on the caissons and the thermo-siphons consist mostly of zinc sulfate (more than 50%). The accretions of forehamber consist mostly of zinc oxide. They also contain ferrites and silicates. The formation of the sulfate zinc accretion in the cold parts of the fluidized bed furnace (the caissons and thermo-siphons) may be explained by a lower temperature on the surface and probably by a catalytic influence of the present oxides in the formation of S02 and sulfates. The nature of the structure of the accretion in the hotter parts of the furnace may supposedly be explained by the formation of elemental vaporous zinc during roasting.

Jan 1, 2003

By P. V. Ananthapadmanabhan

Feedstock powders of metals, alloys and ceramics for thermal spray applications have to meet several specifications. Particle shape, size and distribution, powder flow characteristics and density are the important factors that need to be controlled, in order to ensure high spray efficiency and better coating properties. Thermal plasma technology can be effectively utilized to produce metal, alloy and ceramic powders for spray applications. The present paper describes plasma spheroidisation of commercially available aluminium powder and nickel-aluminium powder blend in a plasma reactor. Results show that the processed powder particles bear spherical morphology with excellent flow characteristics, which make them ideal for thermal spray applications.

Jan 1, 1997

By J. A. Gonzalez-Dominguez

During the electrorefining of lead by the Betts process, ionic concentration gradients become established within the slimes layer. These gradients contribute to precipitation of secondary products and to gradients in electrode potential applied to slimes filaments, and thereby affect the dissolution of noble impurities. This paper describes the experimental results obtained when a typical lead anode was dissolved under galvanostatic conditions with concurrent interruption of current at preset slimes thicknesses. Reference electrodes were incorporated within the lead anode to follow the potential gradients across the slimes electrolyte. Samples of the slimes electrolyte were withdrawn in-situ and their compositional changes were related to transport processes across the slimes layer. Upon current interruption the anodic overpotential decays, first abruptly (as the uncompensated ohmic drop disappears), and then slowly (due to the presence of a back E.M.F. created by ionic concentration gradients that decay slowly). Current interruption measurements showed that: (A) concentration gradients exist across the slimes layer, (B) inner solution potentials within the slimes layer can be larger than those measured from reference electrodes located in the bulk electrolyte, (C) secondary products can shift the inner solution potential to negative values that reverse upon re-dissolution and (D) ionic diffusion is seen upon current interruption but it is complex and difficult to model due to the presence of processes that can support the passage of internal currents. SEM and X-ray diffraction analysis of the slimes filaments indicated that secondary reactions leading to the formation of Si02 and PbF2 take place (mainly at the anodelslimes interface). The onset of these reactions and their relationship to the Pb-F-Si-H20 Eh-pH diagram are linked to the industrial operation of the Betts process.

Jan 1, 1994

By F. H. Froes, O. N. Senkov, N. Srisukhumbowornchai

"Mechanical alloying (MA) and thermohydrogen processing (THP) approaches were used to synthesize amorphous or nanocrystalline powders of the titanium-aluminide-based alloys and composites. Fully dense samples with nanocrystalline and bimodal structures were produced from these powders by hot isostatic pressing. The stability of the microstructures during continuous heating at high temperatures was studied. Characterization techniques including X-ray diffraction, scanning and transmission electron microscopy, energy dispersive spectroscopy, and differential thermal analysis were used in this work.IntroductionAs performance demands increase, so do the demands for enhanced mechanical property combinations at reduced overall weight; and reduced weight can most efficiently be realized by the use of low-density metals with high specific strength, such as titanium alloys and titanium-aluminum intermetallics [l]. The TiAl-based alloys are attractive for high temperature applications, however, they exhibit poor ambient temperature ductility and fracture toughness [2-4]. Incremental improvements can be obtained using ingot metallurgy processing [1,2] but more substantial developments require ""far from equilibrium"" (FFE) synthesis [5-8] which allows development of novel constitutional and microstructural effects, leading to enhanced physical and mechanical properties. Improved ductility of titanium aluminide intermetallics can be achieved by disordering, grain refinement and deoxidation of the matrix, while good elevated temperature properties are achieved due to a dispersion of fine, thermodynamically stable, second phase particles.The approaches for producing nanocrystalline and amorphous TiAl-based alloys and composites used in this work included FFE powder metallurgy techniques such as rapid solidification, mechanical alloying and thermohydrogen processing. The rapid solidification (RS) technique allows extension of solubility limits, production of novel phases, and much more refined microstructures (down to nanostructure or even amorphous range) than is possible using the ingot metallurgy technique [9]. Mechanical alloying (MA) is a process in which heavy working of powder particles results in intimate alloying by repeated deformation, fracturing and welding. This process can produce greater departure from FFE than RS, leading to greater refinement effects; and additionally allows production of a dispersion of second phase particles [10]. Thermohydrogen processing involves hydrogen as a temporary alloying element in titanium to facilitate processes, refine microstructure, and improve final mechanical properties [11]; it was used in the present work to improve MA process. The combination of these three processes was expected to control the final microstructure even better than either process used alone."

Jan 1, 1998

By Donald J. Hallbom

Limonitic nickel laterites slurries exhibit complex rheological properties including time dependency that varies from thixotropy to rheopexy. Chronic problems may occur if plant designers and operators fail to take time dependency into account. Stress decay tests indicate that laterite slurry takes roughly two minutes to approach steady state after a step change in the shear rate. As a result, most rheometer measurements are taken at a non-equilibrium state, making evaluation difficult. Two minutes is also long relative to the time that a unit of slurry in a processing plant is at any given shear state, so the slurry may never reach equilibrium. This paper presents a method to describe the rheology of laterite slurry using a Flow Array, which describes the rheology using an array of instantaneous flow curves crossed by an equilibrium flow curve. A rate equation for structural change in non-equilibrium conditions allows time dependence to be efficiently modeled. This flow array allows the flow behavior of time- dependent slurry to be predicted in non-equilibrium conditions using a simple time-step methodology. Keywords: Rheology. nickel laterite, hydraulic transport, pressure acid leach, flow array

Jan 1, 2004