By S. E. Khalafalla

A method for preparing ferrochromium alloys containing less than 2 pct carbon has been devised in a single vacuum furnace reactor. This method can conserve chromium and should reduce the capital and energy requirements relative to chromite electrothermal reduction. Reduced products containing less than 2 and as low as 0.01 wt pct carbon were obtained by reacting pellets of chromite and carbonaceous reductant mixtures at pressures of 0.1 to 1 ton and temperatures of 1,230° to 1,320° C. The extent of reduction increased with increased temperature and decreased pressure; however, operating conditions were limited due to the onset of significant chromium vaporization at higher temperatures and lower pressures. Foundry coke, anthracite, and carbon black were found to be superior to graphite as reductants. The reduction of chromite to metallics was found to proceed via the carbide intermediates Fe3C or Cr3C2. Lime accelerates the. rate of solid state reduction of chromite and can shorten the furnacin1r time at 1,3000 C under vacuum from 13 hours to less than three hours. Additional lime and silica are added to the hot reduced chromite after releasing the vacuum and raising the furnace. temperature to 1, 700° C. Soaking the charge for about 20 minutes gave a button of low carbon ferrochromium alloy beneath a well-defined slag layer.

Jan 1, 1985

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By Alwin Frei, Aldo Steinfeld, Peter G. Loutzenhiser, Enrico Guglielmini

"Using concentrated solar radiation as the energy source of high-temperature process heat, the carbothermal reductions of Al2O3 to Al and SiO2 to Si were examined thermodynamically and demonstrated experimentally at vacuum pressures. Reducing the system pressure favors Al(g) and Si(g) formation, enabling their vacuum distillation and avoiding contamination by carbides and/or oxycarbides. Exploratory experimentation in a solar reactor was performed with mixtures of charcoal with alumina and silica in the ranges of 1300-2000 K and 1997–2263 K, respectively, at 10-3 bar by direct exposure to concentrated thermal radiation. Distilled samples contained up to 19 wt% of Al in Al-Al2O3 mixtures and 79 wt% of Si in Si-SiO2 mixtures. When the reducing agent is derived from a biomass source, the solar-driven carbothermal processes are CO2 neutral.IntroductionMetallurgical extractive processes for producing Al1-2 from Al2O3 and Si3-6 from SiO2 are characterized by their high specific energy consumption and concomitant emissions. Alternatively, concentrated solar energy can be used as a high-temperature heat source to drive the carbothermal reductions and, thus, avoid greenhouse gas emissions and other pollutants derived from fossil-fuel-based processes7-12. When the reducing agent is biomass charcoal, the solar-driven carbothermal reduction is CO2 neutral. The carbothermal reductions of Al2O3 and SiO2 are represented by the simplified overall stoichiometric reactions:"

Jan 1, 2011

By M. I. Brasileiro

The use of experimental design to the study of mixtures has found a wide range of applications, even in laboratory scale or in industrial development works. The aim of this work was to maximize granite sawing waste content in ceramic tiles using experimental design. Based on the raw materials, specific formulations were developed using the experimental design. The raw materials were mixed and sample bodies were produced using uniaxial pressing. The sample bodies were fired and characterized in terms of water absorption, mechanical strength and X-ray diffraction. Regression models were adjusted relating the water absorption and mechanical strength with the amount of raw materials. The results showed that the methodology of experimental design maximize the content of wastes incorporated in ceramic tiles formulations. Formulations containing up to 40% of waste can be used for the production of ceramic tiles.

Jan 1, 2009

By Christoph Sagadin

Corrosion mechanisms between high melting synthetic ferronickel slags and refractory were investigated. The used slags were prepared by mixing and melting of specific oxides. Substrates of the applied refractory material and specimens of FeNi slags were heated in a hot stage microscope up to 1650 °C. The experiments were performed under a defined gas atmosphere of 60% CO and 40% CO2. A further examination of the formed phases between slag and refractory occurred by scanning electron microscope. The investigations indicate that the slag penetrates between magnesia grains and partly dissolves magnesia. Spot analyses show that iron diffuses into the magnesia grains, which transform to magnesiawustite, meanwhile SiO2 forms different types of olivine like forsterite and monticellite. Thermodynamic calculations confirm the formation of these phases. The combination of practical lab scale experiments and thermodynamic calculations should finally contribute to an improvement of the refractory lifetime and performance.

By G. Bjorling

After complete dissolution of chalcopyrite concentrate in sulphuric acid in presence of nitric acid the excess of the latter is expelled by a surplus of concentrate and the last traces of nitrate removed in the mother liquor after crystallization of the copper and iron sulphates. Zinc accumulates in the mother liquor from which it can be removed by solvent extraction of zinc sulphate as a pair of ions. After dissolution of the sulphate crystals in water the neutral solution is oxidized in an autoclave at 140°C where iron sulphate is thermally hydrolyzed; the iron-free solution is taken to copper electrowinning and the cell acid after partial evaporation recirculated with the mother liquor to the leaching circuit. Total recovery of copper is about 96%; other metals like zinc and iron are concentrated in industrially usable products. At a copper price of about 70 c/lb, the method appears to be profitable also in a small unit.

Jan 1, 1976

By SenYang Qian, ShuangYu Du, Bo Wang, Jieyu Zhang, Jian Zhao

During the solidification process, the flow pattern of the molten steel has significant influence on the formation of solidification microstructure. In present study, the solidification microstructure of 30Cr2Ni4MoV steel ingot under different intensities of mechanical oscillation(forced convection) was simulated by using ProCAST®software. The results showed that the increase of the intensity of oscillation could restrain the development of the columnar grains and refine the grains. As the intensity of oscillation increased, the proportion of columnar grains decreased and the proportion of equiaxed grains increased. When the intensity of oscillation was at a low level, the effect of refining grains could be improved obviously by increasing the intensity. However, as the intensity increased to over 0.833, the effect of refining grains would not be improved.

Jan 1, 2016

By C. E. Hunt

Since the turn of the century, copper-nickel sulphide ores have been processed at the Sudbury, Ontario operations of INCO Limited, currently the largest integrated mining, milling, smelting and refining complex in the free world. Through the years operational, ecomomic, social and legislative changes have dictated the need for research and development directed at mitigating the impact of existing operations on the surrounding natural environment and also the reclamation of areas affected by earlier mining activities. Approximately one hundred years of mining history and the current annual processing of some 12 million tons of ore presents significant challenges with respect to waste disposal, liquid effluent treatment and land reclamation, particularly in light of rapidly evolving environmental regulations' and controls within the Province of Ontario.

Jan 1, 1992

By Marcelo B. Mourao

Interactions of carbonaceous materials with liquid Fe-C melts have been investigated experimentally by determining the volatile yield due to rapid devolatilization (Flash Pyrolysis) and rates of dissolution at temperatures ranging from 1623 to 1873 K. The volatile yield increased with increasing the temperature. The comparison of results of different types of carbonaceous materials was possible by expressing the volatile yield in terms of Enhancement Factor, fE. The rates of dissolution of spectroscopic graphite and an industrial coke seemed to obey the correlation for natural convection under turbulent conditions. The experimental data for the graphite suggested that the rate of dissolution was controlled by the mass-transfer in the liquid boundary layer adjacent to the solid sample. The value for the empirical parameter correlating the dissolution coefficient and the operating variables was found to be 0.19 which was close to that reported in the literature. The comparison of the results obtained for the coke samples with those for the graphite revealed that the impurities and the porosity of the samples can effect the dissolution rates.

Jan 1, 1992

By Kenneth N. Ham

Hydrometallurgy covers a wide spectrum of areas and its knowledge base is enlarged and enhanced by contributions from many other fields. Dissolution of metals and alloys in aqueous media will be used to illustrate how rich the field of metal extraction can be. Comprehensive understanding of the fundamentals of metal and alloy dissolution in aqueous systems requires creative application of thermodynamic principles, solutions chemistry, ligand complexation theory, electrochemistry, transport phenomena and heterogeneous kinetics. In addition, recent developments in instrumentation in the fields of interfacial phenomena and corrosion have tremendously advanced the field of metal extraction in aqueous system. The close relationship between metal extraction in aqueous systems and various physicochemical phenomena occurring in corrosion and interfacial systems will be discussed and illustrated with examples.

Jan 1, 2002

By Richard D. Hagni

Polished sections of pyrometallurgical intermediate products from a simulated commercial flash furnace were examined by reflected light microscopy, scanning electron microscopy-energy dispersive spectrometry and electron backscatter analysis, and microprobe analysis for phase and textural relationships. The smelter feed is a copper concentrate from a porphyry copper deposit. The concentrate consists primarily of chalcopyrite, bornite and pyrite with smaller amounts of covellite, chalcocite, molybdenite, magnetite, galena, and sphalerite. The flash furnace reactions for pyrite and chalcopyrite can be observed by reflected light microscopy. Reacted angular particles of pyrite exhibit successive rims of fibrous pyrrhotite and hematite or magnetite. Reacted angular chalcopyrite particles show successive rims of bornite, digenite, and chalcocite. Spherical particles, formed by the complete melting of former pyrite particles, consist of variable amounts of granular pyrrhotite with magnetite rims and minor hematite. Spherical particles, formed by the complete melting of former chalcopyrite particles, exhibit exsolution intergrowths with varying proportions of intermediate solid solution, bornite, digenite, and chalcocite and have rims of hematite, magnetite, and copper-iron spinel. Sphalerite and molybdenite do not show evident mineralogical reactions.

Jan 1, 1987

By A. A. Shook

The off gas from the #5 converter at BHP Copper's San Manuel smelter was analyzed continuously over a period of several weeks using an online sulfur dioxide analyzer. These data have shown that the oxygen utilization efficiency of this copper converter was somewhat lower than anticipated, and that oxygen efficiency declines significantly during the copper blow. A sharp reduction in sulfur dioxide generation was consistently observed at the end of the copper blow, which could be used by converter operators to prevent over-blowing and minimize rolling out of stack.

Jan 1, 1999

By Guohui Zheng

The ever increasing quantities of solid wastes generated by various industries are at the source of the growing need for proper waste disposal methods. Thermal treatment of combustible wastes is a proven technology which permits the reduction of hazardous material having to be landfilled. However, this method is not universally applicable to waste disposal. For example, the transferal of heavy toxic metals into the thermal remediation products is a major issue of public concern. This paper focuses on the analysis of morphology changes from solid sludge to ash which is a product of the sludge combustion. The morphological parameters analyzed were particle size and external surface. They were determined using Jeol 840 Super Probe. The experiments were conducted in a computer-controlled high-temperature combustion system consisting of the thermogravimetric furnace coupled with Fourier transform infrared spectrometer (TGA-FTIR). Sludge particles were made of complex fibers trapped in the aluminosilicate matrix. At low temperatures, up to 680 K, the solid residue looked similar to the initial sludge. Between 680 K and 1180 K the sludge underwent intensive burning and steadily changed into powdered ash. At the temperature of 1050 K the ash was composed of separate, flat flakes with sizes ranging from 5 to 20 um. At 1470 K the flakes aggregated into large particles. The surface observed at 1670 K was a mixture of mullite crystals. Such structure could result from the solidification of the ash material after its melting. Morphological changes influenced the distribution of metals in the solid residue. For example, Cr was concentrated in small aggregates. Such distribution should allow for recovery of valuable metals from the solid waste residue.

Jan 1, 1996

By M. GONZALES-FERNANDES M

Natural rubber/organophilic clay nanocomposites were prepared and characterized. A brown bentonite from Paraiba’s State, Brazil was modified with a sodium salt and treated with quaternary ammonium salt hexadecyltrimethyl ammonium chloride. The clay in its natural state, after cation exchange with sodium and after organophilization was characterized by XRD, IR, SEM, thermal analysis. Nanocomposite samples were prepared containing 10 resin percent of organophilic clay. The vulcanized samples were analyzed by XRD, SEM. The nanocomposites obtained showed improvement in their mechanical properties in comparison with samples without clay.

Jan 1, 2015

By James P. Bennett, Jasper Kwong

As concerns about the environment and the disposal of industrial wastes increase, the utilization of spent refractories from electric arc furnaces (EAF) is receiving more attention. Longer service life of refractories in an EAF can be achieved by foaming MgO saturated slag. The refractory wastes removed from a melt shop can be utilized as a part of these slags. The Albany Research Center is conducting research on recycling spent basic refractory materials as EAF slag conditioners. A good foaming slag should be a creamy, MgO saturated slag, which contains some solid particles (MgO-FeO). A computer model was developed to calculate the dual saturated slag chemistry with respect to CaO and MgO, the MgO saturated slag chemistry, and the solid content in solution. The effects of C/S ratio, AhO3 and temperature on the MgOsaturated slag as calculated by the model will be discussed.

Jan 1, 2000

By Dumitru Mitrica, Vasile Soare, Elvira Alexandrescu, Mihai Ghita, Marian Burada, Petru Moldovan, Raluca Maria Florea

"Aluminum metal matrix composite Al-Si /SiCp was prepared by reactive gas injection and subsequent remelting. The influence of the remelting process on the microstructure and physicalmechanical properties of the resulted material was investigated. Samples resulted from the synthesis process contained silicon carbide agglomerations in the vicinity of primary silicon and large pore concentrations. In-situ formed silicon carbide presented mostly a polymorphic structure with particle sizes varying from 1 to lOµm. Physical and mechanical properties were largely influenced by the porosity distribution. The remelting process provided a decrease in the composite material porosity and pore size, with significant improvements in the particle distribution and physical-mechanical properties of the composite material. Additions of up to lwt.%Mg in the starting alloy improved the in-situ carbide formation and particles distribution in the solidified material. However, stable and large particle agglomerations were detected in the material in absence of conventional stirring or controlled solidification techniques.IntroductionThe remarkable properties of composite materials (yield strength, stiffuess, hardness and resilience at a reduced specific weight) make them attractive for applications in automotive, aerospace and military industries. Particle reinforced aluminum metal matrix composites (PAMMC) are known for their high strength to weight ratio. The recent development of P AMMC created the possibility to obtain large particles concentrations, exceeding 10% by volume ofreinforcement (SiC, AIN, Al203, etc.). The improvement ofhigh temperature strength and wear resistance made them appropriate for the use in automotive applications, such as the pistons, rotors, disc brakes, and propeller shafts [ 1]. The present main disadvantage of the P AMMCs is their high costs for obtaining and processing related to the final product performance. In order to benefit from the advantages that offer composite materials properties a reasonable production cost - performance ratio must be obtained [2]. Recent innovations in the manufacturing of aluminum-based metal matrix composites provided notable performance improvements but no feasible solutions were found for lowering their present high prices."

Jan 1, 2014

By Jagdish C. Agarwal

Although copper ranks very low in the order of abundance of elements in the crust of the earth, it has been one of the first metals utilized by mar, at his emergence from the Stone Age, about 10,000 years ago. Use of copper for weapons, tools, utensils and ornaments dates back to the twilight of history, 6,000-5,000 B.C. Native copper outcrops and the malleability of the metal explain its very early use by the cave-dwellers. The working, melting and extraction of copper from its minerals are among the oldest metallurgical achievements of the human race. The oldest complete smelting installations for the extraction of copper from its minerals, dated about the fourth millenium B.C., were recently discovered in the Timna Valley, Wadi Arabah, Israel. (1) The history of the developments of the extractive metallurgy of copper has been adequately reviewed recently. (2,3) The center of copper production migrated from the Eastern Mediterranean to Northern Europe (Mansfeld, Germany, Swansea, Wales) towards the end of the Middle Ages (1500 A.D.). The production of the metal was boosted tremendously in North America since the end of the nineteenth century (Fig. 1).

Jan 1, 1976

By B. Mishra

The major waste product of the alkaline extraction of alumina from bauxite [Bayer Process] is known as red-mud. Approximately, a ton of red-mud is produced for every two tons of bauxite that is mined. The red-mud produced from Jamaican bauxite is rich in hematite, alumina and titanium oxide. It has been shown that over 90 wt. pct. alumina can be recovered from red-mud by soda-ash sintering and caustic leaching. Hematite can be carbothermically reduced with a degree of metallization of over 94 pct. At this stage, the product could be charged through the tuyeres in an iron blast furnace or smelted to produce pig iron. The mineralogical characteristics of the reduced product are not amenable to magnetic separation for iron recovery. The problems associated with the use of reduced red-mud as an alternative to direct-reduced iron [DRI] has also been discussed. Special attention has been paid to lower the alkali content of the reduced material. If smelted, the concentration of titanium oxide in the slag will be significantly high justifying its recovery by an acid-leach process. This paper describes the successful efforts of iron and alumina recovery.

Jan 1, 2000

By Kazusuke Sato, Takahiro Uno, Koji Hoshino

"A novel Ni coating technique of Ni(OH)2 powders was developed to improve the positive-electrode performance· of the Ni-MH batteries. It was found out that Ni(OH)2 powder was reduced by N2H4 without any catalysts in an alkaline - solution at high temperatures. In result of observation of pH and potential changes in the solution during the reaction, it was found that the reduced species was HNio2- ion dissociated from Ni(OH)2 in the alkaline solution. The molar fraction of reduced Ni of the Ni(OH)2 was increased in proportion to the amount of added N2H4. At the small Ni fraction, a porous Ni layer was formed on the surface of Ni(OH)2 powder. Open cell tests were carried out with the paste type electrodes made of either the Ni coated Ni(OH)2 powder or non-coat powder, and cell performances were compared. In result, it was found that the Ni coating technique is effective on improvement in the utilization of Ni(OH); as a positive-electrode active material under high current densities.IntroductionNi-MH rechargeable battery is generally used for the power source of portable machines and electric vehicles because of its good performance at high energy density and. long term cyclical life as well as cleanness and good safety. Cell component materials have been improved respectively, and as concerns ·the positive-electrode reducing 'the internal resistance is a principal problem to improve the discharging performance at higher current densities.In recent years, improved Ni(OH)2 powders coated with conductive materials as NI. or CoOOH have been developed for the· positive-electrode active materials in order to· reduce the internal resistance of the electrode1)· 2) The Ni coated Ni(OH)2, however, is costly because it is fabricated by .the -non-electrode plate technique which needs a expensive precious ·metal catalyst as PdC12We found that Ni(OH)2 powder was reduced by N2H4 without any cryatalysts in an alkaline solution at high temperatures. After the treatment, Ni(OH)2 powder become gray color like Ni powder from light-green color; and. turned into a magnetic. In this study, the mechanism of the -reducing reaction was investigated to apply the reactions .to a novel Ni coating technique of Ni(OH)2 powders, · and the performance of the Ni coated Ni(OH)2 powder obtained by the reducing process was evaluated as an -positive-electrode active material of Ni-MH batteries."

Jan 1, 2000

By A. Patti, S. Reutzel, D. M. Herlach, L. Ratke, I. Egry

Cu-Co shows a metastable miscibility gap in the region of the undercooled melt. Undercooling of the melt below the binodal leads to separation of the melt into a Co-rich LI-phase and a Curich L2-phase. Experimentally, undercooling into the metastable miscibility gap is realised by means of electromagnetic levitation (EML), processing in drop tube (DT) and by melt flux embedding. As undercooling is large in these experiments, the velocity of the solidification front is high and the microstructure is frozen in instantaneously. Samples have been undercooled and solidified in the TEMPUS-facility (container less electromagnetic processing under weightlessness) during parabolic flight under reduced gravity conditions. Microstructures of solidified samples have been analysed and compared to those processed under gravitational conditions. The influence of convection on phase growth is much lower in reduced gravity. The microstructure shows spherical droplets of the minority phase, statistically dispersed in the majority phase.

Jan 1, 2004