By Jiangtao Li, Zhongwei Zhao, Xingyu Chen, Xuheng Liu

In order to produce good quality ammonium paratungstate, Sn needs be removed efficiently from the tungstate processing solution. The nascent hydrous ferric oxide has excellent adsorption ability and is often used as an adsorbent to remove metal ions from aqueous solution. In this paper, nascent hydrous ferric oxide is used to remove Sn from tungstate solution. Through experimental, the effects of pH value, reagent amount of adsorbent, reaction temperature and reaction time on the Sn removal are investigated. The study shows that 98% of Sn can be removed effectively from sodium tungstate solution and only 2% of W is lost during process under the conditions of pH 9~12, reagent amount of Fe addition 40 times Sn amount, reaction time 30min and room temperature. As the Fe addition reaches 90 times of Sn concentration in the ammonium tungstate solution, 99% of Sn is removed and APT with zero level purity national standard is obtained.

Jan 1, 2014

By Wenbo Luo, Kang Liu, Jilai Xue

"Coal fly-ash(CFA) from thermal power plants is rich in Al2O3, which has great potential as an alternative resource for alumina production. In this work, Alz03 contained in the coal fly-ash was extracted using an acid sintering-leaching process. This process was enhanced by aid of power ultrasound during the leaching. The recovery rate of Al2O3 was increased with ultrasound, compared with the similar process without ultrasound under the identical operation conditions. Leaching temperature can be lowered by about 10-l5°C and the processing time reduced by about 50%. The process kinetics were investigated in details for a better understanding of the fundamentals on the effects of power ultrasound. The obtained results demonstrate the potential application in reducing processing energy and increasing production rate.Introduction Coal fly ash is a typical solid waste generated from coal combustion in thermal power station. Vast amount of CF A accumulation lead to serious environmental problems such as air and water pollution, cropland occupation, radioactive contamination, etc. However, CFA is rich in Al2O3 and SiO2 content, so that it has a potential use as recourses for alumina and silica production [1]. Aluminum industry, especially in China, has made a rapid expansion in recent years accompanying with a large amount of bauxite consumption, resulting a urgent demand to develop secondary alumina resources like CF A to maintain a sustainable development of aluminum industry that faces grim challenge [2].Acid leaching is an efficient technology to use in alumina extraction from CF A. Since the particle of CF A is not naturally existed mineral but was formed in molten state at high temperature, the internal Al-O-Si bonds are so strong to separate alumina from the ash particle. Because of this reason, the direct acid leaching [3-6] operated at ambient temperature has low extraction efficiency, approximate 30% to 40%, which is attributed to self inhibition effect from CaS04 generated by reaction between CaO and H2S04 [7-8]. High pressure leaching can efficiently decompose mullite to release A12O 3 content in the fly ash particles, but this requires autoclave material having strong acid corrosion resistance, high temperature (100°C-300°C) and pressure (1.0MPa-2.SMPa) resistance while its operating security is low and its acid consumption is large [9]. Concentrated acid boil process is conducted at near acid boiling point (200 °C - 300 °C) in 4 mouth flask wrapped by electric heating jacket with high mass ratio of acid and ash to achieve high Al203 recovery rate from CFA. Its disadvantages are similar to the high pressure leaching technology except no-pressure, and also the operating solution at nearly boiling point acid may easily spill and splash with additional acid loss and potential safety hazard [10]."

Jan 1, 2014

By J. T. I. Poijärvi

The smelter off-gas cleaning and the weak acid treatment at Outokumpu Harjavalta Metals Oy are presented and described in this paper. The smelter consists of the copper and nickel smelters and the acid plant of three separate acid plants two of which are double contact and one single plant and of one liquid sulphur dioxide plant. The preliminary cooling and flue dust separation of the smelter off....,gases from the copper ?and nickel flash smelting furnaces and converters? in the waste heat boilers and in the hot electrostatic precipitators are described. The final cooling and cleaning of the gases in the scrubbers at the sulphuric acid plant and the treatment of the weak acid in the vacuum and in the submerged combustion evaporators for the removal of impurities are presented as well as the treatment of the condensates from the evaporators. The attention is paid to the generation of sulphur trioxide in the smelter off-gas.and to the treatment of that in the weak acid bleed-off and to the utilization of the treated acid.

Jan 1, 1992

By Dachun Liu, Baoqiang Xu, Bin Yang, Yong Deng, Heng Xiong, Xiumin Chen

"In this paper, vacuum distillation technology has been employed to study the possibility and regularity of separating copper and enriching lead, silver and other valuable metals from copper- based multi component alloys. The result of experiment indicated the practicability of vacuum distillation dealing with copper base complex multi-component alloy to separating lead and silver, when the vacuum distillation temperature was 1637K, distillation time was 60min; residual gas pressure was 20-30Pa, the removal rate of silver was 95.86%, of lead was 99.63%; the evaporation rate of copper was 0.745%. The removal rate of arsenic, antimony and tin respectively were 83.09%, 48.12% and 24.54%. Vacuum distillation method is applicable for dealing with the copper-based multi component alloys, silver and lead can realize effective recovery.IntroductionCopper generally go with lead mineral, therefore, to remove copper from lead becomes an inevitable link in lead smelting. Dross from removed copper usually contains lead, arsenic, antimony, tin and noble metal silver. In abroad, soda ash-iron dust is adopted to process copper dross of this kind. The outcomes of this process are lead matte, wet lead, scoria smoke dust etc[1~5] The dominant components of all the outcomes are copper and lead. Moreover, in the process of tin smelting, copper contained by-products are produced, such as, crude tin alloy, tin lead electrolytic anode slime and so on. Copper content of all the products are ranging from few percentages to several tens percentage. Those products, no matter merge into main producing process, or separate treatment cost losses of valuable metal. For one hand, the containing of copper of outcomes from pyrogenic attack is less than 50%, for the other hand, a lot of valuable metal need to be processed, which increase the cost of retrieve."

Jan 1, 2013

By K. Olsen

As aluminum alloy usage in automobiles grows, there are increasing demands on recycling processes and facilities to deal with mixed alloy automotive aluminum scrap. These processes and facilities strive to produce near virgin aluminum stock, which can be relatively costly and difficult. One alternative is to use physical processing methods to upgrade the scrap properties instead of chemically refining the scrap. The Impulse Atomization Process (LAP, patent pending) is a new process for making metallic and ceramic powders. It can produce fine homogeneous microstructures in scrap aluminum alloys due to high undercooling and rapid solidification. The particles have a very narrow size distribution and are in a convenient form for consolidation. This paper compares and contrasts the microstructural features of Impulse Atomized. and quenched Impulse Atomized powders,' for both AL6061 and a scrap aluminum alloy composition.

Jan 1, 1995

By Ann M. Hagni

"Ceramic matrix composites are inorganic materials that are particularly resistant to heat and abrasion. A magnesia (MgO) and aluminum nitride (AlN) based composite is formed by exposing a magnesia preform to a metallic alloy block in a nitrogen atmosphere at 950°C. The metallic alloy, which is composed primarily of aluminum, is wicked into the preform. Aluminum nitride matrix is grown between MgO particles as the wicked metallic aluminum reacts with nitrogen. Unused metallic alloy, remnant metallic alloy (carcass), and composite produced after 8 hours, 50 hours, and 225 hours of processing are characterized mineralogically. Reflected light microscopy, transmitted light microscopy, scanning electron microscopy, energy dispersive spectroscopy, and X-ray diffraction techniques reveal that in addition to anhedral to euhedral AhNi, AbSbSr, and Al crystallizing in the metallic alloy carcass, AIN and (Al,Si)N have formed as well. Nitride rings and nodules in the carcass may hinder AIN growth in the composite. Fine-grained residual AhNi and AhShSr are dispersed throughout the composite matrix. The nitride matrix is composed of AIN and (Al,Si)N. Rim replacement of MgO by spine! occurs in the composite. Aluminum nitrides in the metallic carcass cathodoluminesce deep violet-blue, unlike non-luminescent AIN in the composite matrix. This distinction in cathodoluminescence suggests a different mode of formation for composite AIN than for carcass AIN. Phase interpretations and textural characterizations deduced from the implementation of sophisticated mineralogical techniques have contributed to the understanding, and will aid in the improvement, of MgO/ AlN-based ceramic matrix compositeprocessing."

Jan 1, 1999

By Chen-Ming Kuo, Esher Hsu

"The importers and manufacturers who import or produce products with packaging containers are charged a recycling fee in Taiwan. The amount of waste packaging containers used for calculating the recycling charge is based upon the amount declared by importers and manufacturers which might be underestimated. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explores its distribution. The sampling survey and ratio estimation are conducted for estimating the recycled amount; while the refuse sampling method for municipal solid waste composition is employed to estimate the un-recycled waste packaging containers. The estimated total amount of waste packaging containers in 2011 generated by households in Taiwan is 696,511 m.t., of which, 79.49% of the waste packaging containers were recycled and 20.51 % were landfilled or incinerated. This study shows that the amount of waste packaging containers declared by importers and producers is underestimated around 20%.IntroductionWaste packaging containers including iron cans, aluminum cans, glass bottles, plastic containers, paper containers, aluminum foiled paper packs are officially announced to be recycled in Taiwan. In order to create the economic incentive for raising recycling performance, associated manufacturers and importers are charged a recycling fee to subsidize recyclers. The amount of packaging containers declared by importers and manufacturers is used for calculating the recycling charge and recycling rate. The importers and manufacturers might underreport their producing (importing) amount to pay less recycling fees. Therefore, the estimated waste packaging containers based upon the amount declared by importers and manufacturers is usually underestimated. Related previous studies about waste packaging containers recycling in Taiwan are done by Hsu and co-workers [1-4]. Hsu and Kuo [1] estimated total production values of recycling and evaluated the performance of recycling performance based upon the estimated production values. Hsu and Liu [5] provided a cost analysis of recycling for waste packaging containers in Taiwan. Bor, Chien, and Hsu [2] presented a market-incentive recycling system for waste packaging containers in Taiwan. Hsu and Kuo [4] provided an amending mechanism for product charge and recycling subsidy in response to the social economic changes for waste packaging containers recycling. Lee and Hsu [ 6, 7] explored the distribution, fee rates, and collection rate of waste containers. This study aims to estimate the amount of waste packaging containers generated by households in Taiwan and also explore its distribution."

Jan 1, 2014

By M. -L. Metsärinta, J. Nyberg, A. Roine

The Kokkola roasting plant uses more than 20 different zinc concentrates every year. During recent years there has been an increase in the variation in concentrate quality; in particular, the amount of fine-grained and low-grade concentrates has increased. Therefore, a great deal of development work has been carried out to improve the operational flexibility, online availability, production capacity and calcine quality of the roasting plant. This work consisted of a heat and material balance model of the roasting based on HSC Chemistry software, a new water admixture system for the concentrate feed, a new oxygen feed system for the process air line, improved cooling of the furnace and boiler and improved operational practices, dust removal and concentrate mixing. These new process control tools and other improvements, as well as some test results, will be described in this paper. The oxygen feed may be used to improve production capacity and to decrease the sulfide content of the calcine. The water feed may be used with fine concentrates to decrease both dust carry-over and the temperature in the top part of the furnace. Improved cooling of the furnace and boiler helps to increase production capacity.

Jan 1, 2000

By Khandaker M. Anwar Hossain

This paper presents the development of lightweight concrete (LWC) incorporating pumice aggregate and volcanic ash (VA) based ASTM Type I blended cement (PVAC). Fresh and mechanical properties of LWC mixtures such as slump, air content, compressive strength, tensile strength, density and modulus of elasticity are described. The durability characteristics are investigated by drying shrinkage (DS) and water permeability. The investigation suggests the production of LWCs incorporating blended PVAC and VPA having satisfactory strength/durability characteristics for structural applications. The use of PVAC induces the beneficial effect of reducing drying shrinkage and water permeability. Development of such non- expensive and environmentally friendly LWCs with acceptable strength and durability characteristics is extremely helpful for the sustainable development and rehabilitation of volcanic disaster areas around the world.

Jan 1, 2010

By F. F. Lins

There is a large use of mercury in Brazil by the gold miners in the so called "garimpos" (non registered mining operations), where it is usual to recover the gold contained in the gravity concentrates by amalgamation, which is highly deleterious to environment if not conducted properly. Unfortunately, this is a common practice there. After presenting in brief the modus operandi generally practiced in the garimpos and the environmental problems, this work reviews some of the research conducted in CETEM according to two approaches: (i) replace amalgamation by other processes and (ii) develop technology to treat mercury-contaminated soils and effluents. Conventional processes like froth flotation, to recover gold from gravity concentrates, and centrifuges were considered. Also as alternatives to amalgamation, innovative process like the recovery of gold by coal-oil agglomerates and a technology that is currently under development in our laboratory, called gold-paraffin process, are described in brief, some results presented and their potential use assessed. To reclaim sites already polluted a technology was developed to float mercury selectively from contaminated soils. The potential use of centrifuges to pre-concentrate the mercury is also discussed. The scope for applying the last techniques is to concentrate the pollutants in a small volume of mass which would be suitable for recycling or isolation from the environment. A prospective technology to treat contaminated soils, or mercury concentrates, is the immobilization of mercury by adding inorganics. Concerning the ionic mercury which may be present in effluents, precipitation of the ions and flotation of the precipitates are being studied.

Jan 1, 1994

By Yuanyuan Zhang, Patrick J. Masset

"The reduction of FexO in slag is one of the fundamental reactions in iron and steelmaking technology, including the blast furnace process (BF). Experiments on the reduction reaction of iron oxide using CaO-SiO2-Al2O3-FexO-C mixtures were carried out using thermogravimetric analysis (TGA) under reducing conditions at temperatures up to 1100°C. The composition of the primary slag was chosen so that the FexO concentration varied between 0 and 75 wt % and the CaO/SiO2 ratio being kept constant to 0.90. From the TGA curves recorded isothermally at different temperatures the kinetic parameters of the iron oxide reduction were determined.IntroductionIn blast furnace the iron ores and coke are charged in layers from the top. The reduction of iron oxide by coke is one of the fundamental reactions in the blast furnace process. Although a great amount of work has been done on the topic of reduction of composites [1, 2, 3], gasification of carbon [4, 5] and reduction of iron oxides by CO [4, 5, 6], the mechanism of reduction in iron oxide - carbon powder mixtures is not fully understood. Fruehan [1] and Rao [2] studied the reaction rate of the reduction of iron oxide by different types of carbon and concluded that the reaction mechanism is controlled by the oxidation of carbon at temperatures up to 1200°C. Rao [2] studied the reaction of hematite with graphite as carbon source up to 1080°C. An activation energy close to 300 kJ/mol was calculated within the temperature range of 950°C to 1087°C. In his study, Fruehan [1] determined the rate of reduction of Fe2O3 and FeO by coal, coke and coconut charcoal as carbon sources within the 900°C to 1200°C temperature range. He found that the reduction of Fe2O3 by carbon occurs in two stages and that the reduction of Fe2O3 to FeO is faster than that of FeO to Fe. This is due to the fact that the CO2/CO equilibrium ratio is higher, and hence, the rate of oxidation of carbon is faster. Fortini and Fruehan [3] have studied the reduction reaction of wustite by graphite and wood charcoal. They found that the wustite reduction can have a significant effect on the overall rate of reduction in composites at high temperatures or in the presence of a large excess of carbon. The calculated activation energy of the reduction reaction by wood charcoal was close to 368 kJ/mol, while the activation energy of the reduction reaction by graphite was 444 kJ/mol."

Jan 1, 2011

By Takashi Fujii

In the OG (Osaka Gas) process which includes a fusion process of sewage disposal sludge in coke bed knowledge of molten and fluid properties of the sludge are most important to controll the process in good condition. Thus, the softening and melting temperatures and viscosity were measured by the sessile drop technique and a rotating viscometer. Obtained results are summarized as follows: Melting character of sludge slag is varied according to their composition, but closely related to CaO/SiO2 ratio in ordinary sludge and to CaO/(Cr2O3,+Al2O3+P2O5) ratio in Cr2O3 containing sludge. Fluid property of sludge slag has a correlation with optical basicity or Riboud parameter, However, the correlation is poorer than that of metallurgical slags. Especially, chromium oxide containing sludge shows high viscosity and behaves somewhat different manner from ordinary sludge.

Jan 1, 1992

By Xinghui Meng

The recovery of platinum and palladium from automotive catalysts has been investigated by leaching in iodide solutions with oxidants including oxygen and iodine in an autoclave. An ammonium salt was presented in a neutral leaching solution as a key leaching reagent to achieve high recoveries of the platinum group metals (PGM). The effect of temperature, and concentrations of oxidants and of ammonium salt on the recovery of PGM was examined. Under the experimental conditions studied, the recovery of platinum and palladium was found to be greater than 95%. An economical assessment of this process has also been examined and discussed.

Jan 1, 1995

By Yufeng Guo

Mineralogy and physico-chemical characteristics of a nickel hydrometallurgical residue and recovery of iron-bearing minerals by flocculation-magnetic separation were studied. The results show that the nickel residue is super-fine and fraction less than 0.045mm reaches 85.4%. Ferrous minerals are chiefly magnetite and ferruginous glass. Magnetite accounts for 31.7% and exists as free magnetite. Ferruginous glass is of multicomponent amorphous substances with low-iron grade but strong magnetism, and accounts for 39.9% of total iron minerals. Addition of flocculants increases granularity and magnetic force of fine iron-bearing particles and improves iron grade and recovery. The tests with flocculation separation show that a concentrate assaying 56.68% Fe with 81.72% recovery was obtained in a magnetic tube. A concentrate with 56.92% iron grade and 67.96% recovery was obtained by flocculation-magnetic separation with a magnetic cylinder.

Jan 1, 2006

By Jun Li, Lingling Zhang, Daqiang Cang, Guizhou Zhao

Pilot trial of direct modification of molten blast furnace slag and production of high acidity coefficient slag wool fibers were investigated nearby a blast furnace. Molten blast furnace slag discharged from blast furnace and then directly flow into specialized modification furnace and quartz was simultaneously added into the molten slag as modification agent. The modified molten slag was electric heated to 1500–1550 °C and then the melt was produced into slag wool fibers through high-speed centrifugation method. Melt with acidity coefficient of 1.2, 1.4, 1.6 and 1.8 were investigated and fibers with corresponding acidity coefficient were produced. Slag wool fibers with shot content of 5.5, 5.8, 6.2, 6.8% and average diameter of 4.5, 4.9, 5.6, 6.4 lm for four samples were successfully produced, respectively. Total energy consumption and production costs decreased by 50–70% compared to traditional cupola furnace method. This method provides an energy-saving and emission-reduction technology for the direct utilization of molten blast furnace slag.

Mar 1, 2018

By T. S. Piwonka

Modeling the solidification of shaped castings has progressed beyond the initial problem of determining the correct heat and fluid flow relationships which describe the solidifying castings. Today the challenge is to describe second order effects which determine the ultimate quality of the casting. The challenges to the modeling community posed by the needs of today's foundries for models that work are discussed, with some examples of current modeling problems.

Jan 1, 1992

By Yuanbo Zhang, Zhixiong You, Daoxian Duan, Guanghui Li, Tao Jiang

"Manganese is mainly consumed by steel and battery industries. In recent years, it is essential to utilize the low-grade manganese oxide ores with total manganese grade below 25%, as the high quality manganese ore resources are becoming scarce with the rapid development of the steel industry. Conventional pyro-metallurgical processes for utilizing manganese oxide ores are characterized by high production cost and energy consumption, low productivity, serious environmental pollution, etc. In this study, reduction thermodynamic of MnO2 reduced by sulfur was firstly carried out. Then, a novel process of reduction roasting with sulfur followed by acid leaching was developed to recover manganese from the very low-grade manganese oxide ores. Effects of main factors, including temperature, reduction time and S/Mn mole ratio, were investigated, and a high leaching efficiency of Mn above 95% was obtained under optimal conditions.IntroductionHigh/middle-grade manganese oxide ores are generally used in the metallurgical industries, particularly in steel plants and ferro-alloy units. The consumption of metal manganese in the ferro-alloy industry accounts for 85- 90% of the total Mn demanded [1]. Therefore, high quality manganese ore resources are becoming scarce with the rapid development of steel industry. It is essential to make good use of large quantity of low-grade manganese ores (TMn < 25%) presently available."

Jan 1, 2012

By Richard W. Lawrence

Leaching of copper from sulfide minerals using biooxidation offers a potential route for copper recovery. Oxidation of . sulfide sulfur can proceed either; to sulfate or to elemental sulfur depending on mineralogy and process conditions. The advances in commercial application of biooxidation for sulfidic gold ores has made available operating and cost data which allow the derivation of conceptual costs for copper ore processing for comparison with conventional processing routes. Although costs for copper biooxidation generally remain high relative to conventional smelting, application might be competitive in specific cases. Biooxidation becomes more competitive in the general case if the cost ofS02 emissions in pyrometallurgical processing were to be internalized to a greater degree than currently required. This paper describes the technical aspects of biological processing of copper sulfide ores and concentrates, specifically with respect to the fate of sulfur. The environmental and economic implications of the biooxidation route are discussed in relation to conventional processing.

Jan 1, 1996

By Zhen Zhang, Jiang Diao, Tao Zhang, Yi Ren, Lu Jiang, Xiao-Man Yan, Bing Xie

The precipitation behavior of phosphorus enrichment phase was investigated by slag modification with Al2O3. The mineral phase of the original slag and modified slags were measured by mineral phase microscope, SEM+EDS and XRD. The mechanism of Al2O3 modification was discussed according to the thermodynamic theory analysis software (Factsage version 6.3). The results show that the high phosphorus solid solution (nˊ2CaO·SiO2-3CaO·P2O5) was generated by the continuous reaction of nC2S-C3P (nˊ＜n) solid solution and Al2O3 under 1350℃. The amount of initially precipitated solid solution (nC2S-C3P) was reduced and even disappeared with the increasing of Al2O3. If the addition of Al2O3 is enough in the slag, the high phosphorus solid solution (nˊC2S-C3P) that generated by the above mentioned reaction will continue to react with Al2O3 to produce Ca2Al2SiO7 and even C3P, which was demonstrated that the addition of Al2O3 has a positive influence on the precipitation of phosphorus enrichment phase.

Jan 1, 2015

By M. A. Kader, W. D. Hutchison, M. A. Islam, P. J. Hazell, J. P. Escobedo, A. D. Brown

The effects of post-foaming thermal processing on the quasi-static compressive strength of closed-cell aluminium foam with an average relative density of 0.56 g/cc have been investigated. Samples were subject to one of four material conditions: as-received (AR), warm aged (WA), solution treated (ST), and annealed (AT). X-ray diffraction (XRD) was performed to determine a relationship between each material condition and macro-crystallographic texture of the dendritic α-Al phase. It was found that all heat treated samples contained clear deviations from random texture towards the exterior regions of the samples, indicating non-uniform recrystallization kinetics. The ST and WA samples exhibited the highest yield stresses and energy absorption, with the AT samples exhibiting the lowest. Additionally, it was found that the AR and WA conditions lost 12.8 and 15.6% of their total mass from brittle cell wall crumbling, whereas the AT and ST conditions lost 2.5 and 3.0% of their total mass.

Mar 1, 2017