By L. Katgerman, H. J. Brinkman, J. Duszczyk

"The phase formation sequence in the in-situ synthesis ofTiB2 in A1 from elemental A1, Ti and B powders is identified with a combination of DSC and XRD. After the melting of A1, A1B2 and A13 Ti are formed at the contact areas between A1-B and A1-Ti. The influence of variations in starting composition on the reaction kinetics is explained in terms of there effect on the different processes in the formation sequence. Parameters in the starting composition that were investigated are; fraction ofTiB2 forming reactants, non stoichiometric Ti:2B ratio's, and addition of alloying element Cu.It was found that a liquid Al phase is necessary for the in-situ TiB2 forming reaction from the intermediate A1B2 and A13 Ti phases. If all Al is consumed by the formation of A1B2 and A13 Ti the TiB2 formation is halted until the decomposition of A1B2 and A13 Ti .Overstoichiometric amounts of B are needed for complete conversion of the Ti, present in A13Ti, into TiB2 This is explained by the fact that some of the stable A1B12 phase is formed after the decomposition of A1B2•The addition of Cu leads to an increasing reaction rate in the A1-Ti reaction. A possible explanation for this is that the A1-Cu liquid penetrates more easily between the Ti and its surface oxide than the unalloyed A1 liquid."

Jan 1, 1998

By P. E. Nolan

The disproportionation of carbon monoxide is an important aspect of reduction processes, in the production of carbon filaments for composites, and in the removal of CO from CO,. It can also be a hindrance, causing carbon fouling of equipment and metal dusting. The reaction is thermodynamically favored at lower temperatures, but it occurs slowly. Catalysis of the reaction by transition metals has been examined. A materials science approach to the selection of a catalyst material and of optimum operating conditions is being taken in the present work. Of particular interest is characterization of a catalyst that can be repeatedly regenerated to prevent deactivation in long term use. Experimental data on a less studied catalyst, ruthenium, are reported.

Jan 1, 1992

By J. McKelliget, J. Szekely, Oreper. G. M.

"1. INTRODUCTIONThis paper is concerned with heat and fluid flow phenomena in arc welding operations. Fig. 1 shows a schematic sketch of a typical arc welding arrangement. It is seen that an arc is being struck between an inert electrode and a metal surface and that the resultant current and energy flow will case the formation of a molten weldpool.It is clearly appreciated that the weldpool shape and the nature of circulation in the weldpool may play an important part in determining the ultimate weld quality. It is known, furthermore,· that the weldpool behavior in turn will be affected by the spatial distribution of the current and the heat flux it receives from the arc. Indeed, the inherent coupling between the arc and the weldpool is a key feature of welding operations.Up to the present useful work has been done on the modelling of heat transfer and melt circulation in weldpools (1,2,3,4) and also on the description of arcs, including welding arcs (5,6,7,8). However, the coupling between these two sets of phenomena is relatively unexplored in a qualitative sense. The purpose of the present paper is to examine the interaction between welding arcs and weldpools. The actual material will be presented under the following headings:"

Jan 1, 1986

By D. E. Larson

The U. S. Bureau of Mines has developed a image analysis methodology to correlate the energy consumed during the grinding of an ore to the mineral liberation achieved. Energy consumption values are obtained using a laboratory-scale ball mill equipped with a torque sensor, and an automated image analyzer is used to determine the liberation present in ground products. By combining liberation information with energy consumption data an appraisal can be made of the energy required to liberate the mineral(s) of interest. Results of tests performed on a complex sulfide material determined the effects of grind duration on the liberation achieved and the energy efficiency.

Jan 1, 1995

By H. Conrad, K. Jung

"The effect of an external electric field E=5(+) kV/cm applied during the solution heat treatment at 500°-550°C of three commercial Al-Mg-Si alloys (AA6061, AA6022 and AA61l1) on the asquenched resistivity Pw and hardness H.,NULL, w was investigated. It was found that the field gave a significant increase in Pw and in Hv,w, for AA6022 and AA6111, but had no clear effect on AA6061. Thermodynamic analysis gave that the effect of the field on AA6022 and AA6111 was to reduce both the enthalpy ?H, and entropy ?H, of solution. Considering the chemical composition of the three alloys it appears that the influence of the field may depend on the amount of Cu plus excess Si present in the alloy.IntroductionKlypin and Soloviev [1, 2] were the first to report that the application of an external electric field during solution heat treatment (SHT) of Al alloys gave an increase in the as-quenched resistivity and hardness. They attributed these effects of the field to an increase in solubility of the alloying constituents during the SHT. More recently Liu and coworkers [3, 4] also reported an increase in the as-quenched resistivity of Al-Li alloys with application of an electric field during SHT. Further, the present authors [5] found that the application of an electric field during the SHT of the commercial Al-Mg-Si alloys AA6022 and AA61i1 increased their as-quenched resistivity and hardness. Their thermodynamic analysis of the results indicated that the field decreased both the enthalpy ?H, and entropy ?S, of solution."

Jan 1, 2004

By Du Sichen, S. Seetharaman, J. A. Bustnes

"The present study deals with the kinetic studies of reduction of some selected transition metal tungstates with hydrogen. The measurements were carried out by the isothermal thermogravimetric method. Shallow powder beds were employed in order to avoid the effects due to transport phenomena affecting the reaction rate. In this way, the chemical reaction rates could be selectively studied. The experiments were carried out in the temperature range 873 - 1173 K. From the experimental data, the activation energies were evaluated and were found to be around 88 kJ / mol in the case of both iron as well as cobalt tungstates indicating the similarities in W-O bonds in both cases. The activation energies obtained are discussed in the light of the position of the transition metal in the periodic table as well as the thermodynamic stabilities of the various tungstates.IntroductionThe tungsten containing hard metals, characterized by high density, belong to a class of two-phase metal matrix composites. While these types of materials have traditionally found their applications within the defence industry as armour-piercing projectiles, counterbalance in helicopters and military aircrafts, outer casings of hand-grenades, etc., commercial applications for this class of alloys also exist, including radiation shields, penetrators for the oil industry, turbines for turbo-jet engines and a wide range of sports related parts. A possible route to the production of these alloys is to reduce the tungstates such as FeW04, Co W04 and NiW04 using a reductant like hydrogen or carbon monoxide. In order to have a better understanding of the processes involved in the production, it is important to have a knowledge of the reduction kinetics for these tungstates. According to the knowledge of the present authors, while the reduction ofNiW04 by hydrogen gas has been investigated earlier in the present laboratorypl no systematic reduction study has been carried out previously for the tungstates of iron, cobalt."

Jan 1, 1996

By G. Springer

The identification of lost mineral values in mill tailings frequently requires the inspection of hundreds of thousands to millions of particles. The search of these particles can be made automatic by using an electron microprobe. A standard instrument (Cambridge Mark V) was modified by the addition of stepping motors to advance the specimen stage in a controlled manner. The X-ray Signal is monitored continuously by a computer interfaced to the instrument with an analog-to-digital converter. 400,000 particles of a tailings sample can be scanned in about 3 hours. Particles as small as 2 um and containing as little as 3% of a particular element can be detected.

Jan 1, 1982

By Sevket Acar, Tim Acton

"Zarafshan/Newmont is a 50/25/25 joint venture between Newmont Gold and the State Committee for Geology and Mineral Resources, and Navoi Mining and Metallurgical Combinat, two entities of the Republic of Uzbekistan. The Zarafshan/Newmont joint venture consists of a heap leaching operation which will process 220 million metric tonnes of existing low-grade oxide ore stockpiles (averaging 0.036 oz Au/t) from the Muruntau mine. Net recovery over the 17-year life of the project is expected to be 4.8 million ounces of gold.The plant construction started in October 1993 and operations commenced on May 25, 1995. The crushing plant consists of four stages of crushing and screening to produce a 95% passing 3.35 mm product, followed by heap leaching and gold recovery by the Merrill-Crowe process. The dore metal is refined at the Muruntau refinery. All gold produced by the joint venture is sold on the world market. IntroductionThe Muruntau mine and nearby town of Zarafshan are located in the center of the Kyzylkum desert, 250 miles west of Tashkent, capital of Uzbekistan. Following a mining conference in Moscow in 1990, a Newmont geologist was among the first team of westerners to visit the Muruntau Mine, the second largest gold producer in the former Soviet Union. At Muruntau, they found 220 million tonnes of low grade gold ore that had been stockpiled during the previous 25 years. In February, 1992, six months after Uzbekistan's independence, Newmont signed a 50/50 joint venture agreement with the Uzbek government to use heap leach technology to process the ore. The feasibility study was completed in November of 1992. Plant construction started in October, 1993 and operations commenced on May 25, 1995.Newmont Metallurgical Services performed metallurgical studies to obtain heap leach process design criteria parameters. The initial metallurgical study on 20 grab samples is the subject of this paper."

Jan 1, 1997

By Magnus Ek, Peter Olsson

The Rönnskär Smelter has been faithful to Peirce Smith Converting during its 79 years of existence. Though a visitor to our smelter museum will easily find out that a lot has happened since the beginning – and development continues. In this paper an up-date on Converting and Casting at the Rönnskär Smelter is presented. Recent developments include an investment into converter process gas handling, but also day-to-day operational aspects such as converter aisle productivity and flexibility, but also minimal EH&S impact. 127

Jan 1, 2009

By SenYang Qian, ShuangYu Du, Bo Wang, Jieyu Zhang, Jian Zhao

During the solidification process, the flow pattern of the molten steel has significant influence on the formation of solidification microstructure. In present study, the solidification microstructure of 30Cr2Ni4MoV steel ingot under different intensities of mechanical oscillation(forced convection) was simulated by using ProCAST®software. The results showed that the increase of the intensity of oscillation could restrain the development of the columnar grains and refine the grains. As the intensity of oscillation increased, the proportion of columnar grains decreased and the proportion of equiaxed grains increased. When the intensity of oscillation was at a low level, the effect of refining grains could be improved obviously by increasing the intensity. However, as the intensity increased to over 0.833, the effect of refining grains would not be improved.

Jan 1, 2016

By Masatoshi Ogasawara

Saganoseki smelter & refinery operated two flash smelting furnaces, producing a combined 330,000 metric tons per year (hereinafter mtpy) of copper. [n 1996, however, it successfully shifted to a single fumace operation while maintaining production at the same level. Since then, the production capacity has been further increased to the present 470,000 mtpy by technological improvements. Also, in order to reduce the converter load which represents a bottleneck in efforts to increase production, the matte grade was gradually increased and currently runs at 65 to 66% attaining the low copper content in the slag (hereinafter slag loss) of 0.7 to 0.8%. This ' paper introduces some improvements, recent operation results and thermodynamic analyses.

Jan 1, 2003

By R. Padilla, M. C. Ruiz

Arsenic, antimony and bismuth are commonly found in copper concentrates usually as the minerals enargite, stibnite and bismuthinite, respectively. Concentrates having high levels of arsenic and antimony must be pretreated before smelting. Roasting is the preferred method for removing these toxic impurities from concentrates; However, the removal of As, Sb and Bi in oxidizing roasting by volatilization may not be complete due to the slow reaction rates at 500- 700 °C. Oxidizing/volatilization data were obtained from pure mineral mixtures and from arsenic rich copper concentrate. The reaction mechanism for the volatilization of arsenic and antimony were discussed. Near 100% As and over 95% Sb volatilized in the oxidation of a mixture of pure minerals at 700 °C, 1% oxygen, while over 95% As, and 35% Sb volatilized at 600 °C in 1% oxygen atmosphere when using a copper concentrate containing 3.51% As, 0.14% Sb, and 0.01% Bi. Bismuth did not volatilize.

Jan 1, 2015

By Albert W. Spitz

Profitably recovering copper and precious metals from copper bearing scrap is a demanding and frustrating combination of art, science and economics. With fluctuating markets, varying raw materials and increasingly stringent environmental regulations requiring process revisions, practically everything is changing. The volatile copper market constantly shifts the percentage of copper in the scrap that can be economically processed. Scrap that has value one day may incur a disposal cost the following day. Also with less copper in the scrap, more residuals, slag, fume, etc. are generated which frequently present disposal problems and infrequently generate income. The ever increasing amounts of electronic scrap add value to the copper produced by virtue of the precious metals present. Printed circuit board materials create more slag and organic off gases which must be treated. Finally, the emphasis on reducing emissions of organics and other metals, especially lead, is a continuing challenge. Stack gases, fugitive emissions and ambient air quality all demand constant surveillance.

Jan 1, 1997

By Richard S. Dennis

Acid recovery employs ion exchange (I-X) resin as separation media for inorganic acids from dissolved metallic salts by physical adsorption and without the use of chemicals. This technology has been used for years on spent etching and plating liquors to recover acid for reuse in the bath and to reduce waste acid neutralization costs. It is also used for electrolyte treatment to facilitate valuable metal recovery via acidity reduction. TETRA's ccrxr'" I-X contactor has been used successfully for acid separation from its metallic salt counterpart in a simple, continuous operating mode using strong base anion resins. Efficient separation is enhanced by acid reconcentration to nearly its original strength or as high as 14-20%. Continuous treatment also recovers heat to the tankhouse or bath and improves metal quality due to consistent acid quality. Conventional fixed bed ion exchange (I-X) systems are impractical for acid recovery because of complex control design and large resin inventories needed to process very low liquid-to-resin treatment ratios associated with strong acid concentrations.

Jan 1, 1996

By Wei Lv, Yang Zhou, Qiang Li, Xuling Chen, Zhiyun Ji, Min Gan, Guojing Wang, Xiaohui Fan

Mineralization during sintering is a process to make part of the raw material melt after serial complex chemical reactions at high temperature. However, high temperature mineralization behavior of the adhesion layer and nucleus particles in the granules during the sintering process has been studied. Research findings reveal that solid-phase reactions between iron ores and fluxes in adhesion layer occurred first, of which the product would induct the generation of the initial liquid phase. By the assimilation of the initial liquid phase, fluxes which served as nucleus particles in granules, such as limestone and dolomite, could dissolve in the liquid phase and extend its amount as increasing temperature, whereas iron ore nuclear particles remained as unfused ores for their insufficient mineralization. Therefore, the mineralization proceeding for sintering was achieved: the iron ores in fine fraction (−0.5 mm) reacted with all fractions of fluxes to form the melt zone, while the coarse iron ores (+0.5 mm) acted as unfused ores, which formed the final sinters together with the melt zone.

Mar 1, 2017

By Sarah Beutner Mavrogenes

The mineralogy of three slags from a domestic secondary copper refinery were studied by applied mineralogical techniques to determine the: 1) phases present, 2) phase chemistry, 3) phase abundance, 4) associations, 5) crystalline habit, 6) grain size, 7)microtextures, and 8) causes for certain metallurgical problems, such as metal losses to the slags. The slags were produced by skimming the bath prior to melt-down to allow heat from the flame to reach the bath. The first slag is highly viscous and all three slags contain a large amount of copper. The "first slag", which is skimmed prior to treatment of the bath with fluxes, contains metallic copper, cuprite, delafossite, magnetite, Mg-hercynite, common spinel-chromite solid solution, picrochromite-chromite solid solution, common spinel-picrochromite solid soiution, gahnite, cassiterite, silica-rich glass, and corundum. Its abundant solid refractory phases make the slag difficult to skim. The "soda-rich slag", skimmed after the treatment of the bath with sodium carbonate flux, contains cuprite, delafossite, magnetite, cassiterite, Na-Al-silicate, and Na-Al-Ca-silicate. It contains less metallic copper than the first slag and lacks the refractory minerals. The "phosphorus-rich slag", skimmed after treatment of the bath with a copper phosphide flUX, contains metallic copper, cuprite, delafossite, berlinite, cassiterite, silica, apatite, Cu-Fe-rich apatite, copper phosphate, Cu-Fe-phosphate, and a Pb-phosphate. In contrast to the above three copper-rich slags, recent charges have produced a silver-copper-rich slag. The "silver-rich slag", skimmed after the treatment of the bath with a copper phosphor ide-borax flux, contains, cassiterite, delafossite, cuprite, a Na-Al-silicate, magnetite, metallic copper, MgO, common spinel-chromite solid solution, and wollastonite. Silver ranging from 0.05 to 2.02% was found by atomic absorption and inductively coupled plasma spectrometry analyses in the metallic copper phase.

Jan 1, 1989

By Masayoshi Matswnoto

The Kosaka Smelter and Refinery produces copper and lead, and has a history of more than 100 years as a metallurgical department of Dowa?s Kosaka Mine. The Smelter treats complex sulfide concentrates which are difficult to smelt. Valuable metals are recovered using various processes developed by Kosaka Smelter and Refinery. Effluent waters from the smelter contain large quantities of heavy metals. This paper describes how Kosaka Smelter and Refinery recovers valuable metals from various effluent waters and handles overall waste waters in order to meet strict environmental standards.

Jan 1, 1993

By Xun Hu, Jian Pan, Hongbin Yu, Deqing Zhu, Yanhong Luo

Lump ores are one kind of important burdens for blast furnace (BF), their metallurgical properties have significant influence on BF performance. In this paper, the relationships between the mineralogy of five natural lump ores and the metallurgical performance have been studied. The mineralogy study includes mineral compositions, microstructure and porosity, and the metallurgical performance covers reducibility index (RI), low-temperature reduction degradation index (RDI) and decrepitation index (DI). The results show that the complex lump containing hematite, and goethite has better overall metallurgical performance. For single lump, the RI of goetihte ores is higher, the RDI and the DI is strongly influenced by porosity. The hematite and magnetite ores have good anti-decrepitation and anti-RDI, but generally the RI is lower due to lower porosity, and the RI is related to the grain size, the smaller grain size is, the better reduction will be.

Jan 1, 2015

By John Wallace

"Monitoring compound semiconductor crystal growth using multifrequency eddy currents for sensing illustrates some of the extreme problems of measurement and interpretation that are not often seen in metallic systems. Using sensor arrays and scanning sensors have produced a qualitative and quantitative understanding of some of the high temperature electrical conductivity mechanisms in several compound systems. A detailed review of the CdTe/CdZnTe data is presented showing some of the complexity in the data as opposed to what is found in elemental semiconductors.HistoryThe most common goal in the use of eddy current measurement in crystal growth is to deter-mine the curvature of the liquid solid interface during growth to test if the heat transfer estimates of the thermal design were adequate for single crystal growth[l]. This aim could be met but represented only a small fraction of the data that was produced observing a growth cycle. A secondary consideration was what could be discovered in the recorded data about the growth and subsequent heat treatment as the boule cooled. This is usually a more difficult task because a crystal growth process is not a controlled experiment so much as a process that continually sees modification. Using a sensor arrays or a scanning loop has produced a qualitative and quantitative basis for understanding some of the high temperature electrical conductivity mechanisms. The implication of the these measurements of electrical conductivity variations are important in that they reflect the complex defect states that will occur on cooling and heat treatment following crystal growth. In contrast to the complex behavior of the conductivity of these compound semiconductors in the solid and liquid state we have the very well characterized system silicon to compare. Initially the interest on using eddy currents to monitor compound semiconductors came from G. Westphal at the Texas; Instruments Company in 1987 to monitor aspects of growth and compounding of GaAs. This was followed by work on solution growth of HgCdTe with D. Witter. The initial interest in the use of eddy cur-rents for monitoring CdTe crystal growth came from Prof. Wilcox at Clarkson University in the practical interest to determine and control the crystal interface curvature during vertical brigdeman growth. The first actual work was done by one of his former students. G. Neuge-bauer at the II-VI Corporation which was carried on by G. Rosen at Clarkson and R. Shetty at II-VI Corporation and with A. Socha at Johnson-Matthey Electronics. The work on CdTe extends over four years and yielded sufficient data to allow one to evaluate the utility of the information produced as compared to what could be obtained from monitoring an elemental semiconductor such as silicon."

Jan 1, 1997

By Olli Hyvärinen

The capacity of Outokumpu Pori Copper Refinery has been increased by 50 % to 70 000 t/a in the last five years by adopting periodic current reversal, reducing spacing and installing some new cells in the old tank house building. Five years operation of PCR has proved that it is possible to achieve additional capacity with PCR and yet produce high quality cathodes. The impurity level in anodes has considerably increased, and recently, arsenic, antimony and sometimes bismuth have displaced nickel as the most critical impurity.

Jan 1, 1987