By R. P. King

The essential features of an image analysis system for the measurement of mineral liberation are described. Good procedures for image acquisition and image processing prior to image analysis are defined. The basic stereological methods for the measurement of volume fraction, surface area per unit volume, particle size distribution and liberation spectra are given. The appropriate methods for fractal correction when measuring perimeters of irregular features and for frame correction when measuring linear intercepts are developed. Practically useful and accurate procedures for the stereological correction of particle size and liberation distribution methods are given.

Jan 1, 1995

By R. Shimpo

Equilibrium calculations by a computer may sometimes fail in giving solutions when the system includes a large number of components and more than three phases, and especially when no definite information about stable phases is given. An improved method of calculation is presented in which the number of phases need not to be initially fixed, phases can appear or disappear in the course of' calculation and a new method is combined with the Newton-Raphson method to obtain solutions easily. The improved method is applied to the copper smelting operation and all the successive stages of the operation are successfully simulated.

Jan 1, 1983

By Lu Lin, Yan-ping Bao, Min Wang

In order to forecast the cost of dephosphorization during BOF process, and achieve economical dephosphorization of BOF. The mathematical model of dephosphorization cost for BOF process was established. The model calculations show that, when the silicon content and phosphorus content are increased in hot metal, and the final phosphorus content of BOF is decreased, the dephosphorization cost will be increased. The silicon content of hot metal is increased of 0.1% in the plant, the dephosphorization cost is added by 9 RMB/ton steel. The De-P cost of mode A is much higher than the other two modes for three typical production modes of single slag melting process, when the phosphorus content of hot metal is higher than 0.14%, an increase in the phosphorus content by 0.01%, the De-P cost of mode A is added by about 7 RMB/ton steel. Meanwhile, when the phosphorus content of hot metal is lower than 0.165%, the De-P cost of mode C is higher than mode B’s. For BOF single slag melting process, the dephosphorization cost calculated by model is between ± 2%, proving that the model is reliable for the prediction of dephosphorization cost.

Jan 1, 2015

By Dae Jin Ha

Sticking phenomenon occurring during hot rolling of two STS 430JlL ferritic stainless steels was analyzed by hot-rolling simulation tests. The sticking started from the initial nucleation stage in which the rolled materials were stuck onto the roll specimen surface, proceeded to the growth stage in which stuck fragments grew further, and reached the saturation stage. The modified 430JlL steel had a smaller number of sticking nucleation sites and slower growth rate than the conventional 430JlL steel because of higher high temperature hardness, thereby leading to less serious sticking. When the simulation test was conducted at 1070 °c, Cr oxides were formed on the surface of the rolled materials, and thus the sticking was drastically reduced because of the increased surface hardness of the rolled materials. In order to prevent the sticking, high-temperature properties of the rolled materials should be enhanced when rolled at 900°C or 1000 °C, and rolling conditions and alloying compositions, under which the oxide formation was promoted, were more important than high-temperature properties when rolled at higher temperatures than 1000 oC.

Jan 1, 2008

By M. Tamura, K. Fujita, K Shinozuka, H. Daimon, H. Esaka

"In-situ observation of unidirectional solidification using transparent substance has been performed to investigate the growth direction of solid phase. Cell or dendrite of which preferred growth direction is not parallel to the heat flow direction was observed with various solidification conditions. Dimensionless growth direction (p) changes from 0 to 1 with increasing growth velocity at a constant temperature gradient. Introducing the dimensionless growth velocity, the relation between p and growth condition could be correlated.IntroductionTransition in macroscopic solidified structure from chill to columnar zone which is found in normal castings takes place via grain selection1). Cast products such as turbine blades are unidirectionally solidified, grain selection plays an important role to choose suitable crystals which have reasonable orientation in the region called ""starter"", which is a very initial part of casting2). Therefore, grain selection is a very important process in the formation of casting structure. The present authors have been studying on the process of grain selection using succinonitrile, which is a transparent organic substance and have found that the growth distance necessary for grain selection depends upon the solidification condition3-5). When the solid/liquid interface is dendritic, the grain selection occurs quickly. On the other hand, when the solid/liquid interface is cellular, it occurs slowly. We supposed that the growth direction of dendrite is different from that of cell when the substance is unidirectionally solidified. Indeed, Kurz and Fisher wrote in their text book that dendrite grows along its preferred growth direction, <100>, regardless of heat flow direction and that cell grows along heat flow direction regardless of its preferred growth direction1). However, there is no quantitative description about the growth direction when the solid/liquid interfacial morphology is cellular. Furthermore, there have been little works6) to study the growth direction of cell and dendrite."

Jan 1, 2000

By Ma Lijuan, Zhang Yubing, Wang Bo, Sun Huilan

The effect of lime ratio on phase composition and alumina leaching property of MgO-contained calcium aluminate clinker were investigated by analytical reagent, the XRD analysis of its mechanism was discussed. The results showed that: when the sintering temperature was 1350 ℃, C/A was 1.4, A/S was 1.3 and the content of MgO was 4%, the increase of the C/A promoted the formation of C12A7 and restrained the formation of Q-phase. The alumina-leaching ratio of the clinker (A/S was 1.3) was increased from 74.33% to 91.34% when the content of CaO was 5.21%.

Jan 1, 2015

By Stavros A. Argyropoulos

Exothermic mass transfer takes place in various areas involving metallic systems, ranging from liquid metal processing operations to the growth of thin films in microelectronics. The formation of intermetallic compounds plays an important role in the exothermic mass transfer of metallic systems. Two types of exothermicity are identified , namely , Microexothermicity and Macroexothermicity. The former is encountered when small amounts of metals are mixed, while the latter is exhibited when a solid metal in a lump form is added into liquid metal. In this paper two types of exothermic mass transfer in metallic systems will be presented and reviewed. Mathematical modelling work for these types of exothermic mass transfer will be analyzed.

Jan 1, 1993

By K. S. Kawatra

In recent years, there have been several efforts to develop binder mixtures for iron ore pelletization. Some efforts have been fruitful, while others have encountered failure. For example, adding corn starch to bentonite is effective, while adding fly ash to bentonite is not. When binders are made with fly ash, a pozzolanic reaction occurs, but no such reaction occurs when bentonite and corn starch are used together. The authors analyzed which binders can be mixed, and which binders will succeed. The authors confirmed this analysis with several laboratory and plant studies. This paper presents this critical analysis, along with various combinations of binders for making Iron Ore Pellets.

By J. Samir

The objective of this study is to simulate the isothermal filling up of moulds by a RTM process when adopting CV/FEM and VOF method and when also taking into account the presence of obstacles coupled to the effect of the thickness and reinforcement layers variation. The codes developed intended to ensure an optimal positioning of the injection points and of the vents and also to determine optimal injection pressures, in order to minimize the cycle times. These codes use a mesh generator proper to the team, allowing a discretization of the domain in triangular unstructured elements, with the possibility of a local refinement and inserts inclusion.

Jan 1, 2009

By H. Fukushima, T. Ohgai, N. Baba

The electrodeposition behavior of Zn and the morphology of the deposited Zn were studied in electrowinning solutions containing polymer additives such as gelatin and polyethylene glycol (PEG). The cathode potential was shifted in a less noble direction and the polarization resistance for Zn deposition increased with increasing concentrations and molecular weights of both gelatin and PEG added to the electrolytic solutions. However, when the molecular weights of these additives exceeded about lxlO4, the cathode was depolarized and the polarization resistance for Zn deposition decreased with increasing molecular weight. The crystal grain size and the (002) orientation of the deposited Zn became smaller when the concentration and molecular weight of the additives increased, and the cathode was polarized.

Jan 1, 2000

By Fathi Habashi

"Davy, Faraday, and Bunsen laid the foundation of electrometallurgy which had a· great impact on other areas of metallurgy. Electrometallurgy is presently dominated by the production of aluminum, the electrorefining of copper, and the electrowinning of zinc. It has also been successful in the electrowinning of copper from solutions obtained by leaching-solvent extraction. Electrowinning processes, however, are capital intensive. Improvement of the present technology should be intensely investigated especially when it is expected that such processes will increase greatly as a result of a shift from certain pyrometallurgical processes to pressure hydro metallurgy.INTRODUCTIONPyrometallurgy was used for thousands of years to produce copper and iron from their oxide ores!). Today it is still the only route to produce iron and steel and it is certain that it will remain so for many decades to come because pyrometallurgy is most suitable for the treatment of high grade oxide ores. Even when high grade iron ores are exhausted, it is possible to beneficiate the low-grade ores and produce pellets suitable for reduction in the blast furnace, which is a very efficient reactor, being a heat exchanger as well. Hydrometallurgy on the other hand can be traced to the time of alchemists in the Middle Ages when they were seeking to transmute base metals into gold, and thus were able to prepare many acids and bases which are the essential leaching agents."

Jan 1, 1997

By Luben Xie, Lin Hu, Qiang Wang, Min Gan, Tao Jiang, Wenqi Li, Xiaohui Fan, Zhiyuan Yu

"Crystal precipitation behavior of calcium ferrite (CF) during iron ore sintering process along with the effect of cooling rate, SiO2 and Al2O3 on crystalline condensation were studied. The results show that CF, has strong ability of precipitation. The precipitation is barely affected by extenal factors. It begins to precipitate when the liquid phase cools down to about 1200oC. CF could crystallize rapidly at the cooling speed of 150 °C /min. Furthermore, decreasing of the cooling rate favors the development of crystal. Binder phase transformed from CF system to silicate system when SiO2 content was increased to 5~6%, with a constant basicity (R) 2.0. Increasing Al2O3 content could promote the precipitation of CF and the development of crystal.IntroductionCrystalline condensation is the last stage of sinter mineralization. It includes the processes that crystalline substance and amorphous substance precipitate from high temperature solution phase and the consolidation of material when melt cools down. During the crystallization process, minerals precipitate following the order from high to low melting point coupled with the decreases of free energy. Most of binder phase minerals and part of iron oxides crystallize in this process, which have an important influence on mineral composition and microstructure of sinter. They finally determine the sinter strength and metallurgical properties."

Jan 1, 2011

By Bradley C. Bockrath

Some thirty coals were evaluated for liquefaction activity under a mixture of CO and H2 at 425° C. The viscosity of the liquid products was taken as an indicator of the degree of liquefaction. It was found that the direct liquefaction of a particular coal may be beneficially influenced by the presence of pyrite. Active pyrites are often found in the native mineral matter of the coal itself. For example, subbituminous and bituminous coals and lignites of relatively high pyrite content were found to liquefy more readily than similar coals or lignites which were poor in pyrite. The reactivity of inactive coals could be improved by using blends with active, pyrite-rich coals. In addition, pyrite was effective when added separately as pyrite concentrates obtained from coal beneficiation operations. Various other iron- and sulfur-bearing additives were also effective when used in combination as added slurry-phase catalysts, including iron oxides and mineral residues derived from liquefaction of active coals. Under liquefaction conditions, pyrrhotite ( Fe I- x5) is formed from pyrite or from the iron oxides and many sulfur containing species. Pyrrhotite was shown to be a hydrogenation/dehydrogenation catalyst for tetralin but is not active for initiating a variety of free radical reactions that do occur when pyrite is heated with tetralin. The role of pyrite in coal liquefaction is complex and still not well understood.

Jan 1, 1981

By Dianyuan Dang, Guihong Han, Wenjuan Wang, Tao Jiang, Yanfang Huang

In this study reduction kinetics and swelling behaviors in "two-step process” were investigated by weight-loss technique and visualizing physical changes of pellet. Results showed that reduction degree (r) increased with increasing temperature and time. According to the dynamic calculation, when reduction temperature was lower than 1000°C the reduction process was controlled by chemical reaction with apparent activation energy of 72.27 kJ/mol. When reduction temperature was higher than 1000 , the equation of t/[1-(1-r)1/3] against [1+2(1-r)-3(1-r)2/3]/[1-(1-r)1/3] followed straight lines, demonstrating that reduction was mixed-controlled. Swelling experiments indicated that the maximum swelling index increased with the increase of reduction temperature and CO content.

Jan 1, 2016

By Linfeng Zhou, Yuanbo Zhang, Rong Sun, Guanghui Li, Zhiwei Peng

The volatilization behavior of rhenium in the process of oxidative roasting of a molybdenite concentrate with 43.55 wt.% Mo and 321 g/t Re is explored based on identifying the relationship between volatilization of sulfur and rhenium. The results show that rhenium volatizes after sulfur and precise control of operating variables plays an important role in separating rhenium from molybdenite concentrate. When the roasting parameters are optimized as follows: roasting temperature 600 oC, roasting time 2 h, roasting atmosphere air, the volatilization rate of rhenium reaches 89.26%. In the process of solidification roasting, the volatilization rate of rhenium decreased almost to zero when the ratio of slaked lime/molybdenum concentrate was 10% excess to the stoichiometric requirement at 600 oC for 2 h.

Jan 1, 2016

By R. T. Hernández, I. Hilerio, A. Altamirano, M. A. Barrón

"The principal objective for finishing surfaces is to protect and/or to decorate them. This can be achieved by adding or removing material from the work surface. The addition of aggregated material is called coating or recovering. In this work, mecano-chemical techniques are investigated for surface finishing. For these techniques, barreling or polishing by the friction method will be used. These are the cleaning or finishing processes most used for great volumes of small pieces. These methods improve the surface finishing by eliminating burrs, sharp pointed, tool marks and crusts of casting. They are used to clean metallic pieces, ceramics and polymeric materials. The process is based on rubbing or friction by abrasives. The pieces are arranged in the barrel with an abrasive and an additive (water or chemical additive). The machine produces a rotating movement on the pieces. When the abrasive passes against the surfaces of the pieces, it produces an action of rubbing and impact that cleans the surfaces. The rubbing action is developed when the upper layer of the charge slides to the lower extreme when the barrel rotates. The barrel can be hexagonal or octagonal to facilitate the sliding of the charge. The barrels can be between 15 to 120 cm in length and they can have almost any diameter and velocity of rotation. There are several types of barrel: individual, multiples, and multiple compartments. The barrels are rotated using a wheel spindle or rolling pins, that the can ride horizontally or be tilted to produce an additional movement of the charge.IntroductionShot penning is a cold method in which compressive effects are induced on an exposed surface of a metallic piece, by the impact of a rain of shots directly on the surface of the metal, at great speed under controlled conditions. This differs from cleaning with the help of air, because even when shot penning cleans the surface of the metal, this function is incidental. The main purpose of shot penning is to increase the resistance of the piece to fatigue. The process has other applications: raises the tensile strength and decrease corrosion fracture."

Jan 1, 2012

By Yunhua Gan, Xiaowen Chen, Yang Tong

Experimental studies of electro-spraying were carried out using ethanol as fuel in a microcombustor under combined electric field. And the effects of different electro-spraying modes on the combustion efficiency were analyzed. Results showed that when ring electrode potential was invariant, there were four different electro-spraying modes with the variations of nozzle potentials, which were varying with the flow of ethanol. The cone-jet mode was the stablest one during the whole experimental process. The atomized ethanol was ignited and combusted stably near the steel mesh, the combustion efficiency increased firstly and then decreased along with the increasing of the equivalent ratios, reached the maximum values when the equivalent ratio equal to 1.0. And the maximum values were the highest at the cone-jet mode, and the lowest at the pulsed-jet mode.

Jan 1, 2016

By Jianjun Wang, Jiaqing Peng, Lingen Luo, Zhenbang li, Yinghe Lin

Copper removal from ferronickel by FeS has been exploring studied. It is found that the decopperizing agent FeS makes the copper removal in ferronickel effectively. The effects of FeS addition amount, carbon content in ferronickel and experimental temperature were investigated. The results showed that the removal rate of copper in ferronickel increased with the amount of FeS increasing. When the dosage of FeS is 20% (mass percentage)，the removal rate of copper can reach higher than 11%. The rate of copper removal rises with the amount of carbon content increasing in ferronickel. When the amount of carbon content is 1.86%, the removal ratio of copper is 41.3%. Higher experimental temperature promotes the copper removal reaction in certain extent. The flux is acidity and weak oxidative can also promote the reaction of copper removal.

Jan 1, 2015

By Guangliang Wu, Dongchang Huang, Xinbin Liu

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500 and 600 , all the curves are linear; when the oxidation temperature is above 700 , the curves are close to parabolic. At the temperature of 900 , the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500 900 , and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.

Jan 1, 2016

By Doug Halbe

?Many are called, but few are chosen.? The biblical adage applies not only to life, but also to hydrometallurgical processes. There have been, in the past, many outstanding successes with new processes ? and also some dismal failures. What are the odds of success for a new process? When there have been problems, why? What can you do to make sure these problems don?t occur with your process? What effect will a slow startup have on project economics? How do financial institutions ? the people who loan your company money for the project ? feel about new processes and why? Is it possible to predict or estimate the time required to reach design parameters?and if so, how do you sell this estimate to management ? and financial institutions? Probably most important ? when do you start thinking about the answers to these questions?

Jan 1, 2003