By A. V. Tarasov

In order to improve the efficiency of hydrometallurgical processing of pyrrhotite concentrates, an integrated set of research has been carried out to investigate the use of sulfur dioxide in individual unit operations and as a leaching agent in the autoclave process as a substitute for oxygen. Treating iron-containing raw materials for production of nonferrous metals are based on the selective reaction of SO2 with iron sulfides and oxides. Iron is dissolved as sulfate, which can be treated in a separate circuit to produce iron-containing pigments or it can be disposed of after neutralization. Nonferrous and precious metals contained in pyrrhotite concentrate do not react with sulfur dioxide and remain virtually completely in the solid phase, i.e. high-grade sulfide concentrate to be treated by hydro- or pyrometallurgical methods. Elemental sulfur formed in the process of leaching is separated from the pulp in granulated form as a result of the use of special surfactants. The process of sulfide concentrate leaching with the use of sulfur dioxide is conducted at temperatures above the sulfur melting point (119°C) with distributed feeding of surfactant and under a partial pressure of sulfur dioxide of up to 0.3 to 0.5 MPa.

Jan 1, 2006

By I. Mc Dougall

"The matte/slag tidal zone in a platinum smelting furnace is subject to severe process conditions which can often lead to premature failure of the lining. The MgO-FeO-Si02 slag is aggressive to refractory bricks, whilst the Ni-Cu-Fe-S matte is aggressive to water-cooled copper cooling elements, and can penetrate and sulphidize refractory bricks, particularly at the high matte temperatures often experienced in the PGM industry. A novel approach to the lining design was taken at Lonmin's new 10MW Furnace 2. An indirectly-cooled graphite ring was applied in the matte/slag tidal zone, with refractory bricks on the hot face. Thermal Finite Element modeling was conducted to determine the optimal lining design in this region of the furnace. The resistance of two graphite grades to damage by slag and matte was evaluated experimentally. The graphite lining is not wet by the matte, and is resistant to slag attack at operating temperatures. In comparison to water-cooled copper in various configurations, cooled graphite shows promise as an indirect refractory cooling system in the tidal zone area of furnaces.IntroductionIn South African Platinum Group Metals (PGM) smelting operations, the PGMs are associated with nickel-copper sulphides in magmatic rocks. After ore is mined, it is concentrated by means of a flotation process prior to smelting. Both rectangular 6-in-line and circular 3 electrode AC submerged arc furnaces are used for this purpose. A new 10 MW round furnace is currently under construction by Tenova Pyromet at Lonmin's Marikana Smelter Division. An overview of Lonmin's smelting operations and Lonmin's approach to smelting high chromite containing PGM concentrates is given by Eksteen et al. [1]"

Jan 1, 2012

By Alex Moyano

At present, the Codelco Norte smelter processes in the Teniente Converter and the Flash smelting Furnace 1,420,000 t/y of its Chuquicamata concentrate with an arsenic content of up to 1.5%. In a near future Codelco-Chile is considering different processing options for a new projected concentrates from the Alejandro Hales mine (former Mansa Mina mine with an arsenic content of up to 6%). The main option is the possibility to process 3,000 t/d of mixing concentrates from the Alejandro Hales and the Chuquicamata mines, in the Teniente Converter. The main feature of this smelting unit will be high volatilization of arsenic when processing high arsenic-bearing concentrates. The CN smelter staff carried out a technical feasibility study to evaluate the processing of high arsenic-bearing concentrates directly in the Teniente Converter, thus the low arsenic-bearing concentrates can be processed in the FSF. Accordingly, laboratory scale tests were carried out at the Tohoku University facilities. The lab-scale results allowed an industrial scale test at the Codelco Norte smelter to smelt 2,300 tpd of high arsenic-bearing concentrates in the TC and evaluate the metallurgical impact in the smelting, converting and refining areas of the smelter. The main industrial-scale result confirmed the stabilization of the arsenic content at 0.5% in the 70% Cu produced white metal at the test condition.

Jan 1, 2006

By S. Kang, D. G. C. Robertson

Slag cleaning furnaces require extensive wall cooling because they involve the use of a superheated slag bath. This is in direct contrast to smelting furnaces, where the wall is usually (but not always) protected by "banks" of solid charge. In order to understand the heat transfer and flow in slag cleaning furnaces a number of model studies have been carried out using molten wax to simulate the slag. Wax is a good model fluid because, like slag, it has a high Prandtl number. Wax models cannot simulate the behavior close to the electrodes (DC arc or AC submerged), but they can and do give a good simulation of the flow and heat transfer at the wall. An understanding of these phenomena is of great importance for the design of cooling panels in the walls of the furnace. Since superheated molten slag will eventually wear away any refractory bricks over time, the wall cooling must be designed to form a frozen layer of slag, referred to as a "freeze lining". The heat flux density (Q/A) required to do this is given by Q/A = h* ?T, where h is the heat transfer coefficient in the slag phase at the wall, and Li T is the superheat (bulk slag temperature - liquidus temperature). Both Q/A and h vary greatly with position and both are usually a maximum at the slag line. In the experimental work, molten wax baths were heated by block heaters to provide similar energy densities to those encountered in commercial slag cleaning furnaces. This procedure was considered to be valid since most of the electrical energy into a furnace bath is dissipated as heat. Gas stirring was used to simulate the gas evolved at the electrode in real furnaces - the quantity of this gas could be estimated from a knowledge of electrode consumption. The similarity criterion was equal gas flow per unit area of surface, in model and prototype. Heat transfer coefficients were measured in the models as a function of power density, gas stirring, superheat, etc., and could be related to the full-scale operations by the use of dimensional analysis.

Jan 1, 1999

By T. W. Gonzales

The refractory performance of Peirce-Smith converters is considered to be mainly determined by effects of process control and refractory installation design. BHP Copper has shown that, over the last four years, considerable improvements in tuyere line life can be affected .by maintaining a uniform temperature in the operating converter and by ensuring sufficient and specific placement of expansion allowance in the construction of the refractory brickwork. A combination of optimized crane availability, rapid matte transfer, converter operating practices, new refractory installation techniques and applications has minimized out-of stack time. In addition, larger diameter tuyere pipes and hard piping have increased blowing rates and lowered cycle times, which has resulted in a tuyere line performance in excess of 62,500 tonnes of blister copper before maintenance is required. This paper discusses the refractory installation design changes that were made to increase tuyere line life.

Jan 1, 1999

By Tangstadm Merete, Eli Ringdalen

"This paper presents an overview of results from The Norwegian Research Institution SINTEF and the Norwegian University of Science and Technology, NTNU regarding new and ongoing research in silicon production. The main studies are related to condensation of SiO gas and cavity formation. If SiO gas condensation is increased at the top of the furnace resulting in SiO content in the off-gas closer to equilibrium, the Si yield will be increased significantly. Experimental work, simulating a cavity under industrial conditions, has shown that the cavity grows downwards from one layer. Physical appearance of zones in industrial furnaces, and selected reactions in these, are discussed based on results from excavation of industrial furnaces and results from laboratory experiments. Experimental studies of reaction rates for the formation of SiO are presented. Quartz properties are demonstrated to vary between differing quartz types and the effect of this is discussed.Introduction Both the theoretical and industrial issues associated with the production of silicon are described in detail in the textbook written by Schei et al [1]. This book covers the knowledge of silicon production process up to 1998. Together with the work by Myrhaug [1] and by Aasly[2], this is the main basis for this paper. Recent and ongoing research at SINTEF and NTNU focusing on production of Si and SiO in the high temperature zone, dissociation of SiO and condensate and cavity formation will be discussed."

Jan 1, 2012

By Atsuhiro Nabei, Ken-ichi Yamaguchi

"Wet chlorination process of de-copperized anode slime is followed by de-chlorination stage in which lead-sulfate and metallic silver form silver residue. The silver residue is subsequently reduced to Ag2Se matte and PbO-SiO2 slag to remove lead to the slag in a short rotary furnace. Although this smelting process is proven well in actual operations, few papers have investigated its metallurgical aspects. This paper will describe the effectiveness of controlling parameters adopted at the Naoshima Smelter & Refinery and discuss the decisive factors influencing silver loss to PbO-SiO2 slag.IntroductionThe precious metals plant at Naoshima smelter & refinery was established in 1989, and has produced electrolytic silver, refined gold and platinum-group metals (PGM) from de-copperized anode slime as by-products of electrolytic copper. The process for gold production has been innovated from conventional smelting process to hydrometallurgical process since 2004 [1], while the process for silver production has still remained the same.The process for silver production at the Naoshima smelter & refinery is illustrated schematically in Figure 1. De-copperized anode slime is, at first, concentrated in the froth flotation process, then leached in the wet-chlorination process, and converted to silver residue in the de-chlorination process. The silver residue, which is a mixture of lead-sulfate and metallic silver, is charged to a short rotary furnace for the oxidation roasting to volatilize selenium dioxide and subsequent reduction smelting. In the smelting stage, silver residue and reverts containing selenium are smelted with flux and carbonaceous materials to form PbO-SiO2 slag and Ag2Se matte. Furthermore, Ag2Se matte is transferred to a rotary cupell and oxidized by air with the addition of sodium carbonate and sodium nitrate to produce silver anodes while removing impurities into litharge. Silver anodes are electrolytically refined by the Moebius process. Electrolytic silver is washed, dried and, finally, cast into 30kg-bars."

Jan 1, 2011

By Y. Ono

In lightweight metal processing such as aluminum (AI) and magnesium (Mg), metal cleanliness is a crucial process parameter for refining, part manufacturing and recycling in order to obtain high quality parts and products. In this paper, techniques for cleanliness evaluation of molten AI and Mg using ultrasonic probes with clad steel buffer rods having high signal-to-noise ratio (SNR) are presented. Due to the high SNR of the ultrasonic probes used, backscattered ultrasonic signals from inclusions, which may be oxide films and/or particles, in molten Mg and those from silicon carbide particles, having an average size of 50f.Ull, added in molten AI are successfully detected with reflection configurations of pulse-echo and/or pitch-catch modes at an ultrasonic frequency of 10 MHz. In addition, relative cleanliness evaluation of molten Al and Mg is demonstrated. In order to establish the procedure and to investigate the optimum system configurations for cleanliness evaluation of molten metals, particle flow simulation system using water and polyvinyl chloride (PVC) particles has been constructed. Counting the number and measuring the size distribution of the PVC particles, having an average diameter of 128um, suspended in water with the PVC volume concentrations of 5ppm and 10ppm are performed with ultrasonic pitch-catch mode. The counted numbers of particles by the presented method and system have good agreement with the calculated results with a count error of less than 10% or two counts. Based on the results obtained with water simulation experiments, the prototype system for cleanliness evaluation of molten Mg by counting and sizing inclusions has been developed. Keywords: Ultrasound, Clad buffer rod, Molten metal, Aluminum, Magnesium, Inclusion detection, Cleanliness measurement, Counting, Sizing

Jan 1, 2003

By Cui Wang, Kexin Jiao, Qiuye Cai, Jianliang Zhang

Prolonging the campaign life of the blast furnace has been an important task for iron makers, and it has been studied for decades. Adding titanium-bearing materials is a generally agreed and effective technique to protect the blast furnace hearth. Titanium from titania additions in the burden or tuyere injection react with carbon and nitrogen and form scaffolds on the hearth surface to protect the hearth from subsequent erosion. In this article, the progress on blast furnace hearth protection of titania additions in Chinese steel companies and research institutions is investigated, and the difficulties in the operation and production, such as little effect after adding titaniumbearing materials and the property deterioration of liquid iron and slags, are analyzed. The future research for protection in Chinese blast furnace is proposed, and a comprehensive process which combines protection of titanium bearing materials with reasonable thermal balance and slagmaking regimes should be established.

Jan 1, 2015

By Takao Yasugi

The majority of copper in the raw material migrates to the de-copperized dross that forms when the crude lead produced in the blast furnace is treated in the de-copperizing process. The de-copperized dross is treated in the electric furnace producing matte, speiss, and crude lead. The de-copperized dross also contains the silver. Therefore, it is important to improve the rate of silver migration to the crude lead. For this reason, the behavior of silver between the matte, speiss and crude lead phases was examined. At the same time, several tests to improve the percentage of silver migrating to crude lead were conducted.

Jan 1, 2003

By G. S. Rao

Levitated drops of Fe-18%Cr-2%C were reacted with oxygen-argon mixtures to study the reactions that occur in the AOD process, where the gases are injected into the melt and form bubbles. In the laboratory an argon-oxygen pulse, followed by pure argon, was flowed past the levitated drop to simulate the transient conditions in the gas phase as the bubbles rise in the melt. Oxide layers formed on the drops immediately when they came into contact with gas pulses containing 75% or more oxygen. Once the oxygen flow had ceased, the oxides reacted with the carbon in the drops to form CO gas and eventually disappeared. The de-carburization reaction occurred without oxide formation when the gas contained 50% oxygen or less. Melts that were sampled after EAF tapping, ready to be charged into the AOD, showed a higher tendency to oxide formation and consequent carbon boil than pure ternary Fe-18%Cr-2%C alloys made in the laboratory. The actual steel samples contained significant impurities, such as 0.25% Si and 0.56% Mn. A similar effect of oxide-forming impurities had been observed previously with binary Fe-C alloys. Movies were taken of the oxide formation and decomposition, and the results will be presented, along with data on the experimental conditions, including temperature and oxide compositions. The results are important because they give an insight into the reaction mechanisms in the AOD, which must be understood in order to improve and model the process.

Jan 1, 2006

By Xiping Chen, Wangxing Li

"Spent potlining is unavoidable solid waste from aluminum smelters. About thirty kilograms spent potlining is discharged in China to produce per ton primary aluminum. Spent potlining has high level soluble fluorides and cyanides so that it brings heavy pollution to environment. It is prohibited to keep a large amount of spent potlining in open air because it will lead concentrated pollution to local soil and water source due to hydrated reactions between spent potlining and rain water/moisture in air. Landfill may solve pollution of spent potlining provisionally, but it is difficult to be accepted by aluminum smelters because of its high investment, troublesome monitoring and perennial maintenance. Detoxifying of spent potlining not only can remove deleterious fluorides and cyanides in SPL, but also can make fluorides in SPL recycle and return to aluminum electrolysis cells, at the same time benign SPL solid residue can be recycled and ready for cement production.IntroductionChina became the largest primary aluminum manufacturer in 2001. In the past few years, its aluminum output increased by twentyfive percent every year and reached 12.56 million metric tons in 2007. The whole world was very surprised and focused attention upon Chinese aluminum industry. It is more and more important to keep sustainable and steady development with the rapid development of Chinese economy. Aluminum industry is an important base industry and does a great contribution to Chinese economy. But aluminum industry is high energy-consumption and heavy-pollution industry. The government has paid more attention to aluminum industry in recent years. Nowadays the bothersome problem which counterworks Chinese aluminum industry is pollution from solid wastes. Main Solid wastes from aluminum industry are red mud from alumina refineries and spent potlining (short as SPL) from aluminum smelters. Spent potlining are waste lining materials from aluminum electrolysis cells. During production of aluminum, due to reactions between melted electrolyzer and pot lining as well as penetrating of fluorides into pot lining, newly-formed compounds inlayed in pot lining, destroyed the lining structure and brought pot lining cracking. Melt rushed out of lining cracks, cells have to be stopped running and ready for heavy repair. Cell life generally varies from 1500 to 2000 days. Spent potling is an unavoidable solid waste from aluminum industry."

Jan 1, 2008

By Michael Heximer, Dominic Verfielst, Timothy Moore

"Teck's Trail Operations recently installed new pressure filters in the cold stage purification step in the zinc leaching plant. Alloy 2205 duplex stainless steel was chosen as the material of construction as it was in use in the hot stage purification operation. Within a year of commissioning, an unacceptably high rate (greater than 1 mm/y) of corrosion was observed on the weld heat affected zone (HAZ). Laboratory and field tests were conducted to establish the conditions under which the corrosion was occurring. The tests isolated the aggressive conditions to a unique combination of materials present during the filter regeneration stage. Furthermore, the change of the duplex grain structure of the alloy during welding resulted in the HAZ being more susceptible to the corrosive environment. A new material of construction was recommended as a result of the investigation.IntroductionThe sulphide leaching plant uses four horizontal tank pressure leaf filters to remove solids precipitated in the cold stage electrolyte purification process. The current filters were installed in 2007, and replaced a bank of filter presses. The material of construction for the filters - alloy 2205 duplex stainless steel - was selected based on its successful use in similar service areas of the leaching plant. However, within the first year, unexpected and rapid corrosion of the filter tank material was observed. Although moderate general corrosion was noted throughout the filters, the attack was particularly aggressive in the areas where intense heat was applied during fabrication, observed at the HAZs caused by welding, and on the exposed edge grain of the duplex plates. On the inaugural annual inspection of the filters in the first year of operation, a corrosion penetration rate of 1.0 to 1.5 mm/y was observed at the HAZs. The parent plate of the pressure tank was a minimum of 6 mm, with a minimum allowable thickness of 3 mm under the ASME pressure tank design rules. Therefore, the projected useful life of the filters could then be roughly calculated to be two to three years. Urgent action was required to understand and correct this problem."

Jan 1, 2012

By Adelana Adetunji

Ilmenite ore samples obtained from Dankoli in Zamfara, North Western Nigeria has been characterized using Energy Dispersive X-ray fluorescence (EDXRF) technique, X-ray diffraction (XRD) technique and the Neutron Activation Analysis (NAA) technique. The major constituents in the ore were quantitatively found to be TiO2 and Fe2O3 in concentrations of about 60wt% and 31wt% respectively. These occur in the forms of magnesian ilmenite (Fe, Mg)(Ti, Fe)O3, pure ilmenite (FeTiO3), and barium copper yttrium oxide (Ba2Cu3YO6.56) minerals. Other constituents/impurities in minor or trace quantities include MnO, Ta2O5, Nb2O5, Wo, SnO2, Hf, Zn, V, Zr, Co, Pb, Br, Al, Rb, Y, Th and U.

Jan 1, 2006

By Samuel Senanu, Benjamin Agyei-Tuffour, Lifeng Zhang, Eivind Øvrelid, Adegboyega Nathaniel Femi

"The solar grade silicon ingot produced from directional solidification process usually pushes the impurities to the top and finally cut off and discarded, which leads to material loss. The hard inclusions lead to wire breakages during the cutting of the ingot in wafers. The main kinds of inclusions found in solar grade silicon have been investigated using vacuum filtration: needle-like Si3N4 and lumpy SiC inclusions. Clusters of SiC inclusions and Si3N4 are also found. Surface observations of the scraps before polishing reveals that Si3N4 inclusions are usually bigger and in some cases can be about a few millimeters. SiC inclusions are usually smaller, ~200µm but can be ~500µm in some cases. Inclusions observed after filtration are mainly SiC with diameters ~10µm. Through the vacuum filtration, 99% inclusions can be removed 99%. The possible mechanisms of filtration are cake filtration for the larger sized Si3N4 and SiC inclusions and deep-bed filtration the SiC inclusions. For the directional solidified silicon ingot, an approximate distance of ~10mm gave an encouraging cutoff thickness. The inclusions sizes were below 10µm. Introduction The search for an alternative source of energy to fossil fuel has led to a dramatic increase in the demand for solar energy due to its high dependability (abundant in nature) and environmental friendliness 1). During the last 5 to 10 years, the annual worldwide production of solar cell by the photovoltaic industry has increased to an annual rate of 30 to 40 percent 2). A necessary condition for the maintenance and even an increase of this growth rate is a decrease in the cost of feedstock for the solar cell production 1). The total international production in 1997 was 130 MW worth more than $500 million. In 2004 the consolidated world total production of PV cells increased to 1146 MW or around. $7 billion (Figure 1) 3). Silicon is currently the most dominant semiconductor material used in the PV industry. As shown in Figure 2 3), solar cells consist of two types of material, often the p-type and n-type silicon. Light of certain wavelengths are able to ionize the atoms in the silicon (causing atoms to either gain or lose electrons) and the internal field produced by the junction separates some of the positive charges (“holes”) from the negative charges (electrons) within the photovoltaic device. The holes are swept into the positive or p-layer and the electrons are swept into the negative or n-layer. Although these opposite charges are attracted to each other, most of them can only recombine by passing through an external circuit outside the material because of the internal potential energy barrier. Therefore if a circuit is made, power can be produced from the cells under light because the free electrons pass through the load to recombine with the positive holes."

Jan 1, 2008

By Kazuki Morita

Dissolution mechanism and solubility of chlorine in the oxide melts, such as CaO-SiO2-Al2O3 (-Na2O), Na2O-SiO2-Al2O3 and CaO-SiO2-FeO systems, have been equilibrium technique was employed with controlled Po2 and PCl2, (Po2 = 10-6 -10 19 atm, PCl2 10-6 -10-13 atm at 1673-1748 K). The solubility of chlorine in the 40mass%CaO-40mass%SiO2- 20mass%Al2O3, slag was found to vary in proportion to Pb2/ w and pc/z/p' which proved that chlorine dissolved in the melts as C1 anion. Hence, the chloride capacity (CCI-), indicating the ability of molten oxide to absorb chlorine, has been defined as; The Ccl value was observed to increase with increasing slag basicity and temperature, and showed a reasonable relationship with that Of CS2-. Based on the result obtained in the present study, chlorine distribution during incineration with slags was predicted quantitatively.

Jan 1, 2003

By David Rees

Tomago Aluminium, a 400,OO tonnes per annum primary aluminium smelter in Australia, has installed Ozone for biological control of its process water. The system was designed in Australia by Ionics Watertec Engineering, whilst ANCO Australia monitors the water quality and provides technical support for the project. The motivation was initially to reduce operating costs, however investigations indicated that there were substantial environmental benefits to be achieved by the elimination of a part, or all of, the chemicals being used to control the system. Also the existing chemicals appeared to be losing their ability to control biological growth in the system, in particular, the legionella bacteria. Ozone water treatment commenced in January 1998 and after a short transition period has operated without chemical addition since. There appears to be no doubt that the biological control is effective, the clarity and purity of the water has improved and initial testing indicates that the corrosion control rate is acceptable, although some chemical corrosion control may be introduced after further testing around the total circuit to guarantee protection

Jan 1, 1999

By Takahiko Okura

"It is said that the energy and resources crisis will come before long because the lifetime of known deposits of crude oil and common metals such as Pb, Zn, Cu is estimated to be less than 50 years. Establishing the sustainable society by means of resources-recycling has become an absolute necessity.The non-ferrous metals industry in Japan has been involved in the resource- recycling business for many years, along with the introduction and enforcement of various legislations to preserve the environment and natural resources. Including process-linkage during various manufacturing activities, the non-ferrous metals industry, the iron-making and cement industries are treating considerable amounts of recycled materials and wastes, in an environmentally-sound and economic manner.The Mining and Materials Processing Institute of Japan has submitted “The present and issues in Japanese non-ferrous metals and recycling industries.”The topic of the paper is to highlight the actual conditions within the resources-recycling structures and the present issues.IntroductionGlobalization has been changing the world, introducing the spike of energy and metals price. In addition, the preservation of the environment has also been strongly facing the crisis and many people have been aggrieved by both shortage and the increment in the price of the meals.In the world of metals, even though their reserves are coming depleted, the production rates are increasing, and then the industry has to enhance their productivity under stricter environmental regulations. The Japanese industry experimented the same scenario some 40 years ago, facing big pollution problems, but concurred them and enhanced the technology to overcome the more severe regulations. It will be fruitful to present the current situation in the Japanese industry for the world. The present issues are also presented."

Jan 1, 2008

By V. M. Mukhin

Among the methods proposed for spent activated carbon regeneration, the most acceptable is, thermal reactivation, because in this case the existing equipment for manufacture of activated carbon can be adapted for this purpose. In order to conduct the process of thermal re-activation of spent activated carbon directly at gold mills, a full-scale drum-type furnace with external electric heating has been developed, i.e. EPV-300 model with a throughput rate of 50 to 120 kg/hour. Its use ensures restoration of the adsorption properties of carbon up to the level of fresh activated carbon with an insignificant (by 0.7%) decrease in strength and with a high (95% to 97%) yield of reactivated carbon. During the recent years, activated powder carbon has been extensively used in flotation processes for treating polymetallic ores at ore treating plants to improve recoveries of main metals (copper, lead, nickel, etc.). Especially large volumes of activated powder carbon are used at the Talnakh concentrator of the Norilsk Mining and Metallurgical Complex in Russia for absorption of residual flotation reagents from recycled water in order to ensure efficient selective separation of minerals with similar physical and chemical properties.

Jan 1, 2006

By Z. S. Wronski

In rapidly solidified Fe-Nd-B permanent magnet alloys, the content and distribution of Nd-rich intermetallic and Fe-phases determine coercivity Hc and remanence Br. Consequently, microstructure plays a crucial role in deter- mining the (BH) max-product of permanent magnets fabricated from these alloys. A study has been initiated to investigate changes in microstructure and the effects on magnetic properties as the material is processed from arc-melted ingot to melt-spun flakes and finally to a product consolidated by hot-forming. Anisotropic magnetization behaviour has been observed in rapidly solidified flakes after low-temperature annealing.

Jan 1, 1989