Search Documents

By Byung-Su Kim

Most electric arc furnace dust (EAFD) treatment processes employ carbon as a reducing agent for the zinc oxide in the EAFD. In the present work, the reduction reaction of zinc oxide with carbon in the present of various additives was studied. The effects of temperature and the additives of calcium carbonate, magnetite, and mill scale on the kinetics of the reduction reaction were measured in the temperature range of 1173 K - 1373 K under nitrogen atmosphere using a weight-loss technique. The mill scale is one of byproducts generated from the steel rolling process. From the experimental results, it was concluded that all three additives accelerates the reaction rate of zinc oxide with carbon, but the effect of addition of calcium carbonate is the highest. It was also found that magnetite, mill scale, and calcium carbonate in the reduction reaction of zinc oxide with carbon promotes the carbon gasification reaction.

Jan 1, 2006

By Berndt Moeller

Mercury-cell chlor-alkali production plants generate mercury contaminated wastewater streams from which mercury must be precipitated and filtered, resulting in a sludge containing 2% mercury (designated KI06) that cannot be landfilled in the United States without treatment. REMERC is a chemical treatment process used to recover 99% of the mercury from wastewater sludge generated at these plants. The process uses leaching to oxidize mercury compounds to mercuric chloride, washing and filtration to separate mercuric chloride from the treated sludge, and cementation to reduce the mercuric chloride to metallic mercury. Mercury not recovered in cementation is recycled to the wastewater process for precipitation and filtration. Treated sludge contains less than 260 ppm total mercury and 0.2 ppm TCLP, meeting the USEPA low mercury subcategory specifications that allow landfill disposal. REMERC uses readily available chemicals, is straightforward to control and inexpensive to operate, has no mercury emissions to air, and recovers metallic mercury. REMERC enabled significant cost savings including lower solids disposal costs, recovery and reuse of metallic mercury in the chlor-alkali process, and ability to treat non-wastewater sludge. No new EPA permits were required. REMERC was shown to be a viable process for recovery of metallic mercury from K106 designated sludge.

Jan 1, 2003

By R. Hamar, G. Lamanthe

"To realize complex shaped pieces, like turbine blades, superalloys are cast with the lost-wax process. The end properties of these parts depend upon their microstructure as well as upon the occurence of casting defects such as micropores and hot tears. Such features are governed by the local solidification conditions which may be describe by the calculation of thermal transfers between alloy and mould. It needs the evaluation of numerous parameters which are fitted from experimental measurements in real castings. In further simulations, any parameter may be changed, in order to determine its influence. Such a single modification is quite impossible to realize in real castings, which shows that numerical modeling is a very good way to study casting processes.This modeling technique of casting is applied here to the real study of a typical low pressure turbine blade of a civil engine.IntroductionAircraft engine manufacturers use superalloys to produce turbine blades. They have to obtain a given microstructure and to avoid solidification defects to give good mechanical properties to theirs castings. For example, microporosity is induced by a large shrinkage that cannot be completely fed with the remaining liquid alloy .The optimization of casting processes needs a good Knowledge of the solidification process, that must be controlled at every place in the casting, and at every time of its freezing. Material and heat transfers that occur during the solidification, can be estimated from rather complex calculations. To model these physical phenomena, the evaluation of many parameters must be made. In this aim, some casting experiments are fitted with numerous thermal captors. The identification of experimental and computed thermograms let us estimate these parameters.A long-range scientific cooperation between SNECMA and INPG has enabled the realization of such studies on this topic. From all of them, this paper describes an experimental and computed investigation which has been led on a typical low pressure turbine blade of a civil engine."

Jan 1, 1986

By K. G. Wang, M. E. Glicksman, P. Crawford

"We formulate the mathematical solution to late-stage multi particle diffusion in finite systems. The transition from finite system behavior to that for an infinite system is established. Large-scale simulations are reported regarding the dynamics of phase coarsening. Even in the case of a small volume fraction (Vv = 10-4), the particle size distribution is broader than that for the well-known Lifshitz-Slyozov limit at zero volume fraction. We also report the first simulation studies of extremely low volume fraction, for which corresponding experiments, as well as other simulations, do not exist at present for comparison. However, in the case of moderate volume fractions (Vv = 0.1), the fiucutations in the volumetric growth rate of particles are extracted from our simulations. These simulations provide additional insight into the statistical nature of diffusion interactions, including multiparticle stochastics during microstructural evolution.IntroductionPredicting microstructure evolution in alloys remains one of the cornerstones of materials science. Phase coarsening is a common process in microstrucural evolution that leads to a decrease in the excess total interfacial energy of the system. The system typically consists of separate and identifiable units, or domains, such as second-phase particles distributed in a matrix. During phase coarsening, larger particles grow at the expense of small particles. Over time, this ""competition"" results in an increase in the average size of the particle population, and in a concomitant decrease in the number of particles.Particle size and microstructure of many cast alloys depend on similar coarsening processes. Indeed, properties of these materials, such as strength, toughness, ductility, and electrical conductivity, depend on the material's average particle size and particle size distribution (PSD). Understanding and controlling microstructures in two-phase systems are clearly of widespread technological importance."

Jan 1, 2001

The generation of acid mine water is? due to the oxidation and weathering of sulfide bearing tailings and overburdens. Ferrite precipitation prooess has been applied to treat acid mine water. The conventional ferrite preC1pitatlon requires air oxidation at high temperature, or long aging time or addition of magnetite powder ,as promoter. In this investigation, a modified ferrite, precipitation process is developed by which magnetic ferrite can be produced at an ambient temperature. Acid mine waters from Berkeley Pit (Montana, U. S. A.) and from Noranda Tailings (Quebec, Canada) were used. The co precipitation of heavy metals from these two acid mine waters is studied as a function of FeIM molar ratio, oxidation time and settling rate under applied magnetic field. The investigation indicates that the modified ferrite co precipitation can remove substantially all of the, dissolved metal ions from acid mine water. The ferrite product obtained after precipitation' is characterized by XRD, SEM, BET and saturation magnetization. The results show that spinel ferrite, precipitation can be achieved at room temperature and the saturation magnetization of ferrite product from,acid mine water is comparable to that of pure ferrites.

Jan 1, 1995

By M. Rockandel

"Universal Dynamics Ltd. of Vancouver, Canada has developed, patented and commercialized the ""REMERC"" process for the treatment of mercury contaminated sludges and soils. Mercury is extracted into an acidified and oxidizing, sodium chloride brine solution. REMERC was initially developed to treat mercury contaminated EPA listed wastes (K106) generated by the chlor-alkali industry. More recent work has expanded the capability;' of REMERC to include remediation of mercury contaminated sites, equipment and building materials.In the process mercury is currently recovered from solution by cementation on iron powder in an agitated reactor. The process recovers high purity elemental mercury (99.9% purity). Cementation typically recovers about 90-95% of the mercury in 30 minutes. Higher recovery is not necessary because of the recirculation of the leach solution. When treating highly contaminated chloralkali wastes (5-13% mercury content), REMERC will reduce the mercury laden solutions from 400-1,000 mg/L mercury to 50-100 mg/L. In the treatment of less concentrated wastes «1,000 mg/kg mercury) such as those encountered in site remediation, the treated solutions will generally contain 10-20 mg/L mercury. Cementation while being simple and able to achieve the required recovery has the. undesirable properties of; requiring a solid-liquid separation and adding iron to solution which must be precipitated, ultimately increasing the weight of residue to landfill. .The potential advantages of electrolysis were recognized early in the development of REMERC. Mercury electrolysis is well known in gold and chloralkali processing. Initial testwork utilized a liquid mercury cathode and a coated titanium anode both common to chloralkali producers. The mercury cathode appeared susceptible to polarization and solution impurities significantly affected performance. Agitation of the mercury pool improved performance but it was still not possible to achieve the reduction objectives. Current efficiencies were low, near 10%, and it was apparent that a relatively large cathode pool would be required to limit the current density. A number of electrode combinations with and without a membrane were then tested in a vertical electrode' configuration but the desired performance was not obtained."

Jan 1, 1997

By Sergio Neves Monteiro

This work had as its objective the characterization of a waste material, steel slag, generated from an integrated steel plant, with a view to its recycling and incorporation into red ceramics fabrication. The characterization was performed in terms of chemical composition by X-ray fluorescence (XRF), particles size distribution, X-ray diffraction (XRD), thermal analysis (DTA/TG) and scanning electron microscopy (SEM). The results indicate that the steel slag presents high amount of Ca, Fe, Mg and Si. The weight loss of the steel slag at temperatures above 800oC is associated with calcium carbonate decomposition. The coarse particle size of the steel slag is inadequate for its direct recycling into red ceramic fabrication. It is necessary to screen or to grind the waste. As a possible solution, it is suggested that screening or grinding the steel slag to a convenient particle size distribution would allow its successful industrial incorporation into red ceramics products.

Jan 1, 2006

By L. S. Montagna, R. M. C. Santana

"Since the industrial revolution, plastic products sector has growing bigly, however this fact presents as consequence the increase of municipal plastic waste (MPW).The aim of this work is to developmet polymer mixture from MPW with the adittion of rubber tire (TR) post use and to study the mechanical and morphologycal properties. The polymer mixtures Polypropylene/High impact polystyrene/TR (PP/HIPS/TR), where rate weight TR used was 10, 20 and 30 % and with three size particles (500, 710 e 1000 µm). The specimen tests were obtained by injection molding. Preliminary results of mechanical properties showed that the increase of TR influence in a reduction of the flexural and tensile resistance. Results by scanning electronic microscopy on the fracture surface of mixtures PP/HIPS/TR showed a better interaction of TR particle with HIPS than with PP. Also, the presence of microcavoids was observed, characteristic in PP/HIPS blends, favouring in the increase of its opacity.IntroductionOne great part of the municipal solid waste (MSW) is composed of polymer mixed since commodity plastics, blend to polymer composite. The processing of plastics mixtures for recycling has been attempted with some success, but poor mechanical properties and uncertain economic value limit their more versatile reuse. Polyethylene (PE), polypropylene (PP), polyethylene terephthalate (PET), poly(vinyl chloride) (PVC) and polystyrene (PS) are among the most common plastic waste, predominantly used in packaging food industry [1].One other problem that preoccupy to the society is the increase of rubber tire waste in the proportion of MSW. In Brazil, from 1999 to 2004, 39 % from 386 mil ton of tire post-use were destined to ciment Industry as source of energy [2]. However this destiny produces one other problem, environment pollution, due to gas mixture emitted.Recycling represents a valid alternative to the disposal of post-consumer plastics in common landfills if it is possible to obtain new materials with good final properties compatible with practical and, above all, by cheap methods [3]The reutilization of group tire rubber (TR) powder as a dispersed elastomeric phase in a thermoplastic matrix offers an opportunity to design second generation materials which would be recyclable due to the thermoplastic matrix and which potentially could present thermoplastic elastomer (TPE)-like mechanical behavior. [4]."

Jan 1, 2008

By Jinsheng Wang, Wei Lv, Xuewei Lv, Pingsheng Lai, Jie Dang

The isothermal reduction kinetics of vanadium titanium magnetite sintering ore was investigated by thermo-gravimetric analysis at a temperature range of 1123–1223 K under 30% CO + 70% N2 gas mixtures. The apparent activation energy of reduction was calculated by iso-conversional method and its value is 36.7 kJ/mol. The model function describing the reduction mechanism was discussed by Sharp analysis and the results revealed that the reduction process is controlled first by random nucleation and nucleus growth mechanism (RNNGM) as reduction degree is lower than 0.5, followed by the mixed influence of RNNGM and phase boundary reaction when reduction degree is higher than 0.5.

Mar 1, 2017

By H. Matsuda, T. Iwashita, H. Awata, H. Liwei, D. Hirabayashi, Y. Saito, S. Ozawa, Y. Goto

"The present study is concerned with investigating the effect of chemical treatment on enhancing the HCl absorption capacities of coal burnt ash and slag. It was found that the HCl absorption capacity of coal burnt ash discharged from fluidized bed combustor was improved by hydration with water and 5% polyethylene glycol solution. This phenomenon was based on an increase of the specific surface area of treated coal burnt ash. The HCl absorption capacity of hydrated ash with polyethylene glycol solution was almost equivalent to that of standard CaO and Ca(OH)2. In particular, the specific surface area of hydrated ash with polyethylene glycol solution was found to be 19 m2/g, which was more than over eight times larger than that of raw sample. Hydrated slag treated with lON sodium hydroxide solution also showed high HCl absorption capacity, with highly improved surface area. It was found that the absorption capacity of slag for HCl depended on the treatment time, showing the maximum absorption capacity for 12 hours of hydration treatment.IntroductionA large amount of coal burnt ash, slag and dust are discharged from such industrial processes as coal combustion and metal refinery etc., and it becomes an serious problem to recover and diminish these solid wastes because of the shortage of dump sites and subsequent metal elution to the environment. Figure 1 shows the present situation of reutilization of coal burnt ash and slag in Japan [1,2]. It is shown in this figure that these solid wastes are recycled as materials in the fields of earthwork, agriculture and forestry etc. A part of these solid wastes, however, is still dumped to landfill. To decrease this dumped amount, the development of environmentally friendly reutilization technique for these solid wastes is of great importance."

Jan 1, 2000

By Daniel Helm

The first industrial application of direct solvent extraction of nickel from hypersaline sulfate feed solutions has highlighted the need to investigate the influence of chloride on the extraction behaviour nickel in the presence of calcium using Versatic 10 and the solubility characteristics of gypsum. Temperature-solubility curves for gypsum in various aqueous electrolytes were prepared. The solubility of gypsum is increased significantly by the presence of sulfate ions, while chloride ions decrease it for a given temperature. The anion effects of chloride and sulfate on the extraction of calcium and nickel by Versatic 10 corresponded well with the complexing ability of the anions. It was shown that the presence of chloride shifts the extraction isotherms for both metals significantly to the left, while decreasing the selectivity of Versatic 10 for nickel over calcium. The loading of nickel onto Versatic 10 in this system was shown to be at a maximum within 3 seconds, while calcium extraction took between 4 ? 5 seconds to load to a maximum. Chloride ions had no influence on loading kinetics of nickel, but depressed the rate of calcium loading. It was shown that in the presence of an excess of nickel, calcium loading is effectively eliminated, and that calcium is scrubbed from Versatic 10 within 2.5 seconds of contact with nickel electrolyte.

Jan 1, 2003

By O. A. Ogunseitan

The contamination of aquatic ecosystems by mercury wastes is one of the most serious forms of environmental pollution associated with the metal mining and electrochemical industries. The transformation of inorganic mercury to alkylated species is a reversible bacterially-mediated process. The production of methylated mercury is of ?major public health and eco-toxicological concern because these forms of mercury are highly toxic ?and they bioaccumulate in aquatic organisms. We determined the response of the genetic determinants of mei:cury transrormation by Pseudomonas species (that predominate in contaminated soils and sediments), to the concentration and species? or available mercurfiations. By combining selective isolation and gene. ?probe techniques, the intrinsic genetic potential for mercury detoxification in a contaminated environment ?can be estimated. We determined that genetic units required for mericury volatilization (merA ?for mercuric reductase) are naturally amplified in response to mercury. Mercury-resistant bacteria that tolerate up to 100 ug Hg(Il)/ml of medium contain about 10 times more DNA fragments encoding merA than in unadapted bacteria. The exposure of bacteria to methylated.Hg (10 ug/ml lake water) produced increases (up to 10 times) in .genetic units, and higher levels of genetic expression (up to 50 times) per ml of lake water for the mercury reductase system, than on-induced lake water. The findings suggest that in environments where methylated Hg may accumulate as a result of bacterial activity, the reverse reaction which leads to the removal of mercury through volatilization from the system, may be achieved by inducing genetic ?amplification and expression of the mercuric reductase gene system.

Jan 1, 1991

By Nobuyuki Masuda

In Japan, the municipal solid waste, which amounts to 50 million tons, is generated every year and most of it is incinerated. The fly ash from the municipal waste incineration (the primary fly ash) contains heavy metals, such as lead and zinc, etc., and dioxins. In case of melting, the fly ash from the process (the secondary fly ash) contains high concentration of heavy metals (e.g., Zn; 1-20%, Pb, 1-10%). Metal Mining Agency of Japan launched a four-year project in 1999 to establish the integrated technologies to recover the valuable metals from, and to decontaminate, the primary and secondary fly-ashes in the practical scale by utilizing the existing metallurgical processes and facilities, along with the energy saving. The segregation, flotation and chemical treatment are applied to the treatment of the primary fly ash. The secondary fly ash is treated with MY (Mitsui-type blast furnace) Process after the chlorine removal to recover the heavy metals in the ash, In this paper, the segregation and flotation process for primary fly ash and MF process for secondary fly ash are explained. The main results of experiments done from 1999 to the mid of 2001 to design the pilot plants and to optimize the operating conditions are described. The main results of the experiments are as follows: - The segregation reaction of Cu was confirmed by the experiment on the treatment condition of 800 and 900`C with adding oil cokes and water to the primary fly ash, and 99.98% (toxicity equivalent) of the dioxins were decomposed by the treatment. - Washing tests of secondary fly ash to feed MF resulted that more than 70% of chloride were removed, but still lower than expected, and agglomeration tests were successful by the results of the sufficient strength of briquettes produced though a little more binder for the agglomeration is required than usual operation. - Smelting experiment by downsized MF showed that valuable metals, such as zinc and lead, are recoverable in the furnace dust. Recovery ratios, Zn: 58% and 67%, Pb: 74% and 83%, are accomplished.

Jan 1, 2002

By Markus A. Reuter, Antoinette van Schaik

"Product design engineers select from a wide range of materials and combine them into multimaterial product designs. These include various materials (metals and non-metals) which are complexly integrated (e.g. welded, glued, alloyed, layered). The recycling/recovery rate of consumer products are determined by the different materials and alloys used, but also by the particle size and multi-material particle composition after shredding (combination of materials due to design). Eco-design (for recycling) and Design for Recycling (DfR) can only be conducted if the interconnectivity of material/metal in various unliberated materials is accounted for and its effect on material and energy recovery can be linked back to design. This paper will discuss the basic principles of these DfR models and it is shown how these tools (i) are linked Computer Aided Design (CAD) and Life Cycle Assessment (LCA) software, (ii) affect conceptual design specifications of products, (iii) integrate the complex detail of the recycling system and recyclate quality and hence (iv) make recycling an integrated part of the product system. Furthermore, it is shown how these assessment tools and models can be applied for benchmarking of the recyclability and environmental damage created by the recycling of end-oflife consumer goods in order to e.g. (i) provide the (original) equipment manufacturer with knowledge and solutions to support product stewardship and Extended Producer Responsibility; (ii) create awareness of the consequences/benefits of design, products and recycling systems to manufacturer, designer, legislator, recycler etc.; and (iii) assist the consumer in their choice of consumer goods from an end-of-life point of view.IntroductionA first-principles basis is required in order to be able to simulate and predict the recycling/recovery behaviour of products facilitating Design for Recycling (DfR) and Eco- Design. This links recycling technology and the environmental consequences of recycling directly to product design."

Jan 1, 2008

By Kathie Mcgregor, Muhamad Firdaus, Nathan A. S. Webster, Yvonne Durandet, W. John Rankin, M. Akbar Rhamdhani

There is a growing interest in recycling/recovery of rare earth elements from permanent magnets. A number of processing techniques are currently being developed but are highly sensitive to the oxidation state of the material. The oxidation microstructure of NdFeB magnets is studied at high temperatures (773-1173 K) to understand oxide formation mechanisms and support the development of viable recycling strategies.

Mar 1, 2017

By Tiffany Brown

In the thiosulfate gold leaching process, thiosulfate is used to complex gold following electrocatalytic oxidation of the native metal by Cu(II)-ammines. Unfortunately, Cu(II) complexes also catalyse the undesirable conversion of thiosulfate to polythionates. We have been seeking alternatives to ammonia, which fulfil the role of ammonia but minimize thiosulfate decomposition. One aspect of these studies has involved the determination of the rate of thiosulfate oxidation by the Cu(II) complexes from UV-Visible spectral changes. Various ligand classes, including pyridyls, polyamines, aminocarboxylates and picolinates, have been tested and the majority found to inhibit thiosulfate decomposition. Interesting variations in reactivity with the nature and denticity of the ligand and L/M ratio have been observed. In the case of open chain polyamine ligands with 2 to 5 nitrogen donors, the rate of thiosulfate oxidation was generally found to decrease with the denticity and the concentration of each ligand. Saturation of the Cu(II) coordination sphere appears to inhibit the oxidation of thiosulfate when excess thiosulfate is present. The Cu(II) complex of the branched polyamine ligand, tris(2-aminoethyl)amine (tren) exhibits this behaviour in excess thiosulfate. Interestingly, when the [Cu(tren)(OH2)]2+ complex is in excess oxidation of thiosulfate was observed. This unexpected finding prompted a spectrophotometric study of this reaction which has revealed that the oxidation of thiosulfate involves several processes, two of which involve the formation and decay of a tetrathionate radical.

Jan 1, 2003

By Keiji Toyabe

Several purifying techniques have been developed for controlling the impurity levels in the copper electrolyte at Niihama Copper Refinery. These have been carried out as follows; i ) the study of the reaction in liberation made it possible to raise the current efficiency for arsenic removal by more than 50% and to decrease generation of arsine sharply. By applying this method, a good performance was attained at commercial operation. li) the antimony in the electrolyte can be successfully removed by contacting it with activated carbon. This procedure is applicable particularly when there is a large amount of antimony in the copper anode. lli) for the nickel sulphate recovery from the electrolyte, an electric evaporating system was developed. The characteristics of this process are, capability of continuous operation with less manpower, the high recovery ratio of nickel sulphate (more than 85% as nickel) and no black acid formation in the treated solution.

Jan 1, 1987

By Peng Peng, Ouo Cheng, Guodong Lai, Lijuan Chu, Zebiao Zhang

"The pressure acid leaching residue of zinc concentrate contains a large quantity of sulfur. The present study attempts to leach sulfur using a mixture of ammonium sulfide and water solution at 25°C. Effects of three leaching variables: ammonium sulfide concentration, leaching time, liquid/solid ratio on the sulfur leaching rate were investigated. The process conditions were optimized using response surface methodology based on the central composite design. From the analysis of variance (ANOVA), the significant factors on response were identified. The optimum conditions for leaching elemental sulfur from pressure acid leaching residue of zinc concentrate were obtained using an ammonium sulfide concentration of 2.5 mol/L, leaching liquid-solid ratio of 6.5:1 and leaching time of 7 min. Under the optimum experimental conditions, a maximum of 98.50% of total sulfur was extracted. The experimental results obtained agreed satisfactorily with the model predictions, with a correlation coefficient (R2) of 0.99.IntroductionSulfur is widely used in agriculture, medicine, rubber, building materials, gunpowder, wine and sugar, and other fields [1]. Currently the world sulfur production is 40Mt, out of which more than 90% is recovered from industrial processes, and 10% is natural [2], This highlights the importance of sulfur recovery. As the pressure leaching technologies [3] continue to mature and are increasingly applied to refining, a large quantity of high-sulfur residue is produced [4-5]. It is desirable to recover sulfur from this residue, so that it is economically advantageous, and reduces environmental pollution [6]."

Jan 1, 2012

By T. Wang, R. G. Reddy, D. Mantha

"A new eutectic LiN03-NaN03-KN03-KN02 quaternary molten salt system was calculated using thermodynamic modeling. The eutectic temperature was predicted to be 100°C. The melting point and heat capacity of the salt eutectic composition were determined using DSC. The experimentally determined melting point is in excellent agreement with the predicted value. The melting point is more than 124°C lower than that of the KN03-NaN03 solar salt. The density of the molten salt was experimentally determined as function of temperature. Using the density, heat capacity and the melting point, thermal energy storage density and gravimetric storage density of the quaternary molten salt were calculated and compared with that of solar salt. The larger storage density value of this molten salt indicates that this salt has a better energy storage capacity for solar power generation systems.IntroductionMolten salts have been used as thermal energy storage media for solar energy applications. Nitrates are being used in the solar energy applications for their low melting point, low unit cost, high heat capacity, high thermal stability, negligible vapor pressure and high energy storage density [l]. Solar salt (NaN03/KN03: 60/40) is the most popular thermal energy storage medium which is currently being used with the freezing point of 221 ·c [2]; another ternary system HITEC® which contains NaN03, KN03 and NaN02 has freezing point of 141°C [3]. Newer nitrate salt mixtures are being studied and projected as potential candidates for thermal energy storage (TES) and heat transfer (HT) applications. Based on these favorable features, molten salt can work directly as the energy storage medium below 500°C [l]. Development and synthesis of newer molten salt mixtures with freezing point lower than those currently used for thermal energy storage applications is necessary for sustained utilization of solar energy. The approach to develop lower freezing point molten salt mixtures is by the prediction of new eutectic mixtures and also by the development of new nitrate compounds."

Jan 1, 2012

By Masaru Imaizumi, Hiroyuki Nomura, Mitsuharu Takita

"Cast iron possesses many superior characteristics caused from precipitated graphite structure, for example, castability, wear resistance, solid lubrication, damping capacity. But the more graphite hyper-eutectic cast iron contains, the lower its mechanical strength becomes, because graphite gives a negative effect to strength of cast iron. In addition, primary graphite tends to segregate during solidification, so uniform materials are difficult to be produced.In this study, authors introduced semi-solid processing in developing new and high quality cast iron. A series of semi-solid processing experiments were carried out to clarify the effect of stirring condition; solidification temperature and etc. on microstructures and characteristics of cast iron. In particular much attention is paid to the appearance of ternary eutectic zone at the final stage of solidification. As the results advanced hyper-eutectic cast iron was obtained with high quality of both the mechanical strength and wear resistance. As for the mechanical strength, 300MPa and 0.60% are obtained as the tensile strength and the elongation values, respectively, under the controlled stirring condition. This indicates that semi-solid processed hyper-eutectic cast iron is used prospectively without spheroidization.IntroductionCast iron has various good properties such as wear resistance, solid lubrication, damping capacity and machinability. The characteristics of cast iron are mainly decided by graphite structure, namely graphite shape and its distribution in the matrix. Mechanical strength of cast iron is large in the case of small quantity of graphite particles which are precipitated uniformly, however, it becomes small in the case of large quantity of graphite precipitated flakily."

Jan 1, 2000