By R. S. McClain

Continuous-circuit flotation and batch-scale precipitation tests were made by the Bureau of Nines to determine rejection of carbon and recovery of fluorine and aluminum compounds from aluminum reduction plant residues, About 40 to 60 pounds each of aluminum fluoride and cryolite are lost for each ton of aluminum produced. Gasoline and turpentine were satisfactory for floating carbon from both fresh water and saturated solution systems. Soluble fluorine and aluminum compounds were recovered by precipitation with sodium aluminate and carbon dioxide. Over 99 percent of the carbon was removed by flotation. Fluorine and aluminum recoveries up to 77 and 63 percent, respectively, were obtained in a combined precipitate and nonfloat product, In the fresh water system the combined product was mostly cryolite with some gibbsite. In the saturated solution system the product was mostly sodium fluoride, some cryolite, and minor amounts of gibbsite.

Jan 1, 1963

By D. G. Kesterke

The electrolytic reduction of uranium dioxide to molten uranium in fluoride baths at approximately 1,200° C was demonstrated. Electrolyte constituents were BaF2, UF4, and either MgF2 or LiF. Preliminary laboratory-scale experiments were made in which the uranium oxide was added continuously for 3 to 5 hours to the cell during electrolysis. Over 1,000 grams of metal of 99-8 percent purity was made in some tests, Major impurities were aluminum, barium, iron, silicon, carbon, and oxygen. The effects of cell design, geometry, and bath composition were investigated. Electrode arrangement was the most important factor in cell performance.

Jan 1, 1963

By Albert W. Deurbrouck

This report describes the preparation characteristics of the significant, presently producing coalbeds in Mercer County, W. Va. Approximately 650,000 tons of coal was produced in Mercer County, W. Va., in 1960, of which over 630,000 tons was cleaned in four preparation plants. In 1960 the Pocahontas Nos. 3, 6, and 11 coalbeds supplied 99.5 percent of the total coal mined in the county. Because the number of working mines In this county was small, only six samples were collected; four of which were of metallurgical quality as mined. The remaining two samples could be upgraded by washing at suitable specific gravities. Many of the samples taken were of metallurgical quality as mined; however, the float-and-sink analysis on these coals has been included to point out their amenability to the production of premium quality, special purpose coals. In general the coals were low-volatile bituminous in rank with low ash and sulfur contents.

Jan 1, 1963

By Frank A. Peters

A series of evaluations is being made to determine the relative processing costs of producing metallurgical-grade alumina from low-grade aluminous materials. These evaluations include the estimated operating and capital costs as well as recommendations for additional research and development to improve the processes and to lower their costs. The design for each process is based on published work. The three processes considered in this evaluation are designed to leach alumina as aluminum sulfate from calcined clay with sulfuric acid and to remove the silica residue by filtration. The filtrate from leaching is then purified by one of the following methods: Removal of iron in electrolytic cells using mercury cathodes; removal of iron by chemical precipitation through the formation of an iron-manganese complex; or precipitation of the alumina from an aqueous-ethanol solution, leaving iron in solution. Both the operating and capital costs for these processes are higher than those for the Bayer process. For plants producing 1,000 tons of alumina a day, the estimated operating costs per ton of alumina are: Electrolytic iron-removal process........... $81.35 Chemical iron-.removal process............... 82.08 Ethanol purification process............... 86.17 The investment in mercury is not part of the operating cost since this cost is considered equivalent to catalyst cost which would not be shown. The estimated capital investments for 1,000- ton-per- day plants on a Marshall and Stevens chemical equipment index basis of 240.0 are: Electrolytic iron-removal process...... $116,775,500 Chemical iron-removal process............... 99,418,900 Ethanol purification process................ 94,210,200 These investments include the working capital but not the land for each of the processes. Included in the electrolytic iron-removal process is an investment of $4,859,400 for mercury. Investigation of other methods for removing iron, of the decomposition operation, and of the leaching operation could reduce these costs.

Jan 1, 1963

By L. W. Higley

Procedures were developed for reclaiming high-temperature alloy scrap in the form of standard cobalt-base alloy. A cobalt-base, multicomponent, high- temperature alloy, such as S-816, can be successfully melted from scrap, and its specified chemical composition can be retained. Induction furnace melting in a controlled atmosphere was used to obtain ingots that were subsequently fabricated by impact forging to provide specimens for heat treatment and testing. Of the numerous metal elements in S-816 alloy, only small quantities of molybdenum were lost in the melting operation as finally developed. Test results indicated that the scrap material, after melting, forging, and heat treatment, was equivalent in room-temperature tensile strength, in high-temperature creep and stress-rupture properties, and in chemical composition to commercially produced S-816 alloy made from virgin material.

Jan 1, 1963

By S. J. Hussey

This Bureau of Mines report presents a discussion of the statistical approach to the design of experiments and indicates, by concrete examples, how and when statistical design is essential for obtaining meaningful data with a minimum number of experiments. Every research worker plans his work and designs his experiments in a manner which, based on his experience, seems most rational to him and which he believes will produce the information essential for resolving the problems. If the results obtained are open to multiple interpretations and are not of definitive reliability, the failure of the experiment design to produce the desired information may be due to several causes, These include faulty judgment in selecting the factors to be tested, ignoring the importance of interaction between factors, failure to adequately control test variables, and assuming that meaningful trends in the results can be identified without comparison to a predetermined experimental error. An experienced researcher probably will deduce from the nature of the data obtained that the design is faulty and may by trial and error ultimately arrive at the correct solution to the problem. Statistical methods of planning research minimize the chance of faulty experiment design, embody concrete procedures for testing the validity and reliability of the test data and for indicating mandatory changes in the design, and enable the researcher to obtain meaningful information with the least number of tests.

Jan 1, 1963

By Hillary W. St. Clair

This is an initial progress report on a theoretical study of the iron blast furnace. The purpose is to develop a thermochemical model that will simulate mathematically a real furnace. An analysis is made of the behavior of a hypothetical furnace, operating adiabatically on pure ferric oxide, graphitic carbon, and dry air. Relationships are derived for carbon consumption, gas composition, and reaction temperature for a furnace operating at steady state, and in which the smelting rate is slow enough for the gas and solids to approach thermal and chemical equilibrium. Analyses are made for two contrasting types of gas flow: (1) Nonturbulent flow, having no vertical mixing; and (2) turbulent flow, having perfect mixing during each step of the process. It is shown that some vertical mixing is essential for complete reduction of ferrous oxide and that the extent of vertical mixing is one of the critical factors in the behavior of the furnace, This analysis indicates that the thermochemical relationships in a blast furnace can probably be best simulated by a finite series of gas-solid reactors through which gas and solids flow countercurrently and in which the temperature and composition of gases and solids are assumed to be uniform. Any degree of vertical mixing can be approximated by the proper choice of the number of reactors.

Jan 1, 1963

By Robert C. Johnson

Water-swelling fluormicas and fluormontmorillonoids were synthesized and described. They were found predominantly in the system Mg0 - MgF2 - Si02, with varying amounts of Li+ or Na+, Some water-swelling synthetic minerals were prepared with only strontium or lead in the twelvefold position, Water- swelling compounds containing either K+ or Ba+ were not found. The synthesized water-swelling products were shown by electron microscopy, X-ray diffraction, and chemical analysis to be typically two-silica-layer, platy compounds, Except for the complete substitution of fluoride for hydroxyl, the compounds were similar to the natural micas or montmorillonites. The stability and properties of the compounds were further established by electrodialysis, by differential thermal analysis, and by anion and cation exchange methods. Fluoride in the interlayer positions was nonexchangeable except through decomposition of the product. Exchanging the sodium or the lithium of the synthetic fluormicas or fluormontmorillonoids with potassium ion, particularly those derived from KOH provided a product from which a completely inorganic paper of extraordinary flexibility was fabricated. This paper had excellent mechanical and electrical properties except for water adsorption and a high power factor. Neither of these problems was solved during this investigation. However, papers with dielectric strength from 1,500 to 5,000 volts per mil were readily fabricated, particularly from the lithium containing fluormicas or fluormontmorill onoids.

Jan 1, 1963

By Carl Rampacek

The conversion of dilute sulfur dioxide gas into sulfuric acid by autoxidation in mechanical cells of the flotation or gas absorber types was investigated. Bench-scale tests were made with sulfur dioxide-air mixtures to determine the influence of several factors on autoxidation of sulfur dioxide, using iron and manganese salts as catalysts. The laboratory investigation subsequently was extended to pilot plant acid-making tests, using a modified turbomixer gas absorber having a 12-inch-diameter impeller. Sulfur dioxide gas was produced for the tests by roasting pyrite in a fluidized-bed reactor. In the better tests, made with manganese sulfate as the catalyst, the equivalent of 1,000 pounds of anhydrous H2SO4 was produced per 24 hours as a 10-percent solution; power consumption was 0.2 kwhr per pound of equivalent anhydrous acid synthesized. The batch and continuous tests demonstrated the technical feasibility of producing dilute sulfuric acid by autoxidation of sulfur dioxide gas in mechanical cells when converting pyrite roaster or waste smelter gases.

Jan 1, 1963

By Robert S. Warfield

The Bureau of Mines investigated a geologically favorable area in the Beluga River coalfield in south-central Alaska to determine if there were sufficient minable coal reserves for onsite utilization to meet the projected thermal power needs of the Anchorage area. A program of diamond core drilling and sampling delimited a shallow saucerlike structure estimated to contain indicated reserves of more than 20 million tons of subbitminous coal in a seam over 50 feet thick that could be mined by opencut methods. A large sample of fresh coal was taken across the full width of the seam for washability studies. This sample, with 4 volume-percent of clay partings eliminated, contained 24.4 percent moisture and 16.8 percent ash and had a calorific value of 7,162 Btu per pound. The studies indicated that mechanical cleaning would be of doubtful value.

Jan 1, 1963

By A. W. Deurbrouck

Five preparation plants employing concentrating tables for washing 3/8- inch to 0 raw coal were tested. Two of the plants were washing Pittsburgh-bed coal, two were washing Pocahontas-bed coal, and one was washing Elkhorn-bed coal. Samples of the feed to and products from the tables were collected over the normal operating shift. These samples were analyzed, and complete performance criteria were determined. The results of this study show that the concentrating table is an effective fine-coal cleaner even when operating at 40 percent over the recommended 10 tons per hour feed rate. Recovery efficiencies for the 3/8-inch to 200- mesh size fraction ranged from 97.3 to 99.3 percent; maximum yield errors and ash errors were 2.4 and 1.0 percent, respectively; probable errors ranged from 0.074 to 0.115 specific gravity units and error areas from 52 to 73 square centimeters. The amount of minus 200-mesh material in the water used for feed water and dressing water to the table had no significant effect on the sharpness of the separation achieved but did have an effect on the ash content of the clean- coal product. In the one plant studied, the substitution of fresh water for plant circulating water reduced the ash content of the clean coal by about 6 percentage points.

Jan 1, 1963

By D. J. Bauer

Solvent extraction techniques were used to determine the extraction sequence of yttrium and the rare-earth elements in an amine solvent extraction system. Single-stage extraction with Primene 81-R resulted in separation factors of 3.8 between yttrium and dysprosium and 25 between yttrium and cerium. Yttrium was concentrated in the aqueous phase. EDTA and DTPA, as aqueous phase counterextractants, enhance separation factors in mine-rare-earth sulfate systems. Yttrium separation from heavy rare-earth elements exhibits marked sensitivity to the position of yttrium in the selectivity scale of the rare-earth elements with the sequestrants. Yttrium-ytterbium separation is more effective with EDTA, whereas yttrium-dysprosium separation is more effectively increased with DTPA.

Jan 1, 1963

By Edward W. Parsons

Conventional rock-bolt anchors often fail when installed in weak formations. The purpose of this work was to develop an anchor that would utilize an explosive charge to secure anchorage in any type of rock. Laboratory work to develop a rock-bolt anchored by explosive forming was initiated using rock-bolt models which had a drilled explosive chamber and were composed of various metals. This was followed by the use of several types of seamless tubing which were expanded with a water-coupled explosive capsule. By attaching a length of solid bolt to the anchor tube, a prototype explosive-anchored rock bolt was made. More than 150 laboratory models were expanded during this phase of development, During two field tests in underground mines (A and B) and one in an open- cut mine (C), 87 explosive-anchored bolts, 9 slot-and-wedge bolts, 2 bolts anchored with expanding grout, and 28 expansion-shell bolts consisting of three types of shells were installed and subjected to pull tests. The field tests were run to determine the effects of variables such as the amount and placement of the explosive charge, design changes in the bolt, and the effect on anchorage of different pull-test techniques. The field tests revealed the following: Mine A. The explosive-anchored rock bolt was feasible, but changes were necessary in bolt materials and in some details of bolt design. Mine B. The design and materials of the bolt gave excellent results in hard fractured rock, but no information was obtained concerning variations in the dimensions of the anchor unit or in the explosive charge. Nine C. Varying the explosive charge to produce a beaded surface on the bolt tube and tightening of the anchored bolt before pull-testing were found to increase significantly the anchorage obtained in soft ground.

Jan 1, 1963

By G. T. Krempasky

This report covers the installation and evaluation of lb reinforced concrete sets, 6 in each of 3 mines in the Goeur d'Alene mining district, Shoshone County, Idaho, and is the second of a series to determine the feasibility of a more permanent type of mine support. Closure measurements, where applicable, were made periodically of the concrete-set installations and were compared to the initial cross section of the sets. A different method of blocking was used at each test site; at one test site the type of blocking was changed several times during the test. Results from each test site are reported separately. No attempt was made to compare the cost of the concrete installations with the cost of other types of support used in the district. Such an evaluation of permanent types of support would require a longer period of time. At this time, tests are not complete enough to determine the applicability of underground concrete supports. However, results to date tend to confirm the general opinion that precast concrete mine supports could be used to advantage in openings that require support and must have long life, especially where decay of timber is an important factor.

Jan 1, 1963

By W. T. Abel

Laboratory tests were conducted with a closed, recycling system to evaluate the effectiveness of solid-in-gas suspensions as heat transport mediums. Micronized graphite in helium or nitrogen was circulated by a centrifugal compressor to determine the feasibility of the method and heat transfer capabilities of the mediums. Suspensions were circulated without plugging or eroding the compressor or piping. At low flowrates and light (0.1 to 0.2 volume-percent) graphite loadings, slightly less power was required to transport a given amount of heat with suspensions than with helium alone. Graphite deposition on the heat exchange surfaces of the cooler decreased the heat transfer effectiveness at higher solids concentration. Efforts to eliminate deposition are described.

Jan 1, 1963

By Charles Prasky

This report describes fluidized bed techniques employed by the Bureau of Mines at Minneapolis to differentially sulfatize the manganese in two samples of low-grade manganiferous ferruginous carbonate slates from the Cuyuna Range district, Minn. Suitable mechanics of operation were established. A space rate of 1.25 to 1.5 fps, a retention time of 3 to 3.5 hours, a temperature of 700° C, and a 10 percent sulfur dioxide gas in air were adequate for sulfatizing the slates by fluidization. Under these conditions the overflow product removal rate from the 4-inch-diameter reactor was 4 to 5 pounds per hour. The sulfur dioxide was used more efficiently in the two-stage treatment than in the single-stage treatment. However, approximately 80 percent of the manganese was converted to sulfate by either treatment.

Jan 1, 1963

By R. E. Mussier

This investigation was made to study new methods to prepare high-purity yttrium metal, Various methods were used to prepare pure intermediate compounds, primarily chlorides, bromides, and iodides, which were subsequently reduced to metal. The process found most suitable for the preparation of pure anhydrous yttrium chloride involved thermal dehydration of a mixture of hydrated yttrium chloride and ammonium chloride while under vacuum. Yttrium bromide and iodide were prepared most effectively by the direct halogenation of yttrim carbide. Yttrim carbide was obtained by reacting and melting yttrium oxide-carbon mixtures in a carbon-arc furnace. Yttrium halides were purified by vacuum distillation and reduced by alkali or alkaline-earth metals. Lithium and sodium proved to be the best reductants from the standpoint of yield (>95 pct) and purity (>99.8 pct) of the yttrium. The product of the reduction step was sponge metal, which was consolidated readily by conventional cold-mold, arc-melting procedure. The purest yttrium obtained in laboratory scale work was prepared by sodium reduction of yttrium chloride and contained only 125 pp oxygen; other impurities did not exceed 1,000 ppm. In larger scale tests yttrium containing only 800 to 1,000 ppm total impurities was obtained by lithium reduction of yttrium chloride. The tensile properties of high-purity yttrium were determined. Mechanical tests showed that yttrium can be forged, extruded, rolled, spot welded, and deep drawn.

Jan 1, 1963

By M. E. Tyrrell

Mixtures of zirconium diboride and iron, cobalt, and nickel were resistance sintered to high-density compacts using modified electric welding equipment. To evaluate the use of iron, cobalt, or nickel as binders for zirconium diboride, the sintered compacts were examined in polished section and tested for crushing strength, hardness, microhardness, oxidation rate, and resistance to mechanical shock. Each of the zirconium diboride-metal mixtures produced brittle cermets, but the hardness was generally satisfactory. The iron- and cobalt-bonded cermets exhibited rather poor oxidation resistance. Cobalt provided the least brittle bond, and nickel, the hardest and most resistant to oxidation. Iron tended to form chalky compacts with low resistance to mechanical shock.

Jan 1, 1963

By C. O. Hawk

As an exploratory effort to produce useful products from coal by a new path, the Bureau has made a few experiments on the fast heating of finely ground coal particles by irradiation with a flash of high intensity light. The flash was produced by an electrical discharge at high voltage through a xenon-filled tube. The flashes lasted from 2 to 3 milliseconds. The reaction took place in small sample tubes, ½ inch-dimeter by 4 inches long, and with small amounts of coal (total amount charged 0.1 gram, probable effective amount not more than 20 milligrams). Average particle size of the coal, estimated on a numerical basis, was 20 microns. Temperatures reached were evidently quite high, because all products obtained in quantity were characteristic of high temperature pyrolysis. Apparently, conversion of the coal was extensive where isolated particles received the full benefit of a flash. It seems particularly significant that acetylene was present in appreciable amounts--comprising almost 3 percent of the total gaseous product in one case. This is good evidence of a short heating period to very high temperature (well above 1,000° C) followed by rapid quenching. Although the results are interesting, they do not suggest any immediate practical application.

Jan 1, 1963

By Thomas L. McVay

Laboratory batch and pilot plant flotation tests were made to determine the feasibility of recovering commercial grade kyanite from a quartzite- kyanite rock from the Graves Mountain, Ga., deposit. Best results in laboratory and continuous tests were obtained using sodium carbonate for pH control, citric acid for quartz depression, and oleic acid as the kyanite collector. Over 80 percent of the kyanite was recovered in a concentrate analyzing 56.8 percent Al203 and 3.8 percent hydrochloric acid soluble Fe203. Subsequent treatment of the flotation concentrate by magnetic separation reduced the acid soluble Fe2O3 to 0.6 percent and increased the alumina content to 59.2 percent. Acid leaching of the concentrate gave a product analyzing 59.7 percent Al203 and about 0.1 percent Fe203. As a result of the beneficiation research, a commercial kyanite flotation plant was completed in September 1962 by private industry.

Jan 1, 1963