By D. Paul Bishop, Kevin P. Plucknett, Hung-wei Liu

"Spark plasma sintering (SPS) process has been evaluated for producing the commercially pure (CP) Ti, TiAl and a TiAl-B4C composite. Comparisons were made between the materials in terms of the sintered density, resultant hardness and microstructures. In the present work, the titanium aluminide powders (Ti-48Al, producing a mixture of y-TiAl/a2-Ti3Al) were synthesised „in-house? using a simple reaction-sintering and mechanical attrition approach. This allowed various size distributions to be generated. The powders were then blended with a fine boron carbide (B4C) powder (up to 6 wt.%), and the resulting mixtures were consolidated using spark plasma sintering (SPS) under vacuum in graphite dies. An applied stress of 50 MPa was used for all SPS runs. The SPS parameters were varied in terms of the ultimate sintering temperature (up to 1300°C) and hold time (up to 10 minutes) for each material. It is demonstrated that high densities can be achieved this approach (exceeding 95% of theoretical, with optimised samples close to full density). Microstructural characterisation was conducted using optical microscopy, scanning electron microscopy, and X-ray diffraction. The B4C additions were seen to partially react with the TiAl to form reinforcements, such as TiCx and TiBx. Preliminary mechanical property assessment will also be briefly discussed.INTRODUCTION Titanium- and titanium aluminide-based alloys possess many unique properties, such as excellent corrosion resistance and high temperature strength, respectively (Cardarelli, 2001; Leyens & Peters, 2003). Compared to many other competing materials (e.g. stainless steel or Ni-based alloys), Ti- and TiAl-based alloys also have relatively low densities (~4.5 and ~3.9-4.1 g/cm3, respectively), which is critical for performance in aviation and automobile applications. However, the manufacturing cost is high, due to the expensive raw Ti material and difficulties in machining. TiAl-based alloys are particularly difficult to produce because of their limited ductility (Lütjering & Williams, 2007). To overcome those problems, powder metallurgy (PM) technologies have shown great potential as near-net shape processes for Ti- and TiAl-based alloys. The general PM process largely avoids laborious post-machining and minimises material use. In industrial production, the PM approach has been successfully utilised to manufacture aluminium- and iron-based alloys (Huo & Heath, 2008)."

Jan 1, 2017

By J. L. Bowlby

The heats of combustion of fuels are determined in the laboratory by means of a calorimeter, usually of the oxygen bomb type. A known weight of the fuel is burned in an atmosphere of oxygen under approximately 400 pounds pressure in a heavy metal container-the bomb- and the heat evolved is imparted to a definite quantity of water. From the rise in temperature, measured by means of a Beckmann thermometer, and other data incidental to the determination, the heat value of the sample can be calculated. On paper, the method appears simple indeed, but in practice the determination of the heat of combustion is one of the most difficult of the various coal analyses. This h as led to considerable investigational work in order to obtain formula: whereby calorific values of solid fuels could be calculated from proximate analysis data al one. The proximate analysis of a fuel consists of the determination of moisture, ash, and volatile matter, with fixed carbon by difference. Sulphur determinations properly belong to the ultimate analysis, but in this section of the country, where the sulphur content of the coal is comparatively high, a request for the proximate analysis of a fuel implies the determination of the sulphur as well.

Jan 1, 1929

By Teruo Bitoh, Shogo Izumi

"The effect of B203 flux melting on the structure and the soft magnetic properties of the (Feo.1sBo.20Sio.os)96Nb4 bulk metallic glasses prepared by casting has been investigated. The ringshaped bulk specimens were prepared by the B203 flux melting and copper mold casting. It was confirmed that the flux melting promotes the precipitation of the a-Fe(-Si) and Fe2B phases in the central region of the specimens. The ring-shaped bulk specimens show a flat hysteresis curve, indicating a good linear relationship between the magnetic induction and the applied magnetic field. These results show that it is possible to develop a new soft magnetic material that exhibits constant permeability, which is necessary for producing inductors and choke coils.IntroductionSince the success of forming Fe-based bulk metallic glasses (BMGs) with good soft magnetic properties, great attention has been developed to synthesis and properties of the BMGs [l, 2]. The BMGs have high glass-forming ability (GFA) and, therefore, they can be used to prepare bulk amorphous alloys with a thickness of the order of a few millimeters by casting. The soft magnetic properties of Fe-based BMGs are better than those of ordinary amorphous alloys; therefore, these BMGs have wider applications as soft magnetic materials [3-5]. It is often required for soft magnetic materials that the shape of the hysteresis curve is changed according to the demands of applications. For example, materials with ""flat hysteresis curves,"" which means the magnetic flux density (B) and the applied magnetic field (H) show a linear relationship up to rather high magnetic field, are necessary for producing inductors and choke coils. Flat hysteresis curves can be easily achieved by creating an air gap in the magnetic path. However, magnetic flux leakage generated in the air gap inhibits high-density packing of the electronic components. In order to achieve flat hysteresis curves without creating an air gap, Fe-based ordinary amorphous alloys are subjected to crystallization by annealing and transformed into thin surface layers of a-Fe; the crystallization results in the compression of the remained amorphous phase [6]. Another way to achieve flat hysteresis curves is the formation of secondary phase (such as Fe2B) that act as pinning site of magnetic domain wall displacements [7]."

Jan 1, 2013

By T. A. Farr, I. A. Gibbs, F. Guevara, S. R. Simms, G. Nojima

This paper describes an installation of a medium-voltage adjustable frequency motor drive (AFD) on a high starting torque regrinding mill. This type of application is typically found in the mineral industry dealing with hard ore. The AFD electrical architecture is introduced from line to load. The type of closed loop encoder feedback motor control algorithm is briefly described. The results of the AFD motor identification auto-tuning are compared against the manufacturer’s supplied data. The motor drive performance results are shown for pre-ramp DC fluxing, high starting torque with overload current, excessive load torque stall condition, and blocked rotor. The instrumentation and arrangement for the two watt-meter method to capture low frequency data are presented. The data shown is from the input power quality meter, the AFD computer tool, the output motor protection relay, an oscilloscope, and load shaft connected strain gauge (rotating telemetry for torque assessment). These types of high starting torque constant torque loads are found in mining and process industry applications employing AC adjustable frequency drives. Using field results should help demystify the use of voltage matching output transformers in AFD applications including constant torque loads

Mar 2, 2022

By V. Jares

DESPITE the fact that a combination of metals-aluminum-zinc-tin, and sometimes aluminum-zinc-cadmium-is extensively used for aluminum solders, as well as for die-castings, the constitution of these alloys has not yet been made clear. I. BINARY SYSTEMS The system aluminum-zinc is the basis of the ternary alloys under consideration. Their composition was made sufficiently clear by the investigations of Rosenhain and Archbutt,1 Bauer and Vogel,2 Sander and Meissner,3 Hanson and Gayler4 and Isihara.5 Only the temperature of decomposition of the crystals 0 seems still to be doubtful, whether it is considered as a compound of Al2Zn3 (according to Bauer and Vogel) or as an intermediate phase of variant composition (according to Hanson and Gayler). This temperature is given by most of the authors as in the neighborhood of 256° C., only Isihara giving 280° C. As its accurate determination is of special importance in the study of the ternary alloys under consideration it was experimentally controlled in the following manner: An alloy corresponding in composition to the formula Al2Zn3 was made, in which the temperature effect was found to be the greatest. This was drilled and a silver-constantan thermoelement inserted into the cavity so as to be in direct contact with the alloy. The whole was then very slowly heated and the heating and cooling curves determined. The transition temperature from the heating curve was found to be 281° C., whereas from the cooling curve it was 252° C.

Jan 1, 1927

By Robert Mehl

THE purpose of this investigation was to prepare high-purity iron-carbon alloys, to determine as precisely as possible the A3(GOS), the Acm(SE), and the A1(PSK) transformation temperatures in the meta-stable iron-iron carbide system (up to 1.4 per cent C), and to study the influence of carefully controlled and constant rates of heating and cooling (1/8 to 2° C. per minute) upon the transformation temperature and upon the resulting microstructure. Apart from the general metallurgical importance attending the completion of such a task, it will be noted that highly precise transformation temperatures are of interest and importance in the thermodynamic study of this system1. Several determinations of the iron-iron carbide diagram have been made. These suffer generally from the low purity of the alloys used, and from the application of methods of investigation of low sensitivity. Attempts to compare and weight the many data available in an effort to construct as accurate a diagram as possible have, in the main, been unsuccessful. In general, the wide differences in the results of different workers, the lack of complete analytical data, the omission of important details relating to the heat-treatment of the alloys, and the meager description of the methods of investigation applied, render such a process of averaging nearly meaningless. It may be seen from the summaries by Epstein2 and Körber and Oelsen1 that variations as great as 30° C. exist in the reported data on the A3 temperatures in iron-carbon alloys. For-tunately, the A3 temperature in pure iron is now known to be 910° C. ± 1° C.3 The best recent work on iron-carbon alloys is that of Esser4 on hypoeutectoid steels and that of Sato' on both hypoeutectoid and hyper-eutectoid steels.

Jan 1, 1937

By S. Feinstein, I. Reznik, Y. H. Hatzor, O. Shitrit, Y. O. Rosenberg, H. J. Vinegar, S. Nguyen

"We report the effects of porosity and total organic carbon (TOC) content on the mechanical behavior of organic-rich chalks, based on laboratory measurements. The organic-rich chalks are from the Senonian Ghareb and Mishash formations. This deposit is an immature oil-prone source rock, about 300 meters thick, situated at shallow depths (several hundreds of meters) in the Shefela basin in central Israel. The study is based on core data collected from the Zoharim borehole.Three main phases comprise the bulk volume of this rock: 1) carbonate mineralogical phase (predominantly calcite); 2) pores (mostly saturated with brine); and 3) solid organic phase (type IIS kerogen). The mechanical effects of porosity (23-45%) and TOC (4-19%) are evaluated based on bulk incompressibilities vs. volumetric fractions analysis. Volumetric fractions of mineralogical and organic phases were obtained by porosity, density and TOC measurements. Saturated rock bulk moduli were measured through ultrasonic velocity measurements. Saturated rock bulk moduli correlate best with the sum of kerogen and pore volume fractions, rather than each of them separately. The volumetric fractions were also used to define the range of bulk modulus of the organic-rich chalk, using the Hashin-Shtrikman upper and lower bounds. Based on Marion's Bounding Average Method (BAM), the normalized stiffness factor of the chalk averaged at w=0.197, indicating a soft pore geometry. Using the average normalized stiffness factor, the BAM predictions showed excellent match with the saturated rock bulk modulus and the sum of kerogen and pore volume fractions. Based on our findings, it is inferred that kerogen grains do not support the solid skeleton but are distributed between the minerals grains. We also propose here a straightforward approach for calculating the Hashin-Shtrikman bounds, based on TOC and porosity measurements. The mechanical effects of porosity and TOC indicated here are very important for the understanding of the influence of immature kerogen presence in highly porous chalks, as the Ghareb and Mishash formations."

Jan 1, 2015

By Frank S. Gardner, Morris Cohen, Dara P. Anita

There is a conspicuous lack of information in the literature on the precise role played by residual quantities of austenite in heat-treated steels. While retained austenite may be expected to have significant effects on such important properties as the impact resistance of tools and carburized parts and the dimensional stability of dies and gauges, attempts to study these problems systematically have suffered from the absence of a reliable technique for ascertaining absolute amounts of austenite. With such a technique, not only could the relation between residual austenite and service behavior be investigated, but the chemical and heat-treatment factors that control the quantity of the austenite could also be established. Thus, the retained austenite content could then be regulated in accordance with the results desired. The presence of retained austenite may be inferred by observing the changes in properties (hardness, specific volume, electrical resistance, etc.) due to its decomposition on subatmospheric cooling1 or on tempering,2 but these indirect measurements are not readily translated into percentages of austenite. Quantitative determinations have been achieved in special cases by means of dilatometric3 and magnetic4,5 measurements; but the former procedure requires that observations be conducted during the hardening and involves difficult calibrations that limit its applicability, while the magnetic procedure is very sensitive to extraneous influences and depends upon assumptions that can only be considered as approximate in an absolute sense. Furthermore, both the dilatometric and magnetic effects are volume properties, and cannot be conveniently utilized to explore variations in retained austenite from point to point in a suecimen. Some microstructures lend themselves to accurate evaluation of retained austenite contents by metallo-graphic methods,3 but such instances are not too common, and at best, the procedure is tedious. The characteristic X-ray diffraction lines of austenite permit positive identification of its presence; and in the present paper the intensities of these lines, or the corresponding densities* on photographic film, are employed to measure the amount of the retained austenite. In order to cancel the effect of uncontrollable variations in the X - ray exposure and film - development conditions, a standard reference line is Superimposed on each film by maintaining a foil of aluminum in the path of the incident X-ray beam during the entire exposure. With different samples of steel and the same foil, the ratio of the density of some one austenite line to the density of

Jan 1, 1943

By Morris Cohen, Dara P. Anita, Frank S. Gardner

There is a conspicuous lack of information in the literature on the precise role played by residual quantities of austenite in heat-treated steels. While retained austenite may be expected to have significant effects on such important properties as the impact resistance of tools and carburized parts and the dimensional stability of dies and gauges, attempts to study these problems systematically have suffered from the absence of a reliable technique for ascertaining absolute amounts of austenite. With such a technique, not only could the relation between residual austenite and service behavior be investigated, but the chemical and heat-treatment factors that control the quantity of the austenite could also be established. Thus, the retained austenite content could then be regulated in accordance with the results desired. The presence of retained austenite may be inferred by observing the changes in properties (hardness, specific volume, electrical resistance, etc.) due to its decomposition on subatmospheric cooling1 or on tempering,2 but these indirect measurements are not readily translated into percentages of austenite. Quantitative determinations have been achieved in special cases by means of dilatometric3 and magnetic4,5 measurements; but the former procedure requires that observations be conducted during the hardening and involves difficult calibrations that limit its applicability, while the magnetic procedure is very sensitive to extraneous influences and depends upon assumptions that can only be considered as approximate in an absolute sense. Furthermore, both the dilatometric and magnetic effects are volume properties, and cannot be conveniently utilized to explore variations in retained austenite from point to point in a suecimen. Some microstructures lend themselves to accurate evaluation of retained austenite contents by metallo-graphic methods,3 but such instances are not too common, and at best, the procedure is tedious. The characteristic X-ray diffraction lines of austenite permit positive identification of its presence; and in the present paper the intensities of these lines, or the corresponding densities* on photographic film, are employed to measure the amount of the retained austenite. In order to cancel the effect of uncontrollable variations in the X - ray exposure and film - development conditions, a standard reference line is Superimposed on each film by maintaining a foil of aluminum in the path of the incident X-ray beam during the entire exposure. With different samples of steel and the same foil, the ratio of the density of some one austenite line to the density of

Jan 1, 1943

By D. E. Calisaya, É. Poulin, A. Desbiens, R. del Villar, A. Riquelme

"A 15 cm diameter by 732 cm height, fully automated pilot column was installed in the Agnico-Eagle’s Laronde concentrator (Québec), for evaluating the performance of newly developed sensors and advanced process control algorithms. For eventual comparison purposes, the pilot column is continuously fed with the same slurry feeding the copper-circuit third cleaner column. It is equipped with electrical conductivity-based sensors for estimating the three variables used in the multi-variable control algorithm under evaluation: froth depth, fraction of wash water underneath the interface and gas hold-up. Froth depth is regulated using a PI controller while a predictive controller is formulated as the minimization of the tracking errors of gas hold-up and bias rate, keeping several operating constraints between their practical upper and lower limits. In particular, an unreachable high set point of gas hold-up can be selected in order to maximize the bubble surface area available for particle collection, while maintaining bias rate above a minimum value required for froth cleaning. The proposed strategy may indirectly help optimizing flotation column operation by using these secondary variables, without the implementation of a real-time optimization layer.INTRODUCTION Flotation columns have already been used for more than 30 years, mainly in cleaning stages, as a result of their froth washing capabilities. Despite their widespread usage, the measurement of some pertaining variables and their use for automatic control is rather scarce. Among the most important variables directly related to the process metallurgy (concentrate grade and recovery), froth depth (hf) is the only one normally monitored and controlled. Even though commercial sensors are available, gas hold-up (eg), a variable directly related to concentrate recovery, is seldom measured and never controlled. Another important variable, bias rate (Jb) responsible for concentrate cleaning, is simply not measured at all, as there is no commercial sensor available. Therefore, besides froth depth, continuous monitoring of process variables is limited to flow rates (gas, feed, tailings, wash water), i.e. to manipulated variables. Some new available sensors have been industrially tested, e.g. the Sonar-TracTM for eg (O'Keefe, Viega & Fernald, 2007) and the McGill hold-up sensor (Tavera & Escudero, 2002). Others, for bias rate and frother concentration, have been successfully validated at laboratory scale by Laval’s LOOP researchers (Maldonado, Desbiens, del Villar & Chirinos, 2008b; Maldonado, Desbiens, del Villar & Aguilera, 2010a). Some devices have been extensively used for monitoring bubble size and space distri-bution, e.g. McGill bubble viewer (Gomez & Finch, 2007) and others."

Jan 1, 2012

By A. Khan

The purpose of this paper is to demonstrate the value of identifying and optimizing throughput constraints by utilizing a Constraint Model. This will be achieved by first understanding the overall concept of Operational Excellence, Continuous Improvement and Theory of Constraints as practiced within Vale Canada Limited. Next, the value of utilizing a Constraint Model is demonstrated by primarily identifying constraints. The applications in utilizing Constraint Models will be demonstrated, including the primary benefit of identifying constraints. The remainder of the paper will focus on how to properly setup a Constraint Model using discrete simulation (regardless of simulation software). Benefits of understanding the severity of constraints and movement of the bottleneck will be recognized. The paper will conclude with the summary of real applications within Vale Canada Limited.

Aug 1, 2013

By K. V. Raj, T. Bhowmick

"Computational fluid dynamics (CFD) modeling of an open-pit mine has several challenges. A good quality mesh of the model domain is a pre-requisite for convergence in solution. Good quality tetrahedral meshing and insertion of prism layers in faceted open-pit mine geometry is complicated due to presence of numerous vertices and ridges. Presence of vertices and ridges result in poor quality tetra elements and holes in prism layers, which cause instability in the model. Good quality pit bottom prism mesh elements significantly improve the formation of velocity boundary layer and thermal boundary layer at the pit bottom. This results in an expected temperature dependent micrometeorological buoyancy flow in the pit. Whereas, model geometry without a prism layer, results in abrupt temperature gradient near pit bottom. Buoyancy flow and recirculation have significant effect in lifting mechanism of fugitive dust particles generated near pit bottom. Representative initial and boundary conditions and selection of appropriate turbulence model have significant influences on the simulation results. In this paper, three-dimensional models of open-pit mines are developed using commercial CFD software (CRADLE-CFD). Important constraints and various consequences in modeling complex open-pit geometries are presented. INTRODUCTION Application of Computational fluid dynamics (CFD) to model an open-pit mine to predict fugitive dust and pollutant concentrations in and around a mine is relatively new. In former Soviet republic (USSR), Baklanov [1] and Belousov [2, 3] presented numerical models of pollutant transport in open-pit mines in Arctic regions. In recent years, advances in mathematical and computational fields have enabled better modeling of pollutant dispersion phenomenon around mines using computational fluid dynamics (CFD). Several CFD software packages have been used by various researchers to model the pollutant transport in open-pit mines. Works by Alvarez et al. [4]; Lowndes et al. [5]; Silvester et al. [6]; Torno et al. [7]; Choudhury and Bandopadhyay [8]; Collingwood et al. [9]; Raj et al. [10] and Flores et al. [11]; are examples of application of various commercial and open source CFD packages (COMSOL, ANSYS, OpenFOAM) to model pollutant transport in open-pit mines. These researches provided a strong background for additional research involving CFD modeling of open-pit mines. Due to the limitations of computational times and capacity, 3D modeling and various aspects of fugitive dust dispersion in open-pit mines remained unexplored."

Jan 1, 2015

By Thomas C. Anderson

Tiedback walls are now recognized and accepted as a good solution for a variety of structural problems: ? Retaining Walls and Bridge Abutments in cut situations ? Landslide stabilization ? Repair/support of existing walls Acceptable techniques have been developed for anchoring in cohesive and granular soils and in any kind of rock. Methods have been developed for adequately protecting tieback tendons against corrosion and for testing every tieback to verify its long-term load-carrying capacity. However, the major problem that the industry faces today is how do we get constructable and economical tiedback walls contracted for and built with minimal claims. This paper will explore the issue of "constructability" through a look at specific problems from actual projects. From a research report from the Construction Industry Institute, Austin, Texas (1986), constructability is defined "as the optimum use of construction knowledge and experience in planning, design, procurement and field/operations to achieve overall project objectives." Maximum benefits occur when people with construction knowledge and experience become involved at the very beginning of the project." The design and installation of tiebacks has been developed primarily by specialty contractors; each contractor has evolved its own methods of performing the work, and consequently, many of the techniques are patented and proprietary. The real question is, how do we make effective use of this knowledge and experience during the design phase of the project?

Jan 1, 1991

By Christopher Laughton

A new underground laboratory is under construction at the recently closed Homestake Gold Mine, Lead South Dakota, United States of America. The Deep Underground Science and Engineering Laboratory is designed to meet the needs of an international group of scientists and engineers interested in conducting fundamental and applied research at depth in the Earth’s crust.

Jan 1, 2011

By T. A. Rickard

The writing that is effective is woven with a fine texture into an agreeable pattern; it is free from knots, loose threads, and stray fluff. The instrument that weaves this literary fabric, whether it produce a homely sock or a lordly tapestry, a simple story or a learned 'Itreatise, is a disciplined intelligence, as sure as a steel needle, as precise as a swift loom. The simile breaks down at this point, for the product of the pen is instinct with the human spirit and therefore transcends in beauty anything made by a mere machine. If words are to be woven into eloquent meaning, they must be well knit. Upon the relation of words to each other and of groups of words to other groups, known as phrases, clauses, and sentences, depends the success of writing as a means of trans¬mitting thought from man' to man. To be understood beyond question, you should know not only what your words denote but how to build your sentences; you must not only choose your words aright but construct your sentences properly. A sentence is a combination of words that makes complete sense; it says something about something. ' A clause is a subordinate sentence or a sentence within a sentence. A phrase is a group of words without a predicate; it makes sense, but not complete sense. For example: I shall wait for a few minutes before I go home: The whole statement is a sentence; "I shall wait" and "before I go home" are clauses; "for a few minutes" is an adverbial phrase. The orderly arranging of words and of combinations of words is called `syntax'; and from the original Greek form, ouvaeis (suntaxis), is derived the Greek name for an editor,

Jan 1, 1931

By S. J. Stokowski

Abstract An extensive drilling and laboratory testing program indicates that a construction aggregate resource is present within the Oligocene Sombrerito Formation limestone, southwestern Dominican Republic. The first part of the testing program included the collection, photographing and geologic logging of diamond drill cores to allow lithologic subdivision of the strata into potential quarry layers. The primary lithostratigraphic units are: I- (youngest) approximately 10 m of white, dense marine limestone II-approximately 5 m of white, interbedded dense and chalky marine limestone III-more than 2 m of tan, chalky, calcitic dolomite. Unit I is often altered by lateritic weathering and/or dolomitization. Unit II is often altered by dolomitization. The cores were individually crushed by quarry layer into coarse and fine aggregate sizes for chemical and physical analyses: specific gravity and absorption, MgSO4 soundness, sand equivalent, Atterberg limits of the minus #40 mesh fraction, and LA degradation. The unaltered portion of Unit I is suitable for all construction aggregate uses. Unit II is best suited for crushed stone base. Each of the non-weathered units decreases in coarse-aggregate yield and quality with depth and diagenetic dolomitization. Dolomitization typically causes about 5% lower yield of coarse aggregate, a sand equivalent of about 20 units below the original value an increase in absorption of about 3%, an increase in the LA of up to 13%, and a decrease in the average five-cycle MgSO4 soundness of about 17%.

Jan 1, 1991

By Seedsman R. W

Good roads are essential in moving men and materials to and from the underground workplace. Coffey Partners International Pty Ltd (Coffey) has recently completed a underground coal industry funded project on underground mine road construction and maintenance. This paper discusses practical approaches to construction and maintenance of underground mine roads using transferrable civil technologies and innovative techniques. Mine pavements are generally low-cost (relative to civil roads), constructed to varying standards using locally available materials to best meet the mobility needs of the mine. Performance of pavements is thus largely dependent on the environmental conditions, quality of the available road making materials, maintenance policies and available resources. The paper will detail `what causes bad roads?' in various underground environments, available management strategies, construction and water control techniques, road maintenance and vehicle considerations.

Jan 1, 1995

By G. C. Hodgson

Specification and Tests of Rope Wire Chemical Analysis: The range in composition of steel used in the manufacture of wire rope is as follows: Carbon 0 4 to 0.9 per cent Manganese 0 4 to 0.8 Sulphur Not above 0.04 Phosphorus Not above 0.04 The carbon and manganese content are varied according to the gauge of wire to be drawn and the tensile strength required. Generally speaking, best results are obtained from heats where the melt is not of too large a tonnage. The amount of reduction and patenting of the wire is left to the wire maker, who thus has a free hand in meeting the balance of the specification.

Jan 1, 1931

By A. Bruynesteyn

Many papers 'have been publihed on the role of the bacterium.Thiobacillus ferrooxidans in the oxidation of reduced sulfur compounds, and years of research have established the following environmental factors, which influence biological oxidation. 1. Oxygen is required for the oxidation of reduced sulfur compounds to the sulfate form. Sufficient oxygen. is available from the air, consequently, it is of importance to get the air to the bacteria. 2. The bacteria are active in the pH range 1.4 3.5. Maximum activity occurs at pH 2..0 - 2.8. 3. -In order to allow the bacterial populations to expand, certain essential nutrients must be available. Nitrogen has to be supplied for the production of body protein, and ammonia is the source most readily accepted by the bacteria. Carbon dioxide is the only utilizable source of carbon and the small amounts available in air are the primary source of this element. Small amounts of phosphate, manganese,, potassium,. calcium. and magnesium are also required. These trace minerals are available from the water and host rock in sufficient quantities. 4. Water is required as a carrier for the oxygen carbon dioxide and other nutrients, as-well as a solvent for the metallic sulfates produced. The bacteria are motile and the water allows the bacterial populations to spread:: bacterial activity ceases if the equilibrium relative humidity drops below 100%. 5.-optimum bacterial activity occurs at temperatures of 34 - 35°.C (93 -.95° F). All activity ceases above 45° C. At lower temperatures, activity its dramatically decreased, but there is still a significant amount at 10 - 11° C.- Thiobacillus ferruoxidans has been isolated from a mine with a year round temperature of 3° C. 6. Unpublished results from our laboratory show that biological leach ore oxidation takes place during the rest periods at the same rate as during the wet leaching periods providing there is a film of moisture remaining around the particles. Optimum conditions can be readily achieved in the laboratory, but application of our laboratory knowledge to commercial leaching dumps is riot as simple. Attempts to achieve improved environmental conditions for the bacteria in leaching dumps would require substantial capital investment and careful planning of leaching operations. This paper

Jan 1, 1972

By Martin D. Larisch

The construction of diaphragm walls and most large-diameter bored piles (piers) is often carried out under drilling support fluids to temporarily stabilise the excavation prior to concrete placement. In most cases such fluids are either mineral-based slurries (bentonite) or polymer support fluids. The working mechanisms of these two fluid types are fundamentally different. Designers need to consider possible fluid-related impacts on the permanent design performance of the project-specific deep foundations as well as for the temporary excavation stage during construction. Robust design methods for bentonite slurry-supported excavations have been developed in the last few decades and the working principles and associated risks of such mineral-based slurries are understood reasonably well. However, such meth-ods have not been developed in detail for polymer-based drilling fluids. This document provides a brief overview of the main characteristics of bentonite- and polymer-based drilling fluids as a guide for construction practitioners and design engineers alike. The paper also high-lights some common construction risks related to casing installation and the selection of suitable fluid systems for different ground conditions. Typical defects caused by the incorrect application of drilling support fluids, and their pro-active mitigation, are discussed, too. In addition, the basic concepts of sta-bility calculations for bentonite fluid-supported deep excavations are briefly introduced and their ap-plicability for other fluid types such as polymer-based support fluids or water are reviewed.

Nov 1, 2022