By G. M. Ault, G. C. Deutsch

The paper reviews the efforts made to utilize powder metallurgy to solve problems encountered when using alloys at high temperatures. The following subjects are discussed: comparison of wrought and sintered super alloys, sintered aluminum powder, porous materials for transpiration cooling, molybdenum, and cermets. TODAY, powder-metallurgy techniques are be-JL coming increasingly important, producing materials which at the present time cannot be made by any other method. Among these materials are high melting-point metals such as tantalum and tungsten, porous metals for filters and lubricant-containing bearings, electrical contacts and electrodes (i.e., tungsten-copper), cutting tools of the cemented carbides, and magnet alloys. In addition, the powder-metallurgy industry has grown because, through the application of its methods, shaped parts, such as gears, can be produced at tremendous rates with a low scrap loss in comparison with manufacture by casting or forging and machining. In the past few years, by utilizing powder metallurgy, several approaches to the problem of high temperature materials have been investigated. In this paper the authors will review some of the studies on application of materials having properties above 1350°F. Since their experience lies in the aeronautical field, possible uses of powder-metallurgy techniques in the production of aircraft en- gines will be emphasized. A large portion of the work is classified, but such a restriction has not eliminated any field from discussion, although limiting the amount of detail it is possible to present. The development of high temperature alloys from powders and porous metals for cooling will be discussed as well as research done on molybdenum and molybdenum alloys, cermets, and intermetallics. Some studies on the utilization of cermets will be considered along with special problems that have been revealed through these investigations. Special interest in certain factors of sintered aluminum powder (SAP) makes it desirable to discuss this material although its use temperature is below the 1350°F limitation set for this paper. High Temperature Alloys from Powders In general, components made from powders for room-temperature application have been investigated with the primary purpose of taking advantage of the high production rates and economies made possible by powder metallurgy. From the standpoint of properties, the ojective of the powder metallurgist has been to obtain a product comparable to the cast or wrought product that is to be replaced. Comparisons of the properties of alloys made by powder-metallurgy methods with those of similar compositions made by casting and forging are reported in the literature.12 In many cases equivalent

Jan 1, 1955

By A. G. Guy

IN the course of a research on steady-state diffusion it became necessary to make diffusion calculations for a finite solid. This problem was found to be sufficiently different from the corresponding problem for the semi-infinite solid for an entirely new approach to be necessary in obtaining a useful solution. The assumption of an exponential variation of the diffusion coefficient with concentration' was no longer a practical necessity, so that the new solution offered the possibility of handling diffusion in semi-infinite solids for arbitrary variations of the diffusion coefficient with concentration. In discussing the principle on which this method of calculation is based, it is convenient to consider the relatively simple problem of one dimensional diffusion into a matrix that initially contains none of the diffusing substance. The solution of the set- ond Fick Law,?C/?t=D0?2C/?x2, for diffusion into a semi-infinite solid is3 C/C=1-F(x/2vD0t [1] where C is the concentration of the diffusing substance at a depth x cm below the surface after dif- A. G. GUY, Member AIME, and M. GOLOMB are Professor of Metollurgicol Engineering and Professor of Mathematics, respectively, Purdue University, Lafayette, Ind., A. S. YUE, formerly with Purdue University, is now with the Research Laboratory, Dow Chemical Co., Midland, Mich. TP 4505E. Manuscript, July 18,1956. fusion has occurred for t seconds; C, is the concentration of the diffusing substance at the surface of the matrix; Do is the diffusion constant, expressed in sq cm per sec; and + represents the Gauss error function. The corresponding solution for diffusion into a finite solid of thickness, 1, is conveniently written for the change in concentration, C+, at a point midway through the matrix and for times, t, great enough for the following equation to be used4 c1/2/C1=(1/2-2/?e-?2D0t/l2) [2] In Eqs. 1 and 2 the diffusion coefficient is represented by the symbol Do (rather than by D) to emphasize that these equations are valid only for constant values of D. To understand how these equations can be modified to take account of actual variations of D, such as that shown in Fig. 1, first consider the fact that for a given time of diffusion theconcentration at a given point is determined, not by the D value alone, but by the ratio x/vD0 in Eq. 1 and by a similar ratio, l2/D0 in Eq. 2. Even though in fact D varies, it is possible to keep this ratio constant by using a special coordinate system, x,, that varies with D in the appropriate manner. The necessary character of this special coordinate system can be easily visualized by imagining that

Jan 1, 1958

By A. E. Bibb, J. R. Fascia

Single-crystal wafers of zirconium have been exposed to 680°F neutral water. The single crystals were of known orientation and weight-gain data as a function of crystal orientation were obtained. These data show that all the crystal faces studied obeyed a cubic rate law out to the time of transition whereupon the crystals corroded at an approximately linear rate. The time to transition varied from 114 days for (1074) crystals to about 325 days for the (2130) faces. The epitaxial relationship be-tween metal and monoclinic oxide was found to be (0001) H (111) and [1120] 11 [101]. A black tight adherent oxide layer was formed on the crystals in the pretransition range. This black oxide was found to be monocrystalline. The white corrosion product produced after transition was found to be polycrys-talline but highly oriented. X-ray line-broadening studies found that the black oxide was a highly strained structure whereas the white oxide was relatively strain-free. These results indicate a strain-induced re crystallization or fragmentation accompanies the change from protective black oxide to nonprotective white oxide. ZIRCONIUM alloys have been used quite extensively in high-temperature aqueous environments. Alloy additions can be made to commercial sponge zirconium which enhance the corrosion resistance of the zirconium in both water and steam media, which raise the tolerance limit for certain impurities detrimental to corrosion resistance, and which reduce the amount of free hydrogen pickup during corrosion. The development of the corrosion-resistant zirconium alloys has been a long and tedious job involving trial and error methods. This technique has been necessary because of a lack of fundamental data and hence understanding of the corrosion mechanisms. The objective of the work described herein was to provide some fundamental data with respect to the aqueous corrosion of zirconium crystals as a function of the orientation of the exposed surfaces. Hg. The zirconium chunk was then cooled to below the transformation temperature (862°C) and reheated to 1200°C for 8 hr. The ultimate size of the zirconium grains increased with the number of cycles. Rapid or even furnace cooling through the transformation temperature produces a considerable amount of substructure which was intolerable in corrosion experiments as it would be in the study of any crystallographically dependent property. It was found that a high-temperature a-phase anneal for approximately 4 days reduced the substructure below the limits detectable by visual or X-ray means. Crystals so produced were carefully cut from the massive zirconium chunk and oriented by standard back-reflection Laue techniques. The crystals were then mounted in a goniometer head and, by using the three degrees of freedom available, slices on the order of 0.015 to 0.020 in. were cut parallel to any desired crystal plane. These slices were then carefully polished on both sides to produce smooth flat faces, pickled to remove about 0.002 in. per face, annealed for 1/2 hr at '750°C in a vacuum of approximately 10"5 mm Hg, flash pickled, and checked for orientation. The pickling solution was 45-45-10 vol pct HN0,-H20-HF and continuous agitation was provided to eliminate pitting of the slices. Any slice that was not within 2 deg of the desired orientation was discarded, and any evidence of substructure as indicated by the Laue spots was also grounds for discarding the sample. Thin slices were used for the corrosion tests because weight gain per area data could be obtained with only a minimum area exposed to the corrosive media that was not of the desired orientation. The thin single-crystal slices were of irregular shape and as a result the areas were determined by placing a crystal inside an inscribed square of known area, enlarging a picture of this assembly about X5, and tracing both the enlarged square and crystal with a planimeter. The zirconium used to produce these single crystals was crystal-bar grade, a typical analysis of which is given in Table I. An oxygen analysis on prepared crystals gave a concentration of 205 ppm. The hydrogen concentrations are believed to be less than 15 ppm due to the dynamic vacuum anneal given each crystal. Typical nitrogen values for zirconium treated in this manner are about 10 to 20 ppm. RESULTS AND DISCUSSION Single-crystal wafers have been exposed to de-oxygenated, deionized water in static autoclaves.

Jan 1, 1964

By J. G. Faller, L. P. Skolnick

The distribution of cobalt and vanadium over non-equivalent crystallographic sites in C14-type Zr(VCo), alloys has been investigated. An anomalous X-ray scattering technique developed by Skolnick, Kondo. and lavine7 by which the separation in the scattering factors of two similar atoms can be enhanced was employed. Six alloys spanning the pseudobinary section ZrV1.6Co0.4-ZrVO.6CO1.4 at 10pct steps showed a nonrandom compositionally dependent distribution. Specifically, at high vanadium content cobalt preferentially occupied sites of type (6h) and vanadium, sites of type (2a; at low vanadium content the reverse was observed. In addition to the distribution fraction the structural parameters x and z were obtained. There was no significant deviation of these parameters from those obtained in the ideal C14 structure. Certain suggestions are made to account for the observed nonrandomness in the distribution of atoms on the two types of sites. INTERMETALLIC compounds of formula AB2 iso-morphous with MgCu2, MgZn2, and MgNi2 are known as Laves phases. Because Laves phases exhibit high symmetry and coordination numbers, the highest possible for an AB2-type compound,1 they are among the most frequently observed compounds in nature. In recent years interest has centered about the purely transition metal Laves phases2-' in efforts to understand the function of atomic size and electronic structure in the formation of these compounds. It has been observed that pseudobinary Laves phase systems often show a variation of structure across the phase diagram. Such a system is the ZrV2-ZrCo2 in which the structure varies from cubic MgCu2 to hexagonal MgZn2 to cubic MgCu2.4 Some understanding about the conditions under which the second modification is stable can perhaps be gained by studying the distribution of cobalt and vanadium atoms on lattice sites in the MgZn2 modification of the system ZrV2-ZrCo2. In both the MgZn2 and MgNi2-types there exist nonequivalent positions open to occupancy by the B element, whereas in the MgCu2 prototype all sites are equivalent. Skolnick, Kondo, and La-vine7 have developed an anomalous scattering technique suitable for this type of investigation. Whereas the influence of size on the formation of a Laves phase is well recognized, no substantial evidence has been put forth in support of the size ratio dependence of a particular prototype. Berry and Raynor8 suggested that RA /RB ratio does indeed affect the type of structure that is chosen, MgZn2 compounds tending to cluster about 1.225 while MgCu2 compounds were found at larger deviations from this ratio. Dwight,3 however, from a study of 164 Laves phases does not believe this generalization to be justified. Electronic effects are certain to play a part in the stability of Laves phases in general and in the choice of a structure type in particular. For example, size along would favor the formation of Laves compounds of Ti, Zr, Hf, Ta, or Nb as the A element with nickel or copper as the B element. The absence of such is attributed to an unfavorable electron : atom ratio by Elliott and rostoker.4 Early experiments of Laves and witte9 with pseudobinary and pseudoternary systems of the three prototypes established the dependence of crystal structure upon electron: atom ratios. They observed that the MgCu2 structure dissolved elements of higher valency until the electron: atom ratio of =1.8 was reached; the MgZn2 likewise dissolved elements of lower valency replacing zinc. witte,6 from calculations of the electron : atom volumes of Brillouin Zones, obtained limits of stability for the prototypes MgCu2 and MgZn2. Elliott and Rostoker4 used these limits with considerable success in the all-transition element Laves phases they investigated. According to witte,6 compounds between the electron :atom ratios of 1.80 and 2.32 were of the MgZn2 type; those above and below exhibited the MgCu2-type structure. On the basis of these limits and an assumed valency of zirconium based upon the near tetra-valence of titanium, Elliott and Rostoker obtained valencies for the first transition series elements. For the Laves phases with which this investigation is concerned, ZrV2 and ZrCo2, the authors calculated electron :atom ratios of 2.54 and 1.56, respectively. These ratios are for the MgCu2-type structure and straddle the stability band of the MgZn2 modification. One could, therefore, predict that a pseudobinary system ZrV2-ZrCo2 should pass through the MgZn2 modification in traversing the composition diagram from one end to the other. Implicit in this assumption is a smooth change of the electron: atom ratio from 2'54 to 1.56. MOSS10 states that his finding the low temperature structure of ZrCr2 to be C15 instead of C14 alters greatly Elliott's valency of zirconium and hence the assumed valencies of the other metals. Such a quantitative correlation of structure with electron : atom

Jan 1, 1963

By M. J. Marcinkowski, R. M. Fisher

The flow stress-grain size relationship has been determined at room temperature in both a disordered and a fully ordered FeCo for plastic strains up to 30 pct. The results are in agreement with a Hall-Petch relation of the type given by Of =a,+kd-1/2 where of is the flour stress and a, increases mono-tonically with increasing strain to a maximum value which is much higher for the ordered than for the disordered alloy. The slope, k, is found to increase FOLLOWING the original work of Halll and petch relating the effect of grain size to the lower yield stress of iron and steel, it has been generally found that the yield stress oy.s. of polycrystalline metals with strain to a maximum and then decrease for both ordered and disordered alloys. However, k for the ordered alloy is in general higher than that for the disordered alloy and the critical strain for k max somewhat larger. All of these observations can be satisfactorily accounted for quantitatively and in some cases semiquantitatively by using a slip band-grain boundary intersection model, and by taking note of the fact that, in general, moss slip, while quite common in the disordered alloy, is extremely difficult in the ordered alloy. obeys a relation of the form oy.s.=a0+kd-1/2 [1] where a, and k are constants and d is the mean grain diameter. For convenience, and in accord with prevailing custom, Eq. [I] will be referred to simply as the Petch relation. Tjerkstra3 and Armstrong, Codd, Douthwaite, and petch4 showed that the flow stress af of iron or steel measured at strains of up to at least 20 pct also obeyed a relationship of the type given by Eq. (11. The latter investigators have also shown that Eq. [I] applies to fcc and hcp metals and alloys.

Jan 1, 1965

By R. G. Treuting, W. C. Ellis

The twinned state is characterized by a lattice of coincidence sites. Imperfections are required at stable lateral twin interfaces. Twinned regions can occur with relative ease in the diamond cubic IN recent contributions1,2 on the origin and growth of cubic annealing twins, attention has been directed to the orientation relations between such twinned components and their parent matrix. There are some aspects of twinning which may be illuminated by a more detailed consideration of the twinned state" alone. As an extreme example, the dense twinning in cast ingots of germanium,&apos; as contrasted with the rarity of twins in cast face-centered cubic metals, is yet to be accounted for. It has been this that has led us to the present work, which, it will be noted, uses methods and constructions in many respects similar to those of Kronberg and Wilson.&apos; In the cubic systems, a 70" 32&apos; rotation about a <110> axis is angularly equivalent, as to twinning, to the more usually considered 180" rotation about a <111> axis. Figs. 1 and 2 show a (110) projection of a twinned face-centered cubic lattice and a twinned diamond cubic lattice. In both figures, the two adjacent planes A and B, shown by the larger and smaller circles, are sufficient to represent the entire array. In each case a section of lattice, the original atom sites of which are shown by open circles, has been rotated as indicated through 70" 32&apos; to bring an original. [112] direction into coincidence with the [112] diiection. The latter is the intercept on the (110) projection of the (ill) plane normal thereto, the twinning plane. In the face-centered cubic case the rotation can be performed about an axis passing through an atom-site; the mirror plane then is also a composition plane containing atoms common to both twinned and untwinned lattices. The diamond cubic lattice may be construed as two interpenetrated face-centered lattices. Its (111) planes recur in a sequence of alternately short and long interspacings. Consequently a mirror plane for twinning cannot be a composition plane, but must be the bisector of one of the spacings. When the longer spacing is selected, the closest distance of approach across the mirror plane in the [ill] direc- tion is identical with that in the untwinned structure. In each case periodically recurring (ill) planes (parallel with the twinning plane) are found, on which there is coincidence of atom sites of the pre-twinned and twinned orientations; these are indicated by the cross-hatched circles. In the face-centered lattice there is such coincidence every third (ill) plane; in the diamond cubic lattice, on two adjacent planes in every six. At the twinning interface in the latter, there is on each side of the mirror plane a (ill) plane of atoms common to both twin components. Conceivably, there is little influence on a plane of atoms about to be adhered to such a pair of coincidence planes, whether it be laid down in a normal or in a twinned position with respect to the previously formed structure. Slawson% as attributed the high incidence of twinning in diamond to this boundary state. Further examination shows that the motion of intermediate planes can consist of various pairs of equal and opposite translations, for example of (ill) planes in the [l&apos;;i2) direction, the familiar twinning shear, indicated in the small schematics in the figures. Since the translations form a system of shears of alternating sign between coincidence planes, twinning could take place by such a mechanism over an extended region without extensive shear; in fact, in this case any atom moves but the distance in the [1i2] direction. One alternative construction for the face-centered cubic lattice leading to the same end result is illustrated in Fig. 3. The plane (711) with respect to the pretwinning orientation (the twinning plane of Fig. 1) is given, the twinned region arbitrarily bounded by <110> and <112> directions. The coupled shear is identical to that of Fig. 1. The "rotational" movement about coincidence sites generating the same twinned position could consist as shown of the translation a,/d% for each atom of a group of three in the B layer in a different one of the three <112> directions, and a similar translation of the underlying three atoms in the C layer in either the same or the opposite sense. This is not dissimilar to Kronberg and Wilson&apos;s construction for their 22" rotation of three adjacent (111) planes.

Jan 1, 1952

By R. G. Treuting, W. C. Ellis

D. Whitwham, M. Mouflard, and P. Lacombe (British Council Research Fellow, Labratoire du Professor Chaudron, Vitry-sur-Seine; Inqenieur de Recherches, Labratoire de Vitry; and Maitre de Recherches, Labratoire de Vitry, Professeur Adjoint de Metallurgie, Ecole des Mines, Paris)—The authors&apos; work is of great interest in bringing out the geometrical relations existing between twinned lattices, and for the notion of a coincidence super lattice developed from this. We should like to point out that a similar idea was put forward by Friedel8 in his book on the subject of lattice merohedrism "merihedrie réticulaire:"—When two crystals A and B are twinned with respect to a mirror plane, there exists a common superlattice, "réseau periode," which is independent of the contact surface between the two crystals. The volume V of this superlattice is a simple multiple of the volume v of the lattice of crystals A, or B, (Fig. 5). This "multiple cell" is defined by the twin plane (p q r) and a row of atoms [h k l] normal to this plane, the base being taken as the smallest unit (two-dimensional) of this plane. Two cases must be considered. First when the multiple cell, as defined, has no atom site at its center nor at the center of its faces other than (p q r), v the twinning index is defined by —. In the second v case, when one of the two above conditions does not v apply, then the twinning index is V 2v A more intuitive definition of the twinning index would be the proportion of atoms of C, which would coincide with those of C1 when the C, lattice is imagined to extend on the other side of the contact surface. In the case of cubic crystals, the twinning index

Jan 1, 1952

By P. S. Rudman

Laves phases, AB2, are considered as Izerrzisub-stitutional solutions m1hich are defined by a one-for-truo replacement scheme. Atomic-size tnisfit is considered in terms of deviations of the ratio 2V°b/V°A from unity, where v° = atomic volume. A simple elastic model has been used to calculated deviations from "Vegard&apos;s law of atomic vol-umes". Comparison has been made between calculated and observed atomic-volume deviations fov 222 Laves phases. Agreement is generally very good although there ave some few exceptions which appear to be excusable in terms of electronic changes that ore beyond the scope of the present model. We can consider the formation of a binary sub-stitutional solution A-B from an A solvent as one-for-one replacements of A atoms by B atoms. As the atomic-size ratio deviates from unity, the solution becomes thermodynamically less stable and hence more restricted because of atomic-misfit strain energy. In accordance with our previously presented conclusion1 that the atomic volume, v, is in general the most appropriate measure of atomic size, the ideal size ratio for a binary sub-stitutional solution is vg/vA = 1. The Laves phases have been described by Berry and Raynor2 in terms of various stacking sequences of hexagonal layers of B atoms for the three structures MgZn2(C14), MgCu2(C15), and MgNi2(C36). To form the Laves phase of ideal composition AB, we start with complete hexagonal layers of B atoms in the appropriate stacking sequence and we remove, according to an appropriate scheme for each structure, two out of every four B atoms and replace the two removed atoms by one A atom. We thus might expect to find that the ideal size ratio for the Laves phases is 2v/B/ VA= 1. From this point of view, then, we call Laves phases hemi-substitutional solutions since we employ one-for-two replacements. By analogy with substitutional solutions we can expect for Laves phases that as the ratio 2VB/Va deviates from unity the phase occurrence will be more restricted. Laves3 has plotted the distribution of Laves phases as a function of the radius ratio, ?A/rB, and found that, while the distribution extended from 1.05 < rA/B < 1.50, the

Jan 1, 1965

By E. F. Bailey, W. J. Harris

THE temperature of the ferrite to austenite re-action is established frequently by continuous heating experiments. However, equilibrium studies of this reaction have demonstrated that austenite may form at temperatures considerably below those at which the reaction is first observed during continuous heating. Because of this discrepancy, tempering is sometimes performed above the true critical temperature and in these cases austenite forms during tempering. The lowest temperature at which austenite forms and the kinetics of the reaction have been studied by Bain,&apos; Bleakney and Gros-venor,2 and Dube and Cunningham. This austenite can affect the properties either as austenite per se, if it is retained at room temperature, or as a decomposition product if it transforms. The effect of austenite formation during tempering on low temperature impact properties of an 8 1/2 pct nickel steel was reported by Brophy and Miller4 in work published after the present investigation was initiated. They concluded that the improvement in low-temperature notch toughness which followed tempering at certain temperatures could be attributed to the austenite formed during tempering. Kramer et al.5 found anomalous hardness increases and embrittlement after tempering of a low-carbon manganese-nickel steel. They concluded that austenite formed during tempering, and that the decomposition products were responsible for the increase in hardness and the embrittlement. Quan-titative correlations of the microconstituents and mechanical properties were not made by these investigators. The present study was undertaken in order to establish the kinetics of formation of austenite at various temperatures, the characteristics of the decomposition of this austenite, and the relationship between mechanical properties and the phases present. Experimental Procedure A low-carbon manganese-nickel steel was selected because of the sluggishness of its austenite decom-position reactions. The composition of this steel in percent was: C, 0.10; Mn, 3.52; Ni, 2.34; Mo, 0.52; Cr, 0.17; Si, 0.19; V, 0.15; P, 0.019; and S, 0.020. Samples were prepared by forging sections from a large ingot to 3/4 in. bars. Formation and decomposition of austenite were investigated by dilatometric techniques which were checked by X-ray measurements. Dilatometer specimens were hollow cylinders 1 in. long, 1/2 in. diam, with a 1/8 in. central hole. All specimens were aus-tenitized for 1 hr at 1650°F and quenched in water prior to insertion in the dilatometer. Oxidation was prevented by using an inert atmosphere of purified nitrogen. Dilation was measured with a dial gauge which could be read by interpolation to 0.00005 in. Temperature was maintained within ± 3°F by a Brown Electronik Controller. Chromel-alumel thermocouple leads were welded to opposite ends of the specimen with the specimen serving as the hot junction. As a check on temperature uniformity comparison was made of the specimen temperature as measured with the chromel-alumel leads and the temperature of the center of the specimen as measured with a calibrated platinum—platinum-rhodium thermocouple embedded in asbestos in the central hole of the specimen. During heating a 5°F temperature difference was noted below 1000°F, but none above, while in cooling, a 5°F difference was observed from 1300" to 735°F, but none below. Heating rates of 35°F per min and cooling rates of 60°F per min were employed for all dilatometric studies. For transformation studies below room temperature, the dilatometer was allowed to cool to 150°F and then was quenched into liquid nitrogen.

Jan 1, 1951

By O. P. Arora, M. Metzger

Single-phase aluminum containing 1 to 600ppm copper was studied in 7 to 26 pct HCl. The corrosion rate in the autocatalytic stage was resolved into a constant intrinsic component and an acdelerating autocatalytic component, and attention was focused on the part of this stage where the corrosion rate could be described by a simple empirical relation. Autocatalytic corrosion in this period was localized and its rate increased rapidly with copper content and with the strength and chlaride content of the acid. The effects of adding cupric ion to 16 pct HCI were functionally and quantitatively inconsistent with the autocatalytic rates observed. A theory of these rates was given based on the deposition in nzetallic contact with the aluminum of part of the copper introduced by corrosion. It has long been known in a general way that aluminum containing sufficient copper suffers in hydrochloric acid an autocatalytic acceleration of corrosion resulting from the introduction into the acid of copper ions and their reduction on the specimen as elemental copper, which provides cathodes of low hydrogen overvoltage.&apos;-3 In a previous paper, this phenomenon was identified in single-phase high-purity material at copper levels as low as 20 ppm and an empirical equation describing autocatalytic corrosion rates in 16 and 20 pct HC1 was presented. In the present work the range of acid strength and chemistry studied was extended, a more accurate empirical equation for the autocatalytic rate was determined, and a theory of this rate was formulated. A major source of interest in this system is the intergranular corrosion, which is also strongly influenced by copper content,= and an objective of the present work on general corrosion was to provide a basis for studying the role of copper content in intergranular corrosion, which is experimentally much less accessible.

Jan 1, 1963

By R. J. Wasilewski

THERMAL expansion of rhenium data have been reported by Agte et al.,&apos; and Medoff and cadoff,&apos; respectively, while the linear expansion coefficient was determined by Sims et Al.3 Denoting expansion coefficients parallel and at right angle to c axis by all and Al respectively, their weighted mean should be equal to dilatometric linear coefficient of a random polycrystalline specimen. The values reported for these coefficients are tabulated below: Since these values are in poor agreement, and because of anomalous expansion behavior observed in titanium 4 and chromium, a rede termination of the axial expansion was carried out. A Unicam 19-cm-diam high-temperature camera was used, with unfiltered CuK radiation. Camera calibration was carried out using at Pt wire standarde at temperatures up to 1100oC, the variation between indicated and true temperature being within the experimental error (estimated at <3oC) above 750o C. Rhenium Johnson Matthey spectrographic standard) was vacuum annealed at 1000 oC prior to X-ray diffraction experiments. Lattice parameters were obtained by least-squares solution using the reflec- tions (1232), (1015), (2024), and (3030) for all the patterns, and the additional reflection (2133) for higher temperature (400°C and above) patterns. The relative expansion data obtained are shown in Fig. 1, lengths of the vertical bars indicating the spread in the parameter values obtained by using various combinations of three spacings from the four or five measured. The data calculated from the equation of Ref. 2 are included for comparison purposes. Several specimens were used to obtain the above data, neither of them showing a significant parameter change after completion of the high temperature runs. Some parameter data and the corresponding expansion coefficients between 25 oC and the measurement temperature are tabulated below. The comparison of the present data with those previously reported shows reasonable agreement with the results of Medoff and cadoff2 within the temperature range covered by them (up to 1000 oC). The a values are appreciably higher throughout most of the investigated temperature range. The basal expansion is—in agreement with their findings—appreciably higher than that in the direction of hexagonal axis. The expansion coefficient, al, however, decreases rather more slowly with temperature than previously reported. The expansion along the c axis up to nearly 1000°C appears in excellent agreement. However, at higher temperatures there is a marked deviation towards higher expansion, reproducible between different specimens. Furthermore, there seems to be some irregularity in the variation of all with temperature, the apparent local minimum and maximum values at 510o and 1024o C, Table II, being well outside the experimental error limits. It must be stressed that the apparent discontinuity in the c parameter expansion is still insufficient to account for the expansion value reported by Agte et al.&apos; since a total expansion of close to 2 pct would

Jan 1, 1962

By W. F. Hosford

A series of aluminum single crystals was subjected to axially symmetric flow by drawing through dies. The orientation dependence of the drawing stress, which indicates the resistance to this type of flow, compares reasonably with predictions of Taylor and of Bishop and Hill. Measured lattice rotations likewise are generally consistent with theory. The most successful analyses of the plastic behavior of polycrystalline metal and its relationship to single crystal behavior are those of Taylor1-3 and of Bishop and Hill.4-6 The purpose of this paper is to provide a critical test of some of the basic assumptions involved in these theories. Both treatments apply to fcc metals and assume the shape change of each grain in a polycrystal to be the same as that of the polycrystal as a whole. Thus for a randomly oriented polycrystal extended under uni-axial tension each grain is assumed to undergo axially symmetric flow. dey = dez = -1/2dex, deyZ = dezx = dexy = 0 [l] where x, y, and z are a set of orthogonal axes, x being the tensile axis. Although [011.] oriented grains in bcc and fcc metals may depart markedly from this ideal behavior,7,8 the assumption is probably quite reasonable for most grains. Under a uniaxial tensile stress, ox, the work dW per unit volume expended in producing an increment of axial strain dex is, dW=oxdex [21 Since this work is expended in slip, dw =STi dyi 131 where Ti and yi are the shear stress and shear strain on the active slip systems. In both analyses Ti is taken to be the same on all slip systems, and dependent only on the total prior shear strain on all systems, so dw = Tdy [41 where t is the shear stress required for slip and y is the sum of the shear strain yi on all slip systems. Combining 121 and [4] and defining M = oX/T The ratio M is a generalized Schmid factor. It relates the tensile stress required for axially symmetric flow, ox, to the basic shear stress, 7, and it also expresses the ratio of crystallographic strain, y, to the tensile strain, Ex It depends only on the orientation of the crystal. Taylor evaluated M for various orientations by finding the least value of dy/dEx which could satisfy the shape change. Bishop and Hill, on the other hand, found M by considering the relative work (1/T)dW/dEx expended by stress states which could activate enough slip systems to produce the shape changes. The results of both methods appear to be equivalent, although certain omissions were made in Taylor&apos;s original work. The orientation dependence of M, calculated by the second method,9 is shown in Fig. 1. Taylor used the average 2= 3.06 for all possible orientations to predict the tensile stress-strain curve (oxvs Ex) for a random polycrystal from the shear stress-strain curve (t vs y) of a single crystal. Changes in M from lattice rotation were neglected so points on the ox vs ex curve were simply taken at ox = 3.06t and e = y/3.06 from corresponding points on the t vs y curve. Recent extension of the analyses of Taylor and of Bishop and Hill to crystallographically textured metals has been used to relate plastic anisotropy to textures, and to predict the potential texture hardening that could result from texture control.9 Unfortunately there have been relatively few experimental tests of the underlying theory. Taylor found that the tensile stress-strain curve of polycrystalline aluminum did agree reasonably well with that predicted from a single-crystal T-y curve. Had the single crystal undergone easy glide, how-

Jan 1, 1965

By J. D. Lubahn

The Bauschinger effect, or rounding of the corner of the stress-strain curve upon reloading, represents a temporary apparent softness that is more pronounced at large strains than small and for complete unloading than for partial unloading. Interrupted creep tests on copper exhibit a similar temporary softness (high creep rate) upon reloading. The fact that the strainwise dying-out time of these effects is the same in both tensile and creep tests shows that they are related. Thus, the term Bauschinger effect appears to embrace behavior following partial or complete unloading and reloading in addition to behavior following reversed loading. It is suggested that the term may properly apply also to certain creep behaviors following a small load decrement. INTERRUPTED tensile tests at low temperatures show1 a rounding of the corner of the stress-strain curve for reloading, which indicates a temporarily low deformation resistance. In the absence of recovery, the curve soon rises to the value that would have prevailed if the test had not been interrupted. The rounding of the reloading tensile curve has sometimes been referred to1 as the Bauschinger effect, although the term is more commonly applied to low deformation resistance in compression following tensile prestrain. The unusually broad usage of the term Bauschinger eflect in ref. 1 seems justified by the obvious interconnection of the various behaviors to which it has been applied.&apos; In fact, the following discussion will indicate that still broader usage might be desirable. The Bauschinger effect is common at room temperature but apparently disappears at higher temperatures.2 Interrupted creep tests and tensile tests were made on certified OFHC copper (nongaseous impurities exclusive of silver were 0.004 pct), cold drawn 84 pct to ½ in. diam, and annealed at 600" (about 0.025 mm grains) or 850°C (about 0.2 mm grains). The tests were made in standard creep or tensile machines, using an O.S. Peters microformer-type extensometer or, for the small plastic strains, a special arrangement employing General Electric magnetic gage heads.&apos; Interrupted creep tests at room temperature show3,4 an initial softness after reloading, manifested by an initial creep rate that is higher than that which would have prevailed if the test had not been interrupted. Fig. 1 shows some typical examples. This effect is apparently temporary (as is that in tensile tests): in four of the five tests shown, the log rate vs strain curve becomes parallel to an

Jan 1, 1956

By F. N. Rhines

STUDIES upon the sintering of metal powders, in the solid state, have led to the proposal that the surface energy of the powder particles provides the driving force that causes points of contact between pairs of particles to grow into broad welds which isolate the residual vacant space into pores that tend to spheroidize and gradually to diminish in total volume.&apos; Investigators differ with regard to the mechanism of the movement of the metal, under the influence of surface energy, to accomplish these changes. One school asserts that there is a mass movement of the metal, referred to as a "viscous flow," while the other school prefers to view the movement as a self diffusion process, wherein individual atoms are, transferred without disturbance of the basic pattern of the crystal lattice. Extensive experimental studies upon the sintering of copper, conducted recently by A. J. Shaler,2 have been in- terpreted by their author as support for the viscous flow mechanism of transport, the theory of which was developed originally by J. Frenkel.3 Duplicating a portion of this work with minor changes, G. C. Kuczynski4 is led to the alternate view, namely, that the initial stages of sintering, at least, proceed as a self-diffusion process. Both of these investigations were designed to deal with an isolated unit of sintering, i.e., with the shrinkage of a single pore, or with the growth of a single point weld. It remains to ascertain the behavior of a typical metal powder compact composed of a large number of particles of varying size and sintering to a body with a multiplicity of pores. The observation of density changes alone during sintering is not sufficient in such a case; it is essential to know how the internal geometry of the compact changes. This has been the object of the present investigation, the results of which are used to support the self-diffusion mechanism of sintering. The present studies consist in the measurement of the number of pores as a function of size and time at temperature during the sintering of a copper compact made from a commercial copper powder lightly pressed and sintered in several different atmospheres. A brief survey was made also of the change in shape of the pores, under the influence of the same variables. All of this was done by direct observation with the microscope. Densities were measured on the same sample. It is found that, while the compact is exhibiting an overall shrink-

Jan 1, 1951

By J. J. Gilman, T. A. Read

FOLLOWING the deformation 01 zinc monocrys-tals, sharply bent basal planes are observed near several types of inhomogeneities. Three of these in-homogeneities have characteristics which are quite regular so that they can be studied and analyzed. These are compressive kink bands, "deformation bands," and the inhomogeneities near end restraints. The present paper describes experiments in which "deformation bands" were artificially produced, and bend plane phenomena are discussed in terms of dislocation theory. Also, two new bend plane phenomena are described. The importance of bend plane phenomena in the deformation of crystals is not widely recognized. Many phenomena may be explained in a manner similar to the discussion in this paper. Jillson1 has pointed out that the "punching effect" in zinc is a bend plane phenomenon and is not caused by prismatic slip.&apos; Bowles3 has suggested that they may be involved in diffusionless phase changes. Cahn4 has discussed the role of bend plane formation in the polygonization of zinc. Experimental Work Tensile Kink Bands: Because of the geometrical similarity between "deformation bands" and "kink bands" (compare Fig. 1 of this paper with Fig. 1 of the paper by Hess and Barrett"), the band shown in Fig. 1 of this paper will be called a "tensile kink band," and that shown by Hess and Barrett will be called a "compressive kink band." It is felt that the term "deformation band" should be reserved for banded structures in polycrystalline materials such as iron." Tensile kink bands seem to form spontaneously in aluminum crystals deformed by tensile loading.7-10 In zinc and cadmium crystals they do not form in good, carefully loaded specimens.&apos;." However, tensile kink bands can be produced artificially in zinc crystals. The present authors did this by scratching one of the flat surfaces of triangular crystals transversely with a sharp needle. Natural tensile kink bands caused by inhomogeneities sometimes appeared in deformed crystals which were identical in appearance with the artificially produced ones. Zinc monocrystals were grown by the Bridgman method in graphite molds. Chemically pure zinc (99.999+ pct Zn) was used and the molds were sealed inside evacuated pyrex tubes during growth. The crystal cross sections were equilateral triangles with a typical base of 0.210 in. The artificial kink band shown in Fig. 1 is typical of tensile kink bands in zinc. The band lies between two bend planes which run from upper right to lower left and is inclined oppositely to the slip bands which are sharply bent at the two bend planes. The general form of the artificial tensile kink bands was independent of the scratch depth (1 to 5 mils deep) and also independent of which side was scratched. These variables did cause variations, however. Deep scratches produced more localized kink bands than light scratches. Also, if the angle between the slip plane traces and a transverse scratch varied appreciably among the three sides, then localization of the resulting kink bands also varied. Furthermore, if the slip direction lay nearly parallel to the scratched side, the band was more developed near the scratched side than at the opposite edge. Scratches produced tensile kink bands for crystal orientations from xo = 15" to x, = 75". Fig. 2 shows a scratched crystal after deformation. One triangular side lies in the plane of the photograph. The right hand tensile kink band was produced by a transverse scratch on the upper right side. The next two kink bands were the result of scratches on the front surface. The kink band at the left was caused by a scratch on the lower back side. All four bands have the same general form. A longitudinal scratch was also made on the crystal shown in Fig. 2 to determine the effect of a scratch on the critical shear stress. The critical shear stress of the scratched region was 33.9 g per sq mm compared to 24.4 g per sq mm for the un-scratched region above it. Fig. 3 shows Laue patterns of the crystal shown in Fig. 2. Fig. 3a shows the pattern of the undeformed crystal. The orientation was x, = 21°, A, = 31". After deformation, Fig. 3b was made of the homogeneously deformed portion of the crystal. The spots are compact but split into two halves. This region was elongated 45 pct and its orientation was x = 14", X = 20"; the sine law predicts x = 14", A = 20.5". Fig. 3c was taken near the center of the middle tensile kink band of Fig. 2. The pattern shows a range of orientations and polygonization in this region. The spread in orientation was due to the fact that the basal planes were curved (see Fig. 1) rather than flat as in the ideal case. Some may also have been the result of elastic distortions and "local curvatures." The orientation range was x = 23" to 32", A = 30" to 42". It is apparent from Fig. 3 that the material inside and outside the kink band rotated in opposite directions with respect to the tension axis during deformation. The orientation calculated from the ideal configuration of Fig. 9,

Jan 1, 1954

By N. K. Chen, R. Maddin, K. T. Aust

Lattice rotations occurring on the tension and compression sides during the bending of molybdenum single crystals at room temperature were followed in detail. Observations were also made concerning crystallite rotations and slip traces. &apos;The results indicated the participation of (110) as slip planes and the<111>as slip directions. Crystallite fragmentation during bending was also noted. EVERAL investigations have been conducted on pure bending of face-centered cubic metals.&apos;-" Structural changes as a result of "bend-gliding," and the importance of bending and constraints during conditions of axial stressing, have been noted.&apos;," It was evident that the mechanism by which the bending deformation occurs is more complex than the case of simple shear. Studies of the bending of body-centered cubic metals from the aspect of the crystallographic mechanism appear to be lacking. Molybdenum single crystals therefore were subjected to deformation by bending in order to determine the reaction of the body-centered cubic lattice to bending stresses. It might be expected for the bending of single crystals that lattice rotation as represented by the axis of compression would proceed toward the pole of the active slip plane and that rotation of the tensile stress axis should indicate the slip direction.&apos; It was believed therefore that a study of the tension and compression sides of bent molybdenum single crystals should give data concerning the operative slip system. Specific problems which are pertinent to the overall picture of plastic deformation were also investigated, e.g., whether the constraints offered by pure bending give rise to the deformation band, and also the nature of the asterism occurring on the tension and compression sides during the stages of deformation. Experimental Procedure Eight single crystal specimens were grown from sintered molybdenum rods 143 in. diameter using the method described previously.6 The purity of this material was reported as 99.9 pct as described elsewhere.&apos; The specimens were % to 1/10 in. in diameter x 7 in. long, with single crystals approximately 1 to 2 in. in length occupying the entire center sections of each specimen. The specimens were elec-trolytically polished using an electrolyte of 300 cc methyl alcohol, 60 cc H2SO4, 130 cc HCl, and a current density of 4 amp per sq in. Each specimen was then loaded in a bending apparatus similar to that used by Yen and Hibbard,&apos; as shown in Fig. 1. The load was applied by means of a spring and screw arrangement through four ball-bearing surfaces set 1.5 in. apart. Either the inner two bearings or the outer two (A, B, Fig. 1) were attached to a movable steel plate (D) through which the load was transmitted. Since the apparatus was mounted on a track of the X-ray apparatus, the tension or compression side of the specimen could

Jan 1, 1954

By Jack L. Taylor

As expected from similar crystal structures and favorable atomic size factors, titanium, vanadium, and molybdenum are completely soluble in one another above the transformation temperature of titanium. The fl phase parameters of the continuous solid solution are shown graphically. Limiting compositions for retained fl phase have been determined. VANADIUM and molybdenum both have body-centered-cubic structures at all temperatures and, from the atomic diameter comparison factor, 3.9 pct, would be expected to form a complete series of solid solutions. The existence of complete solubility has been confirmed by work&apos; at the Jet Propulsion Laboratory. Furthermore, vanadium and molybdenum have favorable atomic size factors to form complete binary solid solutions with the B phase, high temperature form of titanium, which also has body-centered-cubic structure. Pietro-kowsky and Duwez&apos; and Hansen et al." have established the existence of the complete series of solutions in these binary systems. It would be logical, therefore, to expect that p-titanium, vanadium, and molybdenum would be completely soluble in one

Jan 1, 1957

By H. R. Ogden, A. G. Imgram, D. N. Williams

The effects of composition on the mechanical properties and aging characteristics of several alloys in the Ti-V-Cr system, with and without aluminum modifications, were evaluated. Increasing the chromium, vandium, or aluminum content increased the strength of quenched structures with chromium being the most effective strengthener. Appreciable aging response was obtained with low chromium alloys, but high chromium alloys age softened rather than. hardened. High vanadium contents had a similar effect. Aluminum additions shifted the aging behavior toward that observed in lower chromium alloys, enabling high chromium alloys to be age hardened. DURING the course of titanium alloy development many a and a-ß alloys have been evolved to commercial status. However, only one all-ß alloy has achieved this same stature. This is the Ti-13V-11Cr-3Al alloy. It is characterized by a very sluggish ß-phase decomposition reaction such that very slow cooling rates can retain the 0 phase at room temperature. In addition, very high strength levels can be obtained by long-time aging treatments. Combinations of cold or warm working followed by aging produce even further improvements in strength. This paper describes the results of a research program in which the effects of composition on the mechanical properties and aging characteristics of several alloys in the Ti-V-Cr system, with and without aluminum modifications, were evaluated. EXPERIMENTAL PROCEDURES Electrolytically refined, high-purity titanium was used as the alloy base for these studies. Iodide chromium, electrolytically refined vanadium granules, and high-purity aluminum sheet were used as alloying additions. The compositions of interest were melted as 250-g ingots in a direct current arc melting furnace under a flowing atmosphere of argon. The ingots were hot forged to 3/4-in.-diam bars, vacuum annealed for 6 hr at 1800°F to reduce residual hydrogen content, and then hot swaged to 1/4-in.-diam rods. Fabrication history, and interstitial analyses after fabrication are given in Table I. All specimens to be heat treated were sealed in Vycor capsules under a partial pressure of argon. Samples used to define the ß transus were quenched from temperatures ranging from 1350° to 1100°F after holding at temperature for 15 min. Samples for aging studies were quenched from above the ß transus temperature and then aged for up to 64 hr at 750°F and for 100 hr at 850°, 900°, and 950°F. The effects of straining prior to aging were also investigated. The results of these studies were used to select the heat treatments for the tensile specimen blanks. Heat treatments of the tensile specimens are described in Table 11. Alloys were aged after solution heat treatment or after solution heat treatment and cold swaging to 50 pct reduction in area. Standard 0.125-in.-diam tensile specimens were machined from the heat-treated blanks. All tensile tests were performed in a Baldwin-Southwark uni-

Jan 1, 1963

By Niels Hansen

Dispersion-strengthened sintered aluminum products are normally manufactured from surface-oxidized aluminum powder, SAP,&apos; or from atomized aluminum powder.&apos; The powder-blending technique consisting in mechanical mixing of the constituents has been used in the manufacture of numerous dispersion-strengthening alloys, but has never been successfully applied to aluminum alloys. This technique may, however, be applicable if it is possible to produce an unagglomerated mixture of the constituents in the form of fine powders, and the present study was initiated to test this assumption in the aluminum/aluminum oxide system.3 Table I lists the two grades of aluminum powder and the aluminum oxide powder used in the manufacture of the alloys. MD 105 A is an aluminum powder with an average grain size less than 5 IJ., which is isolated from the MD 105 powder by centrifugal separation in cyclohexanol. The aluminum powders and the aluminum oxide were blended in a high-speed blender and then subjected to cold compaction and hot compaction at 550" to 600°C. Subsequently the compacts were hot-extruded with an extrusion ratio of 15 to 1. The alloys were evaluated by tensile testing at room temperature and at 400°C, microscopic examination, and heat treatment at 500°C followed by tensile testing at room temperature. For the purpose of comparison, a commercial SAP quality supplied by Swiss Aluminium Ltd. was tested in the same manner. The tensile data at room temperature and at 400°C are plotted in Figs. 1, 2, and 3 as a function of the weight percent of oxide. The oxide content

Jan 1, 1964

By J. H. O’Dette

BLISTER formation on wrought aluminum products has been a matter of concern to aluminum fabricators for many years. The fact that blisters make their appearance during the final stages of fabrication means that much time and effort have been expended before it is evident that the material must be scrapped. This and the loss of production are ample reasons for embarking on a research program to find out more about blistering and possible methods of control. Many excellent papers on this subject have appeared in the technical literature in the last few years. In one of the more recent papers, Kostronl gives a fairly complete review of the problem of gas in aluminum and blistering in general. From the work of the various investigators, a general mechanism for the formation of blisters has evolved and may be summarized briefly as follows: Hydrogen gas is usually present in the cast ingot, in the atomic or ionic state, in excess of the solid solubility. At room temperature the gas atoms are relatively immobile, but at elevated temperatures they become mobile and diffuse to free surfaces where they associate to form molecules. If these free surfaces are discontinuities within the ingot then the associated gas molecules collect and build up considerable pressure until equilibrium is reached with the dissolved gas around the discontinuity. Since the solubility of the gas is proportional to the square root of the partial pressure it is evident that large pressures may be built up at the discontinuities. When the metal is rolled to sheet the pressure of the gas in these, discontinuities is sufficient to deform the surface of the sheet and form a blister, particularly when the strength of the material is reduced during the annealing. Although the mechanism of the formation of blisters was fairly well known, the actual impor- tance of the individual roles played by the gas and the discontinuities was not so well established that positive methods for control of blistering were at hand. It was the object of the investigation to learn more about the nature of the discontinuities giving rise to blistering and to develop methods of control. The investigation was carried out in three stages as follows: a) A study of the more commonly used methods of removing hydrogen from aluminum, such as fluxing and holding, and their effects on blistering. b) Location of the discontinuities giving rise to blistering. c) A study, by indirect methods, of the movement of gas in the metal and its effect on blistering, and the development of methods of blister control during fabrication. Removing Gas and Reducing Blistering by Fluxing or Holding-—The work of removing gas and reducing blistering by fluxing or holding was carried out on metal of Alcan 2s (1100) composition with an artificially high gas content. The high gas content was obtained by introducing water into the melt prior to casting; the water reacted with the aluminum forming A12O3 and hydrogen. The procedure was to raise the gas content by introducing water into an aluminum melt and using half the melt to cast one ingot immediately. The remaining metal was treated again with water to make up for the reduction in gas content during holding, while the first ingot was being cast, and then given a fluxing or holding treatment and cast into an ingot. Samples for gas determination were cast from the molten metal before and after the gassing operation; before, after, and during fluxing, and while casting. Samples were also cut from sections of the ingots. Gas determinations were made on these samples using the well known vacuum fusion technique. All ingots were hot rolled at 500°C to 0.250-in. slab which, in turn, was cold rolled to 0.040 in. sheet. The sheet was coiled and annealed for 2 hr at 500 °C and then cut into 5-in. squares which were inspected for

Jan 1, 1958