By R. G. Gifkins

Mean boundary migration depended linearly upon creep extension under various conditions. Prolonged annealing or air-casting increased the proportion of immobile boundaries at a given stage of tests. Grain growth during annealing followed a power law. The linking of migration and sliding in creep and models for migration are examined; activation energies are calculated from these models. Segregation of oxygen to boundaries appears to be a controlling factor. THE idea that boundary migration and boundary sliding during creep are linked has often been suggested,'-5 especially when evidence has been obtained for an alternation between the two processes. In simple bicrystals sliding can occur without any migration6 but in more complex bicrystals7 it is observed. McLean' and Couling and Roberts 5 made measurements of both sliding and migration; McLean concluded that there was no linking of the two processes whereas Couling and Roberts supported the idea. McLean' also developed a model for migration during creep and annealing. The present work was initiated as part of a study of the recrystallization of lead during creep9 but has been extended to examine some aspects of the mechanism of migration. MATERIALS AND METHODS Specially refined high-purity lead* was used; the total of impurities, excluding oxygen, was 0.0008 wt pct. Oxygen was removed as far as possible by melting in vacuo, treating at 550" to 600°C with hydrogen and then casting at 450°C under a vacuum of 10-2 mm Hg; the oxygen was then believed to be 0.00005 wt pct. Specimens were made from extruded strip and then annealed at the required temperature in an air oven, controlled to 5 lac. They were then polished in a mixture of acetic acid and hydrogen peroxide. At this stage some specimens were etched to give grain contrast and their grain sizes determined by the intercept method. Migration of boundaries during creep was measured on the surface of polished (not etched) specimens, directly loaded at room temperature (22°C) or 50°C (52"C) to initial stresses of 300 to 700 1b per sq in. Twenty six vacuum-cast hydrogen-reduced specimens were used and, in addition, two specimens were from material air cast after hydrogen reduction ("partial" air cast) and two from air-cast material not treated with hydrogen ("full" air cast). Duplicates were made in the majority of tests. At intervals through the creep tests, specimens were unloaded and the migration measured, normal to the direction of migration at the point of measurement, for each boundary along standard traverses. Usually between 110 to 180 boundaries were measured at each of some twelve stages of the tests. Migration was measured on the projected image (X100) using prism illumination. Fig. 1 illustrates the method of measurement and shows the kind of variation of migration found from boundary to boundary and along particular boundaries. Fig. 2 gives an example of more extensive migration. The mean value of distance migrated was generally reproducible to *10 pct but occasional points gave a scatter of *20 pct. The correctibn applied by McLean8 to allow for the contribution sliding makes to the apparent distance of migration could not be used, for the sliding at most boundaries was too small to measure with the equipment available. There were two reasons for supposing the correction unnecessary in the present work;

Jan 1, 1960

By E. S. Machlin, Morris Cohen

The martensite reaction in single crystals and polycrystals of 70 pct Fe-30 pct Ni alloys is shown to be autocatalytic in nature, producing bursts of transformation during cooling. The temperature of the first burst of transformation, called Mb, occurs below M, in these alloys. Experiments were devised to test the athermal embryo and strain embryo theories of martensite nucleation. The results indicate that internal strains, either within the virgin austenite or around existing martensitic plates, control the nucleation process in these alloys. Furthermore, the growth of martensitic plates is not limited by the attainment of an elastic balance with the austenitic matrix, but by the occurrence of plastic deformation at the martensite boundaries which interferes with the propagation mechanism. IN an investigation of the martensitic habit in single crystals of a 69 pct Fe-31 pct Ni alloy,' it was observed that about 25 pct of the austenite transformed during subatmospheric cooling within the time-interval of an audible click. This event proved quite spectacular: The shock wave sent out from the specimen freely suspended on a thread in the refrigerating liquid was occasionally sufficiently intense to shatter the Dewar container and to separate the toluene column in the immersed thermometer. The Present investigation was undertaken to determine- the kinetics and mechanism of this "burst" type of martensitic reaction. The analyses of the alloys studied are given in Table I. The composition of the single crystal specimens is designated by alloy A, while the polycrystal-line specimens were made of alloys B and C as noted in the text. The single crystals were prepared in a vacuum furnace, using a modified Bridgman technique. Most of these crystals were homogenized by holding for 24 hr at about 1300°C just after solidification. However, it may be emphasized here that the degree of homogenization was not a controlling factor in the subsequent experiments, inasmuch as specimens having different degrees of homogenization yielded the same results. All of the single crystals were fully austenitic as slowly cooled to room temperature. An illustration of the burst phenomenon is given in Fig. 1, which shows oscillograms of electrical resistivity and temperature vs. time during the continuous quenching of 1/16 in. wire specimens (alloy B) in a dry ice and acetone bath at —77°C. There are at least two observable bursts in this case, as indicated by the sharp decreases of resistance accompanying the sudden formation of substantial quantities of martensite. The thermal arrest during the quench probably corresponds to the larger burst. Usually the bursts are followed by more or less progressive transformation during continuous cooling. It will also be noted that the resistance continues to decrease after the specimen has reached the bath temperature. This isothermal change denotes the formation of martensite at constant temperature, and will be the subject of another paper. Examination of fiducial scratches on the surface of a transformed single crystal has shown2 that the scratches in adjoining nonparallel martensitic plates are usually bent in opposite directions, as though one plate forms in such a way as to relieve the matrix stresses set up by the adjacent plate. This, together with some of the results described in ref. 1, Table I. Compositions of Alloys Studied, in Percent Alloy Ni C N Mn Si P S Cr A 31±0.3 0.048 0.027 0.003 0.56 0.007 0.002 B 29.5±0.2 0.036 0.02 0.19 0.09 0.008 0.006 C 19.99 0.52 0.37 0.47 0.010 0.015 0.04 led to the tentative concept that a cooperative action exists which provides the impetus for much of the transformation that appears during the burst. The following series of experiments were performed in order to test this idea. Cooperative Nature of the Burst Two adjacent disks, Va in. thick x % in. diam, were cut from a single austenite crystal of alloy A using a jeweler's saw. One of the disks was then cut into 15 parts. Then 12 of the latter pieces and the second disk were austenitized (stress relieved) at 600°C for 30 min and water quenched to room temperature. The temperatures at which the first burst of transformation appeared were determined for

Jan 1, 1952

By M. Cohen, C. Wagner, J. E. Reynolds

If the total volume of a diffusion couple changes during the diffusion, the measurement of distance becomes ambiguous. Use of distance parameters as suggested by Hartley and Crank is discussed. For small concentration differences, the standard form of Fick's second law is retained with conventional length units and the in- terdiffusion coefficient D. It is shown how D can be calculated from experiments involving large concentration differences and analyzed in terms of distance parameters. 'The merits of incremental diffusion couples involving small concentration differences are emphasized. THE conventional form of Fick's second law for one-dimensional diffusion of component B in a binary solution of A and B is where c, is the concentration of component B; x, the distance; t, the time; and D, the interdiffusion coefficient which may depend on ca. Hartley and Crank' have pointed out that Eq. 1 applies only if the total volume of the diffusion couple does not change during the diffusion process; otherwise, the definition of x becomes ambiguous. No change in total volume takes place if the specific volume of the solution is a linear function of the weight fraction Wb, or if the molar volume is a linear function of the mol fraction N. In some alloys, however, these relationships do not hold, and then it is necessary to introduce a modified measure of distance, 4 in order to retain the general form of Eq. 1. The application of Hartley and Crank's suggestions to diffusion in alloys has been discussed by Wagner.' Relation Between Measure of Distance and Units of Concentration The definition of [ depends on the choice of units for the concentration c,, as follows: 1—If the concentration ca is measured as the weight fraction W, (or weight percent), [ = 5, has to be defined so that equal increments of contain equal increments of mass m of the solution, e.g., dm = pSdx = Sdw [2] where p is the local density of the solution, and S is the cross-sectional area in sq cm which is taken to be constant in this problem of one-dimensional diffusion." * da Silva and Mehla have demonstrated the constancy of the cross-sectional area in the usual type of diffusion couple. However, experiments involving diffusion into thin wires4, 5 may exhibit changes in cross-sectional area, and therefore are excluded from the present treatment. Thus and the unit of is gram per sq cm instead of cm. 2—If the concentration c, is the mol fraction N, must be defined so that equal increments of contain equal numbers of mols of solution, e.g., dn= (S/V)dx= Sd [41 where V is the local molar volume of the solution. Thus dt, = dx/V [51 and the unit of is mols per sq cm. 3—If, as may be advisable in the case of interstitial solutions, the concentration C is measured in terms of the molar ratio of components B and A (c,, = Y, = nH/nA, where n and nl are numbers of mols of B and A), = Y has to be defined so that equal increments of contain equal numbers of mols of A, e.g., dnA= (NAS/V)dx = Sdf [6]

Jan 1, 1954

By D. Turnbull, J. C. Fisher

ACCORDING to the "reaction-path" modell,2 of martensite nucleation, the shear angle of the embryonic martensite plate must be treated as a variable, and included in any calculation of nucleus critical size. Also, as can be deduced from this model, the interfacial free energy between austenite and martensite does not reach its final value until the shear is completed. It is zero for zero shear angle. However, in order to account for the kinetics of the martensite transformation, some sort of interfacial energy barrier appears to be necessary even with the reaction-path model, for otherwise the volume and the energy of formation of the critical size nucleus both collapse to zero.3 Cohen independently suggested that surface energy could be incorporated into the reaction-path model, with the overall free energy of a martensite embryo being a function of its volume and shear angle.' It is possible to estimate the energy associated with the formation of a critical-size martensite nucleus starting with the reaction-path model and including a surface free-energy barrier. As the dependence of interfacial free energy upon shear angle is unknown, a simple type of dependence will be assumed, with the belief that the true dependence would not lead to appreciably different results. Consider the work required to form a lenticular martensite plate with radius r, thickness t, and shear angle 8. There are three contributions; one being the interfacial free energy, one being the free energy change in the martensite plate, and one being the free energy increase in the surrounding austenite. The interfacial free energy u is assumed to depend upon the shear angle 0 according to the relationship s=s0(?/?0)n [1] where 8, is the equilibrium shear angle and n is an exponent that may lie in the range 0 n 2. The work required to form the interfaces of a martensite plate then is W. = 2pr² s0(?/?0)n [2] The free energy change per unit volume of martensite is composed of two parts, one the ordinary volume free energy ?f1. which is negative, and the other the elastic strain energy G?m²/2, where G is the shear modulus and 7, the shear strain relative to the martensite structure. This expression for the strain energy is valid only when the shear strain ym, is sufficiently small that the martensite is within its linear elastic range. There is no doubt that ym, lies beyond the linear elastic range for embryos that are considerably subcritical. However, for critical nuclei it will be shown that ym, is 1.5 pct or less, within the linear elastic range of martensite. For embryos of nearly critical size, then, the strain energy of the martensite is correctly given by G?m²/2. The shear strain in the martensite is ym, = 8, — 8, and the work required to form the strained martensite is Wm --= (pr²t/2) [?fv + G(?O - ?)²/2] [3] The free energy change in the austenite is entirely that due to elastic distortion. The elastic strain is not uniformly distributed in the austenite, being large near the martensite plate and small elsewhere. Approximately, however, the energy corresponds to a uniform shear strain ya= (?t/2)/r [4] throughout the volume 4pr³/3 surrounding the plate. The work required to strain the surrounding austenite then is Wa = (4pr³/3) (G?a²/2) = (G?²/6) prt² [51 For simplicity, the same shear modulus G is assumed for each structure. The total free energy for forming a plate then is W = W3 + Wm + Wa. = 2pr² s0 (?/p?0)n + (pr²t/2) [?fr+G(?0-?)²/2] + (G?²6) prt2 [6] This expression is correct for nuclei and for embryos of nearly critical size, where, as will be shown, the strain energy in the martensite is correctly given by the expression G (? — ?)². Having W as a function of r, t, and 8, as in Eq. 6, there is a saddle-point where W has a stationary value, W subsequently decreasing indefinitely as the nucleus volume increases along the reaction path. The stationary value of W is the energy of the critical nucleus. The critical nucleus has radius, thickness, and shear angle such that ?W/?r - awlat: = ?W/?p? = 0. Performing these differentiations and calculating the critical nucleus energy, W* = [8192p(G?/6)²;s/27 ?fv4] [7] where a= (?/?0)3n+1[l +G(8"-8)'/2af.]' [7a] and where 8 is to be determined from the equation (1 + 3n/4) + G8(6O - (9)/[Af. +G(6>o-6>)72] = 0 [8] For ?f, near —200 cal per mol or —10" ergs per cc, and 8, near 1/6, as for iron-base alloys, Eq. 8 gives ?0 - ? ~ - (4 + 3n) ?f1./4G0O [9] as the difference between the equilibrium shear angle and the actual shear angle for a critical nu-

Jan 1, 1954

By M. J. Pool

The partial molar heats of solution in liquid tin of cadmium, silver, tellurium, and zinc have been measured at 655°. 700°, and 750°K by liquid-metal solution calorimetry. Silver, cadmium, and zinc are endothermic at these temperatures while tellurium is exothermic. Only the heat of solution of silver depends on composition while all four elements show a temperature-de pendent heat of solution. The heat of solution of tellurium is constant up to 0.6 g-at. pct, becomes increasingly more exothermic, and reaches a limiting value at 1 g-at. pct Te. The limiting value has been used to calculate the heat of formation of SnTe at 750°K. The heat effects associated with the dissolution of the compounds Ag2 Te, CdTe, and ZnTe in liquid tin were measured at 750°K. These values are cotnOined with the measured hat effects at 750°Kfor silver, cadmium, tellurium, and zinc to detertrline the heats of formation of the telluride compounds. Cadmium lelluride exhibits a heat of dissolution which has a compositional dependence. THERE is a considerable amount of interest in the compounds of tellurium because of their electronic properties. Both cadmium and zinc tellurides are thermoelectric materials and considerable work has been done on their electronic properties but a limited amount of data is available on their ther-modynamic properties. This work was undertaken to elucidate the heat of formation data on cadmium and zinc telluride. Since both cadmium and zinc are in Group II it seemed to be of interest to compare the values obtained for them with the heat of formation of a Group I telluride. Silver telluride was selected for this comparison. In the course of the work it was also possible to determine the heat of formation of tin telluride and therefore to make a comparison of some of the Group I, 11, and lV tellurides with the metallic elements silver, cadmium, and tin being in the same period. There is also a great deal of interest in the energetic changes which occur upon addition of solute elements to a common solvent. This investigation provided an opportunity to study the partial molar heats of solution of silver, cadmium, tellurium, and zinc in liquid tin. The partial molar heats of solution are of theoretical interest because solute-solute interactions are a minimum in dilute solutions and application of solution models is simpli- fied. In order to complete the analysis of solute-solute and solute-solvent interactions the temperature dependence of the partial molar heats of solution was also measured. MATERIALS AND EXPERIMENTAL PROCEDURE All materials were of the highest purity available. The silver, zinc, cadmium, and tellurium were obtained from American Smelting and Refining Co. and were reported to be 99.999 pct pure. The silver telluride, zinc telluride, and cadmium telluride were obtained from Atomergic Chemetals Co., a division of Gallard-Schlesinger Chemical Manufacturing Corp., and were electronic-grade material of 99.999 pct purity. Tin used for the solvent bath and for calibration was obtained from the Vulcan Manufacturing Co. and was reported as being 99.99 pct pure. The liquid-tin solution calorimeter used in this work is similar in principle to the differential twin-type calorimeter described by K1eppa.l Two of three identical calorimeter wells are used together during any set of experiments, one well being active and the other being passive. The wells are positioned 120 deg apart in an aluminum calorimeter block. Each well contains a multijunction thermopile and a Pyrex test tube to hold the liquid metal bath. Forty-eight of the thermopile junctions are distributed over the surface of each calorimeter well adjacent to the test tube and serve to integrate the heat effects occurring. The other forty-eight are next to the aluminum calorimeter block. The thermopiles for the three wells are connected differentially so that any change in temperature at the outer junctions (which will be the same for both wells because of the high conductivity of the aluminum block) will oppose for the two wells and result in no shift of the zero. The electrical output represents the true temperature difference between the two reaction vessels. A reaction occurring in the active well gives a comparison with another body of very similar thermal properties. In this way, any spurious heat effects due to slight temperature drifts within the entire calorimeter block are eliminated. The output of the differential thermopile goes to a dc amplifier with multiple ranges of from * 10 pv to 1 30 mv. The output of the amplifier is then fed into a Leeds and Northrup strip-chart recorder. The adiabatic temperature change is then calculated using the technique of Howlett, Leach, Ticknor, and ever.' The aluminum calorimeter block is contained in a cylindrical furnace with main and control heaters

Jan 1, 1965

By J. W. Clark, C. T. Sims

Wrought chromium-base alloys containing yttrium, cubic monocarbides of the Ti(Zr)C type, and similay alloys containing manganese and rhenium have been melted and fabricated. Strength has been studied by hot hardness and elevated-temperature tensile and rupture measurements, low-temperature ductility by tensile testing, and surface stability by oxidation testing. In additiod, studies have been conducted of the carbide stability, and of aging behavior. The carbide dispersion generates effective elevated-temperature strength, which is further enhanced hv strain-induced precipitation. The dispersion exhibits classical dissolution and aging response. The ductile-to-brittle transition temperature of these alloys is above room temperature. The alloys reported show fairly good oxidation resistance, but nitrogen contamination can cause fortnation of a hard Cr2N layer under the oxide scale. Manganese does not appear to be a promising alloying element in chromium. In the years 1945 to 1950, the metal chromium was considered as a possible base for alloy systems due to its considerably higher melting point than superalloys, its low density, its high thermal conductivity, and its apparent capacity for strengthening. However, this interest in chromium was short-lived. It was found difficult to melt and cast, to be exceptionally sensitive to the effect of minor imperfections, to have a lack of ductility at both room and elevated temperatures, and to be subject to a deleterious effect of alloying elements upon the ductile-to-brittle transition temperature.' Since then, chromium, as a practical alloy base, has remained virtually unstudied. Further, purposeful ignoring of chromium has been promoted by statements that its bcc structure would not allow it to be strengthened to useful values, when compared to the "austenitic" alloys.2 Recently, a new look has been taken at chromium-base alloy systems. Study of the literature will show that chromium, providing some of its disadvantages could be eliminated or minimized, actually has a rather attractive potential as an alloy-system base. Analysis of rather scattered data suggests that chromium is quite capable of being strengthened to high levels. Also, significant strengthening of its two sister elements in Group VI-A, molybdenum and tungsten, has been demonstrated in a number of commercial and exploratory alloys. Chromium should be similar. Since chromium does not readily form a volatile oxide like tungsten or molybdenum, it offers a much higher probability of giving birth to alloy systems with useful oxidation resistance. Concerns about possible high elemental vapor pressure have been mitigated by recent data.3 In addition, the physical properties exhibited by chromium are attractive for application as a high-temperature structural material. For instance, its thermal conductivity varies from 49 to 36 Btu-ft/hr-sq ft-°F over its range of usefulness (which is two to four times higher than most superalloys), its density is about 7.2 g per cc (20 pct less than most nickel-base alloys), its coefficient of thermal expansion varies from 4 to 8 x 10-6 per OF, and it has a relatively high modulus of elasticity, approximately 42 x 10' psi.4 Alloying studies on a chromium base in the past have usually encompassed rather sweeping solid-solution alloy additions for strengthening. This is not consistent with contemporary alloying practice in Group VI-A. For instance, molybdenum, also in Group VI-A, is primarily alloyed for strength improvement by use of heat-treatable carbide dispersions.5 Chromium and molybdenum are similar in their chemical activity and other properties. Thus, strengthening of chromium by carbide dispersions was studied. Chromium-base alloys are plagued with room-temperature brittleness, although high-purity unal-loyed chromium can be made ductile.4,8 Use of yttrium as a scavenger has done much to improve ductility and resistance to nitrogen embrittlement in chromium systems,7 so it was utilized in this program. It has also recently been found8 that small rhenium additions (1 to 5 pct) create improvement in the ductility of Type 218 tungsten wire. This is apparently related to the remarkable effect of rhenium additions near its terminal solid solubility in all Group VI-A metals.9'10 Investigation to establish if dilute concentrations of rhenium would also be effective in chromium appeared to be logical for this program. Since rhenium is too expensive to be practical in alloys for application as structural components, ductility improvements through solid-solution alloying were also sought by substitution of manganese for rhenium; manganese, like rhenium, exists in Group VII of the periodic system. The optimum amount of carbide dispersion for chromium-base alloys was obtained by analogy with molybdenum. Strengthening in molybdenum is achieved by use of Ti-Zr carbide dispersions. A

Jan 1, 1964

By W. Crafts, J. L. Lamont

Electrolytic extraction of carbides from quenched and tempered steel and their examination under the electron microscope were found to be helpful in understanding the mechanism of secondary hardening in alloy steels1 and the same technique has been applied to isothermally transformed steels. A preliminary survey of the utility of the method has indicated that it has promising possibilities for investigating the characteristics of pearlite and bainite. The examination of a few carbon and chromium steels has suggested that pearlite is formed with carbides of two varieties representing the lamellar and nonlamellar forms and that bainite appears to form with a structure analogous to, but significantly different from, martensite. Procedure The method used for examining the carbides was similar to that described previously.1 The chromium steels used in the investigation were made from an Armco iron base in an induction furnace and were not treated with grain-refining deoxidizers. The composition of the steels is given in Table 1. Three-inch square ingots were forged and rolled to 1/8-in. thick sheet for use in the isothermal studies. After rolling, the sheets were sandblasted to remove the rolling scale. Specimens approximately 3/4-in. wide and l1/2-in. long were prepared from the 1/8-in. sheet. They were heated in a salt "bath at 2100°F (1150°C) for 1/2 hour, transferred to other salt baths at 1300°F (704°C), 1000°F (538°C), 800°F (426°C), or 600°F (315°C), held for various periods up to 100 hr and finally quenched in water. After quenching, the specimens were cut in half, one half being submitted to microscopic examination and the other half being used for the electrolytic extraction. The isothermally transformed specimens were submitted to examination under the light microscope to determine the degree of transformation and type of structure and were photographed at 2000 X. Carbide residues were obtained by electrolyzing in 10 pet hydrochloric acid and collecting the residue in glycerine to minimize attack by the acid. As pointed out in the earlier paper, the carbides are attacked to some degree during electrolysis. This attack is relatively minor on the coarser carbides but may be quite severe on the fine bainitic carbides. The residues were washed free of the glycerine with water and alcohol. The alcohol was removed by repeated washings of amyl acetate, and the amyl acetate suspensions were transferred to stoppered vials. Debye-Sherrer X ray diffraction patterns of the residues were prepared using a chromium target. A selection based on the microstructure and X ray data was then made of samples considered most illustrative of the progress of transformation. Electrolytically extracted residues from these samples were submitted to examination by W. D. Forgeng and A. C. Jenkins on the electron microscope at the Research Laboratories of The Linde Air Products Co. and electron micrographs were made at X 5000 and enlarged to 25,000 X. The micrographs obtained with both the light and the electron microscopes are mounted side by side in the accompanying figures. Although no effort was made to establish the T-T-T diagram for the chromium steels, the times for holding in the salt bath were adjusted with the intention of making the samples represent different stages in the transformation at temperatures of 600, 800, 1000, and 1300°F. The degrees of transformation and results of X ray examination are shown in Tables 2—4. The carbide designations refer to orthorhombic or trigonal carbide types and are not meant to imply that the compositions are exactly as indicated. X ray Diffraction Data The occurrence of Fe3C and Cr7C3 in these steels was found to be consistent with published data on comparable chromium steels. Steels A and B with relatively low ratios of carbon to chromium contained Cr7C3 in the pearlitic structures and FeuC in the

Jan 1, 1950

By J. L. Lamon, W. Crafts

Study with the electron microscope of the carbides in vanadium-chromium-molybdenum steels after tempering up to 1000 hr at 600 teelsto 1400°F confirmed that alloy carbides are formed at the secondary hardening temperature by decomposition of the plate-like iron carbides. It was also demonstrated that vanadium carbide persists as much smaller particles than do chromium- or molybdenum-bearing carbides. Conditions conducive to the formation of fine vanadium carbides are indicated to be favorable for high temperature strength. IN order to determine the effects of long exposure at high temperatures on vanadium-bearing steels, a survey has been made of their hardness and carbide structure. The behavior of carbides in the tempering of martensite was studied by X ray diffraction and electron microscope examination of electrolytically extracted residues in greater detail than in an earlier investigation.' A group of steels with about 0.25 pct carbon and containing chromium up to 5 pct, molybdenum up to 1 pct, and vanadium up to 1 pct was either quenched or annealed and then tempered for peri- ods of up to 1000 hr at 600° to 1400°F. Their hardness after tempering agreed with the Hollomon and Jaffe2 relation of equivalency of time and temperature, and with the degree of secondary hardening predicted from composition. Further, the appearance of the carbides indicated that the time and temperature equivalency relation was also applicable to the degree of carbide development. The mechanism of the tempering of martensite was demonstrated more clearly than in the earlier study. It was confirmed that carbides develop from martensite as poorly defined plates of the Fe2C type carbide followed by thickening of the plates with a transition to Fe,C. Finally the plate structure deteriorates into a lacy mass from which alloy carbides emerge as chunky particles that grow slowly with further increase of tempering temperature. Vanadium carbide derived from tempered martensite was found in characteristically small particles that tended to grow very slowly. The addition of chromium or molybdenum to a steel with predominant vanadium carbide tended to introduce carbides of a chromium- or molybdenum-bearing type having a somewhat larger particle size. The Cr,C, type carbide particles were larger than those of the V,C, type and somewhat smaller than the carbides in steel containing both Cr,C and M,C. Similar observations were made of the carbides in the pear lite of annealed steels. It appeared that high temperature properties would be benefited by the retention of the fine carbide particles that result from a balance of composition and heat-treatment designed to produce a maximum amount of vanadium carbide. Procedure: The steels used in the investigation were made with a base of Armco iron in a high-frequency furnace at the Union Carbide and Carbon Research Labs., Inc. The steels were deoxidized

Jan 1, 1951

By J. L. Lamon, W. Crafts

P. Coheur and L. Habraken—We read this paper with great interest and are glad to congratulate the authors for their valuable work, supplying an important contribution to the mechanism of tempering on the carbides in vanadium steels. We are in a good position to appreciate this work since we have been studying, for more than a year, Cr-Mo steels of a composition similar, but less highly alloyed (namely 0.1 pct C, 3 pct Cr, 1 pct Mo). Our results are quite in concordance with the authors', however, we wish to point out that it is very interesting to use equally the electron microscope in order to observe the variations of microstructure in steels. We have studied simultaneouslv the evolution of the carbides in situ with the electron microscope, and, after extraction, again with the electron microscope, and then with X-rays. The first results which we have obtained have been communicated at the Congress of Delft (July 1949) and at the "Journbes de la Metallurgie" in Paris (October 1949). These may be summarized as follows: After tempering with varying either the tempering temperatures or the tempering times, the carbides show two evolutions. The first one is connected to the carbides existing in the steels, principally in the boundaries of the grains. For some groups of steels these carbides may coalesce and for other groups they may

Jan 1, 1951

By L. C. Brown, J. S. Kirkaldy

Measurements have been made of carbon diffuswn in the five ternary austenites Fe-C-Si, Fe-C-Ni, Fe-C-Co, Fe-C-Mn, and Fe-C-Cr in which the carbon (component 1) diffuses through interstitial sites and the ternary addition (component 2) diffuses substitutionally. Values of the diffusion-coefficient ratio, D12/D11 were determined for each system with finite couples using the transient equilibrium method. The effect of temperature and of concentrations of both the carbon and substitutional component upon D12/D was examined and was found to agree with the theoretical predictions. It is concluded that within an experimental uncertainty of 10 to 15 pct, it is possible to calculate the ratio D12/D11 from purely thermody-namic data. Difficulties of measuring the other off-diagonal coefficient, 4,, are discussed. Any quantitative attack on the fundamentals of the hardenability problem in steel must begin with the multicomponent diffusion formalism and with the accumulation of data pertaining thereto. In a recent paper Kirkaldy and purdy 1 employed the formalism derived from irreversible thermodynamics to treat the problem of diffusion in ternary austenites. In the latter solutions, carbon diffuses through interstitial sites and the substitutional component diffuses through the lattice. Examples were given of diffusion in the systems Fe-Mn-C and Fe-Si-C. In the present paper, we present new results on and discuss their agreement with the thermody-namic theory. Since the theory has been slightly modified from the original presentation of Kirkaldy and Purdy, their results on Fe-Si-C and Fe-Mn-C have been recalculated and are presented here for completeness. The flux of the interstitial component with respect to a fixed lattice framework can be written as a linear expansion in the independent concentration gradients, where X1 and X2 are the independent thermody-namic forces in the lattice fixed frame of reference. These forces can be obtained from the general statement for forces in a volume fixed frame2 if the partial molar volume of carbon atoms is set equal to zero and that of the substitutional component 2 is set equal to unity, viz where the are the chemical potentials and the N's are mole fractions. Introducing into [3] and [4] the function If, as suggested by statistical arguments, the off-diagonal interaction L12 is sufficiently small, [6] reduces to i.e., the coefficient ratio becomes purely thermo-dynamic. The activity of components 1 and 2 in a dilute ternary system (standard state at infinite dilution) may be represented by the expansion3

Jan 1, 1964

By G. W. P. Rengstorff, R. B. Fischer

A study was made of the effect of impurities on the bend ductility of cast molybdenum. High purity molybdenum was repared by re-melting under high vacuum. The ductility of "transverse-grain" specimens indicated that intergranular brittleness decreased with an increase in purity of the metal. THE production of as-cast molybdenum with high ductility at room temperature would make working of the metal easier and increase the usefulness of the as-cast metal. Furthermore, a .knowledge of the factors that influence the ductility of as-cast molybdenum might be applied to the problem of making fusion weldments having satisfactory room-temperature ductility. Individual grains of commercial as-cast molybdenum are slightly ductile at room temperature. However, the presence of carbides at the grain boundaries may cause the metal to fracture in a brittle manner. This behavior has been discussed.' The amount and distribution of the impurities in as-cast molybdenum would be expected, from previous research on the metal, to have considerable influence on its ductility. Some effects of oxygen and carbon on the mechanical behavior of the metal were discussed by Parke and Ham,2 Woodside,3 and Zappfe. Landgraf, and Worden.4 Parke and Ham2 found that, if a sufficient number of molybdenum oxide particles were present at the grain boundaries, the intergranular cohesion was reduced to the extent that arc-melted molybdenum would rupture intergranularly during hot forging. They also found that if the oxygen content was less than 0.003 pct, the cast molybdenum was hot forgeable. It is suspected, however, that forgeable molybdenum may contain a small amount of oxide that could reduce the ductility of the as-cast metal at room temperature. Also, there is the possibility of the unfavorable distribution of other impurities having a detrimental effect on the ductility of cast molybdenum. The results of a study of the influence of purity on the room-temperature ductility of cast molybdenum are presented here. Vacuum Arc-Melting to Produce High Purity Mo One way of determining the effect of impurities on the ductility of molybdenum is to prepare and test metal as free of all impurities as possible. Accordingly, the present investigation was undertaken with this in view. Arc melting in high vacuum (less than 0.1 micron of mercury) was chosen as the method for reducing the impurities below the concentrations occurring in commercial molybdenum. Commercial arc melting of molybdenum is carried out at about 50 microns pressure. During the arc melting, carbon and oxygen in the metal react to form carbon monoxide. By virtue of the vacuum process, the partial pressure of carbon monoxide is maintained at such a low value that the reaction greatly lowers oxygen and carbon contents. An excess of at least 0.03 pct C is used in commercial arc melting to insure that the oxygen content will be below 0.003 pct. The excess carbon remaining after the deoxidation step forms carbides on freezing. Some of the carbides precipitate at the grain boundaries and, as will be shown, have an unfavorable effect on the room-temperature ductility. In the present work, only the small amount of carbon (0.003 pct) contained in the commercial powder-metallurgy molybdenum used for melting stock was present. Partial removal of oxygen from the melt probably occurred as the result of the volatilization of molybdenum oxides, or by distillation of oxygen at the high melting tem-

Jan 1, 1953

By John C. Sawyer

A brief review is given to show that catastrophic oxidation of stainless steel in the presence of lead oxide is similar in many respects to catastrophic oxidation as caused by MoO3 and V2O5, Experimental data are presented to show that lead oxide accelerates the normal oxidation process of stainless steel by chemically altering the normally protective oxide film formed on the base metal. Data are given to show that similar reactions occur during oxidation of stainless steel in the presence of MOO3,and V2O5. THE mechanism by which pure metals oxidize at high temperatures has been the subject of intensive research for many years and much has been accomplished towards understanding the processes involved. The mechanisms by which alloys oxidize have also been investigated, but due partly to the fewer number of investigations and partly to the complexity of the oxide systems present, available knowledge is not as extensive as with pure metals. When oxidation processes are further complicated by atmospheres contaminated with sulfide, halide, or oxide vapors, the knowledge of fundamentals becomes meager or altogether lacking. Thus, it is not surprising to find that the catastrophic oxidation of stainless steels in metal oxide vapors of MOO, and V2O5 is not a well understood phenomenon despite the fact that a number of investigations have been undertaken. The literature in dealing with the subject of catastrophic oxidation is primarily concerned with the effects of MOO3 and V2O5, but does mention that other metal oxide vapors, one of which is lead oxide, appear to promote a similar type of accelerated oxidation. While this latter effect is virtually unknown, the deleterious effect of lead oxide is of considerable commercial importance, as it is believed to be one of the fundamental reasons for exhaust-valve failure in gasoline engines. For this reason studies have been in progress for many years attempting to better understand the mechanism involved. Modern exhaust-valve alloys"2containing 20 to 25 pct Cr plus nickel and/or manganese are in effect high-grade austenitic stainless steels exhibiting ex- cellent oxidation resistance in air at exhaust valve operating temperatures of 1100° to 1700°F; yet these same alloys are prone to corrode during engine service because of the conditions attending their operation. These conditions are such that the valves become coated with deposits of complex lead compounds mainly derived from gasoline additives of tetraethyllead, ethylene dibromide, and ethylene dichloride. Literature searches3-7 and discussions with various investigators show that considerable difference of opinion exists as to the nature of the lead-bearing deposits found on the surface of exhaust valves and the atmospheres to which they are subjected; yet, all seem to generally agree that corrosion, a gradual transformation of alloy to nonmetallic products of corrosion, is a consequence of the presence of lead compounds. This majority opinion seems to be substantiated by laboratory engine tests which show that corrosion does not occur to any appreciable extent when lead-free fuels are used. The first observations of catastrophic oxidation reported in the literature were probably made by pfeil,8 but it was Leslie and Fontana9 who undertook the first detailed study of the phenomenon. Their work was chiefly centered on the acceleration of oxidation which took place when stainless steels containing more than 3 pct Mo were heated in air with restricted circulation. These investigators reported that the presence of other oxides near the surface would further accelerate the rapid oxidation which occurred. While they recognized that the effect was attributable to the presence of molybdenum, it was Rathenau and Meijering" who emphasized the fact that the presence of molybdenum in the alloy was incidental to the presence of MOO3 vapor in the atmosphere surrounding the specimens. Evans,11 as well as Cunningham and Brasunas 12 studied similar

Jan 1, 1962

By A. E. Gorum, J. Washburn, E. R. Parker

Experimental evidence was obtained in support of the idea that cleavage fracture can be initiated by dislocation pile-up. The high ductility of MgO crystals when tested in bending comPared to their relative brittleness in tension was explained on the basis that large pile-ups are more likely in a tension specimen. CLEAVAGE fractures have been a problem of major concern for many years. A number of large steel structures have failed in a brittle manner, usually suddenly and without warning; often the failures occurred for no obvious reason and at nominal stress levels well within the generally accepted range. A great deal of data have been collected about factors that contribute to failures,1 but the physics of the fracture process has never been revealed. cottrel12 has recently developed a theory of brittle fracture in ductile materials which was based upon the concept that dislocations moving on two intersecting planes can unite to form a crack nucleus. This theory accounts for the known effect of grain size and for the effect of testing temperature. There has, as yet, been no experimental evidence published that would substantiate this or the earlier theories based on stress concentrations due to piled-up dislocations. The study reported herein was conducted to obtain information that would either substantiate or disprove the

Jan 1, 1960

By B. Tani, K. Anderson, I. Johnson, R. Schablaske

INVESTIGATION of the various rare earth-cadmium binary systems discloses the existence of a compound corresponding to the composition MCd6 in all systems save the La-Cd system. Lattice constants for all of the MCde compounds, except LaCd6 which apparently does not form, and PmCd6 whose synthesis was not attempted, are also recorded herein. Iandelli and Ferro 1 report the existence of the compound CeCd6. No additional information, structural details, and so forth are given. Elliott and Lemons2,3' have measured the vapor pressure of cadmium over CeCd6 and have calculated the activity of cadmium in solid CeCd6. These authors find that CeCd6 exists over a composition range from 5.967 to 6.098 (Cd:Ce ratio) at 584oC, and from 5.971 to 6.118 at 639°C. The following is an excerpt from the paper by Elliott and Lemons: 2 "Recently Mr. F. H. Ellinger of this laboratory has indexed an X-ray diffraction powder pattern of CeCd6.00 which we had prepared by gas phase reaction. The compound has a primitive cubic unit cell with a = 15.783 + 0.001A Based on the volume of the cubes surrounding an elemental cerium or an elemental cadmium atom, Mr. Ellinger finds room for 24.10 CeCd6 formula units in the CeCd6 unit cell; similar calculations based on CeCd2 and CeCd11 yield 24.18 formula units per unit cell. The presence of 24 CeCd6 units per unit cell seems probable with an X-ray density of 8.255 grams per cubic centimeter. The most one can say about in-terstitial~ is that there appears to be room in the crystal even at room temperature." Measurements of the solubility of the rare earths in liquid cadmium4 led to the discovery of GdCd6,

Jan 1, 1964

By G. R. Speich

A cellular precipitation reaction in which cells consisting of an Ni3Ti (DO24) phase and austenite are formed has been studied in an austenitic Fe-30 Ni-6 Ti alloy. The variation of the growth rate and interlamellar spacing of the Ni3Ti cells with temperature has been determined m the range 400" to 975°C; the interlamellar spacing is proportional to the degree of undercooling; the growth rate can be expressed by an equation of the form G = K?T)2 exp(-Q/RT). The habit of the Ni3Ti lamellae is (001)Ni3Ti (111)y;[010]Ni3T2 [010]y. An almost perfectly coherent interface is formed between Ni3Ti lamellae with this orientation rela -tionship and the intervening austenite. This first Ni3Ti cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. CELLULAR precipitation reactions have been studied in copper-base,1,2 Au-Ni,3 pb-sn,4 and iron-base ferritic5,6 solid solutions, and this mode of precipitation has been treated theoretically by smith," Turnbull,8,9 cahn,10 and more recently by bohm.11 In the case of substitutional austenitic iron-base alloys little or no data are available, Cellular precipitation reactions are well known in austenitic nickel-base alloys12,13 but usually these reactions do not proceed to completion because of general precipitation occurring in the matrix, and they have not been studied in detail. Precipitation from an austenitic Fe-30 Ni-6 Ti alloy was studied as part of a larger investigation of the mechanisms of precipitation from substitutional iron-base alloys. This alloy, austenitic at high temperatures, decomposes at lower temperatures by a double cellular precipitation reaction. The first decomposition product consists of alternate lamellae of an Ni3Ti(DO24) phase and austenite. The reaction proceeds to completion, consuming all of the original austenite. This first cellular product is subsequently consumed by a second cellular reaction of much coarser spacing. The first cellular reaction was studied in detail by light and electron microscopy, hardness measurements, and by X-ray and electron diffraction. Interlamellar spacings and growth rates were measured during isothermal aging in the range 400" to 975°C. The orientation relationship between the Ni3Ti and austenite lamellae was determined and indicates that an almost perfectly coherent interface exists between the two phases. This first Ni3Ti cellular reaction is of particular interest because it occurs over such a wide temperature interval. This allows cellular growth rates and interlamellar spacing data to be obtained for much larger degrees of undercooling than reported hitherto. MATERIALS AND EXPERIMENTAL PROCEDURE The Fe-30 Ni-6 Ti alloy was prepared from electrolytic iron, Mond nickel shot, and sponge-purity titanium* by vacuum melting in a zirconia crucible

Jan 1, 1963

By V. Damiano, M. Herman

CELLULAR substructure observed in metal crystals grown from the melt. has been studied extensively'-' and is attributed to the existence of a constitutionally supercooled zone in the liquid ahead of the solidifying interface. The mathematical description of this process has been given in terms of the concentration of solute in the liquid phase, the rate of solidification, and the temperature gradien.t in the liquid as the only variables.5 This technical note presents some evidence of 1) the effect of crystal orientation on some aspects of cellular growth, and 2:) the degeneracy of these cells into dislocation arrays. The zinc single crystals used in these studies were alloyed with cadmium sufficient to produce the constitutional supercooled cellular substructure. Crystals containing 0.05 pct Cd exhibited substructure formation for a growth rate of 10 cm per hr and a temperature gradient of 15°C per cm in accord with the theory. The growing liquid-solid interface was examined after we liquid had been decanted away in a fashion similar to that described by Rutter and Chamers.' The cellular substructure was also observed after polishing and etching the surface directly behind the decanted interface with a solution of HNO, and water. Fig. 1 is a photomicrograph of a typical polished and etched surface revealing substructure, the cleavage plane, and twins. The crystal has been grown with its basal plane parallel to the direction of growth and the plane of the micrograph is per-

Jan 1, 1960

By E. N. Smith, J. C. Redmond

The increasing need for materials capable of withstanding higher operating temperatures for various applications such as gas turbine blading and other parts, rocket nozzles, and many industrial applications, has brought consideration of cemented carbide compositions. The well known usefulness of cemented carbides as tool materials is attributable to their ability to retain their strength and hardness at much higher temperatures than even complex alloys. However, it has been found that the temperatures encountered in cutting operations do not approach by several hundred degrees1 those involved in the applications mentioned above where the interest is in materials possessing strength and resistance to oxidation at temperatures of 1800°F and above. At these latter temperatures, the tool type compositions which are made up essentially of tungsten carbide are found to oxidize very rapidly and to produce oxidation products of a character which offer no protection to the remaining body. As a further consideration, the density of the tungsten carbide type compositions is high, from about 8.0 to 15.0. The refractory metal carbides as a class are the highest melting materials known as shown by Table 1 which summarizes the available data from the literature for the carbides of the elements which are sufficiently available for consideration for these uses. The density is also included in the table, since as mentioned above it is an important consideration in many of the applications for which the materials would be considered. It has been established that in the tool compositions the mechanism of sintering with cobalt is such as to result in a continuous carbide skeleton and that the properties of the sintered composition are thus essen- tially those of the carbide.2 On the hypothesis that this mechanism holds to a greater or less degree in cementing most of the refractory metal carbides with an auxiliary metal, it appears from Table 1 that titanium carbide compositions would offer possibilities for a high temperature material. Titanium carbide has extensive use for supplementing the properties of tungsten carbide in tool compositions. Although the literature contains several references to compositions containing only titanium carbide with an auxiliary metal,3,4,5,6 it may be inferred from the meager data that such compositions were deficient in strength and were considered to have poor oxidation resistance.7 Kieffer, for instance, reports the transverse rupture strength of a hot pressed TiC composition at 100,000 psi as compared to up to 350,000 psi for WC compositions. The work described herein was undertaken to determine the properties of compositions consisting of titanium carbide and an auxiliary metal and to improve the oxidation resistance of such compositions. It appeared possible that the inclusion of one or more other carbides with titanium carbide might improve the oxidation resistance and also that this might be more desirable than other means from the point of view of maintaining the highest possible softening point. Consideration of the available carbides in Table 1 suggests tantalum and columbium carbides because of their high melting points and general refractoriness. The work on improving oxidation resistance was concentrated on the addition of tantalum carbide or mixtures of tantalum and columbium carbide. The auxiliary metals used included cobalt, nickel and iron. It was also desired to learn the general physical properties of these compositions. Experimental Procedure The compositions used in this study were made by the usual powder metallurgy procedure applicable to cemented tungsten carbide compositions. The powdered carbide or carbides and auxiliary metal were milled together out of contact with air. In some cases cemented tungsten carbide balls and in other instances steel balls were used to eliminate any effect of tungsten carbide contamination. A temporary binder, paraffin, was then included in the mix and slugs or ingots were pressed with care to obtain as uniform pressing as possible. The ingots were presintered and the various shapes of test specimens were formed by machining, making the proper allowance for shrinkage during sintering. Thereafter the shapes were sintered in vacuum at temperatures of from 2800 to 3500°F. Final grinding to size was carried out by diamond wheels under coolant. The titanium carbide used contained a minimum of 19.50 pet total carbon and a total of 0.50 pet metallic impurities as indicated by chemical and spectrographic analysis. It was found by X ray diffraction examination with

Jan 1, 1950

By J. B. Clark, F. N. Rhines

brittlement or notch sensitivity progressively increases. Further, in contrast to results obtained with the impact test, the notch strength for the large specimens does not reveal a 500°F embrittlement range. The notch sensitivity as determined with the 0.3-in. specimen of 4340 steel given the stepped austenitizing treatment has been discussed elsewhere. This quantity as measured for the 1.1-in.- diam notch tensile test and given in Fig. 3, is taken to signify that reduced notch sensitivity is encountered in the 600" to 800°F tempering range for specimens given the stepped austenitizing treatment. The stepped austenitizing treatment may, there- fore, be of use in promoting deeper hardenability for a 4340 steel while at the same time giving reduced notch sensitivity in the high-strength range in which this steel is now being used. Acknowledgments The work reported was supported by the U. S. Navy Bureau of Aeronautics. The authors are indebted to the Bureau of Aeronautics for granting permission to publish results of this research and to N. E. Promisel, H. Hessing, and J. Maltz for their interest.

Jan 1, 1958

By M. N. Shetty, A. C. D. Chaklader

RECENTLY, it has been demonstrated that a considerable densification and interparticle bonding can be achieved if a pressure is applied to a powder compact while the material of the compact is undergoing either a decomposition reaction' or a polymorphic transformation.' The term "reactive hot pressing" has been coined to identify this process in which a phase change is combined with pressure to achieve interparticle bonding. This process is based on a principle which postulates that there is an enhanced reactivity and mobility of the molecular species at the phase-transformation temperature and this effect is utilized for interparticle bonding in powder compacts. This note summarizes the results obtained in an attempt to utilize this technique to produce ceramic-metal composites. In this case, a decomposition reaction of a compound (which after decomposition yielded an oxide) was used to achieve interparticle bonding in ceramic-metal composites. The reactive hot pressing was carried out in a Phillips induction heating unit, using either a graphite or a high-temperature steel die which functioned as both the susceptor and the hot-pressing component. The die was heated to the desired temperature in a helium atmosphere. All cermets produced by this technique were based on alumina as the ceramic phase. Different metal phases such as iron, copper, and chromium were used to study the effect of varying the metal phase on the properties of the composite. a Mono-hydrate (Boehmite) was mixed with different proportions of metal powders (-325 mesh) in dry condition in a mortar and pestle. No special precautions were taken for proper mixing. The mixtures were then compacted into a cylindrical form having an approximate dimension of 1 cm in diameter and 1 cm in height. For this compaction an ordinary

Jan 1, 1965

By L. S. Birks

The bainite transformation in a 3.5 pct Ni-1.25 pct Cr steel was studied under various conditions of cooling and stress. Several characteristics may be specified: 1) transformation in the bainite region (925° to 575°F) is very little affected by the manner of cooling from the austenitizing temperature at 1600°F to 575°F)tothe upper limit of bainite transformation at 925°F; 2) starting time for the bainite transformation is the same order of magnitude for either isothermal transformation or continuous cooling, but the rate of transformation is somewhat greater for isothermal transformation; 3) tensile stress accelerates both isothermal and continuous cooling transformation, and 32,000 psi stress changes the form of the isothermal transformation diagram to correspond in appearance to the continuous cooling diagram; 4) transformation for nonlinear, continuous cooling may not be determined directly from the linear, continuous cooling transformation diagram, but may be predicted by assuming first that the fractional amount of austenite transformed in a given small temperature interval depends on the approximate linear cooling rate during that temperature interval and then by summing stepwise over the whole temperature range. IN a previous publication' an X-ray spectrometer was described with which the X-ray diffraction from a specimen could be observed continuously under controlled temperature and tensile stress. This instrument has now been applied to a study of the austenite-bainite transformation in a Ni-Cr steel for both isothermal and continuous cooling conditions, with and without stress. Certain characteristics of the transformation lead to a method of predicting the amount of transformation to be expected at a given temperature for any type of cooling curve. Material and Specimen Preparation The steel chosen for the investigation was a Ni-Cr steel having the composition in the following percentages: 0.30 C, 0.27 Mn, 0.019 P and S, 3.50 Ni, and 1.25 Cr. In order to fabricate specimens suitable for the X-ray spectrometer, a 1/4 in. plate was ground down to 0.060 in. and then cold rolled to about 0.035 in. Next it was heat treated by quenching in oil from 1650°F and tempering at 1200°F for 1 hr. Then it was etched in dilute nitric acid to reduce its thickness to 0.014 in. and cut into blanks in the shape of flat tensile specimens 3 1/4 Vi in. long, 7/16 in. wide, with a notch % in. long and 7/32 in. wide; see Fig. 1. X-Ray Technique Since the X-ray spectrometer has been described in detail elsewhere,' only a brief outline of the principles will be repeated here. A focusing, pow- der-diffraction arrangement' was used, as shown schematically in Fig. 1, and the specimen was mounted vertically in a vacuum furnace (not shown in the figure). The X-rays, moving in a horizontal plane, enter and leave the furnace through beryllium windows. As shown in the figure, X-rays diverging from the line source A are diffracted by the specimen B and converge at the detector slit C. The detector D and the slit C may be set at the proper angle in the horizontal plane to receive X-rays diffracted by either the face-centered phase (austenite) or the body-centered form (ferrite, bainite, martensite). The specimen is heated by electrical conduction between connectors E, and E,, and a Pt—Pt-10 pct Rh thermocouple spot-welded to the center of the notched region on the side away from the X-ray beam indicates the temperature continuously on a Brown recorder. Temperature control is exercised manually with a variable transformer on the input to E,-E,. Any desired time-temperature relationship is easily obtained by first drawing the desired curve on the temperature recorder chart and then adjusting the variable transformer during the run so that the thermocouple

Jan 1, 1957