By J. S. Kirkaldy, D. G. Fedak

The extra degree of freedonz introduced by a second independetzt concentration in a tenzary system gives rise to the possibility of unstable planar phase interfaces in semi-infinite diffision layer couples. Diffusion paths which pass continuously in and out of too-phase regions of the phase diagram but which are not coincident with tie-lines give rise to super saturated zones which may be either adjacent to or isolated from planar phase interfaces, with corresponding nonisolated or isolated precipitates. Nonisolated precipitates are equivalent to morphological development of the interface. Selected couples in the ternary systems Fe-Ni-Cr and Cu-Zn-Sn have been examined nzetallographically and ifz the latter case both isolated and uo~zisolated precipitates have been observed. The diffusion path in one of the couples showing interface morphological developtnent has been examitled using electron probe microanalysis. IGNORING the spurious effects of preferential grain boundary diffusion and anisotropic crystal growth7 it can be unequivocally stated that it is impossible for a binary isothermal diffusion couple constructed of two unsaturated phases to sustain a nonplanar phase interface. Consider for demonstrative purposes the schematic phase diagram of Fig. l(a). Given an initial flat phase interface, semi-infinite boundary conditions and the internal boundary condition fixed by the constitution diagram, xB = xB(T), the unique solution of the diffusion equation requires a persistent flat interface. No other solution is possible. If, however, we anticipate the involvement of surface tension, then the internal boundary condition must be written xB = xB (T,Y) where r is the radius of curvature of a hypothetical nonplanar interface. The introduction of a new parameter such as r can be equivalent to the release of an internal constraint, so that a stable nonplanar interface may be possible after all. Consider a perturbation to the interface as indicated in Fig. 1(b). According to the Ostwald-Freundlich equation: which is applicable to a system of this constitution, the solubility of A in the matrix ß ,xB (Y), at a point of curvature r is given by where Va is the molar volume of the a-phase, R is the gas constant, and a is the interfacial tension. Since the right hand side is positive, xB(r) >xB cm, as indicated in Figs. 1(a) and 1(c). Accordingly, the perturbation will carry the interface concentration in a direction which is opposite to that which would sustain local equilibrium. Such a perturbation is necessarily moderated and the system is returned to its initial condition. This result is general for all binary couples since we can regard an interfacial perturbation as an attempt to precipitate within un-

Jan 1, 1962

By H. R. Ogden

The notch sensitivity of titanium alloys is affected by impurity content, microstructure, and heat treatment. Using notch tensile properties to evaluate notch sensitivity, three commercial titanium-base alloys were investigated over the temperature range of -320o to 390°F. The alloys studied were Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo. Six interstitial levels were studied for each alloy in four mi-crostmctural conditions. The ff- 0 alloys were studied in both the annealed and heat-treated condition. All tests were conducted using 1/4-in. diam round tensile samples. The notched samples had a 50 pct notch with a notch sharpness (a/r) of 53, corresponding to Kt 6.3. Notch sensitivity was increased by increased interstitial content, low temperature, and acicular-type microstructures. The heat-treated, high-interstitial content - 13 alloys were more notch sensitive than the same alloys in the annealed condition. In addition, minima in the notch tensile-temperature curves were observed at temperatures near 32°F. These minima became more pronounced with increasing interstitial content. 1 HE increaseduse of titanium alloys in high strength applications at subzero temperatures requires that a better under standing of the low-temperature behavior of the alloys be obtained. At low temperatures, metals generally exhibit increased strength with lowered ductility and tohness. Notch sensitivity and the factors which influence it become more important as the strength level is increased and the temperature is decreased. Some of the factor s which affect notch sensitivity in ti- tanium alloys are composition, interstitial content, microstructure, and heat-treatment condition. In this paper, the results of a study of these variables on the notch sensitivity of three titanium alloys at temperatures from —320o to 390o are reported. The notch geometry selected for this program was chosen to provide a severe test of notch sensitivity. The ability of the metal to flow without initiating fracture under these severe conditions is reflected in the notch-strength values. Since notch strength is, in part, determined by the constraint exerted by the combined tensile stresses, the behavior of notch specimens reflects the properties of the material under combined stresses. For example, a material with a high notch-unnotch strength ratio may be expected to withstand the biaxial stresses encountered in a pressure vessel better than a material with a low ratio of notch-unnotch strengths. This implies that maximum strength alone is not a sufficient criterion for applications of this type. It further may be concluded that the various conditions that promote poor notch behavior also will affect adversely the performance of materials under combined stresses. In the alloys studied, these included low temperatures, high interstitial levels, and hasformed microstructures. EXPERIMENTAL PROCEDURES Three alloys, Ti-5Al-2.5Sn, Ti-6Al-4V, and Ti-2Fe-2Cr-2Mo, were purchased from commercial producers as 2-in.-dam rod stock. Oxygen and nitrogen were added to these alloys by remelting to obtain a variety of interstitial contents as shown in Table I. In order to Compensate for the much more potent strengthening effect of nitrogen compared with oxygen, an oxygen equivalent content is used to describe the total oxygen plus nitrogen contents studied. It has been suggested previously1 thatnitro-gen is approximately twice as effective in strengthening as oxygen, and carbon, to the extent it is in so-

Jan 1, 1962

By N. J. Feola, E. P. Klier

NOTCH properties of titanium materials have been extensively investigated in the impact test.'-" For the most part the impact strength meas- ured suggests a ductile-brittle transition that lies at relatively high temperatures, thus indicating a possible notch sensitive condition at ambient temperatures. Recently it has been shown' that the impact strength for unalloyed titanium, as for aluminum alloys, may be a nonsensitive index of notch sensitivity as provided by the notch strength as measured in the notch tensile test. The notch strength for unalloyed titanium was found to depend on the nitrogen and carbon contamination levels. In the present work the levels to which oxygen, nitrogen, and carbon contaminants can be tolerated without leading to excessive em-

Jan 1, 1958

By W. Hume-Rothery

RECENT interest has been shown in utilizing solid-state techniques for obtaining large oriented grains in the Alnico Alloys.1-4 Unfortunately, due to the inherent brittleness of these materials it is difficult to introduce sufficient imperfections by deformation to support the nucleation and growth of new, recrystallized grains. As a result, recrystal-lization methods for obtaining large grains, such as the strain-anneal technique, do not appear to be feasible. Steinort et a1.2 used a combination of a thermal gradient and internal strains to obtain large single crystals of Alnico 5 from a poly crystalline casting by annealing at temperatures above 1200°C. It was suggested that the strains were the result of the precipitation of the y phase which exists between -850° and 1200°C. The purpose of the present study was to determine if the grain size of the cast Alnico alloys can be markedly increased by solid state techniques involv-

Jan 1, 1963

By E. Parthe, J. P. Pemsler

TWO references can be found in the literature concerning the ternary system uranium-tantalum -carbon. C. H. Schramm, P. Gordon, and A. R. Kaufmam reported in this Journal1 on the existence of the ternary carbide "UTa10C4." They also report a second face-centered-cubic carbide phase in the system U-Ta-C, which they denote as "white" phase. The publication includes a reproduction of a Debye-Scherrer powder photograph of "UTa10C4" and a list of the sin2 0 values of this compound. H. Nowotny, R. Kieffer, F. Benesovsky, and E. Laube2 report the complete solid solubility between TaC and UC with a B1 structure. Since the ternary phase "UTa10C4" lies very close to the binary system Ta-C, and the established phase Ta2C with a C27 structure had not been mentioned by Schramm et al., it was thought worthwhile to compare the patterns of "UTa10C4" with Ta2C. The strong lines of the given pattern were indexed on a hexagonal unit cell with the approximate cell parameters a = 3.09A and c = 4.93A. These are the values reported for Ta2C in the literature.3 The correspondence between reported and calculated sin2 8 values may be studied in columns 4 and 5 of Table I. The agreement is fair, but there remain weak lines which cannot be assigned to the hexagonal unit cell. The extinctions correspond to those of Ta2C, but a comparison of the calculated and observed intensities of the Ta2C lines (columns 2 and 3) with those of the corresponding lines of "UTa10C4" (column 6) show occasional deviations. To clarify this situation, four new samples were prepared. The compositions of these samples were chosen in such a way as to observe any existing ternary phase in the system TaC-UC-U-Ta. The samples were arc melted in an inert atmosphere and annealed at 1100°C for 36 to 72 hr. Compositions of the samples determined by chemical analysis are given along with the results of X-ray investigations in Table 11. The following conclusions may be drawn from these data: a) No ternary compounds occur in the section TaC-UC-U-Ta of the ternary system Ta-U-C. The "white" phase reported by Schramm et al. corresponds to a solid solution between TaC and UC. Only one three-phase field exists: C27-B1-A2. (Both tantalum and ? uranium have body-centered-cubic A2 structures.) The a uranium observed in sample 4 transformed from the high-temperature ? phase on cooling. b) The phase Ta2C with a C27 structure extends into the ternary system. "UTa10C4" is, therefore, a uranium-enriched Ta2C. Good agreement is ob-

Jan 1, 1960

By D. N. Seidman

In the course of a study of the electronic and thermodynamic properties of Pb-Se alloys it was found necessary to have an accurate knowledge of the phase diagram. However, the literature is in disagreement as to whether or not a monotectic reaction occurs in the lead rich portion of the phase diagram. Pelabonl reported only a two-phase region consisting of lead-rich liquid and solid PbSe extending from almost pure lead to the compound PbSe, and gave the melting point of PbSe as 1065°C. The data of Friedrich and Leroux2 are in general agreement with this type of diagram, with the melting point of the compound being 1088°C. However, Nozato and Igaki by inverse rate thermal analysis observed a monotectic reaction isotherm exlacing at 860°C with a monotectic composition of 20.5 at. pct Se. The miscibility gap in the liquid state extends from 7.5 to 20.5 at. pct Se. Hansen and Anderko4 accepted Nozato and Igaki's phase diagram in the region of the lead-rich monotectic. To reinvestigate this portion of the phase diagram, both thermal analysis and metallographic examination of various compositions were performed. The thermal analysis apparatus was constructed according to the specifications of the National Bureau of Standards. A t/t-l pct Rh thermocouple was calibrated against the melting point of copper (NBS), zinc (NBS), and antimony (A. D. Mackay), the emf being measured with a Rubicon Type B potentiometer sensitive to lpv. The absolute accuracy of the thermal analysis obtainable with this system is ± 0.5oC. Starting materials were semiconductor grade lead and selenium purchased from the American Smelting and Refining Co. Both elements were 99.999 pct pure with only trace impurities detected upon spectroscopic examination. One hundred galloys were sealed in quartz crucibles with a central thermocouple well under a vacuum of less than 1 p. This procedure prevented any composition change due to vaporization during the run. Cooling curves were obtained on the alloys listed in Table I. Data was taken by the direct method at cooling rates ranging between 1/2 to 2°C per min. The alloys were heated well above the liquidus and shaken vigorously to insure homogeneity. No evidence of an arrest indicative of the monotectic reaction was observed, and the two-phase region reported by Pelabonl and Friedrich and Leroux? was confirmed in general, although our data give higher liquidus temperatures than Friedrich and Leroux. The melting point of stoichiomet-ric PbSe determined for two different samples was 1080.7 0.5oC. The results of this investigation are compared with Nozato and Igaki's data in Fig. 1. To Complement the thermal analysis data, an 86 at. pct Pb specimen was examined microscopically. This composition was in the center of the miscibility gap reported by Nozato and Igaki.3 The alloy was heated to 1000°C, held for 1/2 hr, and water quenched. The specimen was polished using standard metallographic techniques for lead. The alloy was etched with an acetic-nitric acid etchant for 10 min at 45°C. Microscopic examination did not indicate the existence of two separate layers or solidified droplets imbedded in a matrix, as would be expected if a miscibility gap were present. The mi-crostructure shown in Fig. 2 consists of uniformly dispersed, dendritic PbSe in a lead-rich matrix.

Jan 1, 1962

By D. I. Bardos, Paul A. Beck

A MARK, Boren, and westgrenl in their X-ray diffraction study of manganese alloys with 10 to 25 at. pct Si reported the occurrence of a phase with complex crystal structure in a Mn + 14.5 at. pct Si alloy after annealing at 800° or at 600°C. Recently Kuzma and Gladyshevskii2 identified Mn6Si as an R phase,3,4 the second binary R phase known. (A binary R phase was previously found in the Mn-Ti system by Waterstrat.5) A ternary R phase was reported earlier0 near the Mn-Si binary border of the Ti-Mn-Si system at 1000°C. In the light of the Russian work it now appears that this "ternary" R phase may be in fact an extension of the binary (Mn6Si)R phase. As already found by Amark, Boren, and Westgren, the corresponding binary phase is absent at 1000°C; the effect of titanium is evidently to stabilize it up to higher temperatures. In a recent paper Wieser and Forgeng7 gave the boundaries of this binary phase, which they referred to as 6. In order to re-examine the identity of this phase, an alloy of Mn + 14.5 at. pct Si was prepared by induction melting in helium atmosphere and annealed for 3 days at 800°C. The powder pattern, taken with an asymmetrical focusing camera of large dispersion and shown in Table I, was found to be that of the R phase, in agreement with the results of Kuzma and Gladyshevskii. For comparison, Table I also lists

Jan 1, 1965

By N. Albon, J. F. Miller, R. W. Coutant

The deposition of nickel from nickel carbonyl onto amorphous substrates has been studied, with attention being paid to the specific effects of the physical and chemical nature of the substrate and to the effect of oxygen on the crystal morphology. With substrates having microscratches or etch lines, nu-cleation was observed to occur preferentially at these surface features. Flame polishing of the substrate surfaces was found to remove any regularity in preferred nucleation sites. Nucleation was observed to occur less readily on substrates having relatively low surface energies, e.g., Teflon and carbon, than on materials having relatively high surface energies such as fused silica. At low oxygen concentrations [Ni(CO)4/O2 > 54 x 1031, apparently pure and well-formed nickel crystals were observed to nucleate and grow irrespective of the presence of oxygen. At higher concentrations of oxygen, a secondary growth process, dependent upon oxygen concentration and resulting in a gradual change in crystal morphology, was observed. It is concluded that the influence of oxygen on the nucleation and growth of nickel is determined by the relative kinetics of the various possible reactions, and that under the experimental conditions employed the 0-Ni interaction occurs at some nucleation or prenuclea-tion stage. THE purpose of the research on crystal nucleation in chemical vapor deposition as described in this paper has been twofold: 1) to examine some effects arising from the use of amorphous substrates, and 2) to study the specific effects of oxygen on the nucleation and growth of nickel in a nickel carbonyl-carbon monoxide system. The nickel-nickel carbonyl system was chosen for study for several reasons: 1) nickel films are of potential interest in electronic technology, and 2) the deposition can be carried out at moderate temperatures, thus making possible detailed study of the processes occurring and the use of a variety of substrate materials (including some which melt at relatively low temperatures). Fairly well-characterized chemical kinetics and a broad background of information are available on the py-rolysis reactions and on the mechanisms of Ni-O interactions. NUCLEATION AND GROWTH THEORY The theoretical background for the analysis of nucleation and growth by vapor deposition for a one-component system (physical vapor deposition) and the problems encountered therein have been reviewed by Hirth and pound.' More recently Mande12 has indicated the difficulties of applying such theory to chemical systems. One of the major problems involved is the possible multiplicity of chemical reactions and deposition routes. For example, those reactions which are probably of significance in a discussion of the pyrolytic deposition of nickel from nickel carbonyl under the conditions of the present experimental work are illustrated in Fig. 1. As is true with most cases of chemical deposition, many of the quantitative data necessary for a complete analysis of the system are either not available or not directly measurable. However, with the present system, sufficient data are available for a discussion of nucleation and growth on a qualitative basis. Classically, the rate of nucleation of a monatomic species being deposited from a vapor phase is given by

Jan 1, 1965

By V. B. Kurfman

Grain refinement of Mg-Al melts by carbonaceous additions has been attributed to nucleation by aluminum carbide. The effects of process and alloy variables are interpreted and predicted in terms of the dispersion and chemistry of this phase. The grain coarsening action of Be, Zr, Ti, R.E., chlorination, temperature extremes, and prolonged holding times is described. Measures necessary to insure an adequate dispersion of the catalyst are discussed. CARBON inoculation treatments have become fairly well known and used for grain refinement of magnesium alloys containing Al. Although there is general agreement that a nucleation process occurs, the process is not understood and the inoculants are used in a rather empirical fashion. The treatment is applied to the class of alloys containing 3 to 10 pct Al, i.e., AZ31A to AM100A. Typical methods involve melting, alloying, and adjusting the temperature to 1400° to 1450°F. Then 0.01 to 0.5 pct C as CaC2, C6C16, or lampblack is added by any convenient means, and the melt poured within 10 to 30 min. Investigators generally have been impressed by an assumed similarity of this refinement process to superheat grain refinement, which depends on heating approximately the same alloys to a temperature in the range of 1550" to 1650°F, then pouring promptly after the melt is cooled to the pouring temperature. Various predictions have been made that carbon refinement would replace superheating in commercial practice due to reduced process costs, but this replacement has not fully taken place because of production difficulties and conflicting observations. Davis, Eastwood, and DeHaven1 agree with Nelson2 and wood3 in suggesting that an excess of inoculant may be harmful. Wood however says that overtreat-ment is not a problem in production use of hexa-chlorobenzene inoculation, and Hultgren and Mitchell4 claim no evidence of harm from excess additions. Various grain coarsening reactions are known to occur, including the possibility of overtreatment mentioned above. Trace amounts of Be,2 Zr, and Ti may prevent refinement by either a carbon treatment or a superheat. Occasionally treatment with cl25 may cause coarsening, although the Battelle refinement process' uses a CC14-C12 blend. Grain coarsening also tends to occur on holding at temperatures below 1350°to 1400°F, especially after a superheat treatment, and for this reason Nelson2 stresses the desirability of a refinement method useful at lower temperatures for open pot melting practice. Since a carbon treatment can be made to work at temperatures below 1400°F, it seems desirable to investigate the mechanism of the refinement and the mechanisms of the coarsening reactions in order to establish control conditions for use in commercial production. The identity of the nucleating phase must first be established and then the factors affecting its chemistry and physical dispersion must be determined. THE IDENTITY OF THE NUCLEATING PHASE Davis, Eastwood, and DeHaven suggested that the nucleating phase in this system is Al4c3,1 but Mahoney, Tarr, and LeGrand8 disagree, largely because they found no evidence of the compound in alloys after carbon treatment and because there is no indication that aluminum carbide should be unstable over the temperature range used in the superheat treatment. This latter objection is based on the assumption that both the carbon treatment and the superheat treatment introduce the same nuclei. Electron diffraction studies have been made to identify the nucleating phase. Samples of grain refined A292 have been selectively etched SO that clean surfaces are obtained and so that secondary phases are in relief. Electron diffraction patterns from these surfaces have established that the carbon treatment of A292 introduces into the metal a large number of small, plate-like particles with a structure very similar to Al4C3. In most cases, the plate-like nature of the particles prevented positive identification but in the cases where the identification could be made the particles proved to be AIN A14C3. However, enough variation in lattice constants was observed so that all compositions from pure A14C3 to the 50:50 solid solution A1N.Al4C3 were probably present.14 In A14C3 and especially AlN.Al4C3 the A1 atoms occur in layers within which they have the same hexagonal symmetry and spacing as the Mg atoms in a single basal plane of a magnesium crystal. The solid solution spacing lies between the 3.16 of AIN and the 3.3? for Al4C3, in satisfactory agree-

Jan 1, 1962

By J. E. Harris

By elimination of other possible nucleation processes, it has been demonstrated, for commercially pure magnesium and a Mg-Al alloy, that at stresses less than that necessary for triple-point cracking creep cavities are most probably nucleated heterogeneously at second-phase particles. Evidence for the existence of such particles is presented and the role of grain boundary sliding in the nucleation process is examined quantitatively. DURING creep deformation of polycrystalline magnesium and its dilute alloys in the temperature range 0.45 to 0.7 Tm (Tm = absolute melting temperature) cavities form mainly along grain boundaries oriented normal to the stress axis and failure eventually occurs by their growth and impingement.' The possibility of low-ductility creep failure of magnesium-alloy reactor cans during service has prompted a number of studies of cavity formation in these materials.2-5 In this paper divergent theories of cavity nucleation6-10 are examined critically and conclusions drawn regarding the most probable mechanism of formation of cavities in magnesium. The paper is divided into two parts. The first section consists of the review and quantitative assessment of the possible role of grain boundary sliding in the nucleation process. In the second part an experimental program is described where an electron-microscope technique has been used to determine if second-phase particles exist in as-received commercially pure magnesium and in a magnesium alloy 1) THEORETICAL REVIEW Possible nucleation sites for creep cavities are: a) high-angle grain boundary triple points,11-14 b) subboundary/grain boundary intersections,15-18 c) ledges in the grain boundary, 19-25 d) second-phase particles. 9,26-30 Each of these possibilities is now considered with special reference to deformation of magnesium. 1.1) Triple-Point Cracking. The stroh31 condition to nucleate fracture is: " > vr [1] where ss = applied shear stress, ? = surface energy, C = shear modulus, L = length of sliding interface. This relationship is independent of the nature of the interface and it is possible to calculate the stress concentration at the end of a sliding high-angle grain boundary and thus deduce, approximately,* the minimum applied stress necessary to nucleate triple-point cracking. Such theoretical predictions for Nimonic alloys have been made by McLean13 and found to agree quite closely with the minimum stress determined by experiment. Stresses capable of nucleating triple-point cracking should also be sufficient to nucleate fracture at a grain boundary due to intragranular slip, for the lengths of sliding interface in the two cases are approximately equal. Thus the minimum stress for triple-point cracking should represent a demarcation between failure due to general "cracking" and that due to cavitation. Hauser, Landon, and Dorn32 have demonstrated that for polycrystalline magnesium in the temperature range 78° to 298°K the fracture stress is inversely proportional to the square root of the mean grain diameter. As pointed out by stroh31 this result indicates that Eq. [I] describes the fracture characteristics of magnesium at low temperatures. Heal3 has reported that for rapid deformation (112 pct hr-1) of polycrystalline magnesium the transition from cracking to cavitation occurs in the temperature range 175" to 275°C. He also presented the fracture-stress values for the same material tested under similar conditions. From Eq. [I] taking G = 1.3 x 10" dynes , ? = 600 ergs . cm-2,33 and L = 0.017 cm, a Stroh-McLean13,31 tensile stress of -266 kg. cm-2 is calculated, corresponding to a transition temperature of -190°C; this is in

Jan 1, 1965

By J. J. Gilman

IT is well established that dislocations exist in crystals and account for crystal plasticity.' However, the origins of the dislocations are not clear. Among the means by which dislocations might originate are: a) through crystal growth accidents, b) by the collapse of condensed sheets of vacancies, or c) by stress-induced nucleation. Theoretical calculations' have indicated that the last means should require very high stresses in order to operate. The purpose of this paper is to show that the stresses around the tips of cracks are large enough to nucleate large numbers of dislocation loops. Specifically, it will be shown that (100) cleavage cracks in LiF crystals nucleate dislocations in regions of the crystals where dislocations did not exist previously. It is believed that the use of LiF for this investigation does not restrict the significance of the 1 results. In fact, it is believed that this complements and extends previous papers by the same author which dealt with metal crystals.10,14 The dislocations were detected by means of the etching techniques that were described in a previous paper by Gilman and Johnston.3 In that paper it

Jan 1, 1958

By Stanley Rajnak, John E. Dorn

The saddle-point activation energy for the nu-cleation of a pair of kinks is estimated as a function of the applied stress, the lattice constants, and the height and shape of the Peierls' hill by employing the line-energy model of a dislocation. The kinetics of disloration motion by the Peierls' mechanism are discussed and the microscopic dislocation velocities and macroscopic strain rates are formulated by the Arrkenius type of approach in terms of the activation energy for the formation of pairs of PEIERLS was the first to illustrate that a straight-dislocation line has its lowest energy when it lies in a potential valley parallel to lines of closest packing kinks. The log of the dislocation velocity is found to be approximately proportional to the log of the local applied stress. It is also shown that the low-temperature mechmical properties of several bcc metals might be explained in terms of the Peierls mechanism, good agreement being obtained between theory and experiment for the flow stress us ternperature, activation energy vs stress, and activation volume us stress curves for these metals. of atoms on the slip plane. When such a straight dislocation is moved rigidly from one valley toward the next, the atoms in the vicinity of the core of the dislocation change their positions and bond angles, causing the energy of the dislocation to increase. Midway between two adjacent valleys, the disloca-tion energy reaches a maximum value and any additional small displacement will cause the dislocation to fall down the hill into the next valley. The maximum shear stress necessary to promote such

Jan 1, 1964

By L. Segle, R. Resnick

NUMEROUS experiments in the past few years have proven that void formation occurs quite generally in the diffusion zone of bimetal specimens1-4 The phenomenon has been explained in terms of the accumulation of lattice vacancies resulting from unequal diffusion of the constituents and their eventual precipitation as holes.= Attention has recently been directed to the fact that voids also form within homogeneous metals during high-temperature creep.' The idea has been put forward that these voids form by the condensation of excess lattice vacancies generated by intersecting dislocations.".' If the precipitation of lattice vacancies from solution is treated as a nucleation and growth process, the predicted vacancy concentration for homogeneous nucleation of voids at an observable rate is 100 to 1000 times the normal thermal equilibrium concentration. It appears that voids actually form during diffusion at vacancy supersaturations which are much lower than this8 According to the calculations of Machlin,' the same must be true for voids formed in homogeneous metals during creep, if these are considered to arise from the precipitation of lattice vacancies. Therefore, if the vacancy mechanism is valid, it seems that the holes which form in diffusion and creep specimens are heterogeneously nucleated by imperfections or impurities in the metal. Irregularities in the frequency and distribution of voids in diffusion couples bear out this explanation.' , It is not known at the present time what the nuclei are on which vacancies condense. Various investigators have speculated that they could be certain dislocation configurations, already existing voids produced during solidification or working, gas pockets, or inclusions in the metal. Relatedly, the precise value of the degree of vacancy supersatura-tion for void nucleation is still uncertain. An initial attempt to estimate this value from diffusion data, made by Balluffi, indicated that voids form in diffusion couples at vacancy concentrations which may

Jan 1, 1958

By C. G. Durdaller, W. H. Robinson, G. M. Pound

The nucleation rate of the a (pay) to 0 (white) tin transformation was measured as a function of temperature and a tin particle size using an X-ray diffraction technique. The powder specimens of a tin were essentially monodisperse and the small dinzension of the particles of these specimens was varied from 13 to 75 p. Several types of nucleation sites of differing potency were fbund to be operative in the nucleation process, but it could not be determined whether these sites were on the free surface of the tin particles or within the volume. Assuming that they were on the free surface, the average density of the most potent sites was calculated to be 2.5 to 5.3 x 10' sites per sq cnz through the application of a Poisson distribztion finction to the isothermal data. Analysis of the temperature dependence' of the rate constmts at a given fraction transformed suggests that the active sites are regions of higher free energy and not catalytic interfaces. Appreciable induction periods were observed at the lower temperatures of transformation. Experimental studies1 of solid-solid phase transformations have led to the belief that the new phase nucleates at structural imperfections. The purpose of the present work was to learn more about the mechanism of nucleation in solids and the nature of the singularities at which nucleation occurs. In this investigation nucleation rates in the isothermal transformation of gray to white tin were measured by an X-ray diffraction technique using essentially monodisperse powders of gray tin. This particular phase transformation was chosen for study because it presented fewer experimental difficulties than most others. The experimental temperature-control problems were minimal because the two phases coexist in equilibrium at 13.3"C, and measurable transformation rates occur at temperatures only slightly above room temperature. The growth rate of the P phase into the a2 is sufficiently fast to make the measured transformation rate equivalent to the nucleation rate, provided that the particle size of the samples is small enough; for the experimental temperatures used in this study, the particle diameter must be less than 100 p. EXPERIMENTAL TECHNIQUE The P tin used in this study was obtained from Capper Pass and Son Ltd., North Ferriby, Yorkshire, England, and was of 99.999 pct purity. It was transformedS to the a phase and ground into a fine powder in an agate mortar. This powder was separated by a Roller air classifier into seven fractions whose dimensions, as determined by microscopic measurement of many thousands of particles, are given in Table I and whose distribution of size within each fraction is given in Figs. 1 and 2. The shape of the particles was roughly that of an oblate spheroid,

Jan 1, 1964

By E. Hornbogen

The deformation mechanisms of a iron-phosphorus alloys were compared at 20oand —196°C. Alloying with phosphorus increases the resistance to slip, but has little effect on the resistance to twinning. The stress for onset of twinning is nearly independent of temperature, but there is an increasing tendency for cleavage along (112) twin boundaries with decreasing temperature and increasing phosphorus content. FIVE iron-phosphorus alloys and one high-purity iron (0.004 pct C, 0.004 pct N, 0.05 pct O) were vacuum melted and cast, then homogenized for 6 hr at 1100oC and water-quenched. Single crystals were cleaved from the coarse grains produced in this manner. The hardness was measured* on polished (100) surfaces of the crystals at 20" and -196°C. Laue back-reflection patterns indicated a deviation of not more than 3 deg from coincidence of the {100} plane with the surface. The deformation mechanisms were studied by relief effects on the polished surfaces. Yield points in compression (0.5 pct offset) were measured with polycrystalline material. At 20°C the addition of phosphorus to a iron leads to a change from slip to twinning as the main deformation mechanism, Figs. 1(a), (b). Between 2 and 4 at. pct P slip and twinning occur simultaneously. In alloys with more than 4 at. pct P twinning is the main deformation mechanism and slip was observed only in the neighborhood of twin intersections. All cracks at 20oC were on (100) planes, some initiated by twins.' From measurements made at-196oC, hardness and yield points of all the alloys were nearly constant and the same as the hardness of high phosphorus alloys that deformed by twinning at 20°C, Figs. 2 and 3. In the high-purity iron, plastic deformation at -196°C occurred by both slip and twinning, but deformation in the iron-phosphorus alloys appeared to be entirely by twinning. In the high phosphorus alloys a large number of cracks formed along the (112) twin boundaries and at intersections of twins, in addition to the (100) cleavage, Fig. 1(c). DISCUSSION In , iron, plastic deformation can occur either by slip or by twinning, depending upon composition,

Jan 1, 1961

By W. J. Wrazej

THE measurements on the formation of multi-layered scales on pure iron1 and the metal -lographic examination of the produced layer of FeO, Fe,O,, and Fe2O3 shown in micrographs2 throw much interesting light on this apparently well-known subject. Professor Paidassi announced2 that in a few months7 time further results are going to be published with regard to the growth of Fe2O3 and Fe2O3 layers on an Armco iron as a function of temperature. Because of the very thin layers of Fe2O3 which are shown by Paidassi (Fig. 10 of ref. 2) when samples were scaled in air at 700°C for 4 hr and because this is not in agreement with the present author's previous observations, the following experiment was recently carried out. Polished cylindrical samples 13/64 in. in diam and 1/4 in. long from electrolytic iron used for spectro-graphic work (Hilger, H.S. Iron rods, F.693) and an Armco iron sample 1/4 in. in diam of the same length were suspended in a muffle furnace on Nichrome wire and annealed in air for 4 hr at 700°C 5OC. Because of the known easy peeling off of the Fe2O3 layer which is mainly in the form of powder (purple red dust on the surface) the samples were protected against any draft and shock. After annealing, the samples were cooled in air and placed in the mount-

Jan 1, 1954

By E. Buehler, J. E. Kunzler

High-pu.1-ity molybdenum has been heat treated, melted, and zone refined and the physical and chemical changes that are produced by these processes have been studied by making resistance ratio measurements. Pronounced effects are observed that are associated with recrystalliza-tion at about 1200°C and with melting. Melting alone is found to result in a substantial purification by the evaporation of impurities such as iron. Zone refining is found to be reasonably effective with four passes producing a three-fold decrease in resistance ratio and a minimum ratio of 0.0003. With the aid of low temperature measurenzents, it has been shown that the build-up of a deposit of the material being zone refined on the radio frequency coil used for heating can lead to contamination of the sample. CONSIDERABLE interest in high-purity refractory metals for the study of mechanical properties has developed during recent years. Also the need for highly pure metals in certain fundamental studies, such as electronic band structure, has become quite widely appreciated. Molybdenum can now be produced with sufficiently high purity to make it attractive for such investigations. The most suitable measure of chemical purity of metals used for many of these studies is its resistance ratio, R,.,o,/Ro, During the purification of molybdenum by zone refining and its subsequent evaluation by this technique, a number of informative observations were made. These observations concern the effectiveness of zone refining, the volatilization of impurities at the melting point, and the recrystallization of molybdenum and appear to be pertinent to other refractory metals. Also, the usefulness of low-temperature resistance measurements as an analytical tool for evaluating the presence of chemical impurities and physical defects in metals is again illustrated. Samples of high-purity molybdenum of known mechanical history were heated to various temperatures between 800°c and their melting point. Resistance ratios of the samples were measured after they had been given a specified treatment. The data were used, along with mass spectrographic analysis, as an aid in interpreting the nature of the processes that occurred in conjunction with each treatment. Changes in the concentrations of chemical impurities and physical defects are typical of things that effect the low-temperature resistivity. SAMPLES The starting material was obtained from Westing-house Corp., Bloomfield, N.J. It was in the form of molybdenum rods, usually 1/8 or 3/16 in. in diameter. These had been previously processed from bars, 5/8 in, in diameter, originally reduced from 4 in. diam arc-cast ingots, by hot swaging at about 1300°c. In the final step, the temperature was lowered to about l lOO°C which resulted in the production of elongated grains. Typical grains were about 0.03 mm thick and 0.6 mm long. The molybdenum was quite pure as is indicated by the results of mass spectro-scopic analysis1 given in Column 2 of Table I. Other nongaseous elements not listed in the table were not detected. ZONE REFINING AND THERMAL TREATMENT OF SAMPLES Several sample rods, 8 to 10 in. long, were zone refined or were heat treated at several temperatures. Both types of operations were performed using 3 me-

Jan 1, 1962

By H. C. Chang, N. J. Grant

REEP studies and measurements in most in-V> stances are based on a relatively gross gage length. Even in some recent theoretical studies on the mechanism of creep, changes were followed by means of X-rays and metallography without regard for the behavior of the individual grains and grain boundaries.'" Analytical studies of creep have frequently indicated that more than one competing process is operative and that the ultimate creep performance depends on the effects of temperature, time, and strain rate as well as grain size.'-" he grains and grain boundaries are known to respond differently to these variables but the extent of the response is still little known, especially in poly-crystalline materials where the relative orientations of grains and grain boundaries are important. This paper reports some experimental observations of the behavior of the grain boundaries and their effect on the deformation in the grains. High purity aluminum was used to avoid complications of aging reactions, second phase, inclusions, etc. Experimental Procedure A small vertical nichrome wound furnace was built to permit direct loading on the test specimen. This furnace is capable of operating up to about 1300°F with reasonable temperature distribution. A ground rectangular quartz window, 1.25x0.5 in., is imbedded in the external stainless steel tube to permit observations of the creep process with a microscope. An argon atmosphere ,was provided to prevent oxidation. The quartz window caused a temperature gradient between the back and front surfaces of the specimen of 15" at 700°F. The temperature gradient could be cut down to 3°F along the length of the specimen by adjusting shunts across the furnace windings. An ordinary metallurgical microscope with a working distance of 14 mm was rebuilt so that it could be moved in three mutual perpendicular directions. Visual examination could be made with either a 30X eyepiece or a 15X filar eyepiece. Using an objective of focal length 24.3 mm and a numerical aperture 0.20 a total magnification of 120X or 240X could be obtained. High purity aluminum rated at 99.995 pct was supplied by the Aluminum Co. of America as % in. then the gage portion was further machined to 3/16 in. diam. The ends were Y4 in. diam and threaded to fit available specimen holders. Two opposite flat surfaces of the gage portion were obtained by milling, giving final dimensions of the gage portion of 3/4x3/16x3/32 in. Machined specimens were first electropolished in Jacquet's solution.' Reference marks were produced by pressing a thin sewing needle into the surface of the specimen. The specimen was then annealed at 900°F for 24 hr and at 1150°F for 12 hr. Typical macrostructures of specimens treated in this manner are shown in Fig. 1. The range of the grain size was 1 to 5.5 mm (see Fig. l), but most of the grains were of 2.5 mm and went through the whole thickness of the specimen. The specimen was re-electropolished and etched electrolytically to reveal the grain boundaries. In order to reveal the orientation difference of the grains, etch pits were produced on the surface of the grains by etching in a mixture of hydrochloric and nitric acids (HC1, 45 pct; HNO,, 10 pct; H,O, 45 , by volume). The specimens were very carefully put into the holders and furnace; yet even with this care, fine slip lines were developed on the specimen surface.

Jan 1, 1953

By D. L. Creighton, S. A. Hoenig

The field-emission microscope has been adapted for the study of microcrack growth during the early stages of fracture in metal wires. Cracks as small as 6 1 in length can be detected and their growth can be followed to specimen failure. The system is quite useful in searching for microcracks since only sharp-edged surface defects will emit electrons under the experimental conditions. THE conditions leading to brittle fracture were discussed a number of years ago by Griffith1 and the term Griffith Cracks is often used for the small surface cracks which are responsible for brittle fracture. Griffith's theory has been modified by stroh2 and more recent results on metals are discussed by Allen,3 pp. 123-40. At present the phenomenon is not completely understood but there is general agreement that at least in certain materials the sequence leading to brittle fracture involves several stages. The initial microcracks are present because of cooling or working stresses, Hahn et al.,3 p. 95. When a stress is applied to the specimen the cracks grow slowly until the release of stored elastic energy is large enough to accelerate the crack and provide the necessary surface energy for crack growth. At this point the growth rate appears to increase rapidly to some new equilibrium velocity, and failure occurs. Since the microcracks are usually about the size of a single metallic grain (Ref. 3, p. 99) it is not easy to find them and it is very difficult to follow their growth under stress. This paper will report on the use of a cylindrical field-emission microscope for observation of the formation and growth of microcracks. I) THE FIELD-EMISSION MICROSCOPE The field-emission microscope (FEM) has a high magnification and resolution and is almost uniquely suited for observations of microcracks. Since the FEM is relatively new as a metallurgical instrument, a short description will be given here. Normally metals at room temperature do not emit electrons; however in the presence of a strong electric-field gradient, electrons can tunnel out through the reduced potential barrier. Since this tunneling is a function of the local field gradient and the local work function, the emitted electrons can be used to produce a highly magnified image of the surface by allowing them to strike a phosphor screen. Because the electron emission is dependent upon the local field gradient, smooth surfaces emit few electrons except at very high fields. On the other hand cracks, extrusions, or other surface defects, having sharp edges, emit strongly since the field gradient is very high in the vicinity of these defects. This indicates that the FEM should be most useful for detection of microcracks on otherwise smooth surfaces. A field-emission microscope was first used by Muller4 in 1936 for observation of metal surfaces, and recent reviews have been given by Muller5 and Gomer.6 The instrument has been used for metallurgical studies in the area of surface diffusion,= recrystallization,7 and grain growth 8 (Ref. 8 is directed specifically at metallurgists). In the work of Muller4,5 and Gomer 6 the specimen was in the form of a sharp metal point at the center of a phosphor-coated glais sphere. The impact of the emitted electrons on the phosphor produced a highly magnified image of the specimens. Such a system is not practical for applying a controlled stress to the specimen and a cylindrical geometry has been used in this investigation. This allowed the application of a controlled tensile stress to the wire specimen. Normally a cylindrical FEM geometry produces magnification only in the radial direction. This is the case because a smooth wire at the center of a cylinder produces a purely radial electrical field. However, if there is a break in the smooth surface of the inner cylinder, the field near the break becomes three-dimensional and the area of the break is highly magnified. The reason for this is clear if it is recalled that the field gradient depends on the relative radii of the inner and outer cylinders; if a crack forms, its edge radii are of atomic dimensions and a very high field gradient is formed near these crack edges. Since the electrons receive most of their acceleration near the crack edge and are always traveling perpendicular to the field lines, they tend to spread out and produce the magnified image observed in the cylindrical field-emission microscope. 11) BRITTLE-FRACTURE STUDIES A) Experimental Apparatus. The geometrical arrangement chosen was that used earlier by Gifford

Jan 1, 1965

By P. E. Doherty, R. S. Davis

Sub boundaries and micropores, as well as certain other imperfections, may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits are attributed to the condensation of vacancies from supersaturated solution. This "vacancy pit" phenomenon has been used as an etching technique for studying the structure of aluminum specimens grown from the melt. Three fundamental structures were studied: stria-tions, cells, and dendrites. Two types of striations, as well as a crosswise structure are reported. Mic-roporosity is observed to occur in the cell walls on freezing. Subboundaries between primary, secondary, and tertiary branches are observed in dendritic growth. A special case is cited in which cellular growth suppresses the formation of striations. SMALL, well-defined pits have been observed to form on the surfaces of electropolished aluminum specimens during cooling from elevated temperatures.' This phenomenon was attributed to the condensation, from supersaturated solution, of vacancies at particular points on the surface. It was shown that the amount of cooling required for the formation of pits increased exponentially with decreasing holding temperatures in a way that was consistent with the thesis that a critical supersaturation of vacancies was required for the pits to form. Pits do not form in the vicinity of certain imperfections, namely, subgrain or normal graind boundaries, phase boundaries, certain surface irregularities, and pores. The width of the pit-free region increases with decreasing cooling rate. This observation suggests that the imperfections in question are effective sinks for vacancies and that the pit-free region around them is material that is not sufficiently supersaturated with respect to vacancies to nucleate the surface pits during cooling.

Jan 1, 1962