By D. T. Novick, M. B. Bever, B. Roessler

Ordered and disordered specimens of the alloy CusAu were cold worked and then annealed at 2880, 310°, and 340°C, together with disordered unworked specimens. me resistivity decreased during annealing mainly as a result of ordering; the resistivity measurements suggest that in cold-worked specimens the growth of antiphase domains is impeded. The strength properties increased during annealing at 288 "C; in cold-worked specimens this increase was lo a level above that for cold-worked specimens which had not been annealed. X-ray diffraction showed that after annealing for a few hours at 288ºC, the long-range order increased to a constant value; additional annealing at 288ºC resulted in the growth of antiphase domains in which the degree of order was constant. Changes in peak breadth and particle size confirmed that in cold-worked specimens the major effects of cold work were not eliminated during annealing at 288 "C, although a slight recovery process occurred. When a specimen of the alloy Cu3Au is heated to a temperature below the critical temperature (388ºC), long-range ordering tends to occur in a specimen containing less than the equilibrium amount of order characteristic of that temperature Ideally, a specimen of Cu3Au contains no long-range order if it has been quenched from above the critical temperature. Long-range order is reduced by cold work. If cold-worked specimens are heated, restoration processes such as recovery and recrystallization may occur,

Jan 1, 1963

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300' to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By S. F. Reiter, You-Chao Liu, W. R. Hibbard

Cyril Stanley Smith in his classic 1948 Institute of Metals Lecture&apos; noted in the case of annealing twins that: "It is well known that approximately the same number of twins per grain and the same general geometry are maintained in large grains as in small ones, a fact that certainly suggests a mechanism such as the above where boundaries and twins grow proportionately together. If this view is correct, a spherical grain should have no mechanism for keeping its twins." Such a constancy of twins per grain would be of particular interest as a tool for the study of the origin of annealing twins. It has been proposed by Mathewson2 and later by Barrett3 that in face-centered cubic metals slip occurs in the {111} Plane by <112> shears which combine in pairs to produce the macroscopically observed <110> movement. This proposal is schematically inviting since <112> slip permits the atoms of one plane to move along the interatomic valleys of its neighbor rather than up the hills across the atom sites. There is strong experimental evidence? that annealing twins result from the growth of nuclei in the form of "twin faults" produced by single <112> shears. It is possible that more twin faults would form at low deformation temperatures than at high ones, because the more rigid lattice may increase the tendency to "freeze" the twin faults and prevent their dissipation in slip. This is suggested by (1) the greater resistance to slip at low temperatures and (2) greater tendency toward mechanical type twinning at low temperatures (a summary of these factors is presented by Seigle and Brick5). These considerations would suggest the following: a. Constant twin/grain ratio for specimens deformed constant amounts at a constant temperature, but annealed at various temperatures above the recrystalliza-tion temperature. b. Larger twin/grain ratios for re-crystallized specimens previously deformed constant amounts at lower temperatures. The purpose of this investigation is to test these considerations. One half in. rods of phosphorous deoxidized electrolytic copper and 70-30 alpha brass (68.36 pct Cu, 0.005 pct Pb, 0.01 pct Fe, 31.62 pct Zn remainder) were rolled to a thickness of 0.350 in., milled to specimens 0.350 X 0.437 X 2 in., and annealed at 700°C to an average grain size of 0.065 and 0.090 mm, respectively. These specimens of each metal were then rolled 50 pct reduction in thickness and annealed one hour under conditions which were all combinations of the following: Rolling Annealing Temperatures. Temperatures. °C °C -70 400 25 500 200 600 Standard metallographic techniques&apos; were used to prepare specimens. By the method of lineal analysis7 using a minimum of ten samples of fifty grains each for each specimen, the ratios of twins* per total grains, twins per twinned grain, twin families* per total grains and twins per twin family were determined. Recrystallized grain size was determined by A.S.T.M. comparison methods.8 All observations were made on the rolling plane. The results are tabulated in Table 1.

Jan 1, 1950

By K. S. Krishnam, A. G. Guy

VOLUME 6 of the Transactions of the Baikov Institute of Metallurgy, Moscow, is devoted to the subject of "the experimental and theoretical study of the physical characteristics of dilute solid solutions,11 and summarizes work that has been done largely in the years 1958-9. In view of the attention that Soviet investigators have given to this subject, it seemed useful to carry out an independent experimental investigation in an effort to judge the scientific basis and practical significance of this field of study. The present note is a preliminary report of this investigation. The first property studied by the Soviet group was X-ray spectra of solid-solution alloys.&apos; An anomaly observed at low concentrations (--0.05 at. pct) of the alloying element led to the theory that each impurity atom in a transition-metal base alloy is the center of a "block" of affected atoms with a radius of about 10"7 cm. This theory was further developed in a later paper.2 By this time similar anomalies had been found in diffusion coefficients3 and in thermal expansion.4 The entire development up to 1959 was reviewed in a comprehensive paper, and further theoretical ideas were also published at this time. Finally, the volume mentioned above was published in 19607 giving new experimental data on anomalies in optical properties and Hall constant, and a new theoretical treatment also appeared.&apos; Although western scientists have done both theoretical work, summarized recently by Friedel,9 and considerable experimental work on dilute solid solutions, there is little support for the marked anomalies reported in the Soviet papers. Of the physical properties studied by the Soviet investigators, thermal expansion was chosen for the present investigation because of the relative ease of obtaining the necessary precision of measurement. A Leitz dilatometer was used for this purpose, and a special technique involving interchanging of the two specimens being compared permitted a precision of 0.05 x X in average thermal expansion over the range 27° to 600°C. The specimens were heated and cooled in vacuum or in a protective atmosphere at a rate of 50 °C per hr. Ferrovac E iron was used as the comparison specimen and in every case had a coefficient of expansion higher than (or equal to) that of the alloy. Since unintentional impurities are an important factor in studies of dilute alloys, special attention was given to the purity of the iron and the alloys used. The alloys were the same of those used by Abrahamson10 and by Michalak," and their preparation is described in these references. Chemical analyses of the Ferrovac E iron and of typical Fe-W and Fe-Mo alloys are given in Table I. The purity of the iron and alloys is undoubtedly higher than in the

Jan 1, 1962

By A. E. Bibb, J. R. Fascia

Single-crystal wafers of zirconium have been exposed to 680°F neutral water. The single crystals were of known orientation and weight-gain data as a function of crystal orientation were obtained. These data show that all the crystal faces studied obeyed a cubic rate law out to the time of transition whereupon the crystals corroded at an approximately linear rate. The time to transition varied from 114 days for (1074) crystals to about 325 days for the (2130) faces. The epitaxial relationship be-tween metal and monoclinic oxide was found to be (0001) H (111) and [1120] 11 [101]. A black tight adherent oxide layer was formed on the crystals in the pretransition range. This black oxide was found to be monocrystalline. The white corrosion product produced after transition was found to be polycrys-talline but highly oriented. X-ray line-broadening studies found that the black oxide was a highly strained structure whereas the white oxide was relatively strain-free. These results indicate a strain-induced re crystallization or fragmentation accompanies the change from protective black oxide to nonprotective white oxide. ZIRCONIUM alloys have been used quite extensively in high-temperature aqueous environments. Alloy additions can be made to commercial sponge zirconium which enhance the corrosion resistance of the zirconium in both water and steam media, which raise the tolerance limit for certain impurities detrimental to corrosion resistance, and which reduce the amount of free hydrogen pickup during corrosion. The development of the corrosion-resistant zirconium alloys has been a long and tedious job involving trial and error methods. This technique has been necessary because of a lack of fundamental data and hence understanding of the corrosion mechanisms. The objective of the work described herein was to provide some fundamental data with respect to the aqueous corrosion of zirconium crystals as a function of the orientation of the exposed surfaces. Hg. The zirconium chunk was then cooled to below the transformation temperature (862°C) and reheated to 1200°C for 8 hr. The ultimate size of the zirconium grains increased with the number of cycles. Rapid or even furnace cooling through the transformation temperature produces a considerable amount of substructure which was intolerable in corrosion experiments as it would be in the study of any crystallographically dependent property. It was found that a high-temperature a-phase anneal for approximately 4 days reduced the substructure below the limits detectable by visual or X-ray means. Crystals so produced were carefully cut from the massive zirconium chunk and oriented by standard back-reflection Laue techniques. The crystals were then mounted in a goniometer head and, by using the three degrees of freedom available, slices on the order of 0.015 to 0.020 in. were cut parallel to any desired crystal plane. These slices were then carefully polished on both sides to produce smooth flat faces, pickled to remove about 0.002 in. per face, annealed for 1/2 hr at &apos;750°C in a vacuum of approximately 10"5 mm Hg, flash pickled, and checked for orientation. The pickling solution was 45-45-10 vol pct HN0,-H20-HF and continuous agitation was provided to eliminate pitting of the slices. Any slice that was not within 2 deg of the desired orientation was discarded, and any evidence of substructure as indicated by the Laue spots was also grounds for discarding the sample. Thin slices were used for the corrosion tests because weight gain per area data could be obtained with only a minimum area exposed to the corrosive media that was not of the desired orientation. The thin single-crystal slices were of irregular shape and as a result the areas were determined by placing a crystal inside an inscribed square of known area, enlarging a picture of this assembly about X5, and tracing both the enlarged square and crystal with a planimeter. The zirconium used to produce these single crystals was crystal-bar grade, a typical analysis of which is given in Table I. An oxygen analysis on prepared crystals gave a concentration of 205 ppm. The hydrogen concentrations are believed to be less than 15 ppm due to the dynamic vacuum anneal given each crystal. Typical nitrogen values for zirconium treated in this manner are about 10 to 20 ppm. RESULTS AND DISCUSSION Single-crystal wafers have been exposed to de-oxygenated, deionized water in static autoclaves.

Jan 1, 1964

By F. W. Aul, R. C. Glenn

EXTRACTION techniques are of particular importance in determining size, shape an: crystal structure of particles smaller than l000Å in steels and other alloys. However, artifacts that can arise during the preparation of extraction replicas may lead to erroneous conclusions. The purpose of this note is to illustrate some of these artifacts and the misinformation that can result from their presence. An alloy of iron with 0.8 pct Cu was investigated in the following conditions: 1) Solution treated 3 days at 925°C in dry hydrogen and quenched in water. Aged in steps to precipitate copper, as follows: heated to 700°C, held 1 day; then furnace cooled to 50O°C, held 3 days; then furnace cooled to room temperature. 2) Solution treated 3 days at 925OC in dry hydrogen and furnace cooled to room temperature. 3) Solution treated 3 days at 925OC or 17 hr at 1100°C in dry hydrogen to dissolve all copper, then quenched in water. A normal parlodion dry-extraction technique was employed after etching the specimens with super picralP or with 2 pct nital. A wet-extraction method

Jan 1, 1962

By J. G. Faller, L. P. Skolnick

The distribution of cobalt and vanadium over non-equivalent crystallographic sites in C14-type Zr(VCo), alloys has been investigated. An anomalous X-ray scattering technique developed by Skolnick, Kondo. and lavine7 by which the separation in the scattering factors of two similar atoms can be enhanced was employed. Six alloys spanning the pseudobinary section ZrV1.6Co0.4-ZrVO.6CO1.4 at 10pct steps showed a nonrandom compositionally dependent distribution. Specifically, at high vanadium content cobalt preferentially occupied sites of type (6h) and vanadium, sites of type (2a; at low vanadium content the reverse was observed. In addition to the distribution fraction the structural parameters x and z were obtained. There was no significant deviation of these parameters from those obtained in the ideal C14 structure. Certain suggestions are made to account for the observed nonrandomness in the distribution of atoms on the two types of sites. INTERMETALLIC compounds of formula AB2 iso-morphous with MgCu2, MgZn2, and MgNi2 are known as Laves phases. Because Laves phases exhibit high symmetry and coordination numbers, the highest possible for an AB2-type compound,1 they are among the most frequently observed compounds in nature. In recent years interest has centered about the purely transition metal Laves phases2-&apos; in efforts to understand the function of atomic size and electronic structure in the formation of these compounds. It has been observed that pseudobinary Laves phase systems often show a variation of structure across the phase diagram. Such a system is the ZrV2-ZrCo2 in which the structure varies from cubic MgCu2 to hexagonal MgZn2 to cubic MgCu2.4 Some understanding about the conditions under which the second modification is stable can perhaps be gained by studying the distribution of cobalt and vanadium atoms on lattice sites in the MgZn2 modification of the system ZrV2-ZrCo2. In both the MgZn2 and MgNi2-types there exist nonequivalent positions open to occupancy by the B element, whereas in the MgCu2 prototype all sites are equivalent. Skolnick, Kondo, and La-vine7 have developed an anomalous scattering technique suitable for this type of investigation. Whereas the influence of size on the formation of a Laves phase is well recognized, no substantial evidence has been put forth in support of the size ratio dependence of a particular prototype. Berry and Raynor8 suggested that RA /RB ratio does indeed affect the type of structure that is chosen, MgZn2 compounds tending to cluster about 1.225 while MgCu2 compounds were found at larger deviations from this ratio. Dwight,3 however, from a study of 164 Laves phases does not believe this generalization to be justified. Electronic effects are certain to play a part in the stability of Laves phases in general and in the choice of a structure type in particular. For example, size along would favor the formation of Laves compounds of Ti, Zr, Hf, Ta, or Nb as the A element with nickel or copper as the B element. The absence of such is attributed to an unfavorable electron : atom ratio by Elliott and rostoker.4 Early experiments of Laves and witte9 with pseudobinary and pseudoternary systems of the three prototypes established the dependence of crystal structure upon electron: atom ratios. They observed that the MgCu2 structure dissolved elements of higher valency until the electron: atom ratio of =1.8 was reached; the MgZn2 likewise dissolved elements of lower valency replacing zinc. witte,6 from calculations of the electron : atom volumes of Brillouin Zones, obtained limits of stability for the prototypes MgCu2 and MgZn2. Elliott and Rostoker4 used these limits with considerable success in the all-transition element Laves phases they investigated. According to witte,6 compounds between the electron :atom ratios of 1.80 and 2.32 were of the MgZn2 type; those above and below exhibited the MgCu2-type structure. On the basis of these limits and an assumed valency of zirconium based upon the near tetra-valence of titanium, Elliott and Rostoker obtained valencies for the first transition series elements. For the Laves phases with which this investigation is concerned, ZrV2 and ZrCo2, the authors calculated electron :atom ratios of 2.54 and 1.56, respectively. These ratios are for the MgCu2-type structure and straddle the stability band of the MgZn2 modification. One could, therefore, predict that a pseudobinary system ZrV2-ZrCo2 should pass through the MgZn2 modification in traversing the composition diagram from one end to the other. Implicit in this assumption is a smooth change of the electron: atom ratio from 2&apos;54 to 1.56. MOSS10 states that his finding the low temperature structure of ZrCr2 to be C15 instead of C14 alters greatly Elliott&apos;s valency of zirconium and hence the assumed valencies of the other metals. Such a quantitative correlation of structure with electron : atom

Jan 1, 1963

By R. G. Treuting, W. C. Ellis

The twinned state is characterized by a lattice of coincidence sites. Imperfections are required at stable lateral twin interfaces. Twinned regions can occur with relative ease in the diamond cubic IN recent contributions1,2 on the origin and growth of cubic annealing twins, attention has been directed to the orientation relations between such twinned components and their parent matrix. There are some aspects of twinning which may be illuminated by a more detailed consideration of the twinned state" alone. As an extreme example, the dense twinning in cast ingots of germanium,&apos; as contrasted with the rarity of twins in cast face-centered cubic metals, is yet to be accounted for. It has been this that has led us to the present work, which, it will be noted, uses methods and constructions in many respects similar to those of Kronberg and Wilson.&apos; In the cubic systems, a 70" 32&apos; rotation about a <110> axis is angularly equivalent, as to twinning, to the more usually considered 180" rotation about a <111> axis. Figs. 1 and 2 show a (110) projection of a twinned face-centered cubic lattice and a twinned diamond cubic lattice. In both figures, the two adjacent planes A and B, shown by the larger and smaller circles, are sufficient to represent the entire array. In each case a section of lattice, the original atom sites of which are shown by open circles, has been rotated as indicated through 70" 32&apos; to bring an original. [112] direction into coincidence with the [112] diiection. The latter is the intercept on the (110) projection of the (ill) plane normal thereto, the twinning plane. In the face-centered cubic case the rotation can be performed about an axis passing through an atom-site; the mirror plane then is also a composition plane containing atoms common to both twinned and untwinned lattices. The diamond cubic lattice may be construed as two interpenetrated face-centered lattices. Its (111) planes recur in a sequence of alternately short and long interspacings. Consequently a mirror plane for twinning cannot be a composition plane, but must be the bisector of one of the spacings. When the longer spacing is selected, the closest distance of approach across the mirror plane in the [ill] direc- tion is identical with that in the untwinned structure. In each case periodically recurring (ill) planes (parallel with the twinning plane) are found, on which there is coincidence of atom sites of the pre-twinned and twinned orientations; these are indicated by the cross-hatched circles. In the face-centered lattice there is such coincidence every third (ill) plane; in the diamond cubic lattice, on two adjacent planes in every six. At the twinning interface in the latter, there is on each side of the mirror plane a (ill) plane of atoms common to both twin components. Conceivably, there is little influence on a plane of atoms about to be adhered to such a pair of coincidence planes, whether it be laid down in a normal or in a twinned position with respect to the previously formed structure. Slawson% as attributed the high incidence of twinning in diamond to this boundary state. Further examination shows that the motion of intermediate planes can consist of various pairs of equal and opposite translations, for example of (ill) planes in the [l&apos;;i2) direction, the familiar twinning shear, indicated in the small schematics in the figures. Since the translations form a system of shears of alternating sign between coincidence planes, twinning could take place by such a mechanism over an extended region without extensive shear; in fact, in this case any atom moves but the distance in the [1i2] direction. One alternative construction for the face-centered cubic lattice leading to the same end result is illustrated in Fig. 3. The plane (711) with respect to the pretwinning orientation (the twinning plane of Fig. 1) is given, the twinned region arbitrarily bounded by <110> and <112> directions. The coupled shear is identical to that of Fig. 1. The "rotational" movement about coincidence sites generating the same twinned position could consist as shown of the translation a,/d% for each atom of a group of three in the B layer in a different one of the three <112> directions, and a similar translation of the underlying three atoms in the C layer in either the same or the opposite sense. This is not dissimilar to Kronberg and Wilson&apos;s construction for their 22" rotation of three adjacent (111) planes.

Jan 1, 1952

By E. F. Bailey, W. J. Harris

THE temperature of the ferrite to austenite re-action is established frequently by continuous heating experiments. However, equilibrium studies of this reaction have demonstrated that austenite may form at temperatures considerably below those at which the reaction is first observed during continuous heating. Because of this discrepancy, tempering is sometimes performed above the true critical temperature and in these cases austenite forms during tempering. The lowest temperature at which austenite forms and the kinetics of the reaction have been studied by Bain,&apos; Bleakney and Gros-venor,2 and Dube and Cunningham. This austenite can affect the properties either as austenite per se, if it is retained at room temperature, or as a decomposition product if it transforms. The effect of austenite formation during tempering on low temperature impact properties of an 8 1/2 pct nickel steel was reported by Brophy and Miller4 in work published after the present investigation was initiated. They concluded that the improvement in low-temperature notch toughness which followed tempering at certain temperatures could be attributed to the austenite formed during tempering. Kramer et al.5 found anomalous hardness increases and embrittlement after tempering of a low-carbon manganese-nickel steel. They concluded that austenite formed during tempering, and that the decomposition products were responsible for the increase in hardness and the embrittlement. Quan-titative correlations of the microconstituents and mechanical properties were not made by these investigators. The present study was undertaken in order to establish the kinetics of formation of austenite at various temperatures, the characteristics of the decomposition of this austenite, and the relationship between mechanical properties and the phases present. Experimental Procedure A low-carbon manganese-nickel steel was selected because of the sluggishness of its austenite decom-position reactions. The composition of this steel in percent was: C, 0.10; Mn, 3.52; Ni, 2.34; Mo, 0.52; Cr, 0.17; Si, 0.19; V, 0.15; P, 0.019; and S, 0.020. Samples were prepared by forging sections from a large ingot to 3/4 in. bars. Formation and decomposition of austenite were investigated by dilatometric techniques which were checked by X-ray measurements. Dilatometer specimens were hollow cylinders 1 in. long, 1/2 in. diam, with a 1/8 in. central hole. All specimens were aus-tenitized for 1 hr at 1650°F and quenched in water prior to insertion in the dilatometer. Oxidation was prevented by using an inert atmosphere of purified nitrogen. Dilation was measured with a dial gauge which could be read by interpolation to 0.00005 in. Temperature was maintained within ± 3°F by a Brown Electronik Controller. Chromel-alumel thermocouple leads were welded to opposite ends of the specimen with the specimen serving as the hot junction. As a check on temperature uniformity comparison was made of the specimen temperature as measured with the chromel-alumel leads and the temperature of the center of the specimen as measured with a calibrated platinum—platinum-rhodium thermocouple embedded in asbestos in the central hole of the specimen. During heating a 5°F temperature difference was noted below 1000°F, but none above, while in cooling, a 5°F difference was observed from 1300" to 735°F, but none below. Heating rates of 35°F per min and cooling rates of 60°F per min were employed for all dilatometric studies. For transformation studies below room temperature, the dilatometer was allowed to cool to 150°F and then was quenched into liquid nitrogen.

Jan 1, 1951

By R. J. Wasilewski

THERMAL expansion of rhenium data have been reported by Agte et al.,&apos; and Medoff and cadoff,&apos; respectively, while the linear expansion coefficient was determined by Sims et Al.3 Denoting expansion coefficients parallel and at right angle to c axis by all and Al respectively, their weighted mean should be equal to dilatometric linear coefficient of a random polycrystalline specimen. The values reported for these coefficients are tabulated below: Since these values are in poor agreement, and because of anomalous expansion behavior observed in titanium 4 and chromium, a rede termination of the axial expansion was carried out. A Unicam 19-cm-diam high-temperature camera was used, with unfiltered CuK radiation. Camera calibration was carried out using at Pt wire standarde at temperatures up to 1100oC, the variation between indicated and true temperature being within the experimental error (estimated at <3oC) above 750o C. Rhenium Johnson Matthey spectrographic standard) was vacuum annealed at 1000 oC prior to X-ray diffraction experiments. Lattice parameters were obtained by least-squares solution using the reflec- tions (1232), (1015), (2024), and (3030) for all the patterns, and the additional reflection (2133) for higher temperature (400°C and above) patterns. The relative expansion data obtained are shown in Fig. 1, lengths of the vertical bars indicating the spread in the parameter values obtained by using various combinations of three spacings from the four or five measured. The data calculated from the equation of Ref. 2 are included for comparison purposes. Several specimens were used to obtain the above data, neither of them showing a significant parameter change after completion of the high temperature runs. Some parameter data and the corresponding expansion coefficients between 25 oC and the measurement temperature are tabulated below. The comparison of the present data with those previously reported shows reasonable agreement with the results of Medoff and cadoff2 within the temperature range covered by them (up to 1000 oC). The a values are appreciably higher throughout most of the investigated temperature range. The basal expansion is—in agreement with their findings—appreciably higher than that in the direction of hexagonal axis. The expansion coefficient, al, however, decreases rather more slowly with temperature than previously reported. The expansion along the c axis up to nearly 1000°C appears in excellent agreement. However, at higher temperatures there is a marked deviation towards higher expansion, reproducible between different specimens. Furthermore, there seems to be some irregularity in the variation of all with temperature, the apparent local minimum and maximum values at 510o and 1024o C, Table II, being well outside the experimental error limits. It must be stressed that the apparent discontinuity in the c parameter expansion is still insufficient to account for the expansion value reported by Agte et al.&apos; since a total expansion of close to 2 pct would

Jan 1, 1962

By J. D. Lubahn

The Bauschinger effect, or rounding of the corner of the stress-strain curve upon reloading, represents a temporary apparent softness that is more pronounced at large strains than small and for complete unloading than for partial unloading. Interrupted creep tests on copper exhibit a similar temporary softness (high creep rate) upon reloading. The fact that the strainwise dying-out time of these effects is the same in both tensile and creep tests shows that they are related. Thus, the term Bauschinger effect appears to embrace behavior following partial or complete unloading and reloading in addition to behavior following reversed loading. It is suggested that the term may properly apply also to certain creep behaviors following a small load decrement. INTERRUPTED tensile tests at low temperatures show1 a rounding of the corner of the stress-strain curve for reloading, which indicates a temporarily low deformation resistance. In the absence of recovery, the curve soon rises to the value that would have prevailed if the test had not been interrupted. The rounding of the reloading tensile curve has sometimes been referred to1 as the Bauschinger effect, although the term is more commonly applied to low deformation resistance in compression following tensile prestrain. The unusually broad usage of the term Bauschinger eflect in ref. 1 seems justified by the obvious interconnection of the various behaviors to which it has been applied.&apos; In fact, the following discussion will indicate that still broader usage might be desirable. The Bauschinger effect is common at room temperature but apparently disappears at higher temperatures.2 Interrupted creep tests and tensile tests were made on certified OFHC copper (nongaseous impurities exclusive of silver were 0.004 pct), cold drawn 84 pct to ½ in. diam, and annealed at 600" (about 0.025 mm grains) or 850°C (about 0.2 mm grains). The tests were made in standard creep or tensile machines, using an O.S. Peters microformer-type extensometer or, for the small plastic strains, a special arrangement employing General Electric magnetic gage heads.&apos; Interrupted creep tests at room temperature show3,4 an initial softness after reloading, manifested by an initial creep rate that is higher than that which would have prevailed if the test had not been interrupted. Fig. 1 shows some typical examples. This effect is apparently temporary (as is that in tensile tests): in four of the five tests shown, the log rate vs strain curve becomes parallel to an

Jan 1, 1956

By J. J. Gilman, T. A. Read

FOLLOWING the deformation 01 zinc monocrys-tals, sharply bent basal planes are observed near several types of inhomogeneities. Three of these in-homogeneities have characteristics which are quite regular so that they can be studied and analyzed. These are compressive kink bands, "deformation bands," and the inhomogeneities near end restraints. The present paper describes experiments in which "deformation bands" were artificially produced, and bend plane phenomena are discussed in terms of dislocation theory. Also, two new bend plane phenomena are described. The importance of bend plane phenomena in the deformation of crystals is not widely recognized. Many phenomena may be explained in a manner similar to the discussion in this paper. Jillson1 has pointed out that the "punching effect" in zinc is a bend plane phenomenon and is not caused by prismatic slip.&apos; Bowles3 has suggested that they may be involved in diffusionless phase changes. Cahn4 has discussed the role of bend plane formation in the polygonization of zinc. Experimental Work Tensile Kink Bands: Because of the geometrical similarity between "deformation bands" and "kink bands" (compare Fig. 1 of this paper with Fig. 1 of the paper by Hess and Barrett"), the band shown in Fig. 1 of this paper will be called a "tensile kink band," and that shown by Hess and Barrett will be called a "compressive kink band." It is felt that the term "deformation band" should be reserved for banded structures in polycrystalline materials such as iron." Tensile kink bands seem to form spontaneously in aluminum crystals deformed by tensile loading.7-10 In zinc and cadmium crystals they do not form in good, carefully loaded specimens.&apos;." However, tensile kink bands can be produced artificially in zinc crystals. The present authors did this by scratching one of the flat surfaces of triangular crystals transversely with a sharp needle. Natural tensile kink bands caused by inhomogeneities sometimes appeared in deformed crystals which were identical in appearance with the artificially produced ones. Zinc monocrystals were grown by the Bridgman method in graphite molds. Chemically pure zinc (99.999+ pct Zn) was used and the molds were sealed inside evacuated pyrex tubes during growth. The crystal cross sections were equilateral triangles with a typical base of 0.210 in. The artificial kink band shown in Fig. 1 is typical of tensile kink bands in zinc. The band lies between two bend planes which run from upper right to lower left and is inclined oppositely to the slip bands which are sharply bent at the two bend planes. The general form of the artificial tensile kink bands was independent of the scratch depth (1 to 5 mils deep) and also independent of which side was scratched. These variables did cause variations, however. Deep scratches produced more localized kink bands than light scratches. Also, if the angle between the slip plane traces and a transverse scratch varied appreciably among the three sides, then localization of the resulting kink bands also varied. Furthermore, if the slip direction lay nearly parallel to the scratched side, the band was more developed near the scratched side than at the opposite edge. Scratches produced tensile kink bands for crystal orientations from xo = 15" to x, = 75". Fig. 2 shows a scratched crystal after deformation. One triangular side lies in the plane of the photograph. The right hand tensile kink band was produced by a transverse scratch on the upper right side. The next two kink bands were the result of scratches on the front surface. The kink band at the left was caused by a scratch on the lower back side. All four bands have the same general form. A longitudinal scratch was also made on the crystal shown in Fig. 2 to determine the effect of a scratch on the critical shear stress. The critical shear stress of the scratched region was 33.9 g per sq mm compared to 24.4 g per sq mm for the un-scratched region above it. Fig. 3 shows Laue patterns of the crystal shown in Fig. 2. Fig. 3a shows the pattern of the undeformed crystal. The orientation was x, = 21°, A, = 31". After deformation, Fig. 3b was made of the homogeneously deformed portion of the crystal. The spots are compact but split into two halves. This region was elongated 45 pct and its orientation was x = 14", X = 20"; the sine law predicts x = 14", A = 20.5". Fig. 3c was taken near the center of the middle tensile kink band of Fig. 2. The pattern shows a range of orientations and polygonization in this region. The spread in orientation was due to the fact that the basal planes were curved (see Fig. 1) rather than flat as in the ideal case. Some may also have been the result of elastic distortions and "local curvatures." The orientation range was x = 23" to 32", A = 30" to 42". It is apparent from Fig. 3 that the material inside and outside the kink band rotated in opposite directions with respect to the tension axis during deformation. The orientation calculated from the ideal configuration of Fig. 9,

Jan 1, 1954

By D. L. Douglas

The ß decomposition of Zr-U-O alloys was studied during an interrupted quench from the a + ß region. Decomposition was more rapid than in binary Zr-U alloys of the same uranium content or qf equivalent ß composition. The rapid transformation has been ascribed to the presence of the primary a phase which provided nucleation sites and which permitted preferential partitioning of oxygen to the a phase and of uranium to the COMMERCLAL heat treatments are designed to produce certain strength and toughness character- istics by controlling the microstructure of an alloy. A desired distribution of microconstituents is achieved in practice by treating an alloy under the correct time-temperature conditions. A knowledge of the phase equilibria in any alloy system is essential in outlining heat treatments, but in addi-

Jan 1, 1961

By Jack L. Taylor

As expected from similar crystal structures and favorable atomic size factors, titanium, vanadium, and molybdenum are completely soluble in one another above the transformation temperature of titanium. The fl phase parameters of the continuous solid solution are shown graphically. Limiting compositions for retained fl phase have been determined. VANADIUM and molybdenum both have body-centered-cubic structures at all temperatures and, from the atomic diameter comparison factor, 3.9 pct, would be expected to form a complete series of solid solutions. The existence of complete solubility has been confirmed by work&apos; at the Jet Propulsion Laboratory. Furthermore, vanadium and molybdenum have favorable atomic size factors to form complete binary solid solutions with the B phase, high temperature form of titanium, which also has body-centered-cubic structure. Pietro-kowsky and Duwez&apos; and Hansen et al." have established the existence of the complete series of solutions in these binary systems. It would be logical, therefore, to expect that p-titanium, vanadium, and molybdenum would be completely soluble in one

Jan 1, 1957

By H. R. Ogden, A. G. Imgram, D. N. Williams

The effects of composition on the mechanical properties and aging characteristics of several alloys in the Ti-V-Cr system, with and without aluminum modifications, were evaluated. Increasing the chromium, vandium, or aluminum content increased the strength of quenched structures with chromium being the most effective strengthener. Appreciable aging response was obtained with low chromium alloys, but high chromium alloys age softened rather than. hardened. High vanadium contents had a similar effect. Aluminum additions shifted the aging behavior toward that observed in lower chromium alloys, enabling high chromium alloys to be age hardened. DURING the course of titanium alloy development many a and a-ß alloys have been evolved to commercial status. However, only one all-ß alloy has achieved this same stature. This is the Ti-13V-11Cr-3Al alloy. It is characterized by a very sluggish ß-phase decomposition reaction such that very slow cooling rates can retain the 0 phase at room temperature. In addition, very high strength levels can be obtained by long-time aging treatments. Combinations of cold or warm working followed by aging produce even further improvements in strength. This paper describes the results of a research program in which the effects of composition on the mechanical properties and aging characteristics of several alloys in the Ti-V-Cr system, with and without aluminum modifications, were evaluated. EXPERIMENTAL PROCEDURES Electrolytically refined, high-purity titanium was used as the alloy base for these studies. Iodide chromium, electrolytically refined vanadium granules, and high-purity aluminum sheet were used as alloying additions. The compositions of interest were melted as 250-g ingots in a direct current arc melting furnace under a flowing atmosphere of argon. The ingots were hot forged to 3/4-in.-diam bars, vacuum annealed for 6 hr at 1800°F to reduce residual hydrogen content, and then hot swaged to 1/4-in.-diam rods. Fabrication history, and interstitial analyses after fabrication are given in Table I. All specimens to be heat treated were sealed in Vycor capsules under a partial pressure of argon. Samples used to define the ß transus were quenched from temperatures ranging from 1350° to 1100°F after holding at temperature for 15 min. Samples for aging studies were quenched from above the ß transus temperature and then aged for up to 64 hr at 750°F and for 100 hr at 850°, 900°, and 950°F. The effects of straining prior to aging were also investigated. The results of these studies were used to select the heat treatments for the tensile specimen blanks. Heat treatments of the tensile specimens are described in Table 11. Alloys were aged after solution heat treatment or after solution heat treatment and cold swaging to 50 pct reduction in area. Standard 0.125-in.-diam tensile specimens were machined from the heat-treated blanks. All tensile tests were performed in a Baldwin-Southwark uni-

Jan 1, 1963

By Niels Hansen

Dispersion-strengthened sintered aluminum products are normally manufactured from surface-oxidized aluminum powder, SAP,&apos; or from atomized aluminum powder.&apos; The powder-blending technique consisting in mechanical mixing of the constituents has been used in the manufacture of numerous dispersion-strengthening alloys, but has never been successfully applied to aluminum alloys. This technique may, however, be applicable if it is possible to produce an unagglomerated mixture of the constituents in the form of fine powders, and the present study was initiated to test this assumption in the aluminum/aluminum oxide system.3 Table I lists the two grades of aluminum powder and the aluminum oxide powder used in the manufacture of the alloys. MD 105 A is an aluminum powder with an average grain size less than 5 IJ., which is isolated from the MD 105 powder by centrifugal separation in cyclohexanol. The aluminum powders and the aluminum oxide were blended in a high-speed blender and then subjected to cold compaction and hot compaction at 550" to 600°C. Subsequently the compacts were hot-extruded with an extrusion ratio of 15 to 1. The alloys were evaluated by tensile testing at room temperature and at 400°C, microscopic examination, and heat treatment at 500°C followed by tensile testing at room temperature. For the purpose of comparison, a commercial SAP quality supplied by Swiss Aluminium Ltd. was tested in the same manner. The tensile data at room temperature and at 400°C are plotted in Figs. 1, 2, and 3 as a function of the weight percent of oxide. The oxide content

Jan 1, 1964

By R. G. Gifkins

Mean boundary migration depended linearly upon creep extension under various conditions. Prolonged annealing or air-casting increased the proportion of immobile boundaries at a given stage of tests. Grain growth during annealing followed a power law. The linking of migration and sliding in creep and models for migration are examined; activation energies are calculated from these models. Segregation of oxygen to boundaries appears to be a controlling factor. THE idea that boundary migration and boundary sliding during creep are linked has often been suggested,&apos;-5 especially when evidence has been obtained for an alternation between the two processes. In simple bicrystals sliding can occur without any migration6 but in more complex bicrystals7 it is observed. McLean&apos; and Couling and Roberts 5 made measurements of both sliding and migration; McLean concluded that there was no linking of the two processes whereas Couling and Roberts supported the idea. McLean&apos; also developed a model for migration during creep and annealing. The present work was initiated as part of a study of the recrystallization of lead during creep9 but has been extended to examine some aspects of the mechanism of migration. MATERIALS AND METHODS Specially refined high-purity lead* was used; the total of impurities, excluding oxygen, was 0.0008 wt pct. Oxygen was removed as far as possible by melting in vacuo, treating at 550" to 600°C with hydrogen and then casting at 450°C under a vacuum of 10-2 mm Hg; the oxygen was then believed to be 0.00005 wt pct. Specimens were made from extruded strip and then annealed at the required temperature in an air oven, controlled to 5 lac. They were then polished in a mixture of acetic acid and hydrogen peroxide. At this stage some specimens were etched to give grain contrast and their grain sizes determined by the intercept method. Migration of boundaries during creep was measured on the surface of polished (not etched) specimens, directly loaded at room temperature (22°C) or 50°C (52"C) to initial stresses of 300 to 700 1b per sq in. Twenty six vacuum-cast hydrogen-reduced specimens were used and, in addition, two specimens were from material air cast after hydrogen reduction ("partial" air cast) and two from air-cast material not treated with hydrogen ("full" air cast). Duplicates were made in the majority of tests. At intervals through the creep tests, specimens were unloaded and the migration measured, normal to the direction of migration at the point of measurement, for each boundary along standard traverses. Usually between 110 to 180 boundaries were measured at each of some twelve stages of the tests. Migration was measured on the projected image (X100) using prism illumination. Fig. 1 illustrates the method of measurement and shows the kind of variation of migration found from boundary to boundary and along particular boundaries. Fig. 2 gives an example of more extensive migration. The mean value of distance migrated was generally reproducible to *10 pct but occasional points gave a scatter of *20 pct. The correctibn applied by McLean8 to allow for the contribution sliding makes to the apparent distance of migration could not be used, for the sliding at most boundaries was too small to measure with the equipment available. There were two reasons for supposing the correction unnecessary in the present work;

Jan 1, 1960

By M. Cohen, C. Wagner, J. E. Reynolds

If the total volume of a diffusion couple changes during the diffusion, the measurement of distance becomes ambiguous. Use of distance parameters as suggested by Hartley and Crank is discussed. For small concentration differences, the standard form of Fick&apos;s second law is retained with conventional length units and the in- terdiffusion coefficient D. It is shown how D can be calculated from experiments involving large concentration differences and analyzed in terms of distance parameters. &apos;The merits of incremental diffusion couples involving small concentration differences are emphasized. THE conventional form of Fick&apos;s second law for one-dimensional diffusion of component B in a binary solution of A and B is where c, is the concentration of component B; x, the distance; t, the time; and D, the interdiffusion coefficient which may depend on ca. Hartley and Crank&apos; have pointed out that Eq. 1 applies only if the total volume of the diffusion couple does not change during the diffusion process; otherwise, the definition of x becomes ambiguous. No change in total volume takes place if the specific volume of the solution is a linear function of the weight fraction Wb, or if the molar volume is a linear function of the mol fraction N. In some alloys, however, these relationships do not hold, and then it is necessary to introduce a modified measure of distance, 4 in order to retain the general form of Eq. 1. The application of Hartley and Crank&apos;s suggestions to diffusion in alloys has been discussed by Wagner.&apos; Relation Between Measure of Distance and Units of Concentration The definition of [ depends on the choice of units for the concentration c,, as follows: 1—If the concentration ca is measured as the weight fraction W, (or weight percent), [ = 5, has to be defined so that equal increments of contain equal increments of mass m of the solution, e.g., dm = pSdx = Sdw [2] where p is the local density of the solution, and S is the cross-sectional area in sq cm which is taken to be constant in this problem of one-dimensional diffusion." * da Silva and Mehla have demonstrated the constancy of the cross-sectional area in the usual type of diffusion couple. However, experiments involving diffusion into thin wires4, 5 may exhibit changes in cross-sectional area, and therefore are excluded from the present treatment. Thus and the unit of is gram per sq cm instead of cm. 2—If the concentration c, is the mol fraction N, must be defined so that equal increments of contain equal numbers of mols of solution, e.g., dn= (S/V)dx= Sd [41 where V is the local molar volume of the solution. Thus dt, = dx/V [51 and the unit of is mols per sq cm. 3—If, as may be advisable in the case of interstitial solutions, the concentration C is measured in terms of the molar ratio of components B and A (c,, = Y, = nH/nA, where n and nl are numbers of mols of B and A), = Y has to be defined so that equal increments of contain equal numbers of mols of A, e.g., dnA= (NAS/V)dx = Sdf [6]

Jan 1, 1954

By M. J. Pool

The partial molar heats of solution in liquid tin of cadmium, silver, tellurium, and zinc have been measured at 655°. 700°, and 750°K by liquid-metal solution calorimetry. Silver, cadmium, and zinc are endothermic at these temperatures while tellurium is exothermic. Only the heat of solution of silver depends on composition while all four elements show a temperature-de pendent heat of solution. The heat of solution of tellurium is constant up to 0.6 g-at. pct, becomes increasingly more exothermic, and reaches a limiting value at 1 g-at. pct Te. The limiting value has been used to calculate the heat of formation of SnTe at 750°K. The heat effects associated with the dissolution of the compounds Ag2 Te, CdTe, and ZnTe in liquid tin were measured at 750°K. These values are cotnOined with the measured hat effects at 750°Kfor silver, cadmium, tellurium, and zinc to detertrline the heats of formation of the telluride compounds. Cadmium lelluride exhibits a heat of dissolution which has a compositional dependence. THERE is a considerable amount of interest in the compounds of tellurium because of their electronic properties. Both cadmium and zinc tellurides are thermoelectric materials and considerable work has been done on their electronic properties but a limited amount of data is available on their ther-modynamic properties. This work was undertaken to elucidate the heat of formation data on cadmium and zinc telluride. Since both cadmium and zinc are in Group II it seemed to be of interest to compare the values obtained for them with the heat of formation of a Group I telluride. Silver telluride was selected for this comparison. In the course of the work it was also possible to determine the heat of formation of tin telluride and therefore to make a comparison of some of the Group I, 11, and lV tellurides with the metallic elements silver, cadmium, and tin being in the same period. There is also a great deal of interest in the energetic changes which occur upon addition of solute elements to a common solvent. This investigation provided an opportunity to study the partial molar heats of solution of silver, cadmium, tellurium, and zinc in liquid tin. The partial molar heats of solution are of theoretical interest because solute-solute interactions are a minimum in dilute solutions and application of solution models is simpli- fied. In order to complete the analysis of solute-solute and solute-solvent interactions the temperature dependence of the partial molar heats of solution was also measured. MATERIALS AND EXPERIMENTAL PROCEDURE All materials were of the highest purity available. The silver, zinc, cadmium, and tellurium were obtained from American Smelting and Refining Co. and were reported to be 99.999 pct pure. The silver telluride, zinc telluride, and cadmium telluride were obtained from Atomergic Chemetals Co., a division of Gallard-Schlesinger Chemical Manufacturing Corp., and were electronic-grade material of 99.999 pct purity. Tin used for the solvent bath and for calibration was obtained from the Vulcan Manufacturing Co. and was reported as being 99.99 pct pure. The liquid-tin solution calorimeter used in this work is similar in principle to the differential twin-type calorimeter described by K1eppa.l Two of three identical calorimeter wells are used together during any set of experiments, one well being active and the other being passive. The wells are positioned 120 deg apart in an aluminum calorimeter block. Each well contains a multijunction thermopile and a Pyrex test tube to hold the liquid metal bath. Forty-eight of the thermopile junctions are distributed over the surface of each calorimeter well adjacent to the test tube and serve to integrate the heat effects occurring. The other forty-eight are next to the aluminum calorimeter block. The thermopiles for the three wells are connected differentially so that any change in temperature at the outer junctions (which will be the same for both wells because of the high conductivity of the aluminum block) will oppose for the two wells and result in no shift of the zero. The electrical output represents the true temperature difference between the two reaction vessels. A reaction occurring in the active well gives a comparison with another body of very similar thermal properties. In this way, any spurious heat effects due to slight temperature drifts within the entire calorimeter block are eliminated. The output of the differential thermopile goes to a dc amplifier with multiple ranges of from * 10 pv to 1 30 mv. The output of the amplifier is then fed into a Leeds and Northrup strip-chart recorder. The adiabatic temperature change is then calculated using the technique of Howlett, Leach, Ticknor, and ever.&apos; The aluminum calorimeter block is contained in a cylindrical furnace with main and control heaters

Jan 1, 1965

By G. Pomey

Heat-resisting chromium steels and alloys treated at 825° or 9.50°C (1527° or 1742°F) in a carburizing atmosphere exhibit an extensive carbide precipitation. This carbide precipitation may be succeeded by the FeCr a phase or by a carbide with a higher carbon content. Point analyses carried out with an electron mi-croanalyzer make it possible to study the depletion of chromium in the matrix after precipitation has occurred and to determine the chemical composition of carbides. In particular the content in the carbides of Fe, Ni, and W, elements which substitute Cr, can be accurately determined. HEAT-resisting chromium steels and alloys employed in the construction of gas carburizing and carbonitriding furnaces are subjected to a succession of oxidizing atmospheres during heating and cooling and to carburizing atmosphere during isothermal stage. Such a sequence of thermal cycling causes embrittlement and corrosion in the furnace materials. A quantitative study of the structural changes induced in the furnace materials has not received much attention in the past. However, utilization of the electron probe microanalyzer and other modern techniques has permitted a point analysis of the various phases formed and to follow their relative evolution. This paper gives results as regards the nature and composition of the carbide precipitation and the distribution of chromium in the matrix during only the carburizing periods. The structural changes subsequently produced during oxidizing periods will be presented eventually. METHODS AND MATERIALS Metallographic, X-ray diffraction and Castaing electron-probe microanalysis1 techniques have been employed to study carbide precipitation and evolution and the changes in the composition of the matrix in heat-resisting steels and alloys.

Jan 1, 1961