By Samuel Storchheim

IT was noted that variations existed in the magnetic properties, namely, coercive force, He, and rema-nence, Br, of 18/8 stainless steel wires of the same analysis when these wires were given the same percentage of reductiori of area at different rates of reduction. In order to determine the extent of these variations, a program was initiated whereby commercial 302 and 304 stainless steels were drawn with a wide variation of speeds. Ultimate tensile strengths and specific resistances, as well as the Hc-BT measurements, were determined. If variations of considerable magnitude were found, it was thought that the knowledge accrued from the investigation could probably aid in determining the particular drawing speed required to obtain desired properties for a given specification for a particular analysis of wire. Drawing Procedure Two specimens (set I, No. 302 and No. 304), the chemical analyses of which are given in Table I, were drawn at different speeds, namely, 45 to 3900 ft per min, directly from 0.016 in. diam wire to 0.004 in. diam wire, a 93.7 pct reduction of area. To obtain this high percentage of reduction, the wire at 0.016 in. was softened by annealing at 1150°C. It was then strung in a No. 16CF variable speed Vaughn drawing unit and passed through 13 B.&S. gage dies of successively smaller diameter, as shown in the accompanying table. Following this step, several hundred feet of the wire was drawn, at a particular speed, through the dies and wound upon a spool. Once the sample of wire was drawn at the desired speed, the spool with the finished sample was removed, tagged for later identification, and an empty spool was placed in the machine. Another wire sample was drawn at a different speed, after making the necessary adjustments upon the Vaughn unit. At the greater speeds, several thousand feet of sample were drawn to insure that the wire to be used for testing would be uniform. This was done because the desired speed was not reached instantly; the wire taking a short while to attain the required drawing rate. All speed measurements were made by placing a tachometer against one of the machine's pulleys during the actual drawing of the specimens. 84.4 pct reduction of area. The 0.072 in. diameter wire was also annealed at 1150°C. The process of obtaining samples was the same as described above. The only difference between the two was that the rates involved were not as extensive, set II covering a range of 625 to 1150 ft per min. Tensile tests were carried out for the 0.004 in. diam wires on a horizontal Scott Tensile Tester, while tensile tests for the 0.028 in. diam wires were made on a vertical Scott Tensile Tester. Each value listed in the tables represented the average of five samples with a maximum deviation of approximately 3 pct among the samples. Resistance per foot of the wires was determined by use of standard bridges accurate to the nearest hundreth of an ohm for the 0.004 in. wire, and to the nearest thousandth of an ohm for the 0.028 in. wire. The resistances per foot were then converted to resistivities by use of the following equation: P = RxCM where R is the resistance per ft in ohms per ft; CM, the area in circular mils; and P, the resistivity in ohms—CM. The values listed in the tables likewise

Jan 1, 1952

By J. W. Borough

THE electrical conductivity of pure copper is markedly decreased by small amounts of impurity in solution. The magnitude of this effect has been very carefully determined by numerous investigators who studied a wide variety of impurity elements. Much of this work is summarized in an excellent review by Pawlek and Reichel.' The case of zinc impurity in copper is an exception to the above in that there has been no well-documented study of the effect using high-purity starting materials. The values for the effect of zinc on conductivity, which are usually taken from unpublished work by Skowronki, indicate that zinc in low concentration has no effect whatever in lowering the conductivity of pure copper. This effect, if true, is unusual since it is generally known that even in lowest concentration, impurities exert an effect on conductivity which is proportional to the amount dissolved. It is more reasonable to suspect that in the original work on the effect of zinc some of the zinc was oxidized out of solution during specimen preparation. The following experi- and calculated d-spacings based on the unit cell dimensions of Baenziger et al. Since the single crystal studies of Baenziger et al. were limited to (hk0) and (hk 1) data, it was not possible to Compare all the intensities of the powder and single crystal patterns. However, the strongest reflections of both studies, the (321) reflection, agree very well when the appropriate multiplicity factor is used. Good agreement was also found in a number of other reflections of lesser intensity. Despite the precautions taken in annealing the U6Fe powder, an appreciable amount of UO, was detected in the powder pattern after heat treatment. The powder pattern reported by Groganoand Clews is given in Table I. Except for the 3.15A line, which is the strongest line of UO,, their pattern, as far as it goes, compares favoEably with the data from this study. Gordon and Kaufmann have reported a diffraction powder pattern purported to be U, Fe but it bears very little resemblance to the patterns of Table I. ments were carried out to redetermine the effect of zinc on conductivity using high-purity starting materials and processing conditions capable of producing oxygen-free alloys. Materials used in the experiment were ASR 99.999 pct Cu and Cumingo 99.999 pct Zn. Four 1 lb melts were prepared with identical procedure in argon atmosphere with crucibles made from Speer No. 580 graphite. The compositions were 0.0, 0.1, 0.3 and 1.0 pct Zn. Standard No. 14 wire (0.064 in. diam) was made from these melts as follows. The 1 pct Zn sample was first reduced 94 pct by cold swaging with five annealing treatments of 800o for 10 min in hydrogen between swagings, and then reduced 94 pct to the

Jan 1, 1962

By H. H. Smith, G. J. Danek, M. R. Achter

Nickel, Type 316 stainless steel, and copper show decreases in reversed bending fatigue strength with increases in air and oxygen pressure. The leveling off of the log N us log p curve for nickel at 300" and 816°C is discussed in terms of a model in which surface saturation gives rise to a critical pressure. A metallographic study indicated that the effect of environment on crack initiation and growth rates is a function of temperature. It is shown that small amounts of impurities in inert gases may substantially reduce the fatigue strength of nickel. 1n a previous investigation1 of high-temperature bending fatigue in air and in vacuum, reversals in the effect of environment with changes in test conditions were atrributed to a mechanism consisting of two processes acting in competition. One of them, oxidation strengthening, has been demonstrated in a straightforward manner by measuring the rupture strength of a sintered nickel-oxide bond.' The detailed operation of the other process, facilitation of crack propagation by surface absorption of oxygen, is uncertain. Thompson et UZ advanced the possibility that the formation of an oxide layer prevented rewelding of cracks during the compressive part of the cycle, while Wads worth and Hutchings4 further proposed that the reaction of oxygen with atoms at the tip of the crack helped the metal to break there, a possibility which has also been advanced to explain crack formation in creep.5 A difficulty in arriving at a mechanism for this lowering of fatigue strength in air is the inconsistency of some of the data. For example, Wadsworth and Hutchings4 found an approximately linear decrease of log cycles-to-fracture (N) with an increase of log pressure-of-air (p) for copper and aluminum at room temperature, while snowden,' although finding a similar linear dependence for aluminum, observed a stepped curve for lead. Between l0-' and 10"1 torr there is a sharp decrease in the fatigue life of lead with increasing air pressure, but plateaus, signifying no dependence on pressure, are found at higher and lower pressures. If, as discussed elsewhere: these environmental effects arise from the adsorption of gas on crack surfaces, it would be expected that as the pressure is increased a saturation point would be observed, beyond which there is no further effect. To gain further information about the form of the log N vs logp curve, it was decided in the present investigation to repeat this type of measurement at elevated temperature on nickel, copper, and Type 316 stainless steel. An additional object of this program was

Jan 1, 1963

By E. E. Underwood, L. L. Marsh

Aluminum single crystals, alloyed with 0.042 atomic pet Cu and 0.11 and 1.1 atomic pct Mg, were subjected to constant stress creep tests, tensile tests, and hot hardness measurements within a temperature range of 300° to 866OK. Calculations based on Dorn's temperature-compensated time parameter, 6, gave a value of DH, = 27,000 cal per mol for the activation energy of early creep in aluminum single crystals. Correlations have been obtained for aluminum alloy single crystals with the parameter E for solid solution strengthening, as well as with the parameter F for solid solution hardening, by using a valence of three for aluminum. Limited measurements on tensile specimens show that the slip band density tends to decrease with increasing temperature and with decreasing solute concentration. INCREASING interest is being shown in the mechanisms of plastic deformation in single crystals during tensile and creep testing. The complexity of deformational processes in polycrystalline materials has led to a search for simpler experimental conditions. Numerous creep and tensile investigations have been conducted with pure, metallic single crystals. To a lesser degree, the effects of alloying elements on the tensile properties of single crystals have been determined. However: the literature dealing with the effects of alloying additions in single crystals under creep conditions is vanishingly small. This paper represents an attempt to narrow this gap in the knowledge of the subject. Previous investigations of creep behavior at the Battelle Memorial Institute1-1 have been of great value in the analysis of the present single crystal data. It is equally desirable, however, to ascertain the extent of correspondence between the behavior of single crystal and polycrystalline materials. For this purpose, correlations, similar to those developed for polycrystalline aluminum alloys by Dorn and co-workers, have been made with the single crystal data. The results from this study have tended to confirm and extend those correlations to the case of alloyed single crystals. Materials and Procedures Three dilute binary aluminum alloys were prepared for this investigation from 99.99 + wt pct Al, 99.8 wt pct Mg, and 99.92 wt pct (electrolytic) Cu. The nominal compositions of the alloys were 0.042 atomic pct Cu, and 0.11 and 1.1 atomic pet Mg. Precautions were taken to avoid contamination of the stock during melting and casting of the alloys. After a heat treatment of 8 hr at 925°F the alloys were extruded, then machined into) threaded tensile specimens with a 3 in. reduced section and a 0.505 in. diam. Spectrographic examination showed less than 47 ppm metallic impurities in each alloy. The single crystals were grown by the strain-anneal method, with a critical strain of about 11/4 pet giving the optimum results. In general, 3 in. crystals were obtained with the Al-Cu alloy, but smaller crystals in the magnesium alloys necessitated the use of 2 in. and 1 in. gage lengths with the low and high magnesium alloy specimens, respectively. After an electrolytic polish, the orientation of that portion of the specimen containing the largest single crystal was determined from Laue back-reflection photographs. Tensile tests were conducted at a constant load rate of about 2 lb per min. Creep runs were made in a constant temperature room, under constant stress at the higher creep temperatures, and constant load at the lower temperatures. The eloneation was measured to within ±5 microin. by a specially designed capacitance extensometer. The ex-tensometer arms were attached to the 3 in. specimens at the shoulders of the test piece or, where the crystals were smaller than 3 in., by knife-edge grips.

Jan 1, 1957

By R. I. Jaffee, F. C. Holden, H. R. Ogden

The effects of ternary and quaternary additions of aluminum, oxygen, and carbon on the mechanical properties of high-purity titanium-molybdenum alloys were studied for several microstructural conditions. Heat treatments were designed to produce 1) ß-quenched, 2) equiaxed ß) transformed (acicular) and 4) stabilized -P microstructures. Tension, impact, and hardness tests were performed. Transformations from the ß phase were followed by hardness measurements and metallography. The ß-to-w transformation was slowed by aluminum additions; carbon and oxygen additions increased the transformation rate. In addition to solid-solution strengthening, these solutes may increase or decrease strength by altering the /3 transformation kinetics. Aluminum additions promote the formation of strain-induced martensite, and lower yield strengths at compositions near 12 pct molybdenum.. a-P alloys are more ductile with equiaxed than with transformed microstructures. High strength levels can be reached by aging in many cases. Strength levels of the aged specimens usually are lowered slightly by straining prior to aging. ALLOYS of molybdenum with titanium form an iso-morphous alloy system which has been the subject of several investigations. Additions of substitu-tional and interstitial -stabilizing elements provide means of improving mechanical strength and con- trolling the heat-treatment response of the binary alloys. The work reported here forms a part of a continued study of the effects of microstructure on the mechanical properties of high-purity titanium alloys. Previous papers have considered the various binary alloys (Ti-Mo, Ti-Al, Ti-C, and Ti-0) that form the bases for the ternary and quaternary alloys included here. The compositions were selected to correspond with the previous binary alloys. Further, the high purity of the alloying components was maintained, so that direct comparisons with earlier work can be made. The total research program included a large number of compositional, microstructural, and testing variables. The data reported here have been selected to provide a reasonably complete and representative summary of the results. The reader is referred to the original Air Force Report for a complete tabulation of the results. EXPERIMENTAL PROCEDURES All the alloys used in this work were prepared from high-purity electrolytic titanium produced by the U.S. Bureau of Mines. A typical furnished analysis showed the following impurities in wt pct, balance This analysis is equivalent to that of iodide-refined titanium. In addition, hardness, tensile, and impact tests made using unalloyed electrolytic titanium showed it to have properties equivalent to those obtained with iodide titanium and suitable for these studies of high-purity base alloys.

Jan 1, 1962

By R. J. Towner

Tensile properties of Aluminum Powder Metallurgy (APM) products at 600°, 800°, and 1000°F were lowered by cold reductions of as little as 10 or 20 pct. The detrimental effect of cold work on yield strength at elevated temperatures increased with temperature. Heating cold-worked products at 850° to 1150°F removed the structural effects of cold work through the process of recovery and restored, at least partially, the strength at 600°F to the level of hot-worked material. Material containing 5 pct A1203 was recrystallized by cold reductions of 97 pct or more followed by annealing at 1100°F. Recrystallization lowered sharply the strength at room temperature, but raised the strength at 600°and 800°F relative to that of the cold-worked state The high strength of Aluminum Powder Metallurgy (APM) products at elevated temperatures'-4 is well-known. In this paper, some conditions of processing that can affect this important characteristic are presented. The following nomenclature will be used to identify different alloys: All of the above alloys are of the aluminum-aluminum oxide type made from milled powders of commercially pure aluminum with the exception of M486, which is fabricated from atomized A1-Fe alloy powder. The products made from milled powders are hardened by a dispersion of aluminum oxide par- ticles in the aluminum matrix, while the intermetal-lic compound FeAL is the dispersion hardening agent in M 486.' The process used for making all APM products involves the application of heat and pressure to form a compact from powder which is fabricated into an extrusion, sheet, strip, or wire by standard techniques. Probably the most common cold-worked APM product is sheet. Cremens, Bryan, and rant' determined the room-temperature tensile properties and the 600°F stress-rupture properties of XAPOOl and XAPOO3 sheet and reported that there was little difference between the as-extruded, cold-worked, and annealed at 1200°F conditions. On the other hand, Emmons6" found that the tensile and stress-rupture properties of XAPOOl and XAPOO3 sheet at 600" and 800°F were lower than those of extrusions. The tensile properties of XAPOO3 sheet were also determined at elevated temperatures by Doyle' and ~ayward.' According to Friske" and Kendal et a1.," cold working by swaging, rolling, and tube drawing reduced the tensile and creep-rupture strength of XAP 001 Recrystallized aluminum powder metallurgy products are rare because the dispersion in the aluminum matrix is usually too fine, uniform, and concentrated to permit recrystallization. However, Lenel12 was able to recrystallize wires made from aluminum powders containing about 1.75 and 3.0 pct oxide and found that the tensile properties at room temperature remained higher than those of annealed commercially pure aluminum because of the dispersed oxide particles. Westerman and Lenel13 found the kinetics of recrystallization of the powder products were very different from those of cold-drawn commercially pure aluminum wire. The alloy containing 3.0 pct oxide recrystallized to a very coarse grain size was more creep-resistant at 400" to 600°C (752" to 1112°F) than in the as-extruded, fine-grained condition, according to Ansell and weertman.14 Ansell and aenel" further studied creep at 500" to 620°C (932" to 1148°F) of recrystallized 1.75 pct oxide wire and confirmed the creep model of Ansell and Weertman. The present work is being reported for the fulfillment of the following objectives: 1) to show the effect of cold work on tensile properties at elevated temperatures;

Jan 1, 1964

By E. S. Greiner

STUDY of the plasticity of germanium or other semiconductor crystals affords unusual opportunities to extend our knowledge of deformation mechanisms. Crystals are available having extraordinary perfection and very high purity. They deform by slip on the systems {111} <110>,1-3 as do crystals of the simple face-centered-cubic structure. Dislocations generated in them during slip are easily revealed in the form of etch pits on either (111) or (100) surfaces.4,5 This fact alone makes possible more detailed studies of mechanisms than is usually the case with metals but, even further, the effect of deformation on their electrical conductivity is very large compared with metals. This comes about not only because the mobility of the charge carriers is reduced, as in deformed metals, but also because the number of these carriers is greatly altered. This latter effect seems closely related to the formation of both line and point imperfections during deformation and thus provides a needed tool for the study of the kinds and distributions of these imperfections. Other investigators have deformed germanium at elevated temperatures by bending,1, 6-8 compres-sion,6, 0,10 tension,2,3,6,11,12 torsion,23 and indentation." Wang and Alexander" have also reported successful indentation at room temperature. Dislocation etch pits consequent to deformation have been observed and studied.7,8,10,18,14,20 The experiments to be de- scribed here include principally the compression and the subsequent annealing of germanium with concomitant studies of etch pits, microstructures, and electrical properties. Both single crystals and heavily twinned specimens were used. Some indentation studies are included. Experimental Methods Plastic compression was effected in the apparatus shown schematically in Fig. 1. It consists of two tantalum platens contained in a helium atmosphere and so arranged that pressure can be applied by a hydraulic press. The specimen between the platens is heated by the surrounding furnace. The specimen is usually a small crystal cube about 0.30 in. on an edge. A control specimen is always inserted so, that it is subject to the same thermal cycle as the one being deformed. This serves to detect any impurity contamination that might accompany the thermal treatment. For high temperature work, where such impurity contamination often occurs, the specimens were first plated with gold whenever subsequent electrical properties were to be determined. This method" is effective in preventing significant contamination of germanium up to temperatures at least as high as 750°C, as evidenced by the constancy of the electrical conductivities of control specimens subjected to the same heat treatments. The total range of temperature used for deformation was from 375°C, the lowest at which significant flow was observed, up to 900°C. Microscopic examination was made after mechanical and chemical polishing and etching. Dislocation pits were revealed with CP-4 etchant by the tech-

Jan 1, 1958

By A. C. Losekamp, R. M. Fincel, J. B. Conway

TANTALUM like several other metals exhibits a great affinity for or reactivity with certain gases. Tested in atmospheres which are not completely pure this metal becomes contaminated by certain impurities (notably nitrogen, oxygen, and hydrogen) with a resultant change in various properties. Well-known are the drastic changes in hardness, ductility, and electrical resistivity. Also previously recorded are the distortions of the lattice1,2 accompanying the increased content of oxygen and nitrogen in tantalum. This pronounced affinity for certain gases along with the significant property variations thereby produced makes it necessary to observe additional experimental precautions in making various property determinations with tantalum. Some recent measurements of the linear thermal-expansion characteristics of tantalum have made this point quite emphatically. Failure to observe the greatest precautions in reducing the contaminating influence has led to some extremely distorted results. Not only does such operation lead to different heating and cooling curves during the thermal-expansion measurements, but upon cooling to room temperature the sample is found to have suffered a permanent (actually semipermanent since the specimen can be returned to its original length by a 3-hr degassing treatment in vacuum at 2300°C) elongation. In addition, subsequent heatings will not follow the initial heating curve unless the expansion measurements are based on the actual specimen length at the beginning of the heating cycle. These thermal-expansion measurements were made by positioning the specimen horizontally at the longitudinal midpoint of a 20-in.-long, 4-in.-diam resistively heated tungsten tube furnace. The specimens were in the form of 20-mil sheet formed into a sharp U-shape about 0.3 in. in width and 0.3 in. in depth. Fiducial marks in the form of 0.010-in. holes drilled at either end of the 2.5-in.-long sheet specimens were viewed by a paired filar micrometer telescope system mounted on an Invar bar on the top of the furnace. Tests were made in helium with temperatures measured by a Pt/Pt-lORh thermocouple to 1000°C; above 1000°C temperature was measured by means of an optical pyrometer sighted into a black-body hole drilled into the specimen-holding fixture in the vicinity of the specimen. Previous tests with black-body holes drilled in a 0.25-in.-diam rod specimen had confirmed the temperature uniformity between specimens and specimen-holding fixture in this furnace. A typical thermal-expansion curve for arc-cast tantalum in helium is shown in Fig. 1 for the case where no attempt is made to remove all the impurities from the cover-gas atmosphere. The initial heating curve appears smooth and has a shape characteristic of all metals. However, it is known that the sample begins absorbing impurities at temperatures above 1000°C which are sufficient to distort the lattice and lead to specimen lengths which are somewhat larger than would be obtained in the absence of contamination. During the cooling cycle the expansion curve is seen to be significantly different from the heating curve. This is due to the impurity content causing a semipermanent (i.e., permanent until the impurities are removed by vacuum degassing) deformation which will not allow the speci-

Jan 1, 1965

By J. H. Wernick

IN temperature-gradient zone-melting1 a molten zone is moved through a solid or across a solid surface by the establishment of a temperature gradient. This technique has both practical and fundamental aspects. One practical application is to make p-n junctions for semiconductive devices, particularly for devices in which the junctions are desired within the semiconductor. From a fundamental point of view, the technique is being investigated as a method for determining diffusivities in liquid alloys, and preliminary diffusivity results have been reported by the writer." In this paper, the effects of crystal orientation, temperature, and molten zone thickness in temperature-gradient zone-melting, and the bearing of these effects on diffusivity measurements and n-p-n junction formation are discussed. Experimental Procedure An effect of crystal orientation was noted in early experiments. To facilitate its study, movements of wire zones across a surface, rather than through the body of a single crystal, were observed for various surface planes and travel directions. The experirr-entai setup is illustrated in Fig. 1. The graphite end-section for the high temperature heater has an apron about 1/16 in. above the upper surface of the crystal. This apron insures that the surface temperature of the block is equal to or greater than the temperature within the block at every point, Thus, the zone does not penetrate the block and convection in the liquid is minimized. The experi-through a block is shown in Fig. 2,

Jan 1, 1958

By W. A. Backofen, R. L. Fleischer

Single crystal, bicrystal, and polycrystal tensile tests of aluminum at 4.2°K, 77°K, and 300°K have been used to examine the role of grain boundaries in the deformation process. Results indicate that a grain boundary may affect the extent and slope of easy glide. The stage II hardening rate, on the other hand, is independent of the presence or absence of grain boundaries. This conclusion allows the size of the region of multiple slip caused by an incompatible grain boundary to be determined. For the size of bicyystal sample used in this study, multiple slip occurs in about half of the cross section. PREVIOUS studies of the stress-strain characteristics of bicrystals of face-centered-cubic metals have been limited to aluminuml-5 at room temperature. Recent results, however, indicate that the stress-strain curves of single crystals of such metals may be separated into at least three stages6 in which different deformation processes are occurring7 provided testing is done at sufficiently low temperatures.&apos; Since for aluminum a well-defined stage II develops only below room temperature, previous studies have not been able to relate effects of grain boundaries to all of the three stages of deformation. It is therefore to be expected that low-temperature deformation of aluminum single crystals and bicrystals should clarify the effects of grain boundaries on the different processes of deformation. EXPERIMENTAL PROCEDURE Single crystals and bicrystals were grown from the melt by the standard techniqueg with aluminum reported by Alcoa to be 99.993 pct pure. Ridges in the boat were used to guide the grain boundary during growth, assuring that the boundary would bisect the sample.10 The rate of furnace motion during growth was 1.0 cm per hr. During growth zone purification resulted, as evidenced by the ability of the first material to freeze to recrystallize at room temperature following severe deformation. Samples were approximately 4.4 X 6.6 mm in cross section and 103.5 mm in length between grips. Samples were annealed at 635" i 5°C for 40 hr and furnace cooled over a 7-hr period. They were then electropolished in a solution of 5 parts methanol to 1 part perchloric acid at a current density of 15 amp per sq dm for about 30 min at temperatures below 0°C. Tensile testing was performed at 295" (room temperature), 77" (sample in liquid nitrogen), and 4.2"K (sample in liquid helium) on the hard-type machine indicated schematically in Fig. 1. The machine con- sists basically of a tube surrounding a rod; one end of the sample is attached to each member, and the rod is pulled up the tube to extend the sample. The rod is rigidly mounted and is moved vertically by a system described by asinski." The pulling force is measured continuously by an electrical strain gage load cell, and the relative displacement of the tube and rod is also recorded continuously by a soft cantilever beam with electrical strain gages. Maximum stress and strain sensitivities were ±2g per sq mm and * 3-10-5. In all tests the strain rate was approximately 5.10-5 per sec. The thin wires in the tensile apparatus introduce softness, which may be corrected for, however, by measuring load vs displacement with the sample replaced by an elastic member. For loads greater than 15 kg the spring constant is 1.875.106 g per cm. The flexible wires also served to reduce substantially the large shearing forces which may arise in the case of grips having horizontal rigidity.&apos;&apos; As in any gripping system, however, bending moments will arise in the course of deformation by single slip. Engineering stress, s = (load)/(original cross-sectional area), and strain, E = (increase in length)/ (original length), are used for stress-strain curves unless otherwise indicated. Tables list resolved shear stress, T=mo and shear strain ? = dm, where m is the usual Schmid resolved shear stress factor for the primary slip system at the start of deformation. The first group of samples to be described forms an isoaxial set, all of the crystals making up the single crystals or bicrystals having the same tensile axis, the orientation of which is indicated by the cross in Fig. 2. For this orientation the primary slip plane and slip direction make angles of 45 deg with the tensile axis and the Schmid factor m has its maximum possible value of 0.5. Rotations about the tensile axis are indexed by means of an angle 0 between the small-area surface of the samples and the projection of the primary slip direction onto the cross section, as defined in Fig. 3. In single crystals, values of 0 were 0 and 90 deg, while in bicrystals 0 values were (0 deg, 180 deg), (90 deg, 270 deg), and (0 deg, 90 deg) as indicated in Fig. 4.

Jan 1, 1961

By H. I. Aaronson, S. Toney

When the component grains of .ferritic hicrystals of an Fe-1.55 pct Si alloy are disoriented through an angle "6 " about a conzmon [ll0] axis, the tendency for preferential growth of austenite crystals along the grain boundary during transformation at elevated temperatures is small when 11 deg, but increases rapidly at larger angles. This type of orientation-dependence indicates that grain boundary diffdsion promotes preferential growth along large-angle boundaries. Morphological differences between austenite crystals formed at small-angle [1101 and [loo] boundaries suggest that precipitate morphology can be dependent on the dislocation structure of the boundary. ThE morphology of precipitate crystals nucleated at a grain boundary can be significantly affected by the structure of the boundary.&apos; The limited amount of experimental evidence available in the literature indicates that the morphological effects of boundaries made up of arrays of dislocations, such as subbound-aries and small-angle grain boundaries, are different from those of boundaries having essentially disordered structures, i.e., large-angle grain boundaries. On the basis of indirect evidence, it has been concluded that large-angle grain boundaries give rise to the formation of grain boundary allotriomorphs (crystals which nucleate at grain boundaries, and grow preferentially and more or less smoothly along them)2 in the proeutectoid ferrite and the proeutec-toid cementite reactions in plain-carbon steels, and apparently also in many non-ferrous alloys.&apos; At small-angle grain boundaries in a plain carbon steel, on the other hand, ferrite crystals were found to take the form of primary side plates. Similarly, Guinie, loys. Primary sideplates formed at a subboundary with a constant orientation tend to be parallel to only one, or occasionally two matrix habit planes, and a marked change in the orientation of the boundary is accompanied by a change in the habit plane. Previous studies on the morphological effects of grain boundary structure were performed on poly-crystalline aggregates. Information on the disorien-tation of the pairs of grains forming the boundaries at which the various morphologies appeared in these specimens was largely either qualitative or semi-quantitative. Precipitate morphologies accordingly could not be accurately and systematically correlated with grain boundary structure, and thus theories which have been proposed for the various morphological effects could not be satisfactorily tested. This investigation was undertaken in an attempt to remedy these deficiencies by studying the morphological effects of grain boundary structure with a method in which the boundaries are formed by matrix grains whose disorientations are known and controlled with reasonable accuracy. EXPERIMENTAL PROCEDURE The crystallographic requirements of this study were fulfilled by means of oriented bicrystals of silicon-iron. Disorientation of the component ferrite crystals was carried out about common, major crystallographic axes through angles ranging from 1/2 to 44 deg. The silicon content was low enough SO that the bicrystals could be partially transformed to austenite by heating to elevated temperatures. The silicon-iron used had the following initial composition: 1.55 pct Si, 0.04 pct C, 0.0031 pct N, 0.17 pct Mn, 0.020 pct S, and 0.002 pct P. The alloy was obtained in the form of 0.036-in. sheet. The procedures employed to prepare seed crystals in strips of this sheet, to reorient the seeds, and to grow them into bicrystals are essentially those described by Dunn and Nonken and aynes." The characteristics of the bicrystals are given in Table I. The "bicrystal type" indicates the crystallographic plane parallel to the broad faces of the strip in both grains and the crystallographic direction which was parallel to the long edges of the strip in both grains prior to disorientation. The angular disorientation of the grains, 8, which was performed about the direction normal to the plane of the broad faces of the strip, was measured between the [ 00l] directions. Orientation of the grain boundary, , was taken as the angle between the plane of the grain boundary and a plane containing the axis of disorienta-

Jan 1, 1962

By A. A. Burr, D. G. Ebeling

The effects of casting texture, grain orientation and grain size upon the performance of Alnico permanent magnets is described. Single-crystal specimens were produced by special sintering and grain coarsening techniques to study the effect of crystal orientation. In addition to texture and orientation effects, an analysis of the results indicates that the permanent magnet performance is impaired by a refinement of the grain size. AN excellent historical review of the development of Alnico permanent magnets has been prepared by Bozorth.1 The desirable permanent magnet characteristics of Fe-Ni-A1 alloys were discovered in 1932 by Mishima.2,3 The work of Ruder&apos; showed that the alloys were age-hardenable, and Betteridge5 defined the best composition and heat treatment for the magnetically isotropic alloy known as "Alnico 3." Horsburgh and Tetley0 increased the energy product by the addition of cobalt and copper, "Alnico 2," and Oliver and Sheddon7 demonstrated that cooling in a magnetic field improved the residual induction of this alloy. Jonas8,9 then disclosed the great practical benefits of heat treating an alloy of higher cobalt content in a magnetic field and the resulting alloy, "Alnico 5," has become the standard of the industry. This paper describes the fundamental aspects of a procedure which can be used to further improve the properties of these anisotropic permanent magnet alloys. A study of the casting techniques used in the production of anisotropic Alnico permanent magnets indicated that the magnetic quality was affected by the as-cast macrostructure. Improved performance was observed in magnets containing a high percentage of columnar grains whose long axes were parallel to the magnetic axis of the casting. McCaig10 studied the effect of such columnar grain structures upon the magnetostriction characteristics of similar alloys, however no data was presented showing the effects on other magnetic properties. The following paragraphs describe two experiments which were conducted to determine the effect of various grain orientations upon the energy product. Special composite molds were prepared of highly conductive and highly refractive components to remove the heat of solidification from the casting in a controlled manner. Representative macrostructures produced by these techniques are shown in Fig. 1, along with the relative volumes of favorably oriented columnar grains. The alloy, Alnico 5, has the highest permanent magnet performance of any commercial magnet material. It has the nominal weight composition of 8 pct Al, 14 pct Ni, 24 pct Co, 3 pct Cu, and 51 pct Fe. A heat of this material was cast into molds producing the type A and B grain structures shown in Fig. 1 and pairs of the resulting magnets were placed in heat-treating boats so as to eliminate any biasing effects of boat position. After a standard heat treatment the type A magnets, with 16 pct of the volume composed of favorably aligned grains, had a maximum energy value of 3,940,000 gauss-oersteds, while the type B magnets with 73 pct aligned grains averaged 5,090,000. This large im-

Jan 1, 1954

By W. R. Hansen, F. W. Boulger

Twenty-nine laboratory steels were studied to determine the effects of composition and ferrite grain size on drop-weight and Charpy V-notch transition temperatures. The experimental steels covered the following ranges in composition.. 0.10 to 0.32 pct C, 0.30 to 1.31 pct Mn, 0.02 to 0.43 pct Si, md nil to 0.136 pct acid-soluble Al. Although most of the data were obtained on hot-rolled samples, some plates were heat-treated in order to cover a wider range in ferrite grain size. The experimental data were used for a multiple-correlation analysis conducted with the aid of an electronic computer. The study showed that carbon raises and that manganese, silicon, aluminum, and finer ferrite grains lower both drop-weight and Charpy transition temperatures. Quantitatively, variations in composition and grain size have a more marked effect on V15 Charpy transition temperatures than on the drop-weight transition temperature. Useful correlations were found between transition temperatures in drop-weight tests and those defined by seven different criteria for Charpy tests. Evidence was accumulated that the conditions ordinarily used for drop-weight tests are more severe for 1-1/4-in. -thick plate than for 5/8- to 1-in. -thickplate. PROJECT SR-151, to study quantitatively the effects of metallurgical variables on performance in the drop-weight test, was established by the Ship Structure Committee late in 1958 on recommendation of the National Academy of Sciences, National Research Council. This project was initiated as a result of the increasing use of the drop-weight (nil-ductility) test in predicting the ductile-to-brittle behavior of steel. Qualitative data indicated the drop-weight was not as sensitive to metallurgical variables as the Charpy V-notch test. Furthermore, the available information indicated that the drop-weight test did not show the superiority of killed steels over semikilled steels reflected by Charpy tests. This difference in sensitivity to brittle fracture is considered important because the drop-weight transition temperature has been reported1 to correlate better with service-temperature failures than the V-notch test does at a constant energy level. Therefore, this project was concerned with establishing quantitatively the effects of metallurgical variables in the drop-weight test. For comparison, Charpy V-notch data were obtained for the steels investigated. This paper summarizes the results of the investigation. Most of the steels used for the study were made and processed in the laboratory. However, some tests were also made on commercial killed steels available from Project SR-139 (SSC-141). During the course of the investigation, data were obtained on the effects of carbon, silicon, manganese, and aluminum on transition temperatures of drop-weight and Charpy specimens. In addition, the effects of heat treatment which changed the ferrite grain size and the transition temperatures were also investigated. Finally a few exploratory studies were made on commercial killed steels to evaluate the effects of plate thickness, grain size, and heat treatment on the performance of drop-weight specimens. EXPERIMENTAL PROCEDURES Preparation of Materials. A total of twenty-nine 500-lb induction-furnace heats were made and processed in the laboratory for the investigation. Carbon, manganese, silicon, and aluminum contents were systematically varied. Melting and rolling techniques proven satisfactory in a previous project2 were used as a guide for the current investigation. Composition. The composition of the twenty-nine laboratory heats made for this project are given in Table I. The steels are divided into three groups. The first group consists of ten aluminum-killed steels similar in composition to Class C ship-plate steel. The second group consists of ten semikilled or Class B type steels. In both of these groups the carbon and manganese contents were intentionally varied over a wide range. This wide range in composition was helpful in obtaining quantitative data from a limited number of steels. The primary purposes of these two groups of steels was to determine the effects of carbon, manganese, and deoxidation practice. In addition, one steel in each group (Steels 2-2 and 9-2) were made about 1 year after the start of the program in order to check consistency of melting practice. The third group of nine steels listed in Table I was intended for studies on the effects of silicon and aluminum. In eight of these steels carbon and manganese were held relatively constant at levels of about 0.2 and 0.8 pct, respectively, while silicon and

Jan 1, 1963

By G. W. P. Rengstorff, L. E. Olds

High purity molybdenum ingots containing controlled amounts of a single impurity element (oxygen, nitrogen, or carbon) were prepared. These ingots were tested for ductility by bending test specimens at various temperatures. The relationship between the plastic behavior of the ingots and their chemical composition has been determined. MANY proposed applications for molybdenum require ductility at or near room temperature. At the present time, it is possible to obtain wrought molybdenum with considerable ductility only if special fabrication techniques are used to control the grain structure. Starting with are-cast or powder metallurgy ingots, the usual methods for obtaining ductility rely on fabrication procedures that result in fibered microstructures in the finished product. Recently, it has been found that the ductility of either powder metallurgy or are-cast molybdenum can be improved by uniform recrystallization of the metal to a very fine equiaxed grain structure.&apos; The need for a fibered or a fine grained structure may limit the practical usefulness of molybdenum. For example, welding. which may be used in fabricating the metal, generally produces coarse grained structures that lead to brittleness. This applies, certainly, to currently available commercial molybdenum. Although commercial molybdenum is brittle when the grains are coarse, it has been shown experimentally that fine grained structures are not always essential for ductility. For instance, as-cast molybdenum with a coarse columnar grain structure is ductile if it is sufficiently pure.&apos; Because high purity cast molybdenum has good ductility even when coarse grained, it is probable that the brittleness in coarse grained commercial molybdenum is caused by the impurity content of the metal. Although the general effects of impurities on the cold ductility of molybdenum have been known in a qualitative manner for some time, no quantitative evaluation of these effects has been available. The present investigation was made in order to determine more accurately the effects of oxygen, nitrogen, and carbon on the cold ductility of cast molybdenum. Oxygen has long been known to be detrimental to ductility, although the minimum amount which will embrittle molybdenum has been open to speculation. Parke and Ham" showed that ingots with oxygen contents above 0.003 pct could not be forged. Maringer and Schwope have described the embrittle-ment of molybdenum wire by oxygen. A discussion on the effects of heat treatment on the distribution of oxygen in molybdenum has been given by Perry, Spacil, and Wulff." Although nitrogen would also be expected to have harmful effects on ductility, no extensive work has been done previously to determine whether this is so. However, Tury and Krausz" found that wires presumably with less than 0.007 pct N were brittle. Carbon is added to commercial cast molybdenum for deoxidation. Parke and Ham" have shown that molybdenum containing as much as 0.06 pct C could be forged if the oxygen was kept below 0.003 pct. Also, Bruckart and others&apos; found that the room temperature ductility of sintered molybdenum improved with carbon contents up to 0.84 pct. However, Rengstorff and Fischer&apos; found that residual carbide particles in cast molybdenum apparently had an unfavorable effect on room temperature ductility.

Jan 1, 1957

By S. I. Liu

THE effects of strain histories, consisting of several prestrains in opposite directions, on the flow and fracturing characteristics of metals determined in a final test have been investigated previously.&apos;" Such strain histories vary from a single prestrain in tension or compression to the number of strain cycles leading to fatigue failure.&apos; Between these two limits, various strain histories could be visualized and some can be attained readily. One such example is a strain history consisting of a first prestrain in tension of various magnitudes and a second prestrain in compression also of various mag-nitude. In this investigation the strain history was extended to the combination of these two limits, i.e., a single prestrain in tension or compression followed by balanced strain cycles of a selected magnitude e, = k0.12. It was found in this case that only compressive initial prestrains could be investigated with sufficient accuracy.* Such strain histories can be considered also as (low cycle) fatigue tests of a metal subjected to various amounts of cold working. It appears from previous publications that cold working within a wide range of reductions usually raises the un-notched fatigue strength of many metals.&apos;-&apos; This effect, however, has been found to be inconsistent and sometimes reversed for other metals?.7 Furthermore, Ludwik reports that the yield strength of cold-worked specimens may be reduced by cyclic strains, while that of materials without cold work is generally increased in the initial cycles." " In addition to the above tests, a study was made of the effect of intermediate re-solution heat treatment on low cycle fatigue behavior. Such anneals should eliminate the strain hardening induced by the cyclic strains. As far as their effect on the fracture characteristics is concerned, a few previous tests seemed to indicate that the damage resulting from cyclic strains is retained only partially after heat treatment." A further investigation was made in which one specimen was subjected to repeated unbalanced tension cycles in which the strain interval was approximately $ 0.013. This repetition of plastic tension damages the material slightly. This result appears to confirm Ludwik&apos;s observations." " Commercial 3/4-in. rod of the aluminum alloy 24ST4 was selected for this investigation. The material was subjected to the following treatments before machining: 1—Re-solution treatment at 920" ± 10°F for 45 min, 2—water quench at room temperature, and 3—aging for four days at room tem-perature.? The treated material then was machined to desired specimen contour and tested. A coolant was used during machining to minimize any artificial aging effects of heating during machining. In some cases the 24ST4 specimens were reheat treated after having been strained. In these cases, the heat treatment was the same as the re-solution heat treatment described above. Procedure As shown in Fig. 1, threaded end specimens with a minimum diameter of 0.266 in. and a contour radius of 2 in. were used for prestraining to an axial compressive strain ranging from 6, = —0.10 to E, = —0.48. For large prestrains, two consecutive corn-

Jan 1, 1952

By D. W. Lillie

Property changes produced by irradiation of Al-0.4 wt pet Li alloys at 270°C to a burnup of 0.155 pct of all atoms are described. Metallographic evidence of the formation of internal pores and the concentration of gases at grain boundaries is shown. Some conclusions are drawn concerning desirable property characteristics for resistance to radiation swelling. RADIATION induced gases are of great practical significance in nuclear engineering since they affect the behavior of fissionable fuels and control rod materials. In fuels the gases xenon and krypton are the major offenders, producing serious em-brittlement at low irradiation temperatures and gross swelling at high irradiation temperatures. In control rod materials containing boron, the production of helium from the B 10 (n, 0) Li7 reaction produces similar reactions. Since the trend in reactor design is for operation at increasingly high temperatures, the phenomenon of high-temperature swelling by these induced gases has been the subject of considerable recent study. The objectives of such work have been to obtain engineering information and quantitative data on the effects in specific fuels and control rods and to obtain further understanding of the mechanism of gas damage so that more intelligent corrective steps can be made. Analogue systems are often useful for the latter objective and in this case alloys containing Li are suitable in view of the reaction Li6 + n - He4 + He 4. Both products are gases and no serious radiation problem is produced to complicate post irradiation handling. Considerable caution is, of course, necessary in any operations in which tritium release is possible. The present program was initiated to provide a detailed study of the effects of He + H3 generated by irradiation in Li-bearing alloys. The results on Mg-Li solid solution alloys have been reported elsewhere.&apos; This paper presents information on irradiation of an A1-0.4 pct Li alloy in which the lithium was present as highly enriched Li6 in order to maximize the radiation burnup. PROCEDURE The original intent in the selection of the alloy content was to have Li in solid solution at all temperatures. It became apparent, however, that the solubility of Li in A1 was substantially lower than that reported in the original reference consulted.&apos; This was substantiated by the work of Nowak3 who reported solubility of less than 0.01 pct Li at 100°C. The alloy used (0.4 pct Li) was therefore two phase at room temperature. The irradiation temperature was estimated to be about 270° C, and at that temperature all or almost all of the Li would be soluble under equilibrium conditions. The precise state of the alloy under irradiation is not known. Aluminum used was 99.996 pct purity (max. impurities Si 0.002 pct, Mg 0.001 pct, Fe 0.0005 pct, and Cu 0.0005 pct). The lithium was obtained from Oak Ridge National Laboratory; 96.1 + 0.1 pct of the lithium was ~i~, but chemical impurities were 0.25 pct Ca, 0.05 pct Fe, 0.02 pct Na, 0.02 pct Cu, 0.01 pct Sr, and 0.01 pct Ba. The two metals were melted in an alumina crucible in a resistance heated furnace in an atmosphere of helium. A l-in. ingot was cast in an iron mold, machined to %-in. round, hot swaged (350°C) to 0.080-in. round, cold swaged to 0.060-in. round, and finally cold drawn to 0.040-in. round. Four-inch wire lengths were then cut and annealed at 250°C for 4 hr in helium. Irradiations were carried out in a VT hole in the Argonne CP-5 reactor. The wires were held in an aluminum jig, sixteen wires per capsule, and were maintained in a helium atmosphere for maximum heat transfer. Eight wires of pure aluminum and eight of Al-Li alloy were placed in each capsule. Argome Laboratory statements were accepted as establishing flux and exposure levels. These were based on previous experience and flux map-

Jan 1, 1961

By G. W. Form, W. A. Spitzig

The effects of hydrogen and vacuum shtering treatments on the physical and mechanical properties of arc plasma-sprayed tungsten were inuestigated. Temperatures examined ranged from 3000" to 4000°F in vacuum and 2000" to 3000°F in hydrogen for both single and duplex sintering cycles. Densities of 92 pct of theoretical density were obtained when a long-time hydrogen treatment at 2000°Fpreceded sintering in vacuum at 4000°F for 4 hr. This cycle also produced the highest ualues for modulus of rupture and bend angle. The results of this investigation point out the desirability of using a low-temperature long-time hydrogen treatment prior to a high-temperature vacuum sinter for arc plasma-sprayed tungsten. ADVANCES in the development of arc plasma-generating equipment have provided a high-temperature heat source that makes the fabrication of tungsten shapes possible by a metallizing process. Tungsten in the as-sprayed condition is very brittle. It has a density between 80 and 85 pct of theoretical density, a lamellar structure with elongated pores, and a high interstitial impurity content. To improve these properties, sintering treatments can be applied to the as-sprayed material, similar to those used for the densification of compacted tungsten powder. However, in view of the differences in the density and microstructure of as-sprayed tungsten as compared with compacted tungsten, responses to sintering were expected to be different. EXPERIMENTAL PROCEDURES The tungsten powder used in this investigation had a particle size varying from 3 to 13 p with an average diameter of 8p. The impurity level was less than 0.1 pct. The arc plasma spraying was done with an F-40 Thermal Dynamics Corp. plasma jet. Spraying was performed in air and thus required cooling of the substrate by an air blast in order to minimize oxidation. The spraying parameters employed in the fabrication of all specimens are listed below: Power input, kw 12 Arc-gas flow, cfh 95N2 + 5H2 Powder feed rate, g per min 33 Powder carrier gas flow, cfh ION, Spray distance, in. 3 Traverse rate, in. per min 30 Mandrel speed, rpm 100 Nozzle orifice, in. 7/32 These values of the spraying parameters correspond to optimum conditions ascertained in a previous study. Sintering was conducted at 3000°, 3500, and 4000°F in vacuum (< 0.1 Hg), and at 2000 and 3000°F in hydrogen. Duplex sintering treatments investigated are listed in Table I together with the designations that will be used for reference throughout this paper. The samples were fabricated by spraying onto a copper mandrel which was removed prior to sintering. The specimens used for the sintering analyses had the shape of small hollow truncated cones 1 in. high with an inside diameter varying from 0.500 to 0.125 in. and a wall thickness of 1/8 in. Specimens for bend testing were taken from hollow hexagonal prisms 1-1/2 in. high with a 1-in. diam across the flats and a wall thickness of 1/8 in. The bend-test specimens were ground to the dimensions 0.085 by 0.350 by 1-1/2 in. Prior to bend testing 0.0025 in. of stock was removed from each surface by electro-polishing. Density measurements were made by the water-displacement method. In addition, a porosimeter was used to determine the amount of interconnected porosity for representative samples. Strength and ductility were determined from recorded values in transverse bending using a cross head speed of 0.020 in. per min. The load was applied at the midpoint of a 1-in. span. The deflection data reported herein refer only to the plastic portion of the total deflection. RESULTS AND DISCUSSION The as-sprayed samples had a density corresponding to 83 pct (l pct) of the theoretical density of tungsten. Fig. 1 shows a representative as-sprayed tungsten structure.

Jan 1, 1964

By R. J. Arsenault

The yield drop that occurs in tantalum, Cu-AZ. and Ag-Al was investigated as a function of strain rate and at several temperatures. From the strain-rate dependence of the yield drop an activation volume was calculated and found to agree with that obtained from differential strain-mte tests. The temperature dependence of the yield drop can he explained in terms of the parameter temperature divided by activation volume. The yield drop is attributed to the rapid multiplication of dislocations during their motion. THE yield-point or yield-drop (upper yield stress minus the lower yield stress) phenomenon has been the subject of numerous investigations1-9 in both bcc and fcc metals. Also, there is no dearth of theoretical explanations10-20 to account for the yield-point phenomenon. The present explanations can be divided into two categories: the concept of dislocation locking and subsequent unlocking and the concept of multiplication of dislocations due to their motion. The Vottrell10,11mechanism of locking and unlocking, as applied to bcc metals, is the best known of the three proposed locking mechanisms. The two additional mechanisms, short-range order (SRO)7,16,17 and Suzuki-type locking,14,15 have been employed to account for the existence of yield points in fcc metals. The experimental evidence supporting the locking of dislocations, especially in bcc metals, is well-established. The dependence of the yield point on interstitial concentrations,&apos; the kinetics of strain aging,2 and the observations by electron-transmission microscopy18 are some of these experimental results. The number of experimental observations supporting dislocation locking in fcc metals is not as extensive as in bcc metals. The unlocking of dislocations, which actually is supposed to account for the yield drop, is by no means well-established by experimental results for either bcc or fcc metals. The similar temperature dependence6 of the yielding and plastic flow is one of the experimental factors that cannot be explained in terms of the unlocking of dislocations. The mechanism based on the rapid multiplication of dislocations has been proposed by several investigators. 18-20 Johnston and Gilman19 have proposed a detailed model of yielding, which was later employed by Hahn21 to predict quantitatively the yield drop in iron. This mechanism was discussed in a previous paper22 and several limitations were pointed out. In the same paper it was shown that an activation volume could be obtained from the strain-rate dependence of the yield drop and that a correlation existed between the activation volumes obtained from the yield-drop tests and from differen-

Jan 1, 1964

By J. A. Snyder, W. L. Finlay

SEVERAL notable studies of the effects of sub- stitutional solutes have been reported. Outstanding among these for its elucidation of general principles, is the summarized work of Hume-Rothery and coworkers.1 For a systematic study of the effects of substitutional solutes on the mechanical properties of the solvent lattice, the work of Brick, Martin, and Angier² on copper; of Frye and coworkers³,4,5 on copper and silver; and of Lacy and Gensamer6 and of Austin7 on iron may be mentioned. Titanium is one of the few elements offering the possibility of a similar study of interstitial solutes since, unlike most metallic elements, it exhibits extended solid solubility for most of the interstitial solutes—hydrogen, boron, nitrogen, oxygen, and carbon. This paper reports a survey of the effects of dilute solutions of nitrogen, oxygen, and carbon on the mechanical properties of high-purity alpha titanium. Previous Work: Van Arkel and De Boer showed" that high purity titanium was quite ductile and De Boer, Burgers and Fast established".&apos; that not only were oxygen and nitrogen very soluble in solid titanium but that, long before the limit of solid solubility of either had been reached, these interstitial solutes rendered the metal brittle. Their electrical resistance data as a function of

Jan 1, 1951

By J. A. Snyder, W. L. Finlay

G. Edmunds—Solid solubility is considered to be of either the interstitial or the substitutional type. Is it possible, in a binary alloy as the simplest case, that some of the solute atoms are present in the normal lattice sites (substitutionally or filling lattice vacancies) while simultaneously others are in interstitial positionss One might even ask whether a distribution of the two types may be the normal situation. H. M. Meyer—Metastable states of interstitial atoms occupying vacant lattice sites possibly occur as well as of substitutional atoms squeezed in between regular matrix positions. However (as we know since Hume-Rothery), the solute atoms choose between the two kinds of solutions; consequently, every solute will be unequivocally either substitutional or interstitial in the equilibrium state of the solid solution. M. Balicki—In view of the fact that the authors apparently correlate the analysis of the alloys at the ingot stage with the properties exhibited at the testing stage, I would like to ask whether this is a fully justifiable procedure. In other words, how good are their determinations of solute concentration for correlating them with the mechanical properties. The answer to this question may explain some of the divergencies. Assuming good enough homogenization of the samples and exact determination of mechanical properties the position of the plotted experimental points will depend solely upon the accuracy of composition determination. If this is not accurate, say due to loss or pickup of elements during processing from the ingot to the testing stage, or due to a systematic error in the method employed for obtaining solute concentration data, the points will deviate from their true position and may align themselves along a different curve than the one expected. H. V. Kinsey—We have been studying the creep-rupture properties of titanium-base alloys at 1000°F. In the course of this work, anomalies in behavior of the alloys that would suggest that the material under test was becoming stronger as the test progressed have been observed. If this was so, the most likely explanation that we could think of was that the test bars were absorbing oxygen and nitrogen from the air during the test and were thereby becoming strengthened. In an attempt to determine the strengthening effect of absorbed oxygen and nitrogen the following experiment was conducted. A length of cold-rolled titanium was supplied by the E. I. du Pont Co. Two test bars, having a 1/4 in. diam gauge length, were prepared from this material. One bar was tested in the as-received condition. The second bar was heated in air at 1550°F for 100 hr and subsequently air cooled prior to testing. A testing temperature of 1000°F was employed. The results of these tests are tabulated in table 11. In the author&apos;s opinion, is it reasonable to assume that the bar that was exposed to air at 1550°F for 100 hr was stronger because it absorbed oxygen and nitrogen from the air during this heat treatment? W. L. Finlay (authors&apos; reply)—Direct experimental evidence for or against Mr. Edmunds&apos; interesting suggestion will probably never be available. It seems possible, however, that mixed interstitial-substitutional solid solution might well occur with interstitial elements. The less likely possibility of interstitial solution of a normally substitutional element like copper in aluminum was recently discussed at length by the

Jan 1, 1951