By H. P. Stüwe

HE recent papers of Aust and Rutter112 have again brought to mind the importance of certain "special" orientation relationships between the lattices of two fcc crystals on the mobility of the grain boundary separating them. No theoretical treatment of this problem has been offered till now. The only principle published so far that has given an indication why certain orientation relationships should be "special" is the counting of "coincidence sites" according to the suggestions by Kronberg and Wilson.3 The "coincidence plots" published by these authors show, for instance, that two fcc lattices rotated by 38 deg around a common (111)-axis have 1/7 of their lattice sites in common. Such an orientation relationship is also characteristic for high boundary mobility. The accuracy of the orientation relationship needed for high mobility is not too rigid. Deviations up to 10 deg from the ideal orientation seem to be tolerable as can be gathered from the experimental data.'j4 The auestion arises, then. how the density of coincidence sites will be affected by a deviatioi from mathematical accuracy. This can be checked by a simple model. Two sieves are prepared, the arrangement of the holes corresponding to lattice sites on a (111)-plane in a fcc crystal. They are placed upon each other, Fig. 1. One is kept fixed, the other is rotated around an axis pushed through one hole in common to both. The light falling through holes of both sieves is then a measure for the density of coincidence sites. If the diameter of the holes is very small, light intensity is contributed only by holes the centers of which coincide "exactly." If the diameter of the holes is rather large, some intensity will be contributed by

Jan 1, 1962

By C. G. Dunn, J. L. Walter

COULOMB' and Coulomb and Lacombe2,3 have recently discussed secondary recrystallization in soft iron (99.5 pct Fe). They found that the appearance of this phenomenon was dependent on both the presence of impurities and the thickness of sheet specimens. They concluded that impurities such as carbon, sulfur, and oxygen in the soft iron stabilized the matrix structure and allowed growth of a few grains of specific orientations. They also found that secondary recrystallization ceased when the final thickness was small and attributed this complete inhibition of growth in thin sheet to the restraining action of thermal grooves. When purer iron (99.99 pct Fe) was used, normal grain growth but not secondary recrystallization was obtained. On the other hand it is known that the necessary stabilization of the matrix structure for secondary recrystallization in high-purity silicon iron probably does not depend on impurities but more likely results from the specimen thickness effect of Beck et al.,4 according to evidence and ideas advanced by Walter and Dunn,5,6 and Detert.7 Furthermore, Mullins8 has indicated that if a gas-metal surface energy difference exists across a grain boundary equal to or greater than about 3 pct of the grain boundary energy, then such a grain boundary should not become stuck. Similarly, Walter and Dunn have estimated that any increase in restraining force due to increased thermal grooving with decrease in

Jan 1, 1962

By Nicholas J. Grant, Robert H. Kane, Bill C. Geissen

The platinum-rich section of the Ta-Pt Phase diagram was worked out by metallographic and X-ray techniques, using twenty alloys; solidus temperatures and solid solubilities were determined. Besides s phase, four intermediate stoi-chiometric phases were found: TaPt (high-temperatzrre phase, structure unknown); TaPt2 (ortho-rhomhic, new type); a TaPt3 (orthorhombic, TiCu3 type); ß TaPf3 (monoclinic, new type). TaPt2 and TaPt3 melt congmentlv; two eutectic, two beritec-tic, and one eutectoid reactions occur in the inuestigated range. THE Ta-Pt system was examined as part of a study of the phase diagrams and the intermediate phases of niobium and tantalum with Group VIII transition metals. Since the main scope of this work was the relation among the ordered close-packed phases occurring in the concentration range from AB to AB3 (A = Nb, Ta; B = Pd, Pt, and so forth), only the platinum-rich side of the diagram was worked out thoroughly, while spot checks were made to determine the approximate outline of the tantalum-rich portion. The system has not been thoroughly treated in the literature; Greenfield and Beck1 in their survey of refractory metal intermediate phases found a o phase between -18 and 37 at. pct Pt which coexists at higher platinum concentrations with an unidentified intermediate phase. Browning2 worked on the range between 55 and 100 at. pct Pt; however, this preliminary study did not cover temperatures >1500°C, and included no conclusive crystallo-graphic data. More recently, a study of the platinum-rich section of the Ta-Pt system has been carried out by Ray,3 while Hartley, Parsons, and steedly4 have studied the tantalum-rich section. The crystal structures of TaPt2, a TaPt3, ß TaPt3, and others have been reported in abstracted form by Giessen and Grant.5 EXPERIMENTAL METHODS The methods of alloy preparation and processing and of the metallographic and X-ray procedures follow very closely those described by Ritter, Giessen, and rant' for other refractory metal-noble metal systems, and will not be repeated except where significant differences exist. Starting materials were: tantalum rod of 99.95 pct purity, supplied by National Research Corp., and platinum sponge 99.9 pct, supplied by The International Nickel Co. An oxygen analysis of the tantalum rod showed 30 ppm O; other impurities were C, N, Si, Nb, Mo, none of these exceeding 50 ppm, and 100 ppm W. Homogeneous buttons were readily prepared as follows: ingots of 5 g were weighed and arc-melted under welding grade argon, followed by two remelts after inverting the button. Between 40 and 100 at. pct Pt, weight losses during the first melt rarely exceeded 0.1 pct, in which case the alloy was rejected, and were nil on subsequent remelts. Since the vapor pressure of platinum far exceeds that of tantalum, the small evaporation loss could be assumed to consist of platinum; therefore, a corresponding amount of platinum was added on the second melt. Since it was confirmed on pure tantalum samples that no weight gain through oxygen or impurity pickup occurs (see Ref. 71, it could be assumed that the uncertainty in the composition did not exceed ±0.1 at. pct for the range 40 to 100 at. pct Pt. For the four control melts from 0 to 40 at. pct Pt, an error of ±0.5 at. pct was calculated. Microscopic examination of the whole buttons after melting showed no inhomogeneity other than local coring. This was eliminated by a homogenization heat treatment. A total of twenty-three alloys were prepared. Heat treatments were carried out in a tantalum

Jan 1, 1965

By J. P. Neumann, L. Raymond

At temperatures near 1000°C, only the (112) (111) slip systems are operatire in tungsten. Therefore, the substructure introduced into the billet upon rleforming a single crystal by rolling at 1000 "C can be controlled by proper selection 01. processing ral'iubles. Using a reduction of 10 pct pel- pass, the (001)[110] and the (110)[001] crystals will deform by duplex slip rip to a 50 pet reduction in thickuess. These rolled single-crystal sheels are characlerized by anisotropic hardening, retention of ductility with warm working, lattice bending which is related to the conlacl (angle, and macroscopic dimensional changecs in the length bid not the width of the billet. When several slip systems become operative, a greater degree of work hardening is itztvoducetl into the crystal. This rolling- condition is characlerized by isotropic hardening, loss of ductilily with warm working, complex lattice distortions, and macro-scopic dimensional changes in both the length rind Width of the billel. IN tungsten, the {1 10}(111) slip systems are operative below room temperature,' while above 700°C only the {112{ (111) slip systems are observed.2,3 In the transition region, i.e., room temperature. both systems appear. It is the purpose of this investigation to show that tungsten single crystals deformed by rolling at a temperature where only one slip system is operative generate dislocation substructure which depends on the crystal orientation. For a specific crystal orientation. the resulting dislocation substructure can be further influenced by modifying the rolling procedure. Crystals oriented for multiple slip display less substructural sensi- tivity to modifications in processing techniques than do single crystals oriented for duplex slip. Under simple slip modes of deformation, very little work hardening is introduced into a rolled single-crystal sheet. Mechanical properties such as room-temperature strength. ductility, and hardness are used to confirm the existence of the different work-hardened conditions generated within the crystal by modified warm-rolling techniques. EXPERIMENTAL PROCEDURE Material. Single-crystal billets of four different crystal orientations. grown by the Arc-Verneuil technique. were ground to a size of 0.25 by 0.375 by 3 in. In terms of their rolling plane and rolling direction, the billets had the following orientations: (1101 [001 ] (110) [110] (001) [110] (001) [100] The actual orientation of all crystals was within 5 deg of the ideal orientations. The typical impurity content of the crystals is given in Table I. Polishing and Etching. Polishing was done elec-trolytically in a 20 g per liter aqueous solution of NaOH at approximately 10 v. It was established by the Laue back-reflection X-ray technique that the surface damage due to grinding and cutting operations with a diamond wheel did not exceed 0.001 in. Therefore after each cutting or grinding operation at least 0.002 in. was removed electrolytically from the surface in order to eliminate surface effects. By lowering the voltage to 3 v, subgrain boundaries and individual dislocations are identified in agreement with Berlec 4 where the etch-pit traces on a cubic plane form a square. The etching time was about 5 sec at room temperature. Rolling. Rolling was carried out on a Loma 2-high mill (Model 600). The peripheral velocity of the 6-in.-diameter rolls was 500 in. per min, with the surface temperature of the rolls about 400° to 450° C The billets were heated before each pass for 30 min in argon to 1000 C. Oxidation of the crystals during rolling in air resulted in a thin layer of greenish-yellow WO 3 This oxide was removed after each pass by immersing the crystals for a few minutes in a boiling NaOH solution. Prior to the initial rolling pass, a surface layer of 0.001 in. was removed by polishing. The crystals were then annealed in vacuum (10-4 torr) at 2400 C for 30 min. All crystals were rolled in the same direction; i.e., the same end was always introduced into the rolls. The rolling program was conducted in

Jan 1, 1965

By J. S. Ll. Leach, M. B. Bever

THE system copper-nickel exhibits complete solid and liquid miscibility1 The thermodynamic properties of such a system would not be expected to deviate greatly from ideality. Although the evidence is conflicting, anomalies in the composition dependence of various physical properties of solid copper-nickel alloys suggest that mixing may not be ideal.' From measurements of the Hall coefficient it has been concluded that clustering occurs in these alloys. ' Considerations involving the phase diagram of the ternary system copper-nickel-chromium have led Mei-jering3 to predict a positive heat of formation for solid copper-nickel alloys. An electrochemical investigation of the activity of nickel in copper-nickel alloys showed unexpectedly large positive deviations from ideality.4 wagner5 has proposed that if the entropy can be considered ideal, these measurements would yield the following equation for the heat of mixing at 700°C H" = 3380 x,vl (l-xVi) cal per g atom [I1 The heat of formation at 722°C of solid copper-nickel alloys of the equiatomic composition has been measured in a reaction calorimeter as 540 cal per g atom. This note reports calorimetric measurements of the heat effects on dissolution of some copper-nickel ndon: in tin. These measurements were preliminary to a larger investigation, which was later discontinued. From them the heats of formation of the alloys can be calculated, if certain assumptions are

Jan 1, 1960

By S. K. Mitra

A refinement of the Seeger model for intersection process is investigated which is in better agreement with experimental observations than the original. It is shown that, in single crystals, the strain hardening in Stage II is mainly due to the short-mnge interactions when intersection is the rate-controlling process. It is also demonstrated that the creep curves, as predicted by this theory, are in good agreement with the experimental observations. MOTT: Cottrell? and Seeger have developed an approximate theory for plastic deformation of single crystals over the range of variables where the strain rate is controlled by the rate of intersection of dislocations. Although it is now generally agreed that the low temperature deformation of many pure metals is controlled by the intersection mechanism, various dictates of the over-simplified Seeger model are not in good agreement with all the experimental facts. It is the purpose of this paper to reveal that by appropriate extensions of the Seeger model, particularly those suggested by Basinski: a much more reliable theory results. The refined model to be presented here will be shown to account, in a satisfactory way, for the effect of stress, temperature, and strain on the creep rate under constant stress and for the effect of temperature and strain on the flow stress in constant strain-rate tests. EXPERIMENTAL METHOD To Check the theoretical deductions, both creep and tension tests were conducted on single crystals of high-purity Al (99.994 pct Al) so oriented that both the active slip plane and the Burger's vector of the operative dislocations on that plane made angles of about 45 deg to the tension axis. Single crystals of aluminum (5/8 in. by 1/10 in. by 8 in.) were grown in a graphite mold under an inert atmosphere using the Bridgman method. The chemical composition of the aluminum is given in Table I. A common seed was used for all crystals and their orientation is shown in Fig 3. The extensometry consisted of two differential transformers with matched outputs mounted so as to measure the extension in a 2 in. gage length. The amplified difference in output of the two transformers was recorded by a potentiometer. The amplification was calibrated before each run so that one chart division of the recording potentiometer indicated a 105 shear strain on the specimen. Stresses were measured to the nearest 1 x l04 dynes per sq cm. ACTIVATION VOLUME The concept of Basinski that the activation volume is not constant but is a function of the force that aids thermal fluctuation in effecting the cutting of dislocations will be adopted in this section. The force acting due to an applied shear stress on the dislocation being intersected is where L is the mean spacing between the forest dislocations, is the Burger's vector and T is the back stress. A detailed discussion about the origin of back stress will be taken up later in this report. As shown by Basinski, the activation energy, U, that must be supplied by a thermal fluctuation in order to effect intersection, is equal to where x is the distance through which the dislocation must be translated for complete intersection, and Fm is the maximum force encountered in intersection. When the applied stress is decreased abrupt ly F also decreases and the activation energy increases correspondingly as documented in Eqs. [ 1 ] and [2]. The Seeger equation for the strain rate when the deformation is controlled by rate of intersection of where the shear strain rate (per sec) N = the number of points per unit vol at which intersection can take place

Jan 1, 1962

By M. T. Simnad, C. E. Birchenall, M. H. Davis

The transport mechanisms previously proposed in wustite and hematite have been confirmed by movement of inert markers during the growth of these phases. By similar measurements the mechanism for magnetite has been determined. The rates of growth of multilayer scales on iron, magnetite and hematite on wustite, and hematite on magnetite have been measured. All rates are found to be diffusion controlled under the conditions of the experiments. MANY studies have been made of the rate of oxidation of iron in both the low temperature, film-forming region and the high temperature scaling range. The interpretation of the results has been greatly complicated by the formation of multi-layered scales containing the various phases of iron oxides. In most cases no attempt has been made to determine the composition of the scale and its dependence on time of oxidation in a quantitative manner. However, several recent studies'" have taken this variable into account. It is generally agreed that the growth of thick scales on iron follows a parabolic rate law for the increase of total thickness. In the thin film region agreement has been claimed with parabolic equations of various forms and with logarithmic equations. The discussion here will be concerned only with the formation of scales of considerable thickness, greater than several microns, although some of the conclusions may be applicable to thin films. A brief survey will be given of the solid phases of the iron-oxygen system, the stability of wiistite in bulk and in thin films, the relative densities of iron in the metal and oxides, and the kinetics of forma- tion of oxide scales on iron. New experimental results will be introduced at several points during the discussion, and an attempt will be made to formulate a mechanistic picture consistent with these observations. The experimental techniques are described in an appendix. Iron-Oxygen System Fig. la shows the iron-oxygen phase diagram. Wüstite ("FeO"): The lowest of the oxides has a NaCl type cubic lattice formed by close-packing of the relatively large oxide ions with the smaller iron ions arranged in the interstices. The ionic radius for 0' is about 1.3 A, while Fe++ has a radius of about 0.8A and Fe"' about 0.7A. Its range of existence on the phase diagram is very wide for an ionic material of this type and does not seem to include the stoi-chiometric composition FeO. These deviations appear to be well established as vacancies on iron lattice sites by the comparison of lattice parameters and densities for a series of compositions by Jette and Foote.4 The limits of the field are disputed, but the work which seems most reliable" indicates vacancies in from 5 pct to more than 12 pct of the iron sites. In order for the crystal to be electrically neutral, there must be electron holes which correspond to the formation of trivalent iron ions equal to twice the number of vacancies. Magnetite ("Fe³O4"): Considerable disagreement also exists in the literature about the stable range of the Fe³O4 field. Some diagrams show the Fe³O4 composition to be lower in oxygen than the formula indicates, but Schenck6 gives a diagram from the

Jan 1, 1952

By F. E. Streigert, J. H. Mallery, A. H. Geisler

The existing data on precipitation in Cu-Be alloys have been reconciled with some new data to present a more complete and rational analysis of the atomic rearrangements involved in the process. Two different coherent precipitates were proposed. Each is responsible for a type of diffuse X-ray diffraction effect. THE nature of the atomic rearrangement involved in the precipitation of the compound y-Cu-Be from supersaturated solid solutions of the copper-base alloys has been the subject of two extensive investigations.'-" he precipitate in this alloy system has a rather simple structure; at equilibrium it has a body-centered cubic unit cell with copper atoms on the corner sites and beryllium atoms on the center site. While a simple mechanism would be expected to obtain for the precipitation process, those which have been proposed do not adequately explain all of the reported data. The purpose of the present report is to rationalize some of the previous observations and to contribute new data on the subject obtained by the usual techniques of structure analyses. The Cu-Be system of alloys represents one of the most extensively investigated precipitation systems, so a detailed review of the pertinent literature on structure is in order. Striations: Since one of the important features of the mechanism—the habit plane—is determined by microscopic examination, microstructural features that have been observed should be considered at this time in order to assess their role in the precipitation process in Cu-Be alloys. One of the most prominent features appears as regularly oriented markings or stripings (ripples or striations) across the crystals on a suitably polished and etched sample of the aged alloy. These have been observed and interpreted by many workers. Masing and Dah14 observed striations in both the a and /3 phases of a 2.5 pct Be alloy, and attributed them to the beginning of the precipitation of very fine y crystals along favored planes of the a matrix and to the local decomposition of the £ crystals into a plus y. These markings were apparent in both the a and /3 phases of the micrographs given by Smith5 for a 2.75 pct Be alloy, while Moore" detected them in the a matrix phase using polarized light. Desch7 attributed the markings to fine precipitate particles lined up on a family of matrix planes like Masing and Dahl had done, and he identified the planes as those of the (111) family, the slip planes of the matrix. The striations were presumably the structure which Northcott- eferred to as "martensitic." He found that this structure was present in samples that had been aged under widely different conditions with hardness values ranging from 160 to 400 VHN. Later Guinier and Jacquet' also found striations in both the a matrix and secondary /3 phase. Their analyses showed that the striations were along (110) planes of the matrix phase, apparently in contradiction of the results of Desch. They found that the striations were developed during aging on the surface of a specimen that had been polished prior to aging.' On this basis they concluded that the striations represented mechanical deformation by slip along (110) planes of the matrix resulting from precipitation stresses.'" Similar but fainter striations were observed in the same manner on an A1-Cu alloy sample, in which the change in volume was much less than for Cu-Be alloys and

Jan 1, 1953

By G. Bhat, J. F. Libsch

A STUDY of the kinetics of embrittlement in engineering alloy steels during tempering has indicated that the presence of alloying elements may define two distinct regions of embrittlement: 1) at 800° to 1000 °F, termed low temperature embrittle-ment, and 2) in the temperature range 1150 ° to 1250°F, termed high temperature embrittlement.13 It has been suggested that embrittlement in each region may be due to a different mechanism. At intermediate temperatures and extended times the course of embrittlement may be influenced by the superposition of the embrittlement occurring in the two regions. Furthermore, low temperature embrittlement has been known to decrease as the temperature is raised slightly above the maximum embrittlement range.' Jaffe and BuffumV ave presented data for a Ni-Cr steel illustrating the removal of the em-brittlement occurring at 932°F by reheating to 1250°F for an hour. Their data further shows that embrittlement proceeds continuously with increased time at 1250°F, becoming pronounced at long times. They interpreted this behavior as a retrogression phenomenon involving the solution of the small nuclei of precipitate formed at 932°F as the temperature was increased, and reprecipitation of larger nuclei stable at 1250°F, with the reoccurrence of embrittlement. It appears desirable to reconsider this explanation in the light of the two regions of embrittlement proposed by the authors1 for some alloy steels. In addition, it appears desirable to determine any influence of a preconditioning treatment in each temperature range upon subsequent development of low and high temperature embrittlement. It is thus the object of this investigation to study the characteristics of the two modes of embrittlement proposed in a commercial Ni-Cr alloy steel (AISI 3140). Experimental Details Material—The material used in this investigation was commercial AISI 3140 steel bar stock, received as % in. hot-rolled rounds. The steel analysis was as follows (in percentages): C, 0.39; Mn, 0.79; Si, 0.30; S, 0.028; P, 0.015; Ni, 1.26; and Cr, 0.77. Material Processing and Heat Treatment—The bar stock was first ground to 0.430 in. squares and cut into specimens 23/4 in. long. These specimens were austenitized at 1650°F for 1 hr and oil

Jan 1, 1958

By M. E. Nicholson

IN order to understand how alloying elements influence hardenability through their effect on the rate of pearlite nucleation, it is advantageous to use a model to describe the mechanism of pearlite nucleation. The model which currently is most widely accepted has been described, among others, by Mehl et a1.1-3 and by Hultgren.4 Pearlite nucleation involves both the nucleation of ferrite and cementite.4,5 Cementite nucleates first, followed rapidly by the formation of ferrite at the cementite-austenite interface. The conclusion that cementite is the first phase to form during the process of pearlite nucleation is based, in part, on the observation that proeutectoid cementite is continuous with pearlitic cementite and that the orientation relationship between proeutectoid ferrite and austenite is not the same as that between pearlitic: ferrite and austenite.6,7 Recently, Smith" has suggested that the dissimilarity in orientation relations, instead of indicating the pearlite nucleation sequence, may be evidence that pearlite is nucleated in a grain adjacent to the one in which it is growing. Also, Modin9 as shown that ferrite in pearlite may be continuous with proeutectoid ferrite, and he has also shown that proeutectoid cementite is not always continuous with pearlitic cementite. Thus, it appears that the conclusion that cementite always initiates the pearlite nucleation process is open to serious question. The author believes that important evidence on the question of how pearlite is nucleated exists in the rates of pearlite nucleation of different steels. The following is a review and analysis of this evidence. If the nucleation of pearlite is considered as requiring the nucleation of both cementite and ferrite, then the time to nucleate pearlite consists of the time to nucleate the first phase to form, plus the time to nucleate the second phase at the advancing interface of the first. In the absence of a visible proeutectoid constituent, the second phase must be nucleated very soon after the first. If cementite is the first phase to form, the time to nucleate pearlite will be approximately equal to the time to nucleate cementite. Since the nucleation rate of a phase precipitating from solid solution increases with the degree of supersaturation, it would be expected that the rate of pearlite nucleation should increase with increasing carbon content. Digges10 has shown that the reverse is true. He determined the quenching velocity necessary to suppress pearlite formation in plain carbon steels as a function of carbon content. His results showed that pearlite formation could be suppressed with lower quenching velocities as the carbon content of the steel increased, at least up to 1.25 pct C, the highest carbon content he studied. Thus, it would appear that in plain carbon steels, in which pearlite is formed at the nose of the C-curve, the hypothesis that cementite nucleates first does not predict the observed change in nucleation rate. The validity of the current model of pearlite nucleation may be tested also by determining whether or not it predicts the relative influence of alloying elements on the nucleation of ferrite and pearlite. This can be done best by a consideration of the changes in a TTT diagram produced by a change in alloy content. Hultgren4 suggests that the general shape of a TTT diagram, as well as what constituents will form from austenite, can be predicted from the relative nucleation rates of ferrite and cementite. This is illustrated in the schematic diagram for a hypoeutectoid low alloy or plain carbon steel shown in Fig. 1. The C-curves for ferrite nucleation and for cementite nucleation are represented by AA' and CC', respectively, and the start of ferrite formation and pearlite formation are represented by AX and BC respectively. Adopting the current theory, Hultgren suggests that between X and C pearlite forms directly from austenite, since cementite nucleates more rapidly than ferrite in this temperature range. Conversely, at temperatures above Tx, ferrite is the first to nucleate and proeutectoid ferrite is formed. As proeutectoid ferrite grows, austenite becomes enriched in carbon, so that the cementite nucleation rate is increased. As a result, pearlite nucleation above temperature Tx is accelerated, beginning along BX and not along C'X. Temperature T, represents the temperature at which the nucleation rate of ferrite equals that of cementite. By extending this type of reasoning, using the principle that the nucleation rates of ferrite and cementite increase with increasing supersaturation of austenite with respect to these phases, it should be possible to predict the influence of carbon content on the shape of the isothermal transformation diagram. For a slightly higher carbon content than that of Fig. 1, the curve A A' representing the beginning of ferrite formation should be moved to the right, whereas the curve CC' representing the beginning of cementite formation should be moved to the left. For hypoeutectoid plain carbon and low alloy steels, this prediction does not agree with existing data. Instead, as the carbon content is increased, the pearlite curve moves to the right along with the ferrite curve and always appears to join it tangen-tially. This behavior is demonstrated by the TTT-curves of a series of manganese steels" shown in Fig. 2. In this figure, TTT-curves for four alloys containing 0.20, 0.40, 0.60, and 1.20 pct C are superimposed. The curves are identified in the figure legend. The letters F, P, and C are used to indicate the start of ferrite, pearlite, and cementite formation, respectively. In these steels, it appears that the nucleation of ferrite and of pearlite are related processes. As a result of the foregoing evidence, it is proposed that the formation of pearlite be considered as follows: Either ferrite or cementite may nucleate from austenite, then grow until the remaining phase is nucleated at the interface between the growing phase and austenite. (The growth of the first phase to form is assumed to be accompanied by a composition change in the adjoining austenite.) According to this model there are two modes of nucleating pearlite: 1—where cementite initiates the succession

Jan 1, 1955

By A. E. Dwight, A. F. Berndt

Binary and ternary alloys of uranium with transition metals were prepared with U2X stoichiometry. The compounds U2Tc, U2Rh, U2Os, and U2lr were formed by peritectic or peritectoid transformations, and were shown to be isostructural with U2Ru. The lattice constants are presented. Miscibility relationships obtained from the study of ternary alloys are graphically summarized in terms of an area-of-stability plot. The compound U2Re is not isostructural with either U2Ru or U2Mo. A series of compounds with stoichiometry U2X has been prepared in which X is technetium, rhodium, rhenium, osmium, or iridium. The only other U2X compounds, for which X is related to the above transition metals by proximity in the periodic table, are U2Mo and U2Ru. The structure of U2Mo is the tetragonal C11b type (MoSi2 type)1 and U2Ru is monoclinic, with a new structure type.' This investigation was undertaken to determine if any of the above compounds are isostructural with either U2Ru or U2Mo and to find the range of occurrence of these phases. EXPERIMENTAL Alloys were prepared from stoichiometric amounts of electrolytic uranium (99.99 pet pure) and transition metals of 99.5 pet purity (98+ pet pure Tc), by arc melting on a water-cooled copper hearth under an Ar-He atmosphere. Weight losses were negligible. The buttons were homogenized at temperatures between 700o and 800°C (900°C for U2Tc) in evacuated capsules and air-cooled. The X-ray powder specimens were annealed briefly at the temperature of homogenization. Except in the case of the technetium alloy, metallographic examination was used to determine the number of phases present. The radiation hazard involved in handling technetium precluded the use of metallography to examine U2Tc. The temperature and mode of formation of the U2X phases were determined by heating the metallographic specimens to successively higher temperatures, until examination indicated the presence of chilled liquid or a peritectoid transformation. RESULTS The U2X compounds investigated were found to be formed under the following conditions: UzTc unknown U2Ru peritectic 897o ± 3°C U2Rh peritectoid 755o ± 5°C U2Re peritectoid3 below 750°C Uas peritectic4 920°C U2Ir peritectoid 775o ± 5oC Debye-Scherrer patterns for the above U2X phases were made with CuKa radiation (nickel filter). The similarities in the positions and intensities of the strongest lines in the front-reflection region strongly suggested that U2Tc, U2Ru, U2Rh, U2Os, and U21r are isostructural with only minor differences in the unit-cell dimensions. The known lattice constants and intensities of the Debye-Scherrer rings for U2RU2 were used as a guide in order to index the low-angle X-ray reflections of the U2TC, U2Rh, U2Os, and U2Ir powder patterns. Approximate lattice constants for these compounds were thus obtained and were used along with the intensities observed for U2Ru to index the strongest lines in the back-reflection regions. A sin2 2? correction term was included and the lattice constants were refined and standard deviations estimated by least squares. Comparison of observed and calculated values of Q(= 4 sin2?/?2) used in these calculations are given in Table I. In each case when the positions of lines could not be resolved on the films they were not measured. The final lattice constants, with their standard deviations, are given in Table 11, along with the unit-cell volume and X-ray density. The values of the atomic volume5 of the transition ele-

Jan 1, 1965

By F. N. Rhines, A. S. Nemy

The mode of high-temperature tertiary creep of 523-0 aluminum alloy was found to be strongly stress dependent. The occurrence of necking and/or fissures during tertiary creep exhibited a sequence with varying stress, wherein fissures with no necking occur at a minimum stress and necking with no fissures occur at a maximum stress. At an intermediate stress, tertiary creep begins without necking but with fissures in a region just beneath the external surface, followed by necking and the development of fissures along the axis of the specimen. The results are interpreted in terms of grain boundary gliding and the hydrostatic stresses produced by restraints to grain boundary gliding. THERE appear to be two possible reasons for the existence of a period of accelerating elongation prior to rupture during high-temperature creep in metals; namely, 1) a change in the structure of the metal itself, leading to a change in its response to loading, and 2) a reduction in the cross section of the metal resulting in a higher unit loading. Howe,' by annealing and retesting broken low-temperature creep specimens, found that irreparable damage is done once a metal is subjected to creep. Andrade2 first pointed out the association between the reduction in cross section and the increase in creep rate. The present research was designed to investigate both of these factors by retesting specimens machined from material which had been subjected to high-temperature creep testing short of rupture. EXPERIMENTAL METHOD An aluminum alloy, 52s-0, was selected for these studies because it is constitutionally simple, is strong enough to be relatively insensitive to mechanical damage during machining,3 and undergoes accelerating creep in a convenient temperature range. This alloy is hardened by 2.6 wt pct Mg in solid solution and is not subject to overaging effects; it has a very small quantity of an insoluble impurity phase, Mg2Si, finely dispersed throughout its micro-structure. Creep specimens, similar in design to ASTM 0.252-in. tensile specimens, were machined from 3/4-in. round stock and the surfaces were electro-polished. A 24-hr anneal at 500°C was then applied to stabilize the grain size to an average diameier of 0.27 mm. Subsequent heating for as long as 700 hr at the intended test temperatures produced no change in the tensile properties, indicating a well-stabilized state of the material. Corresponding to each of the typical testing conditions listed in Table I, one creep specimen was tested to destruction and this test was employed as a guide in the selection of times for subsequent tests. Duplicate creep tests were then run to various points along the creep curve to produce specimens which were used to determine changes in mechanical properties and microstructures. The latter were examined at the midsections of the specimens. Other specimens were tested to various stages of tertiary creep, after which they were remachined to new cylindrical test specimens, electropolished and re-tested in creep. RESULTS The major findings of this investigation may be illustrated by a comparison of the results of three sets of creep tests. These were run at 400°C at three stress levels, namely 750, 1000, and 1500 psi. In presenting these results in Figs. 1, 5, and 8, the creep curves are given in pairs: That curve of each pair which is drawn through filled circles corresponds to the initial test, and the curve drawn through open circles (and designated by - R) represents the result of retesting the same specimen after machining to a new cylindrical surface. The load was readjusted to the original unit stress at the beginning of each retest.

Jan 1, 1960

By Dogan E. Gücer

In the following note, with the help of a new parameter of strain hardening, the attention is drawn to the close relationship between the relative performances of steels under plastic range cycling and their strain hardening characteristics. If a cantilever beam of rectangular cross section is tested with the arrangement shown in Fig. 1 in reversed bending between constant deflection limits at the lever head, the longitudinal strain-deflection hysteresis shown in Fig. 2 is obtained. There is no lateral strain due to constraint at the rectangular test section.' If the absolute value of strain undergone between a maximum state of tension and maximum state of compression is called A, it will be seen that A decreases with cycling rapidly due to the strain hardening in the test section and the ensuing change in the bent beam profile. It will also be seen that A reaches an approximately stable value around 10th cycle. If we call the first cycle strain range, A,, and that of 10th cycle, A,,, then is an index of the strain hardening capacity at a particular deflection level. A plot of n vs ? is reproduced in Fig. 3 for two ASTM steels: A-302 and A-201. A-302 is a low alloy structural steel, A-201 a low-carbon steel. The specimens were first normalized at 1650°F for 75 min then grooved with a milling cutter; and the notches were ground to 50G finish. The final operation before testing was a stress relief at 1150°F for 75 min. The behavior of the two steels changes around ?1 = 0.8 pct or A,, = A, -n = 0.7. If these curves are compared with the endurance life curves given in Fig. 4, it will be seen that the relative performance of the two steels also change around A,, =. 0.70 pct. The steel with lower strain hardening capacity (7) at a certain strain level shows a longer endurance life, irrespective of their strength levels. Since the exponent governs strain hardening at lower strain levels than the Modulus, the relative values of both parameters also coincide with the change in n values and the relative performances of the two steels at different strain levels. These two observations indicate to the close relationship be-

Jan 1, 1962

By B. W. Howlett, M. B. Bever, Somnath Misra

The heats oj- formation at 0°C of the compounds AuSn,, AuSn2, AuSn, and the £ phase were measured in a metal -solution calorimeter with liquid tin or a liquid Sn-Bi alloy as solvent. The melting point, heat of fusion, and heat capacities near the melting point of- the compound AuSn in the solid and liquid state were measured in a constant temperature gradient calorimeter. The free energy and entropy of formation of the compound AuSn at its melting point and at 298 °K were calculated from the experimental results and published data. The heats of formation are discussed in relation to the nature of the compounds. The heat capacity below the melting point, heat of fusion, and entropy of fusion of AuSn are interpreted in terms of processes oc-curring before melting. The atomic arrangement in liquid Au-Sn alloys and the bonding in the intermediate phases of. the Au-Sn system are discussed in the light of the measured thermodynamic properties. THE available thermodynamic information on the intermediate phases in the Au-Sn system consists of the heats of formation of the compounds AuSn4, AuSn2, and AuSnly2 and of one composition of the < phase2 besides values of the heat content of the compound AuSn from 0" to 635".&apos; However, the heats of formation refer to different temperatures ringing from 90" to 450°C. Also, the reported error limits of some of the values are large and several inconsistencies are apparent. In the investigation reported here the heats of formation of the compounds AuS-, AuSnz, and AuSn and of three compositions of the < phase were determined for a single reference temperature of 0°C by liquid metal-solution calorimetry. The compound AuSn, which is the only congruently melting intermediate phase in this system, was further investigated in a constant temperature gradient calorimeter by measuring its heat of fusion, melting point, and heat capacity in the solid and liquid states near the melting point. From these data and published free energies of the liquid of composition Au~n,&apos; the free energies of formation of the compound AuSn at the melting point and at 298°K were calculated. The results shed light on the solid-liquid transition of AuSn and on the atomic bonding and state of association of gold and tin in the solid and liquid phases. 1) EXPERIMENTAL PROCEDURES 1.1) Preparation of Samples. Stoichiometric amounts of gold and tin, each 99.99+ pct pure, were melted in evacuated Vycor capsules (12 mm ID). The melts were maintained approximately 150°C above the liquidus for about 12 hr and shaken repeatedly. Samples of the compound AuSn were cooled slowly to room temperature. Melts of the other phases, all of which solidify by peritectic reactions, were transferred to the narrow end (5 mm ID) of the capsule, which was then quenched into iced brine. The solidified samples were annealed in the unopened capsules for 10 days at 30" to 50° C below the respective solidus temperatures. The absence of microsegregation and second phases was confirmed by metallographic examination. At least two batches of each composition were prepared. 1.2) Solution Calorimetry. The heats of formation were determined by liquid metal-solution calorimetry. In this technique, the difference between the heat effects on dissolution in a liquid metal, or alloy bath, of the compound and a mechanical mixture of its annealed components, adjusted for changes in composition of the bath, is the heat of formation of the compound at the temperature from which the samples are added. Details of the equipment and technique have been described."&apos; A tin bath at 300" or 350°C was used with the compounds AuSn,, AuSnz, and AuSn. The high gold content of the £ phase would have caused it to dissolve with an appreciable exothermic heat effect. In order to achieve thermal compensation, the samples were added from 0°C to a bath at 350°C consisting of 66.2 wt pct Bi (99.999+ pct pure), balance Sn (99.99+ pct pure). This solvent gives thermal compensation because gold dissolves exothermically in tin and endothermically in bismuth. The calorimeter was calibrated by adding from 0°C approximately 0.015 g-atom of the solvent.

Jan 1, 1965

By R. L. Fullman, J. W. Cahn

A method is derived for obtaining the distribution of sphere diameters and plate thicknesses (or pearlite spacings) from size distribution functions obtained along randomly oriented lines. The method described offers several advantages over existing methods. IT is often of interest to measure not only the average particle size but also the distribution in sizes of particles dispersed in an opaque material, such as an alloy. Particles of a single size will exhibit a range of apparent sizes on the plane of polish. If the sample contains a distribution of particle sizes, the distribution of observed sizes on the plane of polish is related to the distribution of actual particle sizes by an integral equation, For example, a distribution of sphere sizes, N(r),

Jan 1, 1957

By J. B. Newkirk

Results of a Debye-Scherrer X-ray investigation are given which show that the order-disorder transformation is a first-order or heterogeneous reaction in Cu-AU alloys with compositions near CuAu. Evidence was found for conventional tie-line segregation across a usual type of two-phase field separating the ordered and disordered fields in the Cu-Au equilibrium phase diagram. The horizontal and vertical widths of the two-phase fields are about 3 atomic pct and 20°C, respectively, at 43 and 54 atomic pct Au. No evidence for the existence of an ordered structure based on a stoichiometric composition of Cu3Au2 could be found. ALTHOUGH the modern theories relating the de-Agree of order of binary alloys to temperature and composition have met with considerable success, the nature of the transformation from the disordered state to the ordered state and vice versa has never been well understood. It has been assumed by some&apos; that this is a second-order transformation, that is, a homogeneous change of state. Others2 hold that the transformation is first-order and that the effects characteristic of heterogeneous phase transformation apply. Since this subject is discussed in detail in a recent paper,&apos; the arguments will not be repeated here. The present paper summarizes an experiment which was designed to distinguish between these two viewpoints for the case of Cu-Au alloys near the composition CuAu. The Cu-Au system is an important one because it furnishes prototype alloys, the behavior of which has formed the basis of much of the present-day order-disorder theory. It has recently been shown- hat in alloys near Cu3Au there is a temperature range within which the ordered and disordered states coexist in equilibrium and are distinguishable as separate phases. Therefore, the transformation must be first-order for these alloys. A similar demonstration for alloys near CuAu, however, has been lacking. Experimental Method Essentially the experiment consisted of equilibrating Cu-Au samples at various temperatures, quenching them in water to retain the high temperature states, and then examining them at room temperature for the coexistence of the ordered and disordered structures. The thermal gradient method of heat treatment- as used because it was important that all temperatures over the transformation range should be represented in the test. Briefly, this method consisted of holding a wire of the desired composition, sealed under vacuum in Pyrex, in a known temperature gradient for a long enough time to allow each part of the wire to assume the crystal structure characteristic of the temperature at which it was held. The temperature gradient was produced by inserting into an ordinary wire-wound cylindrical laboratory furnace, an 18 in. length of 1/8 in. ID ceramic tube which was heavily wrapped with asbestos. The furnace power was controlled by a Tag-liabue Celectray controller and a chromel-alumel thermocouple with the junction located on the heating elements. During the equilibrating treatment the widest variation of temperature within the gradient tube was approximately 4°C at the highest temperature. The temperature at various places within the tube was determined, before inserting

Jan 1, 1954

By H. J. McQueen, G. C. Kuczynski

ThE useful properties of k6-Alfenol and the thermenol alloys (summarized by J. E. Nachman and W. J. Buehler&apos;) have encouraged research into those alloys which, having compositions near 25 at. pct Al, 75 at. pct Fe, undergo an ordering transformation between 500° and 550°C. The equilibrium diagram of the iron-rich iron-aluminum alloys was first determined by Bradley and Jay.2,3 They distinguished three structures: the disordered, which is bcc; FeAl, which is simple cubic with one Fe atom and one Al atom per lattice site; and Fe3Al, which is fcc with three Fe atoms and one Al atom per lattice site. This last structure may be conceived as eight body-centered cubes with Al atoms at the centers of alternate ones, so that Al atoms have only Fe as first and second nearest neighbors. Later, Osawa and Murata4 determined the boundaries of the different superlattice regions in the iron-rich Fe-Al solid solution by dilatometric and X-ray methods. Two of the six phases, which they found between 0 and 50 at. pct Al, were never identified by other workers. A. Taylor and R. M. ones,&apos; concurrently with and independently of this research, redetermined this diagram by measuring lattice parameters at temperature. Further reference will be made to their results. EQUILIBRIUM DIAGRAM A) Experimental Procedure—The alloys were prepared from NRC gas-free iron (99.9 pct Fe) and 99.99 pct Al. They were melted in alumina&apos; crucubles under vacuum in an induction furnace. If the ingots were unsound or showed more than a 3 pct weight loss, they were rejected. The ingots were homogenized at 1100°C for 24 hr before hot-rolling at 700" to 900°C from 1 in. to 0.25 in. thick. It is interesting to note that alloys containing more than 28 at. pct Al were able to take an 80 pct reduction of area in the ordered FeAl region. The dilatometer specimens and specimens for chemical analysis were cut from these plates. A Leitz dilatometer was used to measure the coefficient of linear expansion as a function of temperature. The specimens were slowly cooled from 900" to 300°C where they were annealed for 10 hr before slowly cooling to room temperature. The expansion was recorded photographically as the alloys were heated and cooled at 1.5oC per min between 100" and 1000°C. The magnetic measurements determining the Curie points were performed on the dilatometer specimens in the dilatometer, by using direct current in the furnace windings both to heat the specimen at 1.5°C per min and to serve as the primary coil. The regular specimen holder was replaced by a thin alundum tube on which was wound, as a secondary, a closely spaced coil of fine copper wire. A reversal of current in the furnace windings produced, in the secondary, an emf which was proportional to the induction in the specimen, and which could be detected on a galvanometer. In this way, it was possible to determine the Curie points of alloys to within * 5°C. B) Results and Discussion—The coefficients of linear expansion, as obtained from the dilatometer curves, are plotted as a function of temperature and composition in Fig. 1. Since in many cases the heating and cooling curves were superimposed, it was decided to measure slopes of heating curves only. Definite high peaks, due to the transformations, were observed on each curve between 400" and 520°C, and, for alloys containing more than 23 at. pct Al, a second set of smaller peaks at temperatures above 660°C. The sharpness of the peaks indicates that ordering to Fe3Al is a first-order reaction. The compositions and the temperatures of these peaks are listed in Table I. When these temperatures are plotted as a function of the composition, the result is the constitution diagram presented in

Jan 1, 1960

By G. P. Conard, R. C. Hall, J. F. Libsch

The 50 pct Fe-50 pct Co alloy undergoes a transformation from disorder to an ordered structure of the CsCl type reportedly in the vicinity of 732OC. During this process, the coercive force goes through a maximum, apparently as a result of strains associated with the coherent nucleation and growth reaction. This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction, which is associated with annealing to a high degree of order with the continuous application of a magnetic field. The increase in ratio can be explained on the basis of a decrease in 90&apos; domain boundaries and, perhaps, by an increase in anisotropy resulting from lattice distortion. THE 50 pct Fe-50 pct Co alloy undergoes a disorder-order transformation which has been reported to occur in the vicinity of 732°C1,2 The ordered structure is the CsCl type.&apos; This magnetic alloy also shows a marked increase in the ratio of residual to saturation induction as a result of heat treatment in a magnetic field, sometimes called a response to magnetic anneal.&apos;-&apos; The purpose of this investigation was to study the course of the ordering reaction, the nature of the response to .heat treatment in a magnetic field, and the relation, if any, between ordering and the response. Procedure The method of approach in this investigation was to produce an initial structure as completely disordered as possible and then gradually to order the alloy by isothermal anneals at various temperatures under different conditions of the applied magnetic field. Magnetic, magnetostriction, and X-ray analyses were of primary importance in determining the property and structural changes resulting from the isothermal anneals. Rings of the 50 pct Fe-50 pct Co alloy were prepared from the elemental powders by a powder metallurgy technique, further details of which may be found in ref. 7. The initial structure was produced by annealing the specimens for ½ hr at 1000°C, cooling to and holding for ½ hr at 900°C (in the a range above the ordering temperature), and water quenching. Isothermal anneals were performed at 600°, 675°, 720°, and 740°C. For example, rings were heated to 600°C, held for a predetermined period of time, and cooled by natural cooling at a rate slightly slower than an air cool (average of 20" to 25°C per min). The tests (magnetic, etc.) were made after each heat treatment. All high temperature treatments were performed in a purified hydrogen atmosphere. The treatments at the various temperatures were carried out under one or more conditions of an applied field including 1—no field, 2—field of 20 oersteds applied on cooling only, and 3—field of 20 oersteds applied continuously during heating, holding, and cooling. Magnetic measurements were made using the standard Rowland ring technique8 with a maximum field strength of 100 oersteds. The magnetization curve, induction at 100 oersteds (B.), residual induction (Bt), and coercive force (Hc) were determined. All magnetic analysis data were based on an average of the results from three rings. A strain gage technique9 as used for the measurement of magnetostriction. The X-ray determination of the relative amount of ordered phase present was made on the ring specimen used for magnetic measurement. This was done by the back-reflection method using a rotating specimen (because of the large grain size) with unfiltered CoKa radiation and a 7 hr exposure time. Intensity measurements of the ordered line (300) were made by comparing visually the films so obtained with standard films prepared by exposing for different lengths of time a specimen given a long time anneal (high degree of order). Results In all instances the saturation induction (induction at 100 oersteds) was found to increase slightly with annealing time. This effect was small and appears to be the increase in saturation induction to be expected on ordering.10-13 The residual induction behavior was markedly influenced by the field condition during annealing, Figs. 1, 2. For the condition of no applied field, the ratio of residual to saturation induction remained essentially constant for short annealing times but showed a significant increase at longer times. With increasing annealing temperature, less time was required to produce this increase in the ratio. In the case of the 600°C anneals, the increase did not occur until approximately 20 hr, Fig. I, while on annealing at 740°C the increase was immediate, Fig. 2. Slight decreases in the ratio may be observed at 100 hr for specimens treated at 720°C and at 1 hr for those treated at 740°C. Specimens annealed in a field of 20 oersteds showed a residual to saturation induction ratio consistently higher than that for the specimens annealed without the field. The first anneal with the field (¼ hr) caused an abrupt increase in the ratio at all temperatures; thereafter, the increase in the ratio was generally similar for specimens annealed

Jan 1, 1956

By J. B. Newkirk, A. H. Geisler

The alloy Cu4Pd has a disordered face-centered-cubic structure when quenched from temperatures between 478ºC and the melting point (about 1100°C). Below 478ºC an ordered phase is stable. The results of a Debye-Scherrer X-ray analysis indicate that the ordered phase has a tetragonal unit cell described by the space group C24h — P42/mt with 2 Cu in 2a, 2 Cu in 2f, 4 Cu in 4j (x = 0.2, y = 0.6), 4Pd in 4j (x = 0.4, y = 0.2), and 8 Cu in 8k (x = 0.1, y = 0.3). The orientation relationship between the face-centered-cubic phase and the ordered tetragonal phase is given by: [100],,. // [130]al,. COO1Ia.d.//COO1I,,.. • The behavior of Cu,Pd is typical of ordering alloys except that the transformation is very sluggish. The increase in hardness and the microstructural and X-ray diffraction effects are interpreted in terms of coherency strains caused by the ordering. AN anomalous construction in the Cu-Pd phase diagram (Fig. 1) was reported in 1939 and has been allowed to stand without further published attention since that time. The odd figuration about the composition 10 to 27 atomic pct Pd is derived mostly from the work of Jones and Sykes.1 Evidently several features of this binary system require further study if the constitutional forms are to be well understood. The present paper includes a study of one of these features, that is, the crystal structure of a single ordered alloy containing nominally 20 atomic pct Pd. This choice of composition was suggested by the work of Harker and associates who determined the structure of Ni4Mo2 and Ni4W.3 The nature of the ordering process in Cu4Pd was studied also by observing the hardness, microstructure, and Debye-Scherrer patterns of specimens which had been aged at various temperatures after quenching from an initial disordering treatment. Experimental Methods A 20 gram ingot of Cu4Pd was made by melting spectrographically standardized copper from Johnson, Matthey, and Co., and commercially pure (99.5 + ) palladium in an argon-filled quartz tube. Chemical analysis showed that the ingot contained 80.0 atomic pct Cu. The ingot was rolled about 60 pct to a strip 0.060 in. thick and was homogenized for 16 hr at 950°C in low pressure argon. Rods cut from the rolled strip were worked into wire 0.015 in. in diameter, and specimens for hardness and microscopic examination were cut from the remaining strip. All specimens, with the exception of some of the wire, were given an initial disordering treatment by heating for 16 hr at 950°C, followed by water quenching. A 10 cm length of as-drawn wire was water quenched after being held in a temperature-gradient furnace4 for 89 days. Room-temperature Debye-Scherrer photograms were then made at points along the wire to determine the temperature below which the ordered phase was stable. Although the accuracy of temperature determination in the gradient was only about ±10 °C, the temperature gradient was sufficiently gradual that the sensitivity was much better and locations which had differed by as little as 1°C could be distinguished. An analysis of the crystal structure of the well ordered alloy was made by X-ray diffraction using a specimen cut from this wire. The change of Debye-Scherrer pattern as ordering progressed was studied by using isothermally aged samples of initially disordered wires. The wires were sealed under low-pressure argon in small quartz tubes for heat treatment. After the aging treatment, the tubes were quenched in water and photograms were made at room temperature in a 10 cm diam camera using filtered Cu kX. (A = 1.540511) Hardness was measured on a Vickers hardness tester using a 10 kg load and 2/3 in. objective lens. Reported values are the average of at least three impressions made on flat specimens 0.060 in. thick. After the hardness of a heat-treated sample had been measured, it was resealed in low-pressure argon and returned to the furnace for continued aging at the same temperature. In this way, two samples served for all aging times at each temperature. Hardness specimens which had been aged 500 hr or more were used for metallographic examination after the final aging treatment. A dilute potassium-dichromate etching solution was used.

Jan 1, 1955

By A. G. Metcalfe, R. P. Elliott, F. A. Crossley

THE texture method (utilizing monochromatic copper radiation) was applied to determine the orientation of the columnar grains of two vacuum cast beryllium ingots of 3 in. diam. Samples were mounted in a fixture as illustrated in Fig. 1, which permitted rotation and translation in order to approximate the method used for wires. The specimens were aligned so that the major axes of the columnar grains were parallel. Rotation was around the growth direction. After each translation the specimen holder was rotated 2 deg (1 deg for the samples from the second ingot) until a range of 30 deg on either side of the vertical was covered. The speed of translation was 1 mm per sec. A representative Debye pattern is shown in Fig. 2. The pattern was compared with theoretical patterns for various orientations. Also shown in Fig. 2 is the disposition of reflections on the (10i0), (0002), and (1011) Debye rings for the two possibilities that growth is either in the <10i0> or <ll30> direction. It is apparent that no significant preference for the direction of columnar growth is indicated. It is considered that the lack of a preferred orientation is due to the occurrence of the phase transformation (reported by Martin and oore&apos; to occur above 1250 "C) which masked the original solidification orientation. This research was supported by the United States Air Force under Contract No. AF 33(616)-5911, monitored by the Materials Central, WADD, Wright-Patterson Air Force Base.

Jan 1, 1962