Search Documents

By R. C. Nelson, T. L. Weaver, A. I. Michals

This paper describes the design and performance of an apparatus for making continuous nondestructive resistance measurements throughout a spool of fine wire. Highly reproducible results on clean and graphite coated tungsten and rnolybdenum wires from 1 to 9.5 mil are presented. A linear relation between resistance and wire weight (per standard length) was obtained on clean wires, but only on those coated wires with very uniform coatings. Results indicating a correlation between tensile strength, hardness, and resistivity are reported. THE increasing demand for greater uniformity in fine tungsten and molybdenum wires destined for use as mandrels, grids, and coils in radio tubes and as filaments in light bulbs has rendered inadequate the standard (sampling) approach to the control of wire diameter and other physical properties. This ap-

Jan 1, 1961

By F. V. Lenel

Resistance sintering under pressure is a method of hot pressing in which a powder compact is subjected to pressure and simultaneously heated by passing a low voltage high amperage current through it. Equipment for this process is described. Its basic characteristics such as resistance requirements for powders and compacts, temperature distribution in compacts, and gas reactions during resistance sintering are discussed. Examples of the sintering process in compacts made of a single metal or an alloy powder and in compacts made of mixtures of powders are presented. Potential commercial applications of the process are evaluated. THE usual sequence of operations in commercial powder metallurgy is to compact metal powders in a die at room temperature and sinter the compact subsequently without applying pressure while the compact is in the sintering furnaces. In hot pressing, on the other hand, the compacting and the sintering are combined. The loose powder, or in many cases a cold formed compact, is inserted into the die which is held at the hot pressing temperature, the compact is left in the die until it attains its temperature, and then pressure is applied and maintained for a given length of time. The die may be heated by surrounding it with a suitable furnace, by high frequency induction heating, or by passing current through the die. In hot pressing, compacts of high density and good mechanical properties can be produced in a relatively short time. One of the principal difficulties in hot pressing is the lack of suitable die materials which will have adequate strength at the hot pressing temperature. This difficulty can be overcome at least partially by heating only the material to be hot pressed without heating the die directly. This can be done by passing a low voltage high amperage current through the material and simultaneously subjecting it to pressure. Either loose powders or compacts can be hot pressed by this method in which the desired temperature is produced by the power dissipated in the metal powder. This method of hot pressing has been termed "electrical resistance sintering under pressure." The most significant differences between this operation and conventional hot pressing are: 1—The sintering times are very short, usually a fraction of a second and at most a few seconds. 2—The powder and die are initially cold. 3—Heat is generated within the powder itself and not conducted in from the die. 4— The pressure used is high. 5—Cooling following sintering is rapid, amounting to a quench. Resistance sintering of metal powders under pressure has been suggested repeatedly. In 1933, G. F. Taylor' proposed an apparatus which consisted of an insulating tube made of glass, or a ceramic filled with the powder to be pressed, and plungers above and below the powder. The powder was to be heated by passing an electric current through it and pressure was then applied. The apparatus was intended principally for hot pressing cemented carbides. Although the principle of resistance sintering under pressure is clearly shown in this patent, few details are given. A sintering period of a second or a fraction of a second, which is terminated by the operation of an inertia switch, is mentioned but no values for current density are mentioned. Low pressures, such as atmospheric pressure or a somewhat higher pressure exerted through a lever, are suggested. W. D. Jones' discussed electrical resistance sintering under pressure and proposed using resistance welding apparatus for this purpose. In a patent issued in 1944, G. D. Cremera described a method of electrical resistance sintering under pressure using resistance welding apparatus which was to be applied mostly to nonferrous metals such as copper, brass, bronze, and aluminum. Current densities of 400,000 amp per sq in., sintering times of 1 and 2 cycles of 60 cycle current, and pressures of 5 to 10 tsi are proposed. Cremer suggested using an

Jan 1, 1956

By L. F. Mondolfo

An aluminum-copper 4 pct Cu alloy aged at room temperature for times increasing up to 78,000 hr was annealed at 170°C and the hardness and electrolytic potential determined during retrogression and subsequent aging. It was found that there is a change of behavior with increasing time of aging at room temperature which indicates that, given sufficient time, retrogression disappears and the room-temperature aging tends to progress directly into the high-temperature aging. WHEN an age-hardenable alloy is aged at low temperature after proper quench, changes of properties and structure take place. If this material is then heated to a temperature higher than the previous one, but still well below the solution-treatment temperature, the properties and structure changes produced by the low-temperature aging disappear and the material apparently reverts to the as-quenched condition, ready to undergo aging from the start. This phenomenon is termed reversion or retrogression. First discovered by Cayler3l it has been extensively investigated, as shown by the number of publications listed in the bibliography. From all the information available the following facts emerge: 1) All aeg hardenable alloys can be retrogressed.9 13, 19) 24, 33, 41, 42, 44, 47, 53, 54, 61, 63, 64, 66, 73, 78 2) All the properties changes that take place during aging at low temperature can be retrogressed to a smaller or larger extent.4,5,7,12,19,32,49,50,57,58,60,67,75,76 67, 75, 76 3) Retrogression requires that the temperature be well above the preliminary aging temperature. If the difference between the two temperatures is small, Little or no retrogression takes place.7,20,32,33,41,49 57. 65 4) The larger the difference between the preliminary aging and the retrogression temperature, the faster and more complete is the retrogression.20, 33, 41, 48, 65, 67 5) Retrogression can be produced several times in the same alloy.23, 35,41,57,59 6) The amount of retrogression that can be obtained depends on the aging temperature. Alloys aged at the lower temperatures can be retrogressed the most. The higher the preliminary aging temperature the less retrogression can be produced.20,25,33,37,44,49,54,58 7) Appreciable retrogression after aging at elevated temperatures is possible only if the preliminary aging has lasted a short time. After a certain time of aging at high temerature retrogression does not take place any more,:5,6,9,10,11,21,40,58 8) During retrogression the Guinier-Preston zones redissolve and disappear. The other precipitate

Jan 1, 1960

By H. Herman, M. E. Fine

Kinetics of reversion and reformation of GP I were studied resistometrically in Al-1.7 at. pct Cu. The reversion process is over in roughly 1/2 minute at 205 "C irrespective of the amount of primary aging. After reversion the occurrence of an incubation time before reaging begins has been substantiated. The reaging kinetics is drastically accelerated by plastic deformation to the specimen. An incubation time is observed only if the specimen is aged before reversion. The incubation time and the effect of plastic deformation indicate that nucleation of GP I is heterogeneous. Simple clusters of copper atoms apparently do not act as nuclei for GP I. AFTER quenching aluminum-rich copper from the solid solution range, Guinier-Preston zones of the first kind, GP I, form very rapidly at room temperature. The rate, largely controlled by the concentration of vacancies, is initially most rapid1 (that is, at the time of the first measurement: 1/2 min) and decreases with time. The nucleation is thought to be athermal. If after aging for several days the GP I is dissolved by reversion at 205°C, according to measurement of Young's modulus an incubation period is observed before GP I begins to form on subsequent aging.2 Yet if the reversion is carried out immediately after quenching, both resistivity3 and modulus changes2 show no incubation effect. The zones which form after reversion have the same structure as those which form after the quench.4 Because of entropy considerations and also the short diffusion time, the solid solution after reversion, 2 min at 205°C, is probably more highly clustered than at the original solution treating temperature, 520" to 550°C. It appears most reasonable to associate with nucleation the incubation time observed on reaging after reversion. A simple cluster of copper atoms, many of which are presumed to be present after reversion, is then not a sufficient nucleus for GP I; a GP I nucleus must contain something in addition to a cluster of copper atoms. The purpose of the present note is to give some additional experimental information concerning the incubation time and rates of reaging after reversion. The existence of the incubation time has been verified by measurement of another property, the electrical resistivity. Acceleration of reaging after reversion by plastic deformation has also been investigated. In acl.dition, the kinetics of the reversion process itself was studied. EXPERIMENTAL Electrical resistance was measured by the poten-tiometric four probe method. The 1.7 at. pct Cu alloy was furnished by the Aluminum Co. of America in the form of 1/2 in. rod. The major impurities reported by Alcoa were Fe (0.002 wt pct), Si (0.003 wt pct), and Mg (0.001 wt pct). Specimens for measuremenl of resistance were prepared by rolling to 0.010 in., cutting 2 by 0.2 in. pieces, rolling the middle pclrtions of these to 0.005 in., and splitting the 0.010 in. sections up to the reduced central section to form current and potential leads. Aluminum extension wires insulated with ceramic tubes were spot welded to the leads. The specimen was supported by the lead wires. The whole specimen assembly was annealed at 500" C in an air furnace for more than 12 hr and then aged at room temperature. This was done to assure quick and complete resolution during subsequent solution treatments. These were carried out in Houghton's "430 Temper Salt" at 520'C for 1 hr. Unless otherwise specified, quenching was accomplished by quickly transferring the specimen from a salt pot to 25°C water. Aging was carried out in a 3 liter dewar of distilled water, rotated and stirred. The temperature was controlled to +0.01°C with a thermomercurial regulator in conjunction with a transistorized relay

Jan 1, 1962

By E. P. Abrahamson II

The effect of transition elements which form binary solid solution upon the recrystallization temperature of zirconium has been investigated. All additions raised the recrystallization temperature. A correlation is obtained between the logarithm of the rate of change of recrystallization temperature with atomic percent solute and the free atom ground state electron configuration of the solute element. ThE work of Abrahamson, et al., on dilute binary solid-solution alloys indicated a correlation between the free-atom ground state electron configuration of the solute and either the brittle-ductile transition or recrystallization temperature. These studies were carried out on bcc base materials. The implication is that the outer s and d electrons of the solute are the prime determinant of the absolute rate of change of recrystallization or transition temperature. Furthermore, the limit of linearity has been shown to be a function of solute electron configuration for recrystallization in iron and vanadium. To date no Complete systematic recrystallization study of dilute binary zirconium base alloys has been made. It is the purpose of this study to note whether the change in solvent structure from bcc to hcp will influence the correlation. It was also desired to learn more of the role of the electron configuration of the solvent on recrystallization temperature. PROCEDURE All alloys were made using 99.87 pct Zr with 0.01 Cr, 0.04 Fe, 0.006 Hf, 0.003 Mg, 0.003 Mn, 0.003 N, and 0.080 0 (132 BHN). The solute elements were 99.9 pct pure. According to the published binary phase diagrams6 and metallographic examinations at X750, all alloys used were solid solutions. The alloys were arc melted and remelted six times in the form of cubic 200-g buttons under an argon atmosphere. They were then hot pressed at 950°C to 0.450 in., upset pressed to 0.350 in., and annealed at 800°C for 1 hr. The specimens were then Blanchard ground to 0.250 in., removing 0.050 in. from each side. The grain size of the material at this stage was found to be 8000 100 grains per sq mm. The specimens were then cold rolled to 0.130 in. and cold pressed to 0.125 in., yielding 50 1 pct cold work. All alloys were then chemically analyzed for the principal addition. The interstitial contents remained at the values of the starting material when checked on random alloy specimens. The rolled sheet was cut into 6.75 by 0.25-in. lengths and heat treated in a gradient furnace for 1 hr. The gradient was 250o to 900°C over the 6-in. length, recorded continuously by six thermocouples resting on each specimen. Control was 3oC, accomplished at the hot end. The recrystallization temperature was determined metallographically using polarized light. The criterion chosen was the point on the specimen showing the first recrystallized grain at a constant magnification, X200. Specimens were repeated, and the agreement was found to be 3°C. RESULTS Three different pure zirconium specimens were tested, and the recrystallization temperature was

Jan 1, 1962

By Donald Warren, J. F. Libsch

HIS investigation originated as a result of a pre-vious experimental study' of the magnetic properties of Fe-Co alloys fabricated by the powder metallurgy technique. Densities of powder compacts prepared for the magnetics investigation varied from 7.45 to 7.70 g per cu cm or from 93 to 95 pct of the experimental value of 8.08 g per cu cm for a fused alloy of the same composition.' While this range of density is considered sufficiently high for most applications, the highest possible density is to be desired for maximum magnetic properties. By applying a technique similar to the one described above to a pure electrolytic iron powder, Rostoker³ was able to achieve a density of 7.895 g per cu cm, which is the highest density ever reported for sintered iron. While Rostoker's work involved the sintering of an elemental powder rather than a mixture, it was believed that higher densities should also have been obtained for alloys using the above technique because of the recoining operation and the high sintering temperature. Consequently, it was decided to investigate the various factors affecting the density of this alloy with the idea that such a study might lead to higher densities and, as a result, powder alloys having magnetic properties identical with those of the fused alloys. It was believed that the principal reason that near-theoretical densities for the powdered alloy were not obtained was the interference of gases with the normal sintering mechanism. When present during the sintering operation, gases can exert several harmful effects: they can remain on the particle surface and interfere with surface diffusion and plastic flow; they can be released and, under certain conditions, expand the void spaces through gas pressure; or they can remain trapped in the pores and exert a hydrostatic pressure that retards elimination of the pores. Jones,4 Rhines,5 Goetzel," and others have given the effect of gases in the sintering of powder compacts an extensive treatment. Among the more important sources of gases in the sintering process are dissolved gases, adsorbed gases, air entrapped during pressing, and gaseous products of chemical reactions. During sintering adsorbed gases are partly released at a relatively low temperature, while those gases entrapped during pressing cannot escape until their pressure is increased sufficiently through increasing temperature to expand the interpartjcle openings. The remaining adsorbed gases, gaseous reduction products, and dissolved gases produce a similar effect at the higher temperatures. If, in the sintering process, gas evolution occurs after the interpore channels have been sealed, an exaggerated expansion of the void spaces results. This is particularly true if the temperature is high enough for extensive plastic flow. In his fabrication of powder bars from tantalum, Balke7 had to consider the effect of adsorbed hydrogen and provide for its escape during sintering by limiting the compacting pressure to a maximum of 50 tons per sq in. The effect of gases entrapped during pressing was first noted by Trzebiatowski8 when he found that gold and silver powders decrease in density with increasing sintering temperature if pressed at 200 tsi, while they exhibit the usual increase when pressed at 40 tsi. Recent investigators9-11 have also noted that entrapped gases have an effect on the expansion of copper compacts during sintering. Proper provision for the escape of gaseous products of reduction must be made in order to avoid deleterious effects. Myers" states that in the sintering of electrolytic tantalum powder, the temperature was gradually raised to 2600°F with a pause at 2000°F to permit reduction of the oxides. Experimental Details For the present study, 50 pct Co-50 pct Fe compacts in the form of circular disks 1½ in. in diam and 0.15 in. thick were fabricated by the pressing and sintering of a mixture of the elemental powders. It was decided to follow the sintering process by means of liquid permeability measurements, because it was thought that such measurements might serve as a measure of relative pore sizes, as well as a possible indication of the point at which most of the interpore channels become sealed. However, since the permeability as measured by the flow of a liquid, such as ethylene glycol, does not give an absolute indication of the point where the pores have become isolated, a method for determining the percentage of pores connected to the surface was set up. As an additional cross check on the permeability measurements, metallographic methods were used to study the relative pore size. Finally, the property of ultimate interest, the density, was measured. Raw Materials: The powders used consisted of an annealed, 99.9 pct pure, —150 mesh grade of electrolytic iron powder, and a 98 pct pure, —200 mesh grade of reduced and comminuted cobalt powder. The cobalt powder was not further processed either by hydrogen reduction or annealing. The screen analyses for the iron and cobalt powders are given in Table I, while the chemical analyses for each type of powder are listed in Table 11. Table 111 gives the hydrogen loss measurements for the powders according to the M.P.A. Standard Method and for a higher temperature as well. Preparation of Compacts: Equal amounts of the elemental powders were mixed by rotation for 1 hr and then pressed into compacts approximately 0.15

Jan 1, 1952

By P. R. Sperry

In an investigation of the decomposition of the solid solution in a cold worked high-purity aluminum alloy containing 7 pct Mg, aged at temperatures from 30o to 82°C, the nucleating sites at the earliest stages of precipitation were observed to be of two types. Nucleation occurred at the high angle grain boundaries both when the alloy was initially cold worked and when solution annealed. Nucleation also occurred at certain unique deformation markings which began to appear in abundance at approximately 30 pct reduction in thickness by cold rolling. These deformation markings were identified as deformation (kink) bands rather than as the usually assumed "slip planes." Zn material that was cold rolled 15 pct, only the grain boundary Fig. 2—A1-7 pct Mg alloy, cold worked 60 pct and heated at 230° C for 5 min. Etched with Perryman's reagent. X500. Reduced approximately 25 pct for reproduction. (a) Bright field illumination, precipitate deeply pitted. (b) Phase contrast, showing slip markings.

Jan 1, 1962

By C. H. Li, R. J. Stokes, S. H. Bendel, J. A. Sartell, T. L. Johnston

The mechanism of the oxidation of high-purity copper has been studied at temperatures from 500° to 981°C employing gravimetric, high-temperature microscopic and inert marker techniques. An investigation of the adhesion of copper oxides was also made. The oxidation of copper is found to be parabolic at all temperatures. It is concluded that the controlling mechanism is the outward diffusion of CU+ ions through the Cu2O layer, but the mechanism of diffusion is modified by the state of compressive stress in the oxide layer at the oxidation temperature. At temperatures below the transition from elastic to plastic behavior of Cu2O the growth stresses reach a value sufficiently high to cause CuO whiskers to be extruded. The extrusion of whiskers results in the injection of a large number of vacancies into the CuO. The Cu20 layer grows by the advance of the CuzO/CuO interface into vacancy-rich CuO. Since there is an adequate supply of non -thermally created vacancies, the activation energy for oxidation is that required to move the Cu+ ion through the appropriate saddle point to a neighboring vacancy, which has been determined to be 20,000 cal per mole. At temperatures at which the Cu20 can deform plastically the stresses are never high enough to cause whiskers to form. thus vacancies must be supplied by themal activation and as a result the activation energy increases to 40.000 cal per mole. ALTHOUGH extensive studies of the oxidation kinetics of pure copper have been made in the past. the mechanism has received relatively little attention. As a result, certain features of the kinetic data have not been satisfactorily explained' For example, several workers1,2 have reported that the activation energy for oxidation in the range from 500° to 700° C was about 20,000 cal per mole whereas that above

Jan 1, 1960

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending' upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2'3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn's early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By Jr. W. L . Phillips

The deformation and fracture characteristics of lithium-fluoride single crystals stressed in compression at room temperature have been studied. In as-cleaved specimens the stress-strain curves were variable; two types of {110} fractures were observed in the vicinity of kink bands. The stress-strain curves of annealed crystals were reproducible; {100} cracks formed which propagated along the (100) and (110) planes. The deformation and fracture characteristics were affected by quenching and X-ray irradiation. STUDY of the mechanical behavior of nonmetallic materials has received considerable impetus in recent years because of the need to overcome the problem of brittleness before the refractory properties of nonmetallics can be fully exploited. Ionic crystals provide a convenient and simplified starting point from which to study the deformation and fracture processes in nonmetallic materials. Early investigations of the mechanical behavior of non-metals were restricted largely to determinations of the crystallographic indices of the cleavage and fracture planes and the glide and twinning elements. Until recently, only occasional systematic studies of the deformation characteristics of non-metals have been made; and investigations of the forces necessary to initiate plastic deformation and the factors which affect the flow characteristics have been restricted largely to studies of sodium chloride'-7 , magnesium oxides-l3 and lithium fluoride. 14-22 Fracture studies on alkali halide and metal oxide single crystals have been limited despite the fact that these materials have a number of advantages for fracture studies. Because they are transparent, the cracks which form can be viewed in three dimensions instead of in two dimensions as in metals. Also, they exhibit stress birefringence under polarized illumination, which enables the internal stress pattern and, therefore, the distribution of dislocations to be examined in the vicinity of the fracture. Early workers1-4 have shown that ionic crystals with a cubic structure fracture in tension along the (100) plane normal to the applied stress. These fractures were brittle at room temperature and propagated very rapidly across the cross section of the crystal. More recently, Stokes, Johnston, and Lil0 have studied crack formation in compressed magnesium-oxide single crystals. They found that the cracks, which were observed after about 3 pct strain, formed in the region of a kink band and lay on conjugate (110) slip planes instead of the usual(100) cleavage plane. Two different types of cracks were noted: stroh23 and secondary. The Stroh cracks did not exist merely on the surface but extended through the specimen in the form of tiny slits. A secondary

Jan 1, 1962

By A. Dubé, G. Letendre, C. E. Beaulieu

An experimental study has been made of the time dependence of internal .friction and modulus of rigidity in- freshly quenched steels at room temperature. The effects of frequency, composition, and various thermal treatments are given. The kinetic 1aws observed cannot be fully explained by the so-called first stage of tempering and the transformation of retained austenite. It is suggested that the observed phenomena are due to the progressive immobilization of dislocations introduced by the martensitic transformation. It is generally agreed that the conversion of tetraginal martensite into cubic ferrite and ce-mentite occurs in three stages which at moderate rates of heating take place in the following temperature ranges:'-3 a) The first stage involves mainly a partial loss of tetragonality of martensite and the formation of ?-carbide between 95" and 175oC. b) The second stage consists of the decomposition of retained austenite between 230 and 290' C. c) The third stage covers the formation of ce-mentite between 290o and 400' C. The kinetic laws of these heterogeneous reactions have also been the subject of isothermal studies. Thus, Roberts, Averbach. and cohen3 report a very low reaction rate with a eutectoid steel at room temperature. For example, less than 10 pet of the contraction associated with the first stage is observed after 50 hr at room temperature. Hollonlon, Jaffe, and Buffum4 show that under the same conditions less than 10 pet of the tetragonality is lost. These results have led to the belief that martensite is a relatively stable phase at room temperature. On the other hand, it is well known that important structural changes occur in martensitic steels during the first few minutes at room temperature after quenching. This pretempering has at least two important consequences. In the first place, freshly quenched steels have a tendency to crack at room temperature, a fact which leads to the necessity of tempering as soon as possible after the quench. Another important consequence of pretempering a steel for short periods of time at room temperature is the stabilization of the retained austenite. Thus, as shown by Cohen,5 a very pronounced stabilization is effected with holding periods of 30 min at room temperature. Since these two effects are apparently not caused by the heterogeneous reactions mentioned above, they must be related to the rearrangement of structural defects within the martensite and retained austenite. According to the modern theory of dislocations, the shears required to effect the austenite-marten-site transformation may be realized through the motion of dislocations at the austenite-martensite interface and within the martensite plates.6 In this way, a martensitic transformation closely resembles a plastic deformation. In cold-worked solids, high concentrations of dislocations are left immediately after the plastic deformation and it seems reasonable to assume that appreciable densities of dislocations should also appear in the wake of a martensitic transformation. A considerable part of the high hardness of martensite would then originate in the obstruction of dislocations in analogy

Jan 1, 1961

By Elmer Weber, W. M. Baldwin

Solid lead obeys a single parabolic weight increase vs. time law. In contrast, liquid lead undergoes three successive parabolic weight increases vs. time laws, the first of which has a low constant relative to the latter two. The conversion times for the change from one parabola to the next decrease with increasing temperature. IN recent reports on the subject,1,2 it was noted that zirconium and titanium scale in air by a complex mechanism. The scale first forming on the metal is protective to the extent that it gives a low constant, K, for Tammann's, and Pilling and Bedworth's parabolic equation: w² = Kt [1] relating weight increase, w, due to chemical reaction of the metal with the air, and time, t. After hundreds of hours of apparent stability in some cases the first scale yields to another that offers little protection to the metal. This transition from one scale to another, from a slow parabolic oxidation reaction to a fast one, was not due to impurities in the atmosphere or incidental effects (changing environment, etc.) but was a specific behavior of the metal itself, the transition occurring at definite times (dependent on temperature) and showing other reproducible traits. In view of this behavior how can long-time service behavior be predicted from short-time laboratory tests, not only in the case of these metals, but in any case? Certainly a systematic study of the type of scaling behavior described above—wherever it is found—would help to answer this question. The present paper is a report on the behavior as it is found in lead—the only metal to the authors' knowledge for which the behavior has been described at all, if inadequately, for our present purpose.* At least four oxides of lead are known, of which one occurs in two allotropic forms. They are ß (red) tetragonal PbO stable up to 486°C;8 a (yellow) orthorhombic PbO stable from 486°C up to its dissociation temperature in air at about 2300°C;9 minium or Pb3O4 which from the dissociation pressure data given in Fig. 1 decomposes to PbO at 540°C in air; lead sesquioxide or Pb2O3,; and lead dioxide or PbO2 which, according to Fig. 1, decomposes in air at 400°C to minium. In view of the high dissociation temperature of PbO, lead will scale up to at least its boiling point. Further, it is known that oxygen is almost insoluble in liquid lead.'V his implies a fair probability that an oxide scale would not dissolve in the molten metal and would afford the same protection to lead in the liquid state as in the solid. All of the oxides of lead for which specific gravity data are available are more voluminous than an equivalent weight of metal or a lower oxide from which they might form, hence the scales will be in compression. Lead oxides are known to be ductile, so it would be anticipated that they would form coherent nonporous scales. It is not surprising to learn, then, that both solid and liquid lead scale according to the Tammann, and Pilling and Bed-worth law.14,15 (Gruhl states that at 600°C and above lead oxidizes linearly with time because of "spitting" of the scale.) The parabolic constants K reported by various investigators3,14-16 are badly scattered, however, as shown in Fig. 2. The oxides formed on solid lead were described as being reddish-brown but were not chemically identified by Pilling and Bedworth.15 Gruhl's descripdin³ of the appearance of the scales On his liquid samples indicates that a (yellow orthorhombic) PbO is formed initially on the specimens but gives Way eventually—at least at temperatures below 486 °C— to .ß (red tetraunal) PbO, and that below 540°C minium—Pb3O4 :is firmed at an even later time as an overlay on either the red or yellow PbO. Fig. 3 is a graphical interpretation of Gruhl's description. Gruhl does not indicate any change in the parabolic scaling rate as yellow PbO converts to red. He does indicate that minium reduces the scaling rate, al-

Jan 1, 1953

By R. F. W. Pease, R. A. Ploc

A scanning electron microscope with a resolving power better then 100Å has been developed for the direct examination of surfaces. This instrument was used to study iron undergoing oxidation at 500°C. It was found that the electron current in the scanning electron microscope was low enough (about 10-atrzp) to have no observable effect on the growth of the oxide. "Armco " iron, when oxidized, exhibited an oxide film whose thickness and whiskey population varied with pain orientation; but purer iron, when oxidized, exhibited no such pain dependence and whisker occurrence appeared to be caused by impurities. UNTIL recently most surfaces of opaque specimens could either be studied with a light microscope or, if higher resolution was required, by viewing a replica of the surface in a transmission electron microscope. Direct electron microscopy of a surface has, in general, proved difficult owing to excessive foreshortening and the poor image quality obtained. The scanning electron microscope, however, offers an alternative method of directly viewing a surface without these disadvantages. At low magnification it offers a much larger depth of focus than the light microscope, and at high magnifications it offers much higher resolution (about 100Å). PRINCIPLE OF THE SCANNING ELECTRON MICROSCOPE A schematic diagram is shown in Fig. 1. The electron optical system consists of a gun followed by a series of lenses which focus the electron beam onto the surface of the specimen. The beam is scanned in a rectangular raster across the specimen surface and, by amplifying the secondary electron current from the 'pecimen, a picture of the specimen surface is built UP sequentially on the face of the display cathode-ray tube. The magnification of such a system is given by the ratio of the scan amplitude on the display cathode-ray tube to

Jan 1, 1965

By G. W. P. Rengstorff

In an effort to find an oxidation-resistant alloy of molybdenum, binary and ternary alloys containing aluminum, chromium, cobalt, iron, nickel, silicon, titanium, tungsten, vanadium, and zirconium were screened. Fourteen other alloying additions were also tested. Many of the alloys were more oxidation-resistant than molybdenum, but none were entirely satisfactory. MOLYBDENUM oxidizes extremely rapidly above 1450°F in air. At 1800°F, a loss of metal at the rate of 0.1 in. in 4 hr is typical. The high speed of this oxidation may be judged by comparison with the oxidation rate of 0.1 in. per year (0.00005 in. in 4 hr), sometimes taken as the maximum permissible oxidation rate at 1800°F for a satisfactory Fe-Cr-Ni alloy. Great strides have been made in the development of coatings and cladding to protect molybdenum from oxidizing atmospheres. These developments in surface protection will undoubtedly make it possible to take advantage of the excellent hot strength of molybdellum and its alloys in many new applications. Still, even the best coating can protect molybdenum only as long as the surface layer is unbroken. Research was undertaken to determine whether an alloy of molybdenum could be found which would resist oxidation. Such an alloy would not deteriorate suddenly when the protective surface layer was destroyed in a small area. In seeking an alloy of molybdenum to resist oxidation, the physical properties of molybdenum could not be sacrificed entirely. The development of an alloy with the desired resistance to oxidation was not achieved. The information obtained on the effect of a large number of elements on the oxidation of molybdenum is, however, of value in the development of coatings. Indeed, many of the alloys tested for oxidation resistance were already known to have poor mechanical properties but were tested to aid in the development of coatings. Oxidation of Molybdenum The rapid oxidation of molybdenum is usually attributed to the volatility of Moo,,. Gulbransen and Wysong have shown that molybdenum oxidizes very slowly up to 850°F, the temperature at which the oxide film begins to evaporate. Melting as well as evaporation of molybdenum oxides promotes the oxidation of molybdenum. MoO melts at 1465°F. MOO, the oxide which is believed to form at the metal-oxide interface, combines with MoO, to form a eutectic having a melting point of 1432°F.' The liquid oxide, even if nonvolatile, could cause poor resistance to oxidation by allowing easy transport of molybdenum and oxygen ions through the oxide. Actually, a sudden increase in the rate of oxidation of molybdenum at 1460°F has been observed to coincide with the appearance of a liquid phase. The formation of a volatile oxide is not unique with molybdenum. The problem is also encountered with vanadium, tungsten, and some of the Pt-Pd group of metals. Vanadium not only forms the volatile V2O3 but, like molybdenum, forms a liquid oxide coating. Few attempts have been made, however, to prevent the rapid oxidation of these metals by alloying. Oxidation of Molybdenum Alloys At the beginning of this work, very little was known of the oxidation resistance of molybdenum alloys. It was known that molybdenum disilicide (with 37 pct Si) has extremely good oxidation resistance,' but this compound is so brittle that it has few uses. It is an effective protective coating for molybdenum when allowance can be made for its brittleness. Chromium was known to retard the oxidation of molybdenum,' but at least 50 pct Cr was necessary to have an appreciable effect. Other, unpublished, reports show that a few other alloys have been given preliminary tests, but the results have not been promising." Choice of Alloys to be Investigated An alloying element might be expected to protect molybdenum in either of two ways: Its oxide might combine with molybdenum oxide to form a stable, nonvolatile complex oxide (a molybdate); or the oxide of the alloying element might form in preference to molybdenum oxide, developing an impervious layer which would prevent the formation of a volatile molybdenum oxide. The knowledge available about the formation of molybdates was meager. Therefore, the initial study was made on alloys of molybdenum with elements having especially stable oxides. On this basis, binary and ternary alloys containing the following six elements were investigated: aluminum, chromium, titanium, zirconium, silicon, and vanadium. Nickel was also added as an alloying element. Although it does not form a more stable oxide than molybdenum, it does impart some oxidation resistance to copper and iron. Its inclusion in the study was fortunate because its alloys proved to be the most promising of those first tested. Apparently nickel formed a stable molybdate. Because nickel was effective in reducing the oxidation rate of molybdenum, the elements iron, cobalt, and tungsten were added to the list. The ten alloying elements mentioned form ten binary and 45 ternary alloying systems with molybdenum. A series of alloys was tested in each of these systems. In addition, at least one test was made on the effect of each of the following alloying elements:

Jan 1, 1957

By F. H. Wilson, M. L. Kronberg

The low temperature recrystalliza-tion of very heavily rolled copper produces a fine grained structure with a high degree of preferred orientation. Additional heating to within a few hundred degrees of the melting point may induce an abrupt and pronounced increase in the grain size, with the resulting crystals having new orientations. This behavior at high temperatures is commonly termed "secondary recrystallization." Several investigations have dealt with the phenomenon arid have served to bare many features of the beha~ior.1-4 In general,observations have been made on the sizes and shapes of the grains, and data have been presented showing the existence of an induction period in isothermal experiments. Although it has been well established that the orientation before the change is statistically (100) 10011, the so-called "cubically aligned" texture, there is no such agreement on the orientation after the change. For example, Dahl and Pawlek1 describe it as being equivalent to an approximately 30" rotation about the [l00] axis of the ideal cubic texture which is parallel to the rolling direction, the resulting orientation being near (210)[001]; and Cook and Richards2 find an orientation of approximately (110)[L12]. Since the completion of most of the work to be reported in this paper, Rowles and Boas3 have published their ver] illuminating paper on "secondary recrystallization," in which they present convincing evidence for a third orientation and show that their esperiments give no evidence for either of the other two orientations. The orientation is described as equivalent to an approximately 30° rotation about a [ 111] pole of the ideal cubic orientation. The existence of a variety of reported orientations is not unique for copper, for a similar state of affairs exists for other systems that have been studied— aluminum, nickel, nickel-iron alloys, and others. It seems therefore that the existence of this variety does not necessarily constitute a contradiction, but rather indicates that different experimental conditions yield different results. The fundamental nature of the phenomenon has not been elucidated. However, it has been generally recognized that the large grains could be the end product of growth of a few select grains already existing in the sample in minor amounts—too small to allow detection—or that entirely new ones could be formed by a process of nu-cleation and growth. Existing experimental evidence does not distinguish between these two most apparent possibilities. Nevertheless, the former has been more generally favored largely because our current understanding of the state of an annealed metal has not made it seem reasonable to expect a nucleation event to occur at temperatures above those required for the primary recrystallization. Observations on the Preparation and Heating of Twin-bearing Cubically Aligned Copper The starting material used throughout. the investigation was a bar of OFHC copper, forged and annealed at 950°C. Visual inspection showed the grain size to be around 0.5 mm, and did not disclose any preferred orientation. A chemical analysis showed the following composition: Cu + Ag— 99.99 Pct S — 0.005 pct 0 — <0.005 pct For the preparation of cubically aligned copper, ¾ in. thick slabs were cut from the bar, heavily pickled in concentrated HNO3 and cold rolled to sheets about 0.012 in. thick. The reduction in thickness was approximately 98.5 pct. Standardized annealing techniques were followed. Samples to be heated were lightly dusted with alumina in order to prevent sticking and then sandwiched between 1/16 in. copper plates. The resulting sandwich was heavily wrapped with copper sheet, and then annealed in air. The protection was such that only very thin films of oxide were formed. That the associated light oxidation of the samples had no specific effect on the recrystallization behavior was shown by the similar results that could be obtained on annealing in highly purified and dried hydrogen. Two methods were used in bringing samples to temperature: (1) by placing the package directly in the furnace at temperature and (2) by placing the package in the furnace at room temperature, and then slowly increasing the temperature. The corresponding heating rates are illustrated in Fig 1, and will be referred to as "rapid" and "slow," respectively. Unless specified otherwise, all anneals will be of the former type. Metallographic examination was made on samples prepared by electrolytic polishing and etching as described in the Metals Handhook.* STRUCTURES FOUND BEFORE "SECONDARY RECRYSTALLIZATION" OCCURS Annealing the rolled material for 1 hr at 400°C produced a heavily twinned, cubically aligned structure, the grain size being of the order of 0.03

Jan 1, 1950

By Jean Howard

RECENT attempts to produce secondary recrystalli-zation in high-purity iron have given conflicting results. Coulomb and Lacombe1&apos;2 did not find it but Dunn and Walter3,4 did. The latter workers have stated that (100) [001] and/or (110) [001] orientations develop depending on the oxygen content of the annealing atmosphere. This Technical Note records results which are in agreement with Dunn and Walter in so far as it shows that secondary recrystallization can be produced in high-purity iron, but does not confirm that both types of orientation are obtainable. Similar observations have been made on chromium-iron and molybdenum-iron, although when this technique is used on 3 1/4 pct Si-Fe, both types are obtained as in the work of Dunn and alter.&apos; Pure iron strip was cold-rolled from sintered compacts prepared from Carbonyl Iron Powder-Grade MCP of the International Nickel Co. (Mond) Ltd. The powder contains about 0.5 pct 0, 0.01 pct C, 0.004 pct N, (0.002 pct S, $0.005 pct Mg and Si, and 0.4 pct Ni—that is, it is substantially free from metallic impurities other than nickel, which is thought to be unimportant in the present work. The iron powder was (a) pressed at 25 tons per sq in. into blocks measuring 3 by 1 by 0.3 in., (b) deoxidized in hydrogen (dewpoint -60°C) by heating first at 350°C and then at 600° C until the dewpoint returned to -60°C at each temperature and (c) sintered in hydrogen (dewpoint -40°C) at 1350°C for 24 hr. (when dewpoint is referred to in this Note, it is the value as measured on the exit side of the furnace). The sintered compacts were cold-rolled to 1/8 in., annealed in hydrogen (dewpoint -60°C) at 1050°C for 12 hr and cold-rolled to 0.004, 0.002, and 0.001 in. with inter-anneals at 900°C for 5 hr and a final reduction of 50 pct. Final annealing of strip between alumina or silica plates at 875" to 900°C in hydrogen with dewpoints of -20°, -55" and -80°C produced secondary grains with the (100) in the rolling plane; the extent of secondary recrystallization was greatest when the dewpoint was -55°C. Annealing in a vacuum of 2 x 10"5 mm Hg at the same temperature produced no secondary recrystallization at all. With strip thicker than 0.002 in. very few secondary crystals developed whatever the conditions of annealing. Using a processing schedule somewhat similar to that described above, secondary recrystallization was produced in two bcc alloys of iron, viz. 80 pct Fe + 20 pct Cr and 96 pct Fe + 4 pct Mo. The former was reduced to final thicknesses of 0.001 to 0.004 in. and the latter to final thicknesses of 0.001 to 0.016 in. With the chromium-iron, a final anneal at 1250°C (found to be the most effective temperature for developing secondary crystals in the 0.004-in material) with a dewpoint of -25°C produced a greater degree of secondary recrystallization than with dewpoints of -50°C or -20°C. Secondary crystals developed in strips of all thicknesses from 0.001 to 0.004 in. Final annealing in vacuum produced no secondary crystals at all. For the molybdenum-iron a temperature of 1200°C was most effective. It was found that a dewpoint of -50°C during the final anneal gave better results than a dewpoint of -25 "C on the 0.008 in. material. Final annealing in vacuum gave slightly worse results than annealing in hydrogen with a dew-point of -50°C. Secondary crystals were developed in strips of all thicknesses up to 0.008 in. The experiments show that the extent of secondary recrystallization is a maximum for certain critical values of oxygen content of furnace atmosphere and annealing temperature, and that these values are different for different alloys. The thinner the material, the less critical these values are. The general conclusions are that secondary recrystallization can be obtained in high-purity iron, chromium-iron, and molybdenum-iron, using a processing schedule similar to that which will cause the phenomenon to take place in high purity 3 1/4 pct Si-Fe. Unlike the silicon-iron, however, only the (100) (0011-- orientation has been produced in these alloys, irrespective of the temperature of final annealing and the oxygen content of the furnace atmosphere. The information used in this Note is published by permission of the Engineer-in-Chief of the British Post Office.

Jan 1, 1962

By T. V. Philip, R. E. Lenhart

When commercial silicon iron sheets of varying magnetic quality are isothermally annealed at high temperatures, extremely large grains develop in the material having good magnetic properties. These grains are of the (110) [001] orientation and are formed by secondary recrystallization. The primary driving force for this secondary recrystallization is grain boundary free energy. For the secondary grains, activation energies of 103 kcal per mole for nucleation, and of 75.5 kcal per mole for growth, were obtained. The activation energy for nucleation of the secondary grains is consistent with a model involving redistribution of a precipitate acting as the primary grain growth inhibitor. SINGLY oriented silicon iron sheet was first produced in 1935.1 The material as commercially produced today has a very highly developed preferred orientation or texture; up to 95 pct of the grains are crystallographically oriented with their (110) planes in the plane of the sheet and their [loo] directions parallel to the rolling direction. This texture, usually written as (110) [00l], is referred to as the "GOSS" or the "cube-on-edge" texture. Because the magnetic properties of this material are superior to those of the nonoriented sheets in the direction of rolling, the oriented silicon iron has acquired tremendous industrial importance especially in the manufacture of transformer cores and other electrical equipment. The commercially produced material is essentially an iron-silicon alloy containing about 3 1/4 pct Si with minor impurities totaling less than 0.15 pct. The silicon steel heat is melted in the open hearth or electric furnace. The ingots are hot rolled, with or without being slabbed, to strips of 0.100 to 0.080 in. thickness. They are then cold reduced to an intermediate thickness, recrystallized, cold reduced to final thickness, decarburized, and finally annealed at a high temperature. During this high-temperature anneal, extremely large grains with the cube-on-edge texture are produced in the sheet. Several papers have appeared in the literature2-10 relating to the production of the Goss-textured material. Most of these describe the textures produced on cold rolling and on subsequent annealing of single crystal or polycrystalline silicon iron. May and Turnbull11,12 have recently shown the necessity of a second-phase dispersed impurity in the material for the production of the Goss texture. However, none of these papers describes in detail the nucleation and growth kinetics of the (110) [001] grains during the final high-temperature anneal.* The present work, therefore, is an attempt to understand the nucleation and growth kinetics of the cube-on-edge grains in the silicon iron sheet during the final high-temperature anneal.

Jan 1, 1962

By Jean Howard

ALTHOUGH zone melting has found favor in recent years because of its convenience and its faster rate of production of single crystals, the older technique of strain annealing still has a number of advantages. It has been reported1 that the lattice of a crystal prepared in this manner has fewer defects than one grown from the melt and, of course, the control of the external geometry is easier. Also, the diameter of the crystal which can be grown by zone melting has a theoretical limit determined by the surface tension, thermal conductivity, and specific gravity of the material, while the size of that which can be grown in the solid state is limited only by practical considerations. In a program for the study of the structure-sensitive properties of niobium and its alloys it was desirable, for ease of handling, to have available single crystals of large diameter. This requirement dictated the choice of the strain-anneal technique. Induction heating was chosen in the present work in preference to other methods because of its deep penetration of large-diameter sections. A five-turn coil, powered by a motor generator operating at 10,000 cps, is contained in a vacuum chamber. The work is lowered through the coil for both the recrystallization and the crystal-growth steps. Starting with electron-beam melted material, the bars are cold-swaged, recrystallized, strained in a tensile machine, and then subjected to the growth step. Single crystals have been grown under the following conditions: Reduction in area during swaging— 79 to 99 pct, recrystallization temperature—1500o to 1667°C at the rate of 1.25 in. per hr, strain—1.0 to 2.5 pct, growth temperature—1600o to 2400°C at rates from 0.15 to 1.25 in. per hr. Starting grain sizes achieved after the recrystallization step varied from 0.6 to 1.55 mm. The starting grain size was found to be critical; if it is too fine and has any residual cold work, as shown by the presence of a fiberlike texture, a single crystal cannot be grown. Using this technique niobium single crystals have been grown from 0.250 in. diameter and 12 in. long to 1.00 in. diameter and 5 in. long as shown in Fig. 1. The 1-in. crystal is the largest to be reported for a refractory metal as compared to 0.500 in. for molybdenum grown by zone melting.2 As with zone melting, control of orientation is possible by the use of special procedures. Other investigators, see for example Williamson and Smallman,3 have reported that orientation control may be achieved by a bending technique. In the present work the strained rod is partially lowered through the coil to start the growth of the crystal. Then it is removed and bent at a point ahead of the interface between the single and polycrystalline portions. Finally, it is returned to the chamber and growth is continued "around the corner". The amount of bending which can be imparted to the rod is limited by coil geometry which up to now has been 10 deg. However, by repeating the bending and growing operations it should be possible to attain any desired orientation. The perfection of these single-crystal specimens as a function of process variables is being measured by X-ray and metallographic techniques and the results will be reported in a forthcoming paper. This work was partially supported by the Advanced Research Projects Agency.

Jan 1, 1964

By Jean Howard

ThE formation of the (100) [001) texture in 3-1/4 pct Si-Fe strip was first reported by Assmus ef a1.l in 1957. Since then much experimental work has been carried out with a view to establishing the mechanism involved. The papers cited above state that the (100) [001] texture was developed in strip rolled from material melted and cast in vacuum. (The impurity content of the ingot is reported as 0.005 pct.) The present note records that similar results can be obtained in material processed by powder metallurgy. A processing schedule is described.which enables the texture to be formed in strip up to 0.010 in. thick, but there seems no reason why this should not be achieved in thicker strip, provided that large grains are developed after sintering. The materials were prepared from Carbonyl Iron Powder Grade MCP (particle size 5 to 30 p) of the International Nickel Co. (Mond) Ltd. The powder contains about 0.15 pct 0, 0.01 pct C, 0.004 pct N, <0.002 pct S, $0.005 pct Mg and Si, and 0.4 pct Ni— that is, it is substantially free from metallic impurities other than nickel, which is thought to be unimportant in the present work. The silicon powder was 99.9 pct purity, or material of transistor quality (ground in pestle and mortar). The mixed powders (3-1/4 pct Si to 96-3/4 pct Fe) are heated in hydrogen at 350" and 650°C to deoxidize the iron before sintering loose at temperatures between 1350" and 1460°C (depending upon the ultimate thickness of strip required) for up to 24 hr. The object of the high-temperature sinter is to develop a large grain size at this stage. Alternatively, the loose sintering can be done at a lower temperature followed by rolling or pressing and then annealing at temperatures between 1350" and 1460°C. Both methods produce large grains, which remain large throughout the process. The compact is then hot-rolled to approximately 1/8 in. with high-temperature interstage anneals if necessary. This step is taken to avoid intercrystalline cracking which would occur if the material of such large grain size were cold-worked. The bar is then annealed at 1050°C and reduced to its final thickness by approximately 50-pct reductions and 1050°C interstage anneals. Throughout the process the dew point of the hydrogen furnace atmosphere is maintained at about -40°C. Samples were annealed in hydrogen at various temperatures and times. Secondary recrystalliza-tion to (100) [001] was developed on the thinner material (i.e., up to 0.002 in.) by annealing in hydrogen at 1050" to 1200°C with a dew point of - 40°C or in vacuum (10-5 Torr) at 1050°C. With the thicker materials (i.e., up to 0.010 in.) the best results were obtained by annealing in hydrogen at 1200°C with a dew point of - 55°C. Complete secondary recrystal-lization to (100) [001] textures was obtained. Above these temperatures secondary recrystallization to (110) [001] tended to develop. The final annealing of samples was normally carried out with the samples placed between recrystal-lized alumina plates, but some experiments were performed with the samples suspended so that their surfaces were not in contact with anything except hydrogen, and these were equally successful in developing secondary crystals. An approximate determination of the proportion of material (before secondary recrystallization took place) having crystals with the (100) or (110) planes in or near the rolling plane showed that 11 pct of the sample had (100) and 16 pct (110). The method used for the determination is described below. A sample was annealed at a temperature just below the secondary recrystallization temperature and etched to reveal the (100) planes. The approximate area covered by crystals having (100) or (110) in or very near the surface was measured on the screen of a Vickers projection microscope. This was repeated for twenty positions chosen at random and a mean of the results calculated. The main hindrance to developing the secondary crystals in the thicker materials was the difficulty of obtaining a large enough initial primary grain size before secondary recrystallization. This was overcome by increasing the particle size of the silicon powder used. During the course of the work, it had been observed that the larger the grain size after sintering the more likely it was that the material would be successful in developing secondary crystals at a later stage. An experiment was therefore carried out to determine whether the material with the larger grain was more successful in developing secondary crystals due to the large grain produced at the sintering state per se or whether it was due to the greater reduction of silica brought about when the sintering temperature was raised in order to increase the grain size. A comparison was made between two compacts, one of which was made with silicon powder of 60 to 100 mesh, the other with silicon powder which was finer than 200 mesh. F?r this experiment, use was made of a phenomenon previously observed that the larger the particle size of the silicon powder employed in making a compact, the larger is the grain size of the compact. The silicon powder was ground

Jan 1, 1964

By H. Biloni

A metallographic study of solute segregation produced during controlled solidification of Sn-Pb alloys has previously been reported.&apos; It was found that the growth conditions which produced well-developed cellular substructures led to severe segregation, and even at solute concentrations of 0.2 wt pct Pb regions of a lead-rich phase were formed at the junctions of cell boundaries (nodes). Similar sample preparation and etching techniques have now been applied to several tin alloys at more dilute concentrations. The crystals were solidified uni-directionally under less-severe growth conditions so that the predominant interface structure was composed of two-dimensional cells.* Binary alloys with lead, using 9.999 pct Sn as a solvent, and ternary alloys with lead and bismuth or lead and antimony, using zone-refined tin as a solvent, were examined. The liquid was decanted from the growing crystals in all cases to reveal the interface structure and ensure that two-dimensional cells were being formed. However, since interference may arise from a liquid layer that clings to the interface during decanting,3 an examination of the segregation pattern was always made behind the interface. In all cases, the structure within the bulk of a crystal at greater than 1 cm behind the decanted interface was substantially the same as that nearer the interface. Representative photomicrographs of the dilute Sn-Pb alloy are shown in Figs. 1, 2, and 3. Most observations are similar to those of the previous investigation. For example, the solute concentration at the cell walls is higher than in the intercellular regions; where cell boundaries meet, the segregation is enhanced; the macromosaic or stria-tion substructure and grain boundaries show enhanced segregation; there is also a depletion of solute at cell walls near a striation boundary, as Spittle et a1.4 have observed at decanted interfaces. Not all these observations can be seen in the photos shown since attention has been focused on a special feature; as evident in the photomicrographs, cer-

Jan 1, 1965