By W. D. Donnelly, M. L. Rudee

THE crystallography and morphology of ?-Al3Fe precipitates in an A1 + 0.5 wt pct Fe alloy have been studied by transmission electron microscopy. The alloy was cast in cylindrical ingots, 15 cm in diameter and 60 cm in length, and cooled slowly. The measured composition was 0.527 wt pct Fe, 0.001 wt pct Mg, and 0.003 wt pct Cu. Spectrographic analysis revealed no additional trace impurities. Thin slices were cut from the ingot and reduced by more than 95 pct by rolling to a thickness of 0.1 mm with no intermediate annealing treatments. These thin sheets were then vacuum-annealed for 1 hr at 612°C and air-cooled in their capsules. Thin foils for examination in the electron microscope were prepared by electropolishing. The precipitate is found in the form of oval platelets on the (110) planes of the matrix. The major axes of the platelets are parallel to the (110) directions of the matrix, and vary in length from 1/2 to 2 p. The thickness is about 1/10 µ. Examples of platelets, both in the plane of the foil and normal to the foil, are shown in Figs. l(a) and l(b), respectively. lack' found that ?-A13Fe (more correctly Al13Fe4) belongs to the monoclinic system. Using Black's structural data and simultaneous electron-diffraction patterns from the matrix and precipitates, the habit planes and directions were determined to be: (001)? 1 (110)Al [100]?|| H [001]Al The orthogonal crystallographic axes of the precipitates are accurately in the habit plane, while the measured coincidences of the directions are only within 10 deg. The major axis of the platelet is parallel to [010] in the 0. This orientation corresponds to the direction of nearest registry of the lattices.

Jan 1, 1964

By J. F. Tavernelli, L. F. Coffin

The deformation and fracture characteristics of eight metals subjected to fully reversed cyclic strain ranging from 0.2 to 50 pct were investigated at room temperature. Strain-hardening characteristics unique to the interna1 structure of a particular metal were found. Complete removal of the strain-hardening effects resulting from prior deformation was brought about by subsequent cyclic strain. Further support for the validity of the inverse relationship between the plastic strain range and the square root of the number of cycles for failure is given. THE resistance of materials to cyclic plastic strain is of interest both from a fundamental and practical point of view. It is now a well-accepted fact that fatigue failure in metals is a consequence of the localized slip deformation which occurs within the individual crystals of metal.'-' Hence the failure process should be strongly dependent upon the magnitude of the gross cyclic plastic deformation of the metal under conditions where this is a measurable quantity. Therefore, an experimental investigation of metals in which the cyclic plastic strain is the independent variable should shed new light on some of the basic aspects of the problem. From the practical point of view, there are many uses for information relating to the cyclic strain resistance of metals. One is the case of thermal stress fatigue where fatigue failure can occur as a consequence of a com- paratively few cycles of thermally induced mechanical deformation. Another is the mechanical working of metals where large cyclic strains are employed. In recent years several publications have appeared relating to the cyclic-strain resistance of metals,8-11 dealing mostly with the fracture aspects where the temperature is cycled simultaneously with the mechanical strain. Some work has been reported on the cyclic-strain resistance of metals at constant temperature, again oriented more toward the fracture aspects of the problem than the deformation aspects. 12-16 The present research investigation was undertaken to obtain information regarding the deformation characteristics of several metals whose structure-property relationships were simple and straightforward under conditions of both cyclic and monotonic strain. It has been shown for example that under cyclic-strain conditions some materials will strain harden, while other materials, particularly cold-worked structures, strain soften and these effects required further clarification.8,17-19 It was also de-

Jan 1, 1960

By W. L. Phillips

Stress-strain curves were obtained for single crystals of 70 pct Ag-30 pct Zn tested in tension and shear. Samples tested in tension and shear had comparable resolved shear stresses and stress-strain curves. The {111} <110> slip system was observed. It zoas found that the9.e is a barrier to slip in both latent close -packed directions and that the magnitude of these barriers is proportional to prior strain during easy glide. It was observed that cross-slip in tension and shear was most frequent in crystals with an initial orientation near <100> "Oershoot" zoas observed in tension. The amount of this "overshoot" was independent of initial orientation. AN idealized concept of plastic deformation indicates that a single crystal should yield at some stress that is dependent on crystal perfection and it should then continue to deform plastically by the process of easy glide which is characterized by a linear stress-strain curve and a low coefficient, d/dy, of work hardening. Hexagonal metal crystals generally conform to this ideal concept of laminar flow. In fcc metals the range of easy glide is always restricted in magnitude and it is strongly dependent on orientation, composition, crystal size, shape, surface preparation, and temperature. Since one of the principal differences between the two crystal systems, both of which deform by slip on close packed planes, is the existence of latent slip planes in the fcc crystals, it has been proposed that the transition from easy glide to turbulent flow, characterized by rapid linear hardening, is due to slip on secondary planes intersecting the primary plane.ls Several theories have been proposed to explain the linear hardening and parabolic stages of the stress -strain curve.6"10 The easy-glide region is the least understood of the three stages. The stress-strain characteristics of Cu-Zn, which shows a long easy-glide region, have been extensively investigated."-" In light of recent ideas on dislocations, cross-slip, effect of solute atoms, and stacking fault energy, it was felt that the certain features of this earlier work might be compared with another alloy, Ag-30 pct Zn, which also exhibits a long easy-glide region. Tension and shear stress at room temperatures were employed. The results obtained, together with some interpretation of the observations, are described below. EXPERIMENTAL PROCEDURE The silver and zinc used for mixing the alloys were 99.99 pct pure. The two components were weighed to within 0.1 pct of the weights required fo the alloy composition. They were then placed in a closed graphite mold and the mold and contents were heated in 100°C stages from 500&apos; to 900°C with sufficient time and vigorous agitation at each stage provided to dissolve the silver. The crucible was then heated to 1150°C and agitated violently before being quenched in oil. The resulting alloy rod was machined free of sur face defects and then placed in a graphite mold designed for growing single crystals. The graphite mold was closed with a graphite plug and was encased in a pyrex glass tube which was connected to a vacuum system. The tube and mold assembly were placed in a furnace; the tube was evacuated and the furnace was rapidly heated to a temperature sufficient for fusing and sealing the glass. The glass-encased evacuated mold and contents were then lowered through a vertical furnace. The top section of the furnace was held at 100 °C above the melting point of the alloy. The lowering rate was 1.5 in. per hr. The tension specimens were 1/4 in. diam; the shear specimens were 1/2 in. diam. These specimens were then removed from the mold, etched, and chemically polished with hot (60°C) Chase etch reagent (Crz03-4.0 g, NH4C1-7.5 g, NHOs-150 cc, HzS04-52 cc, and Hz0 to make 1 liter). In preparation for tensile testing, the specimens were carefully machined to a diameter of about 0.200 in. to permit a gage length of 6 in., annealed for 16 hr at 800&apos; to reduce coring, and then cleaned and polished. A modified Bausch-type shear apparatus which has been described previously18 were employed. The gage length was 1/8 in. This shear apparatus was placed in an Instron tensile testing machine. EXPERIMENTAL RESULTS A) Tension. Several specimens were extended at room temperature to determine the effect of initial orientation on the stress-strain curves of Ag-30 pct Zn. The initial orientation and the resolved shear stress supported by the active slip system at various total strains are plotted in Fig. 1. The critical resolved shear stress, t,, initial rate of work hardening, d/dy, and length of the easy-glide region are independent of orientation. The arrival at the symmetry line is shown by an arrow in Fig. 1. During the easy-glide region of the stress-strain

Jan 1, 1963

By P. Duwez, C. B. Jordan

The phenomenon of the change of volume of pressed powder compacts upon sintering is well known in the field of powder metallurgy. Depending upon the metal or metals involved and the pressure used in forming, a compact may, in the course of time of sintering at a given temperature, expand mono-tonically, contract monotonically, or first show a volume change of one sign followed by a change of the opposite sign. It is clearly desirable to have accurate knowledge of the magnitude and sign of the change in dimensions to be expected in any given case, both from the point of view of direct usefulness in the fabrication of parts by powder metallurgy, and from the longer range viewpoint of elucidating the fundamental mechanism of metallic sintering. The present study was therefore undertaken as a first step in acquiring systematic and reasonably quantitative knowledge of the change in density of metal powder compacts during sintering. For practical reasons, copper was selected as the material to be studied first, and its densification followed as a function of temperature and time of sintering in hydrogen and in vacuum. Experimental Procedure The copper powder used was that designated by the manufacturer (Metals Disintegrating Co., Elizabeth, N. J.) as MD-151. This powder was sifted through Tyler standard screens to separate the fraction having particle size range between 200 mesh and 325 mesh, and this fraction was used in all the subsequent work. Compacts weighing about 10 g were then pressed in a 1 in. diam round die, using a pressure of 20,000 psi throughout. Sintering was carried out in commercially built electric furnaces in which the resistance windings are so disposed as to produce a nearly uniform temperature along the axis of the furnace for a length of about 18 in. centrally located. In order to be able to sinter in a controlled atmosphere, a 2 in. stainless steel tubing was inserted in the furnace. Each end of the tube was cooled by a water jacket about 7 in. long, and closed with a rubber stopper. The hydrogen used for one series of specimens was purified as described in Ref. 1. For the other set, a pressure of about 0.5 mm Hg was maintained during sintering by a Welch Duo-Seal Pump. The specimens were heated on square trays made of stainless steel. In placing specimens in the trays, a thin even layer of powdered aluminum oxide was first sprinkled on the bottom of the tray. A copper guard disk about half the thickness of the specimen was then placed in the tray and covered with a second layer of alumina. The actual specimen was then set on the guard disk, and a final coat of alumina sprinkled over the specimen. This technique was evolved for sintering the specimens in such a way as to reduce the influence of unknown extraneous factors to a minimum. If the specimen is placed directly on the tray and sintered, it is found that the resulting shape is that of a frustum of a cone, rather than a section of a right circular cylinder, since friction with the tray prevents the bottom of the specimen from contracting at the same rate as the top. In the arrangement used in these experiments, the guard disk provided a support which shrank at the same rate as the specimen, and the alumina powder reduced to a minimum friction between guard disk and tray, and between specimen and guard disk. The procedure followed in sintering consisted of bringing the furnace to the required temperature, and then inserting the specimen into the central heated portion of the furnace tube in one of the two atmospheres used. At the end of the heating period, the specimen was cooled by bringing it into a portion of the furnace surrounded by a water jacket. These manipulations were carried out without opening the furnace, by means of rods which were attached to the trays and operated through a sliding seal in the rubber stopper. The progress of densification of the copper compacts was studied at 1300, 1400, 1500, 1600, 1700, and 1800°F. At each of these temperatures, a specimen was allowed to sinter for each of the following time intervals: M, 1, 2, 4, 8, 16, 32, and 64 hr. The thickness and diameter of each specimen were measured with micrometers before and after sintering, and each was weighed on an analytical balance after sintering. Results The techniques described in the preceding section were found to give satisfactory results. The specimens were not detectibly warped after sintering, and were usually of uniform diameter (that is, truly round) to within 0.001 in., a very few showing a variation in diameter of ±0.002 in. All specimens were found to have the same diameter

Jan 1, 1950

By P. Duwez, C. B. Jordan

A. J. SHALER*—I should like to congratulate the authors for having carried out such a precise set of experiments. It has been found useful, in sintering experimental compacts in vacuo, to make certain that the residual gas is not one which reacts with the metal. Since traces of oxygen can be kept away only with great difficulty, the technique is often adopted of using a "getter " of powder in the vicinity of the compacts, and, in addition, of permitting a small hydrogen leak to flow into the vacuum chamber. Did the authors use similar devices? This paper brings up a question concerning the definition of the word &apos; sintering.&apos; The authors restrict its use to the adhesion between particles. Kuczynski, in a paper presented at this meeting, applies the word to the growth of areas of contact between particles. I have used it to mean both these phenomena and also the dimensional changes which continue to take place after the first two have run their course. May I suggest that we should come to an agreement on the use of these words ? Fig 1 and 2 show an interesting feature: extrapolation of the curves to zero time does not give a densification parameter of zero. The higher the temperature, the higher is the intercept on that axis. These observations agree with the concept of a practically instantaneous densification taking place while the compact is being brought to heat. Such a change may be brought about by plastic deformation and primary creep. The stress pattern causing this first rapid flow is, to my mind, due to the force of attraction between the surfaces of opposite particles in the regions immediately flanking their common areas of contact. The stress is not temperature-sensitive, but at room temperature plastic deformation only proceeds until the metal in the area of contact can support it elastically. As the metal is heated, the elastic limit falls, and further plastic flow occurs. At the higher temperatures, this is followed by primary creep, and finally by the steady-state rate-reaction which the authors are seeking. If they were to recalculate their densification-parameter values, using, not the initial density of the cold compact, but the density after the compacts have been brought to temperature, the systematic deviations from linearity in Fig 3 and 4 might be eliminated. Such initial densities might be obtained by extrapolating the curves of Fig 1 and 2 to zero time. I am naturally pleased to see that such a very well done series of experiments leads to a heat of activation (for the densification process in hydrogen) that is much higher than that for self-diffusion, in confirmation of the less elaborate results reported by Wulff and myself (Ind. and Eng. Chem., (1948) 40, 838). J. T. KEMP*—I would like to comment on Dr. Shaler&apos;s remarks. There are apparently different interpretations of the word "sintering." It seems to me that an accurate definition of our word is essential in all metallurgy. May I point out, in this connection, that in practical metallurgy the word "sintering" has been applied to a bonding process in the preparation of ores and flue dust for fur-nacing. It would be unfortunate if in the area of powdered metallurgy we should establish a definition that is essentially different in meaning. F. N. RHINES*—I think that I can answer the question by saying that I see no essential difference between the use of the term "sintering" in extractive metallurgy and in powder metallurgy; physically the same things are going on. I admit sintering is used for different end purposes in the two cases. When we resort to the sintering of lead ore mixture we are doing so to obtain a chemically reactive, loose texture of some rigidity. This is only a difference in use. After all, in powder metallurgy we sometimes deliberately produce a very porous material which has just a little strength, just as in the case of sinter cake. P. DUWEZ (authors&apos; reply)—We agree that it would be helpful to have well-established definitions of such terms as "sintering." Since the question has now been raised, the time might be appropriate for its consideration by some suitable committee of one or more of the metallurgical societies. In answer to Dr. Shaler&apos;s first question, no getter nor hydrogen leak was used in our vacuum experiments, except insofar as the guard disks (used to reduce friction between specimens and trays) may have acted as getters. Dr. Shaler&apos;s statement that extrapolation of the curves of Fig 1 and 2 does not lead to zero densification at zero time apparently overlooks the logarithmic

Jan 1, 1950

By C. D. Tedmon, D. P. Ferriss

THE yield stress, o of low-carbon steel has been shown to vary with the average grain diameter, d, according to the relation1-3 where o is taken to be the lower yield-point stress Of is the friction stress on an unlocked dislocation, and ky is a constant. The interpretation2,4 of ky in terms of dislocation theory relates this constant to the stress to unlock a source across a grain boundary. cottrel14 predicted that ky would increase with decreasing temperature. This was observed to be the case by Adams and coworkers5 in their investigation of niobium (columbium). However, petch6 and Backofen: both working with low-carbon steel, found ky insensitive to temperature. In his work with high-purity niobium, Johnson&apos; found ky equal to zero. Evansg showed that k, was essentially zero for niobium containing nitrogen in an appreciable concentration range. The present experiments were designed to check this apparent anomaly in the value of ky in another Group V metal. Yield points were determined as a function of grain size at several temperatures for tantalum and a tantalum-tungsten alloy. The material used was double are-melted tantalum and a double are-melted alloy of 90 pct Ta and 10 pct tungsten (by weight), both obtained as unannealed, swaged rod. The impurity content of the materials is given in Table I. The tantalum was annealed at 1325"C. in a vacuum resistance furnace using a tantalum boat. The alloy was similarly annealed at 1660°C. Annealing times varied from 15 min to 2 hr, depending on the desired grain size. Nominal pressure in the furnace was 3 X 10~4 mm of Kg. Metallographic examination showed that the annealing treatment produced grain sizes ranging frorn 0.021 to 0.200 mm in the tantalum, and 0.060 to 0.160 mm in the alloy. Tensile bars were made by centerless grinding the annealed specimen;, and then electropolishing to remove all grinding marks. The specimens were than pulled :it 2 1/2 pct per rnin in an Instron testing machine. The tantalum specimens were tested at 77", 195", and 300°K. The alloy was tested at 300°K only. All specimens exhibited a yield-point phenomenon at all temperatures. Typical load-elongation curves at the three test temperatures are shown in Fig. 1. The lower yield stress is plotted as a function of (grain size) in Figs. 2 and 3 for tantalum and the 90 pct Ta-10 pct W alloy, respectfully. The position and slope of the curves was determined by least-

Jan 1, 1962

By R. A. Wood, R. I. Jaffee, H. R. Ogden, D. N. Williams

The tensile properties, creep resistance. and thermal stability of highly alloyed Ti-Al-Zr alloys were examined. On the basis of these studies, the Ti-7Al-1ZZr composition was selected for more complete evaluation. The alloy was found to be weldable and free from excessive directionality. In addition, it developed maximum properties without requiring heat treatment other than an annealing operation in the alpha field. The alloy was recommended for scale up and is presently being investigated on a production-level basis. One of the more attractive properties of titanium alloys is their ability to withstand stress at moderately high temperatures, and a considerable amount of effort has been devoted to increasing the maximum service temperature of titanium alloys. This work has suggested that the optimum alloys for high-temperature service will be single-phase a (close-packed hexagonal) alloys containing significant amounts of aluminum. However, the maximum amount of aluminum which can be alloyed with titanium is between 6 and 8 pct,l since at high-aluminum contents an embrittlement reaction occurs in the anticipated service temperature range, 800" to 1100°F. It has been shown that the embrittlement reaction involves decomposition of the high-aluminum a phase to one or more new phases.&apos; Since this reaction does not occur at intermediate or low-aluminum contents, it was felt that intermediate Ti-A1 alloys might be strengthened by a-soluble ternary additions without inducing the embrittlement reaction. The first alloying addition considered was tin, which shows extensive solubility in a titanium and has moderate strengthening tendencies. Unfortunately, it was soon apparent that tin also promoted the embrittlement reaction, and that to obtain a stable alloy, the aluminum content had to be reduced as the tin content was increased. The second alloying addition considered was zirconium, which is similar to tin in its effects on titanium. This element did not contribute to the embrittlement reaction and, in fact, appeared to increase the maximum amount of aluminum which could be alloyed with titanium without inducing instability. This paper describes an investigation of the Ti-A1-Zr a alloy region. Alloys containing from 4 to 12 pct A1 and from 6 to 15 pct Zr were examined. The properties of these alloys are described and the bases for selecting an optimum composition is outlined. This composition, Ti-7A1-12Zr, is presently being scaled up in tonnage quantities, and is being evaluated extensively throughout the industry. In addition to presenting the basis for its selection, this paper presents a description of the properties developed in laboratory material as determined during the alloy investigation. These properties suggest that this alloy can fill an important position in applications requiring light weight, fabrica-bility, weldability, and strength to 1000oF or higher. EXPERIMENTAL PROCEDURES Titanium alloy ingots were prepared by inert electrode arc melting under an argon atmosphere. Alloying elements used were 110 Bhn titanium sponge, high-purity aluminum, and reactor-grade zirconium. Pancake-shaped ingots were prepared weighing approximately 300 g. The composition of the ingots was checked by weight measurements before and after melting. The pancake ingots were forged at 2000°F to approximately half their original thickness to give a flat plate roughly 1/2 in. thick. This plate was then rolled at 1800&apos; to 1600°F to 0.250 in. thick. All of the alloys examined fabricated well. However, alloys containing 15 pct Zr tended to overheat due to exothermic oxidation, and scaling was excessive. As might be anticipated from its effect in decreasing the ß transus, increased zirconium appeared to improve fabricability somewhat, especially during rolling at lower temperatures. Except for a limited study of heat-treatment response, all alloys were examined in the a-annealed condition. Prior to heat treatment the a and ß tran-sus temperatures were determined by metallo-graphic examination of samples quenched after annealing at 50-deg intervals in the transformation region. These data are shown in Fig. 1. Recrystal-lization appeared to occur in about 1 hr in the range 1300º to 1500ºF. Therefore, alloys were annealed for 1 hr at 1550ºF (4 and 5 pct Al), 1600ºF (6 through 7-1/2 pct Al), or 1650°F (8 or more pct Al). This produced an equiaxed a grain structure. In most alloys, a "ghost" structure was visible after the a-annealing treatment, as shown in Fig. 2. This structure apparently resulted from the acicular

Jan 1, 1963

By E. W. Johnson, M. L. Hill

The dijfusiuity D was determined at 25° to 780°C- from hyd?-ogen evolution rates. Anomalous evolution from air-melted iron was att~zbztted to residual hydrogen, which is interpreted as a hydrogen compound that decomposes at a strongly temperature-(Ieperzdent rate above 500°C. Above 200°C, D = 0.0014 cm2sec-1 exp (-3200 cal per g atom/RT). Below, 200°C the diffusivity is anomalously low and represented by D = 0.12 cm2sec-l exp (-7820 cal per g atom/RT). It is postulated that at low temperatures the hydrogen in the metal is "trapped" with an energy 4.8 kcaL per g atom below- that of the interstitial hydrogen. 1 HE purpose of the present experimental study was to determine the diffusivity of hydrogen in a-Fe over an extended temperature range. As certain anomalies were encountered, attempts were made to understand the anomalies themselves. This research was in progress both before and after a determination of the diffusivity of hydrogen in nicke1.l The latter system was found to exhibit none of the anomalies of hydrogen in iron, and its description was far simpler. The experiments on nickel also

Jan 1, 1961

By D. Gupta, S. Weinig

This investigation comprises the study of dislocation-oxygen interactions in a! titanium and its effect on the ductile to brittle transition in titanium. Internal friction techniques using a low-frequency lorsion pendulum were used to study the oxygen atom interactions with dislocations in "superpurity" titanium. A calculation of the interaction energy between an oxygen atom and a dislocation, based on the "breakaway" strain resulted in a value of 0.015 ev as compared to theoretical values of 0.022 and 0.035 ev for edge and screw dislocations, respectively. Both the saturation of the room temperature decrement and the transition from ductile to brittle behavior occurred at 1.5 at. pct 0. It was proposed that the embrittlement was due to oxygen atoms immobilizing the dislocations. It was possible to increase the ductility of the Ti-0 binary alloys by decreasing the oxygen pinning. The increase in uniform elongation was 30 pct for an increase in the preanneal temperature of 300°C. ThE room-temperature ductility of a titanium is significantly affected by interstitial solutes. Although oxygen has a solid solubility of 15.5 pct by weight, the room-temperature ductility extends only to 0.6 pct.&apos; The ductility precipitously falls at this concentration and the fracture characteristics change from ductile to brittle.2 The small effective bulk composition of solute required to destroy the room-temperature ductility of the titanium must be indicative of an in-homogeneous distribution of solute atoms. Internal friction techniques were used in this investigation to

Jan 1, 1960

By John D. Verhoeven

A technique has been developed for carrying out normal freezing experiments with a current density of 2000 amp per sq cut passing through the solid-liquid interface. The equation relating the effective distribution coefficient to the equilibrium distribution coefficient in electric field-aided solidification, originally developed by Huckc et al.,1 has been modified for the case of concentrated solutions. Preliminary experiments on the Sn-Bi system give qualitative agreement with the equation. The data are analyzed by a slightly novel use of the normal freeze equation which allows one to determine the effective distribution coefficient more easily. Very extensive mixing in the liquid was found at these high current densities and it is postulated that the mixing results from a vertical component of the magnetic Lorentz force generated by the electric current. In the search for techniques of obtaining ultrahigh-purity metals the inefficient but very effective technique of electrotransport has received little attention. Electrotransport is most effective in the liquid state and a natural application, therefore, is to apply an electric field across the liquid zone of a zone-melting experiment. The present investigation was undertaken to study the effect of an electric field upon solidification of metals, so that the usefulness of electrotransport in such solidification experiments as zone melting could be determined. In zone-melting and normal-freezing experiments it is difficult to achieve complete mixing in the liquid in the immediate vicinity of the solidifying interface. Consequently a solute build-up will occur at the interface in the portion of the liquid where complete mixing does not occur (an equilibrium distribution coefficient, ko, less than one, and unidirectional atom motion will be implied throughout). This local solute build-up produces a corresponding rise in the solute concentration in the solid so that the ratio of the solute concentration between the solid and the bulk liquid is larger than the equilibrium distribution coefficient. This ratio is defined as the effective distribution coefficient, k,. The differential equation describing the solidification process may be derived by applying the continuity equation to an expression for the net solute flux at the interface. The solution to this differential equation then allows one to determine the solute distribution in the liquid and the relationship between k0 and ke. One of the most useful solutions to this equation was first derived by Burton, Prim, and Slichter,&apos; in which they assumed that a) the equilibrium distribution of solute was maintained on the plane of the interface, 11) the solute build-up ahead of the interface in the liquid disappeared at a distance 6 from the interface, and c) the solute distribution in the liquid was invariant with time. The following well-known relation between ko and ke was then obtained, where R is the rate of solidification and D the diffusion coefficient of the solute in the liquid. This equation appears to correlate the data from a number of different types of solidification experiments very well. Application of an electric field across the solid-liquid interface can produce an additional flow of solute atoms as a result of the electrotransport. When the polarity of the field is such as to direct the electrotransport flux away from the interface the solute build-up may be diminished, even to the point of producing a solute depletion and a consequent ke smaller than ko. The quantitative description of this process and the resulting form of Eq. [I] was first given by Hucke et al.1* and then inde- where E is the electric-field intensity and U is the differential mobility, i.e., the velocity of the solute atoms with respect to the solvent atoms per unit electric field. Both authors follow the method of Burton, Prim, and Slichter in their derivation, the only difference being the additional electrotransport term in the flux equation. It has been pointed out1,3 that Eq. [2] predicts the possibility of a noticeable increase in the purification of materials by solidification in an electric field. The validity of Eq. 121 has not been checked experimentally and it is possible that other factors&apos; arising from the presence of an electric field across

Jan 1, 1965

By P. W. Barton, A. A. Johnson, E. J. Hughes

THE only systematic work on the effect of carbon on the recovery and recrystallization kinetics of iron so far reported in the literature is that of Venturello et al.1 These workers found that doping high-purity iron so that it contained up to 86 ppm C caused a marked retardation of recovery but had little or no effect on the recrystallization kinetics. Such evidence for an effect as was obtained was inconclusive. In the course of a study of electron-beam zone-refined iron the authors have recently examined the effect of added carbon on the recrystallization kinetics of this material. The amount of carbon added was about 50 pct more than was used by Venturello et 01. and definite evidence was obtained that carbon at this level retards recrystallization. The starting material was taken from a batch of 0.2-in.-diameter Johnson-Matthey spectroscopically pure iron rods which had been further purified by being given three passes at 4 in. hr-1 in a standard MRC electron-beam zone-refining unit. The purity of this material. which was used in two other investigations of the properties of high-purity iron,2,3 was established by an extensive series of analyses. Four laboratories, the National Research Corp., Newton, Mass., the Naval Research Laboratory, Washington, D.C.. the Battelle Memorial Institute, Columbus, Ohio, and the National Physical Laboratory. Teddington. Middlesex, England. carried out analyses for carbon. oxygen. and nitrogen. and in addition a complete mass-spectrograph analysis was carried out at Battelle. In all, twelve analyses were carried out for carbon, seventeen for oxygen and twelve for nitrogen. The amounts of these elements found to be present were 10 * 7, 8 i 5, and 0.9 i 0.1 ppm, respectively. The limits given are rms deviations. Two results, one of 46 ppm of oxygen and another of 31 ppm of nitrogen, were rejected as anomalous. The mass-spectrograph analysis revealed the major impurity to be 25 ppm of tungsten. All of the other elements detected were present in amounts less than 0.5 ppm. Some of the rods were doped with carbon by being immersed in a suspension of carbon in oil, heated in a vacuum at 400°C, and then zone-leveled to make the distribution of carbon uniform. Carbon analyses carried out on three of the doped rods gave a mean value of 130 ± 45 ppm. Some of the doped and undoped rods were deformed 58 pct by swaging and cut into specimens 1/2 in. in length. Isothermal recrystallization experiments were then carried out on them at 575", 600°, 615", 630°, and 650°C, the volume fraction of each specimen recrystallized being measured by a point-counting method described by Hilliard and Cahn.4 The results for the two types of specimens are shown separately in Figs. 1 and 2. In Fig. 3 the pairs of recrystallization curves for each temper-

Jan 1, 1965

By E. G. Schempp, W. A. Morgan

The influence of modifications in the molybdenum, vanadium and, to a limited degree, carbon and boron content to a basic composition of 5 pct Cr, 0.75 pct Mo, 1 pct V hot-work tool steel composition, was studied in respect to hardenability, grpain- coarsening temperature, and tempering charactevistics. Tensile, impact, and fatigue pvoperties were studied for the most promising compositions. An alloy with a typical composition of 0.43 pct C, 4.97 pct CI-, 0.33 pct Si, 2.25 pct Mo, and 1.00 pct V uas found to offer the most favorable combination of properties in respect to high-strength applicntions when tempered at 1100°F. MANY 5 pct Cr high-strength steels are at present being manufactured in North America which fit well into the classification of the AISI-SAE system. Much interest has been shown in these materials as ultra-high-strength steels for use at elevated temperatures. The limiting temperature of use lies at the point where the steels begin to soften rapidly. Although a great deal of information has been made available in the past two years on the properties of selected alloys in this series, little information exists on the effect of systematically varying the ccntent of one or more elements in the 5 pct Cr-base alloy. This paper presents the results of an investigation of the effect of variations of the carbon, molybdenum, vanadium, and, to a limited extent, the silicon, manganese, boron, and niobium content of a 5 pct Cr steel to the AISI H-13 base analysis. EXPERIMENTAL PROCEDURE All experimental heats were melted in a 50-lb. induction furnace. The melting stock consisted of

Jan 1, 1962

By N. Nakanishi, C. M. Wayman

The effect of small copper additions on the mar-tensitic transformation behavior in Au-47.5 at. pct Cd was studied by measuring electrical resistivity as a function of temperature. The transformation behavior was found to change and transformation start (M,) temperatures for both the ß to ß&apos; and ß to ß&apos; transformations were depressed substantially by the addition of small amounts of copper. Both M, temperatures were lowered approximately 70°C per at. pct Cu. Copper also had the effect of narrowing the transformation hysteresis region (resistivity us temperature), and for the alloy Au-47.5 Cd-1.5 Cu there was little or no hysteresis; in this alloy, the reverse transfmmation upon heating apparently occurs below the thermodynamic equilibrium temperature, To. THE ß phase in the Au-Cd system occurs at the electron/atom ratio 3/2, and is similar to other ß phases in alloys based on copper, silver, or gold. It is of the CsCl type, in which a considerable degree of long-range order persists to the melting temperature.&apos; The phase boundaries of the ß phase are not known precisely below 300° C, but at room tem- perature the phase exists from approximately 46 to 52* at. pct Cd.2 At low temperatures, the ß phase transforms in a diffusionless (martensitic) manner. Alloys having a composition near 47.5 pct Cd transform upon slow cooling to an orthorhombic3 phase, ß&apos;, at - 60°C. Alloys having a composition near 49.0 pct Cd, transform at - 30°C into a phase, ß", which has been recently identified as trigonal.4 Alloys having compositions near 48.5 pct Cd will transform into both the 0&apos; and 0" phases over a range of temperatures. The progress of transformations can be observed

Jan 1, 1963

By J. T. McGrath, R. C. A. Thurston

Poly crystalline specimens of copper, and copper with various additions of zinc, were tested in plane-bending fatigue. In tests performed at a constant stress, the fatigue life of copper increased slightly with the addition of up to fifteen per cent zinc. There was a sharp increase in fatigue life as further additions of zinc of up to 35 pct were made. Surface observations showed that the coarse slip bands that are characteristic of fatigue became narrower as the concentration of zinc increased. The rate of crack propagation also decreased with increasing zinc content. It is suggested that the fatigue behavior is controlled by cross slip processes. CROSS slip occurs when dislocations move from one primary slip plane to another along a connecting or cross slip plane. The primary and cross slip planes have a common slip direction. Wide stacking faults, having low energy, tend to make cross slip more difficult. According to recent theories, the ability of a material to cross slip is important to the formation and propagation of fatigue cracks. McEvily and Machlin2 have examined this concept experimentally by fatiguing single crys tals of lithium fluoride, sodium chloride, silver chloride, and KRS-5.* The latter two materials ex- hibit easy cross slip, while the former two do not. Normal rapid fatigue failure was obtained in the silver chloride and KRS-5 specimens, whereas it was much more difficult to achieve in sodium chloride and lithium fluoride crystals. Furthermore, numerous slip band extrusions and intrusions were found in silver chloride and KRS-5 crystals, whereas only one isolated extrusion was found in lithium fluoride and none was found in sodium chloride. McEvily and Machlin also consider that there is no clear-cut demarcation between crack initiation and propagation. The intrusion-extrusion process, which initiates crack formation, continues ahead of the cracks to allow propagation of these cracks along slip bands. The process of cross slip is therefore important not only to crack initiation, but also to crack propagation. Holden4 postulates that fatigue crack growth is dependent upon cross slip and thus upon stacking-fault energy. Using an X-ray microbeam technique, he found a cyclic subgrain structure in fatigued aluminum and a-iron. Holden suggests that micro-cracks develop in the densely-packed sub-boundaries ahead of the main crack front, and when sufficiently numerous join up to promote crack growth. The ease with which a subgrain structure could form would depend upon the ability of the dislocations to cross slip, and thus upon the stacking-fault energy. Hence in aluminum, which has a high stack-ing-fault energy and in which cross slip is easy, Holden found that the relative rate of fatigue crack propagation was considerably greater than in stainless steel, a low stacking-fault energy material. It has been shown by a number of investigators that the probability of forming deformation stacking faults in copper increases as zinc is added.5-7 Cross slip should, therefore, become more difficult as the zinc concentration is increased. In order to check the validity of the foregoing theories, it was decided to test copper and copper with various additions of zinc in plane bending fatigue, and determine to what extent their fatigue properties are dependent upon their ability to cross slip. EXPERIMENTAL PROCEDURE Fatigue tests were carried out on polycrystalline OFHC copper and various copper-zinc alloys with 5, 15, 20, 30, and 35 wt pct Zn. The Cu-Zn alloys were obtained commercially in sheet form. Test specimens, as shown in Fig. 1, were machined from sheet that had been reduced to an approximate grain size of 0.040 mm, the heat-treatment procedure being similar to that of Feltham anc copley.8

Jan 1, 1963

By C. R. Simcoe, T. J. Koppenaal

The effect of direct and alternating currents on the quench aging behavior in an Al-4 pct Cu alloy has been investigated by use of resistivity measurements. The reaction rate increases with direct current density in the investigated range of 1000 to 3000 amps per sq cm. Alternating current of a specific frequency is observed to decrease the reaction rate by a factor of about two. ErDMANN-JESNITZER et al.,1,2 investigated the effect of direct and alternating current on the quench and strain aging behavior of low-carbon iron. In both cases they observed that direct current accelerates the aging reaction and that an alternating current can completely inhibit the aging process. The purpose of the present research was to investigate these phenomena in the quench aging behavior of an Al-4 pct Cu alloy and to determine the correlation, if any, between the increase in the observed reaction rate and possible heating effects accompanying the aging with direct current. EXPERIMENTAL PROCEDURE The aluminum-base alloy used in this investigation contained 3.98 wt pct Cu (1.72 at. pct) with impurities of 0.003 pct Si, 0.002 pct Fe, and 0.001 pct Mg. The alloy was rolled into a ribbon about 0.36 mm thick and 3.7 mm wide. The ribbon was split end from end with the ends being used as electrical contacts and the central unsplit section, about 5.3 cm in length, serving as the specimen. Solution treatment was accomplished by quenching from a salt bath at 520° ± 2°C into water at 25° ±0.5°C; the specimen was immediately transferred to a liquid nitrogen bath. All aging was done at 75° ± 0.2°C in a rapidly stirred ethylene glycol bath. Resistivity measurements were made by the double potentio-metric method employing a standard resistor; for purposes of convenience, the resistance measurements were made at 77°K. The transfer of the specimen from the aging bath to a liquid nitrogen dewar was accomplished in less than 1 sec. The aging kinteics were studied with the specimen being aged under the influence of direct current, alternating current, and without any type of current. The amount of heating caused by direct currents was investigated by soldering a thermocouple on the specimen surface and measuring the temperature change after applying various current densities. The temperature was observed to increase (from 75°C, the aging temperature) about 0.8°, 3.0°, and 8.5°C with direct currents of 1000, 2000, and 3000 amp per sq cm, respectively. When employing alternating current, the circuit was monitored with an oscilloscope and adjustments made to produce a normal sine-wave pattern. RESULTS Prior investigations3&apos;4 in the aging characteristics of A1-4 wt pct Cu have shown that the resistivity initially increases, reaches a maximum, and then decreases to values significantly lower than the as-quenched resistivity. This type of behavior is seen in Fig. 1 which shows the resistivity at 77°K as a function of aging time at 75°C observed in this investigation. At this aging temperature, the resistivity maximum is seen to occur in about 1 to 1-1/2 min and it further decreases to the as-quenched value in about 24 min. The behavior observed with the application of direct currents of 1000, 2000, and 3000 amp per sq cm during aging is shown in Fig. 2. With increasing current densities, (+) ?pmax decreases and the rate of the aging process increases. The time necessary to reach the as-quenched resistivity value decreases from 24 min for aging without current to about 16, 10, and 7 min for aging with 1000, 2000, and 3000 amp per sq cm direct current, respectively. Fig. 3 shows the results obtained when two changes were made during the aging with 2000 amp per sq cm

Jan 1, 1963

By J. M. Hodge, H. M. Reichhold, R. D. Manning

The work reported in this paper represents the first of a series of investigations of the factors governing notch toughness in ferritic materials. This paper is concerned with two of these factors, namely, the effect of ferrite grain size, and the effect of an alloy content of 3.64 pct nickel. Every effort has been made to hold other variables constant in order to isolate the effects of these two. The compositions chosen for study were 0.02 pct carbon in order to eliminate the variable of carbide distribution, one steel being a plain carbon steel and the other alloyed with 3.64 pct nickel. Both steels were fully killed with silicon, without an aluminum addition, so that the variable of deoxidation practice was held constant. Finally, all samples were water quenched from 1200°F and tempered 24 hr at 300°F in order to hold the quench aging variable constant and to decrease the tendency for grain boundary carbide precipitation. The ferrite grain size was varied by heat treatment over the range of A.S.T.M. grain size numbers of about 2 to 6 in each steel so that the effect could be evaluated individually and the notch toughness of each steel could be compared at comparable ferrite grain sizes. Materials and Experimental Procedure MATERIALS The materials for this investigation were obtained from Battelle Memorial Institute as 250 Ib induction melts which were forged into 134 in. square bars and then rolled into 0.6 in. square bars. Both steels were deoxidized with silicon, the aluminum content being held to a minimum. Check analyses of these materials are shown in Table 1. HEAT TREATMENT FOR GRAIN SIZE The grain size was varied by varying both the cooling rate and the austeni- tizing temperatures. The heat treatments used and the corresponding grain size values are tabulated in Table 2. A semicontinuous network of grain boundary carbide was observed in the microstructure of both the plain carbon and nickel steels in the as rolled condition and an additional heat treatment was necessary to eliminate this variable. Therefore, all samples were water quenched from 1200°F and tempered 24 hr at 300°F as a final treatment before testing. This heat treatment served to eliminate to a great extent the grain boundary carbide network and to hold the quench aging effect constant. IMPACT TESTING Standard keyhole Charpy impact tests were machmed after heat treatment. A bath of acetone and dry ice was used for refrigeration of the samples down to temperatures of —94°F (—70°C) and a bath of either methyl-cyclohexane or isopentane, cooled by

Jan 1, 1950

By Vito J. Colangelo

The primary object of this study was to determine the effect of ferrite and its orientation upon the mechanical properties of a precipitation -hardening stainless steel with particular attention to the short-transverse properties. The investigation consisted of Jour major parts : the preliminary investigation of billet properties, the effect of forging reduction and ferrite content upon mechanical properties, the effect of notch orientation upon impact strength, and the relationship of heat composition to ferrite content. Low ductility and impact strength in the short transverse direction were found to he associated with the orientation and shape of- the ferrite plates. It was also determined that impact strength varied with notch orientation. The test values obtained with the notch perpendicular to the plane of the ferrite plate were lower than those obtained in the notch-parallel condition. The over-all investigation showed that high ferrite contents in general had a deleterious effect upon mechanical properties and that the ferrite content could he minimized by exercising rigorous control of the heat composition. A careful balance of elements, nitrogen in particular, must he maintained in order to reduce the formation of ferrite. THE precipitation-hardening stainless steels were developed to fulfill a need for high-strength corrosion-resistant alloys. In the annealed condition they are soft and ductile and possess many of the desirable characteristics of the austenitic stainless steels. In the hardened condition, the alloys exhibit the high strength and hardness of the martensitic stainless steels. The alloy under consideration in this investigation has a nominal composition as follows: C Mn Si Cr Ni Mo N 0.13 0.95 0.25 15.50 4.30 2.75 0.10 The hardening mechanism is identical to that of other hardenable steels in that it depends upon the transformation of austenite to martensite. This alloy because of its annealed structure and its ability to be hardened combines the desirable forming and corrosion properties of the austenitic grades with the high hardness and strength levels attainable with the hardenable grades. The reason for this apparent duplicity of proper- ties can be explained by considering a basic metallurgical difference between the hardenable stainless steels and those of the austenitic group. Both types are austenitic at 1800°F but, while the martensitic grades transform to martensite upon rapid cooling to room temperature, the austenitic grades remain austenitic even when cooled to temperatures below room temperature. The major difference then is in the degree of austenite stability. This stability can quantitatively be described by the Ms temperature. The Ms is defined as that temperature at which austenite begins to transform to martensite. The austenitic grades for example may be cooled to -300°F without producing significant quantities of martensite. The hardenable stainless steels on the other hand have an Ms temperature in the vicinity of 400" to 700°F. In cooling to room temperature, these alloys traverse the entire Ms-Mf range and show almost complete transformation to martensite. The semiaustenitic stainless steel, however, occupies an intermediate position with respect to its austenite stability. The analysis is so balanced that the Ills temperature lies at or slightly above room temperature. The resulting alloy retains much of its austenite at room temperature and yet responds to hardening heat treatments. Achieving this delicate balance of elements is therefore of great importance. Slight imbalances of the equivalent Cr-Ni ratios frequently result in the presence of 6 ferrite. It is the effects of this ferrit with which we are concerned, more specifically the effect of the quantity and ferrite orientation upon mechanical properties, particularly ductility. PROCEDURE A) Preliminary Investigation of Billet and Forging Properties. In order to determine the effect of ferrite on billet properties, billet stock from three heats with various ferrite contents was utilized. Tensile specimens were obtained in the transverse and longitudinal directions from this material and heat-treated as shown in Tables I and 11. Forgings were made from these same heats, the purpose being to determine what effect, if any, the ferrite might have upon the mechanical properties. These forgings were made in such a manner as to elongate the ferrite in the longitudinal and transverse directions. The method of forging was as follows. A section was cut from a 6-in.-sq billet of Heat A and flat-forged to 1-1/2 in. thick. Working was done from one direction only with no edging passes as shown

Jan 1, 1965

By F. G. Tahmoush, N. J. Grant, E. P. Abrahamson

The effect of grain size on the brittle -ductile transition temperature of pure iron and three dilute Fe-W alloys has been investigated by slow bend tests. The brittle-ductile transition temperature for pure iron increased with increasing grain sizes from 8000 to 500 grains per sq mm where the transition temperature then decreased with further increase in grain size. The dilute additions of tungsten lowered the transition temperature for fine grain sizes, suppressed a reversal of the curve in the coarse grained portion, and raised the transition temperature for this region. The frequency of twin occurrence increased with increasing grain size and decreasing temperature. The object of the present investigation was to re-examine the effect of grain size on the brittle -ductile transition of pure iron and several dilute Fe-W alloys. Current literature normally presents a simple relationship between grain size and the brittle-ductile transition temperature, namely, that the transition temperature increases with increasing grain size. Heslop and etch&apos; have studied the transition temperature of mild steel by V-notch Charpy impact tests for the grain size range between 200 and 6000 grains per sq mm. The result was a linear plot of In 1-1/2 vs brittle-ductile transition temperature, where 1 is the grain diameter. Recent experiments by sipos2 revealed the possibility of a reversal in the slope of the grain size vs transition temperature plot for pure iron; however, his investigation was limited in scope, and the data obtained were insufficient to permit a definitive curve. The present investigation was undertaken in an effort to confirm or extend the grain size effect observed in iron by Sipos. PROCEDURE All alloys were vacuum induction melted, using 99.95 pct Fe containing 0.03 pct 0 and 0.004 pct C. Four ingots were made, ranging from pure iron to iron with 0.035 pct W. The chemical composition of each alloy, after processing, is given in Table I. The four alloys were prepared as 45 lb heats and cast into 4 in. diam by 16 in. molds. They were then extruded into 3/4 in. rods at 1800oF. Specimens for chemical analysis, taken from various positions along the rods, revealed no variation in tungsten content along the length. The extruded rods were reduced to 0.156 in. diam stock by a series of cold swaging operations involving intermediate vacuum annealing treatments. This procedure yielded a final cold reduction in area ranging from 10 to 90 pct. The swaged rods were chemically cleaned, cold pressed to a cross section of 0.10 by 0.18 by 1.0 in. long (2.54 by 4.73 by 25 mm). The specimens were wrapped in iron foil and vacuum sealed (10-4 mm Hg) in quartz. Various heat treatments at temperatures from 700" to 1300oC were utilized to produce grain sizes from 8000 to 1 grain per sq mm. Grain sizes were determined by measuring the average area of grains in a polished section. In specimens with grain size greater than 20 grains per sq mm, the total number of grains in the cross section was counted and then divided by the area to yield grains per sq mm. Grain size was measured both for longitudinal and transverse cross sections. The average of the two measurements was plotted vs transition temperature. An Instron Table Model testing machine was used to determine the transition temperature of specimens tested in three point horizontal bending. The specimen was supported by two 1/4 in. dowels one in. apart. Bending was accomplished with a push rod, the end of which had an 1/8 in. radius. The head speed was 50 in. per min. Temperatures were established through the use

Jan 1, 1963

By G. W. Tuffnell, S. Floreen

Three Fe-18 pet Ni-base ternary alloys cortaining carbon, molybdenum, or cobalt were aged to pgroduce hardening by carbides, Ni3Mo, or ordering, respectively. Each alloy was tested in rotating-beam fatigue tests after hardening to 195 ksi ultim.ate tensile strength. The fatigue properties of three alloys soere essentially identical. The results suggest that tlze fatigae strength of an igron-base alloy should depend primarily upon the tensile strength, and not iipon the hardening mecaanisrn. THE fatigue strengths of many steels have been found to be directly related to their ultimate tensile strengths. For ultimate strengths below 200 ksi, the fatigue endurance limit at 107 to 10&apos; cycles is approximately half the ultimate strength. Essen- tially all of the steels that have been tested, however, have been hardened by carbon. Thus it is not certain whether the relationship between fatigue and ultimate strengths is a general one that applies for other types of hardening in steels, or whether it applies only for the particular method of hardening by carbon. The recent developments of the martensitic precipitation-hardened stainless steels and the marag-ing steels have shown that it is possible to achieve high strengths in iron-base alloys by other hardening mechanisms than that due to carbon. Therefore, it is now possible to compare the fatigue properties of several iron alloys having the same ultimate strengths but hardened by different mechanisms. For the present study a binary Fe-18 pct Ni martensite was selected as a base material. This particular matrix composition has been found to have deformation characteristics very similar to pure iron.&apos; Three ternary alloys were prepared by adding either 0.23 wt pct C, 5 wt pct Mo, or 20 wt pct Co to this base composition. After suitable heat

Jan 1, 1965

By J. F. Butler

The degree and type of carbide dispersion resulting from changes in the cooling rate from austenite determine the amount of carbon remaining in solution after slow cooling- from a subsequent subcritical annealing treatment. A difjusion model has been proposecl to explain the effect of carbide dispersion on the amount of carbon retained in solution and the amount of carbon in solution has been related to the degree of carbon strain aging. COTTRELL and Leak&apos; have shown that the rate of strain aging in low-carbon steels is dependent upon the amount of carbon and nitrogen in solution. Carbon can be effectively removed from solution as Fe , C by quench aging at temperatures of 200" C or lower; however, the relatively higher solubility of nitrogen at these temperatures prevents sufficient removal of nitrogen as iron nitrides. For this reason, nitrogen in solution has been considered the major cause of strain aging in rimming grades of commercial low-carbon steels. Nitrogen can be effectively removed from solution and nonaging steel produced through the addition of aluminum to form the stable nitride, AlN; however, the aluminum also causes deoxidation resulting in a killed steel. III an attempt to produce a rimmed steel which was also nonaging, Morgan and Shyne 2 investigated tile strain-aging properties of low-carban steels containing boron and found that strain aging was suplx-essed in steels containing as little as 0.007 pet B. The original purpose of this investigation was to determine the mechanism of strain-aging suppression by boron. Early in the study, the function of boron was discovered to be much like that of aluminum in that the formation of a nitride, BN, removed the nitrogen from solution.&apos; However, during the course of the investigation, an effect of heat treatment upon the strain-aging properties and the amount of carbon in solution was found which could be related to the microstructure of the steel. The purpose of this paper is to examine these relationships among heat treatment, microstructure, carbon in solution, and strain aging in steels where nondetectable amounts of nitrogen are present in solution. EXPERIMENTAL PROCEDURE The investigation was carried out using 0.030 in. by 12. in wire specimens which had been cold swaged and drawn to the final diameter. Table I lists the compositions of the low-carbon steels used. Those with &apos;V&apos; designations were vacuum melted and cast; the alloys designated &apos;AISI&apos; were prepared from high-purity iron obtained from the American

Jan 1, 1962