By T. Vasilos, J. T. Smith

THE mechanism of pressure sintering, or hot pressing, for ceramic materials, has been investigated by several researchers.1-8 Plastic flow has been suggested as the rate-determining mech-anism1,2 while grain boundary sliding3,4 and fragmentation processess have been found controlling in other studies. Vasilos and Spriggs5,6 have reported that pressure sintering occurs by a diffusion-controlled mechanism. For the pressure sintering of metals, investigations with lead7 and with tin6 have not identified the operative mechanism during consolidation of these powders. This note reports the results of a pressure sintering study initiated to determine the mechanism controlling the densification of spherical copper powder. Temperatures of 300°, 400°, 500°, and 600°C at 2500, 5000, 7500, and 10,000 psi pressures were investigated. The copper powder for this study was obtained from Metals Disintegrating Co., Elizabeth, N.J. The minimum purity was reported to be 99.9 pct. The powder size was -325 mesh and a lineal analysis showed the average size to be less than 1 p. An alumina die body and punches were employed. Graphite spacers were placed between the copper powder and the punches before pressing. It was expected that the graphite would form carbon monoxide with any entrapped air and form a reducing atmosphere within the die cavity. This condition was generally realized during pressing although a minor amount of oxidation occurred at 500" and 600°C. The oxide particles were located randomly in the pressed samples and were not considered to influence the densification process. Calibration tests showed the temperature of the copper pellet to be about 20°C less than the die wall temperature, probably resulting from heat losses through the punches. This difference was compensated during the experimental pressing operations. The hot pressing equipment employed for this work has been described by Spriggs et a1.9 and was calibrated with a Baldwin-Lima-Hamilton load cell. Travel of the punches was monitored with a dial indicator showing increments of travel to 0.0005 in. Relative density was calculated at selected time intervals for a known copper weight, punch travel, and die diameter. The accuracy of this calculation was *1 pct. Average grain size after hot pressing was obtained by lineal analysis. Typical densification curves are presented in Fig. 1 and Fig. 2 where relative density is plotted vs log time as a function of applied pressure for the 300" and 600°C pressure sintering temperatures, respectively. The curves for 400" and 500°C were similar to those at 300°C and consequently are not shown. The curves at 300°C as well as 400" and 500°C do not show an end-point or limiting density for a particular applied pressure. At 600°C, a density in excess of 95 pct of theoretical has been reached such that further densification is extremely slow for the 5000, 7500, and 10,000 psi pressures. It is suggested that further densification at these pressure levels may be retarded or prevented by discontinuous grain growth, by entrapped gases, and by other microstructural limitations as described by Cob1e.10 The curve for 2500 psi hot pressing pressure is a straight line over the time interval although a slight change in slope may be occurring at the last time intervals. The plastic flow models,1,2 derived for hot pressing, predict the existence of an end-point (or limiting) density dependent on the yield point of the material at the temperature of interest. The yield stress of copper at a 0.005 strain level has been

Jan 1, 1965

By J. W. Rutter, K. T. Aust

In previous studies of grain boundary migration in zone-refined lead, the authors used bicrystal specimens consisting of a striated crystal which was grown from the melt, and an adjacent striation-free crystal, introduced by artificial nucleation and growth.1 While this method permits the study of the motion of individual grain boundaries, it does not provide control of the relative orientations of the grains. The present note will describe a technique for controlling the orientations of the two crystals in this type of specimen. The technique consists essentially of placing a striated crystal and a striation-free crystal of controlled orientations end-to-end in a graphite trough, then melting a short zone at the junction of the two crystals and allowing it to freeze to form the desired grain boundary. The apparatus used to carry out this process is illustrated in Fig. 1. It consists of a trough milled from high-purity graphite,with grooves in the underside for the placement of thermocouples. The graphite piece fans out on one end at the level of the bottom of the trough; the sides of the trough are completed in this region by the attachment of a mating plate with a slot cut at any desired angle to permit reorientation of the crystal placed at this end of the assembly. The joint between the crystals is made at or near the point where the slotted plate joins the rest of the trough. The thermocouple slots are deepened in this region so that the thermocouples are separated from the melt by only 1/32 in. of graphite. An induction heater, with suitable temperature control, is used to obtain the molten zone. The two single crystals used are first chemically polished in a solution consisting of eight parts glacial acetic acid and two parts 30 pct hydrogen peroxide. They are then placed in the trough with the ends to be joined at the position of the thermocouples. Next, cooling is applied to the two crystals by means of air

Jan 1, 1962

By K. E. Nelson

The effect of thorium and zinc variations on the strength and 100-hr creep characteristics of Mg-Th-Zn-Zr alloys was investigated. Optimum resistance to creep at 650° and 700°F are attainable within a certain range of thorium and zinc contents. This range does not conform to that which develops maximum tensile properties. RAPID advances have been made during the last few years in the development of magnesium alloys for elevated temperature applications demanding high resistance to creep. The beneficial effect of rare-earth metals on the creep resistance of magnesium alloys has been emphasized by a number of publications1-13 and such alloys are now in commercial production. The use of thorium as an alloying ingredient in magnesium was mentioned by McDonald and also in two Alien Property Custodian patent applications.10,17 The initial observation of Sauerwald that thorium contributes still higher creep resistance to magnesium than is attainable with rare-earth metals has recently been substantiated.'" " In fact, it has been demonstrated that the useful temperature range of magnesium alloys is appreciably extended by the use of thorium. In all cases, it was observed that zirconium must be included in the alloys in order to render them fine grained and more readily castable. Several recent publications:2-27 indicate that a still further improvement in creep resistance and a further extension of the useful temperature range can be realized by the addition of zinc to alloys. The primary purpose of this paper is to present the results of a comprehensive study of the effect of zinc on the strength and creep characteristics of Mg-Th-Zr alloys. Compositions covering the range of thorium content from M to 6 pct and zinc content from 0 to 5 pct have been investigated. The creep characteristics at 650" and 700°F reported in this paper are based on results of tests of 100-hr duration. It is appreciated that creep tests of 100-hr duration might not yield adequate data for design purposes for parts with much longer expected life. However, for the purposes of the present discussion, it is felt that the combination of stresses and temperatures used in the 100-hr creep tests have yielded a clear representation of the compositional variation of creep resistance at the temperatures investigated. Creep tests of 1000-hr duration are now in progress on a few of the most promising alloys. Preparation and Testing of Alloys The alloys studied in this intensive investigation were prepared in 25 lb capacity mild steel crucibles. The thorium, zinc, and zirconium were alloyed and poured as described in earlier publications The thorium was introduced into the melt in the form of a Mg-Th hardener," the zinc added in the metallic form, and the zirconium alloyed in the form of the commercial hardener containing magnesium and 30 to 50 pct Zr.10, 26 Fluxing practices for melting and refining were the same as for magnesium-rare-earth metal-zirconium alloys. The melts were sampled for analytical determinations and poured into separately cast 1/2 in. diameter standard tensile bars. The test bars were given a precipitation treatment of 16 hr at 600°F in laboratory furnaces. It has been shown by other tests that a high temperature solution treatment followed by an aging treatment is unnecessary for the development of optimum properties in Mg-Th-Zn-Zr alloys. The selection of 600°F as the aging temperature was based on an attempt to achieve metallurgical stability without coalescence of the undissolved phases and the attendant loss in strength. The thorium, zinc, and zirconium contents of each melt were determined chemically. The zirconium contents are reported in two parts, "soluble" and "insoluble," referring, respectively, to the portions present in the alloy which are soluble and insoluble in dilute HCl acid. Distinction is being made between these two components of the zirconium content in the alloys because it has been found that only that portion of the zirconium content which is soluble in dilute inorganic acids affects the structure and properties of the alloys. The usual impurities consisting of copper, iron, manganese, and nickel were determined spectroscopically. The analysis for each melt is listed in Table I. A description of the methods of tension and creep testing has been detailed in earlier papers. The tests were performed with the cast skin re-

Jan 1, 1954

By J. J. Casey, R. S. Busk, D. L. Leman

The mechanical properties and the phase-temperature relationships of magnesium-lithium-aluminum, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys are presented. It is shown that the strengths of some of these alloys can be tripled by heat treating and aging but that the high strength is accompanied by brittleness and lack of stability. MAGNESIUM-LITHIUM alloys are interesting because the hexagonal structure of magnesium can be changed into the more ductile and workable body-centered cubic structure by the addition of only 10 pct lithium.1 After Loonam2 determined that the ductility of the magnesium-lithium alloys is destroyed by even trace quantities of sodium, it was possible to prepare ductile alioys and study their mechanical properties. Jackson3 and coworkers have ably described their results with both the binary and polynary magnesium-lithium alloys. The present paper is a report of the mechanical properties of wrought magnesium-lithium-aluminurn, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys. Experimental Procedure The alloys were made by melting 7 lb of magnesium in a steel crucible under a molten flux of 75 pct LiCl + 25 pct LiF3 previously dried at 1600°F. The metal was heated to 1300°F for alloying aluminum and zinc and then cooled to 1250°F for adding lithium (sodium content: 0.01 to 0.04 pct). After the lithium had been alloyed, dry LiF powder was sprinkled on the melt to thicken the excess flux. After a 15 min holding period, the flux was skimmed off. Paraffin vapors were used to protect the metal as it was poured into 3 in. diam by 11 in. long magnesium molds. Billets were extruded into 3/8-in. diam rod and 1/16 x 3/4-in. strip; sheet was prepared from 1/8x 7/8-in. extruded strip, first by hot rolling and then by cold rolling 2 pct per pass. Hot rollability, or the temperature range through which the alloys could be rolled, was determined by rolling the strip two passes at 30 pct reduction per pass. Cold rollability, or the percentage of cold reduction to cause detrimental cracking, was determined on 0.064-in. hot-rolled sheet. Standard ASTM procedures were followed to obtain the mechanical properties, using 0.2 pct offset for the yield strengths. The level of properties produced with commercial magnesium alloys using the procedure described is given in a previous publication." Results Magnesium - Lithium - Aluminum System: The good workability of magnesium-lithium alloys is illustrated by the data in table I, which shows approximately how the extrusion pressure decreases as the amount of cubic phase increases. Binary magnesium-lithium alloys are soft and weak, but aluminum raises their strengths con-

Jan 1, 1951

By R. J. Allio, C. H. Randall

An automatic system for the quantitative analysis of microstrulcture has been developed. The method is based upon a statistical model of microstructure and employs phase intercept fractions as fundamental random variables. Structure-sensitive properties can be related explicitly to parameters derived from the distribution of phase intercept fractions in a matevial. THE properties of mechanical dispersions and of multiphase alloys art: intimately related to the amount, distribution, and intrinsic properties of the dispersed material. In many instances, the amount and distribution of the dispersed substances have greater influence on the over-all system properties than do the properties of the dispersed substance-Such properties as average particle size, particle size distribution, homogeneity of dispersion, volume per cent of dispersed phase, and mean free path between dispersed particles thus become critical in any evaluation of the properties of a dispersion. Unfortunately, techniques for evaluating quantitatively the microstructural characteristics of dis~ersions rapidly and accurately have not been available. If necessary, qualitative or semiquantitative devices can be utilized. Some such devices are based merely upon comparison of the specimens in question with arbitrary standards. Other techniques involve superposition of grids and tabulation of particles observed in different portions of the grid. Still other methods based upon lineal analysis entail counting lines or points at random upon the specimen to be examined; the number of intersections of the line with a given phase, the proportion of line or number of points which are covered by given phase are variously recorded. The mathematical basis for most of the techniques of quantitative metallography have been amply reviewed in the literature.'l2 without exctption, however, the standard techniques for quantitative metallography are either imprecise or are exceedingly tedious to apply. For example, tranverse integrating stage for rapid manual areal fraction measurement has been designed by Smith.3 Howerer, as in the case of any device based upon visual eslimation, operator bias may cause appreciable error. Various flying spot devices, on the other hand register particle size distributions in 2-dimensions, from which it is difficult to derive other properties of the dispersion. Thus, e.g., the 3-dimensional distribution cannot be inferred unless certain rather broad assumptions are made concerning the randomness of distribution and geometrical configuration of dispersed phase. Many limitations to the application of quantitative structural analysis can be overcome by the use of the microdensitometer, which is essentially an automated areal analysis device. Data obtained in the form of a distribution of phase intercept values are

Jan 1, 1962

By R. P. O’Shea

AS part of a program to investigate phase relationships in ternary systems containing semiconducting elements and compounds, an X-ray survey of alloys in the system Pb-Te-Bi was carried out which revealed that the pair PbTe-Bi probably formed a quasibinary system. This portion of the ternary was examined fully by thermal analysis, X-ray, and microscopic procedures. More than twenty-five alloys were made by melting together the proper combinations of the elements in quartz tubes at a temperature of 1000o C. The compositions which were high in PbTe content were prepared in evacuated, sealed, quartz tubes, allowed to freeze in vacuum, and then transferred to Crucibles for thermal analysis. The bismuth-rich alloys were made directly in the crucibles under a protective gas cover. The starting elements were obtained from the American Smelting and Refining Co. and had a purity greater than 99.99 pct. Cooling curves were made with about 50 g of alloy in graphite crucibles which were placed in a covered quartz container in which a protective atmosphere of helium or nitrogen was maintained. The thermocouple protection tube was made of mul-lite and served as a stirring rod when connected to a reciprocating stirring motor. Temperatures were

Jan 1, 1962

By C. G. Dunn, W. W. Martin

Various X ray diffraction techniques have been developed for determining orientations of crystals. Transmission and back-reflection Laue methods1,2,3 in particular have been found to be very useful. In many applications, however, a need still exists for a simplification of the details of analysis so that orientations can be determined more rapidly, and operators with little or no training in crystallography can be easily instructed in the necessary procedures. Filling this need in part is a system of analysis that has been in use for several years in the Metals Section of the Laboratory, General Electric Co., Pittsfield, Mass. This method is an extension of the one of Majima and Togino,4 which uses fifty-five indexed standard transmission Lauemams to cover the entire range of crystal orientations. Greater rapidity in determining the orientation of a crystal is achieved by using a slightly larger set of standard Lauegrams and by systematizing the steps followed. This system of analysis in its present form constitutes the subject matter of the present paper. Although the method uses transmission X ray Laue patterns, many of the operations are applicable to the analysis of back-reflection Lauegrams. Very briefly the method is based on the fact that Bragg and azimuthal angles for two or more identified Laue diffraction spots completely determine the orientation of a crystal, and standard Laue photographs of the Majima and Togino type provide a ready means for identifying Laue spots. After a preliminary analysis, which consists of identifying the pattern in terms of one of the standard patterns, a correctly marked Lauegram is selected to carry out the final analysis. From measured Bragg and azimuthal angles, the normals (poles) of the reflecting planes for the selected Laue spots are located on a stereographic projection and the orient.at.ion of the crystal determined (in terms of the positions of cube poles for example) by a few additional operations on a \I1ulff net. The actual procedure followed will be illustrated in detail after a brief treatment or X ray problems connected with orientation determinations and a discussion of useful principles and techniques. X Ray and Plotting Problems RELATIVE ADVANTAGES OF BACK-REFLECTION AND TRANSMISSION LAUE DIFFRACTION METHODS In the back-reflection Laue method it is easy to make a direct measurement of the tilt of a zone of Laue spots. Specimen thickness also is generally no problem. In the case of thin specimens, however, the time of exposure is less for the transmission Laue method. For example, with silicon ferrite this advantage holds up to a thickness of 0.6 mm if tungsten radiation at 40 kv peak voltage is used. Furthermore, the transmission photograph represents the entire thickness of the crystal whereas the back-reflection picture represents only a surface layer (a thickness of less than 0.05 mm for silicon ferrite), the deeper layers supplying a negligible amount to the diffraction pattern. If a crystal is distorted, the transmission Laue pattern gives more information particularly with regard to the orientation of the crystal and the overall amount of spread in orientation. Finally a 3 1/4 X 4 in. film suffices for transmission photograms; a 4 X 5 in. or 5 X 7 in. film with a central hole is needed for back-reflection patterns Not only is the manipulation of film easier because of the size of film, but

Jan 1, 1950

By R. M. Hudson

The removal of nitrogen from a nitrogenized low-carbon sheet steel that contained 0.011 wt pct N was determined during heat treatment in Hz-N, mixtures. TIze process followed a first-order rate law; that is, plots of the logarithm of nitrogen content in steel were linear with the time of treatment at a given temperature. The rate of removal increased with an increase in temperature from 900" to 1300°F. By 1400°F the rate in dry hydrogen had decreased to a value intermediate between the rates at 1200" and at 1300°F; in wet (2.47 vol pct water vapor) hydrogen the rate at 1400°F was less than the rate at 1300°F and nearly the same as the rate at 1200OF. The rate at a given temperature increased as the 3/2 power of hydrogen concentration in the atmosphere. While wet atmosplzeres were generally more effective than the corresponding dry atmosplzeres, the effect of water vapor was much less pronounced than the influence of hydrogen content. NITROGEN is the principal agent in the strain aging of ferrite, the effect of carbon being secondary.' To eliminate the return of the yield point after straining and aging, it is claimed2 that the amount of nitrogen in solution in steel must be reduced to 0.0002 wt pct. Strong nitride-forming elements (titanium, vanadium, zirconium, and aluminum) can act to eliminate strain aging by combining with nitrogen. It is extremely difficult to decrease the nitrogen content in commercial steels to the low level required by conventional coil annealing because of the poor contact between the strip surface and the reactive atmosphere. However, a variety of gas-metal reactions can be effected by use of the open-coil annealing method,3 in which the metal surface is fully exposed to the atmosphere. With this possibility in mind, the Applied Research Laboratory has studied the influence of time, temperature, and atmosphere composition on the removal of nitrogen from low-carbon sheet steel. MATERIALS AND EXPERIMENTAL WORK Samples from a commercial nitrogenized low-carbon steel (0.010 in. thick) in the cold-reduced condition were used. The chemical composition of this steel is given in Table I. The gas mixtures used are listed in Table 11. The moisture content in the "wet" annealing atmospheres was controlled at a +70°F dew point (2.47 vol pct water vapor) by passing the gas mixture through a glass tube packed with a solid mixture of 10 pct anhydrous oxalic acid and 90 pct oxalic acid dihydrate held at 127°F; this technique has been described previously.4 For "dry" atmospheres, the gas mixtures were passed through a cold trap immersed in liquid nitrogen. A hinged-top Hevi-Duty electric furnace was used with a Vycor-glass furnace tube. When the furnace was at the desired temperature, the gas mixture was passed through the furnace at a flow rate between 1.1 and 1.2 cfh; coupons (size 3 by 3/4 in.) of the steel were pulled into the center of the Vycor-glass

Jan 1, 1964

By Allan T. Gwathmey, J. Bruce Wagner, Kenneth R. Lawless

Between 250°and 550°C in oxygen pressures of 10 to 760 mm Hg, the relative oxide thicknesses formed per unit time on the (100), (111), (110), and (320), decreased in this order. The predominant oxide orientation was (001)Fe3O4 and [110] Fe304 A small amount of a-Fe2O3 which exhibited a fiber pattern was observed in all oxides except those formed at 250°c in low oxygen pressures. IN order to understand the properties and behavior of thin films, particularly their role in oxidation reactions, there is needed more experimental information on their structure, composition, and kinetics of formation on clean surfaces of known geometry. The present study was undertaken to obtain such information for thin oxide films formed on single crystals of a body centered cubic metal, iron. Crystals in the form of spheres were used in order to expose all possible crystal planes to the reactant gases simultaneously. Using this procedure the relative rates of oxidation of all planes could be estimated, and those exhibiting, maximum or minimum oxidation rates could be selected for a more intensive study of composition and expitaxy. Since the three types of information were obtained from the same experiment using a single crystal substrate, any differences between rate, composition, and expitaxy on the several planes may be attributed to the influence of the substrate structure. EXPERIMENTAL The starting material for this study was Armco iron rods, 6 in. long and 3/8 or 1/2 in. in diam. The analysis was reported to be 99.8 pct Fe, with major impurities listed as carbon 0.018 pct, manganese 0.027 pct, phosphorous 0.005 pct, sulfur 0.029 pct, silicon 0.005 pct, and copper 0.11 pct. These rods were cleaned with ether and heated in an atmosphere of moist hydrogen at 950°C for three days. The purpose of this treatment was to decarburize the iron and to provide a consistent, uniform grain size for the growth of single crystals. Crystals in the form of rods, up to 1/2 in. in diam and 2 in. long, were prepared by a method similar to that reported by Leidheiser and Buck.2 Spherical crystals, 3/8 and 1/2 in. in diam and having a handle about 1/4 in. in diam by 112 in. long, were machined from the single-crystal rods. After machining, each crystal was etched in aqueous nitric acid to remove the cold-worked metal at the surface. Before each experiment, the crystal was polished mechanically with metallographic papers through number 4/0, and electropolished in a perchloric acid-acetic anhydride mixture by the method of Jacquet and Rocquet.3 The crystal was washed in running distilled water for at least 5 min. The excess water was blotted with a soft paper tissue, and the crystal was placed in an all-glass reaction vessel (See Fig. 1). The crystal was heated at 550°C in hydrogen for at least 8 hr prior to the oxidation in order to reduce any surface oxides and to help relieve any stresses in the metal. For the structure and composition studies, flat faces were cut parallel to (loo), (111), and (110) planes on the iron crystal spheres. The orientation of these faces was checked by a back-reflection X-ray diffraction technique. The faces were within 2 deg of the desired orientation. The flat faces were treated as described above except that prior to electropolishing they were given an additional polish on metallographic felt saturated with twenty-minute levigated alumina. After the crystal was heated in hydrogen for at least 8 hr, the temperature was adjusted to the desired value, and the hydrogen was evacuated. Commercial oxygen which had been purified by successively passing through tubes containing magnesium perchlorate, Ascarite and magnesium perchlorate was admitted to the desired pressure as measured by a mercury manometer. A resistance-wound furnace surrounded the oxidation chamber, and a temperature controller maintained the temperature within ±3°C. The furnace was provided with a small window for observing the crystal. The changes in thickness of the oxide films were followed by observing the interference colors. The oxidation was allowed to proceed until the desired oxide thickness was attained on a given crystal plane. The experiment was terminated by evacuating the oxidation

Jan 1, 1962

By R. E. Cech

Metallographic observations on hydrogen-reduced nickel oxide crystals suggest that nucleation of nickel occurs at structural singularities in the oxide. The fully reduced structure contains micron-diameter, worm-like voids occupying 40 to 50 pct of the volume. The crystallographic orientation relationships between nickel oxide and nickel resulting from oxide reduction are recorded and discussed. THE process of reduction of oxide to metal is one of considerable complexity involving a chemical reduction reaction, mass transport of reducing agent to the point of reaction and of reaction product away from it, and finally a transformation whereby metal atoms released from the oxide rearrange to form a stable reduced phase. In addition, nucleation of the reduced phase affects the overall reaction kinetics. Thus far only the thermodynamic aspect of reduction has received the attention warranted by the importance of

Jan 1, 1960

By J. L. Lytton

The flow-stress recovery of high-purity aluminurn following a 10 pct tensile prestrain was studied in terms of a fractional flow-stress recovery parameter fr. The flow-stress recovery behavior was related to the dislocation arrangements using transmissiort electron rnicvoscopy. During recovery at 120° and 160°C, nearly stable strength levels were attained, the strength level for 120°C recovery being greater than that for 160°C. This stabilization of flow stress was related to the formation of meta-stable dislocation networks bounding nearly perfect cells. Both network formation and the annealing of dislocation loops were found to be recovery mechanisms, and the stronger metastable strength level joy 120°C recovery was related to a smaller average cell size. Analysis of the networks was consistent with the reaction of sets of dislocations with a/2 (110) Burgers vector to give product Burgers DURING isothermal annealing of cold-worked metals, a degree of softening occurs without re-crystallization, and the processes responsible for this change are termed recovery processes. During recovery annealing, the dislocations generated during cold work become rearranged into low-energy configurations, and as much as 50 pct of the stored energy is released."' The relationship between this rearrangement of dislocations and mechanical behavior is of considerable importance, since the dislocation substructures formed during recovery provide a significant degree of low-temperature strength3j4 and can favorably alter the course of primary creep at high temperatures.4 The purpose of the present study was to relate the flow-stress recovery behavior of high-purity aluminum to the substructural modifications that occur. Electron transmission microscopy was therefore employed for direct observation of dislocation substructures at various stages of recovery following 10 pct prestrain. Several investigators5-' have proposed that dislocations can become rearranged or lost during the preparation of thin foils. It was found early in the present study that the dislocation structures in the thicker regions of the foils changed in a systematic way during the course of recovery. Therefore, it is unlikely that substantial losses or rearrangements occurred during thinning. This point will be discussed in more detail later. The results of various investigators indicate that recovery processes in fcc metals can result in release of 50 pct or more of the total energy stored in the as-prestrained metal, this percentage decreasing with increasing prestrain.' Alloying elements or impurities tend to increase this percentage. The release of stored energy of fcc metals during recovery appears to occur by 1) annealing of point defects if the deformation occurred at sufficiently low temperaturesg and 2) rearrangement of dislocations into low-energy Configurations.1,2In bcc metals, the annealing of dislocation loops has also been observed during recovery after prestrain,10-12 and it has been proposed that this is a recovery mechanism for unidirectionally strained fcc metals.' The density of dislocations in bcc metals has not been observed to decrease appreciably during recovery,10 although the formation of regular dislocation networks has been observed. has shown that the formation of such networks can result in elimination of long-range stresses and can lead to significant release of stored energy without dislocation annihilation. It might thus be expected that network formation is a significant recovery mechanism in fcc metals, although extensive network formation has apparently not been reported in controlled recovery experiments. The formation of sub-boundaries in aluminum has been observed by various investigators13'17 during recovery studies of aluminum, but the structure of these boundaries was not resolved. In this regard, it is significant to note that Bailey and Hirsch,' using transmission electron microscopy, detected no network or sub-boundary formation during recovery of 99.99 pct Ag. Furthermore, Clarebrough et al.2 found no such rearrangements during recovery of copper. EXPERIMENTAL PROCEDURE The high-purity aluminum used in this investigation was obtained in the form of 0.125-in.-thick sheet. Spectrographic analysis revealed that the sheet was 99.995 pct A1 with the following weight-percent impurities: 0.001 Cu, 0.002 Fe, 0.001 Si, and 0.0004 Mg. The as-received sheet was in the heavily cold-rolled condition. The as-received sheet was cold-rolled at room temperature to 0.040-in.-thick sheet in the longitudinal direction, which was the original rolling

Jan 1, 1965

By W. J. Babyak, F. N. Rhines

It has long been supposed that, regardless of the mechanism by which grain boundaries increase the hardness of a ductile metal, the effect should be linearly proportional to the grain boundary area. At the present time two methods for determining grain boundary area in an isotropic aggregate are available. The first, derived by Angus and Summers,' presumes that the grain boundary area is equal to 3vn, where n is the number of grains per sq mm in a random section through the metal. This estimate is based upon the assumption that the grains are equivalent to cubes whose faces correspond with the grains as observed in the micro-section. Measurements on copper, bronze, and a brass showed that a nearly linear relation exists between 3vn and hardness. This is illustrated, for the case of brass, in Fig. 1. The second method, developed independently by Smith and Guttman2 and by Duff in, Meussner, and Rhines,3 is absolute and employs a simple linear intercept count for measuring grain boundary area. It involves no assumptions with respect to the shape and distribution of the grain boundaries. The total surface in unit volume is 2 NL , where NL is the number of intercepts between grain boundary and unit length of a test line passed randomly through the sample. In practice, NL,, the average number of grain boundaries intercepted by unit length of traverse across a prepared microsection, is ob-

Jan 1, 1961

By M. Kaufman, A. E. Palty

THE mechanical properties of an alloy under given test conditions are in the main determined by the grain size and the phases present, their distribution and temperature-time dependence. Alloys intended for use at elevated temperatures, especially multiphase alloys depending upon precipitation reactions for strengthening, are particularly susceptible to changes in the phases present. Unfortunately, for modern superalloys, very little published information exists which relates the mechanical properties to the basic structural variables. The present work is an effort to do this for an alloy widely used in aircraft gas turbines and related applications, Udimet 500.* The mechanical properties inves- two heats is within the normal specifications for the alloy. However, the elements which most strongly influence the phase reactions, C, Ti, Al, and Mo, are comparable in the two heats. There was no intentional addition of boron, but normal pickup is about 0.002 pct. The vacuum-melted material was received in the form of centerless ground wrought bar stock % in. diam. PHASE STUDIES A) Methods—Two methods were used to determine the phases present: X-ray diffraction measurements on electrolytically digested residues, and microscopic examination. No single commonly used electrolyte will reveal all the phases that may be present; therefore, two complementary acids were selected: HCl and H3PO4. The necessity for this will be shown below in the results. The acid concentrations used were 10 pct HC1 in alcohol and 10 pct H3 PO4 in water. The current density was maintained below 0.1 amp per sq in. Residues were rinsed and separated by centrifuga-tion. X-ray diffraction patterns were obtained in a 114 mm Debye-Scherrer type camera using cobalt radiation. A temperature of 2250°F was selected to obtain as complete solutioning of phases as possible without encountering incipient melting. Specimens were

Jan 1, 1961

By O. N. Carlson, S. A. Bradford

Discontinuous yielding in tensile tests was observed in V-O alloys in the temperature ranges of 150° to 175°C and also 350° to 400°C. The magnitude and intensity of the serrations were found to vary considerably with oxygen content. Maxima were observed in tensile and yield strengths and in the strain-hardening coefficient at the higher temperature only. The strain rate sensitivity was observed to be negative between 150° and 400°C. THIS investigation was undertaken to study the effect of oxygen on the tensile properties of iodide vanadium in the temperature range of 25o to 450°C. Brown1 observed an increase in strength between room temperature and 400°C in vanadium metal, and found that oxygen and nitrogen had a rather pronounced effect on the strength and ductility. A maximum in the tensile strength was observed by Rostoker et al.2 near 300oC and by Pugh3 around 450°C for calcium-reduced vanadium. Pugh also found a maximum in the yield strength and in the strain-hardening exponent, and minima in the elongation and strain rate sensitivity at the same temperature. Eustice and Carlson4 reported the appearance of serrations in the stress-strain curves between 140° and 180°C in iodide vanadium containing 600 ppm O. These anomalies in the mechanical properties indicate that strain aging occurs in vanadium, but the impurity or impurities responsible for the above-mentioned effects have not been identified. The phenomenon of strain aging is usually characterized by the return of the yield point after interruption of a strength test. In the temperature range where strain aging occurs, the yield and tensile strengths attain maximum values, elongation and strain rate sensitivity exhibit minima, and discontinuous yielding is generally observed in the stress-strain curve. Cottrell5, 6 has postulated that strain aging is due to the migration of solute atoms to dislocation sites to produce locking after the dislocations have broken free from their impurity atmospheres during the initial yielding. At the strain-aging temperature the process is a dynamic one in which the solute impurity atoms diffuse to the vicinity of the moving disloca- tion producing "locking" which gives rise to maxima in the tensile strength and serrations in the elongation curves. Cottrel17 has noted that discontinuous yielding in iron occurs when the diffusion coefficient of nitrogen, D, and the strain rate, i, are related by D = 10-9 €. EXPERTMENTAL PROCEDURE The vanadium metal employed in this study was prepared by the iodide refining process as described by Carlson and owen.8 A representative analysis of the vanadium used in this investigation was: 150 ppm O, <5 ppm N, <1 ppm H, 150 ppm C, 150 ppm Fe, 70 ppm Cr, <50 ppm Si, 30ppm Cu, 20 ppm Ni, <20 ppm Ca, <20 ppm Mg and <20 ppm Ti. Alloys containing from 200 to 1800 ppm O, all of which lie in the solid solution range of the V-O system, were prepared by arc melting vanadium together with portions of a high-oxygen master alloy. The master alloy was prepared by tamping pure V2O5 into holes drilled in a vanadium ingot and arc melting this five or six times in an inert gas atmosphere, inverting the button between each melting step. The oxygen content of the master alloy was then determined by vacuum fusion analysis. Vanadium containing less than 150 ppm O was prepared in the following manner. A bar of iodide vanadium was deoxidized by sealing it in a tantalum crucible with a few grams of high-purity calcium. This was held at 1100°C for 4 days to allow time for the oxygen to diffuse to the surface and to react with the calcium vapors. The calcium oxide product was later dissolved from the surface of the bar with dilute acetic acid. In this way vanadium containing from 20 to 50 ppm O was prepared. Sample Preparation. The are-melted ingots were cold swaged into 3/16-in. diam rods and these were machined into cylindrical tensile specimens with a reduced section of 1.00-in. length and 0.120-in. diam. The test specimens were annealed for 4 hr at 900°C in a dynamic vacuum of mm of Hg to remove hydrogen from the metal. This recrystal-lization treatment produced a uniformly fine-grained structure with a mean grain size of approximately 0.06-mm diam. The oxygen contents reported in this paper were determined by a vacuum fusion analysis of the tensile specimens after testing. Analyses for other interstitial or metallic impurities showed no significant changes from that of the original material. Tension Tests. Tension tests were performed on a screw-driven tensile machine at a constant cross-head speed of 0.01 in. per min. Tests at elevated temperatures were carried out by heating the

Jan 1, 1962

By A. H. Daane, B. J. Beaudry

The Sc-Y and Sc-Zr systems were studied by thermal and X-ray methods. Both systems are characterized by complete solid solubility in the low temperature hexagonal form and in the high temperature bcc form. In the Sc-Y system, there is a minimum in the solidus at 50 at. pct and 1365°C, while the solidus in the Sc-Zr system follows a nearly straight line relationship between the melting point of scandium and zirconium. There is a minimum in the temperature of transition from hexagonal to bcc in the Sc-Y system at 43 at. pct Y and 1175°C; while the temperature of transition is raised in the Sc-Zr system to a maximum of 1415 °C at 30 at. pct Zr. INTEREST in the metals of the first transition series has usually stemmed from their useful properties; however, there is now a great deal of interest in determining the fundamental nature of these metals. Since scandium is the first of these transition metals, a study of the preparation and Properties1 and the alloying behavior of scandium2 was initiated. In a continuing study of the alloying behavior of scandium, the systems of scandium with zirconium and yttrium have been established. Extensive solid solubility in both the Sc-Zr and Sc-Y systems was expected from application of the classical rules of Hume-Rothery. Also, the modified Darken and Gurry plot as suggested by Gschneid-ner3 showed ideal conditions for solubility in the Sc-Zr system with less favorable conditions in the Sc-Y system. The effect of scandium on the transformation temperature of zirconium and yttrium was of interest, since a recent empirical observation by Uly and Burr4 predicted that the solute scandium would raise the transformation temperature of zirconium and lower the yttrium transformation. In addition to noting the validity of the above predictions, the SC-Y and Sc-Zr systems were established. EXPERIMENTAL METHODS Materials. The metals employed in this investigation were crystal bar zirconium, distilled scandium prepared by the method described by Spedding, et al.1 and yttrium prepared by the method described by Carlson, et a1.5 The major impurities present in these metals are listed in Table I in ppm. Alloy Preparation. All the alloys examined were initially formed by comelting the two metals in a nonconsumable electrode arc-melting furnace under an atmosphere of purified helium or argon. The buttons were inverted at least five times and re-melted each time to ensure homogeneity. During preparation of Sc-Zr alloys, approximately 1 wt pct was lost which was attributed entirely to the loss of scandium by distillation. When preparing Sc-Y alloys, approximately 1.5 wt pct was lost, but it was assumed that the intended composition was maintained, since the relative weight lost when arc melting the component metals was nearly the same. Samples weighing 15 to 20 g were prepared for time-temperature thermal analysis, while only 1- to 2-g samples were prepared for the optical pyrometer and X-ray diffraction studies. Thermal Methods. The solidus and the melting points of the metals were determined by an optical pyrometer method described previously.2 The temperatures at which the transformation from hexagonal to bcc occurs were determined by differential thermal analysis. Several points on the solidus and liquidus in the Sc-Y system were also determined by this method and are in good agreement with those obtained by the optical pyrometer method. The procedure followed in the preparation of samples for thermal analysis and the furnace used have been described elsewhere.2&apos;6 Since a limited quantity of scandium was available, most of the alloys were not melted during thermal analysis, thus avoiding contamination by the crucible. The alloy could then be reused and the composition changed by adding the desired quantity of solute to obtain the next alloy. Heat Treatment and X-Ray Methods. In order to ensure homogeneity, the "as arc-melted" alloys Were wrapped in tantalum foil, sealed in quartz capsules and heated at 1100°C for 15 hr and then cooled at a rate of 8 deg per min. Samples for X-ray diffraction were filed from these heat-treated alloys, sealed in 1/8 in. by 1/2 in. tantalum capsules under

Jan 1, 1963

By R. P. Abendroth

This study is concerned with the kinetics of selective oxidation of chromium in a commercial Fe-Cr-Ni alloy. Selective oxidation of chromium in this alloy, by use of a low oxygen-potential atmosphere, leads to the formation of a compact, protective layer of Cr2O3. This layer serves to protect this alloy from gross scaling when it is subsequently exposed to severe oxidizing conditions at high temperature. The interaction of low oxygen-potential atmospheres close to equilibrium with Fe-Cr and Ni-Cr alloys has been studied by others."&apos; These studies werk concerned with the surface-structure variations under slightly oxidizing conditions. NO detailed study was made of the oxide scale formation kinetics, however. The alloy samples were cut from 0.012-in.-thick sheet, with an apparent surface area of 7.1 sq cm. These sheet samples were abraded through 4/0 metallographic paper, and washed in alcohol and acetone. The analysis of the sheet alloy is (in weight percent): 42 pct Ni, 5.5 pct Cr, 0.09 pct C, 0.18 pct Al, 0.36 pct Si, 0.26 pct Mn, balance Fe. The weight gain vs time data were obtained with a 2-g capacity fused-silica spring—cathetometer system. The spring deflection was optically magnified ten times before being read by the cathetometer. A sensitivity of about 0.01 mg was attainable. The spring was enclosed in a water jacket maintained at 60°C to minimize the effect of temperature changes. The sample was suspended from the spring with a fused-silica hangdown and was positioned in the thermal center of a mullite furnace tube. Sample temperature was read with the aid of a thermocouple placed outside the mullite tube and an inside vs outside temperature calibration. Temperature change during the course of a run was ±0.25°C, with a temperature gradient of less than l.O°C over the length of the sample. Total temperature uncertainty was no more than ±3.0°C. Alignment difficulties between the hangdown and radiation shields in the furnace tube required that the sample be positioned in the furnace when cold, and heated with the furnace until the temperature stabilized at the desired point. This required 5 to 6 hr, and was carried out in Matheson ultrahigh-purity hydrogen. Oxidation was started, after evacuation, by introducing a hydrogen-water vapor mixture, obtained by saturating hydrogen with water vapor at 31.00o ± 0.02oC. Oxidation was continued for 90 min. Gas flow was 300 ml per min during heat up and oxidation. Since only several milligrams of oxide are formed on each sample, chemical analysis of the oxide is difficult. A representative analysis is: 80 pct Cr2O3, 5 pct Fe2O3, 3 pct Al2O3, 4 pct MnO, 7 pct SiO2, 1 pct or less NiO. X-ray diffraction analysis of the oxide as formed on the alloy gives rhombohedra1 Cr2O3, and barely distinguishable amounts of a cubic spinel phase, and possibly AlZOs and SO2. The identification of these latter two compounds is by no means certain. The spinel phase could be based on iron or manganese as these elements are present in significant amounts in the oxide. The results of the kinetic studies using 31°C dew-point hydrogen-water vapor mixtures were found to conform to a parabolic rate law. In many cases the parabolic plot consisted of two intersecting straight lines, defining an early and a late rate for a particular run, and in the other cases the parabolic plot consisted of one straight line for the entire run. The slopes of the various straight lines were determined by the method of least squares. Reproducibility of the data was good enough for multiple runs at the same temperature such that the value given for the rate constant is the average for two or more closely similar values, rather than widely varying values of the rate, where more than one determination is indicated in Table I. The exhibition of only one or of two rate constants during a run can happen at the same temperature. Thus, Table I shows that at 11&apos;74°C a single rate constant was obtained from one sample, while other samples oxidized at the same temperature gave an early and a late rate constant. It should be noted that the single rate constant corresponds very closely with the early rate constant. This is also true at 1153°C. The time at which the late rate started to appear was variable, usually occurring 20 to 40 min after oxidation had started.

Jan 1, 1964

By K. M. Busen, J. Lindmayer

A heterojunction model is suggested for descrihzng the electronic conditions at oxide -semiconductor interfaces. Detailed study of the silicon oxide-silicon interface shows that the heterojunction model explains many experimental facts; however, it is necessary to assume that a transition layer exists at the interface. It will he demonstrated that ionic contrbution way also he present. Extended low-temperature heating stabilizes the oxide to a charge carrier density in the order of 10&apos; cln-: determined by the heterojuncton model. OXIDIZED semiconductor surfaces are widely used, since they offer technological advantages and "passivate" the surfaces of semiconductor devices. However, it has been recognized that there are always n-type inversion layers formed in the silicon oxide-silicon system, which must be regarded as a definite disadvantage. An added complication is the "instability" of these inversion layers;&apos; the inversion layer appears to vary with the processing and they change at temperatures as low as 100" to 200°C This paper will point out that the inversion layer is a result of the dissimilarity of the contacting materials and therefore must always be present. The dissimilarity is the essence of the heterojunction or electronic model and involves directly the structure of the materials involved. In addition, one finds the contribution from ions; this disturbance, however. can be eliminated for the case of silicon oxide-silicon interface. The strength of the inversion layer or channel will be expressed in terms of the density of elementary charges per square centimeter, N*, maintaining the channel. The next section contains the formulation of the heterojunction model by assuming a contact between two homogeneous materials. This calculation should not imply that silicon oxide is homogeneous; it serves only to point out the general properties of the electronic model. Following the electronic model, the practical case of the silicon oxide-silicon interface will be discussed. I) THE HETEROJUNCTION MODEL Contacting an oxide with a semiconductor, a work-function difference must be accommodated. Fig. 1 represents the oxide and the semiconductor before and after contact. When the contact has been made, one finds that qVi + qV, = A@; i.e., the work-function difference is distributed between the oxide and the semiconductor. Normally, the work-function difference appears on the wide-bandgap material, but in the present case the oxide is thin and far from being a single crystal. Accordingly, a significant fraction of the work-function difference must appear on the semiconductor. The work function of silicon2 is about 4.8 ev, but we shall not assign any particular work function for the oxide as it may vary. However, oxides usually have lower work functions and therefore the potentials must build up in the manner shown in Fig. 1. Such an argument predicts that the inversion layer must be n type, as opposed to the clean surface which is p type. Another important factor to be considered is that the oxide is disorderly and therefore contains many trapping levels. As a result, the charges in the oxide arise primarily from the change in trap occupation, while on the semiconductor side the space charge is composed of mobile free electrons. The consequence of this fact is that a change to another thermal equilibrium will require some time, dictated by the traps in the oxide. The conditions can easily be calculated on the semiconductor side. Assuming an intrinsic semiconductor, Poisson&apos;s equation is

Jan 1, 1965

By J. B. Clark

In 1933, R. paris1 published a phase diagram for the entire Mg-Ca-Zn system. He reported the existence of a ternary intermetallic phase, Mg5Zn5Ca2, which formed a quasi-binary with the magnesium solid solution. Since then, no extensive work has been reported on the system. Recently however, indications of the existence of a second ternary in-termetallic phase in equilibrium with the magnesium solid solution led to a reinvestigation of the solid phase equilibria involving the magnesium solid solution. The 335°C (635°F) isothermal section was chosen for study. Metallography and powder X-ray diffraction were selected as the best mutually corroborating methods for determining the solid phase constitution. Seventy-six alloys were prepared from singly sublimed (99.95 pct) magnesium, electrolytic (99.95 pct) zinc and USP calcium. The analyses of some of the alloys are shown in Fig. 1. The alloys were melted in a graphite crucible under a chloride flu and chill cast in a split graphite mold. Dif-fusion couples (see Fig. 2) were prepared by casting molten Mg-20 wt pct Zn alloy around a cylinder of Mg-30 wt pct Ca alloy. The alloy samples and the diffusion couples were sealed under argon in Pyrex vials and annealed in a furnace capable of controlling within 1/2°C of 335°C. At the conclusion of the anneal, the alloy samples were quenched in ice water and the diffusion couples were air cooled. Procedures standard for magnesium alloys were used for metallographic examination. Powder X-ray diffraction patterns were taken on a G. E. camera with a 14.32 cm dim using nickel-filtered copper radiation. The redetermined 335°C (635°) section of the Mg-Ca-Zn phase diagram is shown in Fig. 1. TWO ternary intermetallic phases, designated w and

Jan 1, 1962

By R. E. Ogilvie, A. R. Kaufmann, S. H. Gelles

The solid-solubility limits of iron in beryllium were determined between 850o and 1200oC by analysis of differential type multiphase diffusion couples, using an X-ray absorption technique. The maximum value of the solubility limit was found to be 0.92 ± 0.02 at. pct (5.46 wt pet) at the eutectic temperature 1225°C. The solubilities of nickel and beryllium were determined between 900°and 1200°C by the same technique and the maximum solubility was found to be 4.93 + 0.01 at. pct (25.2 wt pet) at the eutectoid temperature, 1065°C. A previously unreported high-temperature phase which decomposes eutectoidally at 1065 °C was found to exist in the beryllium-nickel system at a composition of approximately 8 at. pct Ni (36 wt pet) by diffision-couple analysis. The presence of this phase was confirmed by thermal analysis and metallo-graphic analysis of the structure resulting from the eutectoid decomposition. G. V. Raynor1 has treated the solid solubilities of some of the elements in beryllium on the basis of the "Hume-Rothery" rules2 which have been modified to include ionic size and ionic distortion effects. It was predicted that the solubility of iron and nickel in beryllium should be slightly less than that of copper. The lowering of the solubility, according to Raynor, is due to a more unfavorable relative valency effect and an ionic size effect. Kaufmann and corzine3 have compiled data on the solubilities of elements in beryllium and have discussed them in the light of the Raynor paper. These authors feel that, because the elements having the greatest solubility in beryllium systematically fall in the Group VIII and IB Columns of the periodic table, the electronic structure greatly influences the maximum solid solubility of elements in beryllium. The solubility of iron in beryllium was determined by Teitel and cohen4 as part of the study of the beryllium-iron phase diagram. The determination was carried out by X-ray and thermal analysis and according to the phase diagram presented, the maximum solubility of iron in beryllium is 0.41 at. pct (2.5 wt pct) at 1225oC. However, it is estimated that the uncertainty in the position of the a-beryllium primary solid-solution boundary is about 0.5 at. pct (3wtpct). Losana and Goria3 in studying the beryllium-nickel phase diagram, determined the solid solubility of nickel in beryllium by thermal analysis. They found the maximum solubility to be between 1.65 and 2.65 at. pct (10 to 15 wt pct) at 1240°C. This value decreased rapidly with decreasing temperature. In determining approximate ranges of solubilities for different elements in beryllium, Kaufmann, et al,8 reported a value of between 1.3 and 1.7 at. pct (7.9 to 10.1 wt pct) for the solubility of nickel in beryllium. The value was obtained by metallographic examination of quenched alloys and lattice-parameter measurements. However, the authors also noted a single-phase structure for a 1.7 at. pct Ni alloy (10 wt pct) on cooling from the liquid. This would indicate a higher solubility range than was reported. ~isch,&apos; in his X-ray studies of beryllium-copper, beryllium-nickel, and beryllium-iron intermetallic compounds, reports the disappearance of a second phase (Ni,Be2) in the beryllium primary solid solution at approximately 4 at. pct (20 wt pct). THEORY The analysis of concentration gradients in diffusion couples has proven to be a useful tool in determining phase equilibria.8-14 In this particular study the diffusion couples were chosen to straddle the expected composition range of the phase boundary, then heat treated at a given temperature and the concentration gradient evaluated. The composition of the phase boundary for a given temperature appears at a point of discontinuity of the composition gradient. Examples of typical phase diagrams and the concentration gradients which should be found in such systems are shown in Fig. 1. In the present work, gradients of the form of Fig. l(c) were obtained in diffusion couples made of pure beryllium and two-phase alloys of beryllium with either iron or nickel. The composition at the point where the gradient becomes discontinuous, Cs, corresponds to the solubility limit of either iron or nickel in beryllium. The analysis of the concentration gradients was carried out by an X-ra absorption method developed and applied by Ogilvie and later used by Moll13 and Hilliard.l4 It depends on the fact that the absorption of X-rays by matter is determined by the concentration and type of the various atomic species present. The relationship for the intensity, I, of a monochro-

Jan 1, 1960

By A. H. Daane, W. J. Wunderlin, B. J. Beaudry

The solid solubility of holmium in copper, silver, and gold, determined using metallographic techniques, was found to be a maximum of 0.06, 2.4, and 3.2 wt pct, respectively, nt the eutectic temperatures. The temperatures of these eutectic horizontals, determined by differential thermal analysis, were found to be 868", 787", and 778"C, respectively. The first compound on the silver-rich side of the Ag-Ho system was found to be A&Ho2. In a study by Gold et al.,&apos; on the effect of small amounts of soluble impurities on the electrical resistance and thermoelectrical properties of copper, traces of iron were shown to have drastic effects on the thermoelectric power due to the magnetic scattering of the conduction electrons. Since little is known about the state of the iron ion when dissolved in copper, Gold had hoped to repeat these experiments using certain rare earths as the magnetic scattering centers; because of the tightly bound 4f electrons it is not expected that their spectroscopic state would be affected by alloying. In such an experiment the sole role of the trace rare-earth impurity would be to magnetically scatter the copper conduction electrons without producing appreciable distortions in the otherwise pure copper matrix. Since holmium was chosen for such a study because of its high magnetic moment, it was necessary to establish precisely its solid solubility in copper. The study was extended to include the solvents silver and gold, so that an evaluation of the data using classical solubility parameters could be made. No previously reported work on the systems of holmium with copper, silver, or gold was found in the literature. Information on the solubility of other rare earths in these three metals is also very meager. The solubility limit of yttrium in copper was reported as less than 1 wt pct2 and the solubility of praseodymium in gold as 0.35 wt pct,3 while no references were found on solubility studies of rare earths in silver. EXPERIMENTAL Materials. The materials used in this investigation were distilled holmium prepared in this Laboratory, OFHC* copper, electrorefined silver (99.9 *OFHC = oxygen-free high conductivity. pct), and gold with the analyses given in Table I. Sample Preparation. Samples weighing 1 to 2 g were prepared by arc-melting the components together on a water-cooled copper plate under purified argon atmosphere. The samples, turned and remelted at least five times to ensure homogeneity, showed weight changes of less than 0.1 wt pct after melting. Samples containing less than 0.7 wt pct Ho were prepared by diluting 1 to 2 wt pct Ho alloys with the pure solvent, while samples with concentrations greater than 0.7 wt pct Ho were prepared directly from the metals. The samples were wrapped in tantalum foil, sealed in outgassed Vycor tubing under helium, annealed at the desired temperature for at least 24 hr, and then quenched by shattering the Vycor tube in cold water. Metallographic Methods. Standard mechanical polishing methods were used in preparing the silver and gold alloys for examination, while the copper alloys were electropolished using a 40 pct solution

Jan 1, 1963