By S. R. Zimmerley, John Gross

The deductions drawn in crushing and grinding operations have heretofore been based on a separation of the products into various sizes. A crushed product may be sized by sieving, by elutriation and by aid of the microscope. To estimate the surface of each size the relation of the surface to the estimated average diameter must be assumed. Such a relation, owing to the irregularity of the particles, may involve two assumptions: First, a factor to convert average diameter to surface for one particular size; and second, a variation in the factor as the diameter of the particle changes. Obviously a surface measurement in which such assumptions and estimates are involved is questionable. In the first paper of this series1 a method has been given by which an accurate measure of surface of quartz can be obtained from its dissolution rate. By the use of this method, surface measurements have been made on a series of sieve sizes of crushed quartz, the results of which are given and discussed in this paper. Prepaeation of the Quartz Sizes The quartz, consisting of large uniform pieces with a density of 2.65 and a purity of 99.5 per cent. SiO2, was crushed to pass 20 mesh and was then sieved. Tyler standard sieves were used, the sieving being done by hand according to the proposed standard method submitted by the senior author to the Milling Committee of the A. I. M. E. A wet split of the sample was made on a 270-mesh sieve. This was followed by dry sieving until less than 0.05 per cent. of the weight of the sample passed through the sieve in 1-min. sieving. The +28-mesh material was discarded because that size did not contain the difficult grains from the 20-mesh sieve.

Jan 1, 1930

By A. D. Marriott, J. V. N. Dorr

This paper reviews recent developments in the application of classification practice to the origination of fine-grinding flow sheets and traces the history of the mechanical classifier from its initial application for separating cyanide process sands and slimes down to its present six or more distinctly different applications at copper concentrators; it undertakes to show also, by reference to diagrammatic fine-grinding flow sheets and accompanying operating data from nine copper concentrators in western North America, the advantages gained from improved classi-ficiation flow sheets at these properties in terms of reduced grinding costs, improved flexibility of operation or increased recovery. Comparison is only made between different fine-grinding flow sheets at a given plant and no attempt is made to compare different concentrators, on account of ore variations and differences in metallurgical objectives sought,. The adoption of the flotation process in recent years, and especially the development of selective flotation, has brought a demand for much finer grinding than formerly. This has caused much thought to be given to grinding efficiency, and today there is hardly a mill where the grinding flow sheet is not under close study and subject to frequent changes. When closed-circuit grinding was introduced into metallurgy some years ago, its value was recognized at once, and since then the combination of mills and classifiers has been regarded and operated as a grinding unit. Apart from variations in both the grinding and classifying elements of this unit, there have been many variations in grouping tried by different mills to suit varying conditions of ore and plant limitations. Although operators feel that in most cases their present flow sheets are on trial, and the data on present work are often incomplete, we have felt that a discussion of the progress that has been made and an endeavor to show present trends and their results should be of use to the profession. We have therefore prepared flow sheets of some of the larger mills with which we have been in contact and present them with available data as to their results, in the hope that they may be of service now rather than later when practice may have become more standardized and more complete records and analyses have been made. We believe that the data given,

Jan 1, 1930

By P. B. Bucky

In previous publications1 it was shown that a scalar model of any weighty structure, where the stresses produced are mainly due to gravitational forces, will behave similarly to its prototype if the model and prototype material are the same and the model is placed in a centrifugal field of force (substituted for the gravitational field) which has been increased in the same proportion as the linear model scale is decreased. This principle is now being applied to a study of the behavior of mine structures in an attempt to determine the laws that control them. The importance of using models as a means of solving mining problems has been discussed previously, yet it may be well to reiterate here that this method of research and type of solution have been productive of far-reaching results in other engineering fields, notably those of hydraulics and aerodynamics. Model research is a comparatively cheap and time-saving method of checking practical experience. Up to the present time the best guide to what will happen underground has been the judgment of the man who has observed most and been longest acquainted with the local conditions. His experimental work underground is limited by the elements of cost, time and danger, while failure is seldom permissible. In a model, as in a test tube, all elements that affect the solution of a problem are under definite control. Each element may be varied independently at hill and its effects noted. Experimental work on a small-scale model may therefore be performed at a comparatively small expenditure of time and money, instead of on a full scale in the mine, where the cost, time, and danger elements are necessarily great. The experiments described in this paper are to be considered as part of a progress report and a continuation of Technical Paper 425. One object of the research program is to make each experiment point the way for further research on that particular phase of the general problem. The results and conclusions presented here are therefore not to be considered as final, but arc to be interpreted as

Jan 1, 1934

By H. J. Donnell, B. C. Parks, O&apos

In 1930 the late Dr. Reinhardt Thiessen set up a method of microscopic analysis and type classification of coal that has since been followed as standard practice in the coal-petrography laboratory of the Bureau of Mines. Thiessen's terminology which designated the constituent parts of coal in terms of botanical origin was introduced in 1920.1 The technique, however, of preparing a completely representative series of thin sections from a column sample of coal for use in making quantitative determinations of coal components with a microscope was developed about 10 years later by Thiessen and coworkers G. C. Sprunk and H. J. O'Donnell.2 Complete thin-section analyses subsequently have been made of 126 column samples of various ranks and types of American coals. The data and information were assembled from these thin-section studies and published in a large number of reports dealing chiefly with investigations of the coking and hydrogena-tion properties of certain American coals. In the years following adoption of Thies-sen's method, a considerable amount of work was done in collecting column samples of many coals, making routine thin-section analyses of these, interpreting the results, and finding practical application for the information in other fields of coal research. The many reports and papers covering the work in coal petrography, however, offer very little discussion that can be considered as critical appraisal of the technique. Criticism outside the Bureau most often has voiced questioning opinions concerning the accuracy of the method used of measuring coal components microscopically and classifying the coal into arbitrary types on the basis of the quantitative determinations. The principal purpose of this paper is to discuss in some detail and present data showing the results of certain investigative work done in the petrography laboratory on the accuracy of the Bureau's method of microscopic measurement of components in coal thin sections. Data from microscopic analyses on file made by G. C. Sprunk and H. J. O'Donnell were freely used in the investigation, and a table of columnar analyses from an unpublished manuscript by Sprunk is included in this paper for reference. In the course of the experimental work a method was developed for measuring in-strumentally with a planimeter the components shown in micrographs of selected thin sections. Measuring coal components with a planimeter furnished useful information for studying the accuracy of microscopically measuring the same components in thin sections. Petrographic Components and Type Classification of Coal Thiessen considered coal to be composed of two visibly different major components present in various types of coal in greatly varying proportions. He named

Jan 1, 1949

By H. C. Howard

Reaction of oxygen and bituminous coal starts as soon as the coal bed is exposed to air and, with some coals, proceeds with significant velocity even at normal temperatures and at normal oxygen partial pressures of one-fifth of an atmosphere. At higher temperatures, the reaction is greatly accelerated and ultimately a condition is reached where the process is very rapid and we then speak of combustion. It is the purpose of the present paper to discuss the reactions of oxygen and coal at temperatures below those of active combustion. It is these low temperature oxidation reactions which are responsible for heating in storage and for marked changes in agglutinating proper-ties. These reactions may also be employed for the preparation of organic acids, which are of direct interest to the chemical industry. For convenience in discussion, the low temperature reactions of oxygen and bituminous coal can be roughly divided into three stages though there is, of course, overlapping. Stage I is a surface oxidation stage, characterized by the addition of oxygen, with the formation of oxygen containing groups some of which have acidic properties. Carbon dioxide, carbon monoxide and water may be formed con-comitantly and are always liberated at higher temperatures, and in cases where the oxidation is prolonged. Superficially, the coal is little affected by this primary stage of oxidation and usually only minor changes in ultimate composition result. There may be definite changes in coking and coking properties, and heat of combustion susceptibility to further oxidation. The presence of acidic groups can be demonstrated by specific reactions. These groups may show cation exchange properties like the mineral zeolites. The formation of oxalic acid has been reported. If the oxidation is continued, a large fraction of the organic material of the coal is converted ultimately into alkali soluble, acid insoluble products, which have been given the name "regenerated humic acids" and which are the characteristic products of Stage 2. These humic acids, in the solid stage, do not differ greatly in appearance from the original coal, but show large differences in chemical composition and chemical and physical properties. Along with the humic acids, carbon dioxide and some of the water soluble types of Stage 3, are also formed. If the oxidation is carried still further, the humic acids may be degraded completely to the simpler, lower molecular weight acids of Stage 3 which are characterized by solubility in acid as well as in alkaline media, and by their orange, yellow or white colors. Additional carbon dioxide is formed in the transformation from Stage 2 to Stage 3 and, for a number of American coals, a maximum yield of the water soluble types of acids is reached when about 50 pct of the carbon of the coal is converted to carbon dioxide. Primary Oxidation The initial step in the reaction of gaseous oxygen on coal, like that on carbon,

Jan 1, 1949

By Reynold Q. Shotts

The small domestic underfeed stoker as now designed is unusually sensitive to the coking and plastic properties of coals, and when the attempt is made to burn the high rank coking and caking coals of the Appalachian fields, serious trouble may occur. Part of the trouble may be caused by the ash content and clinkering characteristics of the particular coal in use, but more often it is the result of an excessive ac-in of coke in the form of ''trees,, or masses in the fuel bed. Often the zone of burning becomes so restricted that the fire goes out, and in extreme cases the fire may be lifted completely out of the fuel bed and away from the air ports. Even if the fire is preserved, excessive coking may cause response to subsequent heat demand to be slow and irregular. Coke trees seem to grow most readily during periods of hold-fire operation, so that in order to preserve the fire in mild weather it is often necessary to set the timer for such a long operating period each hour that much unneeded and unwanted heat is developed, causing discomfort. During demand periods the fire may pick up so slowly that the intense burning which develops just before stoker cut-off causes a serious overshooting of the thermostat. Stoker coal performance tests which have been made in a number of labora- tories1,2,3,4,5 are one method of approach to the problem Of selecting stoker coals- As yet these tests have not been standardized and they are expensive and time-consuming. The value of the results probably increases with the length of the test. Sherman and co-workers at Battelle Memorial Institute believe that even a one-week test is not too reliable a trial2 and it is quite likely that Others will agree. A great advantage of such tests is that characteristics of coals, other than the tendency to form coke masses, may be evaluated from them. The selection of stoker coals would be greatly facilitated if there existed some simp1e measure Of the tendency Of a a to form coke in a fuel bed. Although possessing all Of the disadvantages Of any small-scale laboratory test, the test for the free-swelling index of coal has been found useful for evaluating the probable effects Of swelling properties upon combustion.7 Ostborg, Limbacherand Sherman, have shown that the test can Predict, roughly, the tendency Of coke to accumulate in the fuel bed Of a domestic stoker. They also gave instances of its value in predicting combustion behavior in some large installations. The use of the test for free-swelling index has become well established and has been adopted as a standard by the American Society for Testing Materials.8 When domestic stoker coal investigations began at the State Mine Experiment Station in the summer of 1944, it was decided

Jan 1, 1949

By Frank H. Reed, P. W. Henline, Harold W. Jackman

A sumMary of the consumption of coal in 1945 shows that the coke industry ac-counted for 17 pct of the total coal used. No substitute for coke and the blast furnace in the reduction of iron ore has gained sufficient prominence so far to be given serious consideration. However, while the same slot-type ovens are being built and used now as were in use a few years ago, the problem of obtaining suitable coking coals, both high- and low-volatile, has forced many operators to revamp coal-blending facilities. Until the beginning of World War 11, high-temperature ooke plants were able to secure the required high-volatile and low-volatile coals from two or three seams and from three or four mines. Thus, many of our coke oven plants were able to operate with storage bins for two coals only. The vari-pnce in raw materials was not great, and uniformity of blend was a relatively simple problem. Since the beginning of World War 11, many and important changes have taken place. Demand for all coals increased greatly. Production, though kept as near maximum capacity as possible, could not meet the demands for coal generally, and particularly for the various kinds of coal which have proved to be satisfactory for specialized uses; coals were allocated as nearly as possible in the order of greatest need; storage piling was reduced to the minimum necessary to keep plants in operation; uniformity of quality could not be maintained, and with this last, uniformity of composition of blends for coking could not be maintained. Whereas before the war producers of metallurgical coke could fill their needs from three or four mines, by the end of the war it was not unusual to find shipments to a single coke oven plant coming from as many as 30 different mines, in a single month. Since many of the mines producing both high- and low-volatile coal for high-grade metallurgical coke are rapidly nearing de-pletion, the problem of seeking new sources and of blending a number of coals in each plant for the production of high-temperature coke is facing practically every producer in the United States at the present time, and is one which will probably continue for many years to come. Midwestern byproduct coke ovens in the Chicago and St. Louis areas use annually from 12 to 15 million tons of bituminous coals which are transported 500 to 700 miles from the Appalachian coal fields of Pennsylvania, West Virginia, and eastern Kentucky. Approximately two-thirds of this coal is high-volatile bituminous. The critical transportation problem confronting the nation in 1943, and the growing scarcity of the best Appalachian coking coals, prompted the Illinois Geological Survey to propose a research program in which would be studied the coking properties of blends of low-sulphur, high-volatile Illinois coal with the high- and low-volatile coals from the eastern fields. Such blends containing Illinois coal, if substituted for the all-eastern blends normally coked,

Jan 1, 1949

By Samuel L. Hoyt

Cemented tungsten carbide, a product of a branch of metallurgy which has never possessed more than a relatively minor interest and importance, has recently commanded the attention of engineers, industrialists, financiers and men of business. New methods, new opportunities, new goals, never before considered, have suddenly been brought within the scope of practical realization. It is these results that attract the interest of the world, but we, as engineers and metallurgists, will have equal interest in the product itself and in that branch of metallurgy from which it comes. It seems appropriate, therefore, to speak today on Hard Metal Carbides and Cemented Tungsten Carbide, as the latter represents one of the outstanding developments of recent date in non-ferrous metallurgy. We are interested in the hard metal carbides as a group of related metallic substances and in cemented tungsten carbide as the leading representative of the metallurgy of this group. The literature of this general field is limited, and, bearing this in mind, it seems advisable to attempt to cover the field broadly and to correlate the subject matter, rather than to present a detailed account of any one of its phases. Our annual lecture lends itself admirably to this plan. The quickened interest in cemented tungsten carbide, once its potentialities were recognized, the many sides to the problem of developing the manufacture and use of this new product, and the desire to economize as much as possible in the time of development, have brought many into this work, both in this country and abroad, notably the Osram Lamp Co. and Friedrich Krupp in Germany and the General Electric Co. in this country. It would be presuming too much to attempt to speak too broadly of the present state of the art and science of the hard metal carbides and my remarks arc guided largely by the work done in the General Electric Co., and by our associates in the Carboloy Co. Even here the activities of many in these two groups have centered around the utilization of cemented tungsten carbide, which is outside the scope of this talk. To those whose work is represented in this lecture, it is my pleasant duty to acknowledge their assistance and advice. To Dr. Zay

Jan 1, 1930

By Arthur L. Christenson, Clarence E. Jackson

In the establishment of the relationship between weldability and hardenability, two methods have been employed in correcting for the grain growth produced in the heat-affected zone: first, the hardenability calculated from chemical composition* may be corrected to the grain size observed in an actual weld? or, second, a hardenability test may be made on the steel quenched from a temperature high enough to produce a grain size comparable to that found in the heat-affected zone.8 In order to obtain grain sizes in the end-quench hardenability bar comparable to those resulting in the base metal from the welding cycle, a quenching temperature of 2Ioo°F. has been used. In studies of the end-quench hardenability specimen quenched from 2Ioo°F. instead of from a lower temperature of I7OO°F., it is impor-TaiiT to ascertain The relative cooling rates for various distances along the bar. It is a question as to whether the cooling occurs at the same rate or whether there is any significant difference from the standard cooling-rate curve published by Jominy and confirmed by others.4,5 This paper reports experimental evidence concerning the effect of quenching temperature on the cooling rates in the end-quench hardenability test. The effect of quenching temperatures on cooling rates has been studied by a number of investigators.6'7 French has considered this effect from both theoretical and experimental aspects. In French's studies on complete quenching of spheres and rounds, an increase in the quenching temperature caused an increase in the cooling rate at 720°C. at the center of the specimen. The center cooling velocity also has been shown to be dependent upon the surface per unit volume for the type of specimens studied; the velocity of cooling increases with an increase in the surface per unit volume. Three methods of indicating the rapidity of cooling of a body of metal during a quenching operation have been propped: I. The time it takes for the metal to cool from the quenching temperature to a temperature halfway between the quenching temperature and the temperature of the quenching medium (half-temperature time): Grossmann, Asimow and Urban7 justify the use of this criterion by the fact that the half-temperature time includes the temperature and time of incubation as well as the zone of formation of pearlite and, further, the data so derived accord very closely with experimental values. 2. The time interval the metal remains in a given temperature range; for example,

Jan 1, 1944

By Arthur L. Christenson, Clarence E. Jackson

In the establishment of the relationship between weldability and hardenability, two methods have been employed in correcting for the grain growth produced in the heat-affected zone: first, the hardenability calculated from chemical composition* may be corrected to the grain size observed in an actual weld? or, second, a hardenability test may be made on the steel quenched from a temperature high enough to produce a grain size comparable to that found in the heat-affected zone.8 In order to obtain grain sizes in the end-quench hardenability bar comparable to those resulting in the base metal from the welding cycle, a quenching temperature of 2Ioo°F. has been used. In studies of the end-quench hardenability specimen quenched from 2Ioo°F. instead of from a lower temperature of I7OO°F., it is impor-TaiiT to ascertain The relative cooling rates for various distances along the bar. It is a question as to whether the cooling occurs at the same rate or whether there is any significant difference from the standard cooling-rate curve published by Jominy and confirmed by others.4,5 This paper reports experimental evidence concerning the effect of quenching temperature on the cooling rates in the end-quench hardenability test. The effect of quenching temperatures on cooling rates has been studied by a number of investigators.6'7 French has considered this effect from both theoretical and experimental aspects. In French's studies on complete quenching of spheres and rounds, an increase in the quenching temperature caused an increase in the cooling rate at 720°C. at the center of the specimen. The center cooling velocity also has been shown to be dependent upon the surface per unit volume for the type of specimens studied; the velocity of cooling increases with an increase in the surface per unit volume. Three methods of indicating the rapidity of cooling of a body of metal during a quenching operation have been propped: I. The time it takes for the metal to cool from the quenching temperature to a temperature halfway between the quenching temperature and the temperature of the quenching medium (half-temperature time): Grossmann, Asimow and Urban7 justify the use of this criterion by the fact that the half-temperature time includes the temperature and time of incubation as well as the zone of formation of pearlite and, further, the data so derived accord very closely with experimental values. 2. The time interval the metal remains in a given temperature range; for example,

Jan 1, 1944

By E. S. Rowland, J. Welchner, R. H Marshall

This paper presents results on an extension into the realm of high-carbon steels of some work recently published1 on the effects of time at temperature, quenching temperature and prior structure on the hardenability of one 0.20 and four 0.40 per cent carbon alloy steels. It was shown at that time that unless the conditions of time, temperature and prior structure are substantially the same in performing the hardenability test as in conducting hardening of parts in production, the correlation of hardenability information with the hardness and properties of production parts is often not of satisfactory accuracy. The general effects of these variables on the austenitic grain size, distribution of excess carbides and critical cooling rate have been known for many years and one or more have been investigated by Shepherd,2,3 Davenport and Bain,4 Digges,5,6 Digges and Jordan,' Post and associates8 and Roberts and Mehl,9 to mention only a few. There has been no systematic investigation, however, into the quantitative variations produced on the hardenability of commercial high-carbon steels by changes in these factors of time, temperature and prior structure. Procedure A plain carbon hypereutectoid steel, S.A.E. 52100 and Graph-Mo, a molybdenum-bearing high-carbon steel containing some graphite, were chosen for this investigation. The chemical analyses of these electric-furnace steels are given in Table I. The procedure used was exactly that reported previously,' hence the details will not be repeated here. Normalized (165o°F.) and spheroidized prior structures were utilized on all steels with hot-rolled and quenched (I600°F. oil) prior conditions added for the plain carbon steel. The end-quench test developed by Jominy10 was sclected for use in this investigation and, with the noted exceptions, the American Society for Testing Materials standard procedure was followed. The effect of time at temperature was examined at intervals of o, 10 and 40 min. and 4 hr., and a few 16-hr. tests were run. Salt-bath heating of the specimens was employed to control and minimize the

Jan 1, 1944

By R. H. Marshall, J. Welchner, E. S. Rowland

This paper presents results on an extension into the realm of high-carbon steels of some work recently published1 on the effects of time at temperature, quenching temperature and prior structure on the hardenability of one 0.20 and four 0.40 per cent carbon alloy steels. It was shown at that time that unless the conditions of time, temperature and prior structure are substantially the same in performing the hardenability test as in conducting hardening of parts in production, the correlation of hardenability information with the hardness and properties of production parts is often not of satisfactory accuracy. The general effects of these variables on the austenitic grain size, distribution of excess carbides and critical cooling rate have been known for many years and one or more have been investigated by Shepherd,2,3 Davenport and Bain,4 Digges,5,6 Digges and Jordan,' Post and associates8 and Roberts and Mehl,9 to mention only a few. There has been no systematic investigation, however, into the quantitative variations produced on the hardenability of commercial high-carbon steels by changes in these factors of time, temperature and prior structure. Procedure A plain carbon hypereutectoid steel, S.A.E. 52100 and Graph-Mo, a molybdenum-bearing high-carbon steel containing some graphite, were chosen for this investigation. The chemical analyses of these electric-furnace steels are given in Table I. The procedure used was exactly that reported previously,' hence the details will not be repeated here. Normalized (165o°F.) and spheroidized prior structures were utilized on all steels with hot-rolled and quenched (I600°F. oil) prior conditions added for the plain carbon steel. The end-quench test developed by Jominy10 was sclected for use in this investigation and, with the noted exceptions, the American Society for Testing Materials standard procedure was followed. The effect of time at temperature was examined at intervals of o, 10 and 40 min. and 4 hr., and a few 16-hr. tests were run. Salt-bath heating of the specimens was employed to control and minimize the

Jan 1, 1944

By Stewart L. Toleman, Robert H. Hafner, Irvin R. Kramer

In his paper on the calculation of harden-ability from chemical composition, Gross-mannl discussed the effect of most of the alloying elements used commercially. The purpose of the work reported in this paper was to determine the effect of several other elements on hardenability—arsenic, antimony, beryllium, cobalt, columbium, germanium, tellurium, tin, aluminum, and titanium—and to extend the range of composition of some of the elements studied by Grossmann—chromium, copper, manganese, molybdenum, nickel and silicon. Experimental Methods To determine the effect on hardenability, suitable amounts of the alloying elements were added to experimental heats and the hardenability determined by means of end-quenched hardenability specimens. The steels were melted in a high-frequency induction furnace with a basic crucible, using ingot iron as a base for some of the heats and S.A.E. 1015 for others. The alloying additions were made as ferroalloys or as metal, depending on the alloying element. Hundred-pound heats were split and poured into square, tapered, cast-iron ingot molds with hot tops. Aluminum was not used as a deoxidizer in most of the heats. The ingots were homogenized for 12 hr. at 1260°C. (23oo°F.) and forged into rounds of I½ -in. diameter. These bars were normalized twice from 840°C. (I55o°F.) before machining into Jominy bars. mined in most Cases by samples taken from the end-quench hardenability spedmen. AS suggested by Crafts,2 acid-soluble (8

Jan 1, 1944

By Robert H. Hafner, Irvin R. Kramer, Stewart L. Toleman

In his paper on the calculation of harden-ability from chemical composition, Gross-mannl discussed the effect of most of the alloying elements used commercially. The purpose of the work reported in this paper was to determine the effect of several other elements on hardenability—arsenic, antimony, beryllium, cobalt, columbium, germanium, tellurium, tin, aluminum, and titanium—and to extend the range of composition of some of the elements studied by Grossmann—chromium, copper, manganese, molybdenum, nickel and silicon. Experimental Methods To determine the effect on hardenability, suitable amounts of the alloying elements were added to experimental heats and the hardenability determined by means of end-quenched hardenability specimens. The steels were melted in a high-frequency induction furnace with a basic crucible, using ingot iron as a base for some of the heats and S.A.E. 1015 for others. The alloying additions were made as ferroalloys or as metal, depending on the alloying element. Hundred-pound heats were split and poured into square, tapered, cast-iron ingot molds with hot tops. Aluminum was not used as a deoxidizer in most of the heats. The ingots were homogenized for 12 hr. at 1260°C. (23oo°F.) and forged into rounds of I½ -in. diameter. These bars were normalized twice from 840°C. (I55o°F.) before machining into Jominy bars. mined in most Cases by samples taken from the end-quench hardenability spedmen. AS suggested by Crafts,2 acid-soluble (8

Jan 1, 1944

By Walter Crafts, John L. Lamont

An investigation has been made of the multiplying factors for some of the more common alloying and deoxidizing elements for use in calculating hardenability of steel according to Grossmann's method. The factors for manganese, silicon, and aluminum that were reported in an earlier communication2 have been confirmed by microscopic determination of the half-martensite structure rather than on the basis of an empirically determined hardness corresponding to a half-martensite structure. Measurement of ideal critical diameter by microscopic examination was found to be necessary for other alloying elements, and multiplying factors for nickel, chromium, molybdenum, zirconium, vanadium, titanium, and boron have been determined. The nature and order of magnitude of the multiplying factors reflect the effect of the alloying elements on the structural character of the steel. Except for nickel and vanadium, the multiplying factors agree fairly well with previously published results. Good correlation between actual and calculated ideal critical diameters has been found in developing the multiplying factors and in checking the results against fairly simple steels. However, some discrepancies have suggested the need for a more thorough study of low-carbon and complex steels. Testing Procedure The investigation was conducted principally on steels made at the Union Car- bide and Carbon Research Laboratories, Inc., in high-frequency induction furnaces using Armco iron and standard alloying materials. However, a few open-hearth steels were used in establishing the effect of nickel, and the hardenability factor for boron was based primarily on open-hearth steels. All bars were normalized prior to the machining of Jominy hardenability specimens. The Jominy test was carried out under conditions standard for the test.3 Austenitizing temperatures judged to be appropriate for the compositions of the steels were used. Chemical analysis was determined on a sample taken adjacent to the Jominy specimen. Residual amounts of phosphorus, sulphur, nickel, chromium, molybdenum, and copper were determined on only one heat of each group made with the same materials during the same period. "Acid-soluble" aluminum and zirconium rather than total amounts were determined, as it is considered probable that the acid-soluble amount is more representative of the effective alloy. As tin was present to the extent of only 0.002 per cent, its effect was neglected. The method used to determine boron in the steels shown in Table 9* was developed by Galen Porter, Vincent Napoleon, and Thomas R. Cunningham, of the Union Carbide and Carbon Research Laboratories, Inc., and is a modification of J. Naftel's procedure for boron in soils

Jan 1, 1944

By John L. Lamont, Walter Crafts

An investigation has been made of the multiplying factors for some of the more common alloying and deoxidizing elements for use in calculating hardenability of steel according to Grossmann's method. The factors for manganese, silicon, and aluminum that were reported in an earlier communication2 have been confirmed by microscopic determination of the half-martensite structure rather than on the basis of an empirically determined hardness corresponding to a half-martensite structure. Measurement of ideal critical diameter by microscopic examination was found to be necessary for other alloying elements, and multiplying factors for nickel, chromium, molybdenum, zirconium, vanadium, titanium, and boron have been determined. The nature and order of magnitude of the multiplying factors reflect the effect of the alloying elements on the structural character of the steel. Except for nickel and vanadium, the multiplying factors agree fairly well with previously published results. Good correlation between actual and calculated ideal critical diameters has been found in developing the multiplying factors and in checking the results against fairly simple steels. However, some discrepancies have suggested the need for a more thorough study of low-carbon and complex steels. Testing Procedure The investigation was conducted principally on steels made at the Union Car- bide and Carbon Research Laboratories, Inc., in high-frequency induction furnaces using Armco iron and standard alloying materials. However, a few open-hearth steels were used in establishing the effect of nickel, and the hardenability factor for boron was based primarily on open-hearth steels. All bars were normalized prior to the machining of Jominy hardenability specimens. The Jominy test was carried out under conditions standard for the test.3 Austenitizing temperatures judged to be appropriate for the compositions of the steels were used. Chemical analysis was determined on a sample taken adjacent to the Jominy specimen. Residual amounts of phosphorus, sulphur, nickel, chromium, molybdenum, and copper were determined on only one heat of each group made with the same materials during the same period. "Acid-soluble" aluminum and zirconium rather than total amounts were determined, as it is considered probable that the acid-soluble amount is more representative of the effective alloy. As tin was present to the extent of only 0.002 per cent, its effect was neglected. The method used to determine boron in the steels shown in Table 9* was developed by Galen Porter, Vincent Napoleon, and Thomas R. Cunningham, of the Union Carbide and Carbon Research Laboratories, Inc., and is a modification of J. Naftel's procedure for boron in soils

Jan 1, 1944

By E. Houdremont, H. Schrader, H. Bennek

The different influences exerted by the various alloying elements in iron and iron-carbon alloys give rise to a great number of complexities, which are difficult to grasp. It is important therefore to study any systematic relations that may exist between the effects exerted by the various alloying elements, in order to obtain a general classification and thus a clearer conception of the nature of alloy steels. A systematic survey of the alloys of iron, based on an investigation of the binary equilibrium diagrams, was recently published by Wever. Although his work deals little with properties of importance in works practice, its purpose being rather to point out the theoretical agreement among the types of binary equilibrium diagrams and the position of the alloying elements in the periodic system (atomic radii, etc.), the classification proposed nevertheless also suggests relationships among the properties of the alloys in question, even though the alloys may contain carbon in addition to iron and the alloying element. Wever divided the alloys of iron into one group exhibiting an open or enlarged gamma field and another exhibiting a closed or restricted gamma field, with both groups capable of further subdivision depending upon whether a continuous series of solid solutions is formed, or, owing to the separation of compounds, etc., only a limited series. Thus all alloying elements which with iron form a closed gamma field, a "gamma loop," produce alloys that beyond the composition corresponding to the greatest extent of the gamma loop are composed of ferrite alone at all temperatures. Alloys of this composition accordingly are not susceptible to ordinary heat treatment because of the lack of transformations. Steels of this class may thus be divided into steels that contain less than the critical amount of alloying element, and are subject to heat treatment, and those that contain more than the critical amount of alloying element and are not subject to heat treatment. Thus chro-

Jan 1, 1935

By H. Schrader, E. Houdremont, H. Bennek

The different influences exerted by the various alloying elements in iron and iron-carbon alloys give rise to a great number of complexities, which are difficult to grasp. It is important therefore to study any systematic relations that may exist between the effects exerted by the various alloying elements, in order to obtain a general classification and thus a clearer conception of the nature of alloy steels. A systematic survey of the alloys of iron, based on an investigation of the binary equilibrium diagrams, was recently published by Wever. Although his work deals little with properties of importance in works practice, its purpose being rather to point out the theoretical agreement among the types of binary equilibrium diagrams and the position of the alloying elements in the periodic system (atomic radii, etc.), the classification proposed nevertheless also suggests relationships among the properties of the alloys in question, even though the alloys may contain carbon in addition to iron and the alloying element. Wever divided the alloys of iron into one group exhibiting an open or enlarged gamma field and another exhibiting a closed or restricted gamma field, with both groups capable of further subdivision depending upon whether a continuous series of solid solutions is formed, or, owing to the separation of compounds, etc., only a limited series. Thus all alloying elements which with iron form a closed gamma field, a "gamma loop," produce alloys that beyond the composition corresponding to the greatest extent of the gamma loop are composed of ferrite alone at all temperatures. Alloys of this composition accordingly are not susceptible to ordinary heat treatment because of the lack of transformations. Steels of this class may thus be divided into steels that contain less than the critical amount of alloying element, and are subject to heat treatment, and those that contain more than the critical amount of alloying element and are not subject to heat treatment. Thus chro-

Jan 1, 1935

By E. H. Denny

In the past few years many men, including technically trained engineers, have been asphyxiated in metal mines, coal mines, tunnels and surface wells where a few relatively simple precautions with regard to ventilation and air testing would have saved them. Death from mine gases is analogous in some respects to death from poison and from drowning. The respiratory passages of a victim who has breathed oxides of nitrogen from burning explosives are badly irritated and a few hours or even a day after exposure he may develop a quick and fatal pneumonia; if, however, he enters without respiratory protective apparatus an atmosphere deficient in oxygen (a condition that may occur in unventilated or poorly ventilated parts of all underground mines) he collapses and if not rescued dies more quickly and surely than a lone nonswimmer who falls suddenly into deep water. An example of an atmosphere virtually without oxygen was demonstrated by an air sample taken by a Bureau of Mines engineer wearing oxygen breathing apparatus in a Cripple Creek shaft some years ago, during the recovery of the bodies of two victims of asphyxiation; analysis of the sample by the Pittsburgh laboratory of the Bureau showed the presence of 18.40 per cent of carbon dioxide, 0.27 per cent of oxygen, and 81.33 per cent of nitrogen, although the atmosphere apparently was clear and normal. In a mine one can pass from good, breathable air to an atmosphere that will kill as quickly as one can dive from a board to deep water below. Some Instances of Asphyxiation by Gases in Metal Mines The following typical examples of comparatively recent instances of asphyxiation in metal mines were taken chiefly from reports of various kinds of the U. S. Bureau of Mines.

Jan 1, 1940

By E. H. Denny

In the past few years many men, including technically trained engineers, have been asphyxiated in metal mines, coal mines, tunnels and surface wells where a few relatively simple precautions with regard to ventilation and air testing would have saved them. Death from mine gases is analogous in some respects to death from poison and from drowning. The respiratory passages of a victim who has breathed oxides of nitrogen from burning explosives are badly irritated and a few hours or even a day after exposure he may develop a quick and fatal pneumonia; if, however, he enters without respiratory protective apparatus an atmosphere deficient in oxygen (a condition that may occur in unventilated or poorly ventilated parts of all underground mines) he collapses and if not rescued dies more quickly and surely than a lone nonswimmer who falls suddenly into deep water. An example of an atmosphere virtually without oxygen was demonstrated by an air sample taken by a Bureau of Mines engineer wearing oxygen breathing apparatus in a Cripple Creek shaft some years ago, during the recovery of the bodies of two victims of asphyxiation; analysis of the sample by the Pittsburgh laboratory of the Bureau showed the presence of 18.40 per cent of carbon dioxide, 0.27 per cent of oxygen, and 81.33 per cent of nitrogen, although the atmosphere apparently was clear and normal. In a mine one can pass from good, breathable air to an atmosphere that will kill as quickly as one can dive from a board to deep water below. Some Instances of Asphyxiation by Gases in Metal Mines The following typical examples of comparatively recent instances of asphyxiation in metal mines were taken chiefly from reports of various kinds of the U. S. Bureau of Mines.

Jan 1, 1940