By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,' and the experimental procedure has been described in full detail.' In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

By P. Chiotti, R. J. Hecht

Vapov pressure data of solid and liquid alloys along with phase diagram data WERE employed in calculating the thermodynamic properties for the Ca-Zn system. The relative excess partial molal free energy for zinc in the liquid alloys was fitted to the relation wnvre i is we tvmpvrutiirc in ucgrees neivtu ana in is the tr~ole fvaction. Relations for the standard free energy of fortnation for the eight cornpounds were developed. ThE phase diagram for the Ca-Zn system as determined by Messing et a1.' is reproduced in Fig. 1. Earlier work on the phase diagram has been summarized by Hansen and Anderko2 and the very limited thermodynamic information for this system has been reviewed by Hultgren et a1.3 The heat of fusion for the compound CaZn2 has recently been determined to be 9260 cal per mole.4 Solubility data for calcium in zinc for the temperature range of 650" to 725°C were fitted by the relation and reported by Johnson and Dilloon5 In the present investigation zinc vapor pressure data were obtained by both the dewpoint and Knudsen methods in order to calculate the thermodynamic properties for liquid and solid alloys. The dewpoint method as employed in this work requires that only one of the components be significantly volatile, in this case zinc, and that the vapor pressure of pure zinc be known. For calculation purposes the vapor pressure data for pure zinc3 were fitted to the relations; for temperatures below 692.7K, the melting point of zinc. The corresponding free-energy relations for vaporization and sublimation of pure zinc are respectively. Some of the calculations also required knowledge of the free energy of fusion of zinc and calcium and the free energy for the 721°K allotropic transformation of calcium. The free energy of fusion of zinc was taken to be the difference between Eqs. [4] and [5], or The free energy of fusion and transition for calcium were based on the enthalpy values of 2040 and 222 cal per g-atom, respectively, as reported by Chiotti et al. 4 and the heat capacity data given by Hultgren et a1.3 and are represented by the relations, In the latter expression the difference in heat capacity between the a and 0 forms of calcium was neglected. MATERIALS AND EXPERIMENTAL PROCEDURES The metals used in preparing the alloys were Bunker Hill slab zinc, 99.99 pct pure, and Ames Laboratory calcium. The average impurities in the calcium in parts per million by weight, ppm, were N-17, H—77, Ba—216, Mg-15, Si—7, C—157, and Fe—9. The zinc was cleaned in dilute nitric acid and the calcium was used as received. The calcium was stored and handled in an argon-filled glove box and when removed from the dry box it was kept in an argon-filled desiccator. Tantalum was found to be a suitable alloy container. The alloy components were contained in a 1-in.-diam cylindri-

Jan 1, 1968

By L. R. Woodyatt, H. J. Beattie, C. T. Sims

Theories correlating the formation of u and related intermetallic compounds to the electron-per-atom density of binary and ternary alloys have appeared regularly in recent technical literature. These same principles can be modified and applied to complex precipitation-strengthened alloys such as the iron-, cobalt-, and nickel-base superalloys and the stainless steels. Since these complex alloys contain carbides and other phases that normally precipitate before the U-type phases, the nature and amount of the precipitated phases must be calculated first. The following general formula is then applied to the residual matrix composition of the alloy: element. The magnitude of the resulting number is indicative of whether the alloy will form a a -type phase. When these calculations (which are computerized) are systematically applied to alloys of knoun phase analysis, a breakoff in average electron-vacancy number is noted between U-free and U-prone alloys. Alloys with an average electron-vacancy number higher than the breakoff form a-type phases, while those with lower ones do not form these phases. This method could then be used to eliminate from consideration all experimental compositions that would precipitate undesirable phases. It also is useful in evaluating analyzed heats of alloys where minor heat-to-heat variations determine whether the alloy is o-free or o-prone. THE highly significant development of strong, ductile superalloys to provide reliable construction materials in the 1000" to 2500° F temperature range has been due principally to unremitting application of Edisonian techniques and logic by the dedicated physical metallurgists who have shouldered this responsibility. Tools such as the electron microscope, phase analysis, and computers to accomplish regression analyses have been used heavily, but the effort has been essentially practice of an art, rather than a science. The objective of this paper is to describe and illustrate application of some relatively fundamental principles to certain of these alloy systems in an attempt to remove some of the empiricism from the technology. Specifically, the work presented here deals with the use of periodic-group relationships to predict the formation of intermetallic phases which can occur in primarily austenitic (fcc) structures. Calculations that have been developed might be applied in the design of new alloys and the evaluation of known alloys, and thus have the potential of eliminating vast areas of unnecessary alloy preparation and evaluation. ALLOYING CONCEPTS AND STRUCTURAL FEATURES OF SUPERALLOYS Strength is produced in austenitic superalloys by three principle mechanisms: 1) precipitation of y'; 2) formation of carbides; 3) solid-solution hardening by soluble refractory metals. The first mechanism requires the addition of aluminum and titanium, the second requires carbon and carbide-forming elements, while the third calls for the addition of molybdenum and/or tungsten. A considerable concentration of chromium is usually maintained to resist oxidation/corrosion, but it is also an important carbide-forming element. Fig. 1 shows a sketch and electron micrograph of the structure of a typical wrought nickel-base super-

Jan 1, 1967

By V. Koump, T. F. Perzak, R. G. Olsson

The vate of dissolutioz of carbon in molten Fe-C alloys urns studied by votating- cylindrical g-vaphite sairlples in a stationary crucible containing the melt. The rate of dissolltion was determdined from the change in the bnth co)npositiorz. Alccss-tvansfev coeffi'cients, calcilated with the assurlption that the inte)yacial liquid ulas saturated with carbon, were found to be in agreement with an existing Correlation fov mass transfer jroni votating cylinders. It is corzcllrded tlat, itz the wnge of- Reynolds' numbers itzvestigated (790 to 18,000), the vate of dissolutio of carborz in Fe-C alloys is controlled by tile rate of carbon difirsion from the interface. The dissolution of carbon in molten Fe-C alloys has been the subject of a number of investigations. Most of these investigations have been inconclusive because of poorly defined experimental variables. Two of the more sophisticated studies are summarized below. Dahlke and Knacke' studied the phenomenon by, in part, immersing graphite rods into 0.5 pct carbon-steel for different lengths of time. Since the experiments were conducted in air or in CO atmospheres, the melt was strongly agitated by gas evolution. It was concluded that the change in bath composition as a function of immersion time was in agreement with the assumption that the dissolution process was transport-controlled. The hydrodynamic conditions in these experiments, however, were not well-defined and gave no indication of the nature of the dissolution process at higher fluid velocities. In a recent study Shurygin and ruk investigated the dissolution of carbon in molten Fe-C, Fe-Si, Fe-P, and Fe-Ni alloys. Small graphite disks were rotated in a crucible containing molten alloys under such conditions that only the lower face of the disk was exposed to the melt. The results of this investigation indicate that, over the range of velocities (100 to 1000 rpm) and bulk liquid concentrations (0.7 to 4.5 wt pct C) considered, the dissolution of carbon in the iron alloys is limited by the diffusion of carbon from the interface to the bulk liquid (a transport mechanism). For the particular geometry used by these authors, exact analytical solutions of hydrodynamic and diffusion problems are aailable. Hence the experimental results obtained by Shurygin and Kryuk permit the evaluation of diffusion coefficients of carbon in the four systems investigated. In the present investigation a series of experiments were conducted in which the rate of dissolution of carbon in Fe-C alloys was measured under conditions which permitted wide variation of the fluid velocity and the carbon concentration of the bulk liquid. Graphite cylinders were rotated at different speeds in a stationary concentric crucible containing various molten Fe-C alloys. THEORETICAL DEVELOPMENT In general, the resistance to mass transfer from a solid interface to a turbulent liquid is assumed to reside in a laminar boundary layer adjacent to the interface. If it is also assumed that the diffusion coefficient is independent of concentration, the steady-state rate of dissolution for the case of arbitrary liquid and solid densities can be obtained from the integration of the equations of continuity. The derivation is similar to that used by Lommel and chalmers4 for the case of pl = ps. The solution, expressed in terms where N = rate of diffusion of the solute from the interface. Exact analytical solutions of the hydrodynamic equation for the boundary layer thickness are available for only a limited number of geometries. Consequently, a mass-transfer coefficient, k, is usually

Jan 1, 1967

By Jack L. Taylor

Single crystals of tungsten grown from powder -metallurgy swaged rod by high-temperative annealing were deformed in tetzsion at temperatures from 2500 to 5000 OF. Orientation of specittzen tensile axis, strained ratrix, and defortnation bands was determined optically by reflections from {110} etch pits. Slip traces meve analyzed and slip directiorz determined. Results indicate that {110}(111) , {112){111}. and {123}{111} type slip occur in tungsten over the terpe,atuve rutge investigated. Slip is orientation-dependent occuvring on tCuzt cowzbitzation oj slip plane and direction which has the highest critical resolved shear stvess. Overshooting appears to be a general occurrence between 2500' and 5000°F. Dejornatiotz bands show rotation in a directiorz opposite to the yotation of tire tensile axis. DEFORMATION in bcc metals has been reviewed by Maddin and Chen,' Keh and eissman,' and most recently by Nabarro, Basinski, and olt. From these reviews it is apparent that some disagreement exists concerning the crystallography of plastic deformation in bcc metals. There is evidence of noncrystallo-graphic slip, the crystal slipping on or near a noncrys-tallographic plane in the (111) zone for which the resolved shear stress is greatest. There is also evidence to indicate that crystallographic slip occurs in the planes of the same zone. On the other hand, there is agreement that the close-packed direction ( 111) is the slip direction in bcc metals. Further, in pure bcc metals4 and alloys the operative crystallographic slip systems are strongly dependent on temperature. Both crystallographic and noncrystallographic slip have been reportede8 in tungsten, a group VIA bcc metal. The number of slip families which operate in the case of crystallographic slip, however, has been in question. The earliest study by oucher' of single-crystal tungsten tested at temperatures of 1800 to 5000°F led to the conclusion that only {112)( 111) type slip operated. Raymond and eumann recently reached the same conclusion studying deformation by rolling of plasma-flame single crystals at 1800°F; however, only [loo] and [110] orientations were studied. Work at high temperatures by Leber and Pughs on tungsten and Chen and Maddin9 on molybdenum suggests that conjugate slip on nonparallel (110) planes may account for the slip on (112) and (123) planes found by others working with bcc metals. The present paper presents evidence of three families or modes of slip in tungsten in the temperature EXPERIMENTAL PROCEDURE Material. Standard microtensile specimens, 0.160 in. diam by 0.640 in. gage length, were ground from commercial powder-metallurgy swaged tungsten rod, type MK. Specimens were heated for 10 min at 5150°F or 6 hr at 5400°F in vacuum of 1 x 105 Torr or less to produce single crystals. At the lower temperature an average of two out of seven specimens heated in a group developed single crystals throughout the specimen length as shown in Fig. 1, the rest remaining wholly poly crystalline. At the higher temperature, three or four out of seven specimens became single crystal. Other than to note that Laue X-ray photographs generally showed sharp, well-defined spots, no attempt was made to assess crystal perfection or measure dislocation density. Two tungsten single crystals grown from the melt by the plasma-arc process were also used for this study.

Jan 1, 1967

By D. A. Munro, G. P. Contractor

Fourteen 50-lb laboratory melts were investigated to determine the effect of uranium on the tenpering characteristics of loo-carbon (0.06 to 0.1 pct C) steels. It was found that uranium additions, particularly in the range 0.30 to 0.45 pct, enhanced the hardness and both ultimate and yield strength of the experivzental steels in the quenched and tempered condition. The structural and morphological chazges indicated that uranium retarded tempering of the tnartensite, thereby hindering the normal formation of polygonal ferrite formed in the late stages of tempering. The effect of this was to make possible the re-tension of the acicilar ferritic structure in the uranium-bearing' steels. The iraniuin-bearing steels also showed IVidnzanstatten-type growth of ferrite plates and had large prior austenite grains containing assenzblies of fine ferrite grains, mainly acicular in geometry. The fine-grained ferrite structure and the presence of more numerous and apparently smaller precipitates in the uranium-bearing steels are thought to he principally responsible for the itnproved tensile strength and hardness of the experinzental uranium-bearing steels. At ternperirzg temperatures above 455% (850'F) the ferrite in the higher-uraniun steels nzaintained acicularity and, hence, its strength and resistance to tempering. Uranium did not produce a secondary hardening peak. However, it retarded softening during the third stage of tempering because of its effect of inhibiting the grouth of cementite particles and of retaining the acicularity of ferrite plates. The resistance to coalescence accounted for the slow grocth of the ferrite grains in the uranium-modified steels and, hence, fov the persistence of the acicular ferrite structure. IT had been found previously1 that uranium additions up to about 0.45 pct had no significant effect on the tensile properties of low-carbon steel (0.06 to 0.10 pct C) in the as-rolled and normalized conditions, Fig. 1. On the other hand, it was observed that uranium in excess of about 0.30 pct had an embrittling effect as revealed by Charpy V-notch impact results. It was also noted that, as the uranium content increased, the morphology of pearlite changed from lamellar to feathery and the ferrite grains showed an etching effect resembling striated or dashed markings, suggestive of precipitation. The sharp drop in the impact properties shown in Fig. 2 warranted an assumption that the uranium content of about 0.30 to 0.45 pct may produce some secondary hardening reaction on tempering, analogous to that associated with a Cr-Mo-V steel, which shows very poor CVN toughness at the secondary hardness peak in the tempering curve.1' With this background and the reported findings of Hasegawa and noda that low-carbon uranium-treated steel showed signs of secondary hardening, the present investigation was undertaken to determine the effect of uranium additions on the mechanical properties of 0.10 pct C steels. No attempts were made to investigate in detail the mechanisms of hardening, although some suggestions based on the experiments are made. MATERIALS AND PROCEDURES A series of 50-lb induction-furnace melts was made using AISI 1008 rimming steel billets as the melting stock. The melting, forging, and rolling techniques proven satisfactory in previous projects'-3 were employed as a guide for this investigation. The steel was deoxidized with aluminum (2 lb per ton) prior to the addition of high-purity uranium. The analysis of each melt is given in Table I. Properties were evaluated as a function of heat treatment and are presented in terms of hardness and tensile strength vs tempering temperatures. The variation of hardness with the tempering temperature was studied on the quenched and tempered specimens, some of which measured 0.50 by 0.25 in. diam and the others 0.40-in. cubes. Before quenching, the specimens were vacuum-sealed in glass tubes and normalized at 900°C (1650°F) for 20 min. Following this treatment, the sealed specimens were hardened by austenitizing at 955°C (1750°F) for 20 min and water quenching, and then tempered for 1 hr in the range 150 to 730°C

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By D. R. Uhlmann, T. P. Seward, O. Chalmers

A magnetic field has been used to damp out liquid convection during the solidification of castings. Ingots of Al-2 pct Cu were poured from various sperheats (10" to 65°C) into a room-temperature graphite mold located between the poles of an electromagnet. The effect on ingot structure of varying the strength and time of application of the magnetic field was investigated, and the results are interpreted in light 01- current theories of ingot structure. In the solidification of alloy systems, thermal gradients in the melt and differences in density of the constituents are expected to produce convective motion in the liquid. The thermal convection caused by temperature gradients should be present during the freezing of both alloys and pure materials, while the solute convection caused by density differences should be of concern only for alloys. The possible influence of this natural convection on the structure of castings has been discussed by Ruddle,' Chalmers, and Tiller. More recently, an experimental investigation of such effects was carried out by Cole and Bolling. These workers took stationary molds containing lead- and tin-based alloys and. using a brine solution. quenched them from various superheats above their respective liquidus temperatures. When grids were placed across the mold diameter to suppress convection, the grid region was later observed to contain a larger percentage of columnar grains than other parts of the casting or than similar castings poured without the grids present. From thermocouple measurements, they found the temperature in the grid region to be higher than that in the region outside the grids throughout the freezing process, and concluded that convection should be an important mode of heat transfer in normal castings. In addition to such convection arising from thermal gradients or differences in density of the constituents, a further source of convective motion, which we shall call "momentum convection", may be particularly important in small (laboratory-size) castings. By this term we refer to the convective motion produced in the initial pouring process, a motion which is damped out as the linear momentum and angular momentum of the liquid are dissipated. Besides these sources of convection, which are present to some extent in all castings. external influences may also be effective in producing convective motion. Examples of such "forced" convection which have been discussed in the literature include stirring the melt, shaking the mold, rotating the mold, and so forth The purpose of the present study was to examine the effect of convection on the structure of castings poured into a cold mold. In this work, a magnetic field was employed to damp out the convective motions within the liquid, and hence control the extent of con- The effect of a magnetic field on convective currents in a conducting liquid is to induce eddy currents which oppose and damp out the convective motion. vection. The technique of magnetic damping was previously used by Utech and F1emings" in their study of convective effects on impurity banding and other substructure in alloy crystals grown unidirectionally from the melt. In their investigation, fields as small as 200 gauss were found to be effective in damping the convection currents which influence the banding. I) EXPERIMENTAL TECHNIQUE In the present study, alloys of A1-2 wt pct Cu were poured into a room-temperature graphite mold. The mold, in the shape of a circular cylinder, 2 in. ID, 2-3/4 in. OD, 5 in. inside height, and 5-1/2 in. outside

Jan 1, 1967

By Wei-Kao Lu, G. Bitsianes

An improved general rate equation for a one-ditnensional gas-solid system has been derived. Fov the veversihle interfacial chemical reaction, there are concentrations of gaseous reactant and product at the reacting zone to be considered. They have been calculated with the velations fuvnished by the constraints on the system, namely, quasi-steady state and equimolal counterdiffusion of the gases. The results of the diffusiori study of Evans, Watson, and ,Mason based on the "dusty gas" model have been applied here. The interfacial chemical reaction is taken as first-order with respect to the concentration of the gases involved. The equation has proper dependence on gas composition and on solid structure through the relative values of Knudsen and normal diffusivities. The existence of the total pressure gradient inside the specimen has been predicted and confirmed experimentally. In a previous communication' we introduced a general rate equation for gas-solid reactions by considering the contributions of chemical reaction at inter- phase boundaries and diffusion through the solid product layer simultaneously. These equations, for one-dimensional and spherical specimens, take care of the whole range continuously from purely diffusion control to purely chemical reaction control. In this paper we study only the one-dimensional system. The corresponding rate equation is reproduced here: Of the two terms on the right-hand side of Eq. [I], the first represents the contribution of interfacial chemical reaction and the second that of gaseous diffusion. The shortcomings of Eq. [I] are that in its derivation the interfacial chemical reaction was assumed to be irreversible and the diffusion rate of gaseous product was not considered. Any pressure effects building up within the porous media were also neglected. Evidently. these simplifying assumptions will limit the general applicability of these equations. The rate of reduction of iron oxide by hydrogen, for instance, is very sensitive to the concentration of water vapor in the main gas stream, as has been reported by cewan' and by Quets et a1.3 Furthermore, the gaseous phase at the reacting interface will contain an appreciable amount of the gaseous product of reaction. If this were not true, a sufficiently high concentration gradient for the outward diffusion of the gaseous product could not be maintained. With these shortcomings in mind, Eq. [1I cannot be rigorously ap-

Jan 1, 1967

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By Robert D. Pehlke, Robert G. Blossey

The solubility of nitrogen in liquid binary and ternary Fe-Ni-Co alloys has been measured by the Sieverts&apos; method between 1550°and 1700°C. Solubility data and standard free energzes and enthalpies of solution for nitrogen in the alloys are presented. Interaction parameters are discussed and presented for binary and ternary alloys. MOST of the studies of nitrogen solubility in liquid metals have been directed toward the dilute alloys of iron. Several of these investigations have included measurements of the nitrogen solubility in Fe-Ni al10s&apos;- and in Fe-Co alloys.435 There has been some work, however, that has extended across the e-i-" and F-CO" binaries. This investigation was undertaken to determine the nitrogen solubility in both binary and ternary alloys of the Fe-Ni-Co system. It was also hoped that the differences between earlier studies might be resolved. EXPERIMENTAL METHOD This investigation was made using a Sieverts&apos; apparatus described previously." The nickel (99.85 pct) and cobalt (99.9 pct) were obtained from Sherritt-Gordon Mines, Ltd., and the iron (99.95 pct) was Fer-rovac-E obtained from Crucible Steel Co. Recrystal-lized alumina crucibles were used throughout the entire investigation with no evidence of crucible-melt reaction. Melt temperatures were measured with an optical pyrometer and the temperature scale calibrated against the melting points of the three pure metals. The emissivity of the melt was assumed to be a linear function of composition for all alloys, as has been shown for Fe-Ni alloys.lZ The emissivity of the pure metals at 1600°C were taken as 0.43 for iron, 0.44 for cobalt, and 0.45 for nickel. Using these emissivities, the trans mis sivity of the system was found to be 0.51 i 0.01. The Sieverts&apos; method was used for this study and followed the procedures outlined previously.l&apos; The individual metals were weighed to give about 100 g of alloy. The alloys were melted in the crucible under a partial pressure of argon. The system was evacuated, and the "hot volume" was measured with argon. To avoid the errors caused by vaporization, the melt was held under vacuum only long enough to ensure that all of the gas in the system had been removed. The influence of any small amount of vaporization on the "hot volume" was shown to be negligible by measuring the "hot volume" after a run. This measurement agreed with that made at the start of the run within the implicit error, 0.2 cc, caused by the limitations in accurately reading the buret. The solubility-pressure relationship was measured in the pure metals and in several alloy compositions throughout the ternary system. These measurements were made by admitting measured amounts of nitrogen to the system, and then determining the equilibrium nitrogen pressure above the melt. This method has the distinct advantage of higher accuracy, particularly at lower pressures, than measurements made by withdrawing gas from the system to reduce the pressure after determining the solubility at 1 atm nitrogen pressure. This latter method has a practical lower limit of about 0.4 atm where an increased error is encountered because the buret must be emptied to permit further measurements at lower pressures. By determining the relation between apparent solubility and pressure, it was possible to make a good estimate of the initial nitrogen content of the metal from the intercept of the solubility curve extrapolated to zero pressure.11 DISCUSSION The solubility data corrected to 1 atm nitrogen pressure are summarized in Table I. The reported solubility has been corrected for the initial nitrogen content of the alloys. The initial nitrogen contents fell between 0.0002 and 0.0010 wt pct, and were lower in the iron and nickel than in the cobalt. Sieverts&apos; law was obeyed in all alloys at pressures up to 1 atm. Examples of this behavior are shown in Fig. 1. The reaction for solution of nitrogen is Taking the standard state as 1 wt pct N in the alloy and the reference state as nitrogen at infinite dilution in the alloy, and noting the adherence to Sieverts&apos; law, K becomes the solubility of nitrogen in the alloy at 1 atm pressure. Thus the solubility data of Table I were used directly to calculate the standard free energy for the solution reaction. These results are also presented in Table I. The enthalpy of solution is also summarized in Table I as calculated from a form of the van&apos;t Hoff relation: Iron-Nickel System. The data for the solubility of nitrogen in liquid Fe-Ni binary alloys is presented in Fig. 2 along the with data of aito, Schenck et al.,&apos; and Humbert and 1liott.l&apos; The data for studies of nitrogen solubility in Fe-Ni alloys containing less than 20 pc t i&apos;- are not presented in Fig. 2, although they are in good agreement with the present work. The results of this study are in good agreement with Schenck

Jan 1, 1967

By C. M. Sellars, F. Maak

Electvomotie -force measurements hazle been made on ten Au-Ni alloys at temperatures 7754 825O, 900O, and 935°C using galvanic cells with solid electrolyte. Partial and ivtegral thermodynamic functions are derived from the determined activities. which show la9,ge positive deviations jvom Raoult&apos;s law. The enthalpies of mixing- are in close accord with calorinletric data and are of comparable accuracy. The results are used to determine the miscibility gap and the spinoidal curL1e, and are qlalitaticely interpreted in terms of the large size difference and electvonic interactions between gold and nickel. Tabulated nalues of the actielities and partial and inteqal free energies, entropies , and enthalpies of mixing are given in the appendix. The Au-Ni binary alloys are of particular interest thermodynamically as despite the large size difference between gold and nickel atoms they have a simple phase diagram.&apos; This shows complete solid solubility above a miscibility gap with a maximum at about 71 at. pct Ni and 810°C. Activity measurements (over a range of temperature) have been made previously on this system using an electrolytic-cell method with a liquid chloride eletrolyte. The accuracy of this data has, however, been queried3&apos;4 as it leads to values for the enthalpy of mixing which are too high when compared with calorimetric measurements.46 Also, the entropy of mixing is too high when compared with the values derived from specific-heat measrements. It was therefore considered worthwhile redetermining the activity data using a galvanic cell with a solid electrolyte (0.85 ZrO, 0.15 CaO). This method is based on a technique introduced by Kiukkola and aner&apos;&apos; and has been used to determine the thermodynamic data for Cu-Ni alloys.&apos; THE ELECTROLYTIC CELL The cell used to determine the activity of nickel in Au-Ni alloys was: The cell reaction, which is discussed for a similar cell by Rapp and Maak, gives a direct measurement of the activity of nickel in the alloys as where aNi(alloy) is the activity of nickel in the alloy, 3 is Faraday&apos;s constant, E is the measured electromotive force, R is the gas constant, and T is absolute temperature. For the valid application of this type of cell the arrangement must be ther modynamic ally stable, which means that: 1) The free energies of formation of the oxides fulfill the relation 2) The vapor pressures or dissociation pressures of each component must be so small that during the time of the experiment the amount of any material transported by the gas is negligible. 3) Side reactions which change the alloy composition must be negligible. These reactions are possible both with the surrounding gas atmosphere and with neighboring solid material. The first two conditions are fulfilled by the above cell.&apos; The third condition is approached by care in the experimental technique. The factors which control the attainment of equilibrium in this type of cell have been considered by Rapp and aak, who conclude that metallic diffusion in the alloy is the rate-control ling step. A lower temperature limit for the practical application of this cell is therefore set by the condition that equilibrium must be attained in reasonable times. EXPERIMENTAL MATERIALS AND TECHNIQUE The starting materials were mint gold (99.99 pct Au) and Mond nickel (99.9 pct Ni). Alloys, nominally 5 at. pct Ni and then each 10 at. pct across the system, were produced by vacuum-levitation melting compacts of mixed drillings of the pure metals. The nickel used for the reference tablets in the cells was melted in a similar manner. The alloy ingots, cast in boron nitride molds, were cold-forged and

Jan 1, 1967

By W. M. Yim

Experimental results are presented which indicate that transverse striations in horizontal zone-leveled Bi-Sb alloy crystals are due to irregular growth rate resulting from thermal fluctuations in the melt (Iring gowth. Thc thermal fluctutations arose from two different sources. The first type was brought about by periodic fluctuations in the furnace temperature. The second type can be attributed to turbulent therrrol conlcclion in the trzelt near the solid-liquid inteyace. Tile arrzplitlcde ond fvequency of the tetiperaticre fluctlrations vesultity from llle lhevnal con1,ecrrell. The striation spacings in Lhe crystals covvelale well with the periodicity 0.f the tempevature flueluatiors. Altliough the strialiors represenl corrlpositiozul inhoiHogeneity oh a rzicroscule, less than f.z cil. be1 S6 in Best&apos;s as deterrirzed by electron-pro be chalq&apos;sis, the slriations roerre fbund to ILUL&apos; no rrleusuanble effect on electical vesistirity rwr on weak field macgnetoresistance of. the Bi-Sb a1lu.y in the ternpevutue ),unge 4.Polo 300°K. DURING the course of an investigation on the horizontal growth of semimetals,&apos; it was found that crystals of Bi-Sb alloys contained many closely spaced parallel arrays of striations. These striations occurred perpendicular to the growth direction and parallel to the solid-liquid interface. We shall refer to them as transverse striations, or just striations&apos;&apos;, to distinguish them from lineage substructures or longitudinal striations which form parallel to the growth direction and have been known to be associated with cellular structures.&apos; Similar transverse striations have been reported previously to occur in other materials prepared by horizontal growth: metals,4 semiconductors,5 as well as their alls. - Various methods of crystal preparation have apparently little effect on the occurrence of the transverse striations. They form whether the crystals were grown by the vertical Czochralski technique, withe1&apos; or without&apos;3- rotation, or by the horizontal zoning methd.- Thus, the transverse striations are not limited to any one class of materials, nor to any particular method of preparation. It is likely, therefore, that all of the observed transverse striations may have some common cause. Previously, workers agreed that periodic changes in the growth rate bring about the striations. However, no agreement exists as to the origin of the growth-rate fluctuations. Some attributed the discontinuous growth to a purely external cause, such as fluctuations in the furnace temperature, jerky motions in the crystal pulling mechanism, or a nonsymmetrical temperature distribution in the melt (in the case of crystals grown by the Czochralski technique with rtation). Others looked for the cause in some fundamental property of the growth process itself. For instance, a certain degree of supercooling is required to initiate growth from the melt. But, with further growth, the degree of supercooling decreases because of the liberation of the heat of solidification at the solid-liquid interface. Thus, crystal growth would be brought to a halt until sufficient supercooling is resotred and the cycle begins again.3&apos;11 According to this model, periodic fluctuations in the melt temperature should exist at the solid-liquid interface. Since the periodic fluctuations in growth rate would result in changes in the segregation coefficient of solute atoms, crystals containing the transverse striations may, in some cases, show a periodic impurity fluctuation along the length, resulting in a degradation of electrical properties. The resistivity striations in doped germanium&apos;9-10 or lnsbB are well-known examples of this microsegregation. The present work was undertaken to explain the exact origin of the transverse striations, and to assess the extent of their effect on chemical homogeneity as well as on electrical properties of Bi-Sb alloy crystals. Results from our previous study of the crystal growth of Bi-Sb alloys1 indicated that the transverse striations may arise from the temperature fluctuations in the melt during growth. This paper will show that the melt temperature fluctuations are indeed responsible for the occurrence of the transverse striations. I) EXPERIMENTAL Although the transverse striations have been observed in all slow-grown Bi-Sb alloys across the entire compositional range, we selected a composition, Big3Sbs, for the present study in view of the extensive data available on the crystal growth of this alloy from a previous study.&apos; High-purity bismuth and antimony, both a 6-nine grade by the manufacturer&apos;s emission spectrographic analysis, were used throughout. Independent mass-spectrographic analysis showed, however, that the starting materials were more nearly a 5-nine grade. each containing metallic impurities of approximately 10 ppm atomic. In zone-leveled Big5Sb5 alloys, the total metallic-impurity content was slightly lower, about 7 ppm atomic, indicating that some degree of purification was achieved during the growth. None of the electrically active impurities, such as tin and lead (acceptors) and tellurium and selenium (donors), were present in significant quantity in undoped Bi95Sb5. Typical analysis of the undoped Bi95Sb5 alloy is shown in Table I. Nonmetallic impurities, such as carbon and oxygen, were detected, sometimes as much as 100 ppm, in both the starting materials and the zone-leveled alloys: but the data were only qualitative. Temperature fluctuations in the melt were monitored over 1 or more days by means of a 5-mil chromel-

Jan 1, 1967

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969

By Y. Nakada, E. J. Fasiska, A. S. Keh, L. Zwell

DURING an investigation of solid-solution hardening of nickel by carbon,&apos; we found that there were no reliable data on the dilating effect of dissolved carbon on the unit cell of nickel. Bernier2 reported an increase in lattice parameter of nickel (3.523A) when an unknown amount of carbon was introduced into solid solution (3.536A). Similarly KG, Tsien, and Misek3 found an increase from 3.523 to 3.531A when nickel was carburized. strong4 studied the variation of nickel lattice constant as a function of dissolved carbon. However, in his case carbon was introduced into nickel by solidifying the melt at 65 kbar. Therefore, his carbon concentrations were much above the highest equilibrium solubility limit5 (2.7 at. pct C at 1 atm). Knowledge of the lattice mismatch between solute and solvent is essential in understanding the mechanism of solid-solution hardening. Therefore, we decided to determine the dilation of the nickel lattice by carbon under the more usual conditions of atmospheric pressure. The material used was Inco Electrolytic Nickel of 99.95 pct purity, as specified by the supplier. The impurity contents in wt pct were: Fe, 0.01; Cu, 0.01; Co, 0.03; 0, 0.005; C, Si, S, N, trace. To this base material various amounts of AUC-grade high-purity carbon were added during vacuum induction casting. Ingots, 2 in. in diam, were heated in a muffle furnace at 1000°C for i hr., hot-rolled to 1/2-in. thickness, and quenched into brine. All ingots with carbon concentration greater than 0.98 at. pct were enclosed in a cast iron box during the heating to minimize decar-burization. Small pieces were then either swaged down to 0.028-in.-diam wire or cold-rolled to 0.010-in.-thick sheets. After the final cold reduction in area of 50 pct, the specimens were recrystallized by heating in evacuated capsules at 1100°C for 60 to 80 sec and then quenched into brine. The final grain size was 50 to 100 µ. The carbon contents of the alloys, Table I, were determined by a combustion method

Jan 1, 1969

By Harold Margolin

The Ti-Al system certainly merits the investigative attention it has been receiving and this latest contribution by Blackburn is therefore to be welcomed. The titanium-rich end of the phase diagram shown here, as well as the diagram by crossley,17 Clark et a1.,18 and Tsujimoto and Adachi,29 reveal no other intermediate phase than Ti3A1, although a previous work by Ence and Margolin20 had reported an additional intermediate phase. Since then, Buerger Precession pictures of single crystals of 10.5, 11.5, and 12.5 wt pct A1 were made at New York university21 and the extinctions were found to be typical of a D6h a Ti structure. Some superlat-tice spots and/or streaks suggesting the presence of an Mg3Cd structure, i.e., Ti3Al, were also found. Since these specimens had been quenched from the y region20 and had revealed a Ti, it was concludedz1 that y does not exist and the structures interpreted as m + y could not be so considered. The absence of normal two-phase behavior in these structures had been indicated in the paper. Accordingly, the two-phase region y + 6 becomes a + Ti3Al and there is some agreement between the results of Blackburn and of Ence and Margolin20 as to both shape and existence above 900°C of an a + Ti3Al field. Crossley 17 proposed that Ti3Al is a line compound which decomposes congruently at 900°C. It is difficult to discount entirely the fact that clear two-phase structures, varying in amount with position in the two-phase field, could be detected above 900°C by Ence and Margolin.20 Precipitation during quenching could not have been so regular and the twin-phase syndrome17 does not apply. The heat treatment and quenching technique was essentially the same as was used by Crossley, whereas Blackburn, who used a rapid quenching procedure, also showed a two-phase a + Ti3A1 field above 900°C. If the two-phase field exists above 900° C, it is easy to picture a two-phase field which could account for the data of Crossley below 900°C without invoking a line compound existence of Ti3A1. All that would be necessary would be an 0 + Ti3Al/Ti3Al boundary which curved sharply to higher aluminum contents below 900° C. It is clear that the controversy must be solved by techniques which obtain data at elevated temperatures without quenching. It is conceivable that the difference in width of the a + Ti3N fields reported by Blackburn and by Ence and Margolin is due to the longer annealing times used by the latter investigators. The criterion for establishment of equilibrium in our work20 was the

Jan 1, 1969

By F. A. Crossley

The key to disagreements between Blackburn&apos;s findings and mine is the word equilibrium". My work attempted to define the equilibrium diagram of the titanium-rich end of the Ti-A1 system. It can readily be shown that Blackburn&apos;s conclusions are based primarily on the examination of structures substantially removed from equilibrium. The diagram presented in Fig. 16 is properly labeled a "phase diagram". However, it appears that Blackburn either does not understand or does not accept the difference between "phase diagram" and "equilibrium diagram" as defined in the Metals Handbook.17 The conflict lies not in Blackburn&apos;s data but in his interpretation of it, and his use of "transformation", "phase diagram", and "equilibrium diagram" as synonymous terms. I share his view that the light microscope is much inferior to the transmission electron microscope for the study of transformations; but this fact does not render the light microscope useless or untrustworthy. The difficulties experienced with the Ti-A1 system have not been due to the limitations of the light microscope, but rather to the extreme sluggishness in achieving equilibrium at temperatures below 1000° C. Were it not for the light microscope employed with polarized light, the twin phase syndrome&apos; might still be unrecognized and, as a consequence, still adding to the confusion of Ti-A1 investigations. (Ref. 1 should read ... Contract No. N161-25952 ... vol. 236.) Other, more sophisticated techniques, including electron transmission, simply confirm the erroneous tentative conclusions drawn from observations of structures due to the twin-phase syndrome. By the standards of most of the investigations of the Ti-A1 systems, seven of the fifteen compositions investigated by Blackburn were seriously contaminated with oxygen. The writer has found that 0.1 wt pct 0 shifts the a + Ti3A1 boundary to 1 at. pct lower A1 content at 700°C. At constant aluminum content, this corresponds to a temperature shift of the boundary of +25°c.18 Blackburn advises that the first group of alloys contained 0.1 to 0.15 wt pct 0, bur he does say whether the analyses were performed on as-received material or on specimens in their final state of heat treatment. This is especially important considering the 20-mil-thick starting materials. If specimens had been annealed in the two-phase a + 6 region it would have provided an indication of the final degree of oxygen contamination since up to about 12 at. pct A1 the boundaries of this region are well-defined for low-oxygen alloys. Blackburn questions the capability of light microscopy in determining phase boundaries in the Ti-A1 system. I submit that the a/a + Ti3A1 boundary in Fig. 1 of Ref. 1 over the composition range from 10 to 18 at. pct A1 was determined by dilatometry and supported by electron diffraction. Specimens of alloys containing 8, 10, 12, and 14 at. pct A1 were aged at 550°C for 1000 hr (under stress of 5000 psi to accelerate the tendency to equilibrium) and then fractured in tension at room temperature. Collodion was applied to the as-fractured (unetched) surface and, when stripped, carried away particles identified by electron diffraction as Ti3A1. Perhaps Blackburn will explain why these electron diffraction data were ignored. At this time, a technique for revealing or indicating

Jan 1, 1969

By J. J. Frawley, W. J. Childs

PREVIOUS studies have shown that if a supercooled liquid metal was perturbed by vibration the probability of nucleation is is During a recent investi- gation to determine quantitatively the amount of energy needed to cause nucleation in a given supercooled liquid specimen, it was found that at low-energy values in the megacycle range, below the threshold energy value for cavitation, the amount of dynamic supercooling was greater than the amount of static supercooling. That is, if a specimen had a given amount of thermal supercooling under static conditions, its thermal supercooling could be increased by the addition of low-energy sound waves. The material used in this investigation was high-purity bismuth. This material was chosen because of its low melting point and the high degree of supercooling which could be easily obtained. The sound gener- ator employed in this work was a commercially built Sperry ultrasonic testing unit. This unit was equipped with a barium titanate crystal as a piezoelectric transducer. These sound waves were transmitted to the supercooled melt by a Pyrex rod, as shown in Fig. 1. The transducer was coupled to this Pyrex rod wave carrier by motor oil. The Pyrex wave carrier was approximately 1.5 ft long to prevent damage to the transducer by heat. The diameter of the Pyrex wave carrier appears to be critical. In the initial tests a wave carrier of 0.5 in. in diam was employed. However, the sound waves had no effect on the amount of dynamic supercooling. When the diameter of the wave carrier was increased to approximately the inside diameter of the Pyrex crucible, the sound waves were more effective. Approximately 200 g of metal was melted under a stannous chloride flux in a 30-ml beaker by induction heating. The temperature was recorded by a Pyrex-encapsulated chromel-alumel thermocoule which was placed in the beaker after the bismuth melted. The Pyrex wave carrier was immersed slightly below the surface of the liquid bismuth and the specimen was reheated to about 500°C. It was observed that the amount of supercooling depends on the amount of superheating the specimen receives; therefore, for meaningful results the amount of superheating was the same for all heating cycles. The specimen was allowed to cool in air and the change in temperature was continuously monitored with a potentiometric strip-chart recorder.

Jan 1, 1969

By M. J. Hordon, M. A. Wright

ReCENT work has indicated that the substantial decrease in the rate of fatigue crack propagation for aluminum observed below a critical vacuum level can be attributed to the depletion of oxygen or water vapor from the vicinity of the fatigue crack opening.&apos; At reduced gas pressures, generally below 10-2 Torr with fatigue strain amplitudes in the range *1 to 2 x 10-3 and cyclic loading rates of 25 to 50 cps, estimated rates of oxide or hydroxide monolayer adsorption on newly formed crack surfaces can fall behind the actual rate of crack extension. Changes in the critical pressure required for the transition in fatigue behavior with changes in temperature, strain amplitude, and cyclic frequency can be interpreted from variations in the adsorption and crack growth rates.&apos;" Although the adsorption model generally appears to explain the enhanced fatigue resistance of reactive metals in vacuum, the specific adsorbing gas species and nature of the adsorption mechanism are uncertain. In addition to the direct dissociation and adsorption of O2 on the metal surfaces,3 the dissociation of H20 and subsequent adsorption of H ions have been advanced for aluminum alloys.4 The present note describes some measurements of the fatigue behavior of 1100 aluminum in reduced partial pressures of specific gases including O2, H2O, and H2 in order to provide additional experimental data. Cantilever-type specimens of 1100-H14 aluminum were fatigued in cyclic reverse bending at constant strain amplitude using a multispecimen vacuum apparatus and procedure described previously.&apos; After initial vacuum evacuation to 1 x 10-7 Torr, the appropriate gas species was bled into the system through a calibrated leak valve. The input rate was adjusted to maintain the desired pressure level under continuous evacuation, thus minimizing possible changes in gas composition during testing. High-purity input gases including 99.9 pct O2, 99.999 pct H 2, and water vapor from triply distilled H 2 O were used to provide residual pressures. Trace amounts of contaminant species were limited by passing the Oz and H 2 input gases through liquid-nitrogen-cooled copper coils prior to entry to the test chamber. Care was taken to repeatedly flush the gas lines and valves before testing to minimize the effect of adsorbed contaminants. Residual gas pressures in the range 10-6 to 5 x x3 Torr were monitored by an NRC ionization gage corrected for each gas species. In the higher-pressure range, 5 x 1CT3 to 5 x 10&apos; Torr, an NRC alphatron gage was used. In operation, eight simultaneous fatigue tests were conducted at a constant strain amplitude of *1.2 x 10 at cyclic bending rates of 25 and 50 cps to give an average fatigue life of 6.5x 105 cycles-to-fracture at standard atmosphere and 3.3 x 106 cycles in 1 x 10"7 Torr vacuum. Representative results for the effect of residual O2, H2O, and H2 contents on the fatigue life are shown in Fig. 1 for tests performed at 50 cps. It is apparent that the presence of either O2 or H2O gas in the system at partial pressures greater than 10"3 Torr was noticeably detrimental to the fatigue life. In contrast, the enhanced fatigue resistance typical of high-vacuum environments was retained with pure H 2 through the pressure range up to 1 Torr. For partial pressures of H2 gas above 1 Torr, the fracture life noticeably decreased. The critical Hz

Jan 1, 1969